CN1230457C - 具有异氰酸酯基团的化合物、含有其的涂料组合物及其制备方法与用途 - Google Patents

具有异氰酸酯基团的化合物、含有其的涂料组合物及其制备方法与用途 Download PDF

Info

Publication number
CN1230457C
CN1230457C CNB998161586A CN99816158A CN1230457C CN 1230457 C CN1230457 C CN 1230457C CN B998161586 A CNB998161586 A CN B998161586A CN 99816158 A CN99816158 A CN 99816158A CN 1230457 C CN1230457 C CN 1230457C
Authority
CN
China
Prior art keywords
compound
acrylate
meth
diisocyanate
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB998161586A
Other languages
English (en)
Chinese (zh)
Other versions
CN1334833A (zh
Inventor
B·布鲁赫曼
E·贝克
H·伦茨
R·科尼格
R·施瓦姆
M·罗凯
W·赖希
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=7892663&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1230457(C) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by BASF SE filed Critical BASF SE
Publication of CN1334833A publication Critical patent/CN1334833A/zh
Application granted granted Critical
Publication of CN1230457C publication Critical patent/CN1230457C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/67—Unsaturated compounds having active hydrogen
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D175/00—Coating compositions based on polyureas or polyurethanes; Coating compositions based on derivatives of such polymers
    • C09D175/04—Polyurethanes
    • C09D175/14—Polyurethanes having carbon-to-carbon unsaturated bonds
    • C09D175/16—Polyurethanes having carbon-to-carbon unsaturated bonds having terminal carbon-to-carbon unsaturated bonds
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/80—Preparations for artificial teeth, for filling teeth or for capping teeth
    • A61K6/884—Preparations for artificial teeth, for filling teeth or for capping teeth comprising natural or synthetic resins
    • A61K6/891—Compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • A61K6/893—Polyurethanes
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C265/00—Derivatives of isocyanic acid
    • C07C265/14—Derivatives of isocyanic acid containing at least two isocyanate groups bound to the same carbon skeleton
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C275/00—Derivatives of urea, i.e. compounds containing any of the groups, the nitrogen atoms not being part of nitro or nitroso groups
    • C07C275/46—Derivatives of urea, i.e. compounds containing any of the groups, the nitrogen atoms not being part of nitro or nitroso groups containing any of the groups, X being a hetero atom, Y being any atom, e.g. acylureas
    • C07C275/58—Y being a hetero atom
    • C07C275/60—Y being an oxygen atom, e.g. allophanic acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/67—Unsaturated compounds having active hydrogen
    • C08G18/671—Unsaturated compounds having only one group containing active hydrogen
    • C08G18/672—Esters of acrylic or alkyl acrylic acid having only one group containing active hydrogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/67—Unsaturated compounds having active hydrogen
    • C08G18/671—Unsaturated compounds having only one group containing active hydrogen
    • C08G18/672—Esters of acrylic or alkyl acrylic acid having only one group containing active hydrogen
    • C08G18/673—Esters of acrylic or alkyl acrylic acid having only one group containing active hydrogen containing two or more acrylate or alkylacrylate ester groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
    • C08G18/78—Nitrogen
    • C08G18/7806—Nitrogen containing -N-C=0 groups
    • C08G18/7818—Nitrogen containing -N-C=0 groups containing ureum or ureum derivative groups
    • C08G18/7837—Nitrogen containing -N-C=0 groups containing ureum or ureum derivative groups containing allophanate groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/81—Unsaturated isocyanates or isothiocyanates
    • C08G18/8141—Unsaturated isocyanates or isothiocyanates masked
    • C08G18/815—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen
    • C08G18/8158—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen
    • C08G18/8175—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen with esters of acrylic or alkylacrylic acid having only one group containing active hydrogen
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Polymers & Plastics (AREA)
  • Medicinal Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oral & Maxillofacial Surgery (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Animal Behavior & Ethology (AREA)
  • Materials Engineering (AREA)
  • Public Health (AREA)
  • General Health & Medical Sciences (AREA)
  • Epidemiology (AREA)
  • Plastic & Reconstructive Surgery (AREA)
  • Engineering & Computer Science (AREA)
  • Veterinary Medicine (AREA)
  • Wood Science & Technology (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Paints Or Removers (AREA)
  • Dental Preparations (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Macromonomer-Based Addition Polymer (AREA)
CNB998161586A 1998-12-23 1999-12-14 具有异氰酸酯基团的化合物、含有其的涂料组合物及其制备方法与用途 Expired - Fee Related CN1230457C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19860041.0 1998-12-23
DE19860041A DE19860041A1 (de) 1998-12-23 1998-12-23 Durch Addition an Isocyanatgruppen als auch durch strahlungsinduzierte Addition an aktivierte C-C-Doppelbindungen härtbare Beschichtungsmittel

Publications (2)

Publication Number Publication Date
CN1334833A CN1334833A (zh) 2002-02-06
CN1230457C true CN1230457C (zh) 2005-12-07

Family

ID=7892663

Family Applications (1)

Application Number Title Priority Date Filing Date
CNB998161586A Expired - Fee Related CN1230457C (zh) 1998-12-23 1999-12-14 具有异氰酸酯基团的化合物、含有其的涂料组合物及其制备方法与用途

Country Status (10)

Country Link
US (1) US6617413B1 (enExample)
EP (1) EP1144476B1 (enExample)
JP (2) JP5105387B2 (enExample)
KR (1) KR100687109B1 (enExample)
CN (1) CN1230457C (enExample)
AT (1) ATE255609T1 (enExample)
CA (1) CA2356685C (enExample)
DE (2) DE19860041A1 (enExample)
ES (1) ES2212662T3 (enExample)
WO (1) WO2000039183A1 (enExample)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109843582A (zh) * 2016-10-14 2019-06-04 奥地利赛诺柏拉斯有限公司 可热变形的片材
CN111072917A (zh) * 2020-01-02 2020-04-28 万华化学集团股份有限公司 一种存储稳定的多异氰酸酯组合物及制备方法

Families Citing this family (129)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6610777B1 (en) 1999-07-30 2003-08-26 Ppg Industries Ohio, Inc. Flexible coating compositions having improved scratch resistance, coated substrates and methods related thereto
WO2001009259A1 (en) 1999-07-30 2001-02-08 Ppg Industries Ohio, Inc. Coating compositions having improved scratch resistance, coated substrates and methods related thereto
AU771282B2 (en) 1999-07-30 2004-03-18 Ppg Industries Ohio, Inc. Coating compositions having improved scratch resistance, coated substrates and methods related thereto
ATE385241T1 (de) 1999-09-30 2008-02-15 Basf Ag Mit uv-strahlung und thermisch härtbare wässrige polyurethandispersionen sowie deren verwendung
DE10031258A1 (de) 2000-06-27 2002-01-10 Basf Ag Härtbare wässrige Polyurethandispersionen
JP4535574B2 (ja) * 2000-07-27 2010-09-01 株式会社興人 新規なウレタンアクリルアミド類および該ウレタンアクリルアミド類を含有した紫外線及び電子線硬化性樹脂組成物
WO2002010292A1 (en) * 2000-07-31 2002-02-07 Ppg Industries Ohio, Inc. Dual cure coating compositions having improved scratch resistance, coated substrates and methods related thereto
US6635341B1 (en) 2000-07-31 2003-10-21 Ppg Industries Ohio, Inc. Coating compositions comprising silyl blocked components, coating, coated substrates and methods related thereto
DE10041635A1 (de) * 2000-08-24 2002-03-28 Basf Coatings Ag Thermisch und mit aktinischer Strahlung härtbare Einkomponentensysteme und ihre Verwendung
DE10041634C2 (de) 2000-08-24 2002-10-17 Basf Coatings Ag Wäßrige Dispersion und ihre Verwendung zur Herstellung von thermisch und mit aktinischer Strahlung härtbaren Beschichtungsstoffen, Klebstoffen und Dichtungsmassen
DE10048275C1 (de) * 2000-09-29 2002-05-29 Basf Coatings Ag Thermisch und mit aktinischer Strahlung härtbares Mehrkomponentensystem und seine Verwendung
DE10048670A1 (de) * 2000-09-30 2002-04-25 Basf Coatings Ag Beschichtungsstoffsystem für die Herstellung farb- und/oder effektgebender Mehrschichtlackierungen auf der Basis von Mehrkomponentenbeschichtungsstoffen
DE10048849A1 (de) * 2000-10-02 2002-04-18 Basf Coatings Ag Verfahren zur Herstellung eines thermisch und mit aktinischer Strahlung härtbaren Mehrkomponentensystems und seine Verwendung
DE10048847A1 (de) 2000-10-02 2002-04-18 Basf Coatings Ag Lösemittelhaltiges, thermisch und mit aktinischer Strahlung härtbares Mehrkomponentensystem und seine Verwendung
MXPA03004456A (es) * 2000-11-20 2003-08-19 Ciba Sc Holding Ag Foto-iniciadores fluorinados sobre resinas de doble curado.
US20030026908A1 (en) * 2001-04-30 2003-02-06 Matthew Lane Sandable, self-healable coating compositions and a process of using the same
DE10129970A1 (de) * 2001-06-21 2003-01-09 Basf Coatings Ag Thermisch und mit aktinischer Strahlung härtbare Beschichtungsstoffe, Verfahren zu ihrer Herstellung und ihre Verwendung
DE10140156A1 (de) * 2001-08-16 2003-03-20 Basf Coatings Ag Thermisch und mit aktinischer Strahlung härtbare Beschichtungsstoffe und ihre Verwendung
DE10140155A1 (de) 2001-08-16 2003-03-06 Basf Coatings Ag Thermisch sowie thermisch und mit aktinischer Strahlung härtbare Beschichtungsstoffe und ihre Verwendung
US6844029B2 (en) * 2001-10-26 2005-01-18 Kansai Paint Co., Ltd. Photocurable primer composition and coating method by use of the same
KR100354193B1 (ko) * 2001-12-21 2002-09-27 (주) 베리콤 광중합형 치과용 조성물
FR2837820B1 (fr) * 2002-03-27 2005-03-11 Rhodia Chimie Sa Composition polyisocyanate de faible viscosite possedant une fonctionnalite elevee et procede de preparation
DE10241299A1 (de) 2002-09-04 2004-03-25 Basf Ag Strahlungshärtbare Polyurethane mit verkappten Aminogrupppen
DE10246512A1 (de) 2002-10-04 2004-04-15 Bayer Ag Niedrigviskose strahlenhärtende und thermisch härtende Polyisocyanate
DE10255664B4 (de) * 2002-11-28 2006-05-04 Kodak Polychrome Graphics Gmbh Für lithographische Druckplatten geeignete Photopolymerzusammensetzung
DE10260269A1 (de) 2002-12-20 2004-07-01 Bayer Ag Neue Dual Cure-Systeme
DE10346327A1 (de) * 2003-10-06 2005-04-21 Basf Ag Strahlungshärtbare Beschichtungsmittel, enthaltend ein aliphatisches Urethan (meth)acrylat
US7144955B2 (en) * 2003-10-27 2006-12-05 Bayer Materialscience Llc Acrylate-functional blocked polyisocyanate resin for UV/thermally curable coatings
DE10357712A1 (de) * 2003-12-09 2005-07-14 Bayer Materialscience Ag Härter
DE102004009437A1 (de) 2004-02-24 2005-09-15 Basf Ag Strahlungshärtbare Verbundschichtplatte oder -folie
DE102004012902A1 (de) * 2004-03-17 2005-10-06 Bayer Materialscience Ag Herstellung von neuen strahlenhärtenden Bindemitteln
DE102004012903A1 (de) * 2004-03-17 2005-10-06 Bayer Materialscience Ag Niedrigviskose Allophanate mit aktinisch härtbaren Gruppen
DE102004043363A1 (de) * 2004-09-08 2006-03-09 Bayer Materialscience Ag Abspalterfrei-härtende blockierte Polyisocyanate für Dual Cure Systeme
DE102004043540A1 (de) * 2004-09-09 2006-03-30 Bayer Materialscience Ag Niedrigviskose Allophanate mit aktinisch härtbaren Gruppen
DE102004043537A1 (de) * 2004-09-09 2006-03-16 Bayer Materialscience Ag Herstellung von neuen strahlenhärtenden Bindemitteln
DE102004043539A1 (de) * 2004-09-09 2006-03-30 Bayer Materialscience Ag Niedrigviskose Allophanate mit aktinisch härtbaren Gruppen
DE102004043538A1 (de) * 2004-09-09 2006-03-16 Bayer Materialscience Ag Herstellung von neuen strahlenhärtenden Bindemitteln
DE102004048873A1 (de) 2004-10-07 2006-04-13 Bayer Materialscience Ag Verfahren zur Herstellung von niedrigviskosen Allophanaten mit aktinisch härtbaren Gruppen
DE502005010145D1 (de) 2004-11-04 2010-10-07 Basf Coatings Ag Verfahren zur herstellung von formteilen, insbesondere zur anwendung im automobilbau, und hierfür geeignete, eine beschichtung aufweisende folien
KR101237495B1 (ko) 2004-11-04 2013-02-27 바스프 코팅스 게엠베하 특히 자동차 산업에서 사용하기 위한 주형된 부품을제조하는 방법, 및 이를 위해 적절한 코팅을 포함하는 필름
US20060106157A1 (en) * 2004-11-17 2006-05-18 Sawant Suresh G Urethane acrylate tie coats
US20060128923A1 (en) * 2004-12-15 2006-06-15 Bayer Materialscience Llc Radiation curable compositions
DE102004060966A1 (de) * 2004-12-17 2006-06-29 Basf Coatings Ag Strukturviskose härtbare Gemische, Verfahren zu ihrer Herstellung und ihre Verwendung
DE102004063102A1 (de) * 2004-12-22 2006-07-13 Basf Ag Strahlungshärtbare Verbindungen
DE102005008032A1 (de) * 2005-02-22 2006-08-31 Bayer Materialscience Ag Verfahren zur Herstellung von Hydroxyalkyl(meth)acrylaten und deren Verwendung
KR101251244B1 (ko) 2005-02-24 2013-04-08 바스프 에스이 방사선 경화성 수성 폴리우레탄 분산액
JP2008531778A (ja) * 2005-02-24 2008-08-14 ビーエーエスエフ ソシエタス・ヨーロピア 放射線硬化性ポリウレタンで少なくとも部分的に被覆された顔料、その生産と利用
DE102005011231A1 (de) * 2005-03-11 2006-09-14 Bayer Materialscience Ag Spezielle Allophanate enthaltende, modifizierte Polyurethane
DE102005020605A1 (de) 2005-05-03 2006-11-09 Basf Coatings Ag Verfahren zur Herstellung von eine Beschichtung(B) aufweisenden Folien(F), die so erhaltenen Folien(F) sowie ihre Verwendung zur Herstellung von Formteilen, insbesondere ihre Anwendung im Automobilbau
DE102005034213A1 (de) * 2005-07-19 2007-01-25 Basf Ag Durch Energieeintrag reparable Beschichtungen
EP1915122B1 (de) 2005-08-11 2013-12-04 Basf Se Copolymere für kosmetische anwendungen
DE102005057245A1 (de) * 2005-11-29 2007-06-06 Bayer Materialscience Ag Lackierte Folien
DE102005057682A1 (de) 2005-12-01 2007-06-06 Basf Ag Strahlungshärtbare wasserelmulgierbare Polyisocyanate
DE102005057683A1 (de) 2005-12-01 2007-06-06 Basf Ag Strahlungshärtbare wasserelmulgierbare Polyisocyanate
DE102006015709A1 (de) * 2006-04-04 2007-10-11 Bayer Materialscience Ag Verfahren zur Herstellung von allophanathaltigen, durch aktinische Strahlung härtbaren Polyurethanprepolymeren mit erhöhter Beständigkeit
EP2089444A1 (de) * 2006-10-09 2009-08-19 Basf Se Strahlungshärtbare verbindungen
US7776969B2 (en) * 2006-12-04 2010-08-17 Bayer Materialscience Llc Allophanate-modified stabilizers and the polymer polyols prepared from these stabilizers
US20080132724A1 (en) * 2006-12-04 2008-06-05 Bayer Materialscience Llc Allophanate modified isocyanates which contain reactive unsaturation
CN101616946B (zh) * 2007-02-15 2012-07-18 巴斯夫欧洲公司 聚氨酯分散体及其制备和用途
DE102007040376A1 (de) * 2007-08-20 2009-02-26 Karl Wörwag Lack- Und Farbenfabrik Gmbh & Co. Kg Lack, flexibler Schichtverbund mit einem Träger und einer darauf aufgebrachten Lackschicht sowie deren Verwendung
DE102007040239A1 (de) 2007-08-25 2009-05-07 Bayer Materialscience Ag Verfahren zur Herstellung von niedrigviskosen Allophanaten mit aktinisch härtbaren Gruppen
DE102007040240A1 (de) 2007-08-25 2009-02-26 Bayer Materialscience Ag Verfahren zur Herstellung von niedrigviskosen Allophanaten mit aktinisch härtbaren Gruppen
DE102008043202A1 (de) 2007-10-29 2009-04-30 Basf Se Verfahren zur Kantenleimung von Textilien
US20100227942A1 (en) 2007-12-18 2010-09-09 Emmanouil Spyrou Dual-cure formulations with components containing uretdione groups
EP2143748A1 (en) 2008-07-10 2010-01-13 Cytec Surface Specialties, S.A. Aqueous radiation curable polyurethane compositions
DE102008036685A1 (de) 2008-08-06 2010-02-11 Basf Coatings Ag Zweischicht-Beschichtungssysteme mit verbesserter Zwischenhaftung
WO2010060109A1 (en) 2008-11-24 2010-05-27 Valspar Sourcing, Inc. Coating system for cement composite articles
DE102009008569A1 (de) 2009-02-12 2010-08-19 Bayer Materialscience Ag Verfahren zur Herstellung von besonders reaktiven und niedrigviskosen Allophanaten mit aktinisch härtbaren Gruppen und deren Verwendung zur Herstellung besonders kratzfester Beschichtungen
DE102009010990A1 (de) * 2009-02-19 2010-08-26 Karl Wörwag Lack- Und Farbenfabrik Gmbh & Co. Kg Solarzellenmodul und Verfahren zu seiner Herstellung
US9759181B2 (en) * 2009-04-24 2017-09-12 Hempel A/S Coating composition for wind turbine blades
WO2011015540A1 (de) 2009-08-06 2011-02-10 Basf Se Strahlungshärtbare wasserdispergierbare polyurethane und polyurethandispersionen
EP2552380B1 (en) 2010-03-31 2019-04-24 3M Innovative Properties Company Polymerizable isocyanurate monomers and dental compositions
DE102010034039A1 (de) 2010-08-11 2012-02-16 Bundesdruckerei Gmbh Verfahren zur Herstellung einer Folie für ein Sicherheits- und/oder Wertdokument
US8697769B2 (en) 2010-09-30 2014-04-15 Voco Gmbh Lacquer composition comprising a monomer with a polyalicyclic structure element
EP2436366B1 (de) 2010-09-30 2015-07-29 VOCO GmbH Kompositmaterial umfassend ein Monomer mit einem polyalicyclischen Strukturelement als Versiegelungsmaterial
JP5534606B2 (ja) * 2010-11-17 2014-07-02 旭化成ケミカルズ株式会社 活性エネルギー線硬化型樹脂組成物
EP2675421A2 (en) 2011-02-15 2013-12-25 3M Innovative Properties Company Dental compositions comprising mixture of isocyanurate monomer and tricyclodecane monomer
US9090736B2 (en) 2011-02-22 2015-07-28 Basf Se Rheological agent for radiation-curable coating compositions
KR20140006959A (ko) 2011-02-22 2014-01-16 바스프 에스이 방사선-경화성 코팅 물질용 레올로지 작용제
EP2581397B1 (de) 2011-10-14 2014-12-10 Allnex IP S.à.r.l. Verfahren zur herstellung von niedrigviskosen, wasserverdünnbaren urethan(meth)acrylaten
ES2523277T3 (es) 2011-10-14 2014-11-24 Allnex Ip S.À.R.L. Procedimiento para la preparación de alofanatos emulsionables en agua, de baja viscosidad, que contienen grupos endurecibles por radiaciones
WO2013110504A1 (en) 2012-01-27 2013-08-01 Basf Se Radiation-curable antimicrobial coatings
US8728455B2 (en) 2012-01-27 2014-05-20 Basf Se Radiation-curable antimicrobial coatings
JP5892799B2 (ja) * 2012-02-03 2016-03-23 新中村化学工業株式会社 伸びがあり耐傷つき性に優れる硬化物を形成するウレタン（メタ）アクリレートおよびそれを含有する光硬化性樹脂組成物
US9193888B2 (en) 2012-03-19 2015-11-24 Basf Se Radiation-curable aqueous dispersions
CN104204021B (zh) 2012-03-19 2018-04-20 巴斯夫欧洲公司 可辐射固化的含水分散体
ES2626506T3 (es) * 2012-05-30 2017-07-25 Igm Malta Limited Compuestos curables por radiación
US9296907B2 (en) 2012-05-30 2016-03-29 Basf Se Radiation-curable compounds
KR20150036655A (ko) * 2012-07-20 2015-04-07 바스프 에스이 급속-건조, 방사선-경화성 코팅 화합물
WO2014066358A1 (en) 2012-10-23 2014-05-01 Basf Se Ethylenically unsaturated oligomers containing polymer stabilizer groups
PL2920222T3 (pl) * 2012-11-16 2017-09-29 Basf Se Poliuretany, ich dyspersje, ich wytwarzanie i zastosowanie
CN103833954A (zh) * 2012-11-27 2014-06-04 中国石油天然气股份有限公司 一种注水井带压作业用小剂量化学堵剂的制备方法
US20140199491A1 (en) * 2013-01-15 2014-07-17 Allnex Ip S.À.R.L. One-component, dual-cure conformal coating compositions
EP2942361A1 (en) 2014-05-06 2015-11-11 Basf Se Grain enhancement with surfactants in water-based uv-radiation curable polyurethane dispersions
SG11201610191PA (en) 2014-06-23 2017-01-27 Carbon Inc Methods of producing polyurethane three-dimensional objects from materials having multiple mechanisms of hardening
WO2016069582A1 (en) * 2014-10-28 2016-05-06 The Board Of Trustees Of The University Of Illinois Dynamic urea bonds for polymers
CN107108833B (zh) 2014-11-24 2022-06-14 Ppg工业俄亥俄公司 通过挤出用于反应性三维打印的方法
RU2017125258A (ru) 2014-12-17 2019-01-17 Басф Се Радиационно-отверждаемая композиция покрытия на основе сшитых полиуретанов с удлиненной цепью
CN104532565A (zh) * 2014-12-18 2015-04-22 湖北久瑞核技术股份有限公司 一种涤纶帘子布浸渍胶、制备方法及浸胶涤纶帘子布
CN104532564A (zh) * 2014-12-18 2015-04-22 湖北久瑞核技术股份有限公司 基于紫外光和高能电子处理浸胶帘子布纤维或帘线的方法
CN104389168A (zh) * 2014-12-18 2015-03-04 湖北久瑞核技术股份有限公司 一种锦纶帘子布浸渍胶、制备方法及浸胶锦纶帘子布
CN104404765B (zh) * 2014-12-18 2018-01-26 江苏久瑞高能电子有限公司 一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布
CN104441319A (zh) * 2014-12-18 2015-03-25 湖北久瑞核技术股份有限公司 基于紫外光和高能电子干燥浸胶帘子布的方法
CN104594036A (zh) * 2014-12-18 2015-05-06 湖北久瑞核技术股份有限公司 一种粘合纤维或纤维织物的方法
EP3034569B1 (de) 2014-12-19 2016-11-30 Evonik Degussa GmbH Thermisch nachhärtende mit aktinischer Strahlung vernetzende Systeme
EP3106448A1 (en) * 2015-06-15 2016-12-21 Eternit AG Coated fiber cement products and methods for the production thereof
EP3170848A1 (de) * 2015-11-23 2017-05-24 Henkel AG & Co. KGaA Kationische phototransferpolymerisation
EP3395849A4 (en) 2015-12-24 2019-08-14 Tosoh Corporation POLYURETHANE-FRYER COMPOSITION, MODULE MEMBRANE SURFACE MATERIAL USING A HOLLOWED OR FLAT-MEMBRANE FIBER-DISRUPTED MEMBRANE USING THE SAID COMPOSITION AND ALLOPHANATE GROUP-CONTAINING POLYISOCYANATE COMPOSITION MADE OF MDI AND METHOD OF MANUFACTURING THEREOF
US10316213B1 (en) 2017-05-01 2019-06-11 Formlabs, Inc. Dual-cure resins and related methods
US10479862B2 (en) 2017-12-07 2019-11-19 Covestro Llc Amine based polymer polyol stabilizers
US10526484B2 (en) 2017-12-20 2020-01-07 Covestro Llc Dithiocarbonate containing polyols as polymer polyol stabilizers
WO2019185302A1 (en) * 2018-03-27 2019-10-03 Mercene Labs Ab Coating and primer
CN108864783A (zh) * 2018-06-06 2018-11-23 Ppg涂料(天津)有限公司 防水涂层
CN108852857A (zh) * 2018-07-16 2018-11-23 潍坊科技学院 一种牙本质脱敏剂材料及制备方法
CN109776756A (zh) * 2019-01-21 2019-05-21 深圳市道尔顿电子材料有限公司 一种双重改性环氧丙烯酸酯及其光刻胶
WO2020156802A1 (en) * 2019-02-01 2020-08-06 Basf Se Polyurethane and uv-moisture dual cure pu reactive hotmelt comprising the same
CN114127150A (zh) * 2019-07-18 2022-03-01 巴斯夫欧洲公司 脲基甲酸酯基分散剂
WO2021069295A1 (de) 2019-10-08 2021-04-15 Basf Se Thermisch härtbare zweikomponentige beschichtungsmassen
WO2021129939A1 (en) * 2019-12-27 2021-07-01 Transitions Optical, Ltd. Curable photochromic polycarbodiimide compositions
LU101630B1 (en) * 2020-01-31 2021-08-03 Tarkett Gdl Sa Surface covering and method for the manufacture thereof
EP4110843A1 (en) * 2020-02-28 2023-01-04 Carbon, Inc. One part moisture curable resins for additive manufacturing
CN111533884B (zh) * 2020-05-08 2022-03-15 深圳市前海博扬研究院有限公司 一种聚氨酯改性丙烯酸酯uv树脂及其制备方法
US20240400748A1 (en) * 2021-01-26 2024-12-05 Mitsui Chemicals, Inc. Monomer composition, curable composition, molded body and method for producing monomer composition
DE102021004169A1 (de) * 2021-08-13 2023-02-16 Mankiewicz Gebr. & Co. (Gmbh & Co. Kg) Transluzente Beschichtungssysteme, Verfahren zur Herstellung der Beschichtungssysteme sowie deren Verwendung
EP4134386B1 (de) * 2021-08-13 2023-11-08 Evonik Operations GmbH Adduktzusammensetzungen aus diisocyanaten und hydroxy- oder aminofunktionalisierten alkylsulfonsäuren und/oder alkylsulfonsäurederivaten
US11884000B2 (en) 2021-08-27 2024-01-30 Carbon, Inc. One part, catalyst containing, moisture curable dual cure resins for additive manufacturing
WO2023118015A1 (en) 2021-12-21 2023-06-29 Basf Se Environmental attributes for care composition ingredients
CN116606563B (zh) * 2023-07-21 2023-12-12 江西美吉新材料科技有限公司 一种环保热吸塑uv油墨及其制备方法和应用
CN117050644A (zh) * 2023-07-26 2023-11-14 广东安捷伦新材料科技有限公司 一种双固化uv钢琴黑涂料及其制备方法

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS55123659A (en) * 1979-03-16 1980-09-24 Mitsui Toatsu Chem Inc Undercoating composition for radical curing paint
DE3563632D1 (en) * 1984-02-13 1988-08-11 Takeda Chemical Industries Ltd Method of adhesion and composition therefor
JPS61243815A (ja) * 1985-04-23 1986-10-30 Nippon Synthetic Chem Ind Co Ltd:The 揺変性を有する樹脂組成物
IT1204812B (it) * 1986-02-19 1989-03-10 Siv Soc Italiana Vetro Procedimento per la fabbricazione di una vetrata di sicurezza per autoveicoli ed edifici,e prodotto cosi' ottenuto
FR2608095B1 (fr) * 1986-12-11 1988-12-30 Altulor Sa Plaques coulees a haute resistance au choc, leur procede de fabrication et articles faconnes obtenus
JPS63175019A (ja) * 1987-01-16 1988-07-19 Dainippon Ink & Chem Inc 放射線硬化型樹脂組成物
CA2073155A1 (en) * 1991-07-16 1993-01-17 National Starch And Chemical Investment Holding Corporation Dual curing composition and use thereof
US5234970A (en) * 1991-07-16 1993-08-10 W. R. Grace & Co.-Conn. Dual curing composition based on isocyanate trimer and use thereof
JPH06206979A (ja) * 1993-01-11 1994-07-26 Dainippon Ink & Chem Inc 熱硬化性樹脂水性分散液及び繊維仕上剤
DE4416113A1 (de) * 1994-05-06 1995-11-09 Bayer Ag Wasserdispergierbare Polyisocyanat-Zubereitungen
DE4417745A1 (de) * 1994-05-20 1995-11-23 Bayer Ag Olefinisch ungesättigte Polyisocyanate
JP3718295B2 (ja) * 1995-08-11 2005-11-24 ジャパンコンポジット株式会社 ビニルエステル樹脂組成物及び硬化物
US5606001A (en) * 1995-09-14 1997-02-25 Bayer Corporation Polyisocyanates containing allophanate groups and optionally isocyanurate groups
JPH09141718A (ja) * 1995-11-21 1997-06-03 Sekisui Chem Co Ltd 反応性樹脂シートの製造方法
JP3790908B2 (ja) * 1996-09-03 2006-06-28 大日本インキ化学工業株式会社 湿気硬化型ウレタンプライマー組成物及びその被覆方法
US5739251A (en) * 1997-03-27 1998-04-14 Bayer Corporation Low viscosity, ethylenically unsaturated polyurethanes containing allophanate groups
US5767220A (en) * 1997-08-25 1998-06-16 Bayer Corporation Low viscosity, ethylenically unsaturated polyurethanes containing allophanate groups

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109843582A (zh) * 2016-10-14 2019-06-04 奥地利赛诺柏拉斯有限公司 可热变形的片材
CN109843582B (zh) * 2016-10-14 2021-09-03 奥地利赛诺柏拉斯有限公司 可热变形的片材
CN111072917A (zh) * 2020-01-02 2020-04-28 万华化学集团股份有限公司 一种存储稳定的多异氰酸酯组合物及制备方法
US12304993B2 (en) 2020-01-02 2025-05-20 Wanhua Chemical Group Co., Ltd. Storage-stable polyisocyanate composition and preparation method

Also Published As

Publication number Publication date
JP5466658B2 (ja) 2014-04-09
WO2000039183A1 (de) 2000-07-06
CA2356685C (en) 2009-10-20
US6617413B1 (en) 2003-09-09
ATE255609T1 (de) 2003-12-15
JP2002533542A (ja) 2002-10-08
DE59907967D1 (de) 2004-01-15
CN1334833A (zh) 2002-02-06
JP2011099119A (ja) 2011-05-19
JP5105387B2 (ja) 2012-12-26
ES2212662T3 (es) 2004-07-16
DE19860041A1 (de) 2000-06-29
EP1144476B1 (de) 2003-12-03
KR100687109B1 (ko) 2007-02-27
KR20010099893A (ko) 2001-11-09
EP1144476A1 (de) 2001-10-17
CA2356685A1 (en) 2000-07-06

Similar Documents

Publication Publication Date Title
CN1230457C (zh) 具有异氰酸酯基团的化合物、含有其的涂料组合物及其制备方法与用途
CN1238398C (zh) 能够用紫外线和热硬化的聚氨酯水分散体,以及它们的用途
KR101232424B1 (ko) 방사선 경화성 조성물
CN1286874C (zh) 光敏水性涂料组合物
JP2004502000A (ja) 硬化性の水性ポリウレタン分散液
JP5763746B2 (ja) 放射線硬化性アミノ（メタ）アクリレート
WO1998048947A1 (en) Novel urethane resins and coating compositions and methods for their use
JPH11140146A (ja) エチレン系不飽和二重結合を有する脂肪族ウレタン官能性プレポリマーをベースとする放射線硬化性配合物、その使用、これを用いる基体の被覆の方法および被覆した基体
WO2006085937A1 (en) Uv curable coating composition
JP2007534800A (ja) 光開始剤を配合した放射線硬化性マイケル付加樹脂
CN1863745A (zh) 含有脂族聚氨酯(甲基)丙烯酸酯的可辐射固化的涂覆剂
JP2006169527A (ja) 放射線硬化性組成物
WO2018236656A1 (en) Coatings with fast return to service
CN1637037A (zh) 硬化剂
KR20150135243A (ko) 활성 에너지선 경화형 도료 조성물
JP4915042B2 (ja) 光硬化型樹脂組成物及びそれを用いた光硬化型コーティング剤、光硬化型フィルム
JPH11279486A (ja) 光硬化性塗料組成物および塗装仕上げ方法
JP4756290B2 (ja) 活性エネルギー線硬化型塗料用組成物
US10781339B2 (en) Reduced discoloration of polyaspartic resins blended with acrylate resins
CN1694912A (zh) 辐射固化的带有封闭氨基的聚氨酯
JPH09124719A (ja) 表面活性のキャップアミノ化合物を含有する放射線硬化可能の組成物
HK1080504A (en) Coating compositions
HK1094001A (en) Radiation curable compositions
HK1085235A (en) Radiation-curing binders and a process for their preparation
HK1091907B (en) Radiation curable compositions

Legal Events

Date Code Title Description
C06 Publication
C10 Entry into substantive examination
PB01 Publication
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CF01 Termination of patent right due to non-payment of annual fee
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20051207

Termination date: 20181214