CN110607074A - 一种耐候性能优异的uv/湿气双固化有机硅树脂组合物及其制备方法 - Google Patents
一种耐候性能优异的uv/湿气双固化有机硅树脂组合物及其制备方法 Download PDFInfo
- Publication number
- CN110607074A CN110607074A CN201910881426.5A CN201910881426A CN110607074A CN 110607074 A CN110607074 A CN 110607074A CN 201910881426 A CN201910881426 A CN 201910881426A CN 110607074 A CN110607074 A CN 110607074A
- Authority
- CN
- China
- Prior art keywords
- organic silicon
- curing
- resin composition
- silicon resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (8)