WO2013047210A1 - 粘着剤、粘着剤層、および粘着シート - Google Patents

粘着剤、粘着剤層、および粘着シート Download PDF

Info

Publication number
WO2013047210A1
WO2013047210A1 PCT/JP2012/073354 JP2012073354W WO2013047210A1 WO 2013047210 A1 WO2013047210 A1 WO 2013047210A1 JP 2012073354 W JP2012073354 W JP 2012073354W WO 2013047210 A1 WO2013047210 A1 WO 2013047210A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
meth
acrylate
weight
Prior art date
Application number
PCT/JP2012/073354
Other languages
English (en)
French (fr)
Inventor
昌嗣 東
清恵 重富
浩司 設樂
亜樹子 田中
神谷　克彦
梓 伊関
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to EP12837537.5A priority Critical patent/EP2762544A1/en
Priority to US14/348,170 priority patent/US9657197B2/en
Priority to CN201280040087.4A priority patent/CN103764781A/zh
Priority to KR1020147000463A priority patent/KR101543975B1/ko
Publication of WO2013047210A1 publication Critical patent/WO2013047210A1/ja
Priority to US15/266,653 priority patent/US20170002235A1/en

Abstract

　本発明の粘着剤は、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートを３０～９９．５重量％および環状窒素含有モノマーを０．５～５０重量％を含むモノマー成分を重合することにより得られた（メタ）アクリル系ポリマーを含む。当該粘着剤は、接着性能を満足し、かつ低誘電率で、耐加湿信頼性を有する粘着剤層を実現することができる。

Description

粘着剤、粘着剤層、および粘着シート
　本発明は、低誘電率を実現することができる粘着剤および当該粘着剤から得られる粘着剤層、およびこのような粘着剤層を支持体の少なくとも片面に有する粘着シートに関する。
　本発明の粘着剤層または粘着シートは、光学用途に好適である。例えば、本発明の粘着剤層または粘着シートは、液晶表示装置、有機ＥＬ（エレクトロルミネッセンス）表示装置、ＰＤＰ（プラズマディスプレイパネル）、電子ペーパーなどの画像表示装置の製造用途や、光学方式、超音波方式、静電容量方式、抵抗膜方式などのタッチパネルなどの入力装置の製造用途に好適に用いることができる。特に、静電容量方式のタッチパネルに好適に用いられる。
　また、本発明の粘着シートは、支持体に光学部材を用いた粘着型光学部材として有用である。例えば、光学部材として透明導電性フィルムを用いる場合には、粘着型光学部材は、粘着剤層付き透明導電性フィルムとして用いられる。当該粘着剤層付き透明導電性フィルムは、適宜加工処理がなされた後に、前記画像表示装置やタッチパネルなどにおける透明電極に用いられる。特に、粘着剤層付き透明導電性フィルムは、透明導電性薄膜をパターニングして、静電容量方式のタッチパネルの入力装置の電極基板に好適に用いられる。その他、粘着剤層付き透明導電性フィルムは、透明物品の帯電防止や電磁波遮断、液晶調光ガラス、透明ヒーターに用いられる。
　また光学部材として光学フィルムを用いる場合には、粘着型光学部材は、粘着剤層付き光学フィルムとして用いられる。当該粘着剤層付き光学フィルムは、液晶表示装置、有機ＥＬ表示装置等の画像表示装置に用いられる。前記光学フィルムとしては、偏光板、位相差板、光学補償フィルム、輝度向上フィルム、さらにはこれらが積層されているものを用いることができる。
　近年、携帯電話や携帯用音楽プレイヤー等の画像表示装置とタッチパネルを組み合わせて用いる入力装置が普及してきている。中でも、静電容量方式のタッチパネルはその機能性から急速に普及してきている。
　現在、タッチパネル用に用いる透明導電性フィルムとしては、透明プラスチックフィルム基材やガラスに透明導電性薄膜（ＩＴＯ膜）が積層されたものが多く知られている。透明導電性フィルムは、他の部材に粘着剤層を介して積層される。前記粘着剤層として各種のものが提案されている（特許文献１～５参照）。
　前記透明導電性フィルムが、静電容量方式のタッチパネルの電極基板に用いられる場合には、前記透明導電性薄膜がパターニングされたものが用いられる。このようなパターニングされた透明導電性薄膜を有する透明導電性フィルムは、他の透明導電性フィルム等とともに粘着剤層を介して積層して用いられる。これら透明導電性フィルムは、２本以上の指で同時に操作できるマルチタッチ方式の入力装置に好適に使用される。即ち、静電容量方式のタッチパネルは、指などでタッチパネルに触れた際にその位置の出力信号が変化し、その信号の変化量がある閾値を超えた場合にセンシングする仕組みになっている。
特開２００３－２３８９１５号公報 特開２００３－３４２５４２号公報 特開２００４－２３１７２３号公報 特開２００２－３６３５３０号公報 国際公開ＷＯ２０１０／１４７０４７ パンフレット
　上記のように、タッチパネルを構成する部材、フィルムの誘電率は、タッチパネルの応答性に関わっており重要な数値である。一方、近年、タッチパネルの普及に伴い、タッチパネルにはより高性能化が求められており、その構成部材である透明導電性フィルムや粘着剤層にも高性能が求められ、薄型化もそのひとつである。しかしながら、粘着剤層を単純に薄型化してしまうと設計した静電容量値が変わってしまうという問題がある。前記静電容量値の数値を変えないで、粘着剤層を薄型化するためには、粘着剤層の低誘電率化が求められる。また、視認性向上のために、印刷付ガラスやフィルムと光学フィルムとの空気層やＬＣＤ上部の空気層を粘着剤層にて層間充填する場合があるが、その一方で、前記粘着剤層の誘電率が高いと誤作動が起きる可能性がある。かかる誤作動防止の観点からも、粘着剤層の低誘電率化が求められる。さらに、粘着剤層の低誘電率化によって、タッチパネルの応答速度や感度の向上が期待される。また、透明導電性フィルムやガラスを、粘着剤層を介して積層した積層物を、加湿条件下に曝露した際には粘着剤層が白濁してしまうという問題がある。
　そこで、本発明は、接着性能を満足し、かつ低誘電率で、耐加湿信頼性を有する粘着剤層を実現することができる粘着剤を提供することを目的とする。
　また本発明は、前記粘着剤により形成された粘着剤層を提供すること、さらには当該粘着剤層を有する粘着剤シートを提供することを目的とする。
　本発明者らは前記課題を解決すべく鋭意検討を重ねた結果、下記粘着剤を見出し、本発明を完成するに至った。
　即ち本発明は、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートを３０～９９．５重量％および環状窒素含有モノマーを０．５～５０重量％を含むモノマー成分を重合することにより得られた（メタ）アクリル系ポリマーを含むことを特徴とする粘着剤、に関する。前記炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートは、アルキル基が分岐を有するアルキル基であるのが好ましい。また前記炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートは、アルキルメタクリレートであることが低誘電率の観点から好ましく、アルキルアクリレートであることが生産性の観点から好ましい。
　上記粘着剤において、モノマー成分は、さらに、カルボキシル基含有モノマー、ヒドロキシル基含有モノマーおよび環状エーテル基を有するモノマーから選ばれるいずれか少なくとも１つの官能基含有モノマーを、０．５重量％以上含むことができる。
　上記粘着剤において、モノマー成分が、さらに、炭素数１～９のアルキル基をエステル末端に有するアルキル（メタ）アクリレートおよび環状のアルキル基をエステル末端に有するアルキル（メタ）アクリレートから選ばれるいずれか少なくとも１種を０．５重量％以上含むことができる。
　上記粘着剤において、モノマー成分が、さらに、多官能性モノマーを３重量％以下含むことができる。
　上記粘着剤において、さらに、前記（メタ）アクリル系ポリマー１００重量部に対して、架橋剤を、０．０１～５重量部含有することが好ましい。
　上記粘着剤は、光学用部材に用いられる、光学部材用の粘着剤として好適である。
　また本発明は、上記のいずれかに記載の粘着剤から得られることを特徴とする粘着剤層、に関する。
　上記粘着剤層は、周波数１００ｋＨｚにおける比誘電率が３．５以下であることが好ましい。
　上記粘着剤層は、ゲル分率が２０～９８重量％であることが好ましい。
　上記粘着剤層は、粘着剤層の厚さが２５μｍの場合のヘイズが、２％以下であることが好ましい。
　上記粘着剤層は、全光線透過率が９０％以上であることが好ましい。
　上記粘着剤層は、光学用部材に用いられる、光学部材用の粘着剤層として好適である。
　また本発明は、支持体の少なくとも片側に、上記のいずれかに記載の粘着剤層が形成されていることを特徴とする粘着シート、に関する。
　上記粘着シートにおいて、粘着剤層の無アルカリガラスに対する９０度ピール接着力（３００ｍｍ／ｍｉｎ）が０．５Ｎ／２０ｍｍ以上であることが好ましい。
　上記粘着シートは、光学用部材に用いられる、光学部材用の粘着シートとして好適である。また、上記粘着シートは、支持体として光学用部材を用いた、粘着型光学部材として用いることができる。
　本発明の粘着剤における主成分である（メタ）アクリル系ポリマーは、長鎖のアルキル基を有するアルキル（メタ）アクリレートおよび環状窒素含有モノマーを所定量含有するモノマー成分を重合することにより得られたものである。かかる本発明の粘着剤によれば、前記長鎖のアルキル基と、窒素原子を有する環状構造の作用により、低誘電率で、耐加湿信頼性に優れた粘着剤層を実現することができ、かつ、接着性能を満足することができる。また、空気層を粘着剤層にて層間充填する場合においても、粘着剤層が低誘電率のため、誤作動を防止することができる。
　誘電率を下げるには、クラジウス－モソッティ（Ｃｌａｕｓｉｕｓ－Ｍｏｓｓｏｔｔｉ）の式より、分子の双極子モーメントを小さくし、モル体積を大きくすれば良いと考えられる。本発明の粘着剤における主成分である（メタ）アクリル系ポリマーを構成する主モノマー単位に係る、アルキル（メタ）アクリレートは長鎖のアルキル基を有し、かつ、共重合のモノマー単位が窒素原子を有する環状構造を有することから、誘電率が下がるものと考えられる。また、窒素原子を有する環状構造における、凝集性と親水性の作用によって耐加湿信頼性を満足することができたものと考えられる。
　例えば、本発明の粘着剤層は、１００ｋＨｚにおける比誘電率が３．５以下の低誘電率を満足することにより、本発明の粘着剤層を薄型化して、静電容量方式のタッチパネルに用いる透明導電性フィルムに適用する粘着剤層に用いた場合においても、静電容量方式のタッチパネルで設計した静電容量値の数値を変えることなく適用することができ、かつ耐加湿信頼性を満足することができる。
本発明の粘着剤層または粘着シートが用いられている静電容量方式のタッチパネルの一例を示す図である。
　本発明の粘着剤は、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートを３０～９９．５重量％および環状窒素含有モノマーを０．５～５０重量％を含むモノマー成分を重合することにより得られた（メタ）アクリル系ポリマーを含む。なお、アルキル（メタ）アクリレートはアルキルアクリレートおよび／またはアルキルメタクリレートをいい、本発明の（メタ）とは同様の意味である。
　前記炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートに係る、ホモポリマーのＴｇは、－８０～０℃であることが好ましく、さらには－７０～－１０℃、さらには－６０～－１０℃であることが好ましい。ホモポリマーのＴｇが、－８０℃未満では、粘着剤の常温での弾性率が下がりすぎる場合があり好ましくなく、０℃を超える場合には接着力が低下する場合があり好ましくない。ホモポリマーのＴｇは、ＴＧ－ＤＴＡにより、測定した値である。また、前記アルキル基は、低誘電率と適度の弾性率を満足できる点から、炭素数１０～１８であるが、（メタ）アクリル系ポリマーの製造方法によって、適宜に好ましいアルキル基を有するアルキル（メタ）アクリレートを選択することができる。例えば、溶液重合等により（メタ）アクリル系ポリマーを製造する場合には、前記アルキル基は、さらには炭素数１０～１６が好ましく、さらには炭素数１０～１４であるのが好ましい。放射線重合等により、（メタ）アクリル系ポリマーを製造する場合には、前記アルキル基は、さらには炭素数１２～１８が好ましく、さらには炭素数１４～１８であるのが好ましい。なお、アルキル（メタ）アクリレートに係る、ホモポリマーのＴｇが－８０～０℃であっても、炭素数が９以下では、粘着剤層を低誘電率化する効果は大きくない。
　前記アルキル（メタ）アクリレートにおける、炭素数１０～１８のアルキル基は、直鎖または分岐鎖のいずれも用いることができるが、粘着剤層を低誘電率化する効果の点からは、分岐鎖のアルキル基の方が、直鎖のアルキル基より好ましい。前記アルキル（メタ）アクリレートの長鎖アルキル基は、アルキル基が分岐を有することでモル体積が増加し、双極子モーメントが下がって、双方のバランスを有する粘着剤層が得られると考えられる。
　前記炭素数１０～１８の分岐を有するアルキル基をエステル末端に有するアルキル（メタ）アクリレートとしては、例えば、イソデシルアクリレート（炭素数１０，ホモポリマーのＴｇ＝－６０℃，以下、単にＴｇと略す）、イソデシルメタクリレート（炭素数１０，Ｔｇ＝－４１℃）、イソミスチリルアクリレート（炭素数１４，Ｔｇ＝－５６℃）、イソステアリルアクリレート（炭素数１８,Ｔｇ＝－１８℃）、２－プロピルヘプチルアクリレート、イソウンデシルアクリレート、イソドデシルアクリレート、イソトリデシルアクリレート、イソペンタデシルアクリレート、イソヘキサデシルアクリレート、イソヘプタデシルアクリレート、および前記例示のメタクリレート系モノマーを例示できる。これらは１種を単独でまたは２種以上を組み合わせて用いることができる。
　また、前記炭素数１０～１８の分岐を有するアルキル基のなかでｔ－ブチル基を有するものは、特に、モル体積が増加し、双極子モーメントが下がって、双方のバランスを有する粘着剤層が得られると考えられる点で好ましい。ｔ－ブチル基を有する、炭素数１０～１８の分岐を有するアルキル基を有するアルキル（メタ）アクリレートとしては、下記式で表わされる、イソステアリルアクリレートが挙げられる。
Figure JPOXMLDOC01-appb-C000001
　また、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートとしては、アルキルメタクリレートの方が、アルキルアクリレートよりも、モル体積の増加と双極子モーメントの低下による、粘着剤層を低誘電率化する効果の点から好ましい。前記アルキルメタクリレートは、前記長鎖アルキル基が直鎖アルキル基の場合においても、モル体積が増加し、双極子モーメントが下がって、双方のバランスを有する粘着剤層が得られると考えられる。一方、アルキルアクリレートの方が、アルキルメタクリレートよりも、環状窒素含有モノマーとの相溶性が良好であり、透明性の良好な（メタ）アクリル系ポリマーが得られる点で好ましく、また（メタ）アクリル系ポリマーを製造する際の重合時間を短縮して生産性を向上できる点で好ましい。特に、（メタ）アクリル系ポリマーの製造を放射線重合により行う場合には、アルキルアクリレートが好適である。
　炭素数１０～１８のアルキル基をエステル末端に有するアルキルメタクリレートとしては、ラウリルメタクリレート（炭素数１２，Ｔｇ＝－６５℃）、トリデシルメタクリレート（炭素数１３，Ｔｇ＝－４０℃）、ステアリルメタクリレート（炭素数１８，Ｔｇ＝３８℃）、イソデシルメタクリレート（炭素数１０，Ｔｇ＝－４１℃）、ウンデシルメタクリレート（炭素数１１）、テトラデシルメタクリレート（炭素数１４）、ペンタデシルメタクリレート（炭素数１５）、ヘキサデシルメタクリレート（炭素数１６）、ヘプタデシルメタクリレート（炭素数１７）などが挙げられる。これらは１種を単独でまたは２種以上を組み合わせて用いることができる。
　以上から、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートとしては、炭素数１０～１８の分岐を有するアルキル基をエステル末端に有するアルキルメタアクリレートが好ましい。
　本発明において、前記炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートは、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、３０～９９．５重量％であり、好ましくは３２～９９．５重量％、さらに好ましくは３５～９９．５重量%であり、さらに好ましくは４０～９９．５重量%であり、さらに好ましくは、４５～９６重量％、さらに好ましくは６５～９５重量％である。３０重量％以上を用いることは低誘電率化の面で好ましく、９９．５重量％以下で用いることは接着力の維持の面で好ましい。
　上記環状窒素含有モノマーとしては、（メタ）アクリロイル基またはビニル基等の不飽和二重結合を有する重合性の官能基を有し、かつ環状窒素構造を有するものを特に制限なく用いることができる。環状窒素構造は、環状構造内に窒素原子を有するものが好ましい。環状窒素含有モノマーとしては、例えば、Ｎ－ビニルピロリドン、Ｎ－ビニル－ε－カプロラクタム、メチルビニルピロリドン等のラクタム系ビニルモノマー；ビニルピリジン、ビニルピペリドン、ビニルピリミジン、ビニルピペラジン、ビニルピラジン、ビニルピロール、ビニルイミダゾール、ビニルオキサゾール、ビニルモルホリン等の窒素含有複素環を有するビニル系モノマー等が挙げられる。また、モルホリン環、ピペリジン環、ピロリジン環、ピペラジン環等の複素環を含有する（メタ）アクリルモノマーが挙げられる。具体的には、Ｎ－アクリロイルモルホリン、Ｎ－アクリロイルピペリジン、Ｎ－メタクリロイルピペリジン、Ｎ－アクリロイルピロリジン等が挙げられる。前記環状窒素含有モノマーのなかでも、ラクタム系ビニルモノマーが誘電率と凝集性の点から好ましい。
　本発明において、環状窒素含有モノマーは、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、０．５～５０重量％であり、好ましくは０．５～４０重量％、さらに好ましくは０．５～３０重量％である。０．５重量％以上であると、低誘電率化および耐加湿信頼性の面で好ましく、５０重量％以下であると、接着力向上の面で好ましい。
　本発明の（メタ）アクリル系ポリマーを形成するモノマー成分には、さらに、カルボキシル基含有モノマー、ヒドロキシル基含有モノマーおよび環状エーテル基を有するモノマーから選ばれるいずれか少なくとも１つの官能基含有モノマーを含むことができる。
　カルボキシル基含有モノマーとしては、（メタ）アクリロイル基またはビニル基等の不飽和二重結合を有する重合性の官能基を有し、かつカルボキシル基を有するものを特に制限なく用いることができる。カルボキシル基含有モノマーとしては、例えば、（メタ）アクリル酸、カルボキシエチル（メタ）アクリレート、カルボキシペンチル（メタ）アクリレート、イタコン酸、マレイン酸、フマール酸、クロトン酸、イソクロトン酸等が挙げられ、これらは単独でまたは組み合わせて使用できる。イタコン酸、マレイン酸はこれらの無水物を用いることができる。これらのなかで、アクリル酸、メタクリル酸が好ましく、特にアクリル酸が好ましい。なお、本発明の（メタ）アクリル系ポリマーの製造に用いるモノマー成分にはカルボキシル基含有モノマーを任意に用いることができ、一方では、カルボキシル基含有モノマーを用いなくともよい。カルボキシル基含有モノマーを含有していないモノマー成分から得られた（メタ）アクリル系ポリマーを含有する粘着剤は、カルボキシル基に起因する金属腐食などを低減した粘着剤層を形成することができる。
　ヒドロキシル基含有モノマーとしては、（メタ）アクリロイル基またはビニル基等の不飽和二重結合を有する重合性の官能基を有し、かつヒドロキシル基を有するものを特に制限なく用いることができる。ヒドロキシル基含有モノマーとしては、例えば、２－ヒドロキシブチル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、６－ヒドロキシヘキシル（メタ）アクリレート、８－ヒドロキシオクチル（メタ）アクリレート、１０－ヒドロキシデシル（メタ）アクリレート、１２－ヒドロキシラウリル（メタ）アクリレート等などのヒドロキシアルキル（メタ）アクリレート；（４－ヒドロキシメチルシクロへキシル）メチル（メタ）アクリレート等のヒドロキシアルキルシクロアルカン（メタ）アクリレートが挙げられる。その他、ヒドロキシエチル（メタ）アクリルアミド、アリルアルコール、２－ヒドロキシエチルビニルエーテル、４－ヒドロキシブチルビニルエーテル、ジエチレングリコールモノビニルエーテルなどが挙げられる。これらは単独でまたは組み合わせて使用できる。これらのなかでもヒドロキシアルキル（メタ）アクリレートが好適である。
　環状エーテル基を有するモノマーとしては、（メタ）アクリロイル基またはビニル基等の不飽和二重結合を有する重合性の官能基を有し、かつエポキシ基またはオキセタン基等の環状エーテル基を有するものを特に制限なく用いることができる。エポキシ基含有モノマーとしては、例えば、グリシジル（メタ）アクリレート、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレートグリシジルエーテル等が挙げられる。オキセタン基含有モノマーとしては、例えば、３－オキセタニルメチル（メタ）アクリレート、３－メチルーオキセタニルメチル（メタ）アクリレート、３－エチルーオキセタニルメチル（メタ）アクリレート、３－ブチルーオキセタニルメチル（メタ）アクリレート、３－ヘキシルーオキセタニルメチル（メタ）アクリレート、等が挙げられる。これらは単独でまたは組み合わせて使用できる。
　本発明において、前記官能基含有モノマーは、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、接着力、凝集力を高める点から０．５重量％以上であるのが好ましく、さらには０．８重量％以上であるが好ましい。一方、前記官能基含有モノマーが多くなりすぎると、粘着剤層が固くなり、接着力が低下する場合があり、また、粘着剤の粘度が高くなりすぎたり、ゲル化したりする場合があることから、前記官能基含有モノマーは、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、３０重量％以下であるのが好ましく、さらには２７重量％以下、さらには２５重量％以下であるが好ましい。
　本発明の（メタ）アクリル系ポリマーを形成するモノマー成分には、前記官能基含有モノマー以外の共重合モノマーを含むことができる。前記以外の共重合モノマーとしては、例えば、ＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２（前記Ｒ１は水素またはメチル基、Ｒ２は炭素数１～９の無置換のアルキル基または置換されたアルキル基を表す。）で表されるアルキル（メタ）アクリレートが挙げられる。
　ここで、Ｒ２としての、炭素数１～９の無置換のアルキル基または置換されたアルキル基は、直鎖、分岐鎖のアルキル基、あるいは環状のシクロアルキル基を示す。Ｒ２は具体的には、炭素数３～９の分岐を有するアルキル基、環状のアルキル基が挙げられる。置換されたアルキル基の場合は、置換基としては、炭素数３－８個のアリール基または炭素数３－８個のアリールオキシ基であることが好ましい。アリール基としては、限定はされないが、フェニル基が好ましい。当該アルキル（メタ）アクリレートとしては、アルキルアクリレートよりも、アルキルメタクリレートの方が、モル体積の増加と双極子モーメントの低下により、低誘電率化の点で好ましい。
　このようなＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２で表されるモノマーの例としては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、ｓ－ブチル（メタ）アクリレート、ｔ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｎ－ペンチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、へキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、イソアミル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ｎ－オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ｎ－ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、ベンジル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、３，３，５－トリメチルシクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレートなどが挙げられる。これらは単独でまたは組み合わせて使用できる。
　本発明において、前記ＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２で表される（メタ）アクリレートは、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、６９．５重量％以下で用いることができ、６５重量％以下が好ましい。さらには５９．５重量％以下が好ましく、さらには５５重量％以下であることが好ましく、さらには５０重量％以下であることが好ましく、さらには４０重量％以下、さらには３０重量％以下であるのが好ましい。なお、前記ＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２で表される（メタ）アクリレートは接着力の維持の面から５重量％以上、さらには１０重量％以上用いることが好ましい。
　前記ＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２で表される（メタ）アクリレートは、前記割合で用いることができるが、（メタ）アクリル系ポリマーの製造方法によって、適宜に好ましい割合を選択することができる。例えば、放射線重合等により、（メタ）アクリル系ポリマーを製造する場合には、前記ＣＨ２＝Ｃ（Ｒ１）ＣＯＯＲ２で表される（メタ）アクリレートの全モノマー成分に対する割合は、粘着特性の観点から、０重量％を超え５５重量％以下であるのが好ましく、さらには２０～５０重量％であるのが好ましい。この場合、炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートの全モノマー成分に対する割合は３０～８０重量％であるのが好ましく、さらには３０～７０重量％であるのが好ましい。
　他の共重合モノマーとしては、酢酸ビニル、プロピオン酸ビニル、スチレン、α－メチルスチレン；（メタ）アクリル酸ポリエチレングリコール、（メタ）アクリル酸ポリプロピレングリコール、（メタ）アクリル酸メトキシエチレングリコール、（メタ）アクリル酸メトキシポリプロピレングリコールなどのグリコール系アクリルエステルモノマー；（メタ）アクリル酸テトラヒドロフルフリル、フッ素（メタ）アクリレート、シリコーン（メタ）アクリレートや２－メトキシエチルアクリレートなどのアクリル酸エステル系モノマー；アミド基含有モノマー、アミノ基含有モノマー、イミド基含有モノマー、Ｎ－アクリロイルモルホリン、ビニルエーテルモノマーなども使用することができる。また、共重合モノマーとしては、テルペン（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート等の環状構造を有するモノマーを用いることができる。
　さらに、ケイ素原子を含有するシラン系モノマーなどが挙げられる。シラン系モノマーとしては、例えば、３－アクリロキシプロピルトリエトキシシラン、ビニルトリメトキシシラン、ビニルトリエトキシシラン、４－ビニルブチルトリメトキシシラン、４－ビニルブチルトリエトキシシラン、８－ビニルオクチルトリメトキシシラン、８－ビニルオクチルトリエトキシシラン、１０－メタクリロイルオキシデシルトリメトキシシラン、１０－アクリロイルオキシデシルトリメトキシシラン、１０－メタクリロイルオキシデシルトリエトキシシラン、１０－アクリロイルオキシデシルトリエトキシシランなどが挙げられる。
　本発明の（メタ）アクリル系ポリマーを形成するモノマー成分には、前記例示の単官能性モノマーの他に、粘着剤の凝集力を調整するために、必要に応じて多官能性モノマーを含有することができる。
　多官能性モノマーは、（メタ）アクリロイル基またはビニル基等の不飽和二重結合を有する重合性の官能基を少なくとも２つ有するモノマーであり、例えば、（ポリ）エチレングリコールジ（メタ）アクリレート、（ポリ）プロピレングリコールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、ペンタエリスリトールジ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、１，２－エチレングリコールジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、１，１２－ドデカンジオールジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、テトラメチロールメタントリ（メタ）アクリレート等の多価アルコールと（メタ）アクリル酸とのエステル化合物；アリル（メタ）アクリレート、ビニル（メタ）アクリレート、ジビニルベンゼン、エポキシアクリレート、ポリエステルアクリレート、ウレタンアクリレート、ブチルジ（メタ）アクリレート、ヘキシルジ（メタ）アクリレート等が挙げられる。中でも、トリメチロールプロパントリ（メタ）アクリレート、ヘキサンジオールジ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレートを好適に使用することができる。多官能性モノマーは、１種を単独でまたは２種以上を組み合わせて使用することができる。
　多官能性モノマーの使用量は、その分子量や官能基数等により異なるが、（メタ）アクリル系ポリマーを形成する全モノマー成分に対して、３重量％以下で用いることができ、２重量％以下が好ましく、さらには１重量％以下が好ましい。多官能性モノマーの使用量が、３重量％を超えると、例えば、粘着剤の凝集力が高くなりすぎ、接着力が低下したりする場合がある。
　このような（メタ）アクリル系ポリマーの製造は、溶液重合、ＵＶ重合等の放射線重合、塊状重合、乳化重合等の各種ラジカル重合などの公知の製造方法を適宜選択できる。また、得られる（メタ）アクリル系ポリマーは、ランダム共重合体、ブロック共重合体、グラフト共重合体などいずれでもよい。
　ラジカル重合に用いられる重合開始剤、連鎖移動剤、乳化剤などは特に限定されず適宜選択して使用することができる。なお、（メタ）アクリル系ポリマーの重量平均分子量は、重合開始剤、連鎖移動剤の使用量、反応条件により制御可能であり、これらの種類に応じて適宜のその使用量が調整される。
　例えば、溶液重合等においては、重合溶媒として、例えば、酢酸エチル、トルエンなどが用いられる。具体的な溶液重合例としては、反応は窒素などの不活性ガス気流下で、重合開始剤を加え、通常、５０～７０℃程度で、５～３０時間程度の反応条件で行われる。
　溶液重合等に用いられる、熱重合開始剤としては、例えば、２，２’－アゾビスイソブチロニトリル、２，２´－アゾビス－２－メチルブチロニトリル、２，２´－アゾビス（２－メチルプロピオン酸）ジメチル、４，４´－アゾビス－４－シアノバレリアン酸、アゾビスイソバレロニトリル、２，２’－アゾビス（２－アミジノプロパン）ジヒドロクロライド、２，２’－アゾビス［２－（５－メチル－２－イミダゾリン－２－イル）プロパン］ジヒドロクロライド、２，２’－アゾビス（２－メチルプロピオンアミジン）二硫酸塩、２，２’－アゾビス（Ｎ，Ｎ’－ジメチレンイソブチルアミジン）、２，２’－アゾビス［Ｎ－（２－カルボキシエチル）－２－メチルプロピオンアミジン］ハイドレート（和光純薬社製、ＶＡ－０５７）などのアゾ系開始剤；過硫酸カリウム、過硫酸アンモニウムなどの過硫酸塩、ジ（２－エチルヘキシル）パーオキシジカーボネート、ジ（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート、ジ－ｓｅｃ－ブチルパーオキシジカーボネート、ｔ－ブチルパーオキシネオデカノエート、ｔ－ヘキシルパーオキシピバレート、ｔ－ブチルパーオキシピバレート、ジラウロイルパーオキシド、ジ－ｎ－オクタノイルパーオキシド、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート、ジ（４－メチルベンゾイル）パーオキシド、ジベンゾイルパーオキシド、ｔ－ブチルパーオキシイソブチレート、１，１－ジ（ｔ－ヘキシルパーオキシ）シクロヘキサン、ｔ－ブチルハイドロパーオキシド、過酸化水素などの過酸化物系開始剤、過硫酸塩と亜硫酸水素ナトリウムの組み合わせ、過酸化物とアスコルビン酸ナトリウムの組み合わせなどの過酸化物と還元剤とを組み合わせたレドックス系開始剤などを挙げることができるが、これらに限定されるものではない。
　前記重合開始剤は、単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量はモノマー１００重量部に対して、０．００５～１重量部程度であることが好ましく、０．０２～０．５重量部程度であることがより好ましい。
　なお、重合開始剤として、例えば、２，２’－アゾビスイソブチロニトリルを用いて、前記重量平均分子量の（メタ）アクリル系ポリマーを製造するには、重合開始剤の使用量は、モノマー成分の全量１００重量部に対して、０．０６～０．２重量部程度とするのが好ましく、さらには０．０８～０．１７５重量部程度とするのが好ましい。
　連鎖移動剤としては、例えば、ラウリルメルカプタン、グリシジルメルカプタン、メルカプト酢酸、２－メルカプトエタノール、チオグリコール酸、チオグルコール酸２－エチルヘキシル、２，３－ジメルカプト－１－プロパノールなどが挙げられる。連鎖移動剤は、単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量はモノマー成分の全量１００重量部に対して、０．１重量部程度以下である。
　また、乳化重合する場合に用いる乳化剤としては、例えば、ラウリル硫酸ナトリウム、ラウリル硫酸アンモニウム、ドデシルベンゼンスルホン酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸アンモニウム、ポリオキシエチレンアルキルフェニルエーテル硫酸ナトリウムなどのアニオン系乳化剤、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ポリオキシエチレン－ポリオキシプロピレンブロックポリマーなどのノニオン系乳化剤などが挙げられる。これらの乳化剤は、単独で用いてもよく２種以上を併用してもよい。
　さらに、反応性乳化剤として、プロペニル基、アリルエーテル基などのラジカル重合性官能基が導入された乳化剤として、具体的には、例えば、アクアロンＨＳ－１０、ＨＳ－２０、ＫＨ－１０、ＢＣ－０５、ＢＣ－１０、ＢＣ－２０（以上、いずれも第一工業製薬社製）、アデカリアソープＳＥ１０Ｎ（ADEKA社製）などがある。反応性乳化剤は、重合後にポリマー鎖に取り込まれるため、耐水性がよくなり好ましい。乳化剤の使用量は、モノマー成分の全量１００重量部に対して、０．３～５重量部、重合安定性や機械的安定性から０．５～１重量部がより好ましい。
　また、（メタ）アクリル系ポリマーは、放射線重合により製造する場合には、前記モノマー成分を、電子線、ＵＶ等の放射線を照射することにより重合して製造することができる。前記放射線重合を電子線で行う場合には、前記モノマー成分には光重合開始剤を含有させることは特に必要ではないが、前記放射線重合をＵＶ重合で行う場合には、特に、重合時間を短くすることができる利点等から、モノマー成分に光重合開始剤を含有させることができる。光重合開始剤は１種を単独でまたは２種以上を組み合わせて使用することができる。
　光重合開始剤としては、特に制限されないが、光重合を開始するものであれば特に制限されず、通常用いられる光重合開始剤を用いることができる。例えば、ベンゾインエーテル系光重合開始剤、アセトフェノン系光重合開始剤、α－ケトール系光重合開始剤、芳香族スルホニルクロリド系光重合開始剤、光活性オキシム系光重合開始剤、ベンゾイン系光重合開始剤、ベンジル系光重合開始剤、ベンゾフェノン系光重合開始剤、ケタール系光重合開始剤、チオキサントン系光重合開始剤、アシルフォスフィンオキサイド系光重合開始剤等を用いることができる。
　具体的には、ベンゾインエーテル系光重合開始剤としては、例えば、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソプロピルエーテル、ベンゾインイソブチルエーテル、２，２－ジメトキシ－１，２－ジフェニルエタン－１－オン［商品名：イルガキュア６５１、ＢＡＳＦ社製］、アニソールメチルエーテル等が挙げられる。アセトフェノン系光重合開始剤としては、例えば、１－ヒドロキシシクロヘキシルフェニルケトン［商品名：イルガキュア１８４、ＢＡＳＦ社製］、４－フェノキシジクロロアセトフェノン、４－ｔ－ブチル－ジクロロアセトフェノン、１－［４－(２－ヒドロキシエトキシ)－フェニル］－２－ヒドロキシ－２－メチル－１－プロパン－１－オン［商品名：イルガキュア２９５９、ＢＡＳＦ社製］、２－ヒドロキシ－２－メチル－１－フェニル－プロパン－１－オン［商品名：ダロキュア１１７３、ＢＡＳＦ社製］、メトキシアセトフェノン等が挙げられる。α－ケトール系光重合開始剤としては、例えば、２－メチル－２－ヒドロキシプロピオフェノン、１－［４－（２－ヒドロキシエチル）－フェニル］－２－ヒドロキシ－２－メチルプロパン－１－オン等が挙げられる。芳香族スルホニルクロリド系光重合開始剤としては、例えば、２－ナフタレンスルホニルクロライド等が挙げられる。光活性オキシム系光重合開始剤としては、例えば、１－フェニル－１，１－プロパンジオン－２－（ｏ－エトキシカルボニル）－オキシム等が挙げられる。
　また、ベンゾイン系光重合開始剤には、例えば、ベンゾイン等が含まれる。ベンジル系光重合開始剤には、例えば、ベンジル等が含まれる。ベンゾフェノン系光重合開始剤には、例えば、ベンゾフェノン、ベンゾイル安息香酸、３，３´－ジメチル－４－メトキシベンゾフェノン、ポリビニルベンゾフェノン、α－ヒドロキシシクロヘキシルフェニルケトン等が含まれる。ケタール系光重合開始剤には、例えば、ベンジルジメチルケタール等が含まれる。チオキサントン系光重合開始剤には、例えば、チオキサントン、２－クロロチオキサントン、２－メチルチオキサントン、２，４－ジメチルチオキサントン、イソプロピルチオキサントン、２，４－ジクロロチオキサントン、２，４－ジエチルチオキサントン、イソプロピルチオキサントン、２，４－ジイソプロピルチオキサントン、ドデシルチオキサントン等が含まれる。
　アシルフォスフィン系光重合開始剤としては、例えば、ビス（２，６－ジメトキシベンゾイル）フェニルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）（２，４，４－トリメチルペンチル）ホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－ｎ－ブチルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－（２－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－（１－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－ｔ－ブチルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）シクロヘキシルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）オクチルホスフィンオキシド、ビス（２－メトキシベンゾイル）（２－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２－メトキシベンゾイル）（１－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，６－ジエトキシベンゾイル）（２－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，６－ジエトキシベンゾイル）（１－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，６－ジブトキシベンゾイル）（２－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，４－ジメトキシベンゾイル）（２－メチルプロパン－１－イル）ホスフィンオキシド、ビス（２，４，６－トリメチルベンゾイル）（２，４－ジペントキシフェニル）ホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）ベンジルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－２－フェニルプロピルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－２－フェニルエチルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）ベンジルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－２－フェニルプロピルホスフィンオキシド、ビス（２，６－ジメトキシベンゾイル）－２－フェニルエチルホスフィンオキシド、２，６－ジメトキシベンゾイルベンジルブチルホスフィンオキシド、２，６－ジメトキシベンゾイルベンジルオクチルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－２，５－ジイソプロピルフェニルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－２－メチルフェニルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－４－メチルフェニルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－２，５－ジエチルフェニルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－２，３，５，６－テトラメチルフェニルホスフィンオキシド、ビス（２，４，６－トリメチルベンゾイル）－２，４－ジ－ｎ－ブトキシフェニルホスフィンオキシド、２，４，６－トリメチルベンゾイルジフェニルホスフィンオキシド、ビス(２，６－ジメトキシベンゾイル)－２，４，４－トリメチルペンチルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)イソブチルホスフィンオキシド、２，６－ジメチトキシベンゾイル－２，４，６－トリメチルベンゾイル－n－ブチルホスフィンオキシド、ビス（２，４，６－トリメチルベンゾイル)フェニルホスフィンオキシド、ビス(２，４，６－トリメチルベンゾイル)－２，４－ジブトキシフェニルホスフィンオキシド、１，１０－ビス[ビス(２，４，６－トリメチルベンゾイル)ホスフィンオキシド]デカン、トリ(２－メチルベンゾイル)ホスフィンオキシド、などが挙げられる。
　光重合開始剤の使用量は、特に制限されないが、例えば、前記モノマー成分１００重量部に対して０．０１～５重量部、好ましくは０．０５～３重量部、さらに好ましくは０．０５～１．５重量部であり、さらに好ましくは０．１～１重量部である
　光重合開始剤の使用量が０．０１重量部より少ないと、重合反応が不十分になる場合がある。光重合開始剤の使用量が５重量部を超えると、光重合開始剤が紫外線を吸収することにより、紫外線が粘着剤層内部まで届かなくなる場合がある。この場合、重合率の低下を生じたり、生成するポリマーの分子量が小さくなってしまう。そして、これにより、形成される粘着剤層の凝集力が低くなり、粘着剤層をフィルムから剥離する際に、粘着剤層の一部がフィルムに残り、フィルムの再利用ができなくなる場合がある。なお、光重合性開始剤は１種を単独でまたは２種以上を組み合わせて使用することができる。
　本発明の（メタ）アクリル系ポリマーの重量平均分子量は４０万～２５０万であるのが好ましい、より好ましくは６０万～２２０万である。重量平均分子量が４０万より大きくすることで、粘着剤層の耐久性を満足させたり、粘着剤層の凝集力が小さくなって糊残りが生じるのを抑えることができる。一方、重量平均分子量が２５０万よりも大きくなると貼り合せ性、粘着力が低下する傾向がある。さらに、粘着剤が溶液系において、粘度が高くなりすぎ、塗工が困難になる場合がある。なお、重量平均分子量は、ＧＰＣ（ゲルパーミネーション・クロマトグラフィー）により測定し、ポリスチレン換算により算出された値をいう。なお、放射線重合で得られた（メタ）アクリル系ポリマーについては、分子量測定は困難である。
　＜重量平均分子量の測定＞
　得られた（メタ）アクリル系ポリマーの重量平均分子量は、ＧＰＣ（ゲル・パーミエー
ション・クロマトグラフィー）により測定した。サンプルは、試料をテトラヒドロフランに溶解して０．１重量％の溶液とし、これを一晩静置した後、０．４５μｍのメンブレンフィルターで濾過した濾液を用いた。
・分析装置：東ソー社製、ＨＬＣ－８１２０ＧＰＣ
・カラム：東ソー社製、（メタ）アクリル系ポリマー：ＧＭ７０００ＨＸＬ＋ＧＭＨＸＬ＋ＧＭＨＸＬ
　芳香族系ポリマー：Ｇ３０００ＨＸＬ＋２０００ＨＸＬ＋Ｇ１０００ＨＸＬ
・カラムサイズ；各７．８ｍｍφ×３０ｃｍ　計９０ｃｍ
・溶離液：テトラヒドロフラン（濃度０．１重量％）
・流量：０．８ｍｌ／ｍｉｎ
・入口圧：１．６ＭＰａ
・検出器：示差屈折計（ＲＩ）
・カラム温度：４０℃
　　・　注入量：１００μｌ
　　・　溶離液：テトラヒドロフラン
　　・　検出器：示差屈折計
　　・　標準試料：ポリスチレン
　本発明の粘着剤は、架橋剤を含有することができる。架橋剤としては、イソシアネート系架橋剤、エポキシ系架橋剤、シリコーン系架橋剤、オキサゾリン系架橋剤、アジリジン系架橋剤、シラン系架橋剤、アルキルエーテル化メラミン系架橋剤、金属キレート系架橋剤、過酸化物などの架橋剤が含まれる。架橋剤は１種を単独でまたは２種以上を組み合わせることができる。前記架橋剤としては、イソシアネート系架橋剤、エポキシ系架橋剤が好ましく用いられる。
　上記架橋剤は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記架橋剤を０．０１～５重量部の範囲で含有することが好ましい。架橋剤の含有量は、０．０１～４重量部含有することが好ましく、０．０２～３重量部含有することがより好ましい。
　イソシアネート系架橋剤は、イソシアネート基（イソシアネート基をブロック剤または数量体化などにより一時的に保護したイソシアネート再生型官能基を含む）を１分子中に２つ以上有する化合物をいう。
　イソシアネート系架橋剤としては、トリレンジイソシアネート、キシレンジイソシアネートなどの芳香族イソシアネート、イソホロンジイソシアネートなどの脂環族イソシアネート、ヘキサメチレンジイソシアネートなどの脂肪族イソシアネートなどが挙げられる。
　より具体的には、例えば、ブチレンジイソシアネート、ヘキサメチレンジイソシアネートなどの低級脂肪族ポリイソシアネート類、シクロペンチレンジイソシアネート、シクロヘキシレンジイソシアネート、イソホロンジイソシアネートなどの脂環族イソシアネート類、２，４－トリレンジイソシアネート、４，４’－ジフェニルメタンジイソシアネート、キシリレンジイソシアネート、ポリメチレンポリフェニルイソシアネートなどの芳香族ジイソシアネート類、トリメチロールプロパン／トリレンジイソシアネート３量体付加物（日本ポリウレタン工業社製，商品名コロネートＬ）、トリメチロールプロパン／ヘキサメチレンジイソシアネート３量体付加物（日本ポリウレタン工業社製，商品名コロネートＨＬ）、ヘキサメチレンジイソシアネートのイソシアヌレート体（日本ポリウレタン工業社製，商品名コロネートＨＸ）などのイソシアネート付加物、キシリレンジイソシアネートのトリメチロールプロパン付加物（三井化学社製，商品名Ｄ１１０Ｎ）、ヘキサメチレンジイソシアネートのトリメチロールプロパン付加物（三井化学社製，商品名Ｄ１６０Ｎ）；ポリエーテルポリイソシアネート、ポリエステルポリイソシアネート、ならびにこれらと各種のポリオールとの付加物、イソシアヌレート結合、ビューレット結合、アロファネート結合などで多官能化したポリイソシアネートなどを挙げることができる。これらのうち、脂肪族イソシアネートを用いることが、反応速度が速い為に好ましい。
　上記イソシアネート系架橋剤は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記イソシアネート系架橋剤を０．０１～５重量部含有することが好ましく、さらには０．０１～４重量部含有することが好ましく、さらには０．０２～３重量部含有することが好ましい。凝集力、耐久性試験での剥離の阻止などを考慮して適宜含有させることが可能である。
　なお、乳化重合にて作成した変性（メタ）アクリル系ポリマーの水分散液では、イソシアネート系架橋剤を用いなくても良いが、必要な場合には、水と反応し易いために、ブロック化したイソシアネート系架橋剤を用いることもできる。
　上記エポキシ系架橋剤はエポキシ基を１分子中に２つ以上有する多官能エポキシ化合物をいう。エポキシ系架橋剤としては、例えば、ビスフェノールＡ、エピクロルヒドリン型のエポキシ系樹脂、エチレングリシジルエーテル、Ｎ，Ｎ，Ｎ′，Ｎ′－テトラグリシジル－ｍ－キシレンジアミン、ジグリシジルアニリン、ジアミングリシジルアミン、１，３－ビス（Ｎ，Ｎ－ジグリシジルアミノメチル）シクロヘキサン、１，６－ヘキサンジオールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、エチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、ソルビトールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、グリセリンジグリシジルエーテル、グリセリントリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ソルビタンポリグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル、アジピン酸ジグリシジルエステル、ｏ－フタル酸ジグリシジルエステル、トリグリシジル－トリス（２－ヒドロキシエチル）イソシアヌレート、レゾルシンジグリシジルエーテル、ビスフェノール－Ｓ－ジグリシジルエーテルの他、分子内にエポキシ基を２つ以上有するエポキシ系樹脂などが挙げられる。上記エポキシ系架橋剤としては、例えば、三菱ガス化学社製、商品名「テトラッドＣ」、「テトラッドＸ」などの市販品も挙げられる。
　上記エポキシ系架橋剤は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記エポキシ系架橋剤を０．０１～５重量部含有することが好ましく、さらには０．０１～４重量部含有することが好ましく、さらには０．０２～３重量部含有することが好ましい。凝集力、耐久性試験での剥離の阻止などを考慮して適宜含有させることが可能である。
　過酸化物の架橋剤としては、加熱によりラジカル活性種を発生して粘着剤のベースポリマーの架橋を進行させるものであれば適宜使用可能であるが、作業性や安定性を勘案して、１分間半減期温度が８０℃～１６０℃である過酸化物を使用することが好ましく、９０℃～１４０℃である過酸化物を使用することがより好ましい。
　用いることができる過酸化物としては、例えば、ジ（２－エチルヘキシル）パーオキシジカーボネート（１分間半減期温度：９０．６℃）、ジ（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート（１分間半減期温度：９２．１℃）、ジ－ｓｅｃ－ブチルパーオキシジカーボネート（１分間半減期温度：９２．４℃）、ｔ－ブチルパーオキシネオデカノエート（１分間半減期温度：１０３．５℃）、ｔ－ヘキシルパーオキシピバレート（１分間半減期温度：１０９．１℃）、ｔ－ブチルパーオキシピバレート（１分間半減期温度：１１０．３℃）、ジラウロイルパーオキシド（１分間半減期温度：１１６．４℃）、ジ－ｎ－オクタノイルパーオキシド（１分間半減期温度：１１７．４℃）、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート（１分間半減期温度：１２４．３℃）、ジ（４－メチルベンゾイル）パーオキシド（１分間半減期温度：１２８．２℃）、ジベンゾイルパーオキシド（１分間半減期温度：１３０．０℃）、ｔ－ブチルパーオキシイソブチレート（１分間半減期温度：１３６．１℃）、１，１－ジ（ｔ－ヘキシルパーオキシ）シクロヘキサン（１分間半減期温度：１４９．２℃）などが挙げられる。なかでも特に架橋反応効率が優れることから、ジ（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート（１分間半減期温度：９２．１℃）、ジラウロイルパーオキシド（１分間半減期温度：１１６．４℃）、ジベンゾイルパーオキシド（１分間半減期温度：１３０．０℃）などが好ましく用いられる。
　なお、過酸化物の半減期とは、過酸化物の分解速度を表す指標であり、過酸化物の残存量が半分になるまでの時間をいう。任意の時間で半減期を得るための分解温度や、任意の温度での半減期時間に関しては、メーカーカタログなどに記載されており、例えば、日本油脂株式会社の「有機過酸化物カタログ第９版（２００３年５月）」などに記載されている。
　前記過酸化物は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記過酸化物０．０２～２重量部であり、０．０５～１重量部含有することが好ましい。加工性、リワーク性、架橋安定性、剥離性などの調整の為に、この範囲内で適宜選択される。
　なお、反応処理後の残存した過酸化物分解量の測定方法としては、例えば、ＨＰＬＣ（高速液体クロマトグラフィー）により測定することができる。
　より具体的には、例えば、反応処理後の粘着剤を約０．２ｇずつ取り出し、酢酸エチル１０ｍｌに浸漬し、振とう機で２５℃下、１２０ｒｐｍで３時間振とう抽出した後、室温で３日間静置する。次いで、アセトニトリル１０ｍｌ加えて、２５℃下、１２０ｒｐｍで３０分振とうし、メンブランフィルター（０．４５μｍ）によりろ過して得られた抽出液約１０μｌをＨＰＬＣに注入して分析し、反応処理後の過酸化物量とすることができる。
　また、架橋剤として、有機系架橋剤や多官能性金属キレートを併用してもよい。多官能性金属キレートは、多価金属が有機化合物と共有結合または配位結合しているものである。多価金属原子としては、Ａｌ、Ｃｒ、Ｚｒ、Ｃｏ、Ｃｕ、Ｆｅ、Ｎｉ、Ｖ、Ｚｎ、Ｉｎ、Ｃａ、Ｍｇ、Ｍｎ、Ｙ、Ｃｅ、Ｓｒ、Ｂａ、Ｍｏ、Ｌａ、Ｓｎ、Ｔｉ等が挙げられる。共有結合または配位結合する有機化合物中の原子としては酸素原子等が挙げられ、有機化合物としてはアルキルエステル、アルコール化合物、カルボン酸化合物、エーテル化合物、ケトン化合物等が挙げられる。
　本発明の粘着剤には、接着力を向上させるために、（メタ）アクリル系オリゴマーを含有させることができる。（メタ）アクリル系オリゴマーは、本発明の（メタ）アクリル系ポリマーよりもＴｇが高く、重量平均分子量が小さい重合体を用いるのが好ましく。かかる（メタ）アクリル系オリゴマーは、粘着付与樹脂として機能し、かつ誘電率を上昇させずに接着力を増加させる利点を有する。
　前記（メタ）アクリル系オリゴマーは、Ｔｇが約０℃以上３００℃以下、好ましくは約２０℃以上３００℃以下、さらに好ましくは約４０℃以上３００℃以下であることが望ましい。Ｔｇが約０℃未満であると粘着剤層の室温以上での凝集力が低下し、保持特性や高温での接着性が低下する場合がある。なお（メタ）アクリル系オリゴマーのＴｇは、（メタ）アクリル系ポリマーのＴｇと同じく、Ｆｏｘの式に基づいて計算した理論値である。
　（メタ）アクリル系オリゴマーの重量平均分子量は、１０００以上３００００未満、好ましくは１５００以上２００００未満、さらに好ましくは２０００以上１００００未満である。重量平均分子量が３００００以上であると、接着力の向上効果が充分には得られない場合がある。また、１０００未満であると、低分子量となるため接着力や保持特性の低下を引き起こす場合がある。本発明において、（メタ）アクリル系オリゴマーの重量平均分子量の測定は、ＧＰＣ法によりポリスチレン換算して求めることができる。具体的には東ソー株式会社製のＨＰＬＣ８０２０に、カラムとしてＴＳＫｇｅｌＧＭＨ－Ｈ（２０）×２本を用いて、テトラヒドロフラン溶媒で流速約０．５ｍｌ／分の条件にて測定される。
　前記（メタ）アクリル系オリゴマーを構成するモノマーとしては、例えばメチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｓ－ブチル（メタ）アクリレート、ｔ－ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、ヘキシル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ウンデシル（メタ）アクリレート、ドデシル（メタ）アクリレートのようなアルキル（メタ）アクリレート；シクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレートのような（メタ）アクリル酸と脂環族アルコールとのエステル；フェニル（メタ）アクリレート、ベンジル（メタ）アクリレートのようなアリール（メタ）アクリレート；テルペン化合物誘導体アルコールから得られる（メタ）アクリレート；等を挙げることができる。このような（メタ）アクリレートは単独であるいは２種以上を組み合わせて使用することができる。
　（メタ）アクリル系オリゴマーとしては、イソブチル（メタ）アクリレートやｔ－ブチル（メタ）アクリレートのようなアルキル基が分岐構造を持ったアルキル（メタ）アクリレート；シクロヘキシル（メタ）アクリレートや、イソボルニル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレートのような（メタ）アクリル酸と脂環式アルコールとのエステル；フェニル（メタ）アクリレートやベンジル（メタ）アクリレートのようなアリール（メタ）アクリレートなどの環状構造を持った（メタ）アクリレートに代表される、比較的嵩高い構造を有するアクリル系モノマーをモノマー単位として含んでいることが好ましい。このような嵩高い構造を（メタ）アクリル系オリゴマーに持たせることで、粘着剤層の接着性をさらに向上させることができる。特に嵩高さという点で環状構造を持ったものは効果が高く、環を複数含有したものはさらに効果が高い。また、（メタ）アクリル系オリゴマーの合成の際や粘着剤層の作製の際に紫外線（紫外線）を採用する場合には、重合阻害を起こしにくいという点で、飽和結合を有したものが好ましく、アルキル基が分岐構造を持ったアルキル（メタ）アクリレート、または脂環式アルコールとのエステルを、（メタ）アクリル系オリゴマーを構成するモノマーとして好適に用いることができる。
　このような点から、好適な（メタ）アクリル系オリゴマーとしては、例えば、シクロヘキシルメタクリレート（ＣＨＭＡ）とイソブチルメタクリレート（ＩＢＭＡ）の共重合体、シクロヘキシルメタクリレート（ＣＨＭＡ）とイソボルニルメタクリレート（ＩＢＸＭＡ）の共重合体、シクロヘキシルメタクリレート（ＣＨＭＡ）とアクリロイルモルホリン（ＡＣＭＯ）の共重合体、シクロヘキシルメタクリレート（ＣＨＭＡ）とジエチルアクリルアミド（ＤＥＡＡ）の共重合体、１－アダマンチルアクリレート（ＡＤＡ）とメチルメタクリレート（ＭＭＡ）の共重合体、ジシクロペンタニルメタクリレート（ＤＣＰＭＡ）とイソボルニルメタクリレート（ＩＢＸＭＡ）の共重合体、シクロペンタニルメタクリレート（ＤＣＰＭＡ）とメチルメタクリレート（ＭＭＡ）の共重合体、ジシクロペンタニルメタクリレート（ＤＣＰＭＡ）、シクロヘキシルメタクリレート（ＣＨＭＡ）、イソボルニルメタクリレート（ＩＢＸＭＡ）、イソボルニルアクリレート（ＩＢＸＡ）、ジシクロペンタニルアクリレート（ＤＣＰＡ）、１－アダマンチルメタクリレート（ＡＤＭＡ）、１－アダマンチルアクリレート（ＡＤＡ）の各単独重合体等を挙げることができる。特に、ＣＨＭＡを主成分として含むオリゴマーが好ましい。
　本発明の粘着剤において、前記（メタ）アクリル系オリゴマーを用いる場合、その含有量は特に限定されないが、（メタ）アクリル系ポリマー１００重量部に対して７０重量部以下であるのが好ましく、さらに好ましくは１～７０重量部であり、さらに好ましくは２～５０重量部であり、さらに好ましくは３～４０重量部である。（メタ）アクリル系オリゴマーの添加量が７０重量部を超えると、弾性率が高くなり低温での接着性が悪くなるという不具合がある。なお、（メタ）アクリル系オリゴマーを１重量部以上配合する場合に、接着力の向上効果の点から有効である。
　さらに、本発明の粘着剤には、粘着剤層のガラスなどの親水性被着体に適用する場合における界面での耐水性をあげる為にシランカップリング剤を含有することができる。シランカップリング剤の配合量は、（メタ）アクリル系ポリマー１００重量部に対して１重量部以下であるのが好ましく、さらに好ましくは０．０１～１重量部、さらに好ましくは０．０２～０．６重量部である。シランカップリング剤の配合が多過ぎるとガラスへの接着力が増大し再剥離性に劣り、少なすぎると耐久性が低下するため好ましくない。
　好ましく用いられ得るシランカップリング剤としては、３－グリシドキシプロピルトリメトキシシラン、３－グリシドキシプロピルトリエトキシシラン、３－グリシドキシプロピルメチルジエトキシシラン、２－（３，４エポキシシクロヘキシル）エチルトリメトキシシランなどのエポキシ基含有シランカップリング剤、３－アミノプロピルトリメトキシシラン 、Ｎ－２－（アミノエチル）－３－アミノプロピルメチルジメトキシシラン、３－トリエトキシシリル－Ｎ－（１，３－ジメチルブチリデン）プロピルアミン、Ｎ－フェニル－γ－アミノプロピルトリメトキシシランなどのアミノ基含有シランカップリング剤、３－アクリロキシプロピルトリメトキシシラン、３－メタクリロキシプロピルトリエトキシシランなどの（メタ）アクリル基含有シランカップリング剤、３－イソシアネートプロピルトリエトキシシラン等のイソシアネート基含有シランカップリング剤などが挙げられる。
　さらに本発明の粘着剤には、その他の公知の添加剤を含有していてもよく、例えば、着色剤、顔料などの粉体、染料、界面活性剤、可塑剤、粘着性付与剤、表面潤滑剤、レベリング剤、軟化剤、酸化防止剤、老化防止剤、光安定剤、紫外線吸収剤、重合禁止剤、無機または有機の充填剤、金属粉、粒子状、箔状物などを使用する用途に応じて適宜添加することができる。
　本発明の粘着剤層は、前記粘着剤から形成される。粘着剤層の厚さは、特に制限されず例えば、１～４００μｍ程度である。また、前記粘着剤層の厚さは、粘着剤に用いる（メタ）アクリル系ポリマーの製造方法によって、適宜に好ましい範囲を設置することができる。例えば、溶液重合等により（メタ）アクリル系ポリマーを製造する場合には、前記粘着剤層の厚さは、１～１００μｍが好ましく、より好ましくは２～５０μｍ、さらに好ましくは２～４０μｍであり、さらに好ましくは５～３５μｍである。また、放射線重合等により、（メタ）アクリル系ポリマーを製造する場合には、前記粘着剤層の厚さは、５０～４００μｍが好ましく、より好ましくは７５～３００μｍ、さらに好ましくは１００～２００μｍである。
　また本発明の粘着剤層は、周波数１００ｋＨｚにおける比誘電率が３．５以下であるのが好ましく、より好ましくは３．３以下、さらに好ましくは３．２以下であり、さらに好ましくは３．０以下である。
　また本発明の粘着剤層のゲル分率は２０～９８重量％であるのが好ましい。粘着剤層のゲル分率は、より好ましくは３０～９８重量％であり、さらに好ましくは４０～９５重量％である。前記粘着剤が架橋剤を含有する場合には、架橋剤全体の添加量を調整することとともに、架橋処理温度や架橋処理時間の影響を十分考慮して、ゲル分率が制御することができる。ゲル分率が小さい場合には凝集力に劣り、大きすぎると接着力に劣る場合がある。かかるゲル分率を有する粘着剤層は、被着体に貼付後の接着力の上昇が非常に小さく、長時間貼り付けた後でも糊残りすることなく、容易に再剥離できるという特徴が発揮される。
　また本発明の粘着剤層は、粘着剤層の厚さが２５μｍの場合のヘイズ値が２％以下であることが好ましい。ヘイズ２％以下であれば、前記粘着剤層が光学部材に用いられる場合に要求される透明性を満足することができる。前記ヘイズ値は０～１．５％であることが好ましく、さらには０～１％であることが好ましい。なお、ヘイズ値は２％以下であれば、光学用途として満足することができる。前記ヘイズ値が２％を超えると白濁が生じて光学フィルム用途として好ましくない。
　粘着剤層の透明性は、モノマー成分の全体量に対する、環状窒素含有モノマーおよび共重合モノマー（特に、ヒドロキシル基含有モノマー）の総量で決まっていると考えられる。前記総量が多いと透明性に優れるが、多すぎると他の特性に悪影響を与えるおそれがある。従って、環状窒素含有モノマーの割合が少ない場合は、例えば、共重合モノマーとしてヒドロキシル基含有モノマーを用いることにより、透明性を制御することができる。
　前記粘着剤層は、例えば、前記粘着剤を支持体に塗布し、重合溶剤などを乾燥除去することにより粘着シートとして形成することができる。粘着剤の塗布にあたっては、適宜に、重合溶剤以外の一種以上の溶剤を新たに加えてもよい。
　粘着剤の塗布方法としては、各種方法が用いられる。具体的には、例えば、ロールコート、キスロールコート、グラビアコート、リバースコート、ロールブラッシュ、スプレーコート、ディップロールコート、バーコート、ナイフコート、エアーナイフコート、カーテンコート、リップコート、ダイコーターなどによる押出しコート法などの方法が挙げられる。
　前記加熱乾燥温度は、好ましくは４０℃～２００℃であり、さらに好ましくは、５０℃～１８０℃であり、特に好ましくは７０℃～１７０℃である。加熱温度を上記の範囲とすることによって、優れた粘着特性を有する粘着剤層を得ることができる。乾燥時間は、適宜、適切な時間が採用され得る。上記乾燥時間は、好ましくは５秒～２０分、さらに好ましくは５秒～１０分、特に好ましくは、１０秒～５分である。
　また前記粘着剤層の形成は、本発明の（メタ）アクリル系ポリマーを、モノマー成分を紫外線照射することにより重合して製造する場合には、前記モノマー成分から（メタ）アクリル系ポリマーを製造するとともに、粘着剤層を形成することができる。モノマー成分には、適宜に架橋剤等の前記粘着剤に配合することができる材料を含有することができる。前記モノマー成分は、紫外線照射にあたり、事前に一部を重合してシロップにしたものを用いることができる。紫外線照射には、高圧水銀ランプ、低圧水銀ランプ、メタルハライドランプなどを用いることができる。
　前記支持体としては、例えば、剥離処理したシートを用いることができる。剥離処理したシートとしては、シリコーン剥離ライナーが好ましく用いられる。
　剥離処理したシート上に粘着剤層を形成した粘着シートは、前記粘着剤層が露出する場合には、実用に供されるまで剥離処理したシート（セパレーター）で粘着剤層を保護してもよい。実用に際しては、前記剥離処理したシートは剥離される。
　セパレーターの構成材料としては、例えば、ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリエステルフィルムなどのプラスチックフィルム、紙、布、不織布などの多孔質材料、ネット、発泡シート、金属箔、およびこれらのラミネート体などの適宜な薄葉体などを挙げることができるが、表面平滑性に優れる点からプラスチックフィルムが好適に用いられる。
　そのプラスチックフィルムとしては、前記粘着剤層を保護し得るフィルムであれば特に限定されず、例えば、ポリエチレンフィルム、ポリプロピレンフィルム、ポリブテンフィルム、ポリブタジエンフィルム、ポリメチルペンテンフイルム、ポリ塩化ビニルフィルム、塩化ビニル共重合体フィルム、ポリエチレンテレフタレートフィルム、ポリブチレンテレフタレートフィルム、ポリウレタンフィルム、エチレン－酢酸ビニル共重合体フィルムなどが挙げられる。
　前記セパレーターの厚みは、通常５～２００μｍ、好ましくは５～１００μｍ程度である。前記セパレーターには、必要に応じて、シリコーン系、フッ素系、長鎖アルキル系もしくは脂肪酸アミド系の離型剤、シリカ粉などによる離型および防汚処理や、塗布型、練り込み型、蒸着型などの帯電防止処理もすることもできる。特に、前記セパレーターの表面にシリコーン処理、長鎖アルキル処理、フッ素処理などの剥離処理を適宜おこなうことにより、前記粘着剤層からの剥離性をより高めることができる。
　本発明の粘着剤層および粘着シートは、光学部材への適用が好適であり、特に光学用途における、金属薄膜や金属電極に対して貼り付ける用途に好ましく使用される。金属薄膜としては、金属、金属酸化物やこれらの混合物からなる薄膜が挙げられ、特に限定はされないが、例えば、ＩＴＯ（酸化インジウムスズ）、ＺｎＯ、ＳｎＯ、ＣＴＯ（酸化カドミウムスズ）の薄膜が挙げられる。金属薄膜の厚みは、特に限定されないが、１０～２００ｎｍ程度である。通常、ＩＴＯなどの金属薄膜は、例えば、ポリエチレンテレフタレートフィルム（特にＰＥＴフィルム）等の透明プラスチックフィルム基材上に設けられ、透明導電性フィルムとして使用される。上記の本発明の粘着シートを金属薄膜に対して貼り付ける際には、粘着剤層側の表面を金属薄膜に貼り付けられる側の粘着面となるようにして使用されることが好ましい。
　また、上記金属電極としては、金属、金属酸化物やこれらの混合物からなる電極であればよく、特に限定されないが、例えば、ＩＴＯ、銀、銅、ＣＮＴ（カーボンナノチューブ）の電極が挙げられる。
　本発明の粘着シートの具体的な用途の一例として、タッチパネルの製造用途に用いる、タッチパネル用粘着シートを挙げることができる。タッチパネル用粘着シートは、例えば、静電容量方式のタッチパネルの製造において、ＩＴＯなどの金属薄膜が設けられた透明導電フィルムと、ポリメタクリル酸メチル樹脂（ＰＭＭＡ）板、ハードコートフィルム、ガラスレンズ等とを貼り合わせるために用いらえる。上記タッチパネルは、特に限定されないが、例えば、携帯電話、タブレットコンピューター、携帯情報端末などに用いられる。
　より具体的な例として、本発明の粘着剤層または粘着シートが用いられている静電容量方式のタッチパネルの一例を図１に示す。図１において、１は静電容量方式タッチパネルであり、１１は装飾パネルであり、１２は粘着剤層または粘着シートであり、１３はＩＴＯフィルムであり、１４はハードコートフィルムである。装飾パネル１１は、ガラス板や透明アクリル板（ＰＭＭＡ板）であることが好ましい。また、ＩＴＯフィルム１３は、ガラス板や透明プラスチックフィルム（特にＰＥＴフィルム）にＩＴＯ膜が設けられているものが好ましい。ハードコートフィルム１４は、ＰＥＴフィルムなどの透明プラスチックフィルムにハードコート処理が施されたものが好ましい。上記静電容量方式タッチパネル１は、本発明の粘着剤層または粘着シートが用いられているので、厚さを薄くすることができ、動作の安定性に優れる。また、外観や視認性が良好である。
　また本発明の粘着シートの支持体としては、光学部材を用いることができる。前記粘着剤層は、光学部材に直接塗布し、重合溶剤などを乾燥除去することにより、粘着剤層を光学部材に形成することができる。また、剥離処理したセパレーターに形成した粘着剤層を、適宜に光学部材に転写して、粘着型光学部材を形成することができる。
　なお、上記の粘着型光学部材の作製にあたって用いた、剥離処理したシートは、そのまま粘着型光学部材のセパレーターとして用いることができ、工程面における簡略化ができる。
　また、前記粘着型光学部材において、粘着剤層の形成にあたっては、光学部材の表面に、アンカー層を形成したり、コロナ処理、プラズマ処理などの各種易接着処理を施した後に粘着剤層を形成することができる。また、粘着剤層の表面には易接着処理をおこなってもよい。
　本発明の粘着型光学部材は、光学部材として透明導電性フィルムを用いた、粘着剤層付き透明導電性フィルムとして用いることができる。透明導電性フィルムは、透明プラスチックフィルム基材の一方の面に、上記ＩＴＯ等の金属薄膜となる透明導電性薄膜を有する。透明プラスチックフィルム基材の他方の面には、本発明の粘着剤層を有する。透明プラスチックフィルム基材には、アンダーコート層を介して透明導電性薄膜を設けることができる。なお、アンダーコート層は複数層設けることができる。透明プラスチックフィルム基材と粘着剤層の間にオリゴマー移行防止層を設けることができる。
　前記透明プラスチックフィルム基材としては、特に制限されないが、透明性を有する各種のプラスチックフィルムが用いられる。当該プラスチックフィルムは１層のフィルムにより形成されている。例えば、その材料として、ポリエチレンテレフタレート、ポリエチレンナフタレート等のポリエステル系樹脂、アセテート系樹脂、ポリエーテルスルホン系樹脂、ポリカーボネート系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリオレフィン系樹脂、（メタ）アクリル系樹脂、ポリ塩化ビニル系樹脂、ポリ塩化ビニリデン系樹脂、ポリスチレン系樹脂、ポリビニルアルコール系樹脂、ポリアリレート系樹脂、ポリフェニレンサルファイド系樹脂等が挙げられる。これらの中で特に好ましいのは、ポリエステル系樹脂、ポリイミド系樹脂およびポリエーテルスルホン系樹脂である。前記フィルム基材の厚みは、１５～２００μｍであることが好ましい。
　前記フィルム基材には、表面に予めスパッタリング、コロナ放電、火炎、紫外線照射、電子線照射、化成、酸化などのエッチング処理や下塗り処理を施して、この上に設けられる透明導電性薄膜またはアンダーコート層の前記フィルム基材に対する密着性を向上させるようにしてもよい。また、透明導電性薄膜またはアンダーコート層を設ける前に、必要に応じて溶剤洗浄や超音波洗浄などにより除塵、清浄化してもよい。
　前記透明導電性薄膜の構成材料、厚みは、特に限定されず、上記金属薄膜で例示したとおりである。アンダーコート層は、無機物、有機物または無機物と有機物との混合物により形成することができる。例えば、無機物として、ＮａＦ（１．３）、Ｎａ3ＡｌＦ6（１．３５）、ＬｉＦ（１．３６）、ＭｇＦ2（１．３８）、ＣａＦ2（１．４）、ＢａＦ2（１．３）、ＳｉＯ2（１．４６）、ＬａＦ3（１．５５）、ＣｅＦ3（１．６３）、Ａｌ2Ｏ3（１．６３）などの無機物〔上記各材料の（）内の数値は光の屈折率である〕が挙げられる。これらのなかでも、ＳｉＯ2、ＭｇＦ2、Ａ１2Ｏ3などが好ましく用いられる。特に、ＳｉＯ2が好適である。上記の他、酸化インジウムに対して、酸化セリウムを１０～４０重量部程度、酸化スズを０～２０重量部程度含む複合酸化物を用いることができる。
　また有機物としてはアクリル樹脂、ウレタン樹脂、メラミン樹脂、アルキド樹脂、シロキサン系ポリマー、有機シラン縮合物などが挙げられる。これら有機物は、少なくとも１種が用いられる。特に、有機物としては、メラミン樹脂とアルキド樹脂と有機シラン縮合物の混合物からなる熱硬化型樹脂を使用するのが望ましい。
　アンダーコート層の厚さは、特に制限されるものではないが、光学設計、前記フィルム基材からのオリゴマー発生防止効果の点から、通常、１～３００ｎｍ程度であり、好ましくは５～３００ｎｍである。
　上記粘着剤層付き透明導電性フィルムは、タッチパネルや液晶ディスプレイなどの種々の装置の形成などにおいて用いられる。特に、タッチパネル用電極板として好ましく用いることができる。タッチパネルは、種々の検出方式（例えば、抵抗膜方式、静電容量方式等）に好適に用いられる。
　静電容量方式のタッチパネルは、通常、所定のパターン形状を有する透明導電性薄膜を備えた透明導電性フィルムがディスプレイ表示部の全面に形成されている。上記粘着剤層付き透明導電性フィルムは、粘着剤層とパターン化された透明導電性薄膜とが対面するように適宜に積層される。
　また、本発明の粘着型光学部材は、光学部材として画像表示装置用の光学フィルムを用いた、粘着剤層付き光学フィルムとして用いることができる。
　光学フィルムとしては、液晶表示装置、有機ＥＬ表示装置等の画像表示装置の形成に用いられるものが使用され、その種類は特に制限されない。例えば、光学フィルムとしては偏光板が挙げられる。偏光板は偏光子の片面または両面には透明保護フィルムを有するものが一般に用いられる。
　偏光子は、特に限定されず、各種のものを使用できる。偏光子としては、例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等が挙げられる。これらの中でも、ポリビニルアルコール系フィルムとヨウ素などの二色性物質からなる偏光子が好適である。これらの偏光子の厚さは特に制限されないが、一般的に５～８０μｍ程度である。
　ポリビニルアルコール系フィルムをヨウ素で染色し一軸延伸した偏光子は、例えば、ポリビニルアルコールをヨウ素の水溶液に浸漬することによって染色し、元長の３～７倍に延伸することで作成することができる。必要に応じてホウ酸や硫酸亜鉛、塩化亜鉛等を含んでいても良いヨウ化カリウムなどの水溶液に浸漬することもできる。さらに必要に応じて染色前にポリビニルアルコール系フィルムを水に浸漬して水洗してもよい。ポリビニルアルコール系フィルムを水洗することでポリビニルアルコール系フィルム表面の汚れやブロッキング防止剤を洗浄することができるほかに、ポリビニルアルコール系フィルムを膨潤させることで染色のムラなどの不均一を防止する効果もある。延伸はヨウ素で染色した後に行っても良いし、染色しながら延伸しても良いし、また延伸してからヨウ素で染色しても良い。ホウ酸やヨウ化カリウムなどの水溶液や水浴中でも延伸することができる。
　透明保護フィルムを構成する材料としては、例えば透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れる熱可塑性樹脂が用いられる。このような熱可塑性樹脂の具体例としては、トリアセチルセルロース等のセルロース樹脂、ポリエステル樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリオレフィン樹脂、（メタ）アクリル樹脂、環状ポリオレフィン樹脂（ノルボルネン系樹脂）、ポリアリレート樹脂、ポリスチレン樹脂、ポリビニルアルコール樹脂、およびこれらの混合物が挙げられる。なお、偏光子の片側には、透明保護フィルムが接着剤層により貼り合わされるが、他の片側には、透明保護フィルムとして、（メタ）アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化性樹脂または紫外線硬化型樹脂を用いることができる。透明保護フィルム中には任意の適切な添加剤が１種類以上含まれていてもよい。添加剤としては、例えば、紫外線吸収剤、酸化防止剤、滑剤、可塑剤、離型剤、着色防止剤、難燃剤、核剤、帯電防止剤、顔料、着色剤などが挙げられる。透明保護フィルム中の上記熱可塑性樹脂の含有量は、好ましくは５０～１００重量％、より好ましくは５０～９９重量％、さらに好ましくは６０～９８重量％、特に好ましくは７０～９７重量％である。透明保護フィルム中の上記熱可塑性樹脂の含有量が５０重量％以下の場合、熱可塑性樹脂が本来有する高透明性等が十分に発現できないおそれがある。
　また光学フィルムとしては、例えば反射板や反透過板、位相差板（１／２や１／４等の波長板を含む）、光学補償フィルム、視覚補償フィルム、輝度向上フィルムなどの液晶表示装置等の形成に用いられることのある光学層となるものが挙げられる。これらは単独で光学フィルムとして用いることができる他、前記偏光板に、実用に際して積層して、１層または２層以上用いることができる。
　偏光板に前記光学層を積層した光学フィルムは、液晶表示装置等の製造過程で順次別個に積層する方式にても形成することができるが、予め積層して光学フィルムとしたものは、品質の安定性や組立作業等に優れていて液晶表示装置などの製造工程を向上させうる利点がある。積層には粘着層等の適宜な接着手段を用いうる。前記の偏光板と他の光学層の接着に際し、それらの光学軸は目的とする位相差特性などに応じて適宜な配置角度とすることができる。
　本発明の粘着剤層付き光学フィルムは液晶表示装置等の各種画像表示装置の形成などに好ましく用いることができる。液晶表示装置の形成は、従来に準じて行いうる。すなわち液晶表示装置は一般に、液晶セルと粘着剤層付き光学フィルム、及び必要に応じての照明システム等の構成部品を適宜に組み立てて駆動回路を組み込むことなどにより形成されるが、本発明においては本発明による粘着剤層付き光学フィルムを用いる点を除いて特に限定は無く、従来に準じうる。液晶セルについても、例えばＴＮ型やＳＴＮ型、π型、ＶＡ型、ＩＰＳ型などの任意なタイプのものを用いうる。
　液晶セルの片側又は両側に粘着剤層付き光学フィルムを配置した液晶表示装置や、照明システムにバックライトあるいは反射板を用いたものなどの適宜な液晶表示装置を形成することができる。その場合、本発明による光学フィルムは液晶セルの片側又は両側に設置することができる。両側に光学フィルムを設ける場合、それらは同じものであっても良いし、異なるものであっても良い。さらに、液晶表示装置の形成に際しては、例えば拡散板、アンチグレア層、反射防止膜、保護板、プリズムアレイ、レンズアレイシート、光拡散板、バックライトなどの適宜な部品を適宜な位置に１層又は２層以上配置することができる。
　以下に、実施例によって本発明を具体的に説明するが、本発明はこれら実施例によって限定されるものではない。なお、各例中の部および％はいずれも重量基準である。実施例等における評価項目は下記のようにして測定を行った。
　実施例１
　＜（メタ）アクリル系ポリマーの調製＞
　攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた４つ口フラスコに、イソデシルメタクリレート（ＩＤＭ）８０重量部、Ｎ－ビニル－ε－カプロラクタム（ＮＶＣ）２０重量部、２－ヒドロキシエチルアクリレート（ＨＥＡ）１０重量部、重合開始剤として２，２´－アゾビスイソブチロニトリル０．１重量部を酢酸エチル１５０重量部と共に仕込み、緩やかに攪拌しながら窒素ガスを導入して１時間窒素置換した後、フラスコ内の液温を５５℃付近に保って１５時間重合反応を行い、（メタ）アクリル系ポリマー溶液を調製した。
　次いで、上記で得られた（メタ）アクリル系ポリマー溶液に、ポリマーの固形分１００重量部に対して、架橋剤として、キシリレンジイソシアネートのトリメチロールプロパン付加物（三井化学社製，商品名Ｄ１１０Ｎ）を０．５重量部配合して粘着剤溶液を調製した。
　次いで、得られた粘着剤溶液を、シリコーン処理を施した７５μｍのポリエチレンテレフタレート（ＰＥＴ）フィルム（東レフィルム加工株式会社，セラピール）の片面に、乾燥後の粘着剤層の厚さが２５μｍになるように塗布し、１３０℃で３分間乾燥を行い、粘着剤層を形成し、粘着シートを作成した。
　実施例２～１３、比較例１～１１
　実施例１において、（メタ）アクリル系ポリマーの調製に用いたモノマーの種類とその組成比、架橋剤の種類とその配合量を表１に示すように変えたこと以外は、実施例１と同様の操作を行い、粘着シートを作成した。
　実施例１４
　＜ＵＶ重合に用いるモノマー成分の調製＞
　２－エチルヘキシルアクリレート（２ＥＨＡ）３９重量部、イソステアリルアクリレート（ＩＳＡ）３９重量部、Ｎ－ビニル－２－ピロリドン（ＮＶＰ）１８重量部、４－ヒドロキシブチルアクリレート（ＨＢＡ）４重量部、２種の光重合開始剤（商品名：イルガキュア１８４、ＢＡＳＦ社製）０．０５重量部および光重合開始剤（商品名：イルガキュア６５１、ＢＡＳＦ社製）０．０５重量部を４つ口フラスコに投入してモノマー混合物を調製した。次いで、前記モノマー混合物を窒素雰囲気下で紫外線に曝露して部分的に光重合させることによって、重合率約１０重量％の部分重合物（アクリル系ポリマーシロップ）を得た。
　上述したアクリル系ポリマーシロップの１００重量部に、トリメチロールプロパントリアクリレート（ＴＭＰＴＡ）０．０３５重量部を添加した後、これらを均一に混合してモノマー成分を調製した。
　＜ＵＶ重合による粘着剤層の作製＞
　次いで、上記で調整したモノマー成分を、片面をシリコーンで剥離処理した厚み３８μｍのポリエステルフィルム（商品名：ダイアホイルＭＲＦ、三菱樹脂株式会社製）の剥離処理面に、最終的な厚みが１００μｍになるように塗布して塗布層を形成した。次いで、塗布されたモノマー成分の表面に、片面をシリコーンで剥離処理した厚み３８μｍのポリエステルフィルム（商品名：ダイアホイルＭＲE、三菱樹脂株式会社製）を、当該フィルムの剥離処理面が塗布層側になるようにして被覆した。これにより、モノマー成分の塗布層を酸素から遮断した。このようにして得られた塗布層を有するシートにケミカルライトランプ（株式会社東芝製）を用いて照度５ｍＷ／ｃｍ２（約３５０ｎｍに最大感度をもつトプコンＵＶＲ－Ｔ１で測定）の紫外線を３６０秒間照射して、塗布層を硬化させて粘着剤層を形成し、粘着シートを作成した。粘着剤層の両面に被覆されたポリエステルフィルムは、剥離ライナーとして機能する。
　実施例１５～２４
　実施例１４において、モノマー成分の調製に用いた単官能性モノマーの種類とその組成比、多官能性モノマーの種類とその配合量、粘着剤層の厚みを表２に示すように変えたこと以外は、実施例１と同様の操作を行い、粘着シートを作成した。
　上記実施例および比較例で得られた、粘着シート（サンプル）について以下の評価を行った。評価結果を表１、表２に示す。
　＜ゲル分率の測定＞
　粘着シートにおける粘着剤層から所定量（最初の重量Ｗ１）を取り出し、酢酸エチル溶液に浸漬して、室温で１週間放置した後、不溶分を取り出し、乾燥させた重量（Ｗ２）を測定し、下記のように求めた。
　ゲル分率＝（Ｗ２／Ｗ１）×１００
　＜誘電率＞
　粘着剤層（粘着シートからシリコーン処理を施したＰＥＴフィルムを剥離したもの）を積層して、約１００μｍの積層粘着剤層を形成した。なお、実施例１４～２４においてＵＶ重合により作製した、厚さ１００μｍおよび１７５μｍのサンプルは積層せず、そのまま用いた。当該積層粘着剤層（または粘着剤層）を、銅箔と電極の間に挟み以下の装置により周波数１００ｋＨｚにおける比誘電率を測定した。測定は３サンプルを作製し、それらの３サンプルの測定値の平均を誘電率とした。
　なお、粘着剤層の周波数１００ｋＨｚでの比誘電率は、ＪＩＳ　Ｋ　６９１１に準じて、下記条件で測定した。
　測定方法：容量法（装置：Ａｇｉｌｅｎｔ　Ｔｅｃｈｎｏｌｏｇｉｅｓ　４２９４Ａ　Ｐｒｅｃｉｓｉｏｎ　Ｉｍｐｅｄａｎｃｅ　Ａｎａｌｙｚｅｒ使用）
　電極構成：１２．１ｍｍΦ、０．５ｍｍ厚みのアルミ板
　対向電極：３ｏｚ　銅板
　測定環境：２３±１℃、５２±１％ＲＨ
　＜接着力＞
　実施例および比較例で得られたサンプルの粘着面に厚み２５μｍのＰＥＴフィルム（東レ社製，ルミラーＳ１０）を貼り付けたものを評価用サンプルとした。当該評価用サンプルを、幅２０ｍｍ×長さ約１００ｍｍに裁断した後、前記ＰＥＴフィルムを剥離して、厚さ０．５ｍｍの無アルカリガラス板（コーニング社製，１７３７）に、２ｋｇのロール一往復で貼付け、室温（２３℃）で４０分間静置した後、剥離角度９０°、剥離速度３００ｍｍ／分で剥離接着を測定した。
　＜ヘイズ、全光線透過率の測定＞
　全光線透過率９３．３％、ヘイズ０．１％の無アルカリガラスの片面に、実施例および比較例で得られた粘着シートを貼り付け、ヘイズメーター（村上色彩技術研究所製，ＭＲ－１００）により、ヘイズおよび全光線透過率を測定した。ヘイズメーターによる測定にあたり、粘着シートが光源側になるように配置した。ヘイズ値は、無アルカリガラスのヘイズ値が０．１％であるため、測定値から０．１％を引いた値をヘイズ値とした。全光線透過率（％）は、測定値を採用した。
　＜加湿後のヘイズ変化＞
　粘着剤層（粘着シートからシリコーン処理を施したＰＥＴフィルムを剥離したものを透明導電性フィルム（厚さ５０μｍのＰＥＴフィルムにＩＴＯを蒸着させたフィルム）のＩＴＯが蒸着されていない面に貼り合わせた。得られた粘着剤層付透明導電性フィルムをヘイズ０．２％のアルカリガラスに貼り合わせた後、５０℃、５ａｔｍで１５分間オートクレーブに入れた。その後、粘着剤層付透明導電性フィルムのＩＴＯ面が光源側になる配置でヘイズ（Ｈ１）を測定した。前記ヘイズ測定をした粘着剤層付透明導電性フィルムを、６０℃、９５%Ｒ．Ｈ．の加湿オーブンに入れて２５０時間保存後に取り出して、常温（２３℃）にて３時間放置した後、前記同様の条件で、粘着剤層付透明導電性フィルムのヘイズ（Ｈ２）の測定を行った。ヘイズ（Ｈ２）からヘイズ（Ｈ１）を引いた値を、ヘイズ変化として、表１、表２に示す。ヘイズ変化は、１．５％未満が好ましく、１．４％以下がより好ましく、１．３％以下がさらに好ましい。
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　表１、表２中、ＩＤＭは、イソデシルメタクリレート（共栄社化学社製，ホモポリマーのＴｇ＝－４１℃）；
　ＬＭＡは、ラウリルメタクリレート（共栄社化学社製，ホモポリマーのＴｇ＝－６５℃）；
　ＴＤＭＡは、トリデシルメタクリレート（SARTOMER社製，ホモポリマーのＴｇ＝－４０℃）；
　ＩＳＴＡは、イソステアリルアクリレート（大阪有機化学工業社製，ホモポリマーのＴｇ＝－１８℃）；
　ＩＤＡは、イソデシルアクリレート（Sartomer社，ホモポリマーのＴｇ＝－６０℃）；
　ＮＶＣは、Ｎ－ビニル－ε－カプロラクタム（ＢＡＳＦ社製）；
　ＮＶＰは、Ｎ－ビニル－２－ピロリドン（日本触媒社製）；
　ＴＭＰＴＡは、トリメチロールプロパントリアクリレート；
　ｉ－ＯＡは、イソオクチルアクリレート（大阪有機化学工業社製，ホモポリマーのＴｇ＝－５８℃）；
　ｉ－ＡＡは、イソアミルアクリレート（共栄社化学社製，ホモポリマーのＴｇ＝－４５℃）；
　ｉ－ＮＡは、イソノニルアクリレート（大阪有機化学工業社製，ホモポリマーのＴｇ＝－５８℃）；
　２ＥＨＡは、２－エチルヘキシルアクリレート（東亜合成社製，ホモポリマーのＴｇ＝－７０℃）；
　ＬＡは、ラウリルアクリレート（共栄社化学社製，ホモポリマーのＴｇ＝－３℃）；
　ＳＴＡは、ステアリルアクリレート（大阪有機化学工業社製，ホモポリマーのＴｇ＝３０℃）；
　ＨＥＡは、２－ヒドロキシエチルアクリレート；
　ＨＢＡは、４－ヒドロキシブチルアクリレート；
　ＢＡ：ブチルアクリレート；
　ＯＡ：オクチルアクリレート；
　ＤＡ：デシルアクリレート；を示す。
　Ｄ１１０Ｎは、キシリレンジイソシアネートのトリメチロールプロパン付加物（三井化学社製，商品名Ｄ１１０Ｎ）、を示す。
　１　静電容量方式タッチパネル
　１１　装飾パネル
　１２　粘着剤層または粘着シート
　１３　ＩＴＯフィルム
　１４　ハードコートフィルム

Claims (19)

  1. 　炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートを３０～９９．５重量％および環状窒素含有モノマーを０．５～５０重量％を含むモノマー成分を重合することにより得られた（メタ）アクリル系ポリマーを含むことを特徴とする粘着剤。
  2. 　炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートのアルキル基が、分岐を有するアルキル基であることを特徴とする請求項１記載の粘着剤。
  3. 　炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートが、炭素数１０～１８のアルキル基をエステル末端に有するアルキルメタクリレートであることを特徴とする請求項１または２記載の粘着剤。
  4. 　炭素数１０～１８のアルキル基をエステル末端に有するアルキル（メタ）アクリレートが、炭素数１０～１８のアルキル基をエステル末端に有するアルキルアクリレートであることを特徴とする請求項１または２記載の粘着剤。
  5. 　モノマー成分が、さらに、カルボキシル基含有モノマー、ヒドロキシル基含有モノマーおよび環状エーテル基を有するモノマーから選ばれるいずれか少なくとも１つの官能基含有モノマーを、０．５重量％以上含むモノマー成分であることを特徴とする請求項１～４のいずれか１項に記載の粘着剤。
  6. 　モノマー成分が、さらに、炭素数１～９のアルキル基をエステル末端に有するアルキル（メタ）アクリレートおよび環状のアルキル基をエステル末端に有するアルキル（メタ）アクリレートから選ばれるいずれか少なくとも１種を０．５重量％以上含むモノマー成分であることを特徴とする請求項１～５のいずれか１項に記載の粘着剤。
  7. 　モノマー成分が、さらに、多官能性モノマーを３重量％以下含むモノマー成分であることを特徴とする請求項１～５のいずれかに１項に記載の粘着剤。
  8. 　さらに、前記（メタ）アクリル系ポリマー１００重量部に対して、架橋剤を、０．０１～５重量部含有することを特徴とする請求項１～７のいずれか１項に記載の粘着剤。
  9. 　光学部材に用いられることを特徴とする請求項１～８のいずれか１項に記載の粘着剤。
  10. 　請求項１～９のいずれか１項に記載の粘着剤から得られることを特徴とする粘着剤層。
  11. 　周波数１００ｋＨｚにおける比誘電率が３．５以下であることを特徴とする請求項１０記載の粘着剤層。
  12. 　ゲル分率が２０～９８重量％であることを特徴とする請求項１０または１１記載の粘着剤層。
  13. 　粘着剤層の厚さが２５μｍの場合のヘイズが、２％以下であることを特徴とする請求項１０～１２のいずれか１項に記載の粘着剤層。
  14. 　全光線透過率が９０％以上であることを特徴とする請求項１０～１３のいずれか１項に記載の粘着剤層。
  15. 　光学部材に用いられることを特徴とする請求項１０～１４のいずれか１項に記載の粘着剤層。
  16. 　支持体の少なくとも片側に、請求項１０～１５のいずれか１項に記載の粘着剤層が形成されていることを特徴とする粘着シート。
  17. 　粘着剤層の無アルカリガラスに対する９０度ピール接着力（３００ｍｍ／ｍｉｎ）が０．５Ｎ／２０ｍｍ以上であることを特徴とする請求項１６記載の粘着シート。
  18. 　光学部材に用いられることを特徴とする請求項１６または１７記載の粘着シート。
  19. 　支持体が光学部材であり、粘着シートが、光学部材の少なくとも片側に粘着剤層を有する粘着型光学部材であることを特徴とする請求項１６～１８のいずれか１項に記載の粘着シート。
     
     
PCT/JP2012/073354 2011-09-30 2012-09-12 粘着剤、粘着剤層、および粘着シート WO2013047210A1 (ja)