WO2018079635A1 - Non-tissé filé-lié et son procédé de fabrication - Google Patents

Non-tissé filé-lié et son procédé de fabrication Download PDF

Info

Publication number
WO2018079635A1
WO2018079635A1 PCT/JP2017/038602 JP2017038602W WO2018079635A1 WO 2018079635 A1 WO2018079635 A1 WO 2018079635A1 JP 2017038602 W JP2017038602 W JP 2017038602W WO 2018079635 A1 WO2018079635 A1 WO 2018079635A1
Authority
WO
WIPO (PCT)
Prior art keywords
nonwoven fabric
spunbonded nonwoven
degrees
tensile strength
filament
Prior art date
Application number
PCT/JP2017/038602
Other languages
English (en)
Japanese (ja)
Inventor
仁 溝上
松浦　博幸
拓史 小林
Original Assignee
東レ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東レ株式会社 filed Critical 東レ株式会社
Priority to KR1020197010948A priority Critical patent/KR102242725B1/ko
Priority to JP2018514481A priority patent/JP7070404B2/ja
Publication of WO2018079635A1 publication Critical patent/WO2018079635A1/fr

Abstract

L'invention concerne un non-tissé filé-lié présentant une résistance à la traction transversale supérieure ainsi qu'une excellente texture et une excellente qualité. Ledit non-tissé filé-lié comprend des filaments continus thermoplastiques et est formé par liaison par thermocompression partielle, ledit non-tissé filé-lié étant caractérisé en ce que le pic de répartition de l'orientation des fibres pour les filaments dans la direction verticale du non-tissé est à 10 à 50° et en ce que le rapport vertical/transversal pour la résistance à la traction du non-tissé est de 1,3 à 1,8.
PCT/JP2017/038602 2016-10-27 2017-10-26 Non-tissé filé-lié et son procédé de fabrication WO2018079635A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020197010948A KR102242725B1 (ko) 2016-10-27 2017-10-26 스펀본드 부직포 및 그의 제조 방법
JP2018514481A JP7070404B2 (ja) 2016-10-27 2017-10-26 スパンボンド不織布の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016210317 2016-10-27
JP2016-210317 2016-10-27

Publications (1)

Publication Number Publication Date
WO2018079635A1 true WO2018079635A1 (fr) 2018-05-03

Family

ID=62025026

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/038602 WO2018079635A1 (fr) 2016-10-27 2017-10-26 Non-tissé filé-lié et son procédé de fabrication

Country Status (4)

Country Link
JP (1) JP7070404B2 (fr)
KR (1) KR102242725B1 (fr)
TW (1) TW201819705A (fr)
WO (1) WO2018079635A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112204193A (zh) * 2018-05-31 2021-01-08 东丽株式会社 墙壁装饰材料用无纺布及其制造方法
JPWO2021200369A1 (fr) * 2020-03-31 2021-10-07
EP3812027A4 (fr) * 2018-06-25 2022-04-20 Toray Industries, Inc. Tissu non-tissé filé-lié destiné à être utilisé dans des filtres, et son procédé de fabrication
JP7405590B2 (ja) 2019-12-12 2023-12-26 花王株式会社 不織布の製造方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW202140885A (zh) * 2020-04-24 2021-11-01 財團法人紡織產業綜合研究所 含羽絨紡織品
JP2023539153A (ja) * 2020-09-08 2023-09-13 コーロン インダストリーズ インク 残留有害物を含有せず向上した開繊品位を有するスパンボンド不織布、その製造方法および製造装置

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60155764A (ja) * 1984-01-25 1985-08-15 旭化成株式会社 不織布の製造方法
JPH09324356A (ja) * 1996-06-07 1997-12-16 Teijin Ltd 長繊維ウェブの製造方法
JP2895960B2 (ja) * 1989-11-08 1999-05-31 ファイバウエブ・ノース・アメリカ・インコーポレーテッド スパンフィラメント束から等分散フィラメントを提供する方法及び装置並びに得られるスパン接着ファブリック
JP2003147672A (ja) * 2001-11-09 2003-05-21 Kobe Steel Ltd 不織布製造装置及び製造方法
JP2006508262A (ja) * 2002-11-27 2006-03-09 ポリフェルト・ゲゼルシャフト・ミト・ベシュレンクテル・ハフツング 溶融紡糸されたフィラメントから一定の等方性を有するジオテキスタイルの製造方法
JP2007197891A (ja) * 2005-12-26 2007-08-09 Toyobo Co Ltd スパンボンド不織布

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100889249B1 (ko) * 2007-10-30 2009-03-17 주식회사 한스물산 통기성필름과 부직포를 적층시킨 하우스랩용 필름
JP2014040677A (ja) 2012-08-21 2014-03-06 Toray Ind Inc ハウスラップ材用不織布およびその製造方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60155764A (ja) * 1984-01-25 1985-08-15 旭化成株式会社 不織布の製造方法
JP2895960B2 (ja) * 1989-11-08 1999-05-31 ファイバウエブ・ノース・アメリカ・インコーポレーテッド スパンフィラメント束から等分散フィラメントを提供する方法及び装置並びに得られるスパン接着ファブリック
JPH09324356A (ja) * 1996-06-07 1997-12-16 Teijin Ltd 長繊維ウェブの製造方法
JP2003147672A (ja) * 2001-11-09 2003-05-21 Kobe Steel Ltd 不織布製造装置及び製造方法
JP2006508262A (ja) * 2002-11-27 2006-03-09 ポリフェルト・ゲゼルシャフト・ミト・ベシュレンクテル・ハフツング 溶融紡糸されたフィラメントから一定の等方性を有するジオテキスタイルの製造方法
JP2007197891A (ja) * 2005-12-26 2007-08-09 Toyobo Co Ltd スパンボンド不織布

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112204193A (zh) * 2018-05-31 2021-01-08 东丽株式会社 墙壁装饰材料用无纺布及其制造方法
EP3812027A4 (fr) * 2018-06-25 2022-04-20 Toray Industries, Inc. Tissu non-tissé filé-lié destiné à être utilisé dans des filtres, et son procédé de fabrication
JP7405590B2 (ja) 2019-12-12 2023-12-26 花王株式会社 不織布の製造方法
JPWO2021200369A1 (fr) * 2020-03-31 2021-10-07
WO2021200369A1 (fr) * 2020-03-31 2021-10-07 東レ株式会社 Tissu non tissé filé-lié
CN115315547A (zh) * 2020-03-31 2022-11-08 东丽株式会社 纺粘无纺布
JP7180761B2 (ja) 2020-03-31 2022-11-30 東レ株式会社 スパンボンド不織布

Also Published As

Publication number Publication date
JP7070404B2 (ja) 2022-05-18
JPWO2018079635A1 (ja) 2019-09-19
KR20190066019A (ko) 2019-06-12
KR102242725B1 (ko) 2021-04-22
TW201819705A (zh) 2018-06-01

Similar Documents

Publication Publication Date Title
WO2018079635A1 (fr) Non-tissé filé-lié et son procédé de fabrication
JP4619947B2 (ja) 高強力不織布
CN109642378B (zh) 纺粘无纺布及其制造方法
JP5199537B2 (ja) ポリ乳酸系複合繊維及びこれを用いた不織布とクッション材
JP2014040677A (ja) ハウスラップ材用不織布およびその製造方法
CN109642377B (zh) 纺粘无纺布及其制造方法
JP7092193B2 (ja) カーテン用不織布およびその製造方法
JP7160094B2 (ja) 壁装材用不織布およびその製造方法
JP2019210591A (ja) 障子用不織布およびその製造方法
JP4140996B2 (ja) ポリエステル系長繊維不織布およびその製造方法
JP6822106B2 (ja) スパンボンド不織布およびその製造方法
JP4140997B2 (ja) ポリエステル系長繊維不織布およびその製造方法
JP2017155385A (ja) エアクリーナー用不織布
JP7409566B1 (ja) 長繊維不織布、これを含んでなるエアバッグ包材および長繊維不織布の製造方法
JP6158117B2 (ja) 不織布断熱材
JPH07207566A (ja) 積層不織布及びその製造方法
WO2023149388A1 (fr) Tissu non tissé, son procédé de production et matériau de construction
JP7473093B1 (ja) スパンボンド不織布、フィルター濾材、エアフィルター、ならびに、フィルター濾材の製造装置
JP2010216044A (ja) フェノール樹脂発泡体用不織布
WO2024024215A1 (fr) Tissu non tissé à fibres longues, conditionnement de coussin de sécurité gonflable le comprenant, et procédé de production de tissu non tissé à fibres longues
JP4211496B2 (ja) 吸音材構成部材および吸音材
JPH09195458A (ja) 防水シート、その製造法、その用途及びその施工方法
JP2024065357A (ja) アスファルトルーフィング基材用スパンボンド不織布、および、アスファルトルーフィング基材
KR20220112773A (ko) 스펀본드 부직포, 집진기 플리츠 필터용 여과재, 집진기 플리츠 필터 및 대풍량 펄스제트 타입 집진기
JP2023097053A (ja) スパンボンド不織布、表皮材用シート、及び表皮材

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2018514481

Country of ref document: JP

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17863376

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20197010948

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17863376

Country of ref document: EP

Kind code of ref document: A1