CN109937142A - 装饰片及装饰板 - Google Patents

装饰片及装饰板 Download PDF

Info

Publication number
CN109937142A
CN109937142A CN201780070297.0A CN201780070297A CN109937142A CN 109937142 A CN109937142 A CN 109937142A CN 201780070297 A CN201780070297 A CN 201780070297A CN 109937142 A CN109937142 A CN 109937142A
Authority
CN
China
Prior art keywords
protective layer
surface protective
cosmetic sheet
resin
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201780070297.0A
Other languages
English (en)
Inventor
大岛野乃花
播摩一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to CN202210111957.8A priority Critical patent/CN114393896A/zh
Publication of CN109937142A publication Critical patent/CN109937142A/zh
Pending legal-status Critical Current

Abstract

提供可抑制装饰板的滑动的装饰片及装饰板。一种装饰片(20)以及一种装饰板(10)，装饰片(20)具备基材(1)以及形成在基材(1)上的表面保护层，装饰板(10)是通过在基板(5)上层叠装饰片(20)而形成的，表面保护层具备在基材(1)上形成的第一表面保护层(3)、以及在第一表面保护层(3)的一部分上形成的第二表面保护层(4)，第一表面保护层(3)含有固化型树脂，且表面的动摩擦系数在0.11以上0.30以下的范围内，第二表面保护层(4)含有树脂珠和无机化合物填料中的至少一者，第一表面保护层(3)的光泽高于第二表面保护层(4)的光泽。

Description

装饰片及装饰板
技术领域
本发明涉及可用于家具及普通内装材料等的装饰片及装饰板。
背景技术
以往，作为可用于家具及一般内装材料等的装饰片，例如有专利文献1所记载的技术。
在专利文献1所记载的技术中，设置在基材上并形成装饰片的最外表面的表面保护层形成为含有防污剂，该防污剂是通过在油性树脂或由电离放射线固化性单体的固化而形成的基质树脂中包含硅油而得到的。由此，对于装饰片的最外表面，将动摩擦系数的下限值设为0.1。
现有技术文献
专利文献
专利文献1：日本特开2008-247020号公报
发明内容
发明所要解决的课题
然而，在专利文献1所记载的技术中存在有以下问题：由于动摩擦系数的下限值低，因而当将贴附装饰片而制造的装饰板装载到车辆等时会发生滑动，堆叠的装饰片可能会倒塌。
本发明是鉴于上述情况而完成的，其目的在于提供一种可抑制装饰板的滑动的装饰片及装饰板。
用于解决课题的技术方案
为了解决上述课题，本发明的一个方面是具备基材、以及在所述基材上形成的表面保护层的装饰片。所述表面保护层含有固化型树脂、以及树脂珠和无机化合物填料中的至少一者，且表面的动摩擦系数在0.11以上0.30以下的范围内。
另外，为了解决上述课题，本发明的一个方面是在基材上层叠装饰片而形成的装饰板。
发明的效果
根据本发明的一个方面，能够提供可抑制装饰板的滑动的装饰片及装饰板。
附图简要说明
[图1]为表示本发明第一实施方式的装饰片及装饰板的构成的截面图。
[图2]为表示本发明第一实施方式的变形例的图。
具体实施方式
在以下的详细说明中，对于本发明的实施方式，为了提供完整的理解，对特定的细节进行说明。然而，显而易见的是，即使没有这些特定细节，也能够实施一个以上的实施方式。另外，为了使附图简洁，公知的结构及装置可能会用概略图来表示。
(第一实施方式)
以下，对于本发明的第一实施方式，参照附图来进行说明。
(装饰板)
参照图1，对装饰板10的构成进行说明。
如图1所示，装饰板10形成为具备装饰片20以及基板5，并且装饰片20层叠在基板5上。需要说明的是，“基板5上”是指在图1中基板5的上侧的面。
需要说明的是，装饰板10适用于(例如)大面积的拉门等内装用途。
(装饰片)
参照图1，对装饰片20的构成进行说明。
如图1所示，装饰片20形成为具备基材1、图案花纹层2、第一表面保护层3及第二表面保护层4，并且从靠近基材5的那一侧起依次层叠基材1、图案花纹层2、第一表面保护层3及第二表面保护层4。
(基材)
基材1是具有防湿性(水蒸气难以通过的性质)的片状的层。
在第一实施方式中，作为一个例子，对由具备第一纸基材1a、第二纸基材1b及防湿树脂层1c的防湿纸形成基材1的情况进行说明。
第一纸基材1a形成了基材1当中的配置在基板5一侧的部分。
因此，第一纸基材1a的一个面(图1中，第一纸基材1a的下侧的面)形成了基材1当中的与基板5相对的面(即背面1T)。
另外，第一纸基材1a通过使用(例如)在纤维素纤维间包含树脂的纸间强化纸来形成。
需要说明的是，作为纸间强化纸，例如优选为包含50质量％以上且小于100质量％的纤维素纤维的材料。另外，纸间强化纸的厚度例如设为15μm以上60μm以下的范围内。
第一纸基材1a的单位面积重量例如设为23g/m2。
第二纸基材1b形成了基材1当中的配置在图案花纹层2一侧的部分。
因此，第二纸基材1b的一个面(图1中，第二纸基材1b的上侧的面)形成了基材1当中的与图案花纹层2相对的面(即表面1S)。
另外，与第一纸基材1a同样地，第二纸基材1b通过使用(例如)在纤维素纤维间包含树脂的纸间强化纸来形成。
第二纸基材1b的单位面积重量例如设为30g/m2。
防湿树脂层1c配置在第一纸基材1a与第二纸基材1b之间。也就是说，基材1具备两片纸基材(第一纸基材1a、第二纸基材1b)、以及配置在两片纸基材之间的防湿树脂层1c。
另外，防湿树脂层1c通过使用不透过水蒸气的防湿树脂来形成。
作为防湿树脂，优选(例如)熔点在100℃以上200℃以下的范围内的烯烃类树脂等热塑性树脂。
防湿树脂层1c的厚度(例如)设为20μm以上70μm以下的范围内。
在第一实施方式中，如上所述，由不透过水蒸气的防湿纸来形成基材1。
由此，可使水蒸气不会从装饰片20的表面侧透过至背面侧，即，不会从第二表面保护层4一侧透过至基板5一侧，从而可以防止基板5因水蒸气(湿气)而变形。
因此，例如，通过采用装饰板10来形成大面积的拉门，可以防止拉门因水蒸气(湿气)而变形，可以防止拉门因变形而不能开闭。
另外，形成基材1的防湿纸具备第一纸基材1a、第二纸基材1b以及防湿树脂层1c，因而可使基材1具有厚度和刚性。
因此，装饰片20不易起皱，另外，可防止装饰片20发生卷曲。由此，可以相对容易地将装饰片20层压至基板5。
需要说明的是，在第一实施方式中，虽然使用防湿纸形成了基材1，但是也可以采用其他的构成，例如，也可以使用具有防湿性的树脂膜来形成基材1。
(图案花纹层)
图案花纹层2层叠于基材1上。需要说明的是，“基材1上”表示在图1中基材1的上侧的面。也就是说，图案花纹层2层叠于第二纸基材1b上。
另外，图案花纹层2是通过印刷而形成的、用于附加赋予设计性用的图案的层。也就是说，图案花纹层2是形成在基材1与表面保护层(第一表面保护层3、第二表面保护层4)之间的、且印刷有图案的层。
作为形成图案花纹层2的印刷油墨，可使用(例如)异吲哚啉酮黄、聚偶氮红、酞菁蓝、炭黑、氧化铁及氧化钛中的任一者、或者它们的混合物作为颜料。另外，形成图案花纹层2的印刷油墨中可使用(例如)乙酸乙酯、乙酸正丁酯、异丁醇及甲基异丁基酮作为溶剂。
作为图案，可选择(例如)木纹、软木、石纹、瓷砖、陶器及抽象图案等适合于使用装饰片20的部位的图案。
另外，图案花纹层2形成为具备图案油墨层2a以及导管油墨层2b，并且图案油墨层2a和导管油墨层2b依次层叠。
图案油墨层2a形成在基材1的表面1S上，并且是覆盖整个表面1S而成为图案的底色的层。
导管油墨层2b是显示底色以外的图案的层。
(第一表面保护层)
第一表面保护层3是形成在图案花纹层2上、且被覆整个图案花纹层2的片状的层。需要说明的是，“图案花纹层2上”是指在图1中图案花纹层2的上侧的面。
另外，第一表面保护层3由透明或半透明的材料(树脂)形成，其程度为可以透过第一表面保护层3而透视到图案花纹层2的图案。
作为第一表面保护层3的材料，优选(例如)热固性树脂。
作为热固性树脂，例如，若考虑到与第二表面保护层4的粘接性、装饰片20的变形追随性、以及耐擦伤性等，则优选使用2液固化型氨基甲酸酯树脂等具有氨基甲酸酯键的热固性树脂(粘结剂树脂)。
在第一实施方式中，作为一个例子，对第一表面保护层3含有固化性树脂(热固性树脂)的情况进行说明。另外，在第一实施方式中，作为一个例子，对第一表面保护层3含有具有氨基甲酸酯键的热固性树脂的情况进行说明。
此外，在第一实施方式中，对第一表面保护层3的表面的动摩擦系数在0.11以上0.30以下的范围内的情况进行说明。
在此，在热固性树脂中不添加二氧化硅颗粒等消光剂。另外，在热固性树脂中可使用乙酸乙酯、乙酸正丁酯作为溶剂。
作为2液固化型氨基甲酸酯树脂，可使用(例如)以多元醇为主体、以异氰酸酯为交联剂(固化剂)的氨基甲酸酯树脂。
作为多元醇，可使用在分子中具有2个以上羟基的多元醇。因此，作为多元醇，可使用(例如)聚乙二醇、聚丙二醇、丙烯酸多元醇、聚酯多元醇、聚醚多元醇、聚碳酸酯多元醇及聚氨酯多元醇。
另外，作为异氰酸酯，可使用在分子中具有2个以上异氰酸酯基的多价异氰酸酯。因此，作为异氰酸酯，可使用(例如)芳香族异氰酸酯、或者脂肪族或脂环式异氰酸酯。
作为芳香族异氰酸酯，可使用(例如)2,4-甲苯二异氰酸酯、二甲苯二异氰酸酯、4,4’-二苯基甲烷二异氰酸酯等。作为脂肪族或脂环式异氰酸酯，可使用(例如)1,6-六亚甲基二异氰酸酯、异佛尔酮二异氰酸酯、氢化甲苯二异氰酸酯、氢化二苯基甲烷二异氰酸酯等。
另外，作为2液固化型氨基甲酸酯树脂，可使用(例如)各种异氰酸酯的加成物或多聚体。例如，可使用甲苯二异氰酸酯的加成物、甲苯二异氰酸酯3聚体(trimer)等。需要说明的是，在上述异氰酸酯中，从耐候性、耐热黄变性也可以变好的方面出发，优选脂肪族或脂环式异氰酸酯，例如可使用1,6-六亚甲基二异氰酸酯。
如上所述，第一表面保护层3包含具有氨基甲酸酯键的热固性树脂即硬度高的树脂。因此，通过暴露于表面的第一表面保护层3，从而可提高装饰片20的耐损伤性。
(第二表面保护层)
第二表面保护层4是部分地形成在第一表面保护层3上、且被覆第一表面保护层3的一部分(例如，在第一表面保护层3的厚度方向上与导管油墨层2b相对向的部分)的层。即，第二表面保护层4可以以在平面视图中与导管油墨层2b重叠的方式而形成在第一表面保护层3上；第二表面保护层4也可以以在平面视图中与导管油墨层2b不重叠的方式而形成在第一表面保护层3上。需要说明的是，“第一表面保护层3上”是指在图1中第一表面保护层3的上侧的面。也就是说，第二表面保护层4形成在第一表面保护层3的一部分上。
如图1所示，第二表面保护层4形成为从第一表面保护层3的表面突出的部分。因此，通过在第一表面保护层3的厚度方向上在与导管油墨层2b相对向的部分处形成第二表面保护层4，从而能够以视觉和触感这两者的方式来显现木纹的导管。
另外，例如，在第一表面保护层3上的0.1％以上的面积上形成第二表面保护层4。需要说明的是，第二表面保护层4的面积的上限设为(例如)第一表面保护层3上的30％以下。
如上所述，在第一实施方式中，由耐伤性及抗污染性高的材料形成了第一表面保护层3。因此，即使第二表面保护层4的面积小，也能够将装饰片20的构成设为耐伤性及抗污染性优异的构成。
另外，第二表面保护层4由透明或半透明的材料(树脂)形成，其程度为可以透过第二表面保护层4及第一表面保护层3而透视到图案花纹层2的图案。
作为第二表面保护层4的材料，优选使用(例如)热固性树脂。
若考虑到与第一表面保护层3的粘接性等，作为热固性树脂，例如优选使用在2液固化型氨基甲酸酯树脂等具有氨基甲酸酯键的热固性树脂(粘结剂树脂)中添加作为无机化合物填料的二氧化硅颗粒等消光剂及合成树脂珠(树脂珠)中的至少一者而得到的混合物。
在第一实施方式中，作为第二表面保护层4的材料，使用了在具有氨基甲酸酯键的热固性树脂中添加作为消光剂的二氧化硅颗粒并且进一步添加合成树脂珠而得的材料。由此，使第一表面保护层3的光泽(光亮)高于第二表面保护层4的光泽。也就是说，第一表面保护层3的光泽高于第二表面保护层4的光泽。需要说明的是，第一表面保护层3的光泽并非一定要高于第二表面保护层4的光泽。即使在第一表面保护层3的光泽低于第二表面保护层4的光泽的情况下，若第一表面保护层3的光泽为(例如)30以上，则也可实现与第一表面保护层3的光泽高于第二表面保护层4的光泽时相同的效果。在此，对于本实施方式中的光泽的高低，虽然可通过目视来确定，但是也可以使用“BYK-Gardner公司”制的光泽计(商品名：Micro-gloss)及“堀場製作所”的光泽计作为光泽计来确定。
因此，在第一实施方式中，通过具有氨基甲酸酯键的热固性树脂(即，不受下层(第一表面保护层3)的光泽的影响的树脂)来形成第二表面保护层4。因此，可由第一表面保护层3和第二表面保护层4来适当地表现出视觉上的立体感。另外，由于具有氨基甲酸酯键的热固性树脂的硬度高，因而可提高装饰片20的耐伤性。
需要说明的是，如上所述，第一表面保护层3中没有添加消光剂。因此，与第一表面保护层3相比，添加了消光剂(二氧化硅颗粒)的第二表面保护层4可减少光的反射量并降低光泽(光亮)。因此，通过第一表面保护层3和第二表面保护层4，在装饰片20的表面上设置了光泽差，从而可以利用人类眼睛的错觉在视觉上感觉到立体感。
相对于热固性树脂的总质量，优选含有5质量％以上的二氧化硅颗粒。由此，可使第二表面保护层4的光泽相对于第一表面保护层3为足够的低，并可增大第二表面保护层4与第一表面保护层3之间的光泽差。因此，即使是第二表面保护层4的面积相对于第一表面保护层3的总面积为较小的构成，也可以适当地感觉到视觉上的立体感。需要说明的是，相对于热固性树脂的总质量，二氧化硅颗粒的上限设为35质量％以下。
在第一实施方式中，作为一个例子，对第二表面保护层4含有5质量％以上35质量％以下的范围内的二氧化硅颗粒的情况进行说明。
另外，在第一实施方式中，作为一个例子，对第二表面保护层4含有具有氨基甲酸酯键的热固性树脂、以及二氧化硅颗粒的情况进行说明。
在第一实施方式中，由于使第一表面保护层3的光泽(光亮)大于第二表面保护层4的光泽(光亮)，因而可提高第一表面保护层3的表面平滑度，指纹(手垢)污物变得难以附着，从而可提高装饰片20的抗污染性。即使在第一表面保护层3的涂布量为低涂布量的情况下也能够获得提高抗污染性的效果。另外，可进行在美国等流行的涂装格调的图案表现(木纹表现等)。另外，由于第一表面保护层3的白浊减少，因而更细腻且有透明感的图案的设计表现成为可能。
作为合成树脂珠，可使用(例如)透明度高的氨基甲酸酯树脂珠。由此，可提高第二表面保护层4的透明度，可更加清楚地透视看到用于赋予设计的图案花纹层2的图案。将合成树脂珠的平均粒径设为30μm以上。需要说明的是，在本实施方式中，对于所添加的合成树脂珠的平均粒径，虽然没有上限值，但是从与膜厚的关系考虑，合成树脂珠的平均粒径优选设为120μm以下。
在第一实施方式中，作为一个例子，对第二表面保护层4含有氨基甲酸酯树脂珠作为树脂珠的情况进行说明。
在第一实施方式中，作为一个例子，对于在第二表面保护层4中，相对于100质量％热固性树脂(粘结剂树脂)，含有20质量％以上25质量％以下的范围内的氨基甲酸酯树脂珠的情况进行说明。
另外，将第二表面保护层4的表面采用接触式粗糙度仪测定的最大高度Rmax值设为30μm以上。也就是说，第二表面保护层4的表面采用接触式粗糙度仪测定的最大高度为30μm以上。由此，可更加适宜地感觉到触感所产生的立体感。在本实施方式中，对于上述采用接触式粗糙度仪测定的最大高度，虽然没有上限值，但是从所添加的氨基甲酸酯树脂珠的尺寸等观点考虑，第二表面保护层4的表面采用接触式粗糙度仪测定的最大高度Rmax值优选为120μm以下。
需要说明的是，在第一实施方式中，虽然使用了热固性树脂作为粘结剂树脂，但是作为粘结剂树脂，也可以使用其他的构成。也就是说，例如也可设为使用电离放射线固化型树脂作为粘结剂树脂的构成。在这种情况下，作为电离放射线固化型树脂，例如紫外线固化型树脂是优选的。另外，作为紫外线固化型树脂，例如可使用(甲基)丙烯酸类树脂、有机硅类树脂、聚酯类树脂、氨基甲酸酯类树脂、酰胺类树脂、环氧类树脂。由此，可提高第二表面保护层4即装饰片20的最外表面层的硬度，并可提高装饰片20的耐磨损性、耐擦伤性、耐溶剂性等表面物性。此外，例如也可以设为使用热固性树脂和电离放射线固化型树脂的混合物作为粘结剂树脂的构成。
另外，在第一实施方式中，虽然示出了在热固性树脂中添加合成树脂珠的例子，但是也可以采用其他的构成。也就是说，例如也可以设为在热固性树脂中添加无机化合物填料的构成。
另外，第二表面保护层4的形状没有特别的限定，可以设为圆形、四边形、六边形等规则排列的定形的形状，也可以设为不定型的图案形状。另外，对于第二表面保护层4的形状，可以设为与图案花纹层2的图案(例如导管油墨层2)一致的形状，在这种情况下，可更真实地看到图案。
如上所述，表面保护层(第一表面保护层3、第二表面保护层4)含有固化型树脂、以及树脂珠和无机化合物填料中的至少一者，且表面的动摩擦系数在0.11以上0.30以下的范围内。
(基板)
基板5是通过使用金属类材料或者木质类材料而形成的板状部件。
作为金属类材料，例如可使用铝、钢、不锈钢、复合板。作为复合板，例如可使用具备成为芯材的树脂层、以及贴附在树脂层的两面的金属板(铝、镀铝锌板、不锈钢等)的材料。
作为木质类材料，例如可使用MDF(medium density fiberboard，中密度纤维板)、胶合板、刨花板(Particle board)等。
需要说明的是，上述第一实施方式是本发明的一个例子，本发明并不限于上述的第一实施方式，即使是本实施方式以外的方式，只要其不脱离本发明所涉及的技术思想，则也可根据设计等进行各种变化。
(第一实施方式的效果)
如上所述，第一实施方式的装饰片20可实现以下效果。
(1)形成在基材1上的表面保护层含有固化型树脂、以及树脂珠和无机化合物填料中的至少一者，且表面的动摩擦系数在0.11以上0.30以下的范围内。
因此，可将装饰片20的动摩擦系数设为能够抑制滑动的发生的数值，可提供能够抑制装饰板10的滑动的装饰片20。
(2)第一表面保护层3含有固化型树脂，且表面的动摩擦系数在0.11以上0.30以下的范围内。另外，第二表面保护层4含有树脂珠和无机化合物填料中的至少一者。并且，第一表面保护层3的光泽高于第二表面保护层4的光泽。
因此，通过第一表面保护层3和第二表面保护层4，在装饰片20的表面上设置了光泽差，从而可以利用人类眼睛的错觉在视觉上感觉到立体感。
(3)第二表面保护层4在5质量％以上35质量％以下的范围内含有二氧化硅颗粒。
因此，通过相对较多地将第二表面保护层4中所含有的二氧化硅颗粒设为5质量％以上，从而可充分地降低第二表面保护层4的光泽，可增大第二表面保护层4与第一表面保护层3的光泽差。由此，即使在第二表面保护层4的面积小的情况下，也可适宜地感觉到视觉上的立体感。
(4)第二表面保护层4的表面采用接触式粗糙度仪测定的最大高度在30μm以上120μm以下的范围内。
因此，可更加适宜地感觉到由触感所产生的立体感。
(5)第一表面保护层3包含具有氨基甲酸酯键的热固性树脂。
因此，可提高第一表面保护层3与其他层(例如图案花纹层2及第二表面保护层4等)的粘接性、装饰片20的变形追随性、以及耐擦伤性。
(6)第二表面保护层4包含具有氨基甲酸酯键的热固性树脂、以及二氧化硅颗粒。
因此，可提高第二表面保护层4与邻近的层(例如第一表面保护层3等)的粘接性、装饰片20的变形追随性、以及耐擦伤性。
(7)相对于100质量％粘结剂树脂，第二表面保护层4中含有20质量％以上25质量％以下的范围内的氨基甲酸酯树脂珠。
因此，可将第二表面保护层4的表面的动摩擦系数设为这样的动摩擦系数，其使得在将贴附装饰片20而制造的装饰板10堆叠的状态下难以发生装饰板10的倒塌。
(8)表面保护层所含有的树脂珠为氨基甲酸酯树脂珠。
因此，可提高第二表面保护层4的透明度，从而可通过第二表面保护层4而更加清楚地透视到用于赋予设计的图案花纹层2的图案。
(9)基材1具备第一纸基材1a、第二纸基材1b、以及配置在该两片纸基材之间的防湿树脂层1c。
因此，可使基材1具有厚度和刚性，装饰片20不易起皱，另外，可防止装饰片20发生卷曲。由此，可以容易地将装饰片20层压于基板5。
(10)具备在基材1与表面保护层之间形成的、且印刷有图案的图案花纹层2。
因此，可对装饰片20附加图案。
另外，如上所述，第一实施方式的装饰板10可实现以下效果。
(11)装饰板10是通过在基板5上层叠装饰片20而形成的。
因此，可将具备装饰片20而形成的装饰板10的动摩擦系数设为能够抑制滑动的发生的数值，可提供能够抑制装饰板10的滑动的装饰板10。
(变形例)
(1)在第一实施方式中，示出了通过第一表面保护层3与第二表面保护层4的光泽差、以及第一表面保护层3与第二表面保护层4的高低差来感觉到视觉的立体感和触感所产生的立体感的例子，但是也可以采用其他的构成。
也就是说，例如，如图2所示，也可以设为这样的构成：对装饰片20施加由压印加工所产生的压印30，通过压印30从而进一步感觉到触感所产生的立体感。因此，关于变形例的装饰片20，对与这样的面(该面为表面保护层(第一表面保护层3、第二表面保护层4)的与基材1相对的面)相反一侧的面(表面1S)进行了压印加工。需要说明的是，压印30也可以形成在第二表面保护层4彼此之间。另外，压印30的形状可以一直延伸到基材1的背面1T。
在这种情况下，压印加工中，可使装饰片20穿过具有深度15μm以上的凹部的压印辊与硬度为50度以上且小于90度的橡胶制背辊之间，从而对装饰片20施加凹凸形状。作为硬度的测量方法，可使用(例如)JIS K 6301 A型。然后，经由粘接层6将基板5贴合到施加有压印30的装饰片20上，从而形成装饰板10。
(2)在第一实施方式中，虽然设为在第二表面保护层4中含有相对于100质量％热固性树脂(粘结剂树脂)为20质量％以上25质量％以下的范围内的氨基甲酸酯树脂珠的构成，但并不限于此。
也就是说，也可以设为在第二表面保护层4中含有相对于100质量％热固性树脂(粘结剂树脂)为10质量％以上35质量％以下的范围内的氨基甲酸酯树脂珠的构成。
实施例
参照第一实施方式的图1，同时，通过下述的实施例来说明实施例1及2的装饰片、以及比较例1及2的装饰片。
(实施例1)
实施例1的装饰片具有以下构成。
基材1通过使用单位面积重量为29g/m2的薄页纸来形成。
表面保护层(第一表面保护层3、第二表面保护层4)通过含有氨基甲酸酯树脂珠而形成。
(实施例2)
除了使用单位面积重量为50g/m2的薄页纸来形成基材1的构成以外，实施例2的装饰片1的构成与实施例1的装饰片相同。
(比较例1)
除了通过含有丙烯酸树脂珠来形成表面保护层的构成以外，比较例1的装饰片的构成与实施例1的装饰片相同。
(比较例2)
除了通过使用单位面积重量为50g/m2的薄页纸来形成基材1的构成以外，比较例2的装饰片1的构成与比较例1的装饰片相同。
(性能评价)
对于实施例1及2的装饰片20、以及比较例1及2的装饰片20，分别依照以下方法来进行性能评价(耐磨损性、耐伤性、耐溶剂性、动摩擦系数、耐剥离性、耐水性、抗污染性、外观)。评价结果示出于表1中。
[表1]
(耐磨损性)
通过磨损C试验来评价耐磨损性。
磨损C试验在负荷500g的250次旋转下进行。
(耐伤性)
耐伤性通过使用Hoffman划痕硬度测试仪(BYK-Gardner公司制)来进行评价。
(耐溶剂性)
耐溶剂性通过进行MEK(甲基乙基酮)反复摩擦试验并使其反复50次来进行评价。
(动摩擦系数)
动摩擦系数(COF：kinetic coefficient of friction)通过滑动试验来进行评价。
滑动试验在以下条件下进行。
板：厚度12mm的刨花板
纸(单元)：装饰纸
表面保护层：涂布100g/m2的2液乙酸乙烯酯树脂乳液粘接剂，加压层叠(50N/cm2)24小时
速度：20mm/s(根据JIS P 8147：2010)
(耐剥离性)
通过在贴附玻璃纸带并在常温环境下放置10日后进行剥离而得的结果、以及在贴附玻璃纸带并在60℃的环境下放置2日后进行剥离而得的结果来评价耐剥离性。
(耐水性)
耐水性通过使用沸水的1小时试验、以及使用蒸馏水的4小时试验来进行评价。
(抗污染性)
抗污染性根据JIS K 6902_2008的对于热固性树脂的高压装饰板试验方法来进行评价。
另外，在高压装饰板试验中，分别使用以下物质来进行4小时：色拉油(J-OilMills股份公司制)、咖啡(将2g速溶咖啡溶于180ml自来水中而得)、红茶(将茶袋浸入120ml沸腾自来水中2分钟而得)、番茄酱(Kagome股份公司制)、以及芥末(SB食品股份公司售)。
(外观)
通过外观设计的感官评价来评价外观。
(综合评价)
如表1所示，可以确认：与比较例1及比较例2的装饰片20相比，实施例1及实施例2的装饰片20的动摩擦系数增加了0.125以上。
(滑动性)
将各实施例及各比较例的装饰片20分别贴附于基板5，从而分别制作了各实施例及各比较例的装饰板10。每片所制作的装饰板10的尺寸为1米×2米(常用的拉门的尺寸)，其质量为约1千克。
以每种装饰片为10片的方式，将各实施例及各比较例的装饰片20堆叠并加装到车辆等上。
结果是，对于实施例1及实施例2的各装饰板10，当加装到车辆等上并移动时未发生滑动，并且所堆叠的装饰板10没有发生倒塌。另一方面，对于比较例1及比较例2的各装饰板10，当加装到车辆等上并移动时发生了滑动，并且所堆叠的装饰板10发生了倒塌。
另外，在以每种装饰板为10片的方式将各实施例及各比较例的装饰板10堆叠的状态下，相对于水平方向将所堆叠的装饰板10倾斜45°。
结果是，对于实施例1及实施例2的各装饰板10，即使在相对于水平方向倾斜45°的状态下也未发生滑动，并且所堆叠的装饰板10没有发生倒塌。
另一方面，对于比较例1及比较例2的各装饰板10，发生了滑动，并且所堆叠的装饰板10发生了倒塌。
由上可得知：相比于比较例1及比较例2的装饰片20，实施例1及实施例2的装饰片20可抑制通过贴附装饰片而制造的装饰板的滑动。
符号的说明
1…基材、1a…第一纸基材、1b…第一纸基材、1c…防湿树脂层、2…图案花纹层、2a…图案油墨层、2b…导管油墨层、3…第一表面保护层、4…第二表面保护层、5…基板、6…粘接层、10…装饰板、20…装饰片、30…压印

Claims (13)

1.一种装饰片，其特征在于，具备：
基材、以及
形成在所述基材上的表面保护层，
所述表面保护层含有固化型树脂、以及树脂珠和无机化合物填料中的至少一者，且表面的动摩擦系数在0.11以上0.30以下的范围内。
2.根据权利要求1所述的装饰片，其特征在于，所述表面保护层具备在所述基材上形成的第一表面保护层、以及在所述第一表面保护层的一部分上形成的第二表面保护层，
所述第一表面保护层含有固化型树脂，且表面的动摩擦系数在0.11以上0.30以下的范围内，
所述第二表面保护层含有树脂珠和无机化合物填料中的至少一者，
所述第一表面保护层的光泽高于所述第二表面保护层的光泽。
3.根据权利要求2所述的装饰片，其特征在于，所述第二表面保护层含有5质量％以上35质量％以下的范围内的二氧化硅颗粒。
4.根据权利要求2或3所述的装饰片，其特征在于，所述第二表面保护层的表面采用接触式粗糙度仪测定的最大高度在30μm以上120μm以下的范围内。
5.根据权利要求2至权利要求4中任一项所述的装饰片，其特征在于，所述第一表面保护层包含具有氨基甲酸酯键的热固性树脂。
6.根据权利要求2至权利要求5中任一项所述的装饰片，其特征在于，所述第二表面保护层包含具有氨基甲酸酯键的热固性树脂、以及二氧化硅颗粒。
7.根据权利要求2至权利要求6中任一项所述的装饰片，其特征在于，所述第二表面保护层包含粘结剂树脂以及氨基甲酸酯树脂珠，
相对于100质量％的所述粘结剂树脂，所述氨基甲酸酯树脂珠的含量在10质量％以上35质量％以下的范围内。
8.根据权利要求7所述的装饰片，其特征在于，相对于100质量％的所述粘结剂树脂，所述氨基甲酸酯树脂珠的含量在20质量％以上25质量％以下的范围内。
9.根据权利要求1至权利要求6中任一项所述的装饰片，其特征在于，所述树脂珠为氨基甲酸酯树脂珠。
10.根据权利要求1至权利要求9中任一项所述的装饰片，其特征在于，所述基材具备两片纸基材、以及配置在所述两片纸基材之间的防湿树脂层。
11.根据权利要求1至权利要求10中任一项所述的装饰片，其特征在于，对所述表面保护层的与所述基材相对的面相反的那一侧的面进行压印加工。
12.根据权利要求1至权利要求11中任一项所述的装饰片，其特征在于，具备在所述基材与所述表面保护层之间形成的、且印刷有图案的图案花纹层。
13.一种装饰板，其特征在于，所述装饰板是通过在基板上层叠权利要求1至权利要求12中任一项所述的装饰片而形成的。
CN201780070297.0A 2016-11-15 2017-11-10 装饰片及装饰板 Pending CN109937142A (zh)