WO2015112232A2 - Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys - Google Patents

Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys Download PDF

Info

Publication number
WO2015112232A2
WO2015112232A2 PCT/US2014/064554 US2014064554W WO2015112232A2 WO 2015112232 A2 WO2015112232 A2 WO 2015112232A2 US 2014064554 W US2014064554 W US 2014064554W WO 2015112232 A2 WO2015112232 A2 WO 2015112232A2
Authority
WO
WIPO (PCT)
Prior art keywords
mold
silicon carbide
facecoat
calcium
bulk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2014/064554
Other languages
English (en)
French (fr)
Other versions
WO2015112232A3 (en
Inventor
Bernard Patrick Bewlay
Joan Mckiever
Brian Michael ELLIS
Nicholas Vincent McLASKY
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Priority to CA2931206A priority Critical patent/CA2931206A1/en
Priority to EP14863065.0A priority patent/EP3074366A2/en
Priority to JP2016555449A priority patent/JP6329636B2/ja
Priority to CN201480074142.0A priority patent/CN105960296B/zh
Publication of WO2015112232A2 publication Critical patent/WO2015112232A2/en
Publication of WO2015112232A3 publication Critical patent/WO2015112232A3/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22C—FOUNDRY MOULDING
    • B22C3/00—Selection of compositions for coating the surfaces of moulds, cores, or patterns
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22C—FOUNDRY MOULDING
    • B22C1/00—Compositions of refractory mould or core materials; Grain structures thereof; Chemical or physical features in the formation or manufacture of moulds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22C—FOUNDRY MOULDING
    • B22C9/00—Moulds or cores; Moulding processes
    • B22C9/02—Sand moulds or like moulds for shaped castings
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22C—FOUNDRY MOULDING
    • B22C9/00—Moulds or cores; Moulding processes
    • B22C9/22—Moulds for peculiarly-shaped castings
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/34—Silicon-containing compounds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D1/00—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40—Additives
    • C09D7/66—Additives characterised by particle size
    • C09D7/67—Particle size smaller than 100 nm
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40—Additives
    • C09D7/66—Additives characterised by particle size
    • C09D7/68—Particle size between 100-1000 nm
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • C08K2003/2206—Oxides; Hydroxides of metals of calcium, strontium or barium
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • C08K2003/2227—Oxides; Hydroxides of metals of aluminium

Definitions

  • the materials used for gas turbines may include titanium alloys, nickel alloys (also called super alloys) and high strength steels.
  • titanium alloys are generally used for compressor parts
  • nickel alloys are suitable for the hot parts of the aircraft engine
  • the high strength steels are used, for example, for compressor housings and turbine housings.
  • the highly loaded or stressed gas turbine components such as components for a compressor for example, are typically forged parts.
  • Components for a turbine are typically embodied as investment cast parts.
  • an investment compound in which magnesium oxide and aluminum oxide are used as main components a fine metallic titanium powder is added in order to reduce the amount of shrinkage of the mold and to compensate for the dimensional error caused by the shrinkage of the cast metal on solidification.
  • the above prior art investment compounds have significant limitations.
  • the investment mold compound that is intended to compensate for the shrinkage due to the solidification of the cast metal by the oxidation-expansion of metallic zirconium is difficult to practice, for several reasons.
  • a wax pattern is coated on its surface with the new investment compound with zirconium and then the coated wax pattern is embedded in the conventional investment compound in an attempt to make the required amount of zirconium as small as possible; coating the wax with zirconium is very difficult and not highly repeatable.
  • waxes of complex shaped components can not be coated in a sufficiently uniform manner.
  • the coated layer can come off the wax when the investment mold mix is placed externally around the coated layer and the pattern, with the result that titanium reacts with the externally placed investment mold mix.
  • aspects of the present disclosure provide casting mold compositions, methods of casting, and cast articles that overcome the limitations of the conventional techniques. Though some aspect of the disclosure may be directed toward the fabrication of components, for example, engine turbine blades, however aspects of the present disclosure may be employed in the fabrication of components in many industries, in particular, those components containing titanium and/or titanium alloys.
  • One aspect of the present disclosure is a mold for casting a titanium-containing article, comprising: a calcium aluminate cement comprising calcium monoaluminate, calcium dialuminate, and mayenite, wherein the mold has an intrinsic silicon carbide-containing facecoat of about 10 microns to about 500 microns between a bulk of the mold and a mold cavity.
  • the intrinsic facecoat is a continuous intrinsic facecoat.
  • the silicon carbide is present at about 15% to about 45% by weight.
  • the silicon carbide-containing intrinsic facecoat comprises silicon carbide that is present at about 15% to about 45% by weight.
  • the mold further comprises silicon carbide wherein the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 10 percent more silicon carbide than the bulk of the mold.
  • the mold further comprises calcium oxide with more than about 10% by weight and less than about 50% by weight of the mold composition in calcium oxide.
  • the mold as recited further comprises less than 2 % silica, for example, colloidal silica.
  • the mold in one example, comprises the bulk of the mold and an intrinsic facecoat, with the bulk of the mold and the intrinsic facecoat having different compositions, and the silicon carbide-containing intrinsic facecoat comprising calcium aluminate with a particle size of less than about 50 microns.
  • the mold comprises the bulk of the mold and a silicon carbide-containing intrinsic facecoat, wherein the bulk of the mold and the silicon carbide-containing intrinsic facecoat have different compositions and wherein the bulk of the mold comprises alumina particles larger than about 50 microns.
  • the mold in another example, comprises the bulk of the mold and a silicon carbide-containing intrinsic facecoat, wherein the bulk of the mold comprises alumina particles larger than about 50 microns and the silicon carbide-containing intrinsic facecoat comprises calcium aluminate particles less than about 50 microns in size.
  • the mold comprises the bulk of the mold and the silicon carbide-containing intrinsic facecoat, wherein the bulk of the mold and the silicon carbide-containing intrinsic facecoat have different compositions and wherein the silicon carbide- containing intrinsic facecoat comprises calcium aluminate with a particle size of less than about 50 microns
  • the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 20 percent more calcium monoaluminate than does the bulk of the mold. In one embodiment, the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 20 percent less alumina than does the bulk of the mold. In another embodiment, the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 20 percent more calcium aluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold. In one embodiment, the silicon carbide-containing intrinsic facecoat further comprises alumina and the level of alumina, by weight fraction, is at least 20 percent less than is present in the bulk of the mold.
  • the silicon carbide-containing intrinsic facecoat further comprises alumina and the level of alumina, by weight fraction, is at least 20 percent less than is present in the bulk of the mold, and wherein the silicon carbide-containing intrinsic facecoat has at least 20 percent more calcium aluminate, and at least 50 percent less mayenite than does the bulk of the mold.
  • the weight fraction of calcium monoaluminate in the silicon carbide-containing intrinsic facecoat is, in one example, more than 0.45 and the weight fraction of mayenite is less than 0.10.
  • the calcium monoaluminate in the bulk of the mold comprises a weight fraction of about 0.05 to 0.95, and the calcium monoaluminate in the silicon carbide- containing intrinsic facecoat is about 0.10 to 0.90.
  • the calcium dialuminate in the bulk of the mold comprises a weight fraction of about 0.05 to about 0.80, and the calcium dialuminate in the silicon carbide-containing intrinsic facecoat is about 0.05 to 0.90.
  • the mayenite in the bulk of the mold composition comprises a weight fraction of about 0.01 to about 0.30, and the mayenite in the silicon carbide-containing intrinsic facecoat is about 0.001 to 0.05.
  • the calcium monoaluminate in the bulk of the mold comprises a weight fraction of about 0.05 to 0.95, and the calcium monoaluminate in the silicon carbide-containing intrinsic facecoat is about 0.1 to 0.90;
  • the calcium dialuminate in the bulk of the mold comprises a weight fraction of about 0.05 to about 0.80, and the calcium dialuminate in the silicon carbide-containing intrinsic facecoat is about 0.05 to 0.90; and wherein the mayenite in the bulk of the mold composition comprises a weight fraction of about 0.01 to about 0.30, and the mayenite in the silicon carbide-containing intrinsic facecoat is about 0.001 to 0.05.
  • the mold further comprises aluminum oxide particles in the bulk of the mold that are less than about 500 microns in outside dimension.
  • the aluminum oxide particles comprise from about 30 % by weight to about 68 % by weight of the composition used to make the mold.
  • the mold further comprises hollow oxide particles, for example, hollow aluminum oxide particles.
  • the calcium aluminate comprises more than 20% by weight of the slurry (that is, more than 20% by weight of the composition used to make the mold).
  • the mold further comprises more than about 10% by weight and less than about 50% by weight of the mold composition in calcium oxide.
  • the mold further comprises aluminum oxide particles, magnesium oxide particles, calcium oxide particles, zirconium oxide particles, titanium oxide particles, silicon oxide particles, or compositions thereof.
  • the percentage of solids in an initial calcium aluminate - liquid cement mixture used to make the mold is, in one example, about 60 % to about 78 %. In another example, the percentage of solids in the final calcium aluminate - liquid cement mixture (i.e. with the large scale alumina), used to make the mold, is about 70 % to about 95 %.
  • One aspect of the present disclosure is a titanium-containing article formed in the mold as disclosed herein.
  • the article in one example, comprises a titanium aluminide- containing turbine blade.
  • One aspect of the present disclosure is a facecoat composition of a mold that is used for casting a titanium-containing article, comprising calcium monoaluminate, calcium dialuminate, silicon carbide, and mayenite, wherein the facecoat composition is a silicon carbide- containing intrinsic facecoat, is about 10 microns to about 500 microns thick, and is located between a bulk of the mold and a surface of the mold that opens to a mold cavity.
  • the silicon carbide-rich facecoat comprises, in one example, of calcium aluminate with a particle size of less than about 50 microns.
  • the silicon carbide is present at about 15% to about 45% by weight of the composition.
  • the facecoat composition further comprises less than 2 % silica, for example, colloidal silica.
  • the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 20 percent more calcium aluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold.
  • the silicon carbide-containing intrinsic facecoat has, by weight fraction, at least 10 percent more silicon carbide than does the bulk of the mold.
  • the weight fraction of calcium monoaluminate in the intrinsic facecoat is, in one example, more than 0.45 and the weight fraction of mayenite is less than 0.10.
  • the calcium monoaluminate in the intrinsic facecoat comprises a weight fraction of 0.10 to 0.90; the calcium dialuminate in the intrinsic facecoat comprises a weight fraction of 0.05 to 0.90; and the mayenite in the intrinsic facecoat comprises a weight fraction of 0.001 to 0.05.
  • the facecoat composition further comprises silicon carbide wherein the silicon carbide is present at about 15% to about 45% by weight of the facecoat composition.
  • the present disclosure is a method for forming a mold for casting a titanium-containing article, comprising: mixing calcium aluminate and silicon carbide with a liquid to produce a slurry, wherein the percentage of solids in the initial calcium aluminate / liquid mixture is about 60%> to about 80%> by weight of the slurry and a viscosity of the slurry is about 30 to about 1500 centipoise; introducing the slurry into a mold cavity that contains a fugitive pattern; and allowing the slurry to cure in the mold cavity to form a mold of a titanium- containing article.
  • the initial calcium aluminate liquid mixture is a slurry without aluminum oxide, or in another example, without hollow oxide particles, further still, in another example, without large scale hollow oxide particles such as hollow aluminum oxide.
  • large scale hollow oxide particles are added to the slurry to form a final calcium aluminate - liquid cement mixture, such that the solids in the slurry are about 70% to about 95% by weight of the slurry.
  • the final calcium aluminate liquid mixture is a slurry that includes aluminum oxide, or in another example, includes hollow oxide particles, or in yet another example, includes large scale (larger than 50 microns in outside dimension) hollow oxide particles such as hollow aluminum oxide.
  • the silicon carbide is added to the calcium aluminate before or during the making of the slurry.
  • the silicon carbide particles are from about 10 microns to about 50 microns in outside dimension. In one embodiment, the silicon carbide particles are from about 1 micron to about 1000 microns in outside dimension. In another embodiment, the particle size of the calcium aluminate is less than about 50 microns in outside dimension. In one embodiment, the calcium aluminate comprises more than 20% by weight of the slurry (composition used to make the mold).
  • the slurry before introducing the slurry into the mold cavity oxide particles are added into the slurry. That is, in one embodiment, the slurry further comprises oxide particles. In one embodiment, these oxide particles may be hollow. In one embodiment, the oxide particles are selected from a group consisting of aluminum oxide particles, magnesium oxide particles, calcium oxide particles, zirconium oxide particles, titanium oxide particles, silicon oxide particles, and compositions thereof.
  • the oxide particles may be aluminum oxide (also known as alumina).
  • the aluminum oxide particles can range in size and may be larger than about 50 microns. In particular instances, the added aluminum oxide particles that may be used are less than about 1500 microns in outside dimension. In one embodiment, the aluminum oxide particles are from about 50 microns to about 1500 microns in outside dimension. In one embodiment, the aluminum oxide particles comprises from about 30 % by weight to about 68 % by weight of the slurry (the composition used to make the mold).
  • calcium oxide is added into the slurry before the slurry is introduced into the mold cavity.
  • the calcium oxide is added such that more than about 10% by weight and less than about 50% by weight of the mold composition is calcium oxide.
  • the percentage of solids in an initial calcium aluminate - liquid cement mixture is about 60 to about 78 %.
  • the percentage of solids in the final calcium aluminate - liquid cement mixture with the large scale aluminum oxide are about 70% to about 95% by weight of the slurry.
  • the difference between the initial and final calcium aluminate liquid cement mixture is that while the initial mixture does not have hollow oxide particles, the final mixture does have hollow oxide particles, for example, large scale hollow aluminum oxide particles.
  • the present disclosure is directed to the mold made according to the presently disclosed method. In one embodiment, the present disclosure is directed to a titanium aluminide-containing turbine blade made using the mold made by the presently disclosed method.
  • the present disclosure is a method for casting titanium and titanium alloys, comprising: obtaining an investment casting mold composition comprising calcium aluminate and large scale aluminum oxide, wherein the calcium aluminate is combined with a liquid and silicon carbide to produce a slurry, and wherein the solids in the final calcium aluminate / liquid mixture with the large scale aluminum oxide are about 70% to about 95% by weight of the slurry; pouring said investment casting mold composition into a vessel containing a fugitive pattern; curing said investment casting mold composition; removing said fugitive pattern from the mold; firing the mold; preheating the mold to a mold casting temperature; pouring molten titanium or titanium alloy into the heated mold; solidifying the molten titanium or titanium alloy; forming a solidified titanium or titanium alloy casting; and removing the solidified titanium or titanium alloy casting from the mold.
  • the percentage of solids in the slurry is about 60 % to about 78 %.
  • the particles of aluminum oxide used in the presently taught method are about 50 microns to about 1500 microns in outside dimension.
  • the silicon carbide particles are about 10 microns to about 100 microns in outside dimension.
  • the silicon carbide increases thermal conductivity during casting compared to if casting is performed in the absence of silicon carbide.
  • the silicon carbide is present between 15% to 45% by weight and provides increased thermal conductivity during casting by at least 25% as compared to casting performed without silicon carbide.
  • the silicon carbide particles are from about 10 microns to about 50 microns in outside dimension.
  • the calcium aluminate particles comprise particles less than about 50 microns in outside dimension.
  • the aluminum oxide particles are about 50 microns to about 1500 microns in outside dimension, or, in another example, from about 50 microns to about 500 microns in outside dimension.
  • the silicon carbide particles are about 10 microns to about 50 microns in outside dimension.
  • the silicon carbide particles are about 1 micron to about 1000 microns in outside dimension.
  • the aluminum oxide particles comprise from about 30 % by weight to about 68 % by weight of the investment casting mold composition used to make the mold.
  • the calcium aluminate comprises more than 20% by weight of the casting mold composition (the investment casting mold composition used to make the mold).
  • the casting mold composition the investment casting mold composition used to make the mold.
  • One aspect of the present disclosure is a titanium or titanium alloy article made by the casting method as recited by the presently disclosed methods.
  • One aspect of the present disclosure is a mold composition for casting a titanium- containing article, comprising: a calcium aluminate cement comprising calcium monoaluminate, calcium dialuminate, silicon carbide and mayenite.
  • the mold composition further comprises hollow particles of aluminum oxide.
  • a titanium-containing article casting-mold composition comprising calcium aluminate and silicon carbide.
  • an aspect of the present disclosure may be uniquely suited to providing mold compositions to be used in molds for casting titanium-containing and/or titanium alloy- containing articles or components, for example, titanium containing turbine blades.
  • the present disclosure is a turbine blade produced by the process, comprising: providing an investment casting mold, said mold comprising calcium aluminate, silicon carbide and aluminum oxide; pouring molten titanium or titanium alloy into the mold; solidifying the molten titanium or titanium alloy; forming a solidified titanium or titanium alloy casting; and removing the solidified titanium or titanium alloy casting from the mold to produce the turbine blade, wherein the turbine blade has an average roughness, Ra, of less than 20 across at least a portion of its surface area.
  • the use of silicon carbide at the range thought herein provides for increased thermal conductivity during casting compared to where casting is performed with little (less than 15% by weight) or no silicon carbide present.
  • the silicon carbide is provided in particles of about 10 microns to about 100 microns in outside dimension.
  • One aspect of the disclosure is a method for manufacturing a turbine component, comprising: making a mold from a mixture comprising calcium aluminate, calcium dialuminate, silicon carbide, mayenite and water, wherein the silicon carbide is present at about 15% to about 45% by weight; firing the mold; pouring molten titanium or titanium alloy into the mold; solidifying the molten titanium or titanium alloy to form a solidified casting; and removing the casting from the mold.
  • the method further comprises hollow aluminum oxide particles that are larger than about 50 microns (large scale alumina).
  • large scale particles comprise particles of greater than 50 microns in outside dimension
  • small scale particles comprise particles of less than 50 microns in outside dimension.
  • the turbine component is, in one embodiment, a turbine blade.
  • Figure 1 shows a schematic of the mold with the silicon carbide-containing facecoat.
  • Figure 2 shows the effect of silicon carbide size and weight fraction on the increase in temperature during curing.
  • Figure 3 shows a flow chart, in accordance with aspects of the disclosure, illustrating a method for forming a mold for casting a titanium-containing article.
  • Figure 4 shows a flow chart, in accordance with aspects of the disclosure, illustrating a method for casting titanium and titanium alloys.
  • Figure 5 shows a flow chart, in accordance with aspects of the disclosure, illustrating a turbine blade produced by the process shown.
  • Figure 6 shows a flow chart, in accordance with aspects of the disclosure, illustrating a method for manufacturing a turbine component.
  • the present disclosure relates generally to mold compositions and methods of mold making and articles cast from the molds, and, more specifically, to mold compositions and methods for casting titanium- containing articles, and titanium-containing articles so molded.
  • titanium based components by investment casting of titanium and its alloys in investment shell molds poses problems from the standpoint that the castings should be cast to "near-net-shape.” That is, the components may be cast to substantially the final desired dimensions of the component, and require little or no final treatment or machining. For example, some conventional castings may require only a chemical milling operation to remove any alpha case present on the casting. However, any sub-surface ceramic inclusions located below the alpha case in the casting are typically not removed by the chemical milling operation and may be formed due to the reaction between the mold facecoat and any reactive metal in the mold, for example, reactive titanium aluminide.
  • the present disclosure provides a new approach for casting near-net-shape titanium and titanium aluminide components, such as, turbine blades or airfoils.
  • Embodiments of the present disclosure provide compositions of matter for investment casting molds and casting methods that provide improved titanium and titanium alloy components for example, for use in the aerospace, industrial and marine industry.
  • the mold composition provides a mold that contains phases that provide improved mold strength during mold making and/or increased resistance to reaction with the casting metal during casting.
  • the molds according to aspects of the disclosure may be capable of casting at high pressure, which is desirable for near- net- shape casting methods. Mold compositions, for example, containing calcium aluminate cement and alumina particles, and preferred constituent phases, have been identified that provide castings with improved properties.
  • the constituent phases of the mold comprise calcium monoaluminate (CaAl 2 0 4 ).
  • the present inventors found calcium monoaluminate cement desirable for at least two reasons. First, it is understood by the inventors that calcium monoaluminate promotes hydraulic bond formation between the cement particles during the initial stages of mold making, and this hydraulic bonding is believed to provide mold strength during mold construction. Second, it is understood by the inventors that calcium monoaluminate experiences a very low rate of reaction with titanium and titanium aluminide based alloys.
  • calcium monoaluminate is provided to the mold composition of the present disclosure, for example, the investment molds, in the form of calcium aluminate cement.
  • the mold composition comprises a mixture of calcium aluminate cement and alumina, that is, aluminum oxide.
  • the mold composition provides minimum reaction with the alloy during casting, and the mold provides castings with the required component properties.
  • the facecoat of the mold provides minimum reaction with the alloy during casting, and the mold provides castings with the required component properties.
  • External properties of the casting include features such as shape, geometry, and surface finish.
  • Internal properties of the casting include mechanical properties, microstructure, defects (such as pores and inclusions) below a specified size and within allowable limits.
  • the mold contains a continuous intrinsic facecoat that contains silicon carbide; this silicon carbide-containing intrinsic facecoat is located between a bulk of the mold and a mold cavity.
  • the silicon carbide-containing intrinsic facecoat is about 10 microns to about 500 microns.
  • the silicon carbide-containing intrinsic facecoat comprises calcium aluminate with a particle size of less than about 50 microns.
  • the mold composition may be such that the bulk of the mold comprises alumina and particles larger than about 50 microns.
  • the silicon carbide- containing facecoat has less alumina than the bulk of the mold, and the silicon carbide-containing facecoat has more calcium aluminate than the bulk of the mold.
  • the percentage of solids in the initial calcium aluminate - liquid cement mix, and the solids in the final calcium aluminate - liquid cement mix are a feature of the present disclosure.
  • the disclosure refers to particles, for example, calcium aluminate, aluminum oxide and silicon carbide, as solids.
  • the initial calcium alumuniate - liquid cement mix comprises calcium monoaluminate, calcium dialuminate, mayenite, oxide particles and silicon carbide mixed with water to form a slurry.
  • the final calcium aluminate - liquid mold formulation comprises large scale oxide particles.
  • the initial calcium aluminate cement mix comprises fine-scale (e.g.
  • the final calcium aluminate cement mix is formed by adding large-scale (in one example greater than 50 microns and in another example, greater than 100 microns) alumina to the initial slurry and mixing for between 2 and 15 minutes to achieve a uniform mix.
  • the percentage of solids in the initial calcium aluminate - liquid cement mix is about 60% to about 78 %. In one example, the percentage of solids in the initial calcium aluminate - liquid cement mix is from about 70% to about 80%. In another example, the solids in the final calcium aluminate - liquid cement mix with the large scale alumina (>100 microns) alumina particles are about 70% to about 95%.
  • the mold composition of one aspect of the present disclosure provides for low- cost casting of titanium aluminide (TiAl) turbine blades, for example, TiAl low pressure turbine blades.
  • TiAl titanium aluminide
  • the mold composition may provide the ability to cast near-net- shape parts that require less machining and/or treatment than parts made using conventional shell molds and gravity casting.
  • near-net-shape implies that the initial production of an article is close to the final (net) shape of the article, reducing the need for further treatment, such as, extensive machining and surface finishing.
  • turbine blade refers to both steam turbine blades and gas turbine blades.
  • the present disclosure addresses the challenges of producing a mold, for example, an investment mold, that does not react significantly with titanium and titanium aluminide alloys.
  • the strength and stability of the mold allow high pressure casting approaches, such as centrifugal casting.
  • the disclosure may improve the structural integrity of net shape casting that can be generated, for example, from calcium aluminate cement and alumina investment molds.
  • the higher strength for example, higher fatigue strength, allows lighter components to be fabricated.
  • components having higher fatigue strength can last longer, and thus have lower life-cycle costs.
  • Surface roughness is one of the indices representing the surface integrity of cast and machined parts. Surface roughness is characterized by the centerline average roughness value "Ra", as well as the average peak-to-valley distance “Rz” in a designated area as measured by optical profilometry. A roughness value can either be calculated on a profile or on a surface. The profile roughness parameter (Ra, Rq,...) are more common. Each of the roughness parameters is calculated using a formula for describing the surface. There are many different roughness parameters in use, but R a is by far the most common. As known in the art, surface roughness is correlated with tool wear. Typically, the surface-finishing process though grinding and honing yields surfaces with Ra in a range of 0.1 mm to 1.6 mm. The surface roughness Ra value of the final coating depends upon the desired function of the coating or coated article.
  • Ra Ra is typically expressed in "millionths" of an inch. This is also referred to as “microinches”.
  • the Ra values indicated herein refer to microinches.
  • An Ra value of 70 corresponds to approximately 2 microns; and an Ra value of 35 corresponds to approximately 1 micron.
  • One aspect of the present disclosure is a turbine blade comprising titanium or titanium alloy and having an average roughness, Ra, of less than 20 across at least a portion of its surface area.
  • aspects of the present disclosure provide a composition for investment casting molds that can provide improved components of titanium and titanium alloys.
  • calcium monoaluminate can be provided in the form of calcium aluminate cement.
  • Calcium aluminate cement may be referred to as a "cement" or "binder.”
  • calcium aluminate cement is mixed with silicon carbide and alumina particles to provide a castable investment mold mix.
  • the calcium aluminate cement may be greater than about 20% by weight in the castable mold mix.
  • the calcium aluminate cement is between about 30 % and about 60 % by weight in the castable mold mix.
  • the use of greater than 20% by weight of calcium aluminate cement in the castable mold mix (casting mold composition) is a feature of the present disclosure.
  • the selection of the appropriate calcium aluminate cement chemistry, silicon carbide and alumina formulation are factors in the performance of the mold.
  • a sufficient amount of calcium oxide may be provided in the mold composition in order to minimize reaction with the titanium alloy.
  • the mold composition may comprise a multi-phase mixture of calcium aluminate cement, silicon carbide, and alumina particles.
  • the calcium aluminate cement may function as a binder, for example, the calcium aluminate cement binder may provide the main skeletal structure of the mold structure.
  • the calcium aluminate cement in one example comprises a continuous phase in the mold and provides strength during curing, and casting.
  • the mold composition in a further example consists of calcium aluminate cement, silicon carbide, and alumina, that is, calcium aluminate cement, silicon carbide and alumina may comprise substantially the only components of the mold composition.
  • the present disclosure comprises a titanium-containing article casting-mold composition comprising calcium aluminate.
  • the casting- mold composition further comprises oxide particles, for example, hollow oxide particles.
  • the oxide particles may be aluminum oxide particles, magnesium oxide particles, calcium oxide particles, zirconium oxide particles, titanium oxide particles, silicon oxide particles, combinations thereof, or compositions thereof.
  • the oxide particles may be a combination of one or more different oxide particles.
  • the casting-mold composition can further include aluminum oxide, for example, in the form of hollow particles, that is, particles having a hollow core or a substantially hollow core substantially surrounded by an oxide.
  • These hollow aluminum oxide particles may comprise about 99 % of aluminum oxide and have about 10 millimeter [mm] or less in outside dimension, such as, diameter.
  • the hollow aluminum oxide particles have about 1 millimeter [mm] or less in outside dimension, such as, diameter.
  • the aluminum oxide comprises particles that may have outside dimensions that range from about 10 microns [ ⁇ ] to about 10,000 microns.
  • the hollow oxide particles may comprise hollow alumina spheres (typically greater than about 100 microns in outside dimension or diameter).
  • the hollow alumina spheres may be incorporated into the casting-mold composition, and the hollow spheres may have a range of geometries, such as, round particles, or irregular aggregates.
  • the alumina may include both round particles and hollow spheres.
  • these geometries were discovered to increase the fluidity of the investment mold mixture.
  • the inventors conceived of using alumina because, inter alia, alumina is more stable that silica or the silicates that are used in certain prior art applications.
  • the enhanced fluidity that hollow alumina particles provide improves the surface finish and fidelity or accuracy of the surface features of the final casting produced from the mold.
  • the aluminum oxide comprises particles ranging in outside dimension from about
  • the aluminum oxide comprises particles that are less than about 500 microns in outside dimension, for example, diameter.
  • the aluminum oxide may comprise from about 0.5 % by weight to about 80 % by weight of the casting-mold composition.
  • the aluminum oxide comprises from about 40 % by weight to about 60 % by weight of the casting-mold composition.
  • the aluminum oxide comprises from about 30 % by weight to about 68 % by weight of the casting-mold composition.
  • the casting-mold composition further comprises calcium oxide.
  • the calcium oxide may be greater than about 10% by weight and less than about 50% by weight of the casting-mold composition.
  • the final mold in one example has a density of less than 2 grams/cubic centimeter and strength of greater than 500 pounds per square inch [psi].
  • the calcium oxide is greater than about 30% by weight and less than about 50% by weight of the casting-mold composition.
  • the calcium oxide is greater than about 25% by weight and less than about 35% by weight of the silicon carbide-containing casting-mold composition.
  • One aspect of the present disclosure is a mold for casting a titanium-containing article, comprising: a calcium aluminate cement comprising calcium monoaluminate, calcium dialuminate, and mayenite, wherein the mold has a silicon carbide-containing intrinsic facecoat of about 10 microns to about 500 microns between a bulk of the mold and a mold cavity.
  • the facecoat is a continuous silicon carbide-containing intrinsic facecoat.
  • the casting-mold composition of the present disclosure comprises a calcium aluminate cement.
  • the calcium aluminate cement includes at least three phases or components comprising calcium and aluminum: calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaALtOy), and mayenite (Cai 2 Ali 4 033).
  • the initial cement formulation is typically not at thermodynamic equilibrium after firing in the cement kiln. However, after mold making and high-temperature firing the silicon carbide-containing mold composition moves towards a thermodynamically stable configuration, and this stability is important for the subsequent casting process.
  • the weight fraction of calcium monoaluminate in the silicon carbide-containing intrinsic facecoat may be more than 0.45 and the weight fraction of mayenite in this facecoat may be less than 0.10.
  • the weight fraction of calcium monoaluminate in the bulk of the mold may be more than 0.5, and weight fraction of mayenite in the bulk of the mold may be less than 0.15.
  • the addition of silicon carbide allows for a mold that is more resistant to reaction during casting, and as a result it is possible to operate at higher casting temperatures.
  • the calcium monoaluminate in the bulk of the mold may comprise a weight fraction of about 0.05 to 0.95, and the calcium monoaluminate in the silicon carbide-containing intrinsic facecoat is about 0.1 to 0.90.
  • the calcium dialuminate in the bulk of the mold may comprise a weight fraction of about 0.05 to about 0.80, and the calcium dialuminate in the silicon carbide-containing intrinsic facecoat is about 0.05 to 0.90.
  • the mayenite in the bulk of the mold composition may comprise a weight fraction of about 0.01 to about 0.30, and the mayenite in the silicon carbide-containing intrinsic facecoat is about 0.001 to 0.05.
  • the silicon carbide may be present in both the bulk of the mold and the facecoat in different amounts.
  • the facecoat may contain a higher concentration (per unit volume of the facecoat) of silicon carbide particles than the bulk of the mold; for example 10 % more.
  • the bulk of the mold and the intrinsic facecoat have substantially similar concentration (per unit volume) of silicon carbide particles.
  • the inventors have discovered that the use of silicon carbide allows for a mold that is more resistant to reaction during casting, and as a result it is possible to operate at higher casting temperatures.
  • the silicon carbide is present between 15% to 45% by weight and provides increased thermal conductivity during casting by at least 25% as compared to casting performed without silicon carbide.
  • the thermal conductivity was increased by more than 50%.
  • the presence of 15% silicon carbide the thermal conductivity was increased by more than about 25%.
  • the presence of 25% silicon carbide by weight resulted in an increase of about 50%>, about 60%>, about 70%>, or about 80%> in thermal conductivity.
  • the exact composition of the bulk of the mold and the silicon carbide-containing intrinsic facecoat may differ.
  • the calcium monoaluminate in the bulk of the mold comprises a weight fraction of about 0.05 to 0.95, and the calcium monoaluminate in the silicon carbide-containing intrinsic facecoat is about 0.1 to 0.90
  • the calcium dialuminate in the bulk of the mold comprises a weight fraction of about 0.05 to about 0.80, and the calcium dialuminate in the silicon carbide-containing intrinsic facecoat is about 0.05 to 0.90
  • the mayenite in the bulk of the mold composition comprises a weight fraction of about 0.01 to about 0.30, and the mayenite in the silicon carbide-containing intrinsic facecoat is about 0.001 to 0.05.
  • the weight fraction of calcium monoaluminate in the calcium aluminate cement may be more than about 0.5, and the weight fraction of mayenite in the calcium aluminate cement may be less than about 0.15. In another embodiment, the calcium aluminate cement is more than 20% by weight of the casting-mold composition.
  • the calcium aluminate cement may have a particle size of about 50 microns or less in outside dimension.
  • the weight fractions of these phases that are suitable in the cement of the bulk of the mold may be 0.05 to 0.95 of calcium monoaluminate, 0.05 to 0.80 of calcium dialuminate, and 0.01 to 0.30 of mayenite.
  • the weight fractions of these phases in the facecoat of the mold may be 0.1 to 0.90 of calcium monoaluminate, 0.05 to 0.90 of calcium dialuminate, and 0.001 to 0.05 of mayenite.
  • the weight fraction of calcium monoaluminate in the facecoat may be more than about 0.6, and the weight fraction of mayenite is less than about 0.1.
  • the weight fraction of calcium monoaluminate in the cement of the bulk of the mold is more than about 0.5, and weight fraction of mayenite is less than about 0.15.
  • Calcium mono-aluminate is an important hydraulic mineral present in calcium alumina cement. Its hydration contributes to the high early strength of the investment mold. Mayenite is desired in the cement because it provides strength during the early stages of mold curing due to the fast formation of hydraulic bonds; the mayenite is, however, removed on heat treatment of the molds prior to casting.
  • the calcium aluminate cement may have a particle size of about 50 microns or less in outside dimension.
  • a particle size of less than 50 microns is used for at least three reasons: first, the fine particle size is believed to promote the formation of hydraulic bonds during mold mixing and curing; second, the fine particle size is understood to promote inter- particle sintering during firing, and this can increase the mold strength; and third, the fine particle size is believed to improve the surface finish of the cast article produced in the mold.
  • the calcium aluminate cement may be provided as powder, and can be used either in its intrinsic powder form, or in an agglomerated form, such as, as spray dried agglomerates.
  • the calcium aluminate cement can also be preblended with fine-scale (for, example, less than 10 micron in size) alumina.
  • the fine-scale alumina is believed to provide an increase in strength due to sintering during high-temperature firing.
  • larger-scale alumina for example, alumina with greater than 50 microns in outside dimension
  • the percentage of solids in the initial calcium aluminate (liquid particle mixture) and the solids in the final calcium aluminate are a feature of the present disclosure.
  • the percentage of solids in the initial calcium aluminate - liquid particle mix is from about 60% to about 80 %. In one example, the percentage of solids in the initial calcium aluminate - liquid particle mix is from about 70% to about 80%.
  • the solids in the final calcium aluminate - liquid particle mix that is calcium aluminate particles with less than about 50 microns in outside dimension along with large scale alumina particles that are larger than about 70 microns in outside dimension, and silicon carbide particles that are about 5 microns to about 100 microns in outside dimension - are about 70% to about 95%.
  • the initial calcium aluminate particles are fine scale, in about 5 microns to about 50 microns, and alumina particles of greater than about 70 microns, and silicon carbide of up to about 100 microns in outside dimension are mixed with water to provide a uniform and homogeneous slurry.
  • the final mix is formed by adding progressively larger scale alumina particles, for example 70 microns at first and then 150 microns, to the initial slurry and mixing for between 2 and 15 minutes to achieve a uniform mix.
  • the large scale particles are hollow particles that have space or pockets of air within the particle(s) such that the particle is not a complete, packed dense particle. The degree of this space / air varies and hollow particles include particles where at least 20 % of the volume of the particle is air. In one example, hollow particles are particles where about 5 % to about 75 % of the volume of the particle is made up of empty space or air.
  • hollow particles are particles where about 10 % to about 80 % of the volume of the particle is made up of empty space or air. In yet another example, hollow particles are particles where about 20 % to about 70 % of the volume of the particle is made up of empty space or air. In another example, hollow particles are particles where about 30 % to about 60 % of the volume of the particle is made up of empty space or air. In another example, hollow particles are particles where about 40 % to about 50 % of the volume of the particle is made up of empty space or air.
  • hollow particles are particles where about 10% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 20% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 30% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 40% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 50% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 60% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 70% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 80% of the volume of the particle is made up of empty space or air. In one example, hollow particles are particles where about 90% of the volume of the particle is made up of empty space or air.
  • the hollow particles serve at least two functions: [1] they reduce the density and the weight of the core, with minimal reduction in strength; strength levels of approximately 500psi and above are obtained, with densities of approximately 2g/cc and less; and [2] they reduce the elastic modulus of the mold and help to provide compliance during cool down of the mold and the component after casting.
  • the increased compliance and crushability of the mold may reduce the tensile stresses on the component.
  • the present disclosure is directed, inter alia, to a composition for investment casting molds that can provide improved components of titanium and titanium alloys.
  • the mold contains a continuous intrinsic facecoat that contains silicon carbide, between the bulk of mold and the mold cavity.
  • a silicon carbide powder size of less than about 50 microns in outside dimension is employed in the mold making process. The inventors of the instant application found that the use of silicon carbide powder of this size promotes segregation of the particles to the facecoat during mold making. Thus, the presence of silicon carbide in the facecoat of the mold provides favorable properties.
  • the bulk of the mold may also contain silicon carbide.
  • the calcium aluminate cement used in aspects of the disclosure typically comprises three phases or components of calcium and aluminum: calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 Oy), and mayenite (Ca ⁇ AlnC ⁇ ).
  • Calcium monoaluminate is a hydraulic mineral present in calcium alumina cement. Calcium monoaluminate 's hydration contributes to the high early strength of the investment mold. Mayenite is desirable in the cement because it provides strength during the early stages of mold curing due to the fast formation of hydraulic bonds. The mayenite is, however, typically removed during heat treatment of the mold prior to casting.
  • the initial calcium aluminate cement formulation is typically not at thermodynamic equilibrium after firing in the cement manufacturing kiln. However, after mold making and high-temperature firing, the mold composition moves towards a thermodynamically stable configuration, and this stability is advantageous for the subsequent casting process.
  • the weight fraction of calcium monoaluminate in the cement is greater than 0.5, and weight fraction of mayenite is less than 0.15.
  • the mayenite is incorporated in the mold in both the bulk of the mold and the facecoat because it is a fast setting calcium aluminate and it is believed to provide the bulk of the mold and the facecoat with strength during the early stages of curing.
  • Curing may be performed at low temperatures, for example, temperatures between 15 degrees Celsius and 40 degrees Celsius because the fugitive wax pattern is temperature sensitive and loses its shape and properties on thermal exposure above about 35 degrees C. In one example the mold is cured at temperatures below 30 degrees C.
  • the calcium aluminate cement may typically be produced by mixing the cement with high purity alumina, silicon carbide and high purity calcium oxide or calcium carbonate; the mixture of compounds is typically heated to a high temperature, for example, temperatures between 1000 and 1500 degrees C in a furnace or kiln and allowed to react.
  • the resulting product known in the art as a cement "clinker,” that is produced in the kiln is then crushed, ground, and sieved to produce a calcium aluminate cement of the preferred particle size.
  • the calcium aluminate cement is designed and processed to have a minimum quantity of impurities, such as, minimum amounts of silica, sodium and other alkali, and iron oxide.
  • the target level for the calcium aluminate cement is that the sum of the Na 2 0, Si0 2 , Fe 2 0 3 , and Ti0 2 is less than about 2 weight percent. In one embodiment, the sum of the Na 2 0, Si0 2 , Fe 2 0 3 , and Ti0 2 is less than about 0.05 weight percent.
  • the final mold is designed and processed to have a minimum quantity of impurities, such as, minimum amounts of silica, sodium and other alkali, and iron oxide.
  • the target level for the final mold is that the sum of the Na 2 0, Si0 2 , Fe 2 0 3 , and Ti0 2 is less than about 2 weight percent. In one embodiment, the sum of the Na 2 0, Si0 2 , Fe 2 0 3 , and Ti0 2 is less than about 0.05 weight percent.
  • a calcium aluminate cement with bulk alumina concentrations over 35% weight in alumina (A1 2 0 3 ) and less than 65% weight calcium oxide is provided.
  • this weight of calcium oxide is less than 50%.
  • the maximum alumina concentration of the cement may be about 88% (for example, about 12% CaO).
  • the calcium aluminate cement is of high purity and contains up to 70% alumina. The weight fraction of calcium monoaluminate may be maximized in the fired mold prior to casting. A minimum amount of calcium oxide may be required to minimize reaction between the casting alloy and the mold.
  • the range for calcium oxide is less than about 50% and greater than about 10%) by weight.
  • the three phases in the calcium aluminate cement/binder in the mold are calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 0 7 ), and mayenite (Cai 2 Ali 4 0 33 ).
  • the calcium monoaluminate in the cement that generates the facecoat has three advantages over other calcium aluminate phases: 1) the calcium monoaluminate is incorporated in the mold because it has a fast setting response (although not as fast as mayenite) and it is believed to provide the mold with strength during the early stages of curing. The rapid generation of mold strength provides dimensional stability of the casting mold, and this feature improves the dimensional consistency of the final cast component.
  • the calcium monoaluminate is chemically stable with regard to the titanium and titanium aluminide alloys that are being cast.
  • the calcium monoaluminate is used relative to the calcium dialuminate, and other calcium aluminate phases with higher alumina activity; these phases are more reactive with titanium and titanium aluminide alloys that are being cast.
  • the calcium monoaluminate and calcium dialuminate are low expansion phases and are understood to prevent the formation of high levels of stress in the mold during curing, dewaxing, and subsequent casting.
  • the thermal expansion behavior of calcium monoaluminate is a closer match with alumina.
  • the mold contains a continuous silicon carbide-containing intrinsic facecoat between the bulk of mold and the mold cavity.
  • the mold is designed to contain phases that provide improved mold strength during mold making, and the continuous facecoat is designed to provide increased thermal conductivity and increased resistance to reaction during casting.
  • the molds are capable of casting at high pressure, which is desirable for net-shape casting methods.
  • a casting mold composition, a facecoat composition, and preferred constituent phases for the facecoat and the bulk of the mold, have been identified that provide castings with improved properties.
  • the facecoat is defined as the region of the mold adjacent to the internal surface, or mold cavity in the mold.
  • the intrinsic facecoat is one that only contains species that are provided to the mold from the original constituents of the formulation. Thus, the intrinsic facecoat does not contain any species that did not come from the original poured ceramic formulation.
  • extrinsic facecoat is a facecoat that is applied separately and contains species that may not be in the components of the original formulation (e.g., generated in a separate operation).
  • the intrinsic facecoat may be considered, in one example, to be a region about 100 microns thick.
  • the silicon-carbide containing intrinsic facecoat may be about 10 microns to about 500 microns thick.
  • the silicon-carbide containing intrinsic facecoat may be about 10 microns to about 300 microns thick.
  • the silicon-carbide containing intrinsic facecoat may be about 10 microns to about 100 microns thick.
  • the silicon-carbide containing intrinsic facecoat may be about 30 microns to about 200 microns thick.
  • the silicon carbide-containing facecoat is about 50 microns, about 100 microns, about 150 microns, about 200 microns, about 250 microns, about 300 microns, about 350 microns, about 400 microns, about 450 microns, or about 500 microns thick.
  • the facecoat may be continuous. A continuous facecoat allows it to be more effective.
  • the region behind the facecoat and further away from the mold cavity is referred to as the bulk of the mold.
  • One aspect of the present disclosure is a silicon carbide-containing facecoat composition of a mold that is used for casting a titanium-containing article, the facecoat composition comprising calcium monoaluminate, calcium dialuminate, and mayenite, wherein the facecoat composition is a silicon carbide-containing intrinsic facecoat, is about 10 microns to about 500 microns thick, and is located between the bulk of the mold and the surface of the mold that opens to the mold cavity.
  • the facecoat comprises, in one example, of calcium aluminate with a particle size of less than about 50 microns in outside dimension.
  • the particle sizes of calcium aluminate in the bulk of the mold can be larger than 50 microns in outside dimension.
  • the facecoat consists of at least the following four phases; calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 Oy), and mayenite (Ca ⁇ AlnC ⁇ ); all of these phases except the silicon carbide can be in the initial calcium aluminate cement.
  • the facecoat can also contain fine-scale alumina particles,.
  • the bulk of the mold behind the facecoat consists of calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 Oy), mayenite (Cai 2 Ali 4 0 33 ), silicon carbide, and alumina.
  • the alumina can be incorporated as alumina particles, or alumina bubbles.
  • the particles can have a range of geometries, such as round particles, or irregular aggregate.
  • the alumina particle size can be as small as 10 microns and as large as 10mm.
  • the alumina may consist of both round particles and bubbles, since these geometries increase the fluidity of the investment mold mixture.
  • These particles may be hollow.
  • the alumina particle size in the bulk of the mold is greater than 50 microns.
  • the fluidity impacts the manner in which the cement partitions to the fugitive pattern (such as a wax) during pouring and setting of the investment mold mix around the fugitive pattern.
  • the fluidity affects the surface finish and fidelity of the surface features of the final casting produced from the mold.
  • the size of the particles in the facecoat are less than 50 microns, and the size of the particles in the bulk of the mold are more than 50 microns.
  • the present disclosure also provides a silicon carbide-containing intrinsic facecoat composition for investment casting molds, and a bulk mold composition, that together can provide improved cast components of titanium and titanium alloys.
  • the mold may comprise calcium aluminate cement and alumina particles.
  • the calcium aluminate cement serves two functions. First, the cement generates an in-situ facecoat in the cavity of the mold that is generated by removal of a fugitive pattern, and second it acts as a binder between the alumina particles in the bulk of the mold behind the facecoat.
  • the facecoat in one example contains silicon carbide.
  • the bulk composition of the mold in one example contains between 10 and 50 weight percent of calcium oxide.
  • the composition of CaO in the facecoat in one example is between 20 and 40 weight percent of the mold.
  • the final mold may have a density of less than 2 grams/cubic centimeter and a strength of greater than 500psi.
  • the mold is designed to contain phases that provide improved mold strength during mold making, and the continuous facecoat that contains silicon carbide, is designed to provide increased thermal conductivity and increased resistance to reaction during casting.
  • the silicon carbide is designed to provide increased thermal conductivity during casting.
  • the silicon carbide particles are, in one example, about 1 to about 100 microns in outside dimension. In another example, the silicon carbide particles are about 1 to about 50 microns in outside dimension. In a particular example, the silicon carbide particles are about 10 microns to about 30 microns in outside dimension. Alternatively, the silicon carbide particles may be about 20 microns to about 30 microns in outside dimension. In a particular example, silicon carbide particles are about 25 microns in outside dimension.
  • the silicon carbide particles are about 10 microns, about 15 microns, about 20 microns, about 25 microns, about 30 microns, about 35 microns, about 40 microns, about 45 microns, about 50 microns, about 60 microns, about 70 microns, about 80 microns, about 90 microns, or about 100 microns in outside dimension.
  • the mold may comprise the bulk of the mold and a silicon carbide-containing intrinsic facecoat, with the bulk of the mold and the silicon carbide-containing intrinsic facecoat having different compositions, and the silicon carbide-containing intrinsic facecoat comprising calcium aluminate with a particle size of less than about 50 microns.
  • the mold may comprise the bulk of the mold and a silicon carbide-containing intrinsic facecoat, wherein the bulk of the mold and the intrinsic facecoat have different compositions and wherein the bulk of the mold comprises alumina particles larger than about 50 microns.
  • the mold in one example, comprises the bulk of the mold and a silicon carbide-containing intrinsic facecoat, wherein the bulk of the mold comprises alumina particles larger than about 50 microns and the intrinsic facecoat comprises calcium aluminate particles less than about 50 microns in size.
  • Net shape casting approaches as provided for in the present disclosure allow parts that can be inspected with non destructive methods, such as x-ray, ultrasound, or eddy current, in greater detail and at lower costs.
  • non destructive methods such as x-ray, ultrasound, or eddy current.
  • the difficulties associated with attenuation and scattering of the inspection radiation in oversized thick sections is reduced. Smaller defects can potentially be resolved, and this can provide parts with improved mechanical performance.
  • the present disclosure provides a casting mold composition and a casting process that can provide improved components of titanium and titanium alloys.
  • the mold is constructed using calcium aluminate cement, or binder, and alumina particles.
  • the mold contains a silicon carbide-containing intrinsic facecoat between the bulk of mold and the mold cavity.
  • the size of the particles in the facecoat are typically less than 50 microns.
  • the size of the particles in the bulk of the mold can be larger than 50 microns.
  • the size of the particles in the bulk of the mold may be greater than 1mm.
  • the facecoat the size of the particles may be less than 50 microns, and the size of the particles in the bulk of the mold may be more than 50 microns.
  • the facecoat is a continuous silicon carbide-containing intrinsic facecoat, allowing it to be more effective.
  • the silicon carbide-containing intrinsic facecoat may have, by weight fraction, at least 20 percent more calcium aluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold.
  • the weight fraction of calcium monoaluminate in the silicon carbide-containing intrinsic facecoat may have more than 0.45 and the weight fraction of mayenite may be less than 0.10.
  • the calcium monoaluminate in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.1 to 0.9; the calcium dialuminate in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.05 to 0.90; and the mayenite in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.001 to 0.05.
  • the increased weight fraction of calcium monoaluminate in the silicon carbide-containing intrinsic facecoat reduces the rate of reaction of the molten alloy with the mold during casting.
  • the silicon carbide-containing intrinsic facecoat may have, by weight fraction, at least 20 percent more calcium monoaluminate than the bulk of the mold.
  • the silicon carbide- containing intrinsic facecoat may have, by weight fraction, at least 20 percent less alumina than the bulk of the mold.
  • the silicon carbide-containing intrinsic facecoat may have, by weight fraction, at least 20 percent more calcium aluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold.
  • the constituent phases of the facecoat, as well as the constituent phases of the bulk of the mold are important to the properties of the casting.
  • the facecoat of the mold provides minimum reaction with the alloy during casting, and as a result the mold provides castings with the required component properties.
  • External properties of the casting include features such as shape, geometry, and surface finish.
  • Internal properties of the casting include mechanical properties, microstructure, and defects (such as pores and inclusions) below a critical size.
  • calcium monoaluminate (CaAl 2 0 4 ) is desirable for at least two reasons.
  • the facecoat comprises calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 Oy), mayenite (Ca ⁇ AlnC ⁇ ), silicon carbide, and alumina.
  • the size of the particles in the facecoat are less than 50 microns in outside dimension.
  • the combination of calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 0 7 ) is more than 50 weight percent, and the alumina concentration is less than 50 weight percent. There may be more than 20 weight percent calcium monoaluminate (CaAl 2 0 4 ) in the facecoat.
  • the region behind the facecoat and further away from the mold cavity is referred to as the bulk of the mold.
  • the combination of calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 0 7 ) is less than 50 weight percent, and the alumina concentration in the bulk of the mold is greater than 50 weight percent.
  • the amount of silicon carbide in the facecoat can vary.
  • the amount of silicon carbide can be varied from 15 weight percent to 45 weight percent.
  • the inventors of the instant disclosure discovered that not only is silicon carbide able to provide superior properties to the mold and facecoat in terms of stability at high temperatures and suitability for casting the titanium alloys, but also that a certain level of silicon carbide in the bulk and the facecoat was discovered to be optimal. For example, 35 weight percent in the facecoat provided can provide good results. If there is too much silicon carbide, that is, the level of silicon carbide is at or above 45 weight percent in the facecoat, then there is a possibility of carbon pick up during casting and an unacceptable level of carbon in the final part. On the other hand, if there is no silicon carbide or a minimal amount (e.g. less than about 20 weight percent), then the silicon carbide will not increase the thermal conductivity of the mold beyond the level of the thermal conductivity of the mold without the silicon carbide.
  • extrinsic facecoats that are used in casting titanium alloys are typically yttria based facecoats, or zirconia based facecoats.
  • extrinsic facecoats in molds that are used for casting can degenerate, crack, and spall during mold processing (such as removal of the fugitive pattern and firing) and casting.
  • the pieces of facecoat that become detached from the extrinsic facecoat can become entrained in the casting when the mold is filled with molten metal, and the ceramic facecoat becomes an inclusion in the final part. The inclusion reduces the mechanical performance of the component that is produced from the casting.
  • the calcium aluminate cement of the present disclosure is referred to as a cement or binder, and in one embodiment, it is mixed with silicon carbide particles and alumina particles to make a castable investment mold mix.
  • the calcium aluminate cement is typically >30% by weight in the castable investment mold mix; the use of this proportion of calcium aluminate cement is a feature of the present disclosure because it favors formation of a silicon carbide- containing intrinsic facecoat. Applicants found that the selection of the correct calcium aluminate cement chemistry and alumina formulation are important in determining the performance of the mold.
  • CaO calcium oxide
  • the facecoat may comprise calcium aluminate cement with a particle size less than about 50 microns.
  • the particle size of the calcium aluminate cement may, in another example, be less than about 10 microns.
  • the bulk of the mold has particles greater than 50 microns in size and can contain alumina.
  • the facecoat has less alumina and more calcium aluminate cement than the bulk of the mold.
  • the silicon carbide-containing intrinsic facecoat may have, by weight fraction, at least 20 percent more calcium aluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold.
  • the calcium monoaluminate in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.1 to 0.9;
  • the calcium dialuminate in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.05 to 0.90; and the mayenite in the silicon carbide-containing intrinsic facecoat comprises a weight fraction of 0.001 to 0.05.
  • the increased weight fraction of calcium monoaluminate and dialuminate in the silicon carbide-containing intrinsic facecoat reduces the rate of reaction of the molten alloy with the mold during casting.
  • the initial cement slurry is mixed to have a viscosity of between 30 and 1500 centipoise. In one embodiment, viscosity range is between 50 and 500 centipoise. If the viscosity is too low, the slurry will not maintain all the solids in suspension, and settling of the heavier particles will occur and lead to segregation during curing, and a silicon carbide- containing intrinsic facecoat will not be formed. That is, if the final slurry mix viscosity is too low, settling of the heavier particles will occur during curing, and the mold will not have the required uniform composition throughout the bulk of the mold.
  • the calcium aluminate particles can not partition to the fugitive pattern, and the intrinsic facecoat will not be formed. That is, if the final slurry/mix viscosity is too high, the final slurry mix will not flow around the fugitive pattern, and the internal cavity of the mold will not be suitable for casting the final required part.
  • the final slurry with the calcium aluminate cement and the alumina particles is mixed to have a viscosity of between approximately 2000 and 8000 centipoise.
  • the final slurry viscosity may range between 3000 and 6000 centipoise.
  • the investment mold may consist of multi-phase mixtures of fine-scale ( ⁇ 50 microns) calcium aluminate cement particles, fine-scale ( ⁇ 50 microns) alumina particles, fine- scale ( ⁇ 50 microns) silicon carbide, and larger scale (>100 microns) alumina particles.
  • the intrinsic facecoat does not contain any alumina particles greater than 50 microns.
  • the silicon carbide-containing intrinsic facecoat is formed because the fine-scale cement particles in suspension in the water-based investment mix partition preferentially to the fugitive/wax pattern during mold making, and forms an intrinsic facecoat layer that is enriched in the fine-scale particles ( ⁇ 50 microns), including the calcium monoaluminate, calcium dialuminate, silicon carbide, and alumina particles.
  • the fine-scale particles ⁇ 50 microns
  • the slurry viscosity and the solids loading are factors in forming the silicon carbide-containing intrinsic facecoat.
  • the absence of large-scale (>100 micron) particles in the intrinsic facecoat improves the surface finish of the mold and the resulting casting.
  • the increased weight fraction of calcium monoaluminate and dialuminate in the intrinsic facecoat reduces the rate of reaction of the molten alloy with the mold during casting.
  • the silicon carbide is typically incorporated as particles with a size of less than
  • the silicon carbide powder used for some examples described in the present disclosure had a particle size of up to about 45 microns, and less than about 20 microns in other examples that are described.
  • the alumina can be incorporated as alumina particles, or hollow alumina particles.
  • the particles can have a range of geometries, such as round particles, or irregular aggregate.
  • the alumina particle size can be as small as 10 microns and as large as 10mm. In one example the alumina consists of both round particles and bubbles or hollow particles, since these geometries increase the fluidity of the investment mold mixture.
  • the fluidity improves the surface finish and fidelity of the surface features of the final casting produced from the mold.
  • the calcium aluminate cement particulate typically has a particle size of less than 50 microns.
  • a particle size of less than 50 microns is used for three reasons: first, the fine particle size promotes the formation of hydraulic bonds during mold mixing and curing, second the fine particle size can promote inter-particle sintering during firing, and this can increase the mold strength, and third, the fine particle size improves surface finish of the mold cavity.
  • the calcium aluminate cement powder can be used either in its intrinsic form, or in an agglomerated form, such as spray dried agglomerates.
  • the calcium aluminate cement can also be preblended with fine-scale (e.g., ⁇ 10 micron) alumina before mixing with larger-scale alumina; the fine-scale alumina can provide an increase in strength due to sintering during high- temperature firing.
  • the silicon carbide particulate typically has a particle size of less than 100 microns, and preferably less than 50 microns; at this size it can be intimately mixed with the calcium aluminate cement particles, and it can contribute to the performance of the facecoat.
  • the silicon carbide particles with a size of less than 100 microns can improve the surface finish of the mold and the subsequent cast component. If the silicon carbide particles are too large (more than 100 microns), for a given weight fraction of silicon carbide that is added, the particles do not generate the desired improvement (i.e. increase) in thermal conductivity.
  • the calcium aluminate cement is the binder, and the binder is considered the main skeleton of the mold structure behind the facecoat. It is the continuous phase in the mold and provides strength during curing, and casting.
  • the bulk of the mold composition comprises fine-scale ( ⁇ 50 microns) calcium aluminate cement particles, and larger scale (e.g., >100 microns) alumina particles.
  • the facecoat composition comprises calcium aluminate cement and silicon carbide.
  • the calcium aluminate cement that makes up the facecoat comprises at least three phases; calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 0 7 ), and mayenite (Cai 2 Ali 4 0 33 ).
  • the facecoat can also contain fine-scale alumina particles.
  • the bulk of the mold behind the facecoat comprises calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 0 7 ), mayenite (Cai 2 Ali 4 0 3 3), silicon carbide, and alumina.
  • the alumina can be incorporated as alumina particles, for example hollow alumina particles.
  • the silicon carbide and alumina particles can have a range of geometries, such as round particles, or irregular aggregates; furthermore, these particles may be hollow.
  • the alumina particle size can be as small as 10 microns and as large as 10mm.
  • the alumina consists of both round particles and hollow particles, since these geometries increase the fluidity of the investment mold mixture.
  • the alumina particle size in the bulk of the mold is greater than 50 microns.
  • the fluidity impacts the manner in which the cement partitions to the fugitive pattern (such as a wax) during pouring and setting of the investment mold mix around the fugitive pattern.
  • the fluidity affects the surface finish and fidelity of the surface features of the final casting produced from the mold.
  • the calcium aluminate cement particulate that generates the facecoat typically has a particle size of less than 50 microns.
  • a particle size of less than 50 microns has several advantages, including: first, the fine particle size promotes the formation of hydraulic bonds during mold mixing and curing, second the fine particle size can promote inter-particle sintering during firing, and this can increase the mold strength, and third, the fine particle size improves surface finish of the mold cavity.
  • the calcium aluminate cement powder can be used either in its intrinsic form, or in an agglomerated form, such as spray dried agglomerates.
  • the calcium aluminate cement can also be preblended with fine-scale (e.g., ⁇ 10 micron) alumina before mixing with larger-scale alumina; the fine-scale alumina can provide an increase in strength due to sintering during high-temperature firing. However, if the alumina particles partition to the facecoat, the casting properties can be reduced.
  • fine-scale e.g., ⁇ 10 micron
  • the molten alloy will react with the alumina in an undesirable way and generate gas bubbles that create surface defects and defects within the casting itself.
  • the properties of the resulting casting such as strength and fatigue strength are reduced.
  • the presently disclosed methods allow for the formation of a facecoat that has significantly less alumina in the silicon carbide-containing intrinsic facecoat than in the bulk of the mold.
  • the treatment of the facecoat and the mold from room tempeature to the final firing temperature can also be important, specifically the thermal history and the humidity profile.
  • the heating rate to the firing temperature, and the cooling rate after firing are features of the present disclosure. If the facecoat and the mold are heated too quickly, they can crack internally or externally, or both; facecoat and mold cracking prior to casting is highly undesirable, it will generate poor surface finish, at least. In addition, if the mold and facecoat are heated too quickly the facecoat of the mold can crack and spall off; this can lead to undesirable inclusions in the final casting in the worst case, and poor surface finish, even if there are no inclusions. If the facecoat and the mold are cooled too quickly after reaching the maximum mold firing temperature, the facecoat or the bulk of the mold can also crack internally or externally, or both.
  • the solids loading of the initial cement mix and the solids loading of the final mold mix have important effects on the mold structure and the ability to form a silicon carbide- containing intrinsic facecoat within the mold.
  • the percentage of solids loading is defined as the total solids in the mix divided by the total mass of the liquid and solids in the mix, described as a percentage. In one embodiment, the percentage of solids in the initial calcium aluminate-liquid cement mix is about 60 percent to about 78 percent.
  • the cement particles in the initial cement slurry are less than about 70 percent, then the cement particles will not remain in suspension and during curing of the mold the cement particles will separate from the water and the composition will not be uniform throughout the mold.
  • the solids loading is too high in the cement (for example greater than about 78 percent)
  • the viscosity of the final mix with the large-scale alumina will be too high (for example greater than about 85%, depending on the amount, size, and morphology of the large- scale alumina particles that are added)
  • the cement particles in the mix will not be able to partition to the fugitive pattern within the mold, and the silicon carbide-containing intrinsic facecoat will not be formed.
  • the percentage of solids in the final calcium aluminate-liquid cement mix with the large-scale may be about 75 percent to about 90 percent.
  • the percentage of solids in the final calcium aluminate-liquid cement mix with the large-scale alumina particles may be about 78 percent to about 88 percent.
  • the percentage of solids in the final calcium aluminate-liquid cement mix with the large-scale alumina particles is about 78 percent to about 84 percent.
  • These alumina particles may be hollow.
  • the percentage of solids in the final calcium aluminate-liquid cement mix with the large-scale alumina particles is about 80 percent.
  • An investment mold is formed by formulating the investment mix of the ceramic components, and pouring the mix into a vessel that contains a fugitive pattern.
  • the investment mold formed on the pattern is allowed to cure thoroughly to form a so-called "green mold.”
  • the silicon carbide-containing intrinsic facecoat and the investment mold are formed on the pattern and they are allowed to cure thoroughly to form this green mold.
  • curing of the green mold is performed for times from 1 hour to 48 hours.
  • the fugitive pattern is selectively removed from the green mold by melting, dissolution, ignition, or other known pattern removal technique.
  • Typical methods for wax pattern removal include oven dewax (less than 150 degrees C), furnace dewax (greater than 150 degrees C), steam autoclave dewax, and microwave de waxing.
  • the green mold then is fired at a temperature above 600 degrees C, for example 600 to 1400 degrees C, for a time period in excess of 1 hour, preferably 2 to 10 hours, to develop mold strength for casting and to remove any undesirable residual impurities in the mold, such as metallic species (Fe, Ni, Cr), and carbon-containing species.
  • the firing temperature is at least 950 degrees C.
  • the atmosphere of firing the mold is typically ambient air, although inert gas or a reducing gas atmosphere can be used.
  • the firing process also removes the water from the mold and converts the mayenite to calcium aluminate. Another purpose of the mold firing procedure is to minimize any free silica that remains in the facecoat and mold prior to casting. Other purposes are to remove the water, increase the high temperature strength, and increase the amount of calcium monoaluminate and calcium dialuminate.
  • the mold is heated from room temperature to the final firing temperature, specifically the thermal history is controlled.
  • the heating rate to the firing temperature, and the cooling rate after firing are typically regulated or controlled. If the mold is heated too quickly, it can crack internally or externally, or both; mold cracking prior to casting is highly undesirable. In addition, if the mold is heated too quickly, the internal surface of the mold can crack and spall off. This can lead to undesirable inclusions in the final casting, and poor surface finish, even if there are no inclusions. Similarly, if the mold is cooled too quickly after reaching the maximum temperature, the mold can also crack internally or externally, or both.
  • the mold composition described in the present disclosure is particularly suitable for titanium and titanium aluminide alloys.
  • the facecoat and the bulk of the mold composition after firing and before casting can influence the mold properties, particularly with regard to the constituent phases.
  • a high weight fraction of calcium monoaluminate in the mold is used, for example, a weight fraction of 0.15 to 0.8.
  • it is desirable to minimize the weight fraction of the mayenite in the bulk of the mold and the silicon carbide-containing intrinsic facecoat for example, using a weight fraction of 0.01 to 0.2, because mayenite is water sensitive and it can provide problems with water release and gas generation during casting.
  • the mold can also contain small weight fractions of aluminosilicates and calcium aluminosilicates.
  • the sum of the weight fraction of aluminosilicates and calcium aluminosilicates may typically be kept to less than 5% in the bulk of the mold and less than 0.5% in the facecoat, in order to minimize reaction of the mold with the casting.
  • One aspect of the present disclosure is a method for forming a casting mold for casting a titanium-containing article.
  • the method comprises combining calcium aluminate and silicon carbide with a liquid to produce a slurry of calcium aluminate, wherein the percentage of solids in the initial calcium aluminate / liquid mixture is about 60% to about 80% by weight of the slurry and a viscosity of the slurry is about 30 to about 1500 centipoise.
  • the method further includes the step of introducing the slurry into a mold cavity that contains a fugitive pattern, and allowing the slurry to cure in the mold cavity to form a mold of a titanium-containing article.
  • oxide particles Prior to the addition of the slurry into the mold cavity, oxide particles may be added, in one example, hollow aluminum oxide particles may be added.
  • Silicon carbide may be added to the calcium aluminate before or during the making of the slurry.
  • the silicon carbide particles may be from about 1 microns to about 1000 microns in outside dimension. In certain circumstances, the silicon carbide particles may be about 5 micron to about 100 microns in outside dimension. In a particular example, the silicon carbide particles are about 10 to about 50 microns in outside dimension. In one example, the particle size of the calcium aluminate is less than about 50 microns in outside dimension.
  • the calcium aluminate cement may comprise more than 20% by weight of the composition used to make the mold.
  • Outside dimension refers to the longest distance between two points on a particle.
  • the outside dimension refers to the diameter. If the particle is an oval shape, then the outside dimension refers to the longest distance between two points that are the furthest away from each other on the circumference of the oval particle. Further still, if the particle is irregularly shaped, the outside dimension refers to the distance between two points on the irregularly shaped particle which are the furthest away from each other.
  • the casting-mold composition of the present disclosure comprises an investment casting-mold composition.
  • the investment casting-mold composition comprises a near-net-shape, titanium-containing metal, investment casting mold composition.
  • the investment casting-mold composition comprises an investment casting- mold composition for casting near-net-shape titanium aluminide articles.
  • the near-net-shape titanium aluminide articles comprise, for example, near-net-shape titanium aluminide turbine blades.
  • the selection of the correct calcium aluminate cement chemistry and alumina formulation are factors in the performance of the mold during casting. In terms of the calcium aluminate cement, it may be necessary to minimize the amount of free calcium oxide in order to minimize reaction with the titanium alloy. If the calcium oxide concentration in the cement is less than about 10% by weight, the alloy reacts with the mold because the alumina concentration is too high, and the reaction generates undesirable oxygen concentration levels in the casting, gas bubbles, and a poor surface finish in the cast component. Free alumina is less desirable in the mold material because it can react aggressively with titanium and titanium aluminide alloys.
  • the method may further comprise adding oxide particles into the slurry.
  • the oxide particles are selected from a group consisting of aluminum oxide particles, magnesium oxide particles, calcium oxide particles, zirconium oxide particles, titanium oxide particles, silicon oxide particles, and compositions thereof.
  • the oxide particles may be aluminum oxide (also known as alumina).
  • the aluminum oxide particles can range in size and may be larger than about 50 microns. In particular instances, the added aluminum oxide particles that may be used are less than about 500 microns in outside dimension.
  • the aluminum oxide particles may comprise from about 30 % by weight to about 68 % by weight of the composition used to make the mold. These oxide particles may be hollow.
  • the mold can be sensitive to pick up of water and carbon dioxide from the environment.
  • the calcium oxide concentration in the investment mold may typically be kept below 50%.
  • the calcium oxide concentration in the bulk of the investment mold is between 10 % and 50 % by weight.
  • the calcium oxide concentration in the bulk of the investment mold is between 10 % and 40 % by weight.
  • the calcium oxide concentration in the bulk of the investment mold may be between 25 % and 35 % by weight.
  • the composition of CaO in the facecoat is between 20 and 40 percent by weight.
  • the calcium oxide concentration in the facecoat of the mold is between 15 % and 30 % by weight.
  • Carbon dioxide can lead to formation of calcium carbonate in the mold during processing and prior to casting, and calcium carbonate is unstable during the casting operation.
  • the water and carbon dioxide in the mold can lead to poor casting quality. If the adsorbed water level is too high, for example, greater than 0.05 weight percent, when the molten metal enters the mold during casting, the water is released and it can react with the alloy. This leads to poor surface finish, gas bubbles in the casting, high oxygen concentration, and poor mechanical properties. In addition, an amount of water can cause the mold to be incompletely filled.
  • the carbon dioxide level is too high, calcium carbonate can form in the mold and when the molten metal enters the mold during casting, the calcium carbonate can decompose generating carbon dioxide, which can react with the alloy; if large amounts of carbon dioxide are released, the gas can cause the mold to be incompletely filled.
  • the resulting calcium carbonate is less than 1 weight percent in the mold.
  • the investment mold Prior to casting a molten metal or alloy, the investment mold typically is preheated to a mold casting temperature that is dependent on the particular component geometry or alloy to be cast. For example, a typical mold preheat temperature is 600 degrees C. Typically, the mold temperature range is 450 degrees C to 1200 degrees C; in one example, the temperature range is 450 degrees C to 750 degrees C, and in certain cases it is 500 degrees C to 650 degrees C.
  • the molten metal or alloy is poured into the mold using conventional techniques which can include gravity, countergravity, pressure, centrifugal, and other casting techniques known to those skilled in the art. Furthermore, a vacuum or an inert gas atmosphere can also be used. For complex shaped thin wall geometries, techniques that use high pressure are preferred.
  • the solidified titanium aluminide or alloy casting is cooled typically to less than 650 degrees, for example, to room temperature, it is removed from the mold and finished using conventional techniques, such as, grit blasting, water jet blasting and polishing.
  • the present disclosure is a method for casting titanium and titanium alloys, comprising: obtaining an investment casting mold composition comprising calcium aluminate and large scale aluminum oxide, wherein the calcium aluminate and alumina are combined with a liquid and silicon carbide to produce a final calcium aluminate / liquid mixture slurry, and wherein the solids in the final mixture are about 70% to about 95% by weight of the slurry; pouring said investment casting mold composition into a vessel containing a fugitive pattern; curing said investment casting mold composition; removing said fugitive pattern from the mold; firing the mold; preheating the mold to a mold casting temperature; pouring molten titanium or titanium alloy into the heated mold; solidifying the molten titanium or titanium alloy; forming a solidified titanium or titanium alloy casting; and removing the solidified titanium or titanium alloy casting from the mold.
  • the silicon carbide particles that are used are, in one example, about 10 microns to about 50 microns in outside dimension. In another example, they are 10 microns to about 100 microns in outside dimension.
  • the silicon carbide was found to increase thermal conductivity during casting compared to if casting is performed in the absence of silicon carbide.
  • the present disclosure is a casting method for titanium and titanium alloys, comprising obtaining an investment casting mold composition comprising calcium aluminate and aluminum oxide, wherein the calcium aluminate is combined with a liquid and silicon carbide to produce a slurry, and wherein the solids in the final calcium aluminate / liquid mixture is about 75% to about 95%.
  • the method may further comprise pouring said investment casting mold composition into a vessel containing a fugitive pattern; curing said investment casting mold composition; removing said fugitive pattern from the mold; and firing the mold.
  • the method may further comprise preheating the mold to a mold casting temperature; pouring molten titanium or titanium alloy into the heated mold; solidifying the molten titanium or titanium alloy and forming a solidified titanium or titanium alloy casting; and removing the solidified titanium or titanium alloy casting from the mold.
  • the silicon carbide particles may be from about 10 microns to about 50 microns in outside dimension.
  • the calcium aluminate particles may comprise particles less than about 50 microns in outside dimension.
  • the aluminum oxide particles may be from about 50 microns to about 1500 microns in outside dimension.
  • the aluminum oxide particles may comprise from about 30 % by weight to about 68 % by weight of the investment casting mold composition used to make the mold.
  • the calcium aluminate cement may comprise more than 20% by weight of the investment casting mold composition used to make the mold.
  • the aluminum oxide particles may be hollow.
  • the calcium oxide may be added such that more than about 10% by weight and less than about 50% by weight of the investment casting mold composition is calcium oxide.
  • the percentage of solids in an initial calcium aluminate - liquid cement mixture used to make the mold may be about 60 % to about 78 %.
  • One aspect of the present disclosure is a titanium or titanium alloy article made by the casting method as recited by the presently disclosed methods.
  • Another aspect of the present disclosure is a casting method for titanium and titanium alloys comprising: obtaining an investment casting mold composition comprising calcium aluminate, wherein the calcium aluminate is combined with silicon carbide particles and alumina particles in a liquid to produce a slurry, such that the solids in the final calcium aluminate / liquid mixture is about 75% to about 95%, and wherein the resulting mold has a silicon carbide-containing intrinsic facecoat.
  • a titanium or titanium alloy article is claimed that is made by the casting method as taught herein.
  • the mold is first heated, or fired, to a temperature of about 600 degrees C to about 1400 degrees C, for example about 950 degrees C or higher, and then cooled to room temperature.
  • the curing step is conducted at temperatures below about 30 degrees C for between one hour to 48 hours.
  • the removing of the fugitive pattern includes the step of melting, dissolution, ignition, oven dewaxing, furnace dewaxing, steam autoclave dewaxing, or microwave dewaxing.
  • the casting may be finished with grit blasting or polishing.
  • the solidified casting is removed from the mold, it is inspected by X-ray or Neutron radiography.
  • the solidified casting is subjected to surface inspection and X-ray radiography after casting and finishing to detect any sub-surface inclusion particles at any location within the casting.
  • X-ray radiography is employed to find inclusions that are not detectable by visual inspection of the exterior surface of the casting.
  • the titanium aluminide casting is subjected to X-ray radiography (film or digital) using conventional X-ray equipment to provide an X-ray radiograph that then is inspected or analyzed to determine if any sub-surface inclusions are present within the titanium aluminide casting.
  • the solidified casting can be subjected to other non-destructive testing, for example, conventional Neutron-ray radiography.
  • the mold compositions described provide a small amount of a material having a high Neutron absorption cross section.
  • a Neutron radiograph is prepared of the cast article. Since the titanium alloy cast article may be substantially transparent to neutrons, the mold material will typically show up distinctly in the resulting Neutron radiograph. In one aspect, it is believed that Neutron exposure results in "neutron activation" of the radiographically dense element.
  • Neutron activation involves the interaction of the Neutron radiation with the radiographically dense element of the casting to effect the formation of radioactive isotopes of the radiographically dense elements of the mold composition.
  • the radioactive isotopes may then be detectable by conventional radioactive detecting devices to count any radiographically dense element isotopes present in the cast article.
  • Another aspect of the present disclosure is a method for forming a casting mold for casting a titanium-containing article.
  • the method includes: combining calcium aluminate with a liquid, such as water, to produce a slurry of calcium aluminate in the liquid; introducing the slurry into a vessel that contains a fugitive pattern; and allowing the slurry to cure in the mold cavity to form a mold of a titanium-containing article.
  • the method further comprises, before introducing the slurry into a mold cavity, introducing oxide particles, for example hollow oxide particles, to the slurry. Additionally, before introducing the slurry into the mold cavity, in one example, hollow particles of aluminum oxide as well as silicon carbide particles that are about 10 microns to about 100 microns are added.
  • the formed mold may be a green mold, and the method may further comprise firing the green mold.
  • the casting mold comprises an investment casting mold, for example, for casting a titanium-containing article.
  • the titanium- containing article comprises a titanium aluminide article.
  • the investment casting-mold composition comprises an investment casting-mold composition for casting near- net-shape titanium aluminide articles.
  • the near-net-shape titanium aluminide articles may comprise near-net- shape titanium aluminide turbine blades.
  • the disclosure is directed to a mold formed from a titanium-containing article casting-mold composition, as taught herein. Another aspect of the present disclosure is directed to an article formed in the aforementioned mold.
  • Yet another aspect of the present disclosure is a titanium or titanium alloy casting made by a casting method comprising: obtaining an investment casting mold composition comprising calcium aluminate, silicon carbide, and aluminum oxide; pouring the investment casting mold composition into a vessel containing a fugitive pattern; curing the investment casting mold composition; removing the fugitive pattern from the mold; firing the mold; preheating the mold to a mold casting temperature; pouring molten titanium or titanium alloy into the heated mold; solidifying the molten titanium or titanium alloy to form the casting; and removing a solidified titanium or titanium alloy casting from the mold.
  • the present disclosure is directed to a titanium or titanium alloy article made by the casting methods taught in this application.
  • the present disclosure is a method for manufacturing a turbine component.
  • the method comprises making a mold by mixing calcium aluminate, calcium dialuminate, silicon carbide, mayenite, and aluminum oxide together with water to form a slurry.
  • the silicon carbide is present, in one example, at about 15% to about 45% by weight.
  • the mold is then fired, and molten titanium or titanium alloy is poured into the mold. After the molten titanium or titanium alloy has cooled and solidified, the casting is removed from the mold.
  • the silicon carbide-containing intrinsic facecoat comprises, in one example, silicon carbide that is present at about 15% to about 45% by weight.
  • Surface roughness is one of the important indices representing the surface integrity of cast and machined parts. Surface roughness is characterized by the centerline average roughness value "Ra", as well as the average peak-to-valley distance “Rz” in a designated area as measured by optical profilometry. A roughness value can either be calculated on a profile or on a surface. The profile roughness parameter (Ra, Rq,...) are more common. Each of the roughness parameters is calculated using a formula for describing the surface. There are many different roughness parameters in use, but R a is by far the most common. As known in the art, surface roughness is correlated with tool wear. Typically, the surface-finishing process though grinding and honing yields surfaces with Ra in a range of 0.1 mm to 1.6 mm. The surface roughness Ra value of the final coating depends upon the desired function of the coating or coated article.
  • Ra Ra is typically expressed in "millionths" of an inch. This is also referred to as “microinches”.
  • the Ra values indicated herein refer to microinches.
  • An Ra value of 70 corresponds to approximately 2 microns; and an Ra value of 35 corresponds to approximately 1 micron.
  • One aspect of the present disclosure is a turbine blade comprising titanium or titanium alloy and having an average roughness, Ra, of less than 20 across at least a portion of its surface area.
  • One aspect of the present disclosure is directed to a mold composition for casting a titanium-containing article, comprising calcium aluminate and silicon carbide.
  • the mold composition further comprises hollow alumina particles.
  • the article comprises a metallic article.
  • the article comprises a titanium aluminide-containing article.
  • the article comprises a titanium aluminide turbine blade.
  • the article comprises a near-net-shape, titanium aluminide turbine blade. This near- net-shape, titanium aluminide turbine blade may require little or no material removal prior to installation.
  • the device comprises a means for obtaining an investment casting mold composition comprising calcium aluminate, silicon caribide and aluminum oxide, wherein the calcium aluminate, silicon caribide and aluminum oxide particles are mixed in a liquid to produce a slurry; a means for pouring said investment casting mold composition into a vessel containing a fugitive pattern; a means for curing said investment casting mold composition; a means for removing said fugitive pattern from the mold; a means for firing the mold; a means for preheating the mold to a mold casting temperature; a means for pouring molten titanium or titanium alloy into the heated mold; a means for solidifying the molten titanium or titanium alloy and forming a solidified titanium or titanium alloy casting; and a means for removing the solidified titanium or titanium alloy casting from the mold.
  • Figure 1 shows a schematic of the mold with the silicon carbide-containing facecoat (10).
  • Figure 1 shows the mold with the silicon carbide-containing intrinsic facecoat (30) that is, for example, approximately 100 microns thick.
  • the schematic shows the silicon carbide- containing intrinsic facecoat (30) with the mold cavity (40) and the bulk of the mold (20) comprising the calcium aluminate mold.
  • the intrinsic facecoat (40) is one that only contains species that are provided to the mold from the original constituents of the formulation. Thus, the intrinsic facecoat does not contain any species that did not come from the original poured ceramic formulation.
  • extrinsic facecoat is a facecoat that is applied separately and contains species that may not be in the components of the original formulation.
  • Figure 3 shows a flow chart, illustrating a method for forming a mold for casting a titanium-containing article (100).
  • the method comprises mixing calcium aluminate and silicon carbide with a liquid to produce a slurry, wherein the percentage of solids in the slurry is about 60% to about 80%) by weight of the slurry and a viscosity of the slurry is about 30 to about 1500 centipoise (110).
  • the slurry is then introduced into a mold cavity that contains a fugitive pattern (120), and allowed to cure to form the mold (130).
  • FIG. 4 shows a flow chart, illustrating a method for casting titanium and titanium alloys (200).
  • the method comprises obtaining an investment casting mold composition comprising calcium aluminate and large scale aluminum oxide, wherein the calcium aluminate and alumina are combined with a liquid and silicon carbide to produce a final calcium aluminate / liquid mixture slurry, and wherein the solids in the final mixture are about 70% to about 95% by weight of the slurry (210).
  • This investment casting mold composition is then poured into a vessel containing a fugitive pattern (120), and cured (230). Once cured, the fugitive pattern is removed from the mold (240) and the mold is fired (250).
  • the mold After firing, the mold is preheated to a mold casting temperature (260), and molten titanium or titanium alloy is poued into the heated mold (270). The molten titanium or titanium alloy is allowed to form a solidified form (280) and this solidified titanium or titanium alloy casting is then removed from the mold (290).
  • Figure 5 shows a flow chart, illustrating a turbine blade produced by the presently disclosed process (300).
  • the method first provides for an investment casting mold comprising calcium aluminate, silicon carbide and aluminum oxide (360).
  • the method further comprises pouring molten titanium or titanium alloy into the mold, having first pre -heated the mold prior to the pouring (370), and solidifying the molten titanium or titanium alloy casting to form a solidified casting (380).
  • the final stage includes removing the solidified titanium or titanium alloy casting from the mold to produce a turbine blade, wherein the turbine blade has an average roughness, Ra, of less than 20 across at least a portion of its surface area (390).
  • Figure 6 shows a flow chart, illustrating a method for manufacturing a turbine component (400).
  • the method includes first making a mold from a mixture comprising calcium aluminate, calcium dialuminate, silicon carbide, mayenite and water, wherein the silicon carbide is present at about 15% to about 45% by weight (420). Additional steps include firing the mold (430), and pouring molten titanium or titanium alloy into the mold (440), solidifying the molten titanium or titanium alloy to form a solidified casting (450), and subsequently removing the casting from the mold (460).
  • a mold was produced by replacing half of the cement in a nominal SiC-free mold with SiC particles with a size of less than 20 microns.
  • a slurry mixture for making an investment mold consisted of 1354 g of a commercially blended 80% calcium aluminate cement, CA25C.
  • the CA25C product nominally consists of a 70% calcium aluminate cement blended with alumina to adjust the composition to 80% alumina.
  • the particle size of the blended cement, CA25C is less than 45 microns.
  • a cement slurry with an initial solids loading of 61 percent was produced using 820.5g of deionized water, and 90.5g of colloidal silica.
  • Typical suitable colloidal silicas include Remet LP30, Remet SP30, Nalco 1030. LP30 was used in this example.
  • 1354g of silicon carbide of a size range of less than about 20 microns was added to the slurry.
  • the solids loading of the mix with the silicon carbide added was 75.6%.
  • 1472g of alumina bubble of a size range of less than about 0.85mm and greater than about 0.5mm was added to the slurry.
  • the alumina bubbles are formed from molten alumina, resulting in hollow spheres of low bulk density.
  • the investment mold mix was poured in a controlled manner into a vessel.
  • the solids loading of the final mold mix was 82.7%.
  • the mold mix poured well with satisfactory viscosity and rheology. After curing, the mix was of good strength (more than 100 pounds per square inch) and uniform composition.
  • the mold was then fired at a temperature of 1000°C for 4 hours.
  • the final mold composition without the water contained 32.2 percent by weight of blended calcium aluminate cement (CA25C), 32.2 percent by weight of silicon carbide, and 35 percent by weight of alumina bubble with 0.6 percent silica.
  • the mold possessed reduced alumina activity from those taught by the conventional molds.
  • a slurry mixture for making an investment mold consisted of 5416 g of a commercially blended 80% calcium aluminate cement, CA25C, produced by the company Almatis.
  • a cement slurry with an initial solids loading of 75.2 percent was produced using 1669g of deionized water, and 181g of colloidal silica.
  • 1472g of silicon carbide was added to the slurry.
  • the solids loading of the mix with the silicon carbide added was 79.5%.
  • the final mold composition without the water contained 64.4 percent by weight of blended calcium aluminate cement (CA25C), 17.5 percent by weight of silicon carbide, and 17.5 percent by weight of alumina bubble with 0.6 percent silica.
  • CA25C blended calcium aluminate cement
  • the amount of SiC and the amount of cement in the mold was found to be a factor in terms of improving mold quality. If the cement is reduced to a concentration that is too low, then the mold can be susceptible to cracking.
  • the size of SiC particles in the mold was also found to be important in terms of improving mold quality, such as external cracks and internal cracks. For example, if the SiC particle size is too large (greater than about 100 microns), then the internal cracking is unacceptable, as will be described in the next example.
  • a significant factor is the curing behavior of the mold, and during curing the mold temperature can increase.
  • the results in Figure 2 show the maximum temperature increase during curing of a range of molds.
  • the graph shows that the replacement of large scale hollow alumina particles (alumina bubble) with a particle size of less than 20 microns in outside dimension SiC reduced the temperature increase during curing from about 30 degrees Celsius to ⁇ 27 degrees Celsius.
  • Figure 2 shows that the replacement of large scale hollow alumina particles with CA25C cement reduced the temperature increase during curing from ⁇ 30degrees Celsius to ⁇ 25 degrees Celsius.
  • the graph further shows that the replacement of large scale hollow alumina particles with a particle size of less than 600 microns or less SiC has little effect on the temperature increase during curing. Further, that replacing large scale (more than about 50 microns in outside dimension) with ⁇ 110 microns in outside dimension SiC has little effect on the temperature increase during curing.
  • the mold was fired at a temperature of 1000°C for 4 hours.
  • the final mold composition without the water contained 24.1 percent blended calcium aluminate cement (CA25C), 40.3 silicon carbide, and 35 percent free alumina bubble with 0.6 percent silica.
  • the mold possessed reduced alumina activity from those taught by the prior art.
  • a slurry mixture for making an investment mold consisted of 2708 g of a commercially blended 80% calcium aluminate cement, CA25C.
  • a cement slurry with an initial solids loading of 61.0 percent was produced using 1641g of deionized water, and 181g of colloidal silica.
  • 2708g of silicon carbide was added to the slurry.
  • the solids loading of the mix with the silicon carbide added was 75.6%.
  • the mold was fired at a temperature of 1000°C for 4 hours.
  • the final mold composition without the water contained 32.2 percent blended calcium aluminate cement (CA25C), 32.2 silicon carbide, and 35 percent alumina bubble with 0.6 percent silica.
  • the mold possessed reduced free alumina activity from those taught by the prior art.
  • Typical high-purity calcined alumina particle types include fused, tabular, and levigated alumina.
  • Typical suitable colloidal silicas include Remet LP30, Remet SP30, Nalco 1030, Ludox.
  • the produced mold was used for casting titanium aluminide-containing articles such as turbine blades with a good surface finish.
  • the roughness (Ra) value was less than 100 microinches, and with an oxygen content of less than 2000 parts per million [ppm].
  • the formulations generally produced a mold that was approximately 120mm diameter and 400mm long, and one that had a density of less than 2 grams per cubic centimeter.
  • the mold possessed a silicon carbide-containing intrinsic facecoat that consisted of calcium aluminate phases, and the facecoat thickness was approximately 100 microns.
  • the mold that was so produced was used successfully for casting titanium aluminide turbine blades with a good surface finish; for example, where the Ra was less than 100, and with an oxygen content of less than 2000ppm.
  • This formulation produced a mold that had a density of less than 2 grams per cubic centimeter.
  • the mold mix was prepared by mixing the calcium aluminate cement, water, and colloidal silica in a container. A high-shear form mixing was used. If not mixed thoroughly, the cement can gel, and the fluidity is reduced so that the mold mix will not cover the fugitive pattern uniformly, and the silicon carbide-containing intrinsic facecoat will not be generated.
  • the alumina particles are added.
  • the fine-scale alumina particles are added.
  • the fine-scale silicon carbide particulate are added and mixed with the cement slurry.
  • the larger-size (for example, 0.5-1.0 mm) alumina particles are added and mixed with the cement-alumina formulation.
  • the viscosity of the final mix is another factor for the formation of a high quality silicon carbide-containing intrinsic facecoat, as it must not be too low or too high.
  • Another factor of the present disclosure is the solids loading of the cement mix and the amount of water.
  • accelerants, and retarders can be used at selected points during the mold making process steps.
  • the investment mix is poured in a controlled manner into a vessel that contains the fugitive wax pattern.
  • the vessel provides the external geometry of the mold, and the fugitive pattern generates the internal geometry.
  • the correct pour speed is a further feature, if it is too fast air can be entrapped in the mold, if it is too slow separation of the cement and the alumina particulate can occur. Suitable pour speeds range from about 1 to about 20 liters per minute. In one embodiment, the pour speed is about 2 to about 6 liters per minute. In a specific embodiment, the pour speed is about 4 liters per minute.
  • the mold formulation was designed so that there was less than
  • the lightweight fused alumina hollow particles incorporated in the mix provide low thermal conductivity.
  • a solids loading of the initial cement slurry mixture with all components without the large-scale alumina particles is 60% and this value is below the desired limit for making a cement slurry that can form a silicon carbide containing facecoat in the mold.
  • the mold formed a silicon carbide-containing intrinsic facecoat with a thickness of approximately 100 microns.
  • the alumina hollow particles provide a mold with a reduced density and lower thermal conductivity.
  • the formulation produced a mold that was approximately 120mm diameter and 400 mm long. The mold was cured and fired at high temperature. The produced mold was used for casting titanium aluminide-containing articles, such as turbine blades, with a good surface finish. The roughness (Ra) value was less than 100, and with an oxygen content of less than 2000 ppm. In most embodiments, the formulation produced a mold that had a density of less than 1.8 grams per cubic centimeter.
  • the thermal conductivity of the bulk of the mold is substantially less than that of alumina at all temperatures. The thermal conductivity was measured using hot wire platinum resistance thermometer technique (ASTM test C-l 113).
  • the mold forms a silicon carbide-containing intrinsic facecoat, but the composition of the bulk of the mold, and in particular the composition of the facecoat, contains too much silica.
  • the bulk composition of silica in the mold is about 1.5 weight percent.
  • the high concentration of colloidal silica in the mix can lead to residual crystalline silica, and silicates, such as calcium aluminosilicate and alumino silicate in the final fired mold.
  • the high silica content of the mold, and the facecoat in particular, provides two limitations of this mold formulation. First, shrinkage can occur on firing and this leads to problems, such as cracking in the facecoat and dimensional control of the component. Second, the high silica content in the facecoat can cause reaction with the molten titanium and titanium aluminide alloys when the mold is filled during casting; this reaction leads to unacceptable casting quality.
  • the mold has a uniform composition along the 16 inch length of the mold in both the bulk of the mold, and the silicon carbide-containing intrinsic facecoat of the mold.
  • the bulk composition of silica in the mold is 0.6 weight percent.
  • the mold forms a silicon carbide- containing intrinsic facecoat with a low silica content.
  • the low silica content of the mold and in particular the silicon carbide-containing intrinsic facecoat provides a mold that is preferred for casting titanium and titanium aluminide alloys.
  • the weight percentage of alumina hollow particles in the mold is about 35 percent.
  • the mold forms a silicon carbide-containing intrinsic facecoat with a thickness of approximately 100 microns.
  • the mold is suitable for casting.
  • the mold formulation that is produced possesses some attractive attributes, but has several limitations.
  • the high silica and silicate content of the mold and the facecoat in particular provides two limitations of this mold formulation.
  • shrinkage can occur on firing and this leads to problems, such as cracking in the facecoat and dimensional control of the component.
  • the high silica content in the facecoat can cause reaction with the molten titanium aluminide alloy when the mold is filled during casting; this reaction leads to unacceptable casting quality.
  • the alumina hollow particles size is too large, this reduces the fluidity of the resulting mix. The lower fluidity leads to a thinner silicon carbide-containing intrinsic facecoat, and the resulting mold produces castings with lower quality.
  • the colloidal silica can affect the rate of reaction of the calcium aluminate phases with water, and it can also affect the mold strength during curing. This rate of reaction of the calcium aluminate phases with water controls the working time of the investment mold mix during mold making. This time was between about 30 seconds and about 10 minutes. If the working time of the investment mold mix is too short, there is insufficient time to make large molds of complex-shaped components, and the continuous silicon carbide-containing intrinsic facecoat is not formed.
  • the constituent phases in the cement that makes up the continuous facecoat of the mold, and provides the binder for the bulk of the mold, are a feature of the present disclosure.
  • the three phases in the calcium aluminate cement comprises calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaALtOy), and mayenite (Cai 2 Ali 4 0 33 ), and the inventors made this selection to achieve several purposes.
  • the phases must dissolve or partially dissolve and form a suspension that can support all the aggregate phases in the subsequent investment mold making slurry.
  • the phases must promote setting or curing of the mold after pouring.
  • the phases must provide strength to the mold during and after casting.
  • the phases must exhibit minimum reaction with the titanium alloys that is cast in the mold.
  • the mold must have a suitable thermal expansion match with the titanium alloy casting in order to minimize the thermal stress on the part that is generated during post-solidification cooling.
  • the three phases in the calcium aluminate cement/binder in the mold and in the facecoat of the mold are, in one example, calcium monoaluminate (CaAl 2 0 4 ), calcium dialuminate (CaAl 4 Oy), mayenite (Cai 2 Ali 4 0 33 ), and silicon carbide.
  • the mayenite is incorporated in the mold because it is a fast setting calcium aluminate and it provides the silicon carbide-containing intrinsic facecoat and the bulk of the mold with strength during the early stages of curing. Curing must be performed at low temperatures, because the fugitive wax pattern is temperature sensitive and loses its shape and properties on thermal exposure above -35 deg C. In one example, the mold is cured at temperatures below 30 deg C.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Wood Science & Technology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Nanotechnology (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Inorganic Chemistry (AREA)
  • Mold Materials And Core Materials (AREA)
PCT/US2014/064554 2013-11-26 2014-11-07 Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys Ceased WO2015112232A2 (en)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CA2931206A CA2931206A1 (en) 2013-11-26 2014-11-07 Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
EP14863065.0A EP3074366A2 (en) 2013-11-26 2014-11-07 Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
JP2016555449A JP6329636B2 (ja) 2013-11-26 2014-11-07 炭化ケイ素含有鋳型とフェースコート組成物、並びにチタン及びチタンアルミナイド合金の鋳造方法
CN201480074142.0A CN105960296B (zh) 2013-11-26 2014-11-07 含有碳化硅的铸模和表面涂层组合物及铸造钛和铝化钛合金的方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US14/090,773 2013-11-26
US14/090,773 US9192983B2 (en) 2013-11-26 2013-11-26 Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys

Publications (2)

Publication Number Publication Date
WO2015112232A2 true WO2015112232A2 (en) 2015-07-30
WO2015112232A3 WO2015112232A3 (en) 2015-10-08

Family

ID=53177866

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/064554 Ceased WO2015112232A2 (en) 2013-11-26 2014-11-07 Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys

Country Status (6)

Country Link
US (1) US9192983B2 (enExample)
EP (1) EP3074366A2 (enExample)
JP (1) JP6329636B2 (enExample)
CN (1) CN105960296B (enExample)
CA (1) CA2931206A1 (enExample)
WO (1) WO2015112232A2 (enExample)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2952597A1 (en) * 2014-06-04 2015-12-09 General Electric Company Casting mold with grading of silicon carbide

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9592548B2 (en) * 2013-01-29 2017-03-14 General Electric Company Calcium hexaluminate-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
CN106488911A (zh) 2014-05-13 2017-03-08 巴斯夫欧洲公司 作为杀真菌剂的取代的[1,2,4]三唑和咪唑化合物
CN110769951A (zh) 2017-01-11 2020-02-07 Ha国际有限责任公司 用于高压模铸中的铸造型芯的组合物和方法
KR102341178B1 (ko) * 2019-12-13 2021-12-21 천지산업주식회사 수평형 원심 주조를 이용한 TiAl 합금계 기계부품 제조방법

Family Cites Families (188)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB569852A (en) 1943-03-24 1945-06-12 Ernest George Whitehead Improvements in melting pots
GB783411A (en) 1952-05-23 1957-09-25 Birmingham Small Arms Co Ltd Improvements in or relating to containers for molten metal
US2781261A (en) 1953-10-30 1957-02-12 Nat Distillers Prod Corp Process for the manufacture of titanium-aluminum alloys and regeneration of intermediates
US2837426A (en) 1955-01-31 1958-06-03 Nat Distillers Chem Corp Cyclic process for the manufacture of titanium-aluminum alloys and regeneration of intermediates thereof
US3084060A (en) 1960-04-25 1963-04-02 Nat Res Corp Process of coating a refractory body with boron nitride and then reacting with aluminum
US3180632A (en) 1961-10-02 1965-04-27 North American Aviation Inc Coated crucible and crucible and mold coating method
US3188231A (en) 1963-07-09 1965-06-08 Zbigniew D Jastrzebski Process of making crucibles
US3286312A (en) 1965-03-29 1966-11-22 Little Inc A Refractory coated casting mold
US3676161A (en) 1969-03-03 1972-07-11 Du Pont Refractories bonded with aluminides,nickelides,or titanides
US3565643A (en) 1969-03-03 1971-02-23 Du Pont Alumina - metalline compositions bonded with aluminide and titanide intermetallics
US3660075A (en) 1969-10-16 1972-05-02 Atomic Energy Commission CRUCIBLE COATING FOR PREPARATION OF U AND P ALLOYS CONTAINING Zr OR Hf
NO140023C (no) 1971-03-16 1979-06-20 Alsacienne Atom Anordning for konduksjonspumpe for flytende metaller
US4148204A (en) 1971-05-07 1979-04-10 Siemens Aktiengesellschaft Process of mechanically shaping metal articles
US3969195A (en) 1971-05-07 1976-07-13 Siemens Aktiengesellschaft Methods of coating and surface finishing articles made of metals and their alloys
US3734480A (en) 1972-02-08 1973-05-22 Us Navy Lamellar crucible for induction melting titanium
LU67355A1 (enExample) 1973-04-04 1974-11-21
GB1464157A (en) * 1974-04-23 1977-02-09 Foseco Int Ingot mould bottom plates
US4040845A (en) 1976-03-04 1977-08-09 The Garrett Corporation Ceramic composition and crucibles and molds formed therefrom
US4028096A (en) 1976-05-13 1977-06-07 The United States Of America As Represented By The United States Energy Research And Development Administration Method of melting metals to reduce contamination from crucibles
JPS54157780U (enExample) 1978-04-26 1979-11-02
US4356152A (en) 1981-03-13 1982-10-26 Rca Corporation Silicon melting crucible
EP0096985A1 (en) 1982-06-28 1983-12-28 Trw Inc. Crucible liner and method of making and using the same
JPS6141740A (ja) 1984-08-02 1986-02-28 Natl Res Inst For Metals 金属間化合物ＴｉＡｌ基耐熱合金
US4738389A (en) 1984-10-19 1988-04-19 Martin Marietta Corporation Welding using metal-ceramic composites
US4836982A (en) 1984-10-19 1989-06-06 Martin Marietta Corporation Rapid solidification of metal-second phase composites
US4751048A (en) 1984-10-19 1988-06-14 Martin Marietta Corporation Process for forming metal-second phase composites and product thereof
JPS61129568A (ja) 1984-11-28 1986-06-17 Horiba Ltd るつぼ空焼き装置
AU5773586A (en) 1985-04-26 1986-11-18 Martin Marietta Corp. Aluminum-ceramic composites
EP0204674B1 (en) 1985-06-06 1991-12-27 Remet Corporation Casting of reactive metals into ceramic molds
US4793971A (en) 1985-12-24 1988-12-27 Aluminum Company Of America Grain refining
US4808372A (en) 1986-01-23 1989-02-28 Drexel University In situ process for producing a composite containing refractory material
US4723764A (en) 1986-02-28 1988-02-09 Gte Products Corporation Crucible for melting reactive metal alloys
US4703806A (en) 1986-07-11 1987-11-03 Howmet Turbine Components Corporation Ceramic shell mold facecoat and core coating systems for investment casting of reactive metals
US5535811A (en) 1987-01-28 1996-07-16 Remet Corporation Ceramic shell compositions for casting of reactive metals
US4746374A (en) 1987-02-12 1988-05-24 The United States Of America As Represented By The Secretary Of The Air Force Method of producing titanium aluminide metal matrix composite articles
US4802436A (en) 1987-07-21 1989-02-07 Williams Gold Refining Company Continuous casting furnace and die system of modular design
US4892693A (en) 1987-07-24 1990-01-09 Aluminum Company Of America Method of making filament growth composite
JPH01139988A (ja) 1987-11-26 1989-06-01 Toshiba Corp 金属溶解用るつぼ
JPH01184392A (ja) 1988-01-18 1989-07-24 Hitachi Ltd 金属溶融用るつぼ
US4996175A (en) 1988-01-25 1991-02-26 Precision Castparts Corp. Refractory composition and method for metal casting
EP0413747A1 (en) 1988-05-05 1991-02-27 Martin Marietta Corporation Arc-melting process for forming metallic-second phase composites and product thereof
US4966225A (en) 1988-06-13 1990-10-30 Howmet Corporation Ceramic shell mold for investment casting and method of making the same
JPH069290Y2 (ja) 1989-02-16 1994-03-09 富士写真光機株式会社 カメラ支持具の不慮の移動防止装置
US4951929A (en) 1989-04-06 1990-08-28 Didier-Taylor Refractories Corporation Refractory assembly including inner and outer refractory members with interference shrink fit therebetween and method of formation thereof
US4919886A (en) 1989-04-10 1990-04-24 The United States Of America As Represented By The Secretary Of The Air Force Titanium alloys of the Ti3 Al type
US5427173A (en) 1989-05-01 1995-06-27 Alliedsignal Inc. Induction skull melt spinning of reactive metal alloys
EP0471798B1 (en) 1989-05-01 1993-06-23 AlliedSignal Inc. Induction skull melt spinning of reactive metal alloys
US4893743A (en) 1989-05-09 1990-01-16 The United States Of America As Represented By The Secretary Of The Air Force Method to produce superplastically formed titanium aluminide components
US5602197A (en) 1989-05-30 1997-02-11 Corning Incorporated Reversible polymer gel binders for powder forming
US5429778A (en) 1989-07-07 1995-07-04 Alliedsignal Inc. Process for preparation of metal carbide fibers
US5011554A (en) 1989-12-26 1991-04-30 General Electric Company Ruthenium aluminum intermetallic compounds
JPH03282187A (ja) 1990-03-30 1991-12-12 Mitsubishi Materials Corp ルツボとその製造方法
US5098653A (en) 1990-07-02 1992-03-24 General Electric Company Tantalum and chromium containing titanium aluminide rendered castable by boron inoculation
EP0464366B1 (de) 1990-07-04 1994-11-30 Asea Brown Boveri Ag Verfahren zur Herstellung eines Werkstücks aus einer dotierstoffhaltigen Legierung auf der Basis Titanaluminid
EP0620287B1 (en) 1990-07-31 1999-11-17 Ishikawajima-Harima Heavy Industries Co., Ltd. Titanium aluminides and precision cast articles made therefrom
RU2020042C1 (ru) 1990-09-19 1994-09-30 Акционерное общество открытого типа "Всероссийский алюминиево-магниевый институт" Способ получения отливок из композиционного материала на металлической основе
FR2666819B1 (fr) 1990-09-19 1994-09-23 Inst Aluminievoi Magnievoi Procede et dispositif pour fabriquer un materiau composite a partir d'un metal de base.
US5284620A (en) 1990-12-11 1994-02-08 Howmet Corporation Investment casting a titanium aluminide article having net or near-net shape
JPH0543958A (ja) 1991-01-17 1993-02-23 Sumitomo Light Metal Ind Ltd 耐酸化性チタニウムアルミナイドの製造方法
US5098484A (en) 1991-01-30 1992-03-24 The United States Of America As Represented By The Secretary Of The Air Force Method for producing very fine microstructures in titanium aluminide alloy powder compacts
US5152853A (en) 1991-02-25 1992-10-06 General Electric Company Ruthenium aluminum intermetallic compounds with scandium and boron
US5678298A (en) 1991-03-21 1997-10-21 Howmet Corporation Method of making composite castings using reinforcement insert cladding
CA2057373A1 (en) 1991-05-06 1992-11-07 Donald E. Larsen, Jr. Tia1 intermetallic articles and method of making same
US5354351A (en) 1991-06-18 1994-10-11 Howmet Corporation Cr-bearing gamma titanium aluminides and method of making same
US5102450A (en) 1991-08-01 1992-04-07 General Electric Company Method for melting titanium aluminide alloys in ceramic crucible
EP0529594A1 (en) 1991-08-29 1993-03-03 Ucar Carbon Technology Corporation A glassy carbon coated graphite component for use in the production of silicon crystal growth
EP0530968A1 (en) 1991-08-29 1993-03-10 General Electric Company Method for directional solidification casting of a titanium aluminide
US5263530A (en) 1991-09-11 1993-11-23 Howmet Corporation Method of making a composite casting
US5205984A (en) 1991-10-21 1993-04-27 General Electric Company Orthorhombic titanium niobium aluminide with vanadium
JP3379111B2 (ja) 1992-02-19 2003-02-17 石川島播磨重工業株式会社 精密鋳造用チタンアルミナイド
US5503798A (en) 1992-05-08 1996-04-02 Abb Patent Gmbh High-temperature creep-resistant material
US5297615A (en) 1992-07-17 1994-03-29 Howmet Corporation Complaint investment casting mold and method
JPH06179930A (ja) 1992-08-25 1994-06-28 Tatsuta Electric Wire & Cable Co Ltd 黒鉛製るつぼ又は鋳型
US5287910A (en) 1992-09-11 1994-02-22 Howmet Corporation Permanent mold casting of reactive melt
US5299619A (en) 1992-12-30 1994-04-05 Hitchiner Manufacturing Co., Inc. Method and apparatus for making intermetallic castings
US5981083A (en) 1993-01-08 1999-11-09 Howmet Corporation Method of making composite castings using reinforcement insert cladding
US5603759A (en) 1993-02-11 1997-02-18 Indresco Inc. Stable, cement-bonded, overhead sprayed insulating mixes and resultant linings
US5366570A (en) 1993-03-02 1994-11-22 Cermics Venture International Titanium matrix composites
US5443892A (en) 1993-03-19 1995-08-22 Martin Marietta Energy Systems, Inc. Coated graphite articles useful in metallurgical processes and method for making same
JP3146731B2 (ja) 1993-03-19 2001-03-19 石川島播磨重工業株式会社 チタンアルミナイドの加工方法
US5368657A (en) 1993-04-13 1994-11-29 Iowa State University Research Foundation, Inc. Gas atomization synthesis of refractory or intermetallic compounds and supersaturated solid solutions
DE9307468U1 (de) * 1993-05-17 1994-09-29 Hüttenes-Albertus Chemische Werke GmbH, 40549 Düsseldorf Schlichte zur Herstellung von Formüberzügen
US5346184A (en) 1993-05-18 1994-09-13 The Regents Of The University Of Michigan Method and apparatus for rapidly solidified ingot production
US5407001A (en) 1993-07-08 1995-04-18 Precision Castparts Corporation Yttria-zirconia slurries and mold facecoats for casting reactive metals
US5350466A (en) 1993-07-19 1994-09-27 Howmet Corporation Creep resistant titanium aluminide alloy
KR970008033B1 (ko) * 1993-08-31 1997-05-20 가부시끼가이샤 히다찌세이사꾸쇼 금형주조용 주형과 그의 제조방법 및 그것을 사용한 주조방법
US5424027A (en) 1993-12-06 1995-06-13 The United States Of America As Represented By The Secretary Of The Air Force Method to produce hot-worked gamma titanium aluminide articles
EP0751228B1 (en) 1994-03-10 1999-10-27 Nippon Steel Corporation Titanium-aluminium intermetallic compound alloy material having superior high temperature characteristics and method for producing the same
JPH07314078A (ja) * 1994-05-24 1995-12-05 Tokuyama Corp 鋳型材
EP0686443B1 (de) 1994-06-09 1999-11-10 ALD Vacuum Technologies GmbH Verfahren zum Herstellen von Gussteilen aus reaktiven Metallen und wiederverwendbare Giessform zur Durchführung des Verfahrens
US5453243A (en) 1994-08-17 1995-09-26 The United States Of America As Represented By The Secretary Of The Interior Method for producing titanium aluminide weld rod
GB2297285A (en) 1995-01-25 1996-07-31 T & N Technology Ltd Investment casting mould
US5749937A (en) 1995-03-14 1998-05-12 Lockheed Idaho Technologies Company Fast quench reactor and method
WO1996030552A1 (en) 1995-03-28 1996-10-03 Alliedsignal Inc. Castable gamma titanium-aluminide alloy containing niobium, chromium and silicon
JPH08281371A (ja) * 1995-04-12 1996-10-29 Tokuyama Corp 鋳型材
CN1060683C (zh) 1995-06-09 2001-01-17 华南理工大学 板式旋膜气液传质反应装置
US5766329A (en) 1996-05-13 1998-06-16 Alliedsignal Inc. Inert calcia facecoats for investment casting of titanium and titanium-aluminide alloys
KR100273054B1 (ko) 1996-06-27 2000-12-01 곤도 데루히사 단결정 인상용 도가니 및 그 제조방법
US5908516A (en) 1996-08-28 1999-06-01 Nguyen-Dinh; Xuan Titanium Aluminide alloys containing Boron, Chromium, Silicon and Tungsten
DE19639514C1 (de) 1996-09-26 1997-12-18 Ald Vacuum Techn Gmbh Verfahren und Vorrichtung zum Herstellen von gesteuert erstarrten Präzisionsgußteilen durch Schleudergießen
US5776617A (en) 1996-10-21 1998-07-07 The United States Of America Government As Represented By The Administrator Of The National Aeronautics And Space Administration Oxidation-resistant Ti-Al-Fe alloy diffusion barrier coatings
US5823243A (en) 1996-12-31 1998-10-20 General Electric Company Low-porosity gamma titanium aluminide cast articles and their preparation
JPH10204555A (ja) 1997-01-17 1998-08-04 Toyota Motor Corp アルミニウム鋳造合金の結晶粒微細化剤の製造方法
CN1101284C (zh) 1997-01-27 2003-02-12 联合讯号公司 低成本铸造γ－TiAI用的整体式坩埚和铸型
DE19735841A1 (de) 1997-08-19 1999-02-25 Geesthacht Gkss Forschung Legierung auf der Basis von Titanaluminiden
JPH11116399A (ja) 1997-10-16 1999-04-27 Denso Corp 炭化タンタルのコーティング方法及びこの方法を用いて製造した単結晶製造装置
WO1999027146A1 (en) 1997-11-20 1999-06-03 Tübitak-Marmara Research Center In situ process for producing an aluminium alloy containing titanium carbide particles
US5997802A (en) 1997-11-28 1999-12-07 The United States Of America As Represented By The United States Department Of Energy Directly susceptible, noncarbon metal ceramic composite crucible
DE19752777C2 (de) 1997-11-28 1999-12-09 Daimler Chrysler Ag Verfahren zur Herstellung eines Al¶2¶O¶3¶/Titanaluminid-Verbundkörpers sowie Verwendung des Verfahrens zur Herstellung von tribologisch beanspruchten Systemkomponenten
US6030472A (en) 1997-12-04 2000-02-29 Philip Morris Incorporated Method of manufacturing aluminide sheet by thermomechanical processing of aluminide powders
AT406673B (de) 1998-03-04 2000-07-25 Treibacher Auermet Prod Gmbh Verwendung von metalloxiden zur bereitung keramischer formmassen
JPH11269584A (ja) 1998-03-25 1999-10-05 Ishikawajima Harima Heavy Ind Co Ltd 精密鋳造用チタンアルミナイド
FR2779716B1 (fr) 1998-06-15 2000-08-18 Vesuvius France Sa Materiau refractaire isolant, procede de preparation et pieces a base de ce materiau
US6352101B1 (en) 1998-07-21 2002-03-05 General Electric Company Reinforced ceramic shell mold and related processes
EP1109640B1 (de) 1998-08-18 2002-05-22 Mannesmannröhren-Werke AG Metallurgisches gefäss
US6174387B1 (en) 1998-09-14 2001-01-16 Alliedsignal, Inc. Creep resistant gamma titanium aluminide alloy
DE19846781C2 (de) 1998-10-10 2000-07-20 Ald Vacuum Techn Ag Verfahren und Vorrichtung zum Herstellen von Präzisionsgußteilen durch Schleudergießen
WO2000044959A1 (en) 1999-01-28 2000-08-03 British Nuclear Fuels Plc Coated graphite crucible
US6283195B1 (en) 1999-02-02 2001-09-04 Metal Casting Technology, Incorporated Passivated titanium aluminide tooling
US6723279B1 (en) 1999-03-15 2004-04-20 Materials And Electrochemical Research (Mer) Corporation Golf club and other structures, and novel methods for making such structures
AUPP939099A0 (en) * 1999-03-23 1999-04-15 Cast Centre Pty Ltd Die coatings for gravity and low pressure diecasting
EP1186216A1 (en) 1999-04-30 2002-03-13 Pacific Aerospace and Electronics, Inc. Composite electronics packages and methods of manufacture
US6284389B1 (en) 1999-04-30 2001-09-04 Pacific Aerospace & Electronics, Inc. Composite materials and methods for manufacturing composite materials
US6355362B1 (en) 1999-04-30 2002-03-12 Pacific Aerospace & Electronics, Inc. Electronics packages having a composite structure and methods for manufacturing such electronics packages
JP3915324B2 (ja) 1999-06-08 2007-05-16 石川島播磨重工業株式会社 チタンアルミナイド合金材料及びその鋳造品
US6425504B1 (en) 1999-06-29 2002-07-30 Iowa State University Research Foundation, Inc. One-piece, composite crucible with integral withdrawal/discharge section
GB9915394D0 (en) 1999-07-02 1999-09-01 Rolls Royce Plc A method of adding boron to a heavy metal containung titanium aluminide alloy and a heavy containing titanium aluminide alloy
US6746508B1 (en) 1999-10-22 2004-06-08 Chrysalis Technologies Incorporated Nanosized intermetallic powders
JP2001208481A (ja) 2000-01-25 2001-08-03 Akechi Ceramics Co Ltd 黒鉛坩堝
JP4287991B2 (ja) 2000-02-23 2009-07-01 三菱重工業株式会社 ＴｉＡｌ基合金及びその製造方法並びにそれを用いた動翼
DE10024343A1 (de) 2000-05-17 2001-11-22 Gfe Met & Mat Gmbh Bauteil auf Basis von gamma-TiAl-Legierungen mit Bereichen mit gradiertem Gefüge
US20020108679A1 (en) 2000-12-19 2002-08-15 Chandley George D. Titanium aluminide material resistant to molten aluminum
ATE340665T1 (de) 2001-05-15 2006-10-15 Santoku Corp Giessen von legierungen mit isotropen graphitformwerkzeugen
AU2002311959A1 (en) 2001-05-23 2002-12-03 Santoku America, Inc. Castings of metallic alloys fabricated in anisotropic pyrolytic graphite molds under vacuum
US6755239B2 (en) 2001-06-11 2004-06-29 Santoku America, Inc. Centrifugal casting of titanium alloys with improved surface quality, structural integrity and mechanical properties in isotropic graphite molds under vacuum
JP2003073794A (ja) 2001-06-18 2003-03-12 Shin Etsu Chem Co Ltd 耐熱性被覆部材
DE10125129B4 (de) 2001-06-26 2006-01-26 Ald Vacuum Technologies Ag Permanentkokille für im Schleuderguß hergestellte Ventile für Hubkolbenmotore
JP2003056988A (ja) 2001-08-07 2003-02-26 Daihatsu Motor Co Ltd 金属溶融用るつぼ
US6596963B2 (en) 2001-08-31 2003-07-22 General Electric Company Production and use of welding filler metal
DE10209346B4 (de) 2002-03-02 2004-02-19 Daimlerchrysler Ag Herstellungsverfahren für ein mehrteiliges Ventil für Verbrennungsmotoren
JP2004017078A (ja) * 2002-06-14 2004-01-22 Fujitsu Ltd 金属成形体製造方法およびこれに用いられる金型
US20050084407A1 (en) 2003-08-07 2005-04-21 Myrick James J. Titanium group powder metallurgy
US7500511B2 (en) * 2003-09-24 2009-03-10 Magneco/Metrel, Inc. Molding composition and method of use
DE10346953A1 (de) 2003-10-09 2005-05-04 Mtu Aero Engines Gmbh Werkzeug zum Herstellen von Gussbauteilen, Verfahren zum Herstellen des Werkzeugs und Verfahren zum Herstellen von Gussbauteilen
DE102004002956A1 (de) 2004-01-21 2005-08-11 Mtu Aero Engines Gmbh Verfahren zum Herstellen von Gussbauteilen
DE102004035892A1 (de) 2004-07-23 2006-02-16 Mtu Aero Engines Gmbh Verfahren zum Herstellen eines Gussbauteils
US7448433B2 (en) 2004-09-24 2008-11-11 Honeywell International Inc. Rapid prototype casting
DE102005015862A1 (de) 2005-04-07 2006-10-12 Ald Vacuum Technologies Gmbh Verfahren zum Herstellen einer Vielzahl von insbesondere aus Titanaluminid bestehenden Bauteilen und Vorrichtung zur Durchführung dieses Verfahrens
DE102005042475A1 (de) 2005-09-07 2007-03-08 Ks Aluminium-Technologie Ag Formtrennschicht für das Gießen von Nichteisenmetallen
US20090169415A1 (en) 2005-09-07 2009-07-02 Ihi Corporation Mold and manufacturing method thereof, and molded article using the mold
TWI400369B (zh) 2005-10-06 2013-07-01 Vesuvius Crucible Co 用於矽結晶的坩堝及其製造方法
US7923127B2 (en) 2005-11-09 2011-04-12 United Technologies Corporation Direct rolling of cast gamma titanium aluminide alloys
EP1797977A3 (en) 2005-12-19 2008-08-06 Howmet Corporation Die casting in investment mold
US20070199676A1 (en) 2006-02-27 2007-08-30 Howmet Corporation Composite mold with fugitive metal backup
EP2022294A4 (en) 2006-05-30 2014-04-16 Howmet Corp FUSION PROCESS USING A GRAPHITE FUSION CONTAINER
GB2440334A (en) 2006-06-13 2008-01-30 Rolls Royce Plc A method of controlling the microstructure of a metal
US20080003453A1 (en) 2006-07-03 2008-01-03 John Ogren Brazing process and composition made by the process
US8136572B2 (en) 2006-10-23 2012-03-20 Manfred Renkel Method for production of precision castings by centrifugal casting
WO2008049452A1 (en) 2006-10-23 2008-05-02 Manfred Renkel Apparatus for centrifugal casting
US7582133B2 (en) 2006-12-27 2009-09-01 General Electric Company Methods for reducing carbon contamination when melting highly reactive alloys
US7790101B2 (en) 2006-12-27 2010-09-07 General Electric Company Articles for use with highly reactive alloys
JP2010523337A (ja) 2007-04-11 2010-07-15 マンフレッド レンケル 遠心鋳造による精密鋳造物の製造方法
US8007712B2 (en) 2007-04-30 2011-08-30 General Electric Company Reinforced refractory crucibles for melting titanium alloys
US20100025001A1 (en) 2007-06-25 2010-02-04 Ching-Pang Lee Methods for fabricating gas turbine components using an integrated disposable core and shell die
US20090133850A1 (en) 2007-11-27 2009-05-28 General Electric Company Systems for centrifugally casting highly reactive titanium metals
US20110094705A1 (en) 2007-11-27 2011-04-28 General Electric Company Methods for centrifugally casting highly reactive titanium metals
US7761969B2 (en) 2007-11-30 2010-07-27 General Electric Company Methods for making refractory crucibles
US8062581B2 (en) 2007-11-30 2011-11-22 Bernard Patrick Bewlay Refractory crucibles capable of managing thermal stress and suitable for melting highly reactive alloys
WO2010036425A2 (en) 2008-06-19 2010-04-01 Borgwarner Inc. Rotor shaft of a turbomachine and method for the production of a rotor of a turbomachine
US8033320B2 (en) 2008-07-25 2011-10-11 General Electric Company High emittance shell molds for directional casting
DE102008042375A1 (de) * 2008-09-25 2010-04-15 Manfred Renkel Verfahren zur Herstellung einer Gussform zum Vergießen von Metallschmelzen
DE102008042376A1 (de) * 2008-09-25 2010-04-08 G4T Gmbh Verfahren zur Herstellung einer Gussform zum Vergießen hochreaktiver Schmelzen
DE102008060520A1 (de) 2008-12-04 2010-06-10 Schott Ag Ein Tiegel zur Prozessierung hochschmelzender Materialien
CN101829770A (zh) 2009-03-13 2010-09-15 通用电气公司 用于离心铸造高活性钛金属的系统
DE102009061055B4 (de) 2009-05-13 2020-09-17 Manfred Renkel Intermetallische Titanaluminid-Legierung
DE102009032668A1 (de) * 2009-07-09 2011-01-13 Hüttenes-Albertus Chemische Werke GmbH Schlichte zur Herstellung von Formüberzügen
DE202009013126U1 (de) 2009-09-29 2009-12-10 Egon Evertz Kg (Gmbh & Co.) Kokille zum Stranggießen
GB0918457D0 (en) 2009-10-21 2009-12-09 Doncasters Ltd Casting long products
US8590595B2 (en) * 2011-03-30 2013-11-26 General Electric Company Casting methods and apparatus
US8579013B2 (en) * 2011-09-30 2013-11-12 General Electric Company Casting mold composition with improved detectability for inclusions and method of casting
US20130084190A1 (en) 2011-09-30 2013-04-04 General Electric Company Titanium aluminide articles with improved surface finish and methods for their manufacture
US8858697B2 (en) 2011-10-28 2014-10-14 General Electric Company Mold compositions
US9011205B2 (en) 2012-02-15 2015-04-21 General Electric Company Titanium aluminide article with improved surface finish
US8932518B2 (en) * 2012-02-29 2015-01-13 General Electric Company Mold and facecoat compositions
US20130248061A1 (en) 2012-03-23 2013-09-26 General Electric Company Methods for processing titanium aluminide intermetallic compositions
US10597756B2 (en) 2012-03-24 2020-03-24 General Electric Company Titanium aluminide intermetallic compositions
US8708033B2 (en) 2012-08-29 2014-04-29 General Electric Company Calcium titanate containing mold compositions and methods for casting titanium and titanium aluminide alloys
US9592548B2 (en) 2013-01-29 2017-03-14 General Electric Company Calcium hexaluminate-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
None
See also references of EP3074366A2

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2952597A1 (en) * 2014-06-04 2015-12-09 General Electric Company Casting mold with grading of silicon carbide
US10391547B2 (en) 2014-06-04 2019-08-27 General Electric Company Casting mold of grading with silicon carbide

Also Published As

Publication number Publication date
US20150144286A1 (en) 2015-05-28
JP6329636B2 (ja) 2018-05-23
US9192983B2 (en) 2015-11-24
CN105960296A (zh) 2016-09-21
EP3074366A2 (en) 2016-10-05
WO2015112232A3 (en) 2015-10-08
CA2931206A1 (en) 2015-07-30
JP2017500210A (ja) 2017-01-05
CN105960296B (zh) 2019-02-26

Similar Documents

Publication Publication Date Title
US10695824B2 (en) Mold compositions and methods for casting titanium and titanium aluminide alloys
US9095893B2 (en) Methods for casting titanium and titanium aluminide alloys
CA3027396C (en) Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
US8708033B2 (en) Calcium titanate containing mold compositions and methods for casting titanium and titanium aluminide alloys
EP2950943B1 (en) Calcium hexaluminate-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
US10391547B2 (en) Casting mold of grading with silicon carbide
US9192983B2 (en) Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14863065

Country of ref document: EP

Kind code of ref document: A2

ENP Entry into the national phase

Ref document number: 2931206

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2016555449

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112016011877

Country of ref document: BR

REEP Request for entry into the european phase

Ref document number: 2014863065

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2014863065

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 112016011877

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20160525