CN1414593A - 电介质糊与等离子体显示器的制造方法 - Google Patents
电介质糊与等离子体显示器的制造方法 Download PDFInfo
- Publication number
- CN1414593A CN1414593A CN02147119A CN02147119A CN1414593A CN 1414593 A CN1414593 A CN 1414593A CN 02147119 A CN02147119 A CN 02147119A CN 02147119 A CN02147119 A CN 02147119A CN 1414593 A CN1414593 A CN 1414593A
- Authority
- CN
- China
- Prior art keywords
- dielectric paste
- coating film
- paste
- forming
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
添加量(重量份) | ||||||||
粘结树脂 | 交联剂 | 聚合引发剂 | 氨基甲酸酯化合物 | |||||
电极糊A | A | 12 | A | 6 | A | 3.0 | - | - |
电极糊B | B | 5 | - | - | - | - | B | 5.0 |
添加量(重量份) | ||||||||
粘结树脂 | 交联剂 | 聚合引发剂 | 氨基甲酸酯化合物 | |||||
隔板糊A | A | 7 | A | 3 | A | 1.5 | A | 1.5 |
隔板糊B | B | 4 | - | - | - | - | B | 6.0 |
添加量(重量份) | 电极图形固化条件 | 电介质糊涂布膜固化条件 | 评价 | ||||||||||||||||
粘结树脂 | 交联剂 | 热聚合引发剂 | 氨基甲酸酯化合物 | 低熔点玻璃 | 填料A | 填料B | 温度(℃) | 时间(分) | 温度(℃) | 时间(分) | 电介质的龟裂(个) | 气泡(个/100μm2) | 致密性 | ||||||
实施例1 | B | 8 | A | 92 | B | 12.3 | A | 1.2 | A | 246 | 106 | 2 | 200 | 15 | 150 | 15 | 0 | 0 | 良好 |
实施例2 | C | 6 | B | 94 | B | 3.3 | B | 0.7 | B | 188 | 71 | 1 | 140 | 3 | 140 | 3 | 0 | 0 | 良好 |
实施例3 | A | 50 | A | 50 | B | 10.0 | A | 4.4 | A | 200 | 136 | 2 | 250 | 10 | 250 | 10 | 0 | 0 | 良好 |
实施例4 | B | 5 | B | 95 | B | 23.8 | B | 14.3 | B | 190 | 72 | 2 | 140 | 3 | 150 | 15 | 1 | 0 | 良好 |
实施例5 | B | 6 | A | 94 | B | 12.5 | A | 3.1 | A | 281 | 94 | 3 | 150 | 15 | 200 | 10 | 0 | 0 | 良好 |
实施例6 | C | 8 | B | 92 | B | 12.3 | B | 6.2 | B | 154 | 184 | 2 | 250 | 20 | 150 | 30 | 0 | 0 | 稍差 |
实施例7 | B | 6 | A | 94 | B | 2.4 | A | 2.4 | A | 188 | 94 | 2 | 200 | 15 | 150 | 15 | 3 | 0 | 良好 |
实施例8 | C | 8 | B | 92 | B | 30.8 | B | 3.1 | B | 246 | 123 | 2 | 200 | 15 | 150 | 15 | 0 | 5 | 良好 |
实施例9 | B | 8 | A | 92 | C | 12.3 | A | 3.1 | A | 246 | 93 | 2 | 200 | 15 | 150 | 15 | 1 | 0 | 良好 |
实施例10 | B | 8 | A | 92 | B | 12.3 | A | 1.2 | A | 246 | 93 | 2 | 200 | 15 | 150 | 15 | 0 | 0 | 良好 |
实施例11 | B | 8 | B | 92 | D | 12.3 | B | 3.1 | B | 246 | 93 | 2 | 200 | 15 | 150 | 15 | 7 | 0 | 良好 |
实施例12 | B | 8 | C | 92 | A | 12.3 | A | 3.1 | A | 246 | 93 | 2 | 200 | 15 | 150 | 15 | 6 | 0 | 良好 |
实施例13 | B | 8 | A | 92 | B | 12.3 | A | 1.2 | A | 246 | 93 | 2 | 120 | 15 | 150 | 15 | 5 | 0 | 良好 |
实施例14 | B | 8 | A | 92 | B | 12.3 | A | 1.2 | A | 246 | 93 | 2 | 200 | 15 | 120 | 15 | 9 | 0 | 良好 |
实施例15 | B | 8 | A | 92 | B | 12.3 | A | 12.3 | A | 246 | 93 | 2 | 200 | 15 | 150 | 15 | 0 | 0 | 良好 |
实施例16 | B | 8 | A | 92 | B | 12.3 | A | 12.3 | A | 246 | 93 | 2 | - | 0 | 150 | 15 | 11 | 0 | 良好 |
比较例1 | B | 8 | A | 92 | - | 0.0 | A | 12.3 | A | 246 | 93 | 2 | - | 0 | - | 0 | >100 | 0 | 良好 |
比较例2 | B | 8 | A | 92 | B | 12.3 | A | 12.3 | A | 246 | 93 | 2 | 200 | 15 | - | 0 | ~80 | 0 | 良好 |
比较例3 | B | 8 | A | 92 | B | 12.3 | A | 12.3 | A | 246 | 93 | 2 | - | 0 | - | 0 | >100 | 0 | 良好 |
Claims (14)