CN1404513A - 预油漆和从预油漆制备油漆的方法 - Google Patents
预油漆和从预油漆制备油漆的方法 Download PDFInfo
- Publication number
- CN1404513A CN1404513A CN01805209A CN01805209A CN1404513A CN 1404513 A CN1404513 A CN 1404513A CN 01805209 A CN01805209 A CN 01805209A CN 01805209 A CN01805209 A CN 01805209A CN 1404513 A CN1404513 A CN 1404513A
- Authority
- CN
- China
- Prior art keywords
- paint
- lacquer
- cover
- pigment
- extender
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
描述了提供包含胶乳聚合物漆基的油漆系的方法。可以使用预油漆的套漆配制系列油漆,它的至少一种包含胶乳聚合物漆基。油漆可以应用为建筑涂料、工业涂料、形象艺术涂料、弹性体涂料、和非胶接性,凝集体面漆涂料,适于直接应用在墙壁上或在外部保温涂饰系统中作为顶涂层。
Description
相关申请的交叉参考
本申请要求如下文献的优先权:2000年2月18日提交的U.S.临时申请Ser.Nos.60/183,655、2000年2月18日提交的60/183,656和2000年11月10日提交的60/247,639。
发明背景
发明领域
本发明涉及使用预油漆的套漆(sets of prepaints)配制油漆系的方法,来自预油漆组合物的套漆的有用油漆,包括作为建筑涂料、工业涂料、形象艺术涂料、弹性体涂料和非胶接性凝集体面漆涂料。
相关技术的描述
数十年来,专业画家/承包人和自己动手的消费者已经能够购买到在销售点而不是在制造设备处染色的油漆。产品分化的此延迟允许购买者从许多种选择,而不是一旦由油漆制造商生产时的有限数目规定所需的油漆颜色。
尽管不在商业上实施,理论上也已知在油漆工业中延迟油漆组分自身的产品分化,只要在油漆制造工艺中可能。参见,例如,在FaergLack Scand.43(2),5-6页(1997)中的Carola Grundfelt-Forsius的文章,该文章描述了使用中间体或组分,即几种没漆原材料成分的混合物,将它们与调色漆混合在一起以得到不同类型的油漆。Grundfelt-Forsius提供了采用用于溶液聚合物体系的聚氨酯漆基的这样体系的例子。
不管这些益处,油漆制造商仅能够成功地对基于溶液聚合物的油漆体系采用产品分化中的延迟。油漆制造商还没有在延迟胶乳聚合物基油漆体系中油漆组分的产品分化方面取得成功。由于大多数目前使用的油漆基于胶乳聚合物,需要在胶乳聚合物基油漆体系中延迟产品分化的实际方法。
由于胶乳不稳定性,当使用胶乳乳液聚合物而不是溶液聚合物时,相当更难以配制稳定的油漆。乳液聚合物对于通常在油漆配方中发现的溶剂和表面活性剂,如表面活性剂,分散剂,流变改进剂,和共溶剂敏感。溶液聚合物按照定义在其中提供它们的溶剂中是稳定的,和没有引起聚合物分子附聚或变成不稳定的热力学驱动力。相反地,胶乳聚合物包含为粒子的聚合物材料,它们不溶于水。这些粒子要求相当的表面改性以使得当在含水介质中提供时它们稳定。如果表面改性不足够,胶乳粒子彼此连接,形成然后分离出胶乳油漆的凝结块。由于在配方中的表面活性材料破坏了表面力的精致平衡,该表面力稳定在水介质中的胶乳粒子,采用胶乳体系配制油漆是非常困难的。
在胶乳聚合物体系(也称为“乳液”)和溶液聚合物体系之间的差异进一步解释在如下文献中:Temple C.Patton的题目为油漆流动和颜料分散的书(纽约:John Wiley and Sons,Inc.1979,192-193页)。在此作者描述了用于两种体系的干燥工艺。主要差异在于对于每种聚合物达到不可逆状态要求的时间。胶乳聚合物比溶液聚合物更快达到此状态和因此使基于胶乳聚合物的油漆比基于溶液聚合物的油漆更难以稳定。在讨论“溶剂类型涂料”中,(它包含溶液聚合物)作者写到“...在干燥时液体载体在颜料粒子周围流动而不是消泡。由于挥发性溶剂的损失,当膜收缩时此流动有助于致密化工艺。尽管当溶剂蒸发时载体变得更为粘性的,流动持续贯穿于大多数干燥工艺。”如作者指出的那样,当溶剂蒸发时,溶液聚合物能够流过大多数干燥循环。对于聚合物乳液不是这样。相同的作者注释:“...存在胶乳悬浮液的初步流动。这发生在当由于初始水损失,胶乳粒子被强制进行紧密接触时间之前。然而,在此相对短但非常重要的初始流动之后,用以达到高临界颜料体积浓度(CPVC)的颜料致密化主要通过塑性消泡和胶乳粒子的聚结达到。”聚结是胶乳粒子之间的不可逆接触。这样的不可逆接触可发生在基于胶乳聚合物的液体油漆中,蛤不发生在基于溶液聚合物的液体油漆中。因此,基于胶乳聚合物的油漆更难以配制。
非常需要开发预油漆的套漆和基于胶乳聚合物使用预油漆的套漆配制油漆的方法。
油漆配制包括如下工艺:以精确比例选择和混合合适的油漆成分,以提供具有特定加工和处理性能的油漆,以及具有所需性能的最终干燥油漆膜。胶乳油漆配方的主要成分是漆基,不透明颜料,选加的颜料增量剂,和水。通常的非必要添加剂包括消泡剂,凝结剂,增塑剂,增稠剂,非增稠流变改进剂,不透明剂,干燥剂,防结皮剂,表面活性剂,杀霉菌剂,杀虫剂和分散剂。在将胶乳油漆配制和涂敷到表面之后,油漆通过水的蒸发而干燥,施加热量或不施加热量,和漆基形成其中包含如下物质的膜:颜料和颜料增量剂粒子,若有的话。
配制油漆是复杂的-它不仅是以不同比例混合一些油漆成分的事情。而是,它涉及依赖于所需油漆的类型,以不同比例不同油漆成分的选择和混合。这要求油漆制造者贮存许多不同的油漆成分和在制造期间根据要制备的具体油漆类型,改变油漆成分。
此外,它要求在供应链中的那些人,特别是油漆零售商,在仓库中和在贮存架上保持较大的油漆存货,以提供系列油漆,如各种光泽水平,调色浆,外用油漆,内部使用油漆,和具有可变质量的油漆。需要制备油漆,在相对大规模工业装置上或在相对较小规模,销售点或使用点位置,使用有限数目的油漆成分以制备所有这些不同的油漆配方,因此,最小化需要制备系列油漆的油漆成分的数目和类型。
发明概述
在此使用的“油漆系”包括至少两种不同的油漆,它们提供在至少一个可观察性能,如光泽、室外耐用性或颜色深度中本质上彼此不同性能的干燥膜。例如,油漆系可包括它的干燥膜具有不同光泽水平的三种油漆,它的干燥膜具有合适内部或外部性能的两种油漆,或它的干燥膜提供不同质量或性能水平的四种油漆,如可以证明的那些,例如通过不同水平的耐洗擦性。
更特定地,油漆系可包括四种不同的油漆,它的干燥膜具有不同的光泽水平,典型地销售为光泽、半光泽、蛋壳色、缎子、或低光泽、和无光的。光泽由油漆中如下物质的体积和类型确定:漆基,颜料,和增量剂,如有的话。
除各种光泽水平以外,通常将油漆配制为中性或重色调(accent)(没有或非常低水平不透明颜料),未染色的(白色)或使用不同的调色浆,包括柔和或淡色调物,中等或中色调物,和深色调物,染色到很多种颜色。此能力要求油漆系具有多达五种油漆。同样,将油漆配制用于外部或内部用途。和将油漆配制以提供某些水平的执行性能,如可以销售为良好/标准,更好和最好/特级。
油漆制造商和零售商典型地提供包括至少两种油漆系的系列油漆。“包括至少两种油漆系的系列油漆”在此表示将定义第一油漆系可观察性能的离散选择水平与定义第二油漆系可观察性能的离散选择水平结合,如以定义系列油漆中的油漆。
制备包括四种油漆系的系列油漆(a range of paints)可能要求制备包括四种光泽水平,四种调色浆,内部和外部用途,和三种质量水平的油漆。对于所有组合,可能需要96种不同的油漆配方(4x4x2x3)。然而,同样包括这样的系列油漆,其中选择某些确定的油漆,某些比例,包括至多10-60%油漆总数目可以忽略,例如,由于商业原因或由于它们不如在此定义的稳定。进一步设想的是这样系列油漆,其中干燥漆膜的可观察性能基本但不完全满足标准定义例如不背离本发明系列油漆的意义,在标准,更好,和最优系中的干燥室外中色调光泽油漆的光泽可以有一些不同。
在此使用的“油漆”是以它的最宽意义使用的术语和包括任何涂料,这些涂料可以涂敷到表面上用于装饰,保护或两种目的。具体包括的是用于如下的那些体系:建筑涂料,工业涂料,弹性体涂料和用作壁上和外部保温和涂饰体系(以下称为“EIFS”)中顶涂层的非胶接性,凝集体面漆涂料。
如果通过混合预油漆形成的油漆并不显示胶体不稳定性的迹象如絮凝,在本文中使用的预油漆是“相互相容的”。优选,当油漆通过325筛孔时,从预油漆形成的油漆显示每升油漆小于5g的残余物如凝胶和粗粒子。更优选,当油漆通过325筛孔时,从预油漆形成的油漆显示每升油漆小于1g的残余物如凝胶和粗粒子。如果包括添加剂以增强具体的油漆性能,和着色剂是完全相容的,即它们可以在任何比例下共混而不诱导胶体不稳定性,则它们可以采用落入需要在最终油漆中达到所需性能情况的配制空间的任何结合而共混。然而,对于预油漆如下情况是足够的:包括选加的添加剂以增强具体的油漆性能,和着色剂是相容的,即它们可以在所需的比例下共混而不诱导胶体不稳定性,以在这类油漆中达到所需的性能情况。
为了将制备一系列油漆所需的油漆成分的数目降至最小,人们需要考虑这一系列油漆所需关键/特性的端点情况和在端点数值和中间点能以不同组合共混以提供所需关键特性的预配油漆。
上述目的通过采用如下物质达到:一套足以配制至少一种油漆系的不同但相互相容流体预油漆的套漆。套漆包括(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;
优选,预油漆的数目为3-15。
还提供一种形成至少一种油漆系的方法,包括如下步骤:
(a)提供足以配制至少一种油漆系的不同但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种不透明预油漆,包括至少一种不透明颜料;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系(paint line)。
优选,预油漆的总数目为3-15。
该方法可进一步包括如下步骤:在将它们分配入容器之前,同时,或之后,或在将它们分配入涂敷器之前或同时,混合预油漆。
进一步提供一种形成系列油漆的方法。该系列油漆包括至少两种油漆系。该方法包括如下步骤:
(a)提供一种足以配制系列油漆、不同但相互相容流体预油漆的套漆,该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和(iv)至少一种选自预油漆(i),(ii),和(iii)的另外不同的预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
优选,预油漆的总数目为4-15。
所述方法可进一步包括如下步骤:在将它们分配入容器之前,同时,或之后,或在将它们分配入涂敷器之前或同时,混合预油漆。所述方法可进一步包括如下步骤:在将它们分配入容器之前,同时,或之后,或在将它们分配入涂敷器之前或同时,使用增稠剂,水,或其混合物,调节分配预油漆的粘度。所述方法可进一步包括如下步骤:加入增强油漆的施用或最终性能的另外材料,包括凝集体和增稠剂。所述方法可进一步包括向分配预油漆中加入至少一种着色剂的步骤。所述方法可以在制造设备点,销售点,或使用点进行和可以由计算机控制。
在另一个实施方案中,提供一种足以形成至少一种用作弹性体涂料的油漆系的不同但相互相容流体预油漆的套漆。该套漆包括(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆。
进一步提供一种形成至少一种用作弹性体涂料的油漆系的方法。该方法包括如下步骤:
(a)提供不同的但相互相容的流体预油漆的套漆,该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
进一步提供一种形成系列油漆的方法,该系列油漆包括至少两种用作弹性体涂料的油漆系。该方法包括如下步骤:
(a)提供一种足以配制至少两种油漆系的预油漆的套漆,该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆;和(iv)至少一种选自预油漆(i),(ii),(iii),和(iv)的另外不同的流体预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。在一个实施方案中,提供一种足以形成用作非胶接性凝集体面漆、不同但相互相容流体非胶接性预油漆的套漆。该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和(iv)至少一种包括凝集体的预油漆。
还提供一种形成至少一种用作非胶接性凝集体面漆的油漆系的方法。该方法包括如下步骤:
(a)提供不同的但相互相容流体非胶接性预油漆的套漆,该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和(iv)至少一种包括凝集体的预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
进一步提供一种形成系列油漆的方法。系列油漆包括至少两种用作非胶接性,凝集体面漆涂料的油漆系。该方法包括如下步骤:
(a)提供足以配制至少两种油漆系、不同但相互相容,流体非胶接性预油漆的套漆,该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;(ii)至少一种包括至少一种体质颜料的增量剂预油漆;(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;(iv)至少一种包括凝集体的预油漆;和(v)至少一种选自预油漆(i),(ii),(iii),和(iv)的另外不同的流体预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
在另一个实施方案中,提供一种足以形成至少一种油漆系的不同但相互相容流体预油漆的套漆,油漆系用于形成着色和透明涂料。该套漆包括:(i)至少一种包括至少一种不透明颜料的不透明预油漆;和(ii)至少两种漆基预油漆,它的每一种包括至少一种胶乳聚合物漆基。
在另一个实施方案中,提供一种足以形成至少一种用于形象艺术应用的油漆系的预油漆的套漆。该套漆包括:(i)至少一种包括至少一种Tg为约-50℃到约10℃的胶乳聚合物漆基的漆基预油漆;(ii)至少一种包括至少一种Tg为约50℃-约140℃的胶乳聚合物漆基的漆基预油漆;和(iii)可选择地,至少一种包括至少一种Tg为约0℃-约65℃的胶乳聚合物漆基的漆基预油漆。形象艺术预油漆可进一步包括选自如下的另外流体相互相容预油漆:(i)包括至少一种碱溶性树脂的预油漆、(ii)包括至少一种光泽添加剂的预油漆、(iii)包括至少一种蜡的预油漆、和(iv)包括至少一种油漆分散体的多种预油漆。
如果需要油漆系,即如果改变一种关键性能(例如,光泽水平,调色浆,使用类型,或质量类型),则可以从不透明油漆(i),增量剂预油漆(ii),和漆基预油漆(iii)的每一种,制备完全的油漆系。
如果需要包括两种油漆系的系列油漆,即如果改变两种关键性能(例如,选自光泽水平,调色浆,使用类型,或质量类型的两个),则可以根据要改变的关键性能,从不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii)和(iii)和至少一种选自不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii)和(iii)的另外不同预油漆的至少每一种,制备系列油漆。
如果需要包括三种油漆系的系列油漆,即如果改变三种关键性能(例如,选自光泽水平,调色浆,使用类型,或质量类型的三个),则可以根据要改变的关键性能,从不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii)和(iii)和至少两种另外预油漆不同的不透明预油漆,增量剂预油漆,和漆基预油漆,制备系列油漆。
如果需要包括四种油漆系的系列油漆,即如果改变四种关键性能(例如,光泽水平,调色浆,使用类型,或质量类型),则可以根据要改变的关键性能,从不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii)和(iii)和至少三种另外不同的预油漆,不透明预油漆,增量剂预油漆,和漆基预油漆,制备完整的系列油漆。
此技术可以随所需许多另外关键性能的变化而拓展。
“另外的不透明预油漆,增量剂预油漆,和漆基预油漆”分别表示不同于不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii)和(iii),但不同地满足与预油漆相关的限定的预油漆。
如上所讨论的那样,“油漆系”包括两种或多种不同的油漆,它们的干燥膜在至少一种可观察性能上本质地彼此不同。油漆彼此不同和必须满足至少一项如下标准:
(1)最不同颜料的颜料体积浓度(PVC)差异必须至少为2%;或
(2)最不同颜料的体积固体(VS)差异必须至少为2%。
颜料体积浓度(PVC)是配方如何“富含漆基”的量度。在此它使用如下公式计算:
PVC(%)=(颜料体积+体积增量剂)/(颜料体积+体积增量剂+体积漆基)×100
体积固体(VS)是颜料的干燥体积加上增量剂的干燥体积加上漆基的干燥体积。在此它由如下公式计算:
VS(%)=(颜料的干燥体积+增量剂的干燥体积+漆基的干燥体积)/配方总体积×100
如果存在添加剂,在确定总干燥体积中不包括它们的体积。在每个以上实施方案中,选择预油漆使得它们覆盖宽的配方空间,使得所需的最终油漆性能位于由在端点预油漆确定的共混合物空间中。在许多情况下,预油漆自身不是实际的油漆。但,通过将预油漆推进到这些端点,人们可以最大化可用于套漆的共混物空间。当预油漆,添加剂和着色剂所有是完全相容的时,它们可以在所需的比例下共混以达到所需的油漆系和系列油漆,而不诱导胶体不稳定性。可以制备油漆系中的具体油漆,而不采用在油漆的套漆中可得的每种预油漆。例如,深色调油漆并不要求使用不透明颜料预油漆。
此技术相似于用于混合物组分设计的统计试验设计和分析的设计原理;然而,不设计混合物空间以探索其中的响应表面,人闪设计混合物空间的边界以最大化油漆体系的灵活性。成功的关键是具有单个预油漆成分和预油漆在混合物空间中的相互相容性。
油漆性能可以采用许多方式预测。一种方案是使用标准混合物组分试验设计统计工具开发共混物空间的响应表面模型。这些简单的统计模型然后可以通过大网格检索或通过图象分析工具,由线性优化程序使用。另一个方案是简单地使用经验方法以确定哪些共混物需要用于具体的油漆系,然后在油漆制造机器软件中将那些简单的经验配方引入。
技术的延伸是使油漆机器自动预测某些关键性能(如粘度,强制干燥光泽或颜色)和在从预油漆配制油漆期间进行较少的调节。在油漆机器中具有反馈回路可提供颜色,光泽,和粘度目标的更精确匹配。
相容性油漆成分可以在各种预油漆中结合和从预油漆形成的油漆提供使用成分数量的性能特性。
优选在此方法中采用的所有流体预油漆具有相同或相似的粘度以有助于混合。
由于使用更低数量的稳定材料,如可相对于通常配制技术使用的表面活性剂,期望从预油漆制备的油漆的耐水性,包括耐砂眼性能,湿粘合力,和耐擦洗性得到改进。此外使用预油漆制备的油漆系或系列油漆可以更可预知地与加入的着色剂反应,使颜色匹配更容易和促进颜色匹配软件的使用。此外,由于在预油漆中成分的预先平衡,期望可降低在最终油漆配方中粘度的波动。
配制预油漆以最大化油漆制造的灵活性。不购买单个的油漆成分,油漆制造商和甚至在销售点和使用点(油漆仓库,油漆部门,和承包人)的使用者,可以购买油漆的套漆以制备所需的系列油漆。根据所需的配制灵活性,这些油漆的套漆包含预油漆x,y和z的至少一种和可能另外的预油漆。可选择地,将以上预油漆与另外的预油漆混合,另外的预油漆包括至少一种着色剂,如着色颜料或染料。
预油漆的套漆和配制方法在此并不仅限于胶乳油漆的制备。它们也可用于制备任何水性涂料或相应的建筑产品,它包括混合成分,包括,但不限于,形象艺术、密封剂、堵漏剂、乳香、漆基、建筑涂料(私房屋主涂敷的和承包人涂敷的墙壁涂料,弹性体墙壁和屋顶涂料和凝集体面漆层)和工业涂料(如系列为原设备制造、保养、木材、金属、通用工业涂饰的那些,和其它工厂涂敷的涂料以及由自己动手者涂敷的较少部分非建筑类型涂料)。
在工业涂料区域中,在此的方法可应用于用于如下的宽范围涂料:汽车、船舶、飞机、其它陆地运输设备、器具、金属家具、机械&设备、盘管、金属容器、磁线、混凝土屋顶瓦、保温清漆、电子类、管线、包装、套印、断路器、木家具、塑料基材、磁媒体、通用金属、工业维修、汽车整修表面、交通油漆、阻燃剂、气溶胶、耐化学试剂涂料、屋顶、罐、甲板、混凝土、砖石部分抗水剂、指甲油、艺术和嗜好用途。例如,使用合适的预油漆的套漆,在此的方法可应用于生产一定范围的金属涂料,包括无光涂料、有光涂料、直接对金属涂料、底漆、中间涂层和耐溶剂涂料。
发明详述
在不透明预油漆的一个实施方案中,预油漆是流体二氧化钛预油漆,它包括(i)至少一种不透明颜料,(ii)至少一种分散剂,(iii)至少一种增稠剂,和水。分散剂和增稠剂与颜料和与其它选加的油漆成分相容。预油漆的体积固体含量为约30%-约70%,优选约35%-约50%和斯托默粘度为约50-约250KU,优选约60-约150KU。
在另外的实施方案中,不透明预油漆是用于配制包含其它油漆成分的一包装,着色胶乳油漆的流体二氧化钛预油漆。预油漆包括(i)至少一种不透明颜料,(ii)至少一种分散剂,(iii)至少一种增稠剂,(iv)至少一种成膜或非成膜聚合物漆基,和(v)水。分散剂,增稠剂和聚合物与颜料和与其它选加的油漆成分相容。预油漆的体积固体含量为约30%-约70%,优选约35%-约50%,PVC为约35%-约100%,优选约50%-约100%,和斯托默粘度为约50-约250KU,优选约60-约150KU。优选,预油漆对沉淀稳定,这在此表示颜料在25℃下10天之后并不沉淀出。可选择地,聚合物漆基吸附在不透明颜料上。
在增量剂预油漆的一个实施方案中,它是流体颜料增量剂预油漆,它包括(i)至少一种矿物质增量剂,(ii)至少一种增稠剂,(iii)选加的聚合物漆基,和(iv)水。预油漆的体积固体含量为约30%-约70%,优选约35%-约65%,PVC为约35%-约100%,优选约40%-约100%,和斯托默粘度为约50-约250KU,优选约60-约150KU。预油漆成分彼此相容和与需要与其使用的其它预油漆成分相容。
在漆基预油漆的一个实施方案中,它是流体胶乳聚合物漆基预油漆,它包括Tg为约-40℃到约70℃,优选约-10℃到约60℃的水性胶乳聚合物漆基。漆基预油漆的体积固体含量为约25%-约70%,优选约30%-约65%,和在1.25秒倒数下布氏粘度小于约100,000厘泊,优选约100-约50,000厘泊。预油漆成分彼此相容和与需要与其使用的其它预油漆成分相容。
在预油漆的实施方案中,不透明预油漆,增量剂预油漆,和漆基预油漆(i),(ii),和(iii),可选择地包括少量,即小于约20wt%,基于预油漆的总重,的常规油漆添加剂,包括酸、碱、消泡剂、凝结剂、共溶剂、杀霉菌剂、杀虫剂、防冻剂、防闪锈剂等。这些添加剂必须与在此方法中采用的预油漆和油漆中的其它油漆成分相容。
合适的不透明颜料包括白色颜料,它赋予油漆在所有可见光波长内散射能力,而没有高的吸收程度。颜料增量剂是无机固体或不透明聚合物,尽管它们可能对这些性能有次级影响,它们并不赋予油漆原色或遮盖力。用于深色调油漆的调色浆典型地不包含或仅包含低水平的不透明颜料。
合适的不透明颜料包括二氧化钛(TiO2)或二氧化钛和如下辅助遮盖颜料的结合物:如有空隙胶乳聚合物粒子、氧化锌、氧化铅、合成聚合物颜料及其混合物。金红石和锐锥石等级二氧化钛在此适用。优选是金红石二氧化钛。可以采用各种有机表面处理和/或无机表面处理,如采用二氧化硅、氧化铝、和氧化锆氧化物的处理,处理这些二氧化钛的表面。煅烧的二氧化硅在此也是有用的。
合适的有空隙胶乳粒子的直径为约100nm-约2,500nm和空隙分数为约10%-约75%。优选,和于本发明方法的有空隙胶乳粒子的粒度为约500nm-约1,100nm。不错的粒子含有至少一个空隙,而且可含有多个空隙,非球形空隙,互连的空隙,含有连接到粒子外部的槽的空隙,和描述为成疱的和海绵状的其它结构。优选,(Tg)含有单个空隙。由差示扫描量热法在20℃/min速率下测量的粒子玻璃化转化温度,至少为约20℃,优选至少约50℃。Tg越高,粒子越硬,使得崩塌的可能性更小。如果有空隙的胶乳粒子崩塌,它们不能有益于遮盖。有空隙的胶乳粒子,它们可由在本领域已知的常规聚合方法制备,如在如下文献中公开的那些:US-A-3,784,391、US-A-4,798,691、US-A-4,908,271、US-A-4,972,000、US-A-5,041,464、US-A-5,157,084、US-A-5,216,044和US-A-6,020,435,以及日本专利申请60/223,873、61/62510、61/66710、61/86941、62/127336、62/156387、01/185311,和02/140272。优选,根据如下文献制备有空隙的胶乳粒子:US-A-4,427,836、US-A-4,469,825、US-A-4,594,363、US-A-4,880,842、US-A-5,494,971和US-A-020,435。
在此使用的体质颜料包括优化用于所需终端用途的内部和外部体质颜料。外部体质颜料在水中不稳定和具有低吸收数目。优化它们优化用于特定市场中的外部耐用性,其中销售油漆,和它们并不减损干燥油漆所需的非裂化、非粉化,和非脏物保持性能。它们也在低成本下提供体积。优化内部体质颜料的遮盖性,光泽和低成本。合适的体质颜料包括硫酸钡(1-15微米)、钡白(0.5-5微米)、碳酸钙(0.05-35微米)、二氧化硅(0.001-14微米)、硅酸镁(0.5-15微米)、硅酸铝(0.2-5微米)、霞石正长岩、云母、膨润土、铝硅酸镁、煅烧的氧化铝、胶体绿坡缕石、合成非晶形铝硅酸钠、铝硅酸钠钾、等。
胶乳聚合物漆基是形成初级油漆膜的聚合物或预聚物。它们粘合颜料和/或增量剂,提供要求的油漆流动,和确定最终油漆膜的光泽和硬度。选择用于预油漆的漆基会依赖于配制油漆的最终用途。适于外部油漆的漆基一般适于内部油漆,但适于内部油漆的漆基可能不适于外部油漆。
合适的胶乳聚合物漆基包括,但不限于,均聚物、共聚物或三元共聚物,例如丙烯酸类和/或甲基丙烯酸类聚合物或共聚物、聚醋酸乙烯酯、苯乙烯-丙烯酸类共聚物、苯乙烯-丁二烯、醋酸乙烯酯-丙烯酸类共聚物、乙烯-醋酸乙烯酯共聚物、醋酸乙烯酯-有支链的烷烃羧酸乙烯酯聚合物、.醋酸乙烯酯-马来酸乙烯酯聚合物、醋酸乙烯酯-氯乙烯-丙烯酸类三元共聚物、乙烯-醋酸乙烯酯-丙烯酸类三元共聚物、和尿烷聚合物。聚合物可包含至多10wt%官能单体,(例如,但不限于,羧酸、磷酸酯、硫酸酯、磺酸酯和酰胺)基团,其它单体,及其混合物。可选择地在预油漆x,y,x’,y’,或其它预油漆中引入的胶乳聚合物漆基可以与预油漆z的胶乳聚合物漆基相同或不同。
可以想象的是对于工业涂料,预油漆会采用许多热塑性和热固性聚合物漆基,它们在本发明的预油漆和方法中可以是一罐式,两罐式或可能量固化的,包括但不限于:沥青、石蜡、煤焦油、醇酸树脂、醋酸乙烯酯、醋酸乙烯酯/丙烯酸类、苯乙烯-丁二烯、饱和聚酯、不饱和聚酯、聚氨酯、丙烯酸清漆、丙烯酸磁漆、丙烯酸胶乳、丙烯酸热固性物质、丙烯酸电沉积和自动沉积物、苯乙烯丙烯酸类物、乙烯基甲苯丙烯酸类物、可辐射固化的丙烯酸类物、蜜胺、脲、环氧类物(双酚A,双酚F的二缩水甘油醚、环脂族,单官能环氧类物等)、醋酸乙烯酯共聚物N-羟甲基丙烯酰胺、醋酸乙烯酯-乙烯、醋酸乙烯酯三元共聚物、醋酸乙烯酯-有支链的烷烃羧酸乙烯酯、聚氯乙烯、聚偏二氯乙烯、乙烯-丙烯酸、乙烯-甲基丙烯酸、离子交联聚合物、乙烯-丙烯酸甲酯、纤维素、硝基纤维素、乙酸丁酸纤维素、虫胶、酚类物、硅酸乙酯、聚缩醛、苯乙烯-烯丙醇、氯化橡胶、聚乙烯醇、丁基橡胶、苯乙烯-乙烯丁烯-苯乙烯嵌段共聚物橡胶、尿烷丙烯酸酯、聚酰胺酰亚胺、聚酯酰亚胺、硅氧烷、聚苯硫醚、芳族聚酯、聚酰亚胺、硅氧烷酰亚胺、氟聚合物、芳族聚酰胺、硬脂酸酯聚合物、油性树脂、和氯化聚烯烃和双-环苯并丁烯。
聚合物漆基优选是水性胶乳,但也可以是溶剂性,水稀释性、可再分散性胶乳,及其结合物。
聚合物漆基可以是一包装或两包装形式。如果聚合物漆基是两包装形式,聚合物漆基可以由如下方式使用:
(1)把两包装体系的一种组分分为单独预油漆;
(2)把两包装体系的一种组分分出并将它包括和在不透明预油漆或增量剂预油漆中;
(3)独立于任何预油漆加入两包装体系的一种组分;和
(4)它们的结合。
增稠剂是用于描述加入到油漆中以改进它的流变情况的任何材料的通用术语。优选的增稠剂是结合增稠剂。在此使用的合适增稠剂包括聚乙烯醇(PVA)、在本领域已知为HASE的疏水性改性的,碱溶性乳液、在本领域已知为ASE的碱溶性或碱溶胀性乳液,在本领域已知为HEUR增稠剂的疏水性改性的环氧乙烷-尿烷聚合物、和纤维素增稠剂如羟甲基纤维素(HMC)、羟乙基纤维素(HEC)、疏水性改性的羟乙基纤维素(HMHEC)、羧甲基纤维素钠(SCMC)、羧甲基2-羟乙基纤维素钠、2-羟丙基甲基纤维素、2-羟乙基甲基纤维素、2-羟丁基甲基纤维素、2-羟乙基乙基纤维素、2-羟丙基纤维素等。同样可用作增稠剂的是煅烧的二氧化硅、绿坡缕石粘土和其它类型的粘土、钛酸盐螯合剂等。
在此使用的合适分散剂包括非离子、阴离子和阳离子分散剂如2-氨基2-甲基1-丙醇(AMP)、二甲基氨基乙醇(DMAE)、三聚多磷酸钠(KTPP)、多磷酸三钠(TSPP)、柠檬酸和其它羧酸等。同样合适用作分散剂的是阴离子聚合物如基于多羧酸的均聚物和共聚物,包括已经疏水性改性的或亲水性改性的那些,如聚丙烯酸或聚甲基丙烯酸或马来酸酐与各种单体如苯乙烯、丙烯酸或甲基丙烯酸酯、二异丁烯、和其它亲水性或疏水性共聚单体以及上述分散剂的盐,及其混合物。
合适的消泡剂包括硅氧烷基和矿物油基消泡剂等。
如果在漆基预油漆中使用无溶剂胶乳聚合物漆基,凝结剂不是必须的。无溶剂漆基典型地具有低Tg和低最小成膜温度使得它们在环境温度下,如20℃下成膜。如果要求凝结剂,优选在漆基预油漆和包括胶乳聚合物漆基的任何其它预油漆中将它引入。
合适的凝结剂,增塑剂,和其它非必要溶剂包括乙二醇、丙二醇、己二醇、2,2,4-三甲基-1,3-戊二醇单异丁酸酯(TEXANOLTM)、二醇醚、溶剂油、甲基卡必醇、丁基卡必醇、邻苯二甲酸酯、己二酸酯等。
合适的杀霉菌剂和杀虫剂包括氧化锌、异噻唑酮、三唑等。
合适的表面活性剂包括阳离子、阴离子、和非离子表面活性剂。
合适的凝集体包括小凝集体(典型地40目和更高)、中凝集体(典型地20-40目)和大凝集体(典型地20目和更低),如砂子、大粒度碳酸盐(石灰石)、陶瓷、玻璃、纤维、煤、花网岩、滑石、多色彩石英、碎海贝壳、循环产物如含沥表的材料、玻璃纤维、蛭石、珍珠岩、XO凝集体等。
合适的防闪锈剂包括氨乙基乙醇胺、苯甲酸铵、硝酸钠、苯甲酸氨、二羧酸和二酚,如戊二酸、丙二酸、辛二酸、癸二酸、己二酸、琥珀酸、邻苯二甲酸、间苯二甲酸、对苯二甲酸、噻二酚和磺酰基二苯酚的铵和胺盐和它们的铵和胺配合锌盐、C-12到C-14叔烷基胺、含有(2-苯并噻唑基硫代)-丁二酸的化合物、(2-苯并噻唑基硫代)丁二酸、4-氧代-4-对甲苯基丁酸与4-乙基吗啉的加合物、锆与4-甲基-δ-氧代-苯-丁酸的配合物等。
合适的交联剂包括多价金属离子,如锌、镁、锆、钙等离子。
反应性颜料是这样的材料,将它加入到涂料配方中以通过为了基材的牺牲性腐蚀而赋予耐腐蚀性。合适的反应性颜料包括钼磷酸钙锌、磷酸锌、三磷酸铝、硅磷酸锶锌、钼酸盐改性的磷酸锌等。
合适的蜡包括巴西棕榈蜡、石蜡、聚乙烯蜡、微粉化乙烯-丙烯酸蜡、聚四氟乙烯(PTFE)蜡等。
碱溶性树脂是这样的聚合物,它包含足够的酸官能度和足够低的分子量以当采用碱中和时,在含水介质中溶解。它们显示牛顿流变性,和作为分散剂(即降低含水介质的表面张力)。合适的碱溶性树脂包括丙烯酸和甲基丙烯酸与羧酸单体共聚的酯(这样的共聚物,例如,购自Rohm and Haas Company和以商品名AcrysolTM I-62和AcrysolTM I-2074销售)、苯乙烯和丙烯酸与非必要α-甲基苯乙烯的共聚物(这样的共聚物,例如,购自Rohm and Haas Company和以商品名MorezTM101销售)、苯乙烯/马来酸酐共聚物等。
在另一个优选的实施方案中,本发明的预油漆和方法可用于制备适用于墙壁或屋顶应用的弹性体涂料。这些预油漆可以采用各种比例混合以获得不同质量,柔韧性、防霉性的弹性体涂料,和适于在墙壁或屋顶上应用的基材粘合力。
区分弹性体涂料和典型建筑涂料的主要特征在于具有低温(<0℃)柔韧性漆基的使用和涂敷涂敷的厚度(典型地用于墙壁应用的干燥涂料厚度为约6-约20密耳和用于屋顶应用的干燥涂料厚度为约15-约40密耳)。当它们在可能产生裂纹的墙壁,如砖石墙壁,或具有随气侯高尺寸变化程度的屋顶基材上使用时,低温柔韧性对于弹性体涂料是特别所需的。除涂料柔韧性以外,需要弹性体涂料系具有不同程度的低温柔韧性,不同质量,粘合到不同基材上的能力,和外观中的变化。
对于经历过整个冬天冷冻温度的气侯,如下特征可用于描述不同的质量水平:
质量水平
描述
PVC
TiO 2 PVC
柔韧性温度
高 <40 >5 <0°F
中 <40 4-5 <0°F
中 >40 >5 <0°F
低 >40 <4 <0°F
对于经历过整个冬天仅有几天冷冻温度的气侯,如下特征可用于描述不同的质量水平:
质量水平
描述
PVC
TiO 2 PVC
柔韧性温度
高 <40 >5 <0°F
中 <40 4-5 <32°F
中 >40 >5 <32°F
低 >40 <4 <32°F
低 >40 >4 <40°F
弹性体涂料的质量可进一步依赖于是否在配方中存在氧化锌(ZnO)而变化。氧化锌改变涂料的机械性能。
最后,弹性体涂料可进一步通过着色剂的加入而变化。典型地,将这些着色剂在涂料研磨部分中干燥研磨和制备。
对于弹性体涂料,人们可以确定如下性能,它们可在涂料制造中改变以制备不同的弹性体涂料:涂料柔韧性、涂料质量(耐用性)、基材粘合力和外观。
为根据弹性体涂料的柔韧性区分,人们可以调节漆基的Tg,涂料的PVC,和氧化锌的存在和水平。为根据弹性体涂料的耐用性区分,人们可以调节二氧化钛(TiO2)的水平。为根据弹性体涂料对基材的粘合力区分,人们可以通过改变漆基组成和水平以配制以涂敷墙壁或屋顶。为根据弹性体涂料的外观区分,人们可以调节着色剂的水平和类型。为获得这些不同的性能,人们可以制备以下实施例36-41中的预油漆的套漆,和将它们以合适的数量混合以制备改变上述性能的弹性体涂料。
在另一个优选的实施方案中,在此的预油漆和方法可用于制备直接涂敷在壁上和作为外部保温和涂饰体系(以下称为“EIFS”)中顶涂层的非胶接性,凝集体面漆涂料。可以将这些预油漆或预配制的组分采用各种比例混合以获得不同柔韧性,质量(耐用性),颜色,和纹理的涂料。
如下配方性能提供人们如何影响特别用于EIFS的它的非胶接性,凝集体面漆涂料的耐用性的例子。其它类型的凝集体面漆可具有相应于不同质量的不同范围的PVC。
因此,以下描述仅表示用于EIFS的凝集体面漆涂料的例子,和不表示用于确定在其它非胶接性,凝集体面漆涂料中PVC水平。
质量
描述
PVC
高 <72
中 72-77
低 >77
此外,人们可以确定影响颜色强度的如下配方性能。其它类型的凝集体面漆可具有相应于不同颜色强度的不同TiO2水平。因此,以下描述仅表示用于EIFS的凝集体面漆涂料的例子,和不表示用于确定用于其它凝集体面漆的TiO2水平。
描述
TiO 2 PVC(%)
白色,柔和 >1.5
中色调 0.5-1.5
深色调 <0.5
最后,人们也可以确定影响涂料纹理的如下配方性能。
描述
小凝集体
大凝集体
细 >90% ≤10%
粗 ≤90% >10%
可以通过改变漆基柔韧性或Tg改变凝集体面漆性能中的进一步变化。
作为涉及非胶接性,凝集体面漆涂料的本发明具体实施方案,人们可以在涂料制造中改变如下性能以制备不同的涂料:PVC水平,TiO2水平,凝集体比例和漆基Tg。
为根据非胶接性,凝集体面漆涂料的柔韧性区分,人们可以调节漆基的Tg。为根据非胶接性,凝集体面漆涂料的耐用性区分,人们可以调节涂料的PVC。为根据非胶接性,凝集体面漆涂料的颜色区分,人们可以调节TiO2水平和着色剂的类型和水平。为根据非胶接性,凝集体面漆涂料的纹理区分,人们可以调节大凝集体的尺寸和水平和大凝集体对小凝集体的比例,为获得这些不同性能,人们可以制备以下实施例54-58中的预油漆的套漆,和将它们以合适的数量混合以制备改变上述性能的非胶接性,凝集体面漆涂料。
在另一个优选的实施方案中,预油漆可用于本发明的方法以形成有用的涂料系列油漆,其中一些涂料包含不透明颜料和/或体质颜料和其中一些涂料不包含不透明颜料(“透明”)。这些涂料可以涂敷到各种基材上,包括金属、木材、和水泥基材,如混凝土屋顶瓦。
在另一个优选的实施方案中,预油漆可用于在此的方法以形成形象艺术油漆系的系列油漆,用于许多应用包括,但不限于,礼品包装纸、波形基材、新闻纸、纸板、标签、冰箱袋、贮存袋、金属膜、箔用的油墨;以及用于通用目的如耐水性,耐摩擦性和高滑动涂敷的套印涂料。
在此公开的所有范围是包括性的和成套范围的最小值和最大值是可结合的。
测试程序
使用ASTM方法D562测量预油漆的斯托默粘度。在6rpm下使用布氏粘度计的针#4测量漆基预油漆和最终油漆的布氏粘度。使用ASTM方法D3205-77测量预油漆和油漆的ICI粘度。可以通过差示扫描量热法在20℃/分钟的速率下测量玻璃化转变温度(“Tg”)。
实施例
实施例1
此实施例描述白色预油漆的制备,它通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-二氧化钛淤浆(76.5%固体)(Ti-PureTMR-746-DuPont) 1152.25分散剂(TamolTM1124-Rohm and Haas) 7.06消泡剂(DrewplusTML-475) 1.00漆基丙烯酸类(50%固体-Tg28℃)(RhoplexTMSG-10M-Rohm 166.32and Haas)乳浊剂-有空隙胶乳粒子(RopaqueTMOP-96-Rohm and Haas) 151.80凝结剂(TexanolTM) 12.95流变改进剂(AcrysolTMRM-8W-Rohm and Haas) 12.76碱-氨(28%) 1.65
使用具有45°节距搅拌叶片的实验室混合器制备预油漆。将水,分散剂,和消泡剂结合和混合。将二氧化钛淤浆缓慢加入和将混合物搅拌15-20分钟。然后加入漆基,凝结剂,流变改进剂,氨,和如需要另外的水。
获得的预油漆具有100加仑的总体积,1,505.8lbs.的总重量,80.0%的总PVC,44.0%的体积固体,67.1%的重量固体,15.058lbs./加仑的密度,在颜料固体上0.40%分散剂,和在胶乳固体上10.0%凝结剂。它的初始和平衡斯托默粘度为88和90KU。它的初始和平衡pH是8.8和8.6。
实施例2
此实施例描述外部颜料增量剂预油漆的制备,如上它通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-霞石正长岩(7.5μ)(MinexTM4) 784.30分散剂(TamolTM1124-Rohm and Haas) 7.84消泡剂(DrewplusTML-475) 2.00漆基丙烯酸类(53.5%固体-Tg18 157.49℃)(RhoplexTMML-200-Rohm and Haas)凝结剂(TexanolTM) 5.90流变改进剂(AcrysolTMRM-8W-Rohm and Haas) 2.55水 368.86
获得的预油漆具有100加仑的总体积,1,328.9lbs.的总重量,80.0%的总PVC,45.0%的体积固体,65.4%的重量固体,13.29lbs./加仑的密度,在颜料固体上0.50%总分散剂,和在漆基固体上7.0%凝结剂。它的初始和平衡斯托默粘度为90和93。它的初始和平衡pH是8.9和8.7。
实施例3
此实施例描述内部颜料增量剂预油漆的制备,如上它通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-碳酸钙(12μ)(OmyacarbTM12) 405.67颜料-碳酸钙(3.2μ)(VicronTM15-15) 203.59颜料-硅酸铝(1.4μ)(OptiwhiteTM) 165.41分散剂(TamolTM1124-Rohm and Haas) 7.75消泡剂(DrewplusTML-475) 1.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14 157.61℃)(RESTM3803-Rohm and Haas)凝结剂(TexanolTM) 6.07流变改进剂-HEUR(AcrysolTMRM-2020-NPR) 17.53碱-氨(28%) 0.87水 356.59
获得的预油漆具有100加仑的总体积,1,322.1lbs.的总重量,80%的总PVC,45%的体积固体,65.15%的重量固体,13.2210lbs./加仑的密度,在颜料固体上0.50%分散剂,和在漆基固体上7.00%凝结剂。它的初始和平衡斯托默粘度为94和97。它的初始和平衡pH都是9.2。
实施例4
此实施例描述醋酸乙烯酯/丙烯酸类胶乳聚合物漆基预油漆,它如上所述制备,区别在于将漆基,消泡剂,凝结剂,氨,水,和流变改进剂结合和混合。成分和数量如下:成分
数量(lbs./100加仑)消泡剂(DrewplusTML-475) 8.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14 788.06℃)(RESTM3803-Rohm and Haas)凝结剂(TexanolTM) 30.34流变改进剂-HEUR(AcrysolTMSCT-275-Rohm and Haas) 3.02碱-氨(28%) 1.95水 60.08
获得的预油漆具有100加仑的总体积,891.5lbs.的总重量,45.0%的体积固体,48.6%的重量固体,8.91lbs./加仑的密度,和在漆基固体上7.0%凝结剂。它的初始和平衡斯托默粘度为88和90。它的初始和平衡pH是8.6和8.4。它的平衡布氏粘度应当小于10,000cps。
实施例5
此实施例描述无光丙烯酸类漆基预油漆,如上所述它通过结合如下成分制备:成分
数量(lbs./100加仑)消泡剂(DrewplusTML-475) 8.00漆基-醋酸乙烯酯/丙烯酸类(53.5%固体-Tg18 769.96℃)(RhoplexTMML-200-Rohm and Haas)凝结剂(TexanolTM) 28.83流变改进剂(HEUR)(AcrysolTMRW-8W-Rohm and Haas) 1.15碱-氨(28%) .57溶剂-丙二醇 60.00水 12.84
获得的预油漆具有100加仑的总体积,881.4lbs.的总重量,44.0%的体积固体,46.7%的重量固体,8.81lbs./加仑的密度,和在漆基固体上7.0%凝结剂。它的初始和平衡斯托默粘度为91和89。它的初始和最终pH两者是8.9/9.0。它的平衡布氏粘度应当小于10,000cps。
实施例6
此实施例描述光泽丙烯酸类漆基预油漆,如上所述它通过结合如下成分制备:成分
数量(lbs./100加仑)消泡剂(DrewplusTML-475) 8.00漆基-丙烯酸类(50%固体-Tg28℃)(RhoplexTMSG-10M-Rohm 737.08and Haas)凝结剂(TexanolTM) 36.85流变改进剂-HEUR(AcrysolTMRM-8W-Rohm and Haas) 11.62碱-氨(28%) .35溶剂-丙二醇 60.00水 21.26
获得的预油漆具有100加仑的总体积,875.2lbs.的总重量,39.0%的体积固体,42.11%的重量固体,8.75lbs./加仑的密度,和在漆基固体上10.0%凝结剂。它的初始和平衡斯托默粘度为97和98。它的初始和平衡pH是9.0。它的平衡布氏粘度应当小于10,000cps。
实施例7
此实施例描述白色颜料预油漆的制备,该预油漆包括无溶剂丙烯酸类漆基和没有使用凝结剂。使用如下所示的成分和数量,如实施例1所述将成分混合。成分
数量(lbs./100加仑)颜料-二氧化钛(Ti-PureTMR-706-DuPont) 734.49乳浊剂-有空隙胶乳粒子(RopaqueTMOP-96-Rohm and Haas) 164.43分散剂(TamolTM731-Rohm and Haas) 29.38非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KathonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL) 3.00漆基丙烯酸类(43.5%固体-Tg-2℃)(RhoplexTMSF-012-Rohm 165.96and Haas)流变改进剂-HEUR(AcrysolTMRM-825-Rohm and Haas) 5.00流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 42.69碱-氨(28%) .49水 250.13
获得的预油漆应当具有100加仑的总体积,1,401.3lbs.的总重量,80.0%的PVC,40.0%的体积固体,61.1%的重量固体,14.01lbs./加仑的密度,和在颜料固体上1.0%分散剂。它的预测斯托默粘度为102KU。它的pH应当为8.5-9.0。
实施例8
此实施例描述采用无溶剂丙烯酸类漆基和没有使用凝结剂,外部颜料增量剂预油漆的制备。使用如下所示的成分和数量,如实施例1所述将成分混合。成分
数量(lbs./100加仑)颜料-霞石正长岩(7.5μ)(MinexTM4) 697.16分散剂(TamolTM731-Rohm and Haas) 27.89非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KathonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL) 3.00漆基丙烯酸类(46.5%固体-Tg1℃)(PrimalTMSF-015Rohm 160.84and Haas)流变改进剂HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 101.80水 284.47
获得的预油漆应当具有100加仑的总体积,1,280.9lbs.的总重量,80.0%的PVC,40.0%的体积固体,60.27%的重量固体,12.81lbs./加仑的密度,和在颜料固体上1.0%分散剂。它的斯托默粘度应当为95KU。它的pH应当为8.5-9.0。如果不,如实施例7所述调节pH。
实施例9
此实施例描述内部颜料增量剂预油漆的制备,该预油漆包括无溶剂醋酸乙烯酯/丙烯酸类漆基和没有使用凝结剂。使用如下所示的成分和数量,如实施例1所述将成分混合。成分
数量(lbs./100加仑)颜料-碳酸钙(3.2μ)(SnowflakeTM) 451.20颜料-硅酸铝(1.4μ)(OptiwhiteTM) 220.37分散剂(TamolTM1254-Rohm and Haas) 19.19非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KathonTMLX(1.5%)) 2.00消泡剂(FoamasterTMVL) 3.00漆基-醋酸乙烯酯/丙烯酸类(55%固体)(RovaceTM9900) 139.86流变改进剂HASE(AcrysolTMDR-3) 9.00碱-氨(28%) 0.86水 405.69
获得的预油漆应当具有100加仑的总体积,1,254.9lbs.的总重量,80.0%的PVC,40.0%的体积固体,59.65%的重量固体,12.55lbs./加仑的密度,和在颜料固体上1.0%分散剂。它的斯托默粘度应当为95KU。它的pH应当为8.5-9.0。
实施例10
此实施例描述醋酸乙烯酯/丙烯酸类胶乳聚合物漆基预油漆的制备,该预油漆包括无溶剂醋酸乙烯酯/丙烯酸类漆基和没有凝结剂。使用如下所示的成分和数量,如实施例4所述将成分混合。成分
数量(lbs./100加仑)漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg10 699.25℃)(RovaceTM9900-Rohm and Haas)消泡剂(FoamasterTMVL) 3.00流变改进剂HASE(AcrysolTMDR-3-Rohm and Hass) 12.96碱-氨(28%) 2.90水 405.69
获得的预油漆应当具有100加仑的总体积,885.2lbs.的总重量,40.0%的体积固体,43.5%的重量固体,8.85lbs./加仑的密度。它的斯托默粘度应当为99KU。它的布氏粘度应当小于10,000cps。它的pH应当为8.5-9.0。
实施例11
此实施例描述无光胶乳聚合物漆基预油漆的制备,该预油漆包括无溶剂丙烯酸类漆基和没有凝结剂。使用如下所示的成分和数量,如实施例4所述将成分混合。成分
数量(lbs./100加仑)消泡剂(FoamasterTMVL) 8.00漆基-丙烯酸类共聚物(43.5%固体-Tg-2 723.77℃)(RhoplexTMSF-012-Rohm and Haas)流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 3.00水 133.75
获得的预油漆应当具有100加仑的总体积,868.5lbs.的总重量,36.0%的体积固体,38.8%的重量固体,8.69lbs./加仑的密度。它的斯托默粘度应当为99KU。它的布氏粘度应当小于10,000cps。它的pH应当为8.5-9.0,和如果不,如上所述调节pH。
实施例12
此实施例描述使用无溶剂丙烯酸类漆基和没有凝结剂,光泽胶乳聚合物漆基预油漆的制备。使用如下所示的成分和数量,如实施例4所述将成分混合。成分
数量(lbs./100加仑)消泡剂(FoamasterTMVL) 8.00漆基-丙烯酸类共聚物(43.5%固体-Tg-2 767.57℃)(RhoplexTMSF-012-Rohm and Haas)流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 23.00水 61.62
获得的预油漆应当具有100加仑的总体积,860.4lbs.的总重量,37.0%的体积固体,38.8%的重量固体,8.60lbs./加仑的密度。它的斯托默粘度应当为99KU。它的布氏粘度应当小于10,000cps。它的pH应当为8.5-9.0,和如果不,如上所述调节pH。
实施例13
此实施例描述使用内部光泽级二氧化钛,白色颜料预油漆的制备,该预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-二氧化钛(Ti-PureTMR-900-DuPont) 734.49乳浊剂-有空隙的胶乳粒子(30.5%固体) 164.43(RopaqueTMUltra-Rohm and Haas)分散剂(TamolTM1254-Rohm and Haas) 20.99非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KathonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL-来源) 3.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tgl4 140.10℃)(RES3083-Rohm and Haas)流变改进剂-HEUR(AcrysolTMRM-825-Rohm and Haas)凝结剂(TexanolTM) 11.37流变改进剂HASE(AcrysolTMDR-3) 11.47碱-氨(28%) 1.20溶剂-丙二醇 50.00水 264.38
获得的预油漆具有100加仑的总体积,1405.4lbs.的总重量,80%的PVC,40%的体积固体,61.25%的重量固体,14.05lbs./加仑的密度,和在颜料固体上1.0%分散剂,和在漆基固体上9.0%凝结剂。斯托默粘度为100KU。布氏粘度为15,300cps。pH为8.8。
实施例14
此实施例描述使用外部光泽级二氧化钛,白色颜料预油漆的制备,该预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-二氧化钛(Ti-PureTMR-706-DuPont) 734.56乳浊剂-有空隙的胶乳粒子(30.5%固体) 164.44(RopaqueTMUltra-Rohm and Haas)分散剂(TamolTM731-Rohm and Haas) 29.38非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KathonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL) 3.00漆基-丙烯酸类共聚物(50%固体-Tg28 151.20℃)(RhoplexTMSG-10-Rohm and Haas)凝结剂(TexanolTM) 12.49流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 42.69碱-氨(28%) .49溶剂-丙二醇 50.00水 211.34
获得的预油漆具有100加仑的总体积,1403.6lbs.的总重量,80%的PVC,40%的体积固体,61.2%的重量固体,14.04lbs./加仑的密度,和在颜料固体上1.0%分散剂,和在漆基固体上9.0%凝结剂。斯托默粘度为100KU。布氏粘度为4,010cps。pH为8.8。
实施例15
此实施例描述外部颜料增量剂预油漆的制备。它通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-霞石正长岩(7.5μ)(MinexTM4) 697.16分散剂(TamolTM731-Rohm and Haas) 27.89非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂KathonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL) 3.00漆基-丙烯酸类(53.5%固体-Tg18 139.98℃)(RhoplexTMMultilobe200-Rohm and Haas)凝结剂(TexanolTM) 5.24流变改进剂-HEUR(AcrysolTMRM-2020-Rohm and Haas) 101.80溶剂-丙二醇 50.00水 254.40
获得的预油漆具有100加仑的总体积,1281.5lbs.的总重量,80.0%的PVC,40.0%的体积固体,60.3%的重量固体,12.81lbs./加仑的密度,和在颜料固体上1.0%分散剂,和在漆基固体上7.0%总凝结剂。斯托默粘度为96KU。布氏粘度为7,210cps。pH为9.8。
实施例16
此实施例描述内部颜料增量剂预油漆的制备。它通过结合如下成分制备:成分
数量(lbs./100加仑)颜料-碳酸钙(5μ)(SnowflakeTM) 451.20颜料-硅酸铝(1.4μ)(OptiwhiteTM) 220.37分散剂(TamolTM1254-Rohm and Haas) 19.19非离子表面活性剂(TritonTMCF-10) 2.00杀虫剂(KalthonTMLX(1.5%)-Rohm and Haas) 2.00消泡剂(FoamasterTMVL) 3.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14 140.10℃)(RES3083-Rohm and Haas)凝结剂(TexanolTM) 6.93流变改进剂HASE-(AcrysolTMDR-3-Rohm and Haas) 11.00碱-氨(28%) 0.86溶剂-丙二醇 50.00水 348.48
获得的预油漆具有100加仑的总体积,1255.1lbs.的总重量,80.0%的PVC,40.0%的体积固体,59.7%的重量固体,12.55lbs./加仑的密度,和在颜料固体上1.0%分散剂,和在漆基固体上9.0%总凝结剂。斯托默粘度为102KU。布氏粘度为3,410cps。pH为8.9。
实施例17
此实施例描述醋酸乙烯酯/丙烯酸类预油漆的制备。它通过结合如下成分制备:成分
数量(lbs./100加仑)消泡剂(FoamasterTMVL) 3.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14 700.48℃)(RES3083-Rohm and Haas)凝结剂(TexanolTM) 34.67流变改进剂-HASE(AcrysolTMDR-3-Rohm and Haas) 12.96碱-氨(28%) 2.90溶剂-丙二醇 50.00水 83.48
获得的预油漆具有100加仑的总体积,887.5lbs.的总重量,40.0%的体积固体,43.4%的重量固体,8.88lbs./加仑的密度,和在漆基固体上9.0%总凝结剂。它的斯托默粘度为98.0。布氏粘度为13,600cps。它的pH为9.0。
实施例18
此实施例描述无光丙烯酸类漆基预油漆的制备。它通过结合如下成分制备:成分
数量(lbs./100加仑)消泡剂(FoamasterTMVL) 3.00漆基-丙烯酸类(53.5%固体-Tg18℃)(RhoplexTM 699.92Multilobe200-Rohm and Haas)凝结剂(TexanolTM) 26.21流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 1.44碱-氨(28%) 0.35溶剂-丙二醇 50.00水 96.59
获得的预油漆具有100加仑的总体积,877.5lbs.的总重量,40.0%的体积固体,42.7%的重量固体,8.78lbs./加仑的密度,和在漆基固体上7.0%总凝结剂。它的斯托默粘度为94.0。布氏粘度为4,900cps。它的pH为8.9。
实施例19
此实施例描述光泽丙烯酸类漆基预油漆的制备。它通过结合如下成分制备:成分
数量(lbs./100加仑)消泡剂(FoamasterTMVL) 3.00漆基丙烯酸类(50%固体-Tg28℃)(RhoplexTMSG-10M-Rohm and 755.99Haas)凝结剂(TexanolTM) 37.80流变改进剂-HEUR(AcrysolTMRM-2020NPR-Rohm and Haas) 11.62碱-氨(28%) 0.35溶剂-丙二醇 50.00水 17.68
获得的预油漆具有100加仑的总体积,876.4lbs.的总重量,40.0%的体积固体,43.1%的重量固体,8.76lbs./加仑的密度,和在漆基固体上10.0%总凝结剂。它的斯托默粘度为96。布氏粘度为5,000cps。它的pH为8.8。
实施例20
此实施例描述通过结合如下成分,白色预油漆的制备:成分
数量(lbs./100加仑)颜料-二氧化钛(Ti-PureTMR-706-DuPont) 1001.66分散剂(TamolTM1124-Rohm and Haas) 20.03消泡剂(DrewplusTML-475) 1.00漆基丙烯酸类(50%固体-Tg28℃)(RhoplexTMSG-10M-Rohm and 189.00Haas)乳浊剂-有空隙胶乳粒子(RopaqueTMOP-96-Rohm and Haas) 172.50凝结剂(TexanolTM) 14.72流变改进剂(AcrysolTMRM-8W-Rohm and Haas) 2.00碱-氨(28%) 1.65水 200.44
获得的预油漆应当具有100加仑的总体积,1,603.0lbs.的总重量,80.0%的PV℃,50.0%的体积固体,71.7%的重量固体,16.03lbs./加仑的密度,在颜料固体上1%分散剂,和在胶乳固体上10.0%凝结剂。
实施例21
此实施例描述了采用着色成疱聚合物珠,白色颜料预油漆的制备。着色起疱聚合物珠具有12.5微米的粒度,大约7%(s/s)二氧化钛,和大约77%的空隙体积。使用如下所示的成分数量,如实施例1所述将成分混合。成分
数量(lbs./100.加仑)着色起疱聚合物珠(SpindriftTM25) 733.00分散剂(TamolTM1124-Rohm and Haas) 0消泡剂(DrewplusTML-475) 2.00漆基丙烯酸类(53.5%固体-Tg28℃)(RhoplexTMML-200-Rohm 154and Haas)凝结剂(TexanolTM) 5.90流变改进剂(AcrysolTM RM-8W-Rohm and Haas) 2.55水 15.89
获得的预油漆应当具有100加仑的总体积,913.3lbs.的总重量,80.0%的PVC,44.0%的体积固体,28.28%的重量固体,9.13lbs./加仑的密度。它的斯托默粘度应当为91KU。它的pH应当为8.5-9.0。如果不,如实施例7所述调节pH。
实施例22
此实施例描述通过结合如下成分,外部颜料增量剂预油漆的制备:成分
数量(lbs./100加仑)颜料-霞石正长岩(7.5μ)(MinexTM4) 871.44分散剂(TamolTM1124-Rohm and Haas) 8.71消泡剂(DrewplusTML-475) 2.00漆基丙烯酸类(60.5%固体-Tg16℃)(RhoplexTMAC-264-Rohm 154.74and Haas)凝结剂(TexanolTM) 6.56流变改进剂(AcrysolTMRM-8W-Rohm and Haas) 3.00水 326.08
获得的预油漆应当具有100加仑的总体积,1,382.5lbs.的总重量,80.0%的PVC,50.0%的体积固体,69.8%的重量固体,13.82lbs./加仑的密度,在颜料固体上0.5%分散剂,和在胶乳固体上7.0%凝结剂。
实施例23
此实施例描述通过结合如下成分,内部颜料增量剂预油漆的制备:成分
数量(lbs./100加仑)颜料-碳酸钙(12μ)(OmyacarbTM12) 450.67颜料-碳酸钙(3.2μ)(VicronTM15-15) 226.17颜料-硅酸铝(1.4μ)(OptiwhiteTM) 183.76分散剂(TamolTM1124-Rohm and Haas) 8.61消泡剂(DrewplusTML-475) 1.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14℃)(RES 175.093803)凝结剂(TexanolTM) 6.74流变改进剂-HEUR(AcrysolTMSCT-275) 15.00碱-氨(28%) 0.87水 308.13
获得的预油漆应当具有100加仑的总体积,1376.0lbs.的总重量,80.0%的总PVC,50.0%的体积固体,69.5%的重量固体,13.76lbs./加仑的密度,在颜料固体上0.5%分散剂,和在漆基固体上7.0%凝结剂。
实施例24
此实施例描述通过结合如下成分,醋酸乙烯酯/丙烯酸类漆基预油漆的制备:成分
数量(lbs./100加仑)消泡剂(DrewplusTML-475) 2.00漆基-醋酸乙烯酯/丙烯酸类(55%固体-Tg14℃)(RESTM3803) 875.62凝结剂(TexanolTM) 13.00流变改进剂-HEUR(AcrysolTMSCT-275-Rohm and Haas) 9.29
获得的预油漆应当具有100加仑的总体积,899.9lbs.的总重量,0.0%的总PVC,50.0%的体积固体,53.2%的重量固体,8.99lbs./加仑的密度,和在胶乳固体上10.0%凝结剂。
实施例25
此实施例描述通过结合如下成分,无光丙烯酸类预油漆的制备:成分
数量(lbs./100加仑)消泡剂(DrewplusTML-475) 8.00漆基丙烯酸类(60.5%固体-Tg16 773.67℃)(RhoplexTMAC-264-Rohm and Haas)凝结剂(TexanolTM) 23.40流变改进剂(HEUR)(AcrysolTMRM-8W-Rohm and Haas) 13碱-氨(28%) 0.50溶剂-丙二醇 60.00水 1.84
获得的预油漆应当具有100加仑的总体积,880.4lbs.的总重量,0.0%的总PVC,50.0%的体积固体,53.2%的重量固体,8.80lbs./加仑的密度,和在胶乳固体上5.0%凝结剂。
实施例26
此实施例描述通过结合如下成分,光泽丙烯酸类预油漆的制备:成分
数量(lbs./100加仑)漆基-丙烯酸类(50%固体-Tg28 836.85℃)(RhoplexTMSG-10M-Rohm and Haas)凝结剂(TexanolTM) 41.84
获得的预油漆应当具有100加仑的总体积,878.7lbs.的总重量,0.0%的总PVC,44.3%的体积固体,47.4%的重量固体,8.78lbs./加仑的密度,和在胶乳固体上10.0%凝结剂。
实施例27
此实施例描述使用实施例14的白色颜料预油漆,实施例15的外部颜料增量剂预油漆,实施例17的醋酸乙烯酯-丙烯酸类(PVA)漆基预油漆,和实施例18的无光丙烯酸类漆基预油漆的结合,具有改变质量和色调的九种外部无光胶乳油漆的制备。通过将白色颜料预油漆和外部颜料增量剂预油漆加入到漆基预油漆中和充分混合,配制预油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固 白色 外部增 PVA漆基 无光丙
(wt.)
体(%) 量剂 烯酸类
漆基
(Ex14)
(Ex15)
(Ex17)
(Ex18)27-1 45.0 35.0 395.53 269.60 - 335.92 104.3427-2 50.0 30.0 317.19 311.10 - 246.80 208.6827-3 50.0 30.0 263.69 359.94 197.64 51.38 208.6827-4 42.5 35.0 197.77 415.12 - 359.92 104.3427-5 47.5 30.0 158.60 425.86 - 267.37 208.6827-6 47.5 30.0 131.84 450.28 214.11 55.67 208.6827-7 40.0 35.0 - 560.64 - 383.91 104.3427-8 45.0 30.0 - 540.62 - 287.93 208.6827-9 45.0 30.0 - 540.62 230.58 59.95 208.68
油漆27-1,27-4和27-7是特级质量淡,中等和深色调油漆;油漆27-2,27-5和27-8是第一质量淡,中等和深色调油漆;和油漆27-3,27-6和27-9是第二质量淡,中等和深色调油漆。
实施例28
此实施例描述分别使用实施例14和15的白色颜料预油漆和外部颜料增量剂预油漆,和实施例17和18的醋酸乙烯酯-丙烯酸类(PVA)漆基预油漆和无光丙烯酸类漆基预油漆的不同结合,具有改变质量和色调的九种外部缎光胶乳油漆的制备。如上所述配制油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固
体 白色 外部增量 PVA漆基 无光丙烯
(wt.)
(%) 剂 酸类漆基
(Ex14)
(Ex15)
(Ex17)
(Ex18)28-1 35.0 35.0 395.53 129.44 - 431.90 104.3428-2 37.0 30.0 351.59 123.51 - 353.75 208.6828-3 40.0 26.0 263.69 175.73 228.35 59.41 292.1528-4 32.5 36.0 197.77 287.98 - 468.92 83.4728-5 34.5 30.0 175.75 253.98 - 374.31 208.6828-6 37.5 26.0 131.84 270.07 242.63 63.12 292.1228-7 30.0 36.0 - 432.50 - 493.60 83.4728-8 32.0 30.0 - 384.44 - 394.88 208.6828-9 35.0 26.0 - 364.42 256.87 66.86 292.15
油漆28-1,28-4和28-7是特级质量淡,中等和深色调油漆;油漆28-2,28-5和28-8是第一质量淡,中等和深色调油漆;和油漆28-3,28-6和28-9是第二质量淡,中等和深色调油漆。
实施例29
此实施例描述分别使用实施例14和15的白色颜料预油漆和外部颜料增量剂预油漆,和实施例17和19的醋酸乙烯酯-丙烯酸类(PVA)漆基和光泽丙烯酸类漆基预油漆的不同结合,九种外部光泽胶乳油漆的制备。如上所述配制油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固
体 白色 PVA漆基 光泽丙烯酸
(wt.)
(%) 类漆基
(Ex14)
(Ex17)
(Ex19)29-1 26.0 35.0 435.66 - 494.85 104.3429-2 30.0 30.0 460.50 - 413.60 166.9429-3 30.0 30.0 429.93 304.15 88.51 208.6829-4 13.0 35.0 217.83 - 630.87 104.3429-5 15.0 30.0 230.25 - 557.38 166.9429-6 15.0 30.0 214.96 409.14 119.06 208.6829-7 - 35.0 - - 766.89 104.3429-8 - 30.0 - - 701.15 166.9429-9 - 30.0 - 514.12 149.61 208.68
油漆29-1,29-4和29-7是特级质量淡,中等和深色调油漆;油漆29-2,29-5和29-8是第一质量淡,中等和深色调油漆;和油漆29-3,29-6和29-9是第二质量淡,中等和深色调油漆。
实施例30
此实施例描述分别使用实施例14和16的白色颜料和内部增量剂预油漆,和实施例17和18的醋酸乙烯酯-丙烯酸类(PVA)和无光丙烯酸类漆基预油漆的不同结合,九种内部无光胶乳油漆的制备。如上所述配制油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固
体 白色 外部增量 PVA漆基 无光丙烯
(wt.) (%) 剂 酸类漆基
(Ex14)
(Ex16)
(Ex17)
(Ex18)30-1 50.0 30.0 351.59 273.94 197.64 51.38 208.6830-2 60.0 30.0 263.69 470.21 166.40 - 208.6830-3 75.0 25.0 128.02 620.95 34.67 - 313.0230-4 47.5 15.0 175.79 401.73 214.11 55.67 208.6830-5 57.5 30.0 131.84 558.69 187.20 - 208.6830-6 72.5 25.0 64.01 653.67 52.00 - 313.0230-7 45.0 30.0 - 529.51 230.58 59.95 208.6830-8 55.0 30.0 - 647.18 208.01 - 208.6830-9 70.0 25.0 - 686.40 69.34 - 313.02
油漆30-1,30-4和30-7是特级质量淡,中等和深色调油漆;油漆30-2,30-5和30-8是第一质量淡,中等和深色调油漆;和油漆30-3,30-6和30-9是第二质量淡,中等和深色调油漆。
实施例31
此实施例描述分别使用实施例14和16的白色颜料和内部增量剂预油漆,和实施例17和18的醋酸乙烯酯-丙烯酸类(PVA)和缎光丙烯酸类漆基预油漆的不同结合,九种内部无光胶乳油漆的制备。如上所述配制油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固
体 白色 外部增量 PVA漆基 无光丙烯
(wt.)
(%) 剂 酸类漆基
(Ex14)
(Ex16)
(Ex17)
(Ex18)31-1 35.0 36.0 395.53 140.51 355.75 92.49 83.4731-2 37.0 30.0 351.59 120.98 357.77 - 208.6831-3 40.0 20.0 263.69 172.12 288.43 - 292.1531-4 32.5 36.0 197.77 282.06 375.51 97.96 83.4731-5 34.5 30.0 175.79 248.76 378.57 - 208.6831-6 37.5 26.0 131.84 264.52 306.46 - 292.1531-7 30.0 36.0 - 423.61 395.28 102.77 83.4731-8 32.0 30.0 - 376.54 399.37 - 208.6831-9 35.0 26.0 - 356.93 324.49 - 292.15
油漆31-1,31-4和31-7是特级质量淡,中等和深色调油漆;油漆31-2,31-5和31-8是第一质量淡,中等和深色调油漆;和油漆31-3,31-6和31-9是第二质量淡,中等和深色调油漆。
实施例32
此实施例描述分别使用实施例14的白色颜料预油漆,和实施例17和19的醋酸乙烯酯-丙烯酸类(PVA)和光泽丙烯酸类漆基预油漆的不同结合,九种内部光泽胶乳油漆的制备。如上所述配制油漆。油漆 预油漆(wt.) 水No.
PVC(%) 体积固
体 白色 PVA漆基 光泽丙烯酸
(wt.)
(%) 类漆基
(Ex14)
(Ex17)
(Ex19)32-1 26.0 35.0 435.66 - 494.85 104.3432-2 30.0 38.0 429.93 304.15 88.51 208.6832 3 30.1 28.0 403.18 366.31 - 250.4232-4 13.0 35.0 217.83 - 630.87 104.3432-5 15.0 30.0 214.96 409.14 119.06 208.6832-6 15.0 28.0 201.59 493.78 - 250.4232-7 - 35.0 - - 766.89 104.3432-8 - 30.0 - 514.12 149.61 208.6832-9 - 28.0 - 621.24 - 250.42
油漆32-1,32-4和32-7是特级质量淡,中等和深色调油漆;油漆32-2,32-5和32-8是第一质量淡,中等和深色调油漆;和油漆32-3,32-6和32-9是第二质量淡,中等和深色调油漆。
实施例33
此实施例描述用于建筑涂料的胶乳油漆的制备,它可以使用实施例20的白色颜料预油漆,实施例22的外部颜料增量剂,和实施例25的无光丙烯酸类漆基预油漆制备。如上所述配制油漆。
油漆 | 预油漆(wt.) | 水 |
PVC(%) 体积固体(%)35 48 | 白色 外部增量 无光丙烯酸剂 类漆基(Ex20) (Ex21) (Ex24)331.27 294.95 475.42 | (wt.)33.39 |
获得的油漆应当是具有缎光涂饰和淡色调的特级油漆。
实施例34
此实施例描述使用实施例20的白色颜料预油漆,实施例23的内部颜料增量剂,和实施例24的醋酸乙烯酯-丙烯酸类(PVA)和光泽丙烯酸类漆基,低固体内部无光油漆的制备。
油漆 | 预油漆(wt.) | 水 |
PVC(%) 体积固体(%)75 15 | 白色 内部增量 PVA漆基(Ex20) 剂(Ex22) (Ex23)107.22 294.97 16.87 | (wt.)584.31 |
实施例35
此实施例描述使用实施例1-6的预油漆制备油漆。通过如下方式制备油漆:将颜料预油漆和漆基预油漆混合,然后加入增稠剂,水和着色剂和充分混合。斯托默粘度,ICI粘度,和pH是平均测量值。
部分A-外部无光油漆(最好和良好)
预油漆(lbs.) 增稠剂(lbs.)油漆 白色颜料 外部体 PVA漆基 无光丙 Acrysol Acrysol 水
(lbs.) 着色剂No.
(Ex1) 质颜料
(Ex4) 烯酸类 SCT-
275 RM2020
NPR
(lbs.)
(Ex2) 漆基
(Ex6)35-1a 353.86 278.01 - 306.97 10.40 14.00 149.68 -35-2b 235.96 351.50 177.30 46.09 26.40 11.20 237.06 -35-3a - 516.00 - 351.00 32.68 - 146.45 16235-4b - 500.00 206.58 53.70 48.48 - 237.06 162
a.最好的淡色调和深色调油漆
b.良好的淡色调和深色调油漆
计算性能
测量的平衡值油漆 斯托默
粘 ICI粘
pH
体积 A
重量 *
PVC 体积固 重量
固
密度 No.
度
度
体
体
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35-1c 102 1.15 8.76 100 1112.92 45.05 35.08 50.66 11.1335-2d 101 0.87 8.30 100 1085.52 50.04 30.05 45.68 10.8635-3e 110 1.90 9.02 100 1046.13 39.94 35.00 47.92 10.4635-4f 121 1.80 8.70 100 1045.82 45.09 29.76 43.25 10.36
c.有基于干燥颜料的0.44%分散剂和基于干燥聚合物的7.48%凝结剂
d.有基于干燥颜料的0.46%分散剂和基于干燥聚合物的7.40%凝结剂
e.有基于干燥颜料的0.50%分散剂和基于干燥聚合物的7.00%凝结剂
f.有基于干燥颜料的0.50%分散剂和基于干燥聚合物的7.00%凝结剂
部分B-外部缎光油漆(更好)预油漆(lbs.) 增稠剂(lbs.)油漆 白色颜料 外部体 PVA漆基 无光丙 Acrysol Acrysol 水 着色剂No.
(Ex1) 质颜料
(Ex4) 烯酸类 SCT-
275 RM2020
(lbs.)
(lbs.)
(Ex2) 漆基
NPR
(Ex6)35-5 314.56 137.00 - 323.00 17.82 17.58 234.22 -
计算性能
测量的平衡值油漆 斯托默 ICI粘
pH
体积
重量
PVC 体积 重量
密度 No.
粘度
度 固
体
固体
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35.5 104 1.19 8.95 100.00 1044.18 36.94 29.96 43.26 10.44
有基于干燥颜料的0.43%分散剂和基于干燥聚合物的7.43%凝结剂
部分C-外部半光泽(最好和良好)
预油漆(lbs.) 增稠剂(lbs.)油漆 白色颜料 外部体 PVA漆基 无光丙 Acrysol Acrysol 水 着色剂No.
(Ex1) 质颜料
(Ex4) 烯酸类 SCT-
275 RM2020
(lbs.)
(lbs.)
(Ex2) 漆基
NPR
(Ex5)35-6a 389.40 - - 530.37 - 15.20 98.44 -35-7b 383.98 - 85.33 294.89 22.40 26.00 217.67 -
a.最好
b.良好
计算性能
测量的平衡值油漆 斯托默 ICI粘
度
pH
体积
重量
PVC 体积固
体 重量固
体
密度 No.
粘度
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35-6c 99 1.19 8.54 100.00 1033.41 26.00 35.00 46.91 10.3335-7d 102 1.05 8.20 100.00 1030.27 30.00 29.90 42.43 10.30
c.有基于干燥颜料的0.40%分散剂和基于干燥聚合物的10.00%凝结剂
d.有基于干燥颜料的0.40%分散剂和基于干燥聚合物的7.97%凝结剂
部分D-内部无光
预油漆(lbs.) 增稠剂(lbs.)油漆 白色颜料 外部体 PVA漆基 无光丙 Acrysol Acrysol 水 着色剂No.
(Ex1) 质颜料
(Ex4) 烯酸类 SCT-
275 RM2020
(lbs.)
(lbs.)
(Ex3) 漆基
NPR
(Ex5)35-8a 314.56 280.69 177.31 46.09 24.00 20.80 230.22 -35-9 115.95 590.05 30.04 - 34.60 - 336.19 -35-10a - 496.07 206.55 53.67 41.92 - 236.60 16235-11 - 643.99 62.04 - 51.36 - 320.17 162
a.油漆35-8和35-10是最好的淡和深色调油漆。
油漆35-9和35-11是良好的淡和深色调油漆。
计算性能
测量的平衡值油漆
No. 斯托默 ICI粘
度
pH
体积
重量
PVC 体积固
体 重量
固体
密度
粘度
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35-8 99 1.05 8.45 100.00 1093.67 50.00 30.00 45.88 10.9435-9 84 0.70 8.50 100.00 1106.83 75.15 24.99 43.08 11.0735-10 120 1.90 8.60 100.00 1034.81 45.04 29.99 43.36 10.3535-11 108 1.88 8.80 100.00 1077.56 70.00 25.05 41.74 10.78
对于油漆nos.34-8到34-11,在干燥颜料上的分散剂百分比分别是0.45%,0.48%,0.50%和0.50%。对于油漆nos.34-8到34-11,凝结剂百分比分别是7.53%,47%,7.00%和7.00%。
部分E-内部缎光油漆
预油漆(lbs.) 增稠剂(lbs.)油漆No. 白色颜料 外部体质 PVA漆基 无光丙烯 Acrysol Acrysol 水(lbs.) 着色剂
(Ex1) 颜料 (Ex4) 酸类漆基 SCT-275 RM2020NPR (lbs.)
(Ex3) (Ex5)35-12 314.56 138.00 319.00 - 24.96 21.40 229.76 -
油漆是更好的淡色调油漆。
计算性能
测量的平衡值油漆 斯托默粘度 ICI粘度 pH 体积A 重量* PVC 体积固体 重量固体 密度No.
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35-12 93 0.91 8.37 100.00 1047.68 37.05 29.99 43.54 10.48
在干燥颜料中的分散剂是0.43%。
在干燥聚合物中的凝结剂是7.42%。
部分F-半光泽油漆
预油漆(lbs.) 增稠剂(lbs.)油漆No. 白色颜料 外部体质 PVA漆基 无光丙烯 Acrysol Acrysol 水(lbs.) 着色剂
(Ex1) 颜料 (Ex4) 酸类漆基 SCT-275 RM2020NPR (lbs.)
(Ex3) (Ex5)35-13 383.98 - 294.89 85.33 22.40 26.00 217.67 -35-14 359.89 - 347.58 - 28.80 28.00 255.70 -
油漆nos.35-13是更好和良好的淡色调油漆。
计算性能
测量的平衡值油漆
No. 斯托默 ICI粘
度
pH
体积 A
重量 *
PVC 体积固
体 重量
固
密度
粘度
体
(KU) (cp) (加仑) (lbs) (%) (%) (%) (b/gal)35-13 102 1.05 8.20 100.00 1030.27 30.01 29.91 42.43 10.3035-14 101 1.19 7.90 100.00 1019.97 30.02 28.02 40.22 10.20
对于油漆35-13和35-14,在干燥油漆上的分散剂是0.40%。
对于油漆35-13和35-14,凝结剂分别是7.97%和7.47%。
实施例36
此实施例描述用于弹性体涂料的白色不透明颜料预油漆的制备。预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(50.5%固体,Tg=-16 177.11℃)(Rhoplex2438-Rohm and Haas)水 257.90分散剂(Tamol165A-Rohm and Haas) 49.24消泡剂(Nopco NXZ) 12.44碱-氨(28%) 3.94凝结剂(Texanol) 2.68流变改进剂-(AcrysolSCT-275) 5.00颜料-二氧化钛(Ti-Pure R-960-DuPont) 1292.48
使用高速分散器制备预油漆。将水,分散剂,丙烯酸类漆基,消泡剂,碱,和流变改进剂结合和在低速下简单混合和加入干燥颜料。在加入所有干燥颜料之后,如对于本领域技术人员是已知的那样,应当将混合物在高速下分散15-20分钟。
获得的预油漆具有100加仑的总体积,1,800.80lbs.的总重量,80.00%的总PVC,50.00%的体积固体,76.74%的重量固体,18.008lbs./加仑的密度,和在颜料固体上0.80%分散剂,和在胶乳固体上3.0%凝结剂。
实施例37
此实施例描述用于弹性体涂料包含氧化锌的白色不透明颜料预油漆的制备。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(50.5%固体,Tg=-16℃,Rhoplex2438-Rohm 177.11and Haas)水 278.10分散剂(Tamol2001-Rohm and Haas) 26.99分散剂(TritonX-405-Union Carbide) 10.00消泡剂(Nopco NXZ) 5.00碱-氨(28%) 3.94凝结剂(Texanol) 2.68流变改进剂(AcrysolSCT-275) 5.00颜料-氧化锌(XX-503-Zinc Corporation of America) 283.26颜料-二氧化钛(Ti-Pure R-706-DuPont) 1133.50
获得的预油漆具有100加仑的总体积,1,925.58lbs.的总重量,80.00%的总PVC,67.90%的二氧化钛PVC,50.00%的体积固体,78.22%的重量固体,19.2558lbs./加仑的密度,在颜料固体上0.80%分散剂,和在胶乳固体上3.0%凝结剂。
实施例38
此实施例描述用于弹性体涂料的体质颜料预油漆的制备。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)水 295.80分散剂(TamolTM731A-Rohm and Haas) 10.82消泡剂(NopcoTMNXZ) 13.36碱-氨(28%) 6.68凝结剂(Texanol) 1.79流变改进剂(Natrosol 250HR) 1.00漆基丙烯酸类(50.5%固体,Tg=-16℃,RhoplexTM2438-Rohm 177.11and Haas)颜料-碳酸钙(DuramiteTM) 901.50
获得的预油漆具有100加仑的总体积,1,408.05lbs.的总重量,80.00%的总PVC,50.00%的体积固体,70.38%的重量固体,14.0805lbs./加仑的密度,在颜料固体上0.30%分散剂,和在胶乳固体上2.0%凝结剂。
实施例39
此实施例描述具有良好低温柔韧性的低Tg丙烯酸类漆基预油漆的制备。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(50.5%固体,Tg=-16 814.71℃,Rhoplex2438-Rohm and Haas)消泡剂(Nopco NXZ) 1.33流变改进剂(Natrosol 250HR) 5.32溶剂-丙二醇 26.62碱-氨(28%) 2.66凝结剂(Texanol) 8.23水 6.06
获得的预油漆应当具有100加仑的总体积,864.93lbs.的总重量,46.00%的体积固体,47.57%的重量固体,8.6493lbs./gal.的密度,和在胶乳固体上2.0%凝结剂。
实施例40
此实施例描述具有仅低到-5℃的低温柔韧性的中等范围Tg苯乙烯/丙烯酸类漆基预油漆的制备。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-5 803.91℃,Rhoplex2019R-Rohm and Haas)消泡剂(Nopco NXZ) 1.33流变改进剂(Natrosol 250 HR) 5.32溶剂-丙二醇 26.62碱-氨(28%) 2.66凝结剂(Texanol) 8.84水 10.99
获得的预油漆应当具有100加仑的总体积,859.69lbs.的总重量,50.00%的体积固体,51.43%的重量固体,8.5969lbs./gal.的密度,和在胶乳固体上2.0%凝结剂。
实施例41
此实施例描述具有差的低温柔韧性的高Tg(14℃)丙烯酸类漆基预油漆的制备。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(53.5%固体,Tg=14℃MultilobeTM200-Rohm 822.40and Haas)消泡剂(Nopco NXZ) 1.33流变改进剂(Natrosol 250HR) 5.32溶剂-丙二醇 26.62碱-氨(28%) 2.66凝结剂(Texanol) 26.40水 0.36
获得的预油漆应当具有100加仑的总体积,885.11lbs.的总重量,47.00%的体积固体,49.71%的重量固体,8.8511lbs./gal.的密度,和在胶乳固体上6.0%凝结剂。
实施例42
此实施例描述使用实施例36和37的白色颜料预油漆,实施例38的增量剂预油漆,和实施例39,40和41的漆基预油漆的不同结合,11种具有改变质量和耐霉菌性的弹性体墙壁涂料配方的制备。通过如下方式配制油漆:将白色颜料预油漆和增量剂预油漆加入到漆基预油漆中和充分混合。
表1:混合在一起的预油漆数量如下所示。所有的重量以lbs.计,每种弹性体涂料的总体积是100加仑,配制到45%体积固体。
实施例预油漆的重量 | ||||||||
油漆 | 36 | 37 | 38 | 39 | 40 | 41 | 水 | 总计 |
42-1 | 70.9 | 0.0 | 419.8 | 528.8 | 0.0 | 0.0 | 42.4 | 1061.9 |
42-2 | 0.0 | 89.3 | 409.9 | 528.8 | 0.0 | 0.0 | 42.4 | 1070.5 |
42-3 | 70.9 | 0.0 | 657.4 | 370.2 | 0.0 | 0.0 | 54.6 | 1153.1 |
42-4 | 0.0 | 89.3 | 647.5 | 370.2 | 0.0 | 0.0 | 54.6 | 1161.6 |
42-5 | 131.7 | 0.0 | 372.3 | 528.8 | 0.0 | 0.0 | 42.4 | 1075.2 |
42-6 | 0.0 | 165.9 | 353.9 | 528.8 | 0.0 | 0.0 | 42.4 | 1091.0 |
42-7 | 131.7 | 0.0 | 609.9 | 370.2 | 0.0 | 0.0 | 54.6 | 1166.3 |
42-8 | 0.0 | 165.9 | 591.5 | 370.2 | 0.0 | 0.0 | 54.6 | 1182.2 |
42-9 | 70.9 | 0.0 | 419.8 | 0.0 | 483.6 | 0.0 | 83.0 | 1057.3 |
42-10 | 0.0 | 89.3 | 647.5 | 0.0 | 338.5 | 0.0 | 83.0 | 1158.3 |
42-11 | 70.9 | 0.0 | 657.4 | 227.5 | 0.0 | 141.6 | 58.7 | 1014.5 |
表2:获得的弹性体涂料的期望PVC,TiO2水平,低温柔韧性,和质量如下所示。
油漆 | PVC | ZnO存在 | TiO2PVC | 弯曲 | 质量 |
42-1 | 30 | 否 | 3.5 | 0°F | 中等 |
42-2 | 30 | 是 | 3.5 | 0°F | 中等 |
42-3 | 45 | 否 | 3.5 | 0°F | 低 |
42-4 | 45 | 是 | 3.5 | 0°F | 低 |
42-5 | 30 | 否 | 6.5 | 0°F | 高 |
42-6 | 30 | 是 | 6.5 | 0°F | 高 |
42-7 | 45 | 否 | 6.5 | 0°F | 中等 |
42-8 | 45 | 是 | 6.5 | 0°F | 中等 |
42-9 | 30 | 否 | 3.5 | 20°F | 中等 |
42-10 | 45 | 是 | 3.5 | 20°F | 低 |
42-11 | 45 | 否 | 3.5 | 40°F | 差 |
如上所示的弹性体涂料制备表示质量的范围依赖于在低温下的耐用性和柔韧性。这些实施例不是限制性的。例如,所有的颜料和增量剂预油漆可以与或不与漆基配制,和漆基可具有比在这些实施例中使用的更高Tg。此外,增量剂预油漆并不表示限制到使用碳酸钙,但用于表示也包括其它通常使用的增量剂,如粘土、二氧化硅、硅酸镁等的例子。
用于屋顶的弹性体涂料可以用于墙壁的弹性体涂料的相同方式区分,具有两个另外的变化,官能增量剂如三水合铝的使用以促进阻燃性,和对于具体作屋顶基材的增强粘合力。以下实施例用于显示当应用到弹性体屋顶涂料时预油漆概念的能力,和不用于限制。
实施例43
此实施例描述白色颜料预油漆的制备,预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-29 159.75℃,RhoplexEC-1791-Rohm and Haas)水 268.95分散剂(Tamol165A-Rohm and Haas) 49.24消泡剂(Nopco NXZ) 12.44碱-氨(28%) 3.94凝结剂(Texanol) 2.64流变改进剂(AcrysolSCT-275) 10.00颜料-二氧化钛(Ti-Pure R-960-DuPont) 1292.48
使用高速分散器制备预油漆。将水,分散剂,丙烯酸类漆基,消泡剂,碱,和流变改进剂结合和在低速下简单混合和加入干燥颜料。在加入所有干燥颜料之后,如对于本领域技术人员是已知的那样,应当将混合物在高速下分散15-20分钟。
获得的预油漆应当具有100加仑的总体积,1,799.45lbs.的总重量,80.00%的总PVC,50.00%的体积固体,76.71%的重量固体,17.9945lbs./加仑的密度,和在颜料固体上0.80%分散剂,和在胶乳固体上3.0%凝结剂。
实施例44
此实施例描述白色不透明预油漆的制备,预油漆用于制备具有对沥青屋顶材料良好粘合力的涂料。预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-8℃,Lipacryl 160.69MB-3640-Rohm and Haas)水 268.12分散剂(Tamol165A-Rohm and Haas) 49.24消泡剂(Nopco NXZ) 12.44碱-氨(28%) 3.94凝结剂(Texanol) 2.65流变改进剂(AcrysolSCT-275) 10.00颜料-二氧化钛(Ti-Pure R-960-DuPont) 1292.48
如实施例43所示,使用高速分散器制备预油漆。获得的预油漆应当具有100加仑的总体积,1,799.56lbs.的总重量,80.00%的总PVC,50.00%的体积固体,76.73%的重量固体,17.9956lbs./加仑的密度,和在颜料固体上0.80%分散剂,和在胶乳固体上3.0%凝结剂。将此预油漆设计成在用于沥青基材的涂料中工作最好。
实施例45
此实施例描述包含氧化锌的白色不透明预油漆的制备。预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-29 159.75℃,RhoplexEC-1791-Rohm and Haas)水 272.67分散剂(Tamol731A-Rohm and Haas) 44.09分散剂(TritonX-405-Union Carbide) 10.00消泡剂(Nopco NXZ) 5.00碱-氨(28%) 3.94凝结剂(Texanol) 2.64流变改进剂-(AcrysolSCT-275) 12.00颜料-氧化锌(XX-503-Zinc Corporation of America) 275.47颜料-二氧化钛(Ti-Pure R-960-DuPont) 1102.32
获得的预油漆应当具有100加仑的总体积,1,887.88lbs.的总重量,80.00%的总PVC,68.23%的氧化钛PVC,50.00%的体积固体,77.63%的重量固体,18.8788lbs./加仑的密度,和在颜料固体上0.80%分散剂,和在胶乳固体上3.0%凝结剂。
实施例46
此实施例描述用于弹性体涂料的体质颜料预油漆的制备。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)水 310.92分散剂(Tamol 731A-Rohm and Haas) 10.82消泡剂(NopcoNXZ) 13.36碱-氨(28%) 6.68凝结剂(Texanol) 1.76流变改进剂(Natrosol 250HR) 2.00漆基丙烯酸类(55.0%固体,Tg=-29 159.75℃,RhoplexEC-1791-Rohm and Haas)颜料-碳酸钙(Duramite) 901.50
获得的预油漆具有100加仑的总体积,1,406.78lbs.的总重量,80.00%的总PVC,50.00%的体积固体,70.33%的重量固体,14.0678lbs./加仑的密度,在颜料固体上0.30%分散剂,和在胶乳固体上2.0%凝结剂。
实施例47
此实施例描述体质颜料预油漆的制备,预油漆用于制备具有对沥青屋顶材料良好粘合力的涂料。预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)水 310.09分散剂(Tamol731A-Rohm and Haas) 10.82消泡剂(NopcoNXZ) 13.36碱-氨(28%) 6.68凝结剂(Texanol) 1.77流变改进剂(Natrosol 250HR) 2.00漆基丙烯酸类(55.0%固体,Tg=-8 160.69℃.LipacrylMB-3640-Rohm and Haas)颜料-碳酸钙(Duramite) 901.50
获得的预油漆具有100加仑的总体积,1,406.90lbs.的总重量,80.00%的总PVC,50.00%的体积固体,70.36%的重量固体,l4.0690lbs./加仑的密度,在颜料固体上0.30%分散剂,和在胶乳固体上2.0%凝结剂。
实施例48
此实施例描述使用三水合铝,体质颜料预油漆的制备,已知三水合铝可赋予阻燃性能。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)水 311.61分散剂(Tamol731A-Rohm and Haas) 9.70消泡剂(Nopco NXZ) 13.36碱-氨(28%) 6.68凝结剂(Texanol) 1.76流变改进剂(Natrosol 250HR) 2.00漆基丙烯酸类(55.0%固体,Tg=-29℃, 159.75RhoplexEC-1791-Rohm and Haas)颜料-三水合铝(Solem SB-432Huber) 807.94
获得的预油漆具有100加仑的总体积,1,312.79lbs.的总重量,80.00%的总PVC,50.00%的体积固体,68.24%的重量固体,13.1279lbs./加仑的密度,在颜料固体上0.30%分散剂,和在胶乳固体上2.0%凝结剂。
实施例49
此实施例描述低Tg丙烯酸类漆基预油漆的制备,预油漆应当具有良好的低温柔韧性和对各种屋顶基材良好的粘合力。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-29 798.75℃,RhoplexEC-1791-Rohm and Haas)消泡剂(Nopco NXZ) 1.33流变改进剂(Natrosol 250HR) 5.32溶剂-丙二醇 26.62碱-氨(28%) 2.66凝结剂(Texanol) 8.79水 16.45
获得的预油漆应当具有100加仑的总体积,859.93lbs.的总重量,50.00%的体积固体,51.09%的重量固体,8.5993lbs./gal.的密度,和在胶乳固体上2.0%凝结剂。
实施例50
此实施例描述中等范围Tg丙烯酸类漆基预油漆的制备,预油漆应当具有对沥青屋顶基材良好的粘合力。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-8 803.45℃,LipacrylMB-3640-Rohm and Haas)消泡剂(Nopco NXZ) 1.33流变改进剂(Natrosol 250HR) 5.32溶剂-丙二醇 26.62碱-氨(28%) 2.66凝结剂(Texanol) 8.84水 12.29
获得的预油漆应当具有100加仑的总体积,860.52lbs.的总重量,50.00%的体积固体,51.35%的重量固体,8.6052lbs./gal.的密度,和在胶乳固体上2.0%凝结剂。
实施例51
此实施例描述用于弹性体涂料包含氧化锌的黄褐色颜料预油漆的制备。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)漆基丙烯酸类(55.0%固体,Tg=-29 143.78℃,RhoplexEC-1791-Rohm and Haas)水 307.35分散剂(Tamol731A-Rohm and Haas) 30.07分散剂(TritonX-405-Union Carbide) 10.00消泡剂(Nopco NXZ) 5.00碱-氨(28%) 3.94凝结剂(Texanol) 2.37流变改进剂(AcrysolSCT-275) 40.00颜料-氧化锌(XX-503-Zinc Corporation of America) 480.33颜料-黄褐色氧化铁(Mapico422) 1023.06
获得的预油漆具有100加仑的总体积,2,045.89lbs.的总重量,80.00%的总PVC,45.00%的体积固体,77.35%的重量固体,20.4589lbs./加仑的密度,在颜料固体上0.50%分散剂,和在胶乳固体上3.0%凝结剂。
实施例52
此实施例描述使用结晶二氧化硅,体质颜料预油漆的制备,已知结晶二氧化硅可提供良好的耐用性和耐磨性。如上所述预油漆通过结合如下成分制备:成分
数量(lbs./100加仑)水 296.22分散剂(Tamol731A-Rohm and Haas) 26.54消泡剂(NopcoNXZ) 13.36碱-氨(28%) 6.68凝结剂(Texanol) 1.76流变改进剂(Natrosol 250HR) 2.00漆基丙烯酸类(55.0%固体,Tg=-29 159.75℃,RhoplexEC-1791-Rohm and Haas)二氧化硅增量剂(Silver Bond B) 884.81
获得的预油漆应当具有100加仑的总体积,1,391.11lbs.的总重量,80.00%的总PVC,50.00%的体积固体,69.92%的重量固体,13.9111lbs./加仑的密度,在颜料固体上0.75%分散剂,和在胶乳固体上2.0%凝结剂。
实施例53
此实施例描述15种具有变化质量,柔韧性,粘合力和阻燃性的弹性体屋顶涂料配方的制备。使用实施例43,44和45的白色预油漆,实施例16的非白色颜料预油漆,实施例46,47,48的52的增量剂预油漆和实施例40,49和50的漆基预油漆的不同结合,配制涂料。通过如下方式配制油漆:将颜料预油漆和增量剂预油漆加入到漆基预油漆中和充分混合。混合的数量是以下引用的那些。所有的重量是以lbs.计,和每种弹性体涂料的总体积是100加仑。体积固体是45%。
实施例预油漆的重量油漆 43 44 45 51 46 47 48 52 40 49 50 水 总计53-1 70.9 - - - 419.4 - - - - 483.7 - 83 1057.053-2 - - 87.2 - 409.8 - - - - 483.7 - 83 1063.753-3 70.9 - - - 656.8 - - - - 338.6 - 83 1149.253-4 - - 87.2 - 647.2 - - - - 338.6 - 83 1156.053-5 131.6 - - - 371.9 - - - - 483.7 - 83 1070.253-6 - - 161.9 - 354.2 - - - - 483.7 - 83 1082.753-7 131.6 - - - 609.3 - - - - 338.6 - 83 1162.553-8 - - 161.9 - 591.6 - - - - 338.6 - 83 1175.053-9 70.9 - - - - - 391.4 - - 483.7 83 83 1028.953-10 - - 88.9 - - - 647.8 - - 338.5 - 83 1158.253-11 91.1 - - - 403.6 - - - 483.6 - - 83 1061.253-12 - - 112.1 - 628.7 - - - 338.5 - - 83 1162.253-13 - 131.6 - - - 530.2 - - - - 387.2 83 1132.153-14 131.6 - - - 530.2 - - - 387.2 - - 83 1132.053-15 - - - 179.0 - - - 548.0 - 368.0 - 76 1171.0
获得的弹性体涂料混合物的期望PVC,TiO2水平,低温柔韧性,增量剂类型,和特殊粘合的存在,和质量见表3油漆 PVC ZnO TiO2PVC 颜色 增量剂 弯曲温度 特殊粘合 质量53-1 30 否 3.5 白色 CaCO3 -15°F 各种 中等53-2 30 是 3.5 白色 CaCO3 -15°F 各种 中等53-43 45 否 3.5 白色 CaCO3 15°F 各种 低53-4 45 是 3.5 白色 CaCO3 -15°F 各种 低53-5 30 否 6.5 白色 CaCO3 -15°F 各种 高53-6 30 是 6.5 白色 CaCO3 -15°F 各种 高53-7 45 否 6.5 白色 CaCO3 -15F15°F 各种 中等53-8 45 是 6.5 白色 CaCO3 -15°F 各种 中等53-9 30 否 3.5 白色 ATH -15°F 各种 中等53-10 45 是 3.5 白色 ATH -15°F 各种 低53-11 30 否 4.5 白色 CaCO3 20°F 各种 中等53-12 45 是 4.5 白色 CaCO3 20°F 各种 低53-13 40 否 6.5 白色 CaCO3 20°F 沥青 中等53-14 40 否 6.5 白色 CaCO3 20°F 沥青共混物 中等53-15 42 是 0 tan silica -15°F 各种 中等
以上所示的弹性体涂料表示质量的范围依赖于涂料在低温下的耐用性和柔韧性。不同增量剂预油漆用于促进干燥涂料中的阻燃性。包括的是使用干燥研磨的着色剂和没有TiO2制备的预油漆以开发染色油漆。这些实施例不是限制性的。例如,所有的颜料和增量剂预油漆可以与或不与漆基配制,和漆基可具有比在这些实施例中使用的更高Tg。此外,增量剂预油漆并不表示限制到使用碳酸钙,但用于表示也包括其它通常使用的增量剂,如粘土、二氧化硅、硅酸镁等的例子。
实施例54
此实施例描述白色颜料预油漆/预配制组分的制备。
成分
数量(lbs./100加仑)
水 275.83
溶剂-丙二醇 50.00
分散剂(Tamol731A-Rohm and Haas) 26.71
消泡剂(Nopco NXZ) 1.50
表面活性剂(TritonCF-10) 1.00
颜料-二氧化钛(Ti-PureR-902-DuPont) 1335.56
碱-氨(28%) 4.00
消泡剂(Nopco NXZ) 1.50
增稠剂(AcrysolRM-2020 NPR-Rohm and Haas) 50.00
水 93.45
将水,二醇,消泡剂,分散剂和表面活性剂结合和在低速下简单地混合。然后加入干燥颜料。在加入所有干燥颜料之后,如对于本领域技术人员是已知的那样,应当将混合物在高速下分散15-20分钟。
获得的白色预油漆/预配方应当具有100加仑的总体积,1,839.55lbs.的总重量,100.00%的总PVC,40.12%的体积固体,72.60%的重量固体,18.4495lbs./加仑的密度,和在颜料固体上0.50%分散剂。
实施例55
此实施例描述小粒度增量剂预油漆/预配制组分的制备。
成分
数量(lbs./100加仑)
漆基丙烯酸类(46.5%固体,Tg=17 201.32
℃)(RhoplexEI-2000-Rohm and Haas)
溶剂-丙二醇 5.00
分散剂(Tamol731A-Rohm and Haas) 10.42
消泡剂(Nopco NXZ) 2.00
增稠剂#1(Attagel 50) 27.96
小粒度增量剂(Minex 4) 840.53
凝结剂(Texanol) 3.28
碱-氨(28%) 2.00水 283.42
增稠剂#2(AcrysolASE-60-Rohm and Haas) 4.00
将水,丙烯酸类漆基,消泡剂,碱,和二醇结合和在低速下简单地混合。然后加入干燥颜料。在加入所有干燥颜料之后,如对于本领域技术人员是已知的那样,应当将混合物在高速下分散15-20分钟。
获得的白色预油漆/预配方应当具有100加仑的总体积,1,379.93lbs.的总重量,80.00%的总PVC,50.00%的体积固体,69.72%的重量固体,13.7993lbs./加仑的密度,在颜料固体上0.30%分散剂,和在胶乳固体上3.50%凝结剂。
实施例56
此实施例描述漆基预油漆/预配方的制备。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(46.5%固体,Tg=17℃Rhoplex 805.28EI-2000-Rohm and Haas)消泡剂(Nopco NXZ) 1.33增稠剂(AcrysolASE-60-Rohm and Haas) 20.00溶剂-丙二醇 10.00碱-氨(28%) 2.66凝结剂(Texanol) 13.11水 21.92
获得的漆基预油漆/预配制包装物应当具有100加仑的总体积,874.31lbs.的总重量,40.00%的体积固体,42.83%的重量固体,8.7431lbs./加仑的密度,和在胶乳固体上3.50%凝结剂。
实施例57
此实施例描述用于主好低温柔韧性的漆基预油漆/预配方的制备。使用具有45°节距搅拌叶片的实验室混合器制备预油漆。成分
数量(lbs./100加仑)漆基丙烯酸类(61%固体,Tg=-29℃ Rhoplex 584.20EC-2848-Rohm and Haas)消泡剂(Nopco NXZ) 1.33增稠剂(AcrysolASE-60-Rohm and Haas) 20.00溶剂-丙二醇 10.00碱-氨(28%) 2.66凝结剂(Texanol) 12.47水 226.92
获得的预配制包装物应当具有100加仑的总体积,857.59lbs.的总重量,40.00%的体积固体,41.55%的重量固体,8.5759lbs./加仑的密度,和在胶乳固体上3.50%凝结剂。
实施例58
此实施例描述用于向凝集体面漆提供细纹理的小粒度凝集体的制备。成分
数量(lbs./100加仑)砂-小粒度(砂#90) 2,211.18
获得的预配制包装物应当具有100加仑的总体积,2,211.18lbs.的总重量,100.00%的体积固体,100.00%的重量固体,22.1118lbs./加仑的密度。
实施例59
此实施例描述提供粗纹理的预配制大粒度凝集体的制备。它使用螺带混合器制备。成分
数量(lbs./100加仑)砂-大粒度(砂#15) 442.24砂-小粒度(砂#90) 1768.94
获得的预配制包装物应当具有100加仑的总体积,2,211.18lbs.的总重量,100.00%的体积固体,100.00%的重量固体,22.1118lbs./加仑的密度。
实施例60
此实施例描述19种具有变化质量,颜色强度,和纹理的凝集体面漆配方的制备。为制备这些不同的凝集体面漆,在各种比例下使用实施例55的小粒度增量剂预配方,实施例56和57的漆基预配方,实施例54的白色颜料预油漆,和实施例58和59的大粒度凝集体的不同结合物。通过如下方式配制凝集体面漆:将小粒度增量剂预配方加入到漆基预配方中和然后如需要加入白色颜料预油漆,和最后加入水和大粒度凝集体。使用螺带混合器将组分完全混合。混合的数量是如下所示的那些。所有的重量以lbs.计,每种凝集体面漆的总体积是100加仑,配制到67%体积固体。
使用实施例54-57的预配方,以及大粒度凝集体如在实施例58和59中的那些的混合物,制备九种不同的凝集体面漆。
实施例预油漆的重量 | 水 | 总计 | ||||||
油漆 | 55 | 56 | 57 | 58 | 59 | 54 | ||
60-1 | 64.72 | 429.09 | 995.56 | 0.00 | 10.03 | 1499.40 | ||
60-2 | 41.60 | 432.75 | 995.56 | 30.90 | 6.55 | 1507.11 | ||
60-3 | 6.93 | 438.24 | 995.56 | 77.26 | 1.34 | 1518.66 | ||
60-4 | 180.29 | 337.56 | 995.56 | 0.00 | 27.41 | 1540.82 | ||
60-5 | 157.17 | 341.22 | 995.56 | 30.90 | 23.93 | 1548.52 | ||
60-6 | 122.50 | 346.71 | 995.56 | 77.26 | 18.72 | 1560.08 | ||
60-7 | 295.86 | 246.03 | 995.56 | 0.00 | 44.79 | 1582.24 | ||
60-8 | 272.74 | 249.69 | 995.56 | 30.90 | 41.31 | 1589.94 | ||
60-9 | 238.07 | 255.18 | 995.56 | 77.26 | 36.10 | 1601.50 | ||
60-10 | 122.50 | 340.08 | 995.56 | 77.26 | 18.72 | 1553.45 | ||
60-11 | 64.72 | 429.09 | 995.56 | 0.00 | 10.03 | 1499.40 | ||
60-12 | 41.60 | 432.75 | 995.56 | 30.90 | 6.55 | 1507.11 | ||
60-13 | 6.93 | 438.24 | 995.56 | 77.26 | 1.34 | 1518.66 | ||
60-14 | 180.29 | 337.56 | 995.56 | 0.00 | 27.41 | 1540.82 | ||
60-15 | 157.17 | 341.22 | 995.56 | 30.90 | 23.93 | 1548.52 | ||
60-16 | 122.50 | 346.71 | 995.56 | 77.26 | 18.72 | 1560.08 | ||
60-17 | 295.86 | 246.03 | 995.56 | 0.00 | 44.79 | 1582.24 | ||
60-18 | 272.74 | 249.69 | 995.56 | 30.90 | 41.31 | 1589.94 | ||
60-19 | 238.07 | 255.18 | 995.56 | 77.26 | 36.10 | 1601.50 |
获得的凝集体面漆涂料配方的PVC,TiO2水平,期望的颜色强度,纹理,和低温柔韧性如下所示。
油漆 | PVC | TiO2PVC | 纹理 | 弯曲 | 颜色色调 | 质量 |
60-1 | 70 | 0 | 细 | 40°F | 深 | 高 |
60-2 | 70 | 1 | 细 | 40°F | 中等色调 | 高 |
60-3 | 70 | 2.5 | 细 | 40°F | 柔和 | 高 |
60-4 | 75 | 0 | 细 | 40°F | 深 | 中等 |
60-5 | 75 | 1 | 细 | 40°F | 中等色调 | 中等 |
60-6 | 75 | 2.5 | 细 | 40°F | 柔和 | 中等 |
60-7 | 80 | 0 | 细 | 40°F | 深 | 低 |
60-8 | 80 | 1 | 细 | 40°F | 中等色调 | 低 |
60-9 | 80 | 2.5 | 细 | 0°F | 柔和 | 低 |
60-10 | 75 | 2.5 | 细 | 40°F | 柔和 | 中等 |
60-11 | 70 | 0 | 粗 | 40°F | 深 | 高 |
60-12 | 70 | 1 | 粗 | 40°F | 中等色调 | 高 |
60-13 | 70 | 2.5 | 粗 | 40°F | 柔和 | 高 |
60-14 | 75 | 0 | 粗 | 40°F | 深 | 中等 |
60-15 | 75 | 1 | 粗 | 40°F | 中等色调 | 中等 |
60-16 | 75 | 2.5 | 粗 | 40°F | 柔和 | 中等 |
60-17 | 80 | 0 | 粗 | 40°F | 深 | 低 |
60-18 | 80 | 1 | 粗 | 40°F | 中等色调 | 低 |
60-19 | 80 | 2.5 | 粗 | 40°F | 柔和 | 低 |
以上所示的凝集体面漆涂料表示质量,纹理,和着色能力的范围依赖于大粒度增量剂的PVC,TiO2水平,和粒度比例。这些配方不是通过实施例加以限制。例如,可以没有漆基配制所有的增量剂预油漆/配方。此外,增量剂预油漆/配方并不表示限于使用霞石正长岩,但用于显示包括其它通常使用的增量剂如粘土、二氧化硅、硅酸镁、碳酸钙等的例子。TiO2淤浆可以加入到增量剂预油漆/配方中。
实施例61
以下预油漆应当提供用于木材的涂料系列油漆,包括包含不透明颜料的涂料(“着色涂料”)和不包含不透明颜料或颜料上增量剂的涂料(“透明涂料”)。
通过将7979g的Rhoplex CL-104漆基加入到容器中制备漆基预油漆1。采用良好的搅拌,然后加入800g乙二醇单丁基醚,240g二丙二醇单丁基醚,和1800g水。
通过将6636g的Rhoplex CL-105漆基加入到容器中制备漆基预油漆2。采用良好的搅拌,然后加入800g乙二醇单丁基醚,240g二丙二醇单丁基醚,和1800g水。
通过将760g的RoShield3188漆基加入到容器中制备漆基预油漆3。采用良好的搅拌,然后加入400g乙二醇单丁基醚,120g二丙二醇单丁基醚,900g水,和100g的ParaplexTMWP-1聚(环氧丙烷),单酚基醚(Rohm and Haas Company,费城,PA)。
在搅拌下,通过共混如下物质制备添加剂预油漆1∶70g的TegoFoamex 805消泡剂,30g的Tego GlideTM410(在Dowanol DPM溶剂中50%)蜡(Tego Chemie Service),30g的SurfynolTM 104DPM表面活性剂,25g的AcrysolTMRM-825 HASE增稠剂,和200g的Michem Emulsion39235。
按如下在Cowles混合器中制备二氧化钛预油漆:研磨
重量(磅)
体积(加仑)水 282.96 33.90Tamol 731TM分散剂 58.51 6.35TritonTMCF-10表面活性剂 2.19 0.25KathonTMLX1.5%杀虫剂 2.19 0.26Ti-PureTMR-706二氧化钛 1462.80 43.81调漆氨(28%) 0.66 0.09AcrvsolTM调漆RM-2020 NPR HEUR增稠剂
54.76
6.29总计 1939.64 100.00
用于木材的通用目的顶涂层 | 用于木材的耐溶剂顶涂层 | 用于板的涂料 | 热固性涂料 | |||||||||||||||
A | B | C | D | E | F | G | H | I | J | K | L | M | N | O | ||||
以克计的所有数量 | 光泽 | 无光的 | DIY光泽 | DIY无光 | 白色光泽 | 光泽 | 无光的 | DIY光泽 | DIY无光 | 白色光泽 | 光泽 | 无光的 | 擦拭污渍 | 外部高构造着色 | 白色 | |||
漆基预油漆1 | 10,810 | 10,810 | 10,810 | 10,810 | 7000 | - | - | - | - | - | - | - | - | - | - | |||
漆基预油漆2 | - | - | - | - | - | - | - | - | - | - | 9476 | 9476 | 6120 | 6120 | - | |||
漆基预油漆3 | - | - | - | - | - | 9200 | 9200 | 9200 | 9200 | 6550 | - | - | - | - | - | |||
漆基RhoplexAC-1024 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | 3945 | |||
添加剂预油漆1 | 896 | 896 | 800 | 800 | 258 | 800 | 800 | 800 | 800 | 258 | 200 | 200 | - | - | 1700 | |||
TiO2预油漆 | - | - | - | 1520 | - | - | - | - | 1520 | - | - | - | - | - | 1192 | - | ||
平光剂SyloidTM7000 | - | 120 | - | 120 | - | - | 120 | - | 120 | - | - | 120 | - | - | - | |||
预分散的颜料AquasperseBurntUmber877-1314 | - | - | - | - | - | - | - | - | - | - | - | - | 772 | 772 | - | |||
凝结剂丙二醇 | - | - | - | - | - | - | - | - | - | - | - | - | 258 | 258 | - | |||
水 | - | - | - | - | - | - | - | - | - | - | - | - | 2573 | 2573 | 983 | |||
凝结剂己基卡必醇 | - | - | 400 | 400 | - | - | - | 300 | 300 | - | - | - | - | - | - | |||
增稠剂AcrysolTMRM-2020NPR | - | - | 180 | 180 | - | - | - | 120 | 120 | - | - | - | 86 | 160 | - |
AC-1024,白色,热固性配方-采用在总配方上1973g下的尿甲醛树脂使用
这些配方也可用作在硬纸板,MDF,夹板,取向条板上的着色物和透明物。
实施例62
将以下预油漆制备和用于配制用于金属基材的涂料系列油漆,它典型地用于维修或原始设备制造应用:
预油漆配方
(磅/100加仑)
成分 | TiO2预油漆 | 增量剂预油漆1 | 增量剂预油漆2 | 增量剂预油漆3 | 漆基预油漆 |
Dowanol TMDPM酯溶剂 | 116.9 | 79.15 | 98.0 | 82.2 | - |
水 | 227.3 | 302.8 | 190.1 | 314.3 | - |
TamolTM 165A分散剂 | 64.95 | 43.97 | 54.19 | 45.64 | - |
TritonTMCF-10表面活性剂 | 6.5 | 4.4 | 5.5 | 4.6 | - |
TegofoamexTM1488消泡剂 | 9.7 | 6.6 | 8.3 | 6.9 | - |
Ti-PureTMR-706TiO2 | 1266.4 | - | - | - | - |
2610Lo MicronTM滑石 | - | 857.5 | - | - | - |
AlbaglosTMCaCO3 | - | - | 1062.6 | - | - |
HaloxTMSZP-391反应性颜料(Halox,Inc.,Hammond,IN) | - | - | - | 889.9 | - |
氨15% | 2.8 | 1.9 | 2.4 | 1.9 | - |
水 | 32.5 | 21.9 | 27.5 | 22.8 | 31.45 |
KathonTMLX杀虫剂 | 2.1 | 1.4 | 1.6 | 1.5 | - |
AcrysolTMRM-2020NPR HEUR增稠剂 | 56.1 | 56.1 | 56.1 | - | - |
NatrasolTM250GR(4%)HEC增稠剂 | - | - | - | 58.3 | - |
MaincoteTMHG-54D漆基 | - | - | - | - | 754.8 |
TexanolTM凝结剂 | - | - | - | - | 47.17 |
15%硝酸钠 | - | - | - | - | 10.48 |
氨15% | - | - | - | - | 5.24 |
AcrysolTMRM-8W HASE增稠剂 | - | - | - | - | 2.62 |
pH=~8.5-9
粘度=90-110KU
Hegmen在用于该等级颜料的具体范围研磨。
可以结合以上预油漆以形成以下用于金属的涂料系列油漆:
产物 | 高PVC白色底漆 | 光泽白色 | 低光泽白色 | 低光泽透明顶部 | 透明顶涂层 |
组分 | wt% | wt% | wt% | wt% | wt% |
TiO2预油漆 | 10.1 | 13 | 12.5 | - | - |
增量剂预油漆1 | 5.4 | - | - | - | - |
增量剂预油漆2 | 6.1 | - | 4.2 | 2.9 | - |
增量剂预油漆3 | 10.8 | - | - | - | - |
漆基预油漆 | 57.6 | 87 | 83.3 | 97.1 | 100 |
PVC | 31.89 | 17.82 | 13.98 | 3.37 | - |
固体-体积 | 34.67 | 35.56 | 35.41 | 35.19 | 35.02 |
固体-重量 | 48.31 | 46.01 | 44.96 | 38.11 | 36.78 |
实施例63
可以从共混原材料的有限套漆(“预油墨”或“预油漆”)生产形象艺术油墨系。按如下制备预油漆:
预油漆1(“硬漆基预油漆”)通过如下方式制备:将94份Lucidene370聚合物(Rohm and Haas Company)加入到容器中。采用良好的搅拌,加入5份Luciwax 37蜡(Rohm and Haas Company)和1份消泡剂。
预油漆2(“中等Tg漆基预油漆”)通过如下方式制备:将94份Lucidene615聚合物(Rohm and Haas Company)加入到容器中。采用良好的搅拌,加入5份Luciwax37蜡(Rohm and Haas Company)和1份消泡剂。
预油漆3(“软漆基预油漆”)通过如下方式制备:将89份Lucidene605聚合物(Rohm and Haas Company)加入到容器中。采用良好的搅拌,加入5份Luciwax37蜡(Rohm and Haas Company),1份消泡剂和5份异丙醇。
预油漆4(“碱溶性树脂添加剂预油漆”)是Morcryl 132树脂(Rohmand Haas Company),以在32%固体和pH8.5下提供的方式使用。
预油漆5(“光泽添加剂预油漆”)是Morcryl 350树脂(Rohm andHaas Company),以在50%固体和pH9.0下提供的方式使用。
预油漆6(“蜡添加剂预油漆”)是Michem Lube 743蜡(Michelman,Inc.),以在32%固体和pH7下提供的方式使用。
使用颜料分散体,如在约40%固体下提供,以多个颜色的SunFlexiverse Dispersion(Sun Chemical Co),将颜色加入到油墨中。
在下表中描述形象艺术油墨系。每种产品通过采用良好搅拌将指示的材料(以克计的重量)共混而制备。如需要采用另外的水和或异丙醇调节最终的粘度。当指示材料对共混物的范围时,可以获得最终产物中性能的范围。例如,在用于冰箱袋的油墨中使用最小水平的预油漆3会导致更好的低温耐起皱性。在大多数油墨中使用最高水平的预油漆4会导致在印刷机上更好的转印。
油墨产物 | 漆基预油漆1 | 漆基预油漆2 | 漆基预油漆3 | 添加剂预油漆4 | 添加剂预油漆5 | 添加剂预油漆6 | 颜料分散体 |
礼品包装纸 | 55-65 | - | - | 10-20 | - | - | 25-30 |
波纹箱 | 55-65 | - | - | 10-20 | - | 4-6 | 25-30 |
新闻纸 | 65-75 | - | - | - | - | - | 30 |
纸板 | 55-65 | - | - | - | 10-20 | - | 25-30 |
标签 | 28-33 | 28-33 | - | 10-20 | - | - | 25-30 |
冰箱袋 | - | - | 55-65 | 10-20 | - | - | 25-30 |
贮存袋 | - | - | 55-65 | - | 10-20 | - | 25-30 |
金属膜 | - | 28-33 | 28-33 | - | - | - | 25 |
箔 | - | 28-33 | 28-33 | - | 10-20 | - | 25-30 |
通用目的套印物 | - | 80 | - | 15-25 | - | - | - |
35-45 | - | 35-45 | - | 20 | - | - | |
耐水套印物 | - | 35-45 | 35-45 | 10-20 | - | - | - |
耐摩擦套印物 | - | 75-85 | - | 20 | - | 4-6 | - |
高滑动角套印物 | - | 80 | - | 15-25 | - | - | - |
供应商信息
材料名称 | 材料类型 | 供应商 |
TamolTM 1124 | 分散剂 | Rohm and Haas Company(费城,PA) |
TamolTM 1254 | 分散剂 | Rohm and Haas Company(费城,PA) |
TamolTM 731 | 分散剂 | Rohm and Haas Company(费城,PA) |
AcrysolTM DR-3 | HASE增稠剂/流变改进剂 | Rohm and Haas Company(费城,PA) |
AcrysolTM RM-2020 NPR | HEUR增稠剂/流变改进剂 | Rohm and Haas Company(费城,PA) |
AcrysolTM RM-8W | HEUR增稠剂/流变改进剂 | Rohm and Haas Company(费城,PA) |
AcrysolTM RM-825 | HEUR增稠剂/流变改进剂 | Rohm and Haas Company(费城,PA) |
RhoplexTM Multilobe 200 | 乳液聚合物漆基 | Rohm and Haas Company(费城,PA) |
RhoplexTM SG-10M | 乳液聚合物漆基 | Rohm and Haas Company(费城,PA) |
RES 3083 | 乳液聚合物漆基 | Rohm and Haas Company(费城,PA) |
KathonTM LX 1.5% | 杀虫剂 | Rohm and Haas Company(费城,PA) |
TritonTM CF-10 | 表面活性剂 | Union Carbide Company(Danbury,CT) |
FoamasterTM VL | 消泡剂 | Henkel Corporation(King of Prussia,PA) |
DrewplusTM L-475 | 消泡剂 | Drew Chemical Corporation(Kearny,NJ) |
Ti-PureTM R-746 | 二氧化钛 | E.I.Dupont de Nemours andCo.,Inc.(Wilmington,DE) |
Ti-PureTM R-706 | 二氧化钛 | E.I.Dupont de Nemours andCo.,Inc.(Wilmington,DE) |
Ti-PureTM R-900 | 二氧化钛 | E.I.Dupont de Nemours andCo.,Inc.(Wilmington,DE) |
Ti-PureTM R-902 | 二氧化钛 | E.I.Dupont de Nemours andCo.,Inc.(Wilmington,DE) |
MinexTM 4 | 矿物质增量剂 | Inimin Corp.(Dividing Creek,NJ) |
OptiwhiteTM | 粘土增量剂 | Burgess Pigment(Sandersville,GA) |
SnowflakeTM | 碳酸钙增量剂 | ECC International Zmerya(Sylacauga,AL) |
VicronTM 15-15 | 碳酸钙增量剂 | Pfizer(纽约,NY) |
OmyacarbTM | 碳酸钙增量剂 | Omya(Proctor,VI) |
TexanolTM | 凝结剂 | Eastman Chemical(Kings Port,TN) |
Claims (51)
1.一种足以形成至少一种油漆系的不同但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆。
2.权利要求1的预油漆的套漆,其中预油漆的数目是3-15。
3.权利要求1的预油漆的套漆,其中不透明预油漆进一步包括至少一种吸附在不透明颜料上的微粒聚合物漆基。
4.权利要求1的预油漆的套漆,其中增量剂预油漆进一步包括至少一种吸收在不透明颜料上的微粒聚合物漆基。
5.一种形成至少一种油漆系的方法,包括如下步骤:
(a)提供不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种不透明预油漆,包括至少一种不透明颜料;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
6.一种形成系列油漆的方法,该系列油漆包括至少两种油漆系,该方法包括如下步骤:
(a)提供足以配制至少两种油漆系的不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和
(iv)至少一种选自(i),(ii),和(iii)的另外,不同的不透明,增量剂,或漆基预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成系列油漆。
7.权利要求5的方法,进一步包括如下步骤:在将它们分配入容器之前,同时,或之后混合预油漆。
8.权利要求5的方法,进一步包括如下步骤:在将它们分配入涂敷器之前,同时,或之后混合预油漆。
9.权利要求5的方法,进一步包括如下步骤:在将它们分配入容器之前,同时,或之后调节预油漆的粘度。
10.权利要求5的方法,进一步包括如下步骤:在将它们分配入涂敷器之前,同时,或之后调节预油漆的粘度。
11.权利要求5的方法,进一步包括加入至少一种添加剂的步骤,该添加剂增强油漆的涂敷或最终性能。
12.权利要求11的方法,其中添加剂是凝集体材料。
13.权利要求11的方法,其中添加剂是增稠剂。
14.权利要求5的方法,进一步包括向预油漆中加入至少一种着色剂的步骤。
15.权利要求5的方法,其中不透明预油漆进一步包括至少一种吸收在不透明颜料上的微粒聚合物漆基。
16.权利要求5的方法,其中增量剂预油漆进一步包括至少一种吸收在不透明颜料上的微粒聚合物漆基。
17.权利要求5的方法,其中方法在油漆制造设备处进行。
18.权利要求5的方法,其中方法在销售点进行。
19.权利要求5的方法,其中方法在使用点进行。
20.权利要求5的方法,其中方法由计算机控制。
21.权利要求5的方法,其中预油漆的数目为4-15。
22.一种用于配制一包装着色胶乳油漆的流体不透明预油沫,该胶乳油漆的体积固体含量为约30%-约70%和斯托默粘度为约50-约250KU,该预油漆包含其它油漆成分,该预油漆基本由如下物质组成:
(i)至少一种不透明颜料,
(ii)至少一种分散剂,
(iii)至少一种增稠剂,和
(iv)水;
其中分散剂和增稠剂与油漆和与其它油漆成分相互相容。
23.权利要求22的预油漆,其中体积固体含量为约35%-约50%和斯托默粘度为约60-约150KU。
24.一种用于配制包含其它油漆成分的一包装着色胶乳油漆的流体白不透明预油漆,该预油漆的体积固体含量为约30%-约70%,PVC为约35%-约100%,和斯托默粘度为约50-约250KU,该预油漆基本由如下物质组成:
(i)至少一种不透明颜料,
(ii)至少一种分散剂,
(iii)至少一种增稠剂,
(iv)至少一种成膜或非成膜聚合物,和
(v)水;其中分散剂,增稠剂,和聚合物与油漆和与其它油漆成分相容和其中预油漆可对沉淀稳定。
25.权利要求24的预油漆,其中体积固体含量为约35%-约50%,PVC为约50-约100%,和斯托默粘度为约60-约150KU。
26.权利要求24的预油漆,其中聚合物吸附在不透明颜料上。
27.权利要求22或24的预油漆,其中不透明颜料是选自二氧化钛、氧化锌、氧化铅、合成聚合物油漆,及其混合物的材料。
28.权利要求22或24的预油漆,其中不透明颜料是金红石二氧化钛。
29.权利要求27的预油漆,其中合成聚合物油漆是有空隙的胶乳聚合物粒子。
30.权利要求22或24的预油漆,其中分散剂选自2-氨基-2-甲基-1-丙醇、二甲基氨基乙醇、三多磷酸钾、多磷酸三钠、柠檬酸、聚丙烯酸、二烯烃/马来酸酐加合物、疏水性改性的聚丙烯酸、亲水性改性的聚丙烯酸、和它们的盐、和它们的混合物。
31.权利要求22或24的预油漆,其中增稠剂选自碱溶性或碱溶胀性乳液(ASE)、疏水性改性的碱溶性乳液(HASE)、疏水性改性的环氧乙烷-尿烷聚合物(HEUR)、纤维素、疏水性改性的纤维素、疏水性改性的聚丙烯酰胺、聚乙烯醇、煅烧的二氧化硅、绿坡缕石粘土、钛酸盐螯合剂,及其混合物。
32.权利要求24的预油漆,其中聚合物选自丙烯酸类聚合物、聚醋酸乙烯酯、苯乙烯-丙烯酸类聚合物、苯乙烯-丁二烯聚合物、醋酸乙烯酯-丙烯酸类聚合物、乙烯-醋酸乙烯酯聚合物、醋酸乙烯酯-有支链的烷烃羧酸乙烯酯聚合物、醋酸乙烯酯-氯乙烯-丙烯酸类聚合物、乙烯-醋酸乙烯酯-丙烯酸类聚合物及其混合物和其中聚合物进一步包括至多约10wt%的单体聚合物,单体选自官能单体、共聚单体、及其结合物。
33.权利要求22或24的预油漆,进一步基本由选自如下的至少一种添加剂组成:酸、碱、消泡剂、凝结剂、共溶剂、杀霉菌剂、杀虫剂、防冻剂,添加剂的存在量小于约10wt%,基于预油漆的总重量。
34.一种用于配制包含其它油漆成分的一包装着色胶乳油漆的流体油漆增量剂预油漆,该预油漆基本由如下物质组成:
(i)至少一种体积固体含量为约30%-约70%,PVC为约35%-约100%,和斯托默粘度为约50-约250KU的矿物质填量剂,
(ii)至少一种增稠剂,
(iii)水,和
(iv)选加的聚合物漆基;其中预油漆成分彼此相容和与油漆的成分相容。
35.一种用于配制胶乳油漆的两种不同,但相互相容漆基预油漆的套漆,该套漆包括:
(a)权利要求22或24的预油漆,和
(b)体积固体含量为约25%-约70%或在1.25秒倒数下布氏粘度小于约100,000的胶乳聚合物漆基预油漆,该预油漆基本由Tg为约-430℃到约70℃的水性聚合物漆基和水组成;
其中预油漆成分相互彼此相容和与套漆中其它预油漆的成分相容。
36.权利要求35的预油漆的套漆,其中漆基预油漆的体积固体含量为约30%-约65%或在1.25秒倒数下布氏粘度为约100-约50,000,和基本由Tg为约-10℃到约60℃的水性聚合物漆基组成。
37.权利要求35的预油漆的套漆,其中漆基预油漆进一步基本由选自如下的至少一种添加剂组成:酸、碱、消泡剂、凝结剂、共溶剂、杀霉菌剂、杀虫剂、防冻剂,添加剂的存在量小于约10wt%,基于预油漆的总重量。
38.一种用于配制胶乳油漆的三种不同但相互相容流体预油漆的套漆,该套漆包括:
(a)权利要求35的预油漆的套漆,其中增量剂预油漆的体积固体含量为约30%-约70%,PVC为约35%-约100%,和斯托默粘度为约50-约250KU;和
(b)基本由如下物质组成的流体油漆增量剂预油漆:
(i)至少一种矿物质增量剂,
(ii)至少一种增稠剂,
(iii)水,和
(iv)可选择地聚合物漆基。
39.权利要求38的预油漆的套漆,其中增量剂预油漆的体积固体含量为约35%-约65%,PVC为约40%-约100%,和斯托默粘度为约60-约150KU。
40.权利要求35的预油漆的套漆,其中增量剂预油漆进一步基本由选自如下的至少一种添加剂组成:酸、碱、消泡剂、凝结剂、共溶剂、杀霉菌剂、杀虫剂、防冻剂,添加剂的存在量小于约20wt%,基于预油漆的总重量。
41.一种由包括如下步骤的方法生产的油漆系:
a.提供不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆
b.将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
42.一种足以形成至少一种用作弹性体涂料的油漆系的,不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆。
43.一种形成至少一种用作弹性体涂料的油漆系的方法,该方法包括如下步骤:
(a)提供不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
44.一种形成系列油漆的方法,系列油漆包括至少两种用作弹性体涂料的油漆系,该方法包括如下步骤:
(a)提供足以配制至少两种油漆系的预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;和
(iii)至少一种包括至少一种Tg小于约0℃的胶乳聚合物漆基的漆基预油漆;和
(iv)至少一种选自(i),(ii),(iii),和(iv)的另外不同的预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成系列油漆。
45.一种足以形成用作非胶接性,凝集体面漆的不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和
(iv)至少一种包括凝集体的预油漆。
46.一种形成至少一种用作非胶接性,凝集体面漆的油漆系的方法,该方法包括如下步骤:
(a)提供不同,但相互相容流体非胶接性预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;和
(iv)至少一种包括凝集体的预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。
47.一种形成系列油漆的方法,系列油漆包括至少两种用作非胶接性,凝集体面漆涂料的油漆系,该方法包括如下步骤:
(a)提供足以配制至少两种油漆系的不同流体,但相互相容,非胶接性预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;
(ii)至少一种包括至少一种体质颜料的增量剂预油漆;
(iii)至少一种包括至少一种胶乳聚合物漆基的漆基预油漆;
(iv)至少一种包括凝集体的预油漆;和
(v)至少一种选自(i),(ii),(iii),和(iv)的另外不同的预油漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成系列油漆。
48.一种足以配制至少一种油漆系的不同,但相互相容流体预油漆的套漆,油漆系用于形成着色和透明涂料,该套漆包括:
(i)至少一种包括至少一种不透明颜料的不透明预油漆;和
(ii)至少两种预油漆,它的每一种包括至少一种胶乳聚合物漆基。
49.一种足以形成至少一种用于形象艺术应用的油漆系的不同,但相互相容流体预油漆的套漆,该套漆包括:
(i)至少一种包括至少一种Tg为约-50℃到约10℃的胶乳聚合物漆基的预油漆;
(ii)至少一种包括至少一种Tg为约50℃-约140℃的胶乳聚合物漆基的预油漆;和
(iii)可选择地,至少一种包括至少一种Tg为约0℃-约65℃的胶乳聚合物漆基的预油漆。
50.权利要求49的预油漆的套漆,它进一步包括至少一种选自如下的另外预油漆:包括至少一种碱溶性树脂的预油漆、包括至少一种光泽添加剂的预油漆、包括至少一种蜡的预油漆、和至少一种包括至少一种油漆分散体的预油漆。
51.一种形成至少一种油漆系的方法,该方法包括如下步骤:
(a)提供权利要求48,49或50的预油漆的套漆;和
(b)将预定量的每种预油漆分配入容器或涂敷器以形成油漆系。