CN101626995B - 处理的耐火材料和制造方法 - Google Patents

处理的耐火材料和制造方法 Download PDF

Info

Publication number
CN101626995B
CN101626995B CN200880007318.5A CN200880007318A CN101626995B CN 101626995 B CN101626995 B CN 101626995B CN 200880007318 A CN200880007318 A CN 200880007318A CN 101626995 B CN101626995 B CN 101626995B
Authority
CN
China
Prior art keywords
refractory material
refractory
protective
protective material
treated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200880007318.5A
Other languages
English (en)
Chinese (zh)
Other versions
CN101626995A (zh
Inventor
A·M·汤普森
R·舒巴
P·J·梅施特
K·L·卢特拉
V·贝拉尼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Air Products and Chemicals Inc
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Publication of CN101626995A publication Critical patent/CN101626995A/zh
Application granted granted Critical
Publication of CN101626995B publication Critical patent/CN101626995B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/12—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on chromium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/009—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone characterised by the material treated
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C04B41/50—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials
    • C04B41/5007—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials with salts or salty compositions, e.g. for salt glazing
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C04B41/50—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials
    • C04B41/5025—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials with ceramic materials
    • C04B41/5031—Alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/80—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone of only ceramics
    • C04B41/81—Coating or impregnation
    • C04B41/85—Coating or impregnation with inorganic materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3206—Magnesium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C04B2235/3225—Yttrium oxide or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3232—Titanium oxides or titanates, e.g. rutile or anatase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
    • C04B2235/3248—Zirconates or hafnates, e.g. zircon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3272—Iron oxides or oxide forming salts thereof, e.g. hematite, magnetite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3418—Silicon oxide, silicic acids or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3427—Silicates other than clay, e.g. water glass
    • C04B2235/3463—Alumino-silicates other than clay, e.g. mullite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y10T428/249955—Void-containing component partially impregnated with adjacent component
    • Y10T428/249956—Void-containing component is inorganic
    • Y10T428/249957—Inorganic impregnant

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Compositions Of Oxide Ceramics (AREA)
  • Furnace Housings, Linings, Walls, And Ceilings (AREA)
CN200880007318.5A 2007-03-07 2008-02-06 处理的耐火材料和制造方法 Expired - Fee Related CN101626995B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US11/683,260 US8105683B2 (en) 2007-03-07 2007-03-07 Treated refractory material and methods of making
US11/683,260 2007-03-07
PCT/US2008/053136 WO2008109222A2 (en) 2007-03-07 2008-02-06 Treated refractory material and methods of making

Publications (2)

Publication Number Publication Date
CN101626995A CN101626995A (zh) 2010-01-13
CN101626995B true CN101626995B (zh) 2014-02-19

Family

ID=39387154

Family Applications (1)

Application Number Title Priority Date Filing Date
CN200880007318.5A Expired - Fee Related CN101626995B (zh) 2007-03-07 2008-02-06 处理的耐火材料和制造方法

Country Status (7)

Country Link
US (1) US8105683B2 (enExample)
EP (1) EP2121539B1 (enExample)
JP (1) JP5503297B2 (enExample)
CN (1) CN101626995B (enExample)
AU (1) AU2008223302B2 (enExample)
CA (1) CA2679382C (enExample)
WO (1) WO2008109222A2 (enExample)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090188347A1 (en) * 2007-03-07 2009-07-30 General Electric Company Treated refractory material and methods of making
US8481152B2 (en) * 2008-08-14 2013-07-09 General Electric Company Refractory material with improved resistance to molten slag
US8197566B2 (en) * 2008-12-08 2012-06-12 General Electric Company Gasifier additives for improved refractory life
US20110033613A1 (en) * 2009-08-04 2011-02-10 Battelle Memorial Institute Method and Composition for Protection of Refractory Materials in Aggressive Environments
DE102009045698A1 (de) * 2009-10-14 2011-04-21 Evonik Degussa Gmbh Verfahren zum Infiltrieren von porösen keramischen Bauteilen
DE112011103740A5 (de) 2010-11-12 2013-08-08 Technische Universität Bergakademie Freiberg Auskleidungsmaterial für Vergasungsanlagen bestehend aus einem alkalikorrosionsbeständigen und temperaturwechselbeständigen chromoxid- und kohlenstofffreien oxidkeramischen Werkstoff und seine Verwendung
FR2974081B1 (fr) 2011-04-15 2016-02-26 Saint Gobain Ct Recherches Produit d'oxydes de chrome, de zirconium et d'hafnium
DE102011115759B4 (de) * 2011-10-12 2015-10-01 Thyssenkrupp Industrial Solutions Ag Keramikkörper, Verfahren zu seiner Herstellung und Verwendung eines Beschichtungsmaterials
CN102514293B (zh) * 2011-11-16 2014-09-24 中钢集团洛阳耐火材料研究院有限公司 一种纳米多孔高效隔热板的制备方法
DE102012003478B4 (de) 2012-02-21 2015-08-06 Technische Universität Bergakademie Freiberg Verwendung eines oxidkeramischen Werkstoffes aus CaZrO3 als Auskleidungsmaterial für Vergasungsanlagen
WO2013187182A1 (ja) * 2012-06-15 2013-12-19 株式会社ノリタケカンパニーリミテド アルミナ多孔質体およびその製造方法
BR112015003774A2 (pt) 2012-08-21 2017-07-04 Stellar Mat Incorporated composição refratária e processo para formar um artigo refratário
FR2996843B1 (fr) 2012-10-15 2020-01-03 Saint-Gobain Centre De Recherches Et D'etudes Europeen Produit d'oxyde de chrome.
CN103011817B (zh) * 2012-12-24 2014-06-11 中国科学院金属研究所 一种钇硅氧多孔高温陶瓷材料的制备方法
CN103496992B (zh) * 2013-09-22 2015-04-01 郑州亨瑞达新材料有限公司 一种铬锆莫来石耐火材料及其制备方法
DE102016220246A1 (de) * 2016-10-17 2018-04-19 Siemens Aktiengesellschaft Keramische Hitzeschilde mit Infiltrationscoating
CN106747157A (zh) * 2016-11-24 2017-05-31 天津航空机电有限公司 一种用于探测器腔体的填充材料
CN110294633B (zh) * 2018-03-23 2021-11-09 国家能源投资集团有限责任公司 多孔陶瓷以及气化渣制备多孔陶瓷的方法
CN108637231B (zh) * 2018-07-30 2023-09-12 广东中天创展球铁有限公司 一种球化处理用铁水包及其制作工艺
CN112811448A (zh) * 2021-01-18 2021-05-18 朱广东 一种氧化镁还原渣的回收工艺
CN114891376B (zh) * 2022-05-07 2023-04-25 武汉科技大学 基于铬化工渣的高发射率红外辐射涂料、涂层及其制备方法
CN116422339B (zh) * 2023-03-21 2024-09-27 榆林学院 一种改性气化渣载镍锡催化剂及其在环己醇脱氢中的应用
CN117362015B (zh) * 2023-10-27 2024-04-12 河南省瑞泰科实业集团有限公司 高纯刚玉砖及其制备方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3789096A (en) * 1967-06-01 1974-01-29 Kaman Sciences Corp Method of impregnating porous refractory bodies with inorganic chromium compound

Family Cites Families (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3031340A (en) * 1957-08-12 1962-04-24 Peter R Girardot Composite ceramic-metal bodies and methods for the preparation thereof
GB1087035A (en) 1964-11-27 1967-10-11 Shinagawa Fire Brick Co Ltd A process for the manufacture of refractory brick
US3734767A (en) * 1970-06-18 1973-05-22 Kaman Sciences Corp Ceramic treating process and product produced thereby
US3888790A (en) * 1971-11-24 1975-06-10 Du Pont Process for preparing a catalytically active ceramic coatings
US3992161A (en) * 1973-01-22 1976-11-16 The International Nickel Company, Inc. Iron-chromium-aluminum alloys with improved high temperature properties
GB1569474A (en) * 1976-03-26 1980-06-18 Centre Rech Metallurgique Method of the quality of refractory bricks
FR2345408A1 (fr) 1976-03-26 1977-10-21 Centre Rech Metallurgique Procede pour ameliorer la qualite des briques refractaires
JPS6042184B2 (ja) 1977-10-12 1985-09-20 東芝セラミツクス株式会社 緻密質酸化クロム耐火物の製造方法
JPS6025396B2 (ja) 1978-12-08 1985-06-18 日本化学工業株式会社 改質セラミツクスの製造法
US4374897A (en) * 1980-03-04 1983-02-22 Nippon Chemical Industrial Co., Ltd. Chromium oxide-based sintered bodies and process for production thereof
US4568652A (en) 1984-10-15 1986-02-04 The United States Of America As Represented By The Secretary Of The Interior Soluble additives to improve high temperature properties of alumina refractories
JPS6270258A (ja) 1985-09-20 1987-03-31 日本特殊陶業株式会社 酸化クロム質焼結体
FR2647437B1 (fr) * 1989-05-26 1991-10-04 Savoie Refractaires Nouvelles compositions refractaires contenant de la zircone monoclinique et articles formes a partir de ces compositions presentant une resistance mecanique a chaud et une resistance aux chocs thermiques ameliorees
JPH03228860A (ja) 1990-01-31 1991-10-09 Nippon Steel Corp マグクロ質耐火れんがの製造方法
FR2665434B1 (fr) 1990-08-03 1993-09-24 Prod Cellulosiques Isolants Procede pour la fabrication d'un materiau refractaire isolant et materiau ainsi obtenu.
JP2951432B2 (ja) 1991-05-16 1999-09-20 黒崎窯業株式会社 マグネシア含有不焼成耐火物
JPH0543306A (ja) 1991-08-16 1993-02-23 Kurosaki Refract Co Ltd マグネシア−クロミア質焼成耐火物
DE4140417C1 (enExample) * 1991-12-07 1993-04-29 Dyko Industriekeramik Gmbh, 4000 Duesseldorf, De
JPH07165461A (ja) 1993-12-14 1995-06-27 Harima Ceramic Co Ltd マグネシア−クロム質焼成レンガおよびその製造方法
JPH07291716A (ja) 1994-04-15 1995-11-07 Nippon Steel Corp 塩基性耐火物
JPH0859345A (ja) * 1994-08-25 1996-03-05 Shinagawa Refract Co Ltd ジルコニア質複合焼結体及びその製造方法。
JPH08245261A (ja) 1995-03-08 1996-09-24 Okayama Ceramics Gijutsu Shinko Zaidan 耐アルカリ性クロム系耐火材料及びそれを用いた耐火煉瓦の製造方法
KR100611136B1 (ko) * 1996-12-10 2006-08-10 지멘스 악티엔게젤샤프트 열 절연층을 가지며 고온 가스에 노출될 수 있는 제품 및 그 제조 방법
US6200631B1 (en) 1997-10-27 2001-03-13 Praxair Technology, Inc. Method for producing corrosion resistant refractories
JP2000327406A (ja) 1999-05-11 2000-11-28 Nippon Steel Corp 耐スラグ浸潤性に優れたクロミア含有れんがおよび溶融金属容器
JP2002020161A (ja) 2000-07-03 2002-01-23 Mitsubishi Heavy Ind Ltd 高耐食性耐火物用バインダー材
JP3723093B2 (ja) 2001-04-20 2005-12-07 三菱重工業株式会社 高耐食性耐火物材の製造方法
US6815386B1 (en) * 2002-10-23 2004-11-09 Kyei-Sing Kwong Use of phosphates to reduce slag penetration in Cr2O3-based refractories
JP4178239B2 (ja) * 2003-10-09 2008-11-12 独立行政法人産業技術総合研究所 高密着性酸化物皮膜及びその製造方法
CN1296323C (zh) 2004-04-30 2007-01-24 洛阳耐火材料研究院 以Cr2O3为基的耐火复合材料
US7666512B2 (en) * 2004-08-09 2010-02-23 United Technologies Corporation Thermal resistant environmental barrier coating
KR101157047B1 (ko) 2004-12-24 2012-06-21 주식회사 포스코 마그네시아-크롬질 내화벽돌 및 그 제조방법
FR2883282B1 (fr) 2005-03-15 2007-05-25 Saint Gobain Ct Recherches Revetement interne de reacteur de gazeificateur

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3789096A (en) * 1967-06-01 1974-01-29 Kaman Sciences Corp Method of impregnating porous refractory bodies with inorganic chromium compound

Also Published As

Publication number Publication date
US8105683B2 (en) 2012-01-31
JP2010520149A (ja) 2010-06-10
EP2121539A2 (en) 2009-11-25
AU2008223302B2 (en) 2012-02-02
CN101626995A (zh) 2010-01-13
CA2679382A1 (en) 2008-09-12
JP5503297B2 (ja) 2014-05-28
WO2008109222A3 (en) 2008-10-30
EP2121539B1 (en) 2014-08-13
US20080216603A1 (en) 2008-09-11
WO2008109222A2 (en) 2008-09-12
AU2008223302A1 (en) 2008-09-12
CA2679382C (en) 2013-11-12

Similar Documents

Publication Publication Date Title
CN101626995B (zh) 处理的耐火材料和制造方法
US20090188347A1 (en) Treated refractory material and methods of making
US7037477B2 (en) Silicon carbide-based porous material and process for production thereof
US5011529A (en) Cured surfaces and a process of curing
US8481152B2 (en) Refractory material with improved resistance to molten slag
CN105188987B (zh) 耐火物和铸造用喷嘴
JP7020795B2 (ja) スラリー系反応結合された環境バリアコーティング
WO2009119683A1 (ja) プレートれんが及びその製造方法
JP2012502878A (ja) 多孔質のムライト含有複合体の作製方法
KR20140011307A (ko) 산화 매질에서 고온에 견딜 수 있는 재료 및 부품, 및 그들의 제조 방법
JP2018177607A (ja) 耐火物及びその製造方法
JPH10510474A (ja) 気体不透過性の層を形成することのできる外層を有する停止ロッド
JP2000327401A (ja) スライドゲート用プレート
JP2005144462A (ja) 連続鋳造用浸漬ノズル及びその製造方法
JPH10310474A (ja) ＳｉＣ−Ｓｉ複合セラミックス材
JP4312628B2 (ja) 鋼の連続鋳造用ストッパー
JPH0772105B2 (ja) 窒化珪素質焼結体およびその製造方法
JP2948020B2 (ja) 炭素含有耐火物
JPH05132354A (ja) 不焼成マグネシア・カーボンれんが
JP2000095556A (ja) マグネシア・カーボン系耐火物
JPH1110319A (ja) スライディングノズルプレート
JPH0632648A (ja) 炭素含有耐火物
JPH05139818A (ja) 不焼成マグネシア・ドロマイト・カーボンれんが
JPH1110320A (ja) イマージョンノズル
JPH1046281A (ja) 耐食性及び熱衝撃抵抗性に優れた複合材料とそれを用いた構造体

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
TR01 Transfer of patent right

Effective date of registration: 20200103

Address after: Pennsylvania, USA

Patentee after: Air Products and Chemicals, Inc.

Address before: New York State, USA

Patentee before: General Electric Co.

TR01 Transfer of patent right
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20140219

CF01 Termination of patent right due to non-payment of annual fee