CN85108839A - 电极的制备及其在电化学加工上的应用 - Google Patents

电极的制备及其在电化学加工上的应用 Download PDF

Info

Publication number
CN85108839A
CN85108839A CN85108839.2A CN85108839A CN85108839A CN 85108839 A CN85108839 A CN 85108839A CN 85108839 A CN85108839 A CN 85108839A CN 85108839 A CN85108839 A CN 85108839A
Authority
CN
China
Prior art keywords
compound
family element
interpolation
electrode
plating bath
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN85108839.2A
Other languages
English (en)
Other versions
CN1008748B (zh
Inventor
安东尼奥·尼多拉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
De Nora SpA
Original Assignee
De Nora Permelec SpA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from IT24067/84A external-priority patent/IT1196372B/it
Priority claimed from IT22529/85A external-priority patent/IT1185464B/it
Application filed by De Nora Permelec SpA filed Critical De Nora Permelec SpA
Publication of CN85108839A publication Critical patent/CN85108839A/zh
Publication of CN1008748B publication Critical patent/CN1008748B/zh
Expired legal-status Critical Current

Abstract

本发明涉及在电化学加工中使用的电极的制备方法，该电极是以伽伐尼电镀法将电催化涂层沉积在导电的支承体上制成，并用ⅠB、ⅡB、ⅢA、ⅣA、ⅤA、Ⅷ等族元素加固。
在制涂层的伽伐尼电镀浴中加入适合的上述掺杂元素的化合物所制得的本发明的电极，当作为隔膜或膜片氯-碱槽的阴极时，呈现低的氢超电势，对时间稳定，并在实质上能避免碱液中的铁、汞或其他杂质的毒化作用。

Description

电极的制备及其在电化学加工上的应用
本发明涉及用于电化学加工特别是电解碱金属囟化物的离子交换电槽或渗透性隔膜电槽中使用的阴极的制备方法，更具体地说，是在碱金属氢氧化物溶液存在时作为释放氢的阴极的制备方法
本发明的另一目的也是关于上述电极的。
工业电极的主要要求是要有较低的氢超电势，这样就可降低能量消耗，对安装时出现的应力或操作时因液体的湍动产生的应力也有一定的机械稳定性。
将满足上述要求的电极安装在适合的导电材料上，如铁、钢、不锈钢、镍和其合金、铜和其合金，并在其上镀以电催化涂层。
所说的电催化涂层，可用电镀或无电沉积用导电的金属或金属合金制成，但只有部分电催化金属呈现较低的氢超电势，如镍或其合金、铜或其合金、银或其合金、铂族金属，这些金属以均相在涂层中存在，最可能是固溶体。
电催化涂层可以导电金属用伽伐尼电镀制备，也可用无电沉积制备。但只有部分含分散颗粒的电催化金属呈现释放氢的较低超电势，如上面所述的镍、铜、银及其合金。电催化颗粒可属于下面一组中的元素，包括钛、锆、铌、铪、钽、铂族金属、镍、钴、锡、锰等并以金属或其合金或其氧化物、混合氧化物、硼化物、氮化物、碳化物、硫化物的形式悬浮于用于沉积的（电）镀浴中。
在涂层中分散电催化颗粒的电极的例子，已在比利时专利No.848，458（相应的专利为意大利专利申请No.29，506    A/76和美国专利No.4，465，580）中说明。
使用上述电极有一特别严重的缺点，即当作为电解金属囟化物的隔膜或离子交换电槽的阴极时，由于电解液中所含的金属离子对催化表面构成进行性毒化作用，结果氢超电势逐渐增高。这代表了包括必须定期替换阴极在内的一特别严重的问题，影响了电加工效率。
引起毒化作用的金属杂质包括Fe、Co、Ni、Pb、Hg、Sn、Sb或类似金属。
在隔膜槽中电解盐水的特定情况下，金属杂质经常是铁和汞。
杂质铁的来源有二：
一为化学来源，即来自阳极电解液，当原料盐中含有作为防结块剂使用的亚铁氰化钾时。
一为电化学来源，即来自阴极室及其附件钢结构的腐蚀。
杂质汞槽转变为隔膜槽后在盐水回路中发现。
这些杂质通常以络合物的形式存在于溶液中，一经扩散到阴极表面，它们便迅速电沉积成金属状态，在相当短的时间里便生成了电催化层，电催化性能极差。
这种催化老化现象取决于不同的因素，如阴极材料的类型（组成和结构）、操作条件（温度，阴极电解液的浓度）和杂质的性质。甚至只有百万分之几的杂质浓度存在时，操作很短的时间后就会产生显著的老化作用，而且是不可逆的。鉴于这些实质性的实际缺点，发明者仔细研究了有不同组成的电催化涂层的一些阴极的行为，惊异地发现将某些元素加入伽伐尼电镀沉积浴中（已如上述，并见于技术文献和专利文献）得到了呈现低氢超电势的电极，并保持稳定，或者延长工作周期时接近稳定（电解液中也有杂质存在）。特别发现了本发明的电极的电催化涂层当制备涂层的伽伐尼浴中有添加物时实际上不被铁和汞所毒化（如权利要求5的特征部分所述，如果浓度范围为0.005～2，000ppm）。在下面的描述和例子中，用上述方法得到的涂层被标记为加固涂层，有助于抵抗涂层毒化的元素属于周期表中的ⅠB、ⅡB、ⅢA、ⅣA、ⅤA、ⅤB、ⅥA、ⅥB、Ⅷ族，称之为掺杂元素。
在支承体上沉积电催化涂层是按电镀技术中所熟知的常规方法进行的。例如，伽伐尼镍电镀浴可以是瓦特浴（Watt    bath）（氯化镍和硫酸镍，在硼酸或其他缓冲剂存在下）、稳定的或不稳定的氨基磺酸盐浴（sulpha-mate    bath）、韦斯伯格浴（Weisberg    bath）、氯化镍浴、氯化镍和醋酸镍浴等等：按照上述专利中的方法，是将适量铂族金属的可溶性盐溶于溶液，或者，作为选择，将适量的事先选择的电催化材料的颗粒加入，搅拌成悬浮液，并且，如果需要，可加入表面活性剂。在典型例子中，金属支承体是镍片或镍编织物做的，铂族金属的可溶盐是三氯化钌，悬浮的电催化物质颗粒是二氧化钌。
很明显，基于铜、银、铜银合金或其他金属或其合金的涂层（代替用镍），就需使用基于这些金属的伽伐尼镀浴或无电浴。
电催化涂层的厚度、涂层中作为均相的铂族金属的百分数，或者（作为选择）分散于涂层中的电催化颗粒的量和大小，在本质上都不是关键的，而是以实际和经济为基础：通常涂层厚度介于1至50微米（micron），作为均匀相的铂族金属的重量百分数为0.1至50%;分散颗粒的等效直径为0.01至150微米，其量介于1至50%（重量百分比）之间。
就上述方法和专利文献（比利时专利No.848，458，美国专利No.4，465，580）所述方法而言，本发明的新颖之处在于在上述伽伐尼沉积浴中添加适量的至少一种上文提到的掺杂元素的化合物。由于这种添加，涂层中就会有不同量的掺杂元素：沉积浴中掺杂元素的化合物的浓度相同时掺杂元素的浓度视沉积的条件，特别是电流密度、温度，浴的pH值而有较大的变化（如下例子中所述）。然而，将这样制成的电极作为阴极工作，其抗毒化作用似乎完全与涂层中的掺杂元素的浓度变化无关。
关于加入涂层中的掺杂元素对于毒化的阻止作用以及其本身的化学性质（所用化合物的细分散体中元素状态和氧化态之间的关系不是0），还难完全讲得清楚。可以这样假设：次贵金属掺杂元素（less    noble    doping    elements）（如Zn、Cd、V）是以水合氧化物或碱性盐存在的，能使涂层表面与汞滴和微晶铁之间的可湿性和粘结特性发生明显的改变，汞滴和微晶铁是在污染的碱溶液中将电极作为阴极而工作时形成的。事实上由于铂族金属或电催化颗粒在逐渐形成涂层的过程中的存在，从一开始，阴极沉积电势就不足以使掺杂元素放电形成金属状态。
因此，按本发明所制的涂层在本质上与先有技术中常用的涂层不同，例如，在先有技术中，锌作为金属大量存在并经沥滤以提供高孔隙率和增高活性的表面。
至于贵金属掺杂元素，特别是Pt和Pd，只要添加极小量（加0.01ppm于伽伐尼镀浴和更小量于涂层）就足以十分有效地阻止铁和汞的毒化作用。
这些有控制的添加构成了本发明的新颖性。事实上，铂族金属含量高的电催化涂层，或只含上述元素（极限情况）的涂层，当在污染的碱溶液中当电极时，是容易失去活性的〔关于Ru和Pt，请参考D.E.Grove文章，铂金属评论（Platinum    Metals    Rev.）1985，29（3），98-106]。
为进一步阐述本发明的内容，下一部分报告了一些有意义的例子，但并不局限于此。例如，在下面的例子中，涂层是用伽伐尼电镀沉积形成的，但是对熟悉本技术的人来说，非电沉积也可包括在内。
实例1
由直径为0.1mm的镍丝制成的各种25网目的样品，经蒸气脱脂，并在15%的硝酸中浸泡约60秒钟。用这种镍样品为基板在电镀浴中进行电沉积，电镀浴的组成如下：
-硫酸镍    210克/升
-氯化镍    60克/升
-硼酸    30克/升
-氧化钌    Ru    4克/升（金属）
-添加物（类型和浓度见表1）
浴温约为50℃，电流密度为100安/米2，浴中氧化钌颗粒平均直径约为2微米，最小者0.5微米，最大者5微米。
用机械搅拌将粉末悬浮于溶液中，电沉积进行时间约为2小时。
沉积的涂层厚约为25微米，涂料体积的10%是由氧化钌均匀分布在镍基体上构成的，在涂层表面发现仅仅部分被镍覆盖的氧化物颗粒（其表面呈树枝状）。
所得到的阴极以时间函数测定其电势，其条件是：90℃，3千安/米2，50ppm铁和10ppm汞污染的33%的NaOH碱溶液。然后将测定值与在无添加物的浴中制得的阴极的特性作比较。
表1的结果概括了催化老化的实际效果，特别是汞对未加固的阴极的催化老化：由加入上述掺杂元素的化合物的镍电镀浴制得的阴极，其催化老化现象已基本消除或显著减少。
在此例和后面的例子中，以ppm表示的电镀浴中各添加物的浓度、33%    NaOH溶液中铁和汞的浓度，均为元素浓度，因而10ppm的TlCl（氯化亚铊）即指电镀浴中含117ppm（约为每升117毫克）的盐，相当于100ppm（约为每升100毫克）的金属。
表1
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐或氧化物    ppm    开始    1天    10天    元素    ppm
Ni+RuO2- - - 1050 1050 1050 - -
Ni+RuO2- - - 1040 1060 1070 Fe 50
Ni+RuO2- - - 1050 1150 1750 Hg 10
Ni+RuO2Tl TlCl 100 1050 1050 1050 Fe 50
Ni+RuO2Pb Pb（NO3）2100 1050 1050 1050 Fe 50
Ni+RuO2Sn SnCl2100 1050 1050 1050 Fe 50
Ni+RuO2As As2O3100 1050 1050 1050 Fe 50
Ni+RuO2Sb Sb2O3100 1050 1050 1050 Fe 50
Ni+RuO2Bi Bi2O3100 1050 1050 1050 Fe 50
Ni+RuO2Tl TlCl 100 1050 1050 1100 Hg 10
Ni+RuO2Pb Pb（NO3）2100 1040 1040 1080 Hg 10
Ni+RuO2Sn SnCl2100 1040 1040 1090 Hg 10
Ni+RuO2As As2O3100 1040 1050 1090 Hg 10
Ni+RuO2Sb Sb2O3100 1040 1060 1120 Hg 10
Ni+RuO2Bi Bi2O3100 1040 1070 1130 Hg 10
涂层的试验只做了少数样品（破坏性试验-如完全溶解后进行比色测定或原子吸收测定，非破坏性试验-如X射线衍射法）。
在加铅后产生的加固效应的情况下，发现涂层含100至1000ppm的元素铅（依搅拌强度而有不同，其他条件不变）。
同样，如果以锡加固，发现涂层中含有少量的元素锡，其范围为100至300ppm.沉积温度愈高（如由50℃改为70℃），则检出量愈高。
实例2
直径为0.1毫米的镍丝编织样品，经适当的电解浸渍，用镍电镀瓦特浴电催化涂层进行活化（如实例1所述），浴中含氧化钌悬浮颗粒和Pt、Pd、Cu、Ag、Au的可溶性盐（如表2中指明）。
将用此法制得的样品在90℃、电流密度为3KA/米2的33%NaOH溶液（未经毒化或用10ppm的汞分别进行毒化）中作为阴极进行试验，所得结果列于表2。
表2
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐    ppm    开始    1天    10天    元素    ppm
Ni+RuO    -    -    -    1050    1050    1050    -    -
Ni+RuO    -    -    -    1050    1150    1750    Hg    10
Ni+RuO Pt PtCl40.01 1040 1040 1090 Hg 10
Ni+RuO Pd PdCl20.01 1050 1050 1100 Hg 10
Ni+RuO Cu CuCl20.01 1050 1050 1150 Hg 10
Ni+RuO Ag AgCl（NH3）20.01 1040 1040 1120 Hg 10
Ni+RuO Au AuCl30.01 1040 1040 1180 Hg 10
实例3
按实例2的方法制备阴极，只是在镍电镀浴中加入汞盐和铁盐以代替Pt、Pd、Cu、Ag、和Au盐。
将所得的阴极进行试验，试验操作条件同实例2，增长时间，用分别以铁（50ppm）和汞（10ppm）毒化的33%NaOH溶液。所得结果列于表3。
表3
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐    ppm    开始    1天    10天    元素    ppm
Ni+RuO2- - - 1050 1050 1050 - -
Ni+RuO2- - - 1040 1060 1070 Fe 50
Ni+RuO2- - - 1050 1150 1750 Hg 10
Ni+RuO2Fe Fe（NO3）2
+
（NH4）2SO41 1040 1060 1070 Fe 50
重量比
1∶10
Ni+RuO2Fe 1∶10 10 1040 1060 1060 Fe 50
Ni+RuO2Fe 1∶10 100 1040 1060 1070 Fe 50
Ni+RuO2Hg Hg（NO3）21 1050 1150 1450 Hg 10
Ni+RuO2Hg Hg（NO3）210 1040 1150 1450 Hg 10
Ni+RuO2Hg Hg（NO3）2100 1040 1250 1450 Hg 10
实例4
用直径0.1毫米的镍丝制成镍编织样品，经适当的电解浸渍后，用含氧化钌悬浮颗粒和表4中添加物的镍电镀瓦特浴制得的电催化涂层进行活化（如实例1所述）。
然后将样品作为阴极在未毒化或被铁（50ppm）和汞（10ppm）毒化的33%NaOH溶液中于80℃、3KA/米电流密度下进行试验。阴极电势-电解时间列于表4。
表4
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层    开始    30    60
元素    盐    ppm    分钟    分钟    元素    ppm
Ni+RuO2- - - 1000 1000 1000 - -
Ni+RuO2- - - 1000 1080 1116 Fe 50
Ni+RuO2- - - 1000 1800 - Hg 10
Ni+RuO2Cd CdCl2100 1080 1090 1080 - -
Ni+RuO2V VOCl21 1010 1010 1010 - -
Ni+RuO2Mo Na2Mo O410 1020 1020 1020 - -
Ni+RuO2Cd CdCl21 1075 1420 - Hg 10
Ni+RuO2Cd CdCl210 1050 1370 1410 Hg 10
Ni+RuO2Cd CdCl2100 1080 1180 1190 Hg 10
Ni+RuO2V VOCl21 1010 1080 1110 Fe 50
Ni+RuO2V VOCl21 1000 1050 1105 Hg 10
Ni+RuO2V VOCl21 1010 1000 1200 Hg 10
Ni+RuO2Mo Na2MoO410 1020 1002 1006 Fe 50
Ni+RuO2Mo Na2MoO41 1020 1100 1250 Hg 10
Ni+RuO2Mo Na2MoO45 1000 1080 1230 Hg 10
Ni+RuO2Mo Na2MoO410 1010 1020 1090 Hg 10
Ni+RuO2Mo MoO31 1080 1260 1290 Hg 10
Ni+RuO2Mo MoO35 1090 1230 1240 Hg 10
Ni+RuO2Mo MoO310 1045 1220 1260 Hg 10
实例5
按实例1所述方法将镍编织物样品进行活化。唯一的区别是加入不同量的硫代硫酸钠作为掺杂添加物。
有关数据（添加物浓度ppm，阴极电势）列于表5。
表5
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层    开始    30    60
元素    盐    ppm    分钟    分钟    元素    ppm
Ni+RuO2- - - 940 980 980 - -
Ni+RuO2- - - 1000 1090 1150 Fe 50
Ni+RuO2- - - 980 2000 - Hg 10
Ni+RuO2S Na2S2O310 990 1000 1040 Fe 50
Ni+RuO2S Na2S2O3100 990 1000 1020 Fe 50
Ni+RuO2S Na2S2O3500 960 960 960 Fe 50
Ni+RuO2S Na2S2O310 970 1600 - Hg 10
Ni+RuO2S Na2S2O325 970 1550 - Hg 10
Ni+RuO2S Na2S2O350 970 1500 - Hg 10
Ni+RuO2S Na2S2O3100 950 1100 1580 Hg 10
Ni+RuO2S Na2S2O3500 940 1050 1200 Hg 10
Ni+RuO2S Na2S2O31000 980 1030 1180 Hg 10
Ni+RuO2S Na2S2O3500 940 940 940 - -
实例6
直径为0.1毫米的镍丝制成的镍编织物样品，经适当电解浸渍，在含有氧化钌悬浮颗粒和溶解两种以上掺杂元素化合物的镍电解瓦特浴中按本发明方法进行活化。掺杂元素及化合物列于表6。表6也报告了90℃时电流密度为3KA/米2的33%NaOH溶液[分别为铁（50ppm）和汞（10ppm）毒化]的有关电解的数值。
表6
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐或氧化物    ppm    开始    1天    10天    元素    ppm
Ni+RuO2- - - 1050 1050 1050 - -
Ni+RuO2- - - 1040 1060 1070 Fe 50
Ni+RuO2- - - 1050 1150 1750 Hg 10
Ni+RuO2Sb+S Sb2O3100 1040 1050 1040 Fe 50
Na2S 100
Ni+RuO2Cd+Mo Cd（NO3）2100 1040 1040 1040 Fe 50
MoO3100
Ni+RuO2Sb+S Sb2O3100 1040 1050 1100 Hg 10
Na2S 100
Ni+RuO2Bi+Se Bi（NO3）2100 1040 1040 1100 Hg 10
SeO2100
实例7
直径为0.1毫米的镍丝编织样品，经适当电解浸渍后，用镍-钌电解催化涂层活化，用含有表7中所列三氯化钌（RuCl3）（比例为每毫升1克钌）和掺杂元素的镍电镀瓦特浴，沉积条件如实例1。
将所得样品作为阴极于90℃、3KA/米2电流密度在33% NaOH溶液[分别被铁（50ppm）和汞（10ppm）毒化]中进行试验。
表7
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐或氧化物    ppm    开始    1天    10天    元素ppm
Ni-Ru    -    -    -    1090    1090    1090    -    -
Ni-Ru    -    -    -    1090    1180    1180    Fe    50
Ni-Ru    -    -    -    1100    1650    2100    Hg    10
Ni-Ru    Tl    TlCl    100    1090    1110    1150    Fe    50
Ni-Ru Pb Pb（NO3）2100 1100 1100 1110 Fe 50
Ni-Ru Sn SnCl2100 1100 1110 1130 Fe 50
Ni-Ru As As2O3100 1100 1110 1120 Fe 50
Ni-Ru Sb Sb2O3100 1100 1110 1150 Fe 50
Ni-Ru Bi Bi2O3100 1090 1090 1120 Fe 50
Ni-Ru    Tl    TlCl    100    1090    1380    1750    Hg    10
Ni-Ru Pb Pb（NO3）2100 1090 1490 1750 Hg 10
Ni-Ru Sn SnCl2100 1090 1510 1750 Hg 10
Ni-Ru As As2O3100 1100 1420 1820 Hg 10
Ni-Ru Sb Sb2O3100 1200 1600 1980 Hg 10
Ni-Ru Bi Bi2O3100 1090 1590 1870 Hg 10
实例8
按实例7的方法制得镍-钌涂层，只是掺杂添加物的种类不同，掺杂添加物按实例4所使用的种类。
所得的结果与实例4相同。
实例9
按与实例7相同的方法将镍编织物进行活化，但（与实例8不同）将Pt、Pd、Cu、Au的盐加入含RuCl3（如表7所示）的电镀浴，测定90℃时、电流密度为3KA/米2的33%NaOH溶液（10ppm的汞毒化）的各阴极电势。
表8
阴极电势-操作时间
33%
浴中添加物    阴极电势    NaOH
mV（NHE）    中的杂质
涂层
元素    盐    ppm    开始    1天    10天    元素    ppm
Ni-Ru    -    -    -    1100    1090    1100    -    -
Ni-Ru    -    -    -    1100    1650    2100    Hg    10
Ni-Ru Pt PtCl40.01 1100 1150 1160 Hg 10
Ni-Ru Pd PdCl20.01 1100 1150 1170 Hg 10
Ni-Ru Cu CuCl20.01 1100 1140 1150 Hg 10
Ni-Ru Ag AgCl（NH3）20.01 1100 1060 1180 Hg 10
Ni-Ru Au Au Cl30.01 1100 1060 1060 Hg 10

Claims (27)

1、一种用伽伐尼法制备电化学加工的电极的方法，该类型的电极包括：(a)一个导电支承体和(b)有电催化物质颗粒分散于其中的金属或金属合金的电催化涂层，所说的方法包括在伽伐尼电镀浴中将所说的电催化涂层电镀沉积在所说的导电支承体上，电镀浴中含有所说电催化物质的悬浮颗粒，该方法的特征是所说的伽伐尼电镀浴中另外还含有0.005至2000ppm的至少一种其它元素的化合物添加物，这些元素属于周期表中的ⅠB、ⅡB、ⅢA、ⅣA、ⅤA、ⅤB、ⅥA、ⅥB、Ⅷ族。
2、根据权利要求1所述的方法，其特征在于ⅠB族元素的添加化合物是银化合物。
3、根据权利要求1所述的方法，其特征在于ⅡB族元素的添加化合物是镉或汞的化合物。
4、根据权利要求1所述的方法，其特征在于ⅢA族元素的添加化合物是铊的化合物。
5、根据权利要求1所述的方法，其特征在于ⅣA族元素的添加化合物是铅的化合物。
6、根据权利要求1所述的方法，其特征在于ⅤA族元素的添加化合物是砷的化合物。
7、根据权利要求1所述的方法，其特征在于ⅤB族元素的添加化合物是钒化合物。
8、根据权利要求1所述的方法，其特征在于ⅥA族元素的添加化合物是硫的化合物。
9、根据权利要求1所述的方法，其特征在于ⅥB族元素的添加化合物是钼的化合物。
10、根据权利要求1所述的方法，其特征在于Ⅷ族元素的添加化合物是铂或钯的化合物。
11、根据权利要求1至10所述的方法，其特征在于伽伐尼电镀浴是镍或铜或银电镀浴。
12、根据上述任何一项权利要求所述的方法，其特征在于悬浮的颗粒电催化物质是属于下面一组物质中的至少一种元素组成：钛、锆、铌、铪、钽、铂族金属;镍、钴、锡、锰金属或其合金或其氧化物、混合氧化物、硼化物、氮化物、碳化物、硫化物。
13、根据权利要求12所述的方法，其特征在于悬浮的颗粒电催化物质是氧化钌。
14、一种用伽伐尼法制备电化学加工电极的方法，该类型的电极包括：（a）导电支承体和（b）含均相铂族金属的金属或金属合金的电催化涂层，所说的方法包括在电镀浴中将所说的电催化涂层电镀沉积在所说的导电支承体上，电镀浴中有铂族金属的可溶性盐，此方法的特征在于在所说的伽伐尼电镀浴中另外还含有0.005至2，000ppm的至少一种其它元素的化合物添加物，这些元素属于周期表中的ⅠB、ⅡB、ⅢA、ⅣA、ⅤA、ⅤB、ⅥA、ⅥB、Ⅷ族。
15、根据权利要求14所述的方法，其特征在于ⅠB族元素的添加化合物是金的化合物。
16、根据权利要求14所述的方法，其特征在于ⅡB族元素的添加化合物是镉的化合物。
17、根据权利要求14所述的方法，其特征在于ⅢA族元素的添加化合物是铊的化合物。
18、根据权利要求14所述的方法，其特征在于ⅣA族元素的添加化合物是铅或锡的化合物。
19、根据权利要求14所述的方法，其特征在于ⅤA族元素的添加化合物是砷的化合物。
20、根据权利要求14所述的方法，其特征在于ⅤB族元素的添加化合物是钒化合物。
21、根据权利要求14所述的方法，其特征在于ⅥB族元素的添加化合物是钼的化合物。
22、根据权利要求14所述的方法，其特征在于Ⅷ族元素的添加化合物是铂或钯的化合物。
23、根据权利要求14至22所述的方法，其特征在于伽伐尼电镀浴是镍、铜或银电镀浴。
24、根据权利要求14至22任一项所述的方法，其特征在于铂族金属的可性盐是三氯化钌。
25、根据权利要求23所述的方法，其特征在于铂族金属的可性盐是三氯化钌。
26、按本发明所述权利要求中任一项的方法所制得的用于电化学加工的电极。
27、根据权利要求26所述的电极作为电解槽的阴极使用，其特征在于透气的和透液的阳极是由可渗透的隔膜或离子交换膜分隔的，这种膜实质上是不透电极液流的，所说的电解槽有碱金属氢氧化物的溶液（即使被铁和/或汞所污染）作为电解液。
CN85108839A 1984-12-14 1985-12-13 含添加剂的电催化阴极及其在氯—碱电解中的应用 Expired CN1008748B (zh)