WO2019111481A1 - Feuille d'usinage de pièce et procédé de production de pièce usinée - Google Patents

Feuille d'usinage de pièce et procédé de production de pièce usinée Download PDF

Info

Publication number
WO2019111481A1
WO2019111481A1 PCT/JP2018/033767 JP2018033767W WO2019111481A1 WO 2019111481 A1 WO2019111481 A1 WO 2019111481A1 JP 2018033767 W JP2018033767 W JP 2018033767W WO 2019111481 A1 WO2019111481 A1 WO 2019111481A1
Authority
WO
WIPO (PCT)
Prior art keywords
sensitive adhesive
pressure
work
adhesive layer
active energy
Prior art date
Application number
PCT/JP2018/033767
Other languages
English (en)
Japanese (ja)
Inventor
孝文 小笠原
美紗季 坂本
尚哉 佐伯
Original Assignee
リンテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リンテック株式会社 filed Critical リンテック株式会社
Priority to JP2019558016A priority Critical patent/JP7162612B2/ja
Priority to CN201880063272.2A priority patent/CN111149191B/zh
Priority to KR1020207008253A priority patent/KR102515877B1/ko
Priority to TW108101471A priority patent/TWI809030B/zh
Publication of WO2019111481A1 publication Critical patent/WO2019111481A1/fr

Abstract

Une feuille d'usinage de pièce comprend un matériau de base et une couche adhésive stratifiée sur un côté surface du matériau de base. La feuille d'usinage de pièce est caractérisée en ce que : la couche adhésive comprend un adhésif durcissable par rayonnement d'énergie active ; le rapport d'atomes d'oxygène R0 n'est pas supérieur à 28 % atomique, tel que mesuré par spectroscopie photoélectronique à rayons X sur une surface sur le côté opposé de la couche adhésive au matériau de base ; et le rapport d'atomes d'oxygène R100 est situé dans la plage allant de 20 à 29 % atomique, tel que mesuré par spectroscopie photoélectronique à rayons X à une position dans la couche adhésive qui se situe à une profondeur de 100 nm de la surface sur le côté opposé de la couche adhésive au matériau de base. Ladite feuille d'usinage de pièce permet d'éliminer de manière adéquate l'adhésif au moyen d'eau courante et permet de séparer de manière adéquate la pièce après usinage, ledit adhésif étant dérivé de la couche adhésive fixée à la pièce après usinage.
PCT/JP2018/033767 2017-12-07 2018-09-12 Feuille d'usinage de pièce et procédé de production de pièce usinée WO2019111481A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
JP2019558016A JP7162612B2 (ja) 2017-12-07 2018-09-12 ワーク加工用シートおよび加工済みワークの製造方法
CN201880063272.2A CN111149191B (zh) 2017-12-07 2018-09-12 工件加工用片及已加工工件的制造方法
KR1020207008253A KR102515877B1 (ko) 2017-12-07 2018-09-12 워크 가공용 시트 및 가공된 워크의 제조방법
TW108101471A TWI809030B (zh) 2017-12-07 2019-01-15 工件加工用片材及加工完成的工件的製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-235377 2017-12-07
JP2017235377 2017-12-07

Publications (1)

Publication Number Publication Date
WO2019111481A1 true WO2019111481A1 (fr) 2019-06-13

Family

ID=66750873

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/JP2018/033767 WO2019111481A1 (fr) 2017-12-07 2018-09-12 Feuille d'usinage de pièce et procédé de production de pièce usinée
PCT/JP2018/043553 WO2019111760A1 (fr) 2017-12-07 2018-11-27 Feuille d'usinage de pièce à travailler et procédé de production de pièce à travailler usinée

Family Applications After (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/043553 WO2019111760A1 (fr) 2017-12-07 2018-11-27 Feuille d'usinage de pièce à travailler et procédé de production de pièce à travailler usinée

Country Status (5)

Country Link
JP (2) JP7162612B2 (fr)
KR (2) KR102515877B1 (fr)
CN (2) CN111149191B (fr)
TW (2) TWI783085B (fr)
WO (2) WO2019111481A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021095449A (ja) * 2019-12-13 2021-06-24 日東電工株式会社 粘着シート剥離方法
CN113388331A (zh) * 2020-03-13 2021-09-14 日东电工株式会社 再剥离粘合带

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2024010412A (ja) * 2022-07-12 2024-01-24 日東電工株式会社 保護シート

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013067708A (ja) * 2011-09-21 2013-04-18 Nitto Denko Corp 塗膜保護シートおよびその製造方法
WO2016199787A1 (fr) * 2015-06-12 2016-12-15 東亞合成株式会社 Composition adhésive et procédé de production de celle-ci, et produit adhésif
JP2018172596A (ja) * 2017-03-31 2018-11-08 株式会社クレハ フッ化ビニリデン共重合体粒子及びその利用

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5019657B2 (fr) 1972-02-08 1975-07-09
JPS5352496Y2 (fr) 1973-06-21 1978-12-15
JPH09213663A (ja) * 1996-02-06 1997-08-15 Mitsui Toatsu Chem Inc 半導体ウエハの加工方法
JP4800778B2 (ja) * 2005-05-16 2011-10-26 日東電工株式会社 ダイシング用粘着シート及びそれを用いた被加工物の加工方法
JP2007069476A (ja) * 2005-09-07 2007-03-22 Toppan Printing Co Ltd インク吐出ヘッドのノズル面インク付着低減方法およびインク吐出ヘッド
US20110274933A1 (en) * 2008-12-12 2011-11-10 Lintec Corporation Laminate, method for producing same, electronic device member, and electronic device
JP5422055B2 (ja) * 2010-09-07 2014-02-19 リンテック株式会社 粘着シート、及び電子デバイス
JP5027321B2 (ja) * 2010-09-24 2012-09-19 古河電気工業株式会社 半導体加工用テープ
JP2011046964A (ja) * 2010-11-19 2011-03-10 Nitto Denko Corp 粘着テープ及び粘着テープ用基材
JP5117630B1 (ja) * 2012-07-06 2013-01-16 古河電気工業株式会社 半導体ウェハ表面保護用粘着テープおよびそれを用いた半導体ウェハの製造方法
JP6343883B2 (ja) * 2013-07-29 2018-06-20 東亞合成株式会社 活性エネルギー線硬化型樹脂組成物
JP6210827B2 (ja) * 2013-10-04 2017-10-11 リンテック株式会社 半導体加工用シート
JP6140066B2 (ja) * 2013-12-10 2017-05-31 リンテック株式会社 半導体加工用シート
WO2015133420A1 (fr) * 2014-03-03 2015-09-11 リンテック株式会社 Feuille de traitement d'éléments de type semi-conducteur et procédé de fabrication de puce mettant en œuvre ladite feuille
JP6019054B2 (ja) * 2014-03-24 2016-11-02 富士フイルム株式会社 ガスバリアフィルムおよびガスバリアフィルムの製造方法
JP6272109B2 (ja) * 2014-03-31 2018-01-31 リンテック株式会社 粘着剤組成物、粘着シート、および粘着シートの製造方法
WO2015190432A1 (fr) 2014-06-12 2015-12-17 東レ株式会社 Produit en couches et procédé pour sa production
WO2016013510A1 (fr) * 2014-07-22 2016-01-28 日本合成化学工業株式会社 Composition adhésive sensible à la pression durcissable par rayonnement d'énergie active, adhésif sensible à la pression et feuille adhésive sensible à la pression l'utilisant
JP6521823B2 (ja) * 2015-10-01 2019-05-29 リンテック株式会社 ダイシングダイボンディングシート
JP2017069474A (ja) 2015-10-01 2017-04-06 イビデン株式会社 回路基板及びその製造方法
JP2017132874A (ja) * 2016-01-27 2017-08-03 リンテック株式会社 電子部品貼付用アースラベル

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013067708A (ja) * 2011-09-21 2013-04-18 Nitto Denko Corp 塗膜保護シートおよびその製造方法
WO2016199787A1 (fr) * 2015-06-12 2016-12-15 東亞合成株式会社 Composition adhésive et procédé de production de celle-ci, et produit adhésif
JP2018172596A (ja) * 2017-03-31 2018-11-08 株式会社クレハ フッ化ビニリデン共重合体粒子及びその利用

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021095449A (ja) * 2019-12-13 2021-06-24 日東電工株式会社 粘着シート剥離方法
CN113388331A (zh) * 2020-03-13 2021-09-14 日东电工株式会社 再剥离粘合带

Also Published As

Publication number Publication date
KR20200094728A (ko) 2020-08-07
KR20200094727A (ko) 2020-08-07
CN111149191A (zh) 2020-05-12
TWI783085B (zh) 2022-11-11
TW201927964A (zh) 2019-07-16
KR102579064B1 (ko) 2023-09-15
JPWO2019111481A1 (ja) 2020-12-24
TWI809030B (zh) 2023-07-21
CN111149192A (zh) 2020-05-12
JPWO2019111760A1 (ja) 2020-12-17
WO2019111760A1 (fr) 2019-06-13
CN111149191B (zh) 2023-08-29
JP7162612B2 (ja) 2022-10-28
TW202010807A (zh) 2020-03-16
CN111149192B (zh) 2023-09-15
KR102515877B1 (ko) 2023-03-30
JP7162614B2 (ja) 2022-10-28

Similar Documents

Publication Publication Date Title
TWI809030B (zh) 工件加工用片材及加工完成的工件的製造方法
KR20210088525A (ko) 워크 가공용 시트
CN111164738B (zh) 工件加工用片及已加工工件的制造方法
JP7086103B2 (ja) ワーク加工用シートおよび加工済みワークの製造方法
JP6980680B2 (ja) ステルスダイシング用粘着シート
JP7200260B2 (ja) ワーク加工用シートおよび加工済みワークの製造方法
JP2024007771A (ja) ワーク加工用シートおよび半導体装置の製造方法
WO2019008810A1 (fr) Feuille adhésive pour découpage en dés furtifs, et procédé de production de dispositif à semi-conducteur

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18885791

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019558016

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18885791

Country of ref document: EP

Kind code of ref document: A1