CN104404765B - 一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布 - Google Patents

一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布 Download PDF

Info

Publication number
CN104404765B
CN104404765B CN201410786817.6A CN201410786817A CN104404765B CN 104404765 B CN104404765 B CN 104404765B CN 201410786817 A CN201410786817 A CN 201410786817A CN 104404765 B CN104404765 B CN 104404765B
Authority
CN
China
Prior art keywords
cord fabric
aramid fiber
fiber cord
acrylate
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410786817.6A
Other languages
English (en)
Other versions
CN104404765A (zh
Inventor
冯敬涛
张良均
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu new century energy Electronics Co. Ltd.
Original Assignee
Jiangsu New Century Energy Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu New Century Energy Electronics Co Ltd filed Critical Jiangsu New Century Energy Electronics Co Ltd
Priority to CN201410786817.6A priority Critical patent/CN104404765B/zh
Publication of CN104404765A publication Critical patent/CN104404765A/zh
Application granted granted Critical
Publication of CN104404765B publication Critical patent/CN104404765B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布，属于轮胎制造技术领域，芳纶帘子布浸渍胶由多异氰酸酯、丙烯酸酯和烯醚类单体组成，所述多异氰酸酯选自于含有两个以上异氰酸基的异氰酸酯中的一种或几种的组合物；其制备方法，将多异氰酸酯、丙烯酸酯和烯醚类单体置于一起，在35~50℃下搅拌25~40分钟；而浸胶芳纶帘子布则是由芳纶帘子布浸渍胶浸渍而成。与现有技术相比，本发明的有益效果：工艺设备简单；节省能源，能量利用率高；无溶剂排放，安全无污染；固化速度快，生产效率高；生产的帘子布与橡胶粘结性能优越。

Description

一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布
技术领域
本发明属于轮胎制造技术领域，涉及一种帘子布浸渍胶，特别涉及一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布。
背景技术
帘子布：用强力股线作经，用中、细支单纱作纬，织制的轮胎用骨架织物。其中经线排列紧密，纬纱排列稀疏，状似帘子，因此得名帘子布。
帘子布用作轮胎等橡胶制品的骨架，使其承受巨大压力、冲击负荷和强烈震动。可以看出帘子布是影响轮胎性能和寿命的重要材料。其中经线(又称帘子线)承受负荷，而纬纱固定经线位置。对帘子线的要求是：①强度和初始模量高；②耐热；③耐疲劳；④结构稳定；⑤能和橡胶粘合。
帘子布种类繁多，就芳纶帘子布而言，主要工序为纤维的生产和浸胶，两者直接影响到产品的性能。
就浸胶方面，目前市场没有很好的浸胶方法。先用D-417预浸液浸渍，再用RFL(RFL浸渍胶制备：间苯二酚和甲醛预先配置成RF溶液；还要将丁二烯、苯乙烯、2-乙烯基吡啶通过乳液聚合合成VP胶；最后将RF溶液和VP乳胶混合成RFL)浸渍胶浸渍芳纶帘子布。采用二浴方法缺点在于RF溶液配制是间苯二酚和甲醛在氢氧化钠的催化作用下缩聚7小时而成，需要消耗大量时间，此外缩聚使得RF溶液粘度越来越大，进而会凝胶失去使用性；并且由于芳纶纤维具有特殊的分子结构，通用的RFL浸渍胶与芳纶帘子布粘接效果很差。
现有技术文献，“芳纶浸渍帘布的研究开发”，《轮胎工业》，第22卷第10期，公开日2002年12月31日)是最接近的现有技术。
发明内容
本发明的目的在于提供一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布，运用辐照来进行固化干燥，具有制备简单、浸胶工艺节能高效的优点。
为了达到上述目的，本发明提供了一种芳纶帘子布浸渍胶，由多异氰酸酯、丙烯酸酯和烯醚类单体组成，所述多异氰酸酯选自于含有两个以上异氰酸基的异氰酸酯中的一种或几种的组合物。更优选地，所述多异氰酸酯选自于二苯基甲烷二异氰酸酯、4，4′，4″-三苯基甲烷三异氰酸酯、2，2′-二甲基-3，3′，5，5′-三苯基甲烷四异氰酸酯中的一种或几种的组合物。
本发明基于以下理论：
多异氰酸酯和丙烯酸酯反应，制备成一多异氰酸酯与丙烯酸酯加成物溶液，利用加成物溶液中残留的的-NCO基团和芳纶帘子布的-NH-基团起交联反应，使胶液以化学键方式附着于芳纶帘子布上，再以辐照的固化方式使加成物溶液中的双键产生自由基聚合而固化。
更进一步解释，多异氰酸酯和丙烯酸酯结合，得到一同时含有-NCO基团和碳碳双键的中间产物。该中间产物的-NCO基团与芳纶中-NH-基团反应，使其连接到芳纶上；该中间产物的碳碳双键与烯醚类单体中的碳碳双键打开，聚合，最终固化。
其中，浸渍胶中的异氰酸基总数过量于丙烯酸酯中的羟基的方法，对于本领域技术人员是非常常见的。
优选地，所述丙烯酸酯为单羟基丙烯酸酯。更优选地，所述丙烯酸酯选自于甲基丙烯酸羟乙酯、丙烯酸羟乙酯、甲基丙烯酸羟丙酯、丙烯酸羟丙酯、4-羟基丁基丙烯酸酯或3-羟基-1-金刚烷基甲基丙烯酸酯中的一种或几种的组合物。
优选地，所述烯醚类单体选自于丙烯基乙醚、乙烯基丁醚或丙烯基苄醚中的一种或几种的组合物。
优选地，本发明的芳纶帘子布浸渍胶，以重量份计，由100～300份的多异氰酸酯、70～240份的丙烯酸酯和10～40份烯醚类单体组成。
本发明还提供了一种所述芳纶帘子布浸渍胶的制备方法，将多异氰酸酯、丙烯酸酯和烯醚类单体置于一起，在35～50℃下搅拌25～40分钟。
本发明同时还提供了一种浸胶芳纶帘子布，由所述芳纶帘子布浸渍胶浸渍而成。
为了更较为直观解释发明原理，以下通过化学反应加以说明：
以三官能度的多异氰酸酯和单羟基丙烯酸酯反应为例，
第一步，浸渍胶的生成：
加入烯醚类单体调节浸渍胶黏度。
第二步，浸渍胶与芳纶的交联反应：
第三步，电子束辐照固化浸渍胶：
其中，R1＝-H，-CH3
R2＝-CH2CH3，-CH2CH2CH2CH3，
与现有技术相比，本发明的有益效果：
工艺设备简单；节省能源，能量利用率高；无溶剂排放，安全无污染；固化速度快，生产效率高；生产的帘子布与橡胶粘结性能优越。
具体实施方式
各实施例均按照以下步骤进行：将浸渍有芳纶帘子布浸渍胶的芳纶帘子布，经过电子束辐照固化干燥，而后对浸胶帘子布的性能进行检测，其中检测的性能指标有机械稳定性、化学稳定性和H抽出力。
固化的辐照电压为350KV，亦可以选择200～600KV中的其他数值；辐照吸收剂量选定为20KGy，亦可以选取0.5～100KGy中的其他数值。
测试结果
本发明提供了一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布，属于轮胎制造技术领域，芳纶帘子布浸渍胶由多异氰酸酯、丙烯酸酯和烯醚类单体组成，所述多异氰酸酯选自于含有两个以上异氰酸基的异氰酸酯中的一种或几种的组合物；其制备方法，将多异氰酸酯、丙烯酸酯和烯醚类单体置于一起，在35～50℃下搅拌25～40分钟；而浸胶芳纶帘子布则是由芳纶帘子布浸渍胶浸渍而成。与现有技术相比，本发明的有益效果：工艺设备简单；节省能源，能量利用率高；无溶剂排放，安全无污染；固化速度快，生产效率高；生产的帘子布与橡胶粘结性能优越。

Claims (7)

1.一种芳纶帘子布浸渍胶，其特征在于，由多异氰酸酯、丙烯酸酯和烯醚类单体组成，所述多异氰酸酯选自于含有两个以上异氰酸基的异氰酸酯中的一种或几种的组合物；所述多异氰酸酯选自于二苯基甲烷二异氰酸酯、4,4',4”-三苯基甲烷三异氰酸酯、2,2'-二甲基-3,3',5,5'-三苯基甲烷四异氰酸酯中的一种或几种的组合物。
2.根据权利要求1所述的芳纶帘子布浸渍胶，其特征在于，所述丙烯酸酯为单羟基丙烯酸酯。
3.根据权利要求1所述的芳纶帘子布浸渍胶，其特征在于，所述丙烯酸酯选自于甲基丙烯酸羟乙酯、丙烯酸羟乙酯、甲基丙烯酸羟丙酯、丙烯酸羟丙酯、4-羟基丁基丙烯酸酯或3-羟基-1-金刚烷基甲基丙烯酸酯中的一种或几种的组合物。
4.根据权利要求1所述的芳纶帘子布浸渍胶，其特征在于，所述烯醚类单体选自于丙烯基乙醚、乙烯基丁醚或丙烯基苄醚中的一种或几种的组合物。
5.根据权利要求1所述的芳纶帘子布浸渍胶，其特征在于，以重量份计，由100～300份的多异氰酸酯、70～240份的丙烯酸酯和10～40份烯醚类单体组成。
6.一种如权利要求1所述的芳纶帘子布浸渍胶的制备方法，其特征在于，将多异氰酸酯、丙烯酸酯和烯醚类单体置于一起，在35～50℃下搅拌25～40分钟。
7.一种浸胶芳纶帘子布，其特征在于，由如权利要求1所述的芳纶帘子布浸渍胶浸渍而成。
CN201410786817.6A 2014-12-18 2014-12-18 一种芳纶帘子布浸渍胶、制备方法及浸胶芳纶帘子布 Active CN104404765B (zh)