WO2012157643A1 - 化粧料保持体、化粧料保持体を用いた化粧料、及び化粧料の製造方法 - Google Patents

化粧料保持体、化粧料保持体を用いた化粧料、及び化粧料の製造方法 Download PDF

Info

Publication number
WO2012157643A1
WO2012157643A1 PCT/JP2012/062416 JP2012062416W WO2012157643A1 WO 2012157643 A1 WO2012157643 A1 WO 2012157643A1 JP 2012062416 W JP2012062416 W JP 2012062416W WO 2012157643 A1 WO2012157643 A1 WO 2012157643A1
Authority
WO
WIPO (PCT)
Prior art keywords
cosmetic
cosmetic composition
slurry
composition
cosmetics
Prior art date
Application number
PCT/JP2012/062416
Other languages
English (en)
French (fr)
Inventor
喜輝 鹿又
弘康 成岡
茂起 松村
建太郎 小中
光信 山本
めぐみ 小野澤
Original Assignee
日本製紙パピリア株式会社
株式会社コーセー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=47176960&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2012157643(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 日本製紙パピリア株式会社, 株式会社コーセー filed Critical 日本製紙パピリア株式会社
Priority to JP2013515165A priority Critical patent/JP5981912B2/ja
Publication of WO2012157643A1 publication Critical patent/WO2012157643A1/ja

Abstract

　化粧料を保持するための化粧料保持体(1)であって、化粧料保持体は、基材(2)を所望の立体形状に成形し、一定の形状を保持する。

Description

化粧料保持体、化粧料保持体を用いた化粧料、及び化粧料の製造方法
　本発明は、化粧料保持体、化粧料保持体を用いた化粧料、及び化粧料の製造方法に係り、詳しくはファンデーション、頬紅、口紅等の化粧料を保持するのに好適な立体に成形された化粧料保持体、立体に成形された化粧料保持体を用いた化粧料、及び化粧料の製造方法に関する。
　ファンデーション、アイシャドウ、頬紅等の化粧料は、宣伝のため新聞や雑誌の広告に掲載されることがある。このような広告では、読み手への印象をより強く残したり、遊び心を刺激して関心を起こさせたりするために、化粧料には色合い等だけでなく、見栄えの良さを求められることが多い。そのため、化粧業界では様々な工夫をしており、例えば化粧料の容器の形状や化粧料自体に工夫がなされている。
　化粧料への工夫として、例えば、化粧料容器に充填された固形状の化粧料は、その表面にレーザ光を用いて加飾模様を形成することや（特許文献１参照）、粉体化粧料にバインダーを混合して球状に固形成型する（特許文献２参照）ことで、より美しさや面白さを出すものがあった。
　一方、携帯性を向上させたり、化粧料のサンプルとして台紙に化粧料を塗布した技術がある（特許文献３、特許文献４参照）。従来、このような台紙に化粧料を塗布させる目的として、携帯用、サンプル配布用として利用されており、化粧料容器や塗布具の代わりとなることが多かった。そのため、台紙は通常の化粧料と同様に平面であり、その平面上に化粧料を塗布するものであった。
特開２００６－６２９８０号公報 特開平６－１９２０３７号公報 特許２７０８６９０号公報 特公平７－１４８５６号公報
　しかしながら、上記特許文献１では、加飾模様を形成する化粧料にある程度の大きさと厚さとが求められ、加飾模様を形成することのできる化粧料の形状に限りがあり、また平面に形成されたものになってしまう。また、上記特許文献２のように化粧料を球状にすると、これらの集合体を化粧料とする場合、化粧料の輸送時、また使用中に、形状が欠けたり崩れたりすることをある程度防止することはできるものの、形状を複雑にすると、立体形状の角がぶつかり合って割れてしまうことがあり、形状を維持することが困難である。また、厚みのない形状にすると、集合体にしなくても形状を維持することは困難である。
　本発明は、上述した課題を解決すべくなされたものであり、その目的とするところは、所望の種々の形状に成形しても化粧料の形状を維持することができ、化粧料を保持することのできる化粧料保持体を提供すること、このような化粧料保持体を使用して化粧料としての品質を保持しながら２種類以上の配色も可能な化粧料を提供すること、及びこのような化粧料保持体の製造方法を提供することにある。
　上記の目的を達成するべく、請求項１の化粧料保持体は、化粧料を保持するための化粧料保持体であって、前記化粧料保持体は、基材を所望の立体形状に成形し、一定の形状を保持してなることを特徴とする。
　請求項２の化粧料保持体は、請求項１において、前記基材は、シート状の基材であることを特徴とする。
　請求項３の化粧料保持体は、請求項１または２において、前記基材は、少なくとも熱可塑性樹脂繊維を含有する不織布であることを特徴とする。
　請求項４の化粧料保持体は、請求項１または２において、前記基材は、少なくとも熱可塑性樹脂繊維を含有する布であることを特徴とする。
　請求項５の化粧料保持体は、請求項１または２において、前記基材は、熱可塑性樹脂からなる樹脂フィルムであることを特徴とする。
　請求項６の化粧料保持体は、請求項１乃至５のいずれかにおいて、前記基材は、多孔性であることを特徴とする。
　請求項７の化粧料保持体は、請求項１乃至６のいずれかにおいて、前記化粧料保持体は、熱プレス及び真空成形の少なくともいずれかで成形されることを特徴とする。
　請求項８の化粧料は、請求項１乃至７のいずれかに記載の化粧料保持体に化粧料組成物が保持されていることを特徴とする。
　請求項９の化粧料は、請求項８において、前記化粧料組成物が、着色顔料を含有することを特徴とする。
　請求項１０の化粧料は、請求項８または９において、前記化粧料保持体には、複数色の化粧料組成物が保持されていることを特徴とする。
　請求項１１の化粧料は、請求項８乃至１０のいずれかにおいて、前記化粧料保持体に接着剤を塗布し、前記化粧料組成物を保持させることを特徴とする。
　請求項１２の化粧料の製造方法は、化粧料組成物を揮発性の溶媒と混合して化粧料スラリーを調製し、該化粧料スラリーに請求項１乃至７のいずれかに記載の化粧料保持体を浸漬することで保持させた後、前記揮発性の溶媒を除去することを特徴とする。
　請求項１３の化粧料の製造方法は、化粧料組成物を揮発性の溶媒と混合して化粧料スラリーを調製し、該化粧料スラリーを請求項１乃至７のいずれかに記載の化粧料保持体に吹き付けて保持させた後、前記揮発性の溶媒を除去することを特徴とする。
　請求項１４の化粧料の製造方法は、請求項１２または１３において、さらに、前記化粧料保持体に前記化粧料スラリーを吹き付けて保持させた後、前記揮発性の溶媒を除去することを特徴とする。
　請求項１５の化粧料の製造方法は、化粧料組成物を加熱溶解してペースト状または液状とし、該ペースト状または該液状の化粧料組成物を請求項１乃至７のいずれかに記載の化粧料保持体に浸漬、または吹き付けにより保持させた後、冷却固化することを特徴とする。
　請求項１の化粧料保持体によれば、化粧料保持体は基材を立体成形して形成されるので、様々な基材を用いて多様な立体形状の化粧料保持体を得ることができる。
　請求項２の化粧料保持体によれば、化粧料保持体はシート状の基材なので、容易に成形加工でき、様々な立体形状の化粧料保持体を得ることができる。
　請求項３乃至５の化粧料保持体によれば、シート状の基材は少なくとも熱可塑性樹脂繊維を含有する不織布、少なくとも熱可塑性樹脂繊維を含有する布、または熱可塑性樹脂からなる樹脂フィルムであるので、このような基材に熱を加えて立体形状に加工することで、化粧料組成物を保持させても、立体形状を維持することのできる化粧料保持体を得ることができる。
　請求項６の化粧料保持体によれば、多孔性の基材を使用して化粧料保持体を形成し、化粧料保持体に化粧料を塗布、浸漬、または吹き付けることによって、基材の空孔内に化粧料組成物を担持させることができる。
　請求項７の化粧料保持体によれば、化粧料保持体は熱プレス及び真空成形の少なくともいずれかで成形されるので、化粧料担持体の形状を立体的に成形することができると共に、保持安定性の高い化粧料担持体を得ることができる。従って、化粧料として使用しても型くずれが起こりにくく、美粧性の高い化粧料を得ることができる。特に、不織布を使用するのが好ましく、不織布を使用して化粧料保持体を形成することで、化粧料保持体の形状安定性をより向上させることができる。
　請求項８の化粧料によれば、立体成形された化粧料保持体に化粧料組成物が保持されるので、装飾性が高く、美粧性を有する化粧料を得ることができる。また、使用者がスポンジ、ブラシ、はけ、筆等の化粧用小道具を使用して化粧料を擦り取って使用しても、化粧料担持体の形状が維持されるので、美粧性を維持することができる。
　請求項９の化粧料によれば、化粧料組成物に着色顔料が含有されるので、装飾性が高く、美粧性を有する化粧料を得ることができる。
　請求項１０の化粧料によれば、立体成形された化粧料保持体に複数色の化粧料組成物を保持させることで、装飾性が高く、美粧性を有する化粧料を得ることができる。また、使用者がスポンジ、ブラシ、はけ、筆等の化粧用小道具を使用して化粧料を擦り取って使用しても、化粧料担持体の形状が維持されるので、美粧性を維持することができる。また、複数色の化粧料組成物を化粧料保持体にそれぞれ保持させるようにすれば、より美粧性を向上させることができる。
　請求項１１の化粧料によれば、化粧料保持体に接着剤を塗布した後に、化粧料組成物を保持させるので、化粧料組成物が厚く形成されることがあっても、化粧料組成物が化粧料保持体に接着剤を介して保持されるので、運搬時の衝撃等による化粧料の脱落を低減することができる。
　請求項１２の化粧料の製造方法によれば、立体成形された化粧料保持体に、揮発性の溶媒と混合してスラリー状に調製した化粧料組成物を浸漬して保持させて溶剤を除去することにより、化粧料保持体の形状に沿って化粧料組成物が保持されるので、美粧性の高い化粧料を得ることができる。
　請求項１３の化粧料の製造方法によれば、立体成形された化粧料保持体に、スラリー状に調製した化粧料組成物を吹き付けて保持させて溶剤を除去することにより、化粧料保持体の形状に沿って化粧料組成物が保持されるので、美粧性の高い化粧料を得ることができる。
　請求項１４の化粧料の製造方法によれば、化粧料組成物が保持された化粧料保持体にさらに化粧料スラリーを吹き付けて保持させることにより、複数色の化粧料組成物を化粧料保持体に保持させることが可能であり、装飾性が高く、美粧性を有する化粧料を得ることができる。
　請求項１５の化粧料の製造方法によれば、化粧料組成物を加熱溶解してペースト状または液体状として化粧料保持体に浸漬または吹き付けて保持させ、冷却固化することにより、化粧料保持体の立体形状に沿って化粧料組成物が保持されるので、美粧性の高い化粧料を得ることができる。
本発明の実施形態に係る化粧料保持体を形成するために使用されるシート状基材の概略図である。 本発明の実施形態に係る化粧料保持体の一例を示す斜視図である。 熱プレス機の概略構成を示す斜視図である。 熱プレス機の作動状態を示す斜視図である。 折り加工の一例を示す概略図である。 折り加工の他の一例を示す概略図である。 真空成形における、シート状基材の加熱状態を表す概略構成図である。 真空成形機を示す概略構成図である。 本発明の実施形態における化粧料の製造工程を示すフローチャートである。 シート状基材の裁断を示す概略構成図である。 図８に示す工程での化粧料保持体の状態を示す、成形工程を行った後の化粧料保持体の上面図である。 図８に示す工程での化粧料保持体の状態を示す、１回目の化粧料保持工程を行った後の化粧料の上面図である。 図８に示す工程での化粧料保持体の状態を示す、２回目の化粧料保持工程を行った後の化粧料の上面図である。 図８に示す工程において、化粧料が保持された化粧料保持体を乾燥させる状態を示す概略図である。 本発明の実施形態の変形例における化粧料の製造工程を示すフローチャートである。 図１２に示す成形工程を行った後の化粧料保持体の状態を示す上面図である。 図１２に示す接着剤塗布工程を行った後の化粧料保持体の状態を示す上面図である。 図１２に示す１回目の化粧料保持工程を行った後の化粧料保持体の状態を示す上面図である。 図１２に示す２回目の化粧料保持工程を行った後の化粧料保持体の状態を示す上面図である。 化粧料保持体の概略図である。 図１４ＡのXIV－XIV線に沿う断面図である。 図１４Ａの化粧料保持体に化粧料が保持された化粧料の概略図である。 図１５ＡのXV－XV線に沿う断面図である。 実施例２１で作成した立体形状の化粧料の上面図である。 実施例２１で作成した２種類の化粧料を重ねて得た立体形状の化粧料の上面図である。
　以下、本発明に係る化粧料保持体、化粧料保持体を使用した化粧料、及び化粧料保持体の製造方法の実施形態について図面を参照しながら説明する。
　図１Ａは、本発明の実施形態に係る化粧料保持体を成形するために用いられるシート状基材の概略図、図１Ｂは、本発明の実施形態に係る化粧料保持体Ｘの一例を示す斜視図である。化粧料保持体Ｘは、シート状基材（基材）を裁断、立体成形して成形される。本実施形態では、例としてシート状基材を花弁に立体成形して化粧料保持体Ｘを形成するが、化粧料保持体Ｘの形状は後述するように花弁に限定されるものではない。シート状基材は、立体成形できる基材であれば特に限られないが、例えば、不織布、布、または樹脂フィルムとするのが好ましい。
（不織布）
　シート状基材として使用される不織布は、少なくとも熱可塑性樹脂繊維を含有して構成されている。このような不織布は、パルプを含んでいてもよい。不織布を構成するパルプとして、製紙用に用いられる木材系パルプ、非木材系パルプ、再生セルロース繊維等がある。木材パルプとして、例えば、針葉樹クラフトパルプ、広葉樹クラフトパルプ、溶解パルプ、マーセル化パルプ等がある。非木材系パルプとして、例えば、亜麻パルプ、マニラ麻パルプ、ケナフパルプ等がある。再生セルロース繊維として、例えば、ビスコースレーヨン、銅アンモニアレーヨン、リヨセル（登録商標）等がある。
　一方、熱可塑性樹脂繊維として、例えば、ポリプロピレン、低密度ポリエチレン、高密度ポリエチレン、綿状低密度ポリエチレン、プロピレンとエチレン、及びプロピレンとブテン－１，４－メチルペンテン－１等との二元または多元共重合体である共重合ポリプロピレン等のポリオレフィン系樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、テレフタル酸及びイソフタル酸の少なくともいずれか一方を加えて共重合した低融点ポリエステル等のポリエステル系樹脂、ナイロン６、ナイロン６６等のポリアミド系樹脂、ポリエチレン、ポリウレタンエラストマー、ポリエステルエラストマー、ポリテトラフルオロエチレン等がある。また、ポリプロピレン及びポリエチレン、ポリプロピレン及びポリエステル、及び高融点ポリエステル及び低融点ポリエステル等の組み合わせからなるサイドバイサイド型複合繊維や、芯鞘型複合繊維等を用いてもよい。
　このようなパルプと熱可塑性樹脂繊維の配合比率は、パルプが０～８０質量％（以下、単に「％」とする）、熱可塑性樹脂繊維が２０～１００％とするのが好ましい。熱可塑性樹脂繊維の配合比率を２０％以上とすることで、シート状基材の成型性が向上する。一方、熱可塑性樹脂繊維の配合比率が２０％未満になると、シート状基材としての成形性が低下するため、好ましくない。
　不織布の製造方法としては、ウェブを形成する工程、及び形成したウェブを結合する工程の２つがある。ウェブを形成する方法としては、繊維と水とを混ぜ合わせて抄紙方式で形成する湿式法、繊維をシート状に形成する乾式法、溶出した樹脂を紡糸するスパンボンド法、スパンボンド法の一種で、繊維に高温のエアを噴出させてさらに細い繊維にするメルトブロー法等がある。湿式法では、円網抄紙機、短網抄紙機、長網抄紙機、及びこれらのコンビネーションマシンを使用して不織布が製造される。特に、繊維の地合がよい円網抄紙機、短網抄紙機、または抄き網として円網、短網を組み合わせて抄き合わせるのが好ましい。一方、ウェブを結合する方法としては、高圧の水流で繊維を絡ませるスパンレース法、接着剤を使用して繊維交点を接着させるケミカルボンド法、針で突き刺して繊維を絡ませるニードルパンチ法等がある。
　上述した製造方法で製造された不織布は、坪量が１５～５００ｇ／ｍ２、好ましくは３０～２００ｇ／ｍ２、さらに好ましくは５０～１００ｇ／ｍ２であるのがよい。不織布の坪量が１５ｇ／ｍ２未満では、不織布の強度が低下し、成形物の剛度が低下してしまい、化粧料の使用時に形状を保持できないため好ましくない。また、不織布の坪量が５００ｇ／ｍ２を超えると、後述するスラリー状にした化粧料を化粧料保持体Ｘに保持させる工程において、スラリーに含まれる溶媒が化粧料保持体Ｘの内部に選択的に吸収され、化粧料粉末と溶媒とが分離してしまうため、化粧料保持体Ｘに保持された化粧料の表面が粗くなり外観を損なってしまい好ましくない。
（不織布の加工条件）
　不織布から化粧料保持体Ｘを立体成形する方法として、熱プレス、または折り加工等の方法を使用することができる。特に、後述する熱プレスによる加工は、化粧料保持体Ｘの形状安定性が向上するため好ましい。
　ここで、熱プレス及び折り加工について以下に説明する。まず、熱プレスについて述べる。図２にプレス機の概略図を示すように、化粧料保持体Ｘとして所望する形状の凸型の金型４と凹型の金型６とを準備する。金型４、６の材質は、真鍮、アルミニウム、鉛等の金属である。特に、耐久性及び安全性の面から、真鍮が好ましい。このような金型４、６を電熱ヒータなどの加熱手段８ａ、８ｂを有するプレス機１０に設置し、使用するシート状基材の成形に適した温度まで加熱する。金型４、６を加熱後、金型４、６の間にシート状基材を挟み、図３に示すようにシート状基材を所定の圧力及び時間でプレスし、化粧料保持体Ｘを成形する。
　上述した熱プレスで不織布を化粧料保持体Ｘに立体成形する場合、不織布を熱プレス機１０で化粧料保持体Ｘに加工する際の熱プレス機１０の金型４、６の温度は、８０～２５０℃、印加する圧力は０．５～３ｋｇ／ｃｍ２であるのがよく、この温度及び圧力の下で不織布を０．２～１０秒間加熱及び加圧するのがよい。なお、不織布に含有される熱可塑性樹脂繊維の融点、及び不織布の坪量等に合わせて、温度、圧力、加熱及び加圧時間は適宜変更される。
　折り加工は、シート状基材を折りたたむことによって所望の形状を成形するものである。折り加工は、所望の形状に応じて種々選択可能であり、折り加工をすることで、シート状基材が立体成形される。例えば、図４に示すような鶴の折り加工としてもよいし、図５に示すような花の折り加工としてもよい。折り加工では、折り目をアイロンのような熱プレス機で熱圧処理することによって、形状を保持することが可能となる。なお、折り加工はこれらに限られない。
（布）
　シート状基材として使用される布は、少なくとも熱可塑性樹脂繊維を含有して構成されている。布を製造するために使用する繊維として、綿、絹、麻、ウール、カシミヤ、及びモヘア等の天然繊維、ナイロン、ポリエステル、ポリウレタン、ポリプロピレン、及びアクリル等の合成繊維、レーヨン、及び再生ポリエステル等の再生繊維等がある。また、布に含まれる熱可塑性樹脂繊維としては、ナイロン、ポリエステル、ポリウレタン、アクリル、再生ポリエステル、ポリプロピレン等を使用する。これらの繊維を使用して、平織り、綾織り、及び朱子織り等の織物、平編み、ゴム編み、及びパール編み等の編み物、レース、及びフェルト等に製造される。
（布の加工条件）
　布から化粧料保持体Ｘを成形するための加工方法として、熱プレス、折り加工等が使用される。特に、熱プレスによる加工は、化粧料保持体Ｘの形状安定性が向上するため好ましい。
　布を図２に示す熱プレス機１０で化粧料保持体Ｘに加工する際の熱プレス機１０の各設定は、金型４、６の温度を８０～２５０℃、印加する圧力を０．５～８ｋｇ／ｃｍ２とし、この温度及び圧力の下で布を０．２～１０秒間加熱及び加圧するのがよい。なお、布を構成する繊維の種類、布に含有される熱可塑性樹脂繊維の融点、及び布の坪量等に合わせて、温度、圧力、加熱及び加圧時間は適宜変更される。
（樹脂フィルム）
　シート状基材として使用される樹脂フィルムは、熱可塑性樹脂からなる。熱可塑性樹脂フィルムとして、例えば、ポリエステル、ポリアミド、ポリプロピレン、プリエチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、またはその共重合体等がある。
（樹脂フィルムの加工方法）
　樹脂フィルムから化粧料保持体Ｘを成形するための加工方法として、熱プレス、真空成形、折り加工等が使用される。特に、熱プレスまたは真空成形による加工は、化粧料保持体Ｘの成形性がよく、好ましい。折り加工を使用する場合は、折り目をアイロンのような熱プレス機で熱圧処理することによって、形状を保持することが可能となる。
　樹脂フィルムを熱プレス機１０で化粧料保持体Ｘに加工する際の熱プレス機１０の各設定は、金型４、６の温度を１００～１８０℃、印加する圧力を０．５～８ｋｇ／ｃｍ２とし、この温度及び圧力の下で樹脂フィルムを０．２～１０秒間加熱及び加圧するのがよい。なお、樹脂フィルムである熱可塑性樹脂フィルムの種類に応じて、温度、圧力、加熱及び加圧時間は適宜変更される。
　真空成形について図６、図７から説明する。図６は、真空成形において、シート状基材２を加熱する概略構成図、図７は真空成形の概略構成図をそれぞれ示している。図６に示すように、シート状基材２をヒータ等の上側加熱手段１２、及び下側加熱手段１４を使用して、シート状基材２の成形に適した温度までシート状基材２を、例えば１２０～２００℃の範囲で設定された温度で加熱して軟化させる。次に、真空成形機１６に所望の形状の型１８を配置し、型１８の上側にシート状基材２を配置する。ここで、型１８は、木型、金型、樹脂型、石膏型等から選択される。そして、真空成形機１６は、シート状基材２と型１８との間の空気を下から吸引して型１８に密着させ、シート状基材２を型１８の形状に成形する。その後、シート状基材２を所定の温度、例えば７０℃未満になるまで冷却して、化粧料保持体Ｘを成形する。なお、図７で型１８は凸型としているが、これに限られない。また、図７に示した真空成形機１６でシート状基材２を加熱して軟化させるようにしてもよい。
（化粧料組成物）
　本発明の化粧料組成物に用いられる粉体は、通常、化粧料に用いられる粉体であれば、球状、板状、針状等の形状や煙霧状、微粒子、顔料級等の粒子径、または多孔質、無孔質等の粒子構造等によって特に限定されず、無機粉体類、光輝性粉体類、有機粉体類、色素粉体類、金属粉体類、複合粉体類等を使用することができる。具体的な粉体としては、酸化チタン、酸化亜鉛、酸化セリウム、硫酸バリウム等の白色無機顔料、ベンガラ、黄色酸化鉄、黒色酸化鉄、カーボンブラック、黒色酸化チタン、酸化クロム、水酸化クロム、紺青、群青等の有色無機顔料、タルク、白雲母、金雲母、紅雲母、黒雲母、合成雲母、絹雲母（セリサイト）、合成セリサイト、カオリン、炭化珪素、スメクタイト、酸化アルミニウム、酸化マグネシウム、酸化ジルコニウム、酸化アンチモン、珪ソウ土、ケイ酸アルミニウム、メタケイ酸アルミニウムマグネシウム、ケイ酸カルシウム、ケイ酸バリウム、ケイ酸マグネシウム、炭酸カルシウム、炭酸マグネシウム、ヒドロキシアパタイト、窒化ホウ素、二酸化珪素等の白色体質粉体、二酸化チタン被覆雲母、二酸化チタン被覆合成金雲母、二酸化チタン被覆オキシ塩化ビスマス、酸化鉄被覆雲母、酸化鉄被覆雲母チタン、紺青処理雲母チタン、カルミン処理雲母チタン、オキシ塩化ビスマス、魚鱗箔、二酸化チタン被覆ガラス末、アルミニウムパウダー等の光輝性粉体、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末、ポリエチレンテレフタレート・ポリオレフィン積層フィルム末、ポリエチレンテレフタレート・ポリメチルメタクリレート積層フィルム末、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末等の樹脂積層末のラメ剤、ポリアミド系樹脂、ポリエチレン系樹脂、ポリアクリル系樹脂、ポリエステル系樹脂、フッ素系樹脂、セルロース系樹脂、ポリスチレン系樹脂、スチレン－アクリル共重合樹脂等のコポリマー樹脂、ポリプロピレン系樹脂、シリコーン樹脂、ウレタン樹脂等の有機高分子樹脂粉体、Ｎ－アシルリジン等の有機低分子性粉体、澱粉、シルク粉体、セルロース粉末等の天然有機粉体、赤色２０１号、赤色２０２号、赤色２０５号、赤色２２６号、赤色２２８号、橙色２０３号、橙色２０４号、青色４０４号、黄色４０１号等の有機顔料粉体、赤色３号、赤色１０４号、赤色１０６号、橙色２０５号、黄色４号、黄色５号、緑色３号、青色１号等のジルコニウム、バリウムまたはアルミニウムレーキ等の有機顔料粉体、またはさらにアルミニウム粉、金粉、銀粉等の金属粉体、微粒子酸化チタン被覆雲母チタン、微粒子酸化亜鉛被覆雲母チタン、硫酸バリウム被覆雲母チタン、酸化チタン含有二酸化珪素、酸化亜鉛含有二酸化珪素等の複合粉体等を例示することができる。なお、これらの粉体は、フッ化系化合物、シリコーン系化合物、金属石鹸、レシチン、水素添加レシチン、コラーゲン、炭化水素、高級脂肪酸、高級アルコール、エステル、ワックス、ロウ、界面活性剤等の中の１種または２種以上を用いて表面処理を施していてもよい。
　この中でも、発色性のある着色顔料を配合することで、化粧料の立体形状のみならず、色彩による美しさを演出することができるため好ましい。具体的には、酸化チタン、酸化亜鉛、酸化セリウム、硫酸バリウム等の白色無機顔料、酸化鉄、カーボンブラック、酸化クロム、水酸化クロム、紺青、群青等の有色無機顔料、二酸化チタン被覆雲母、二酸化チタン被覆合成金雲母、二酸化チタン被覆オキシ塩化ビスマス、酸化鉄雲母チタン、紺青処理雲母チタン、カルミン処理雲母チタン、オキシ塩化ビスマス、魚鱗箔、二酸化チタン被覆ガラス末等の光輝性粉体、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末、ポリエチレンテレフタレート・ポリオレフィン積層フィルム末、ポリエチレンテレフタレート・ポリメチルメタクリレート積層フィルム末、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末等の樹脂積層末のラメ剤、赤色２０１号、赤色２０２号、赤色２０５号、赤色２２６号、赤色２２８号、橙色２０３号、橙色２０４号、青色４０４号、黄色４０１号等の有機顔料粉体、赤色３号、赤色１０４号、赤色１０６号、橙色２０５号、黄色４号、黄色５号、緑色３号、青色１号等のジルコニウム、バリウム、またはアルミニウムレーキ等の有機顔料粉体、またはさらにアルミニウム粉、金粉、銀粉等の金属粉体、微粒子酸化チタン被覆雲母チタン、微粒子酸化亜鉛被覆雲母チタン、硫酸バリウム被覆雲母チタン、酸化チタン含有二酸化珪素、酸化亜鉛含有二酸化珪素等の複合粉体等を例示することができる。なお、これらの粉体は、フッ素系化合物、シリコーン系化合物、金属石鹸、レシチン、水素添加レシチン、コラーゲン、炭化水素、高級脂肪酸、高級アルコール、エステル、ワックス、ロウ、界面活性剤等の中の１種または２種以上を用いて表面処理を施していてもよい。
　化粧料組成物における全粉体中における着色顔料は０．０１％以上が好ましい。化粧料組成物中の粉体の含有量は、特に限定されず、所望する化粧料や化粧料組成物を化粧料保持体に保持させる場合の状態にもよるが、例えば、化粧料組成物を加熱溶解して保持させる場合は、化粧料組成物中の０．１～５０％が好ましく、さらに１～４０％が好ましい。また、粉体を主体として揮発性の溶媒と混合して保持させる場合は、化粧料組成物中の５０％～１００％が好ましく、さらに６０～９０％が好ましい。油剤を主体として揮発性の溶媒と混合して保持させる場合は、化粧料組成物中の０．１～５０％が好ましく、さらに１～４０％が好ましい。この範囲であると、化粧料の取れや肌への付着性の面で特に優れた効果を得ることができる。なお、本発明において、化粧料とは、化粧料保持体Ｘに上述した化粧料組成物を保持させたものである。
　また、化粧料組成物において粉体が主体となる場合は、タルク、マイカ、セリサイト等を含むことが好ましい。これらの粉体を配合することで、取れや強度の面で特に優れた効果を得ることができる。
　本発明に用いられる化粧料組成物は、さらに、油剤、界面活性剤、水性成分、保湿剤、紫外線吸収剤、酸化防止剤、防腐剤、香料、美容成分等の通常化粧料に汎用される成分の配合が可能である。油ゲル化剤、水溶性高分子、トリメチルシロキシケイ酸等の油溶性被膜形成剤、水性成分、パラオキシ安息香酸誘導体、フェノキシエタノール等の防腐剤、ビタミン類、美容成分、香料等の成分を配合することも可能である。
　油剤としては、通常、化粧料に用いられる油剤であれば特に限定されない。具体的には、パラフィンワックス、セレシンワックス、オゾケライト、マイクロクリスタリンワックス、モンタンワックス、フィッシャトロプシュワックス、ポリエチレンワックス、流動パラフィン、スクワラン、ワセリン、ポリイソブテン、ポリブテン等の炭化水素類、カルナウバロウ、ミツロウ、ラノリンワックス、キャンデリラ等の天然ロウ類、トリベヘン酸グリセリル、ロジン酸ペンタエリスリットエステル、ホホバ油、セチルイソオクタネート、パルミチン酸オクチルドデシル、ミリスチン酸イソプロピル、トリオクタン酸グリセリル、トリイソステアリン酸ジグリセリル、リンゴ酸ジイソステアリル、ジペンタエリトリット脂肪酸エステル、マカデミアナッツ油脂肪酸フィトステリル等のエステル類、ステアリン酸、ベヘニン酸等の脂肪酸類、セタノール、ステアリルアルコール、ベヘニルアルコール等の高級アルコール類、オリーブ油、ヒマシ油、ミンク油、モクロウ等の油脂類、ラノリン脂肪酸イソプロピル、ラノリンアルコール等のラノリン誘導体類、Ｎ－ラウロイル－Ｌ－グルタミン酸ジ（コレステリル・ベヘニル・オクチルドデシル）等のアミノ酸誘導体類、ジメチルポリシロキサン、メチルフェニルポリシロキサン、アルキル変性オルガノポリシロキサン、アルコキシ変性オルガノポリシロキサン、高級脂肪酸変性オルガノポリシロキサン、フッ素変性オルガノポリシロキサン等のシリコーン化合物類、パーフルオロポリエーテル、パーフルオロデカン、パーフルオロオクタン等のフッ素系油剤類、デキストリン脂肪酸エステル、蔗糖脂肪酸エステル、デンプン脂肪酸エステル、イソステアリン酸アルミニウム、ステアリン酸カルシウム等の油性ゲル化剤類等が挙げられ、これらの１種または２種以上を用いることができる。
　化粧料組成物中の油剤の含有量は、特に限定されず、所望する化粧料や化粧料組成物を化粧料保持体に保持させる場合の状態にもよるが、例えば、化粧料組成物を加熱溶解して保持させる場合は、化粧料組成物中の５０～９９．９％が好ましく、さらに６０～９９％が好ましい。また、油剤を主体として揮発性の溶媒と混合して保持させる場合は、化粧料組成物中の５０～９９．９％が好ましく、さらに６０～９９％が好ましい。粉体を主体として揮発性の溶媒と混合して保持させる場合は、化粧料組成物中の０～５０％が好ましく、さらに１０～４０％が好ましい。この範囲であると、化粧料の取れや肌への付着性の面で特に優れた効果を得ることができる。
　また、化粧料組成物を加熱して保持させる場合、全油剤中の固形油剤、半固形油剤は、１～５０％が好ましく、さらに５～３０％が好ましい。また、全油剤中の液状油剤は、５０～９９％が好ましく、さらに７０～９５％が好ましい。この範囲であると、化粧料の取れや肌への付着性の面で特に優れた効果を得ることができる。
　界面活性剤としては、化粧料に用いられている界面活性剤であれば何れのものでも使用することができ、非イオン性界面活性剤、アニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤等が挙げられる。例えば、ステアリン酸、ラウリン酸のような脂肪酸の無機及び有機塩、グリセリン脂肪酸エステル及びそのアルキレングリコール付加物、ポリグリセリン脂肪酸エステル及びそのアルキレングリコール付加物、ソルビタン脂肪酸エステル及びそのアルキレングリコール付加物、ポリオキシエチレン硬化ヒマシ油、ポリオキシアルキレンアルキル共変性オルガノポリシロキサン、ポリエーテル変性オルガノポリシロキサン、レシチン等が挙げられる。このような界面活性剤を化粧料組成物に配合する配合量は０．００１～１０％が好ましく、より好ましくは０．０１～１％である。この範囲であると、外観の発色がよく、この点で特に優れた効果を得ることができる。
　水性成分はモイスチャー効果を付与する目的で用いることができ、水及び水に可溶な成分であれば何れでもよく、水の他に、例えば、エチルアルコール等のアルコール類、プロピレングリコール、１，３－ブチレングリコール、１，２－ペンタンジオール、ジプロピレングリコール、ポリエチレングリコール等のグリコール類、グリセリン、ジグリセリン、ポリグリセリン等のグリセロール類、アロエベラ、ウイッチヘーゼル、ハマメリス、キュウリ、レモン、ラベンダー、ローズ等の植物抽出液が挙げられる。
　水溶性高分子としては、グアーガム、コンドロイチン硫酸ナトリウム、ヒアルロン酸ナトリウム、アラビアガム、アルギン酸ナトリウム、カラギーナン等の天然系の物質、メチルセルロース、ヒドロキシエチルセルロース、カルボキシメチルセルロース等の半合成系の物質、カルボキシビニルポリマー、アルキル付加カルボキシビニルポリマー、ポリアクリル酸ナトリウム等の合成系の物質を挙げることができる。
　紫外線吸収剤としては、例えば、２－ヒドロキシ－４－メトキシベンゾフェノン－５－スルホン酸等のベンゾフェノン系、パラジメチルアミノ安息香酸２－エチルヘキシル等のＰＡＢＡ系、パラメトキシケイ皮酸２－エチルヘキシル等のケイ皮酸系、サリチル酸系等、４－ｔｅｒｔ－ブチル－４’－メトキシジベンゾイルメタン、オキシベンゾン、ジエチルアミノヒドロキシベンゾイル安息香酸ヘキシル、メチレンビスベンゾトリアゾルテトラメチルビチルフェノール、フェニルベンズイミダゾールスルホン酸、ビスエチルヘキシルオキシフェノールメトキシフェニルトリアジン等の紫外線吸収剤が挙げられ、保湿剤としては、例えばタンパク質、ムコ多糖、コラーゲン、エラスチン、ケラチン等が挙げられる。
　酸化防止剤としては、例えばα－トコフェロール、アスコルビン酸等があげられる。美容成分としては、例えばビタミン類、消炎剤、生薬等が挙げられ、防腐剤としては、例えばパラオキシ安息香酸エステル、フェノキシエタノール、１，３－ブチレングリコール、１，２－ペンタンジオール等のグリコール類等が挙げられる。
（化粧料の製造方法）
　次に、上述したような化粧料保持体Ｘを使用した化粧料の製造方法について、図８～図１０Ｄを参照しながら説明する。図８は、化粧料の製造工程を示すフローチャート、図９は、シート状基材２の裁断工程を示す概略構成図、図１０Ａ～図１０Ｄは、図８に示す各工程における化粧料保持体Ｘのそれぞれの状態を表す上面図である。まず、図８のフローチャートに基づいて説明する。
　ステップＳ１では、シート状基材２を所望の形状に裁断する。例えば、図９に示すように、所望の形状に形成した型２０を使用して、シート状基材２に型２０を配置し、プレス機２２で打ち抜き加工するようにしてもよい。
　ステップＳ２では、上記ステップＳ１で裁断したシート状基材２を立体成形して化粧料保持体Ｘを成形する（成形工程）。シート状基材２は上述した不織布、布、樹脂フィルムから選択される。このようなシート状基材２を使用して所望の形状に立体成形することにより、形状安定性の高い化粧料保持体Ｘを得ることができる。
　シート状基材２を立体成形する手法は、シート状基材２の材質に応じて、上述した熱プレス、真空成形、及び折り加工から適宜選択される。化粧料保持体Ｘの形状は、立体成形されるならいずれの形状でもよく、例えば、半球、円錐、円錐台、角錐、角錐台等の立体形、花弁、果実、葉等の植物やその一部、貝殻、宝石、星型、ハート型のような形状、または目、唇、頬等、実際に化粧料を保持する部分の形状としてもよい。このように、様々な形状の化粧料保持体Ｘを成形することが可能である。なお、本実施形態では、図１０Ａに示すように、シート状基材２を花弁に立体成形して化粧料保持体Ｘを成形するものとする。
　ステップＳ３では、上記ステップＳ２で成形された化粧料保持体Ｘに化粧料組成物を保持させる。本発明の化粧料組成物を化粧料保持体Ｘに保持させる方法は、化粧料組成物の種類により適宜選択することができる。化粧料保持体Ｘに保持させる化粧料組成物として、例えば、ファンデーション、頬紅、フェイスパウダー、アイカラー、ボディーパウダー、制汗パウダー等の化粧料組成物、或いは、コンシーラ、口紅、リップクリーム、練り香水等の化粧料組成物がある。なお、以下に説明するように、本発明において、このような化粧料組成物を揮発性の溶媒と混合してペースト状または液状として調製、或いは化粧料組成物をそのまま加熱溶解してペースト状または液状としたものを化粧料スラリーという。このような化粧料組成物は、タルク、雲母、シリカ、プラスチックピグメント等の体質顔料、酸化鉄、酸化チタン、酸化亜鉛等の無機色材を含有する。化粧料組成物に配合されるその他の任意成分として、アルコール、水、香料等が挙げられる。
　例えば、化粧料組成物を溶媒と混合して化粧料スラリーを調製し、これを化粧料保持体Ｘに塗布して保持させ、溶媒を除去することにより製造することができる。溶媒としては、エタノール、イソプロピルアルコール、ヘキサン、イソドデカン、軽質流動パラフィン、環状シリコーン等の揮発性の有機溶剤や、水、エチルアルコール、及びこれらの混合物等の水性溶剤、水中油型乳化組成物等、トルエン、キシレン等の炭化水素系溶剤、酢酸エチル等を挙げることができる。この中で、イソプロピルアルコールを用いることが作業性の点で好ましい。化粧料組成物をスラリー状に調製する場合、化粧料組成物１００質量部に対し、溶媒は１０～３００質量部が好ましく、より好ましくは５０～２００質量部である。この範囲であると、化粧料保持体Ｘに保持する化粧料組成物の保持量を調整する点で特に優れた効果を得ることができる。
　また、上述した溶媒を使用せずに、化粧料組成物を加熱して溶融または軟化させてペースト状または液体状とした化粧料スラリーを化粧料保持体Ｘに塗布して保持させることもできる。例えば化粧料組成物のワックス成分が溶解する温度まで加熱し、化粧料組成物をスラリー状にして化粧料保持体Ｘに保持するようにしてもよい。この際、ワックス成分の溶融温度は化粧料組成物に含まれるワックスに依存するが、例えば３０～１５０℃が好ましい。また、ペースト状または液体状の化粧料組成物を浸漬、または霧化機器による吹き付けにより、化粧料保持体Ｘに化粧料組成物を保持させるようにしてもよい。
　このように、化粧料組成物を溶媒に分散させてスラリー状にした化粧料、または化粧料組成物を加熱溶解してスラリー状にした化粧料組成物を化粧料保持体Ｘに保持させる。保持させる方法として、スラリー状の化粧料組成物に化粧料保持体Ｘを含浸塗布させて保持させるようにしてもよい。他の方法として、スラリー状の化粧料組成物をスプレーガン等の霧化機器に入れて化粧料保持体Ｘに噴霧してもよいし、筆を使用してスラリー状の化粧料を化粧料保持体Ｘに保持させてもよい。
　化粧料組成物を保持させた化粧料保持体Ｘは、保持した化粧料組成物に欠落が生じないよう、図１１に示すように支持体３６の一端部に支持されたクリップ３８で挟持して宙吊りの状態で乾燥機に入れ、化粧料スラリーに調製する際に使用した溶媒を除去することで、スラリー状の化粧料組成物を固化する。他の方法として、加熱溶融してスラリー状にした化粧料組成物が保持された化粧料保持体Ｘを冷却して、スラリー状の化粧料組成物を固化するようにしてもよく、自然乾燥、加温乾燥、真空吸引、吸い取り、圧縮して吸い取り等で行ってもよい。これにより、図１０Ｂに示すように、化粧料保持体Ｘに化粧料組成物２４が固化して形成された化粧料３０が得られる。
　ステップＳ４では、上記ステップＳ３で化粧料組成物が保持された化粧料保持体Ｘに、さらにスラリー状の化粧料組成物を保持させる。スラリー状の化粧料組成物を保持及び固化させる方法は、上記ステップＳ３と同様としてもよいし、または、スラリー状に調製した化粧料組成物を霧化機器で噴霧することで、図１０Ｃに示すように、化粧料組成物２４と化粧料組成物２６のグラデーションが形成された化粧料３１を得ることができる。
　上述したような化粧料組成物を保持させる方法により、単色または複数色の化粧料組成物が保持された化粧料を得ることができる。なお、当該ステップＳ４は行わなくてもよい。
　このように、本実施形態によれば、所望の形状に裁断したシート状基材２を立体形成して形状安定性の高い化粧料保持体Ｘを成形し、スラリー状に調製した化粧料組成物を化粧料保持体Ｘに保持することにより、使用者がスポンジ、ブラシ、はけ、筆等の化粧用小道具を使用して化粧料から化粧料を擦り取っても化粧料保持体Ｘの形状が保たれるので、装飾性が高く、美粧性の高い化粧料を得ることができる。また、複数色の化粧料組成物を化粧料保持体Ｘに保持させることにより、より美粧性の高い化粧料を得ることができる。
　なお、本実施形態の化粧料の製造方法では、上記ステップＳ３及び上記ステップＳ４を行うことで、化粧料保持体Ｘに保持する化粧料組成物の保持量を調整するとしたが、上記ステップＳ３で化粧料保持体Ｘにスラリー状の化粧料組成物を保持させる際に、スラリー状の化粧料の保持量を増やすようにして、化粧料組成物の保持量を調整してもよい。また、化粧料保持体Ｘへの化粧料組成物の保持工程は上記ステップＳ３及び上記ステップＳ４の２回行うとしたが、上記ステップＳ３または上記ステップＳ４を複数回行うようにしてもよいし、上記ステップＳ３、Ｓ４を組み合わせて複数回行うようにして、化粧料組成物の保持量を調整してもよい。
（化粧料の製造方法の変形例）
　上記実施形態の変形例について以下に説明する。この変形例では、上記実施形態に対して、立体成形した化粧料保持体Ｘに接着剤を塗布して保持させた後に化粧料組成物を保持させるという点が異なっており、その他の構成は共通している。従って、共通箇所については説明を省略し、相違点についてのみ説明する。図１２は、化粧料の製造工程の変形例を示すフローチャート、図１３は、図１２の工程における化粧料保持体Ｘの状態を表す上面図である。まず、図１２に示すフローチャートに基づいて以下に説明する。
　ステップＳ１では、シート状基材２を所望の形状に裁断する。続くステップＳ２では、上記ステップＳ１で裁断したシート状基材２を立体成形して化粧料保持体Ｘを成形する（成形工程）。これにより、図１３Ａに示すような化粧料保持体Ｘが立体成形される。
　ステップＳ２１では、立体成形した化粧料保持体Ｘに接着剤を塗布する。本ステップの接着剤は、上述したステップＳ３以降で保持させるスラリー状の化粧料組成物において、化粧料組成物を分散させる溶媒と接触して溶解または膨潤することで接着性が現れるものを使用する。このような接着剤として、アクリル樹脂系、ウレタン樹脂系、ポリ酢酸ビニル樹脂系等のアルコール膨潤性樹脂を主体とする接着剤、ポリビニルピロリドン、エチルセルロース、ヒドロキシプロピルセルロース等のアルコール溶解性高分子を主体とする接着剤が挙げられる。接着後の化粧料組成物の接着性、使用性等から、アルコール膨潤性樹脂を主体とする接着剤を使用するのが好ましい。
　このような接着剤を化粧料保持体Ｘに塗布する際、図１３Ｂに示すように、化粧料保持体Ｘの側縁部を含む一部に接着剤２８を塗布する。接着剤２８を塗布する方法として、化粧料保持体Ｘを接着剤２８に含浸塗布してもよいし、スプレー等の噴霧器を用いて化粧料保持体Ｘの両面に噴霧してもよい。ここで、接着剤２８を塗布した側を下と定義する。
　続くステップＳ３では、上記ステップＳ２で成形された化粧料保持体Ｘにスラリー状の化粧料組成物を保持させ、乾燥または冷却して化粧料組成物を固化する。これにより、図１３Ｃに示すように、化粧料組成物２４が保持された化粧料３２が得られる。ステップＳ４では、上記ステップＳ３で化粧料が保持された化粧料保持体Ｘに、さらにスラリー状の化粧料組成物をスプレーガン等の霧化機器を使用して吹き付け、乾燥または冷却して化粧料組成物を固化する。一例として、化粧料３２の側縁部を含む上部に、グラデーションを形成するように霧化機器を使用してスラリー状の化粧料組成物を吹き付けると、図１３Ｄに示すように、化粧料組成物２４と化粧料組成物２６とでグラデーションが形成された化粧料３３が得られる。なお、当該ステップＳ４は行わなくてもよい。
　このように、化粧料保持体Ｘに接着剤２８を塗布した後にスラリー状の化粧料組成物２４、２６を保持させることにより、化粧料保持体Ｘに保持された化粧料組成物が固化した後に生じる脱落を低減することができる。つまり、化粧料組成物２４及び化粧料組成物２６をそれぞれ保持させた後に宙吊りで固化させると、化粧料保持体Ｘの下側にスラリー状の化粧料組成物が溜まり、そのまま固化すると化粧料保持体Ｘの下側の化粧料組成物が厚くなり割れやすくなるが、化粧料保持体Ｘの下側に接着剤を塗布することにより、その後に保持させるスラリー状の化粧料組成物２４及び化粧料組成物２６の溶媒と接着剤とが混ざり合って、化粧料保持体Ｘの下端部に化粧料組成物が溜まって化粧料組成物が他の部分より厚く形成されても化粧料が接着剤に付着するので、運搬時の衝撃等による化粧料の脱落を抑制することができる。
　なお、上記各実施形態では、化粧料保持体Ｘに保持される化粧料組成物として、単色の化粧料組成物の保持、及び２色の化粧料組成物の保持について説明したが、３色以上の化粧料組成物を保持させるようにしてもよい。
　また、上記各実施形態では、化粧料保持体Ｘとして使用可能な基材として、不織布、布、樹脂フィルムを挙げたが、化粧料保持体Ｘとして例えばパルプモールド等の紙成形物を用いてもよいし、プラスチックを射出成形した成形物を用いてもよい。
　また、上記各実施形態では、化粧料保持体Ｘの成形方法として、熱プレス、真空成形、折り加工を示したが、形状安定性を得ることのできる加工方法であればこれに限られない。
　さらに、上記各実施形態では、化粧料組成物をスラリー状にして用いると説明しているが、化粧料保持体Ｘに接着剤を用いる場合には、接着剤を介して化粧料組成物をそのまま噴霧等の方法で化粧料保持体Ｘに保持させることも可能である。
　また、上記ステップＳ１におけるシート状基材２の裁断では、シート状基材２を型２０で打ち抜く打ち抜き加工で裁断するとしたが、ステップＳ１ではシート状基材２を所定の大きさに裁断し、ステップＳ２で熱プレス及び真空成形のいずれかで立体成形して化粧料保持体Ｘを成形した後に、化粧料保持体Ｘの形状に合わせて余分な部分のシート状基材２を除くようにしてもよい。
　また、立体成形された化粧料保持体Ｘの一部を化粧料保持部とするようにしてもよい。一例として、図１４Ａに、花型に成形された化粧料保持部４０を有する化粧料保持体Ｘ’を示す。化粧料保持体Ｘ’は、上述したシート状基材２を立体成形して形成される。図１４Ｂに図１４ＡのXIV－XIV線に沿う断面図を示すように、化粧料保持部４０は凸状の花型に立体成形されている。
　このような化粧料保持体Ｘ’の化粧料保持部４０にスラリー状の化粧料組成物４４を保持させて、図１５Ａ、図１５Ｂに示す化粧料４６を得ることができる。スラリー状の化粧料組成物４４を保持させる方法は上述した通りである。なお、化粧料保持部４０として立体形成する形状は花型に限られず、上述した種々の形状に立体成形するようにしてもよい。また、化粧料保持体Ｘ’の形状は、図１４Ａ、図１５Ａの形状に限られない。
　以下に示す実施例に従って、本発明をより詳細に説明する。なお、本発明はこれに限定されるものではない。
＜実施例１＞
（化粧料保持体の成形）
　ＮＢＫＰ６６％、２．２ｄｔｅｘ×１０ｍｍのポリプロピレン繊維３２％、ポリビニルアルコールバインダー繊維２％を紙料とし、短網ヤンキー式抄紙機で坪量７０ｇ／ｍ２の湿式不織布、即ちシート状基材を得た。
　ここで得られた湿式不織布を所定の大きさの形状に裁断し、２００℃に加熱した真鍮型を使用して、裁断した湿式不織布を熱プレス機で２ｋｇ／ｃｍ２の圧力で１秒間プレスし、直径３ｃｍ程度の図１に示すような立体に成形された花弁の形状をした化粧料保持体Ａを得た。
＜実施例２＞
（化粧料保持体の成形）
　ポリエステル繊維製の布をシート状基材として準備し、布を所定の大きさの形状に裁断し、１６０℃に加熱した真鍮型を使用して、裁断した布を熱プレス機で２ｋｇ／ｃｍ２の圧力で１秒間プレスし、直径３ｃｍ程度の図１に示すような立体に成形された花弁の形状をした化粧料保持体Ｂを得た。
＜実施例３＞
（化粧料保持体の成形）
　厚さ３００μｍのＡ－ＰＥＴフィルムをシート状基材として準備し、真空成形により図１４に示すような凸状の花型に立体成形された化粧料保持体Ｃを得た。
　実施例１～３でそれぞれ立体成形した化粧料保持体Ａ～Ｃの評価結果を表１に示す。シート状基材を使用して化粧料保持体を成形した場合の成形性［成形性評価］、化粧料保持体のしなりを表す剛度［剛度評価］、化粧料組成物を保持させた場合の表面の性状を表す表面性［表面性評価］についてそれぞれ評価した。成形性評価では、使用した型に従って細部にわたって立体成形できる場合を◎、細部の成形は劣るものの立体成形できる場合を○、細部は成形できないものを△とした。
Figure JPOXMLDOC01-appb-T000001
　表１に示されるように、実施例１の化粧料保持体Ａは、細かいシワ等の細部まで成形型に従った形状に成形されており、成形性が良好であった。また、成形された化粧料保持体Ａは、コシがありしなるため、粉体を主体とした化粧料組成物のような柔らかい化粧料組成物を保持させるために使用するのに適していた。また、実施例１の化粧料保持体Ａに保持された化粧料組成物の表面は滑らかであった。
　実施例２の化粧料保持体Ｂは、成形により型の細部は成形できないが、立体形状に成形することは可能であった。また、成形された化粧料保持体Ｂは、コシが弱く、保持された化粧料組成物をはけで擦り取る際、変形し易いが使用可能であった。また、実施例２の化粧料保持体Ｂに保持された化粧料組成物の表面は、シート状基材の織り目模様を認識できた。
　実施例３の化粧料保持体Ｃは、型の細部の成形性は実施例１よりも劣るが、立体成形可能であった。また、成形された化粧料保持体Ｃは硬く変形しにくいため、油剤を主体とした化粧料組成物のような粘性の高い化粧料組成物を保持させるために使用するのに適していた。また、実施例３の化粧料保持体Ｃに保持された化粧料組成物の表面は滑らかであった。
（頬紅の製造）
　化粧料組成物Ａ（黄色の頬紅）と、後述する表２に示す組成の化粧料組成物Ｂ～Ｈ（赤色の頬紅）とを下記の方法でそれぞれ製造し、化粧料（頬紅）を得た。なお、化粧料組成物Ａの組成は以下の通りである。
（成分）　　　　　　　　　　　　　　　　（％）
１．黄色４号　　　　　　　　　　　　　　０．４
２．黄酸化鉄　　　　　　　　　　　　　　０．１５
３．酸化チタン　　　　　　　　　　　　　２
４．マイカ　　　　　　　　　　　　　　　３
５．シリコーン処理マイカ　　　　　　　残量
６．タルク　　　　　　　　　　　　　　２０
７．セスキイソステアリン酸ソルビタン　　０．２
８．流動パラフィン　　　　　　　　　　１１．８
９．トリオクタン酸グリセリル　　　　　１０
　――――――――――　化粧料組成物１００％
１０．イソプロピルアルコール　　　　１８５部
（化粧料組成物Ａの製造方法）
ａ：成分１～６を均一に混合した。
ｂ：成分７～９を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ａを得た。
（化粧料組成物Ｂ～Ｈの製造方法）
ａ：成分１～５を均一に混合した。
ｂ：成分６～８を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｂ～Ｈを得た。
＜実施例４＞
（化粧料の製造方法）
　化粧料組成物Ｂ（赤色の頬紅）１００部をイソプロピルアルコール１２２部に加えて撹拌し、化粧料スラリーＣを調製した。そして、化粧料保持体Ａを化粧料スラリーＣに含浸塗布して保持させ、８０℃の送風乾燥機内で３分間乾燥して、化粧料Ｈを得た。
＜実施例５＞
（化粧料の製造方法）
　化粧料組成物Ｃ（赤色の頬紅）１００部をイソプロピルアルコール１２２部に加えて撹拌し、化粧料スラリーＤを調製した。そして、化粧料保持体Ａを化粧料スラリーＤに含浸塗布して保持させ、８０℃の送風乾燥機内で３分間乾燥して化粧料Ｉを得た。
　化粧料組成物Ａ（黄色の頬紅）１００部をイソプロピルアルコール１８５部に加えて撹拌し、化粧料スラリーＥを調整した。そして、スプレーガンを用いて、化粧料Ｉの一面の側縁部を含む上端部にグラデーションを形成するように化粧料スラリーＥを噴霧して保持させた後、８０℃の送風乾燥機内で３分間乾燥してイソプロピルアルコールを除去した。乾燥した後、化粧料Ｉの背面の側縁部を含む上端部にスプレーガンを用いてグラデーションを形成するように化粧料スラリーＥを噴霧して保持させた後、８０℃の送風乾燥機内で３分間乾燥してイソプロピルアルコールを除去し、２色の化粧料組成物でグラデーションが形成された、花弁の立体形状の化粧料Ｊを得た。
＜実施例６＞
（接着剤の塗布）
　固形分濃度５％に調製したアクリルエマルジョン系の接着剤に、化粧料保持体Ａの側縁部を含む下端部に含浸塗布し、乾燥させて花弁の立体形状の化粧料保持体Ｆを得た。
（化粧料の製造方法）
　化粧料組成物Ｃ（赤色の頬紅）１００部をイソプロピルアルコール１２２部に加えて撹拌し、化粧料スラリーＤを調製した。そして、化粧料保持体Ａを化粧料スラリーＤに含浸塗布して保持させ、８０℃の送風乾燥機内で３分間乾燥して化粧料Ｋを得た。
　化粧料組成物Ａ（黄色の頬紅）をイソプロピルアルコールに加えて撹拌し、固形分濃度３５％の化粧料スラリーＥを調整した。その後、スプレーガンを用いて、化粧料Ｋの一面の側縁部を含む上端部にグラデーションを形成するように化粧料スラリーＥを噴霧し、８０℃の送風乾燥機内で３分間乾燥した。その後、化粧料Ｋの背面の上端部に、グラデーションを形成するように化粧料スラリーＥをスプレーガンを噴霧して保持させた後、８０℃の送風乾燥機内で３分間乾燥して、２色の化粧料組成物でグラデーションが形成された花弁の立体形状をした化粧料Ｌを得た。
＜実施例７＞
（化粧料の製造方法）
　化粧料組成物Ｂ（赤色の頬紅）１００部をイソプロピルアルコール１２２部に加えて撹拌し、化粧料スラリーＣを調製した。そして、化粧料保持体Ｂに化粧料スラリーＣを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｍを得た。
＜実施例８＞
（化粧料の製造方法）
　化粧料組成物Ｄ（赤色の頬紅）１００部をイソプロピルアルコール１００部に加えて撹拌し、化粧料スラリーＨを調製した。そして、化粧料保持体Ａに化粧料スラリーＨを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｎを得た。
＜実施例９＞
（化粧料の製造方法）
　化粧料組成物Ｅ（赤色の頬紅）１００部をイソプロピルアルコール１００部に加えて撹拌し、化粧料スラリーＩを調製した。そして、化粧料保持体Ａに化粧料スラリーＩを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｏを得た。
＜実施例１０＞
（化粧料の製造方法）
　化粧料組成物Ｆ（赤色の頬紅）１００部をイソプロピルアルコール１００部に加えて撹拌し、化粧料スラリーＪを調製した。そして、化粧料保持体Ａに化粧料スラリーＪを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｐを得た。
＜実施例１１＞
（化粧料の製造方法）
　化粧料組成物Ｇ（赤色の頬紅）１００部をイソプロピルアルコール１００部に加えて撹拌し、化粧料スラリーＫを調製した。そして、化粧料保持体Ａに化粧料スラリーＫを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｑを得た。
＜実施例１２＞
（化粧料の製造方法）
　化粧料組成物Ｈ（赤色の頬紅）１００部をイソプロピルアルコール１００部に加えて撹拌し、化粧料スラリーＬを調製した。そして、化粧料保持体Ａに化粧料スラリーＬを含浸塗布して保持させた後、これを８０℃の送風乾燥機内で３分間乾燥させてイソプロピルアルコールを除去し、化粧料Ｒを得た。
　実施例４～１２で得た頬紅（化粧料Ｈ、Ｊ、Ｌ～Ｒ）は、各２０枚ずつ、それぞれの容器に充填し、頬紅として評価した。
（評価方法）
　２０名の化粧料評価専門パネルに、表２の実施例４～１２で得た頬紅（化粧料Ｈ、Ｊ、Ｌ～Ｒ）を、イ：外観の発色の良さ、ロ：ブラシでの化粧料のとれ、ハ：肌への付着性について、各自が以下の評価基準に従って５段階に評価し、さらに全パネルの評点の平均点を以下の判定基準に従って判定した。なお、ロ、ハの項目については、化粧料評価専門パネルにブラシを用いて実際に使用したときの評価をしてもらった。
（評価基準）
評価結果：評点
非常に良好：５点
良好：４点
普通：３点
やや不良：２点
不良：１点
（判定基準）
評点の平均点：判定
４．５以上：◎
３．５以上～４．５未満：○
１．５以上～３．５未満：△
１．５未満：×
（強度の評価方法）
　ニ：強度については、別途準備した容器に実施例４～１２で得た化粧料Ｈ、Ｊ、Ｌ～Ｒをそれぞれ２０枚ずつ、それぞれの容器に充填した状態で上下に５回振り混ぜ、化粧料保持体からの化粧料組成物の脱落状態を目視にて以下の評価基準に従って５段階評価し、これを５回行ったときの各評点の平均点を以下の判定基準に従って判定した。
（評価基準）
評価結果：評点
変化なし：５点
小さな脱落があるが使用性に問題なし：４点
小さな脱落が目立つ：３点
大きな脱落が目立つ：２点
ほとんど脱落している：１点
（判定基準）
評点の平均点：判定
４．５以上：◎
４以上～４．５未満：○
２以上～４未満：△
２未満：×
　結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　表２に示すように、実施例４～７の頬紅は、イ：発色の良さ、ロ：ブラシでの化粧料のとれ、ハ：肌への付着性の全ての項目で優れた化粧料であった。また、実施例８、９の頬紅は、イ：発色の良さでは実施例４～７の頬紅に若干劣るものの良好であり、ロ：ブラシでの化粧料のとれ、ハ：肌への付着性の項目については優れた化粧料であった。実施例１０～１２の頬紅は、イ：発色の良さの項目では優れているものの、ハ：肌への付着性の項目は他の実施例と比べて若干劣るものの良好な結果となった。
　ニ：強度については、実施例４、６、８、１０～１２で得られた化粧料が優れた結果となった。他の実施例で得られた化粧料は、若干劣るものの強度として使用性に問題のない良好な結果を得ることができた。
（口紅の製造）
＜実施例１３＞
（成分）　　　　　　　　　　　　　　　　　　　　　（％）
１．エチレン・ピロピレンコポリマー（注２）　　　　１０
２．キャンデリラワックス　　　　　　　　　　　　　　１
３．ポリエチレンワックス　　　　　　　　　　　　　　４
４．トリオクタン酸グリセリル　　　　　　　　　　　残量
５．テトラ２－エチルヘキサン酸ペンタエリスリット　１０
６．トリイソステアリン酸ジグリセリル　　　　　　　３５
７．トリイソステアリン酸グリセリル　　　　　　　　　４
８．重質流動イソパラフィン　　　　　　　　　　　　　５
９．シリル化処理無水ケイ酸（注３）　　　　　　　　　１
１０．赤色２０２号　　　　　　　　　　　　　　　　　１
１１．黄色４号　　　　　　　　　　　　　　　　　　　０．５
１２．酸化チタン　　　　　　　　　　　　　　　　　　０．５
１３．黒酸化鉄　　　　　　　　　　　　　　　　　　　０．１
１４．雲母チタン　　　　　　　　　　　　　　　　　　５
１５．酸化チタン被覆ガラス末（注４）　　　　　　　　１
注２：ＥＰ－７００（ニューフェーズテクノロジー社製）
注３：ＡＥＲＯＳＩＬ　Ｒ９７２（日本エアロジル社製）
注４：メタシャイン１０８０ＲＲ（日本板硝子社製）
（製造方法）
ａ：成分１～８を１１０～１２０℃で加熱溶解後、成分９～１５を加えて均一混合し、化粧料組成物Ｉを得た。
ｂ：化粧料組成物Ｉを脱泡後、１１０℃に加熱し、化粧料保持体Ｃの凸状の花型に成形した部分を浸漬して化粧料組成物を保持させ、室温冷却した。
ｃ：ｂを１枚作成し、容器に充填して化粧料Ｓとして口紅を得た。
（評価方法）
　評価方法及び判定結果は上述した評価方法及び判定結果と同様である。結果を表３に示す。なお、化粧料小道具として、口紅用の筆を使用した。
Figure JPOXMLDOC01-appb-T000003
　表３に示すように、実施例１３で得られた口紅は、イ：外観の発色の良さ、ロ：筆での化粧料のとれ、ハ：唇への付着性、ニ：強度の何れの項目でも優れた化粧料を得ることができた。
（ファンデーションの製造）
＜実施例１４＞
（成分）　　　　　　　　　　　　　　　　　　　（％）
１．ベンガラ　　　　　　　　　　　　　　　　　　　１
２．黄酸化鉄　　　　　　　　　　　　　　　　　　　１
３．酸化チタン　　　　　　　　　　　　　　　　　１０
４．酸化亜鉛　　　　　　　　　　　　　　　　　　　３
５．シリコーン処理セリサイト（注５）　　　　　　残量
６．タルク　　　　　　　　　　　　　　　　　　　１５
７．パラメトキシケイ皮酸２－エチルヘキシル　　　　５
８．トリオクタン酸グリセリル　　　　　　　　　　１４
９．ジメチルポリシロキサン（注６）　　　　　　　　４
１０．水添ポリイソブテン　　　　　　　　　　　　　２
１１．防腐剤（ｐ－オキシ安息香酸メチル）　　　　適量
　　　―――――――――――――　化粧料組成物１００％
１２．イソプロピルアルコール　　　　　　　　　１２０部
注５：ジメチルポリシロキサン２％処理
注６：ＫＦ９６Ａ（６ｃｓ）（信越化学工業社製）
（製造方法）
ａ：成分１～６を均一に混合した。
ｂ：成分７～１１を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｊを得た。
ｃ：化粧料組成物Ｊを１００部に、成分１２の揮発性溶媒を１２０部加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ａを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを２５枚作成して容器に充填し、化粧料Ｔとしてファンデーションを得た。
　このようにして得られた実施例１４のファンデーションは、外観の発色の良さ、化粧料のとれ、肌への付着性、強度共に優れる化粧料であった。
（アイカラーの製造）
＜実施例１５＞
（成分）　　　　　　　　　　　　　　　　　　　　　　（％）
１．ベンガラ　　　　　　　　　　　　　　　　　　　　　２
２．黄酸化鉄　　　　　　　　　　　　　　　　　　　　　１
３．酸化チタン　　　　　　　　　　　　　　　　　　　　５
４．オクチルトリエトキシシラン処理タルク（注７）　　２０
５．シリコーン処理セリサイト（注５）　　　　　　　　残量
６．雲母チタン　　　　　　　　　　　　　　　　　　　　５
７．マイクロクリスタリンワックス　　　　　　　　　　　０．５
８．ワセリン　　　　　　　　　　　　　　　　　　　　　２
９．トリオクタン酸グリセリル　　　　　　　　　　　　１３
１０．防腐剤（ｐ－オキシ安息香酸メチル）　　　　　　適量
１１．香料　　　　　　　　　　　　　　　　　　　　　適量
　　　―――――――――――――――　化粧料組成物１００％
１２．イソプロピルアルコール　　　　　　　　　　　１００部
注７：２％処理
（製造方法）
ａ：成分１～７を均一に混合した。
ｂ：成分８～１１を１１０℃に加熱混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｋを得た。
ｃ：化粧料組成物Ｋを１００部に、成分１２の揮発性溶媒を１００部加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ａを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを１０枚作成して容器に充填し、化粧料Ｕとしてアイカラーを得た。
　このようにして得られた実施例１５のアイカラーは、外観の発色の良さ、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
（ボディパウダーの製造）
＜実施例１６＞
（成分）　　　　　　　　　　　　　　　　　（％）
１．シリコーン処理セリサイト（注５）　　　残量
２．タルク　　　　　　　　　　　　　　　　３０
３．無水ケイ酸　　　　　　　　　　　　　　　３
４．リン酸Ｌ－アスコルビルマグネシウム　　　３
５．ジカプリン酸プロピレングリコール　　　１２
６．流動パラフィン　　　　　　　　　　　　１０
７．ジメチルポリシロキサン（注８）　　　　　３
８．防腐剤（ｐ－オキシ安息香酸メチル）　　適量
　　　――――――――――　化粧料組成物１００％
９．イソプロピルアルコール　　　　　　　　９０部
注８：ＫＦ９６Ａ（２０ｃｓ）（信越化学工業社製）
（製造方法）
ａ：成分１～４を均一に混合した。
ｂ：成分６～８を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｌを得た。
ｃ：化粧料組成物Ｌを１００部に、成分９の揮発性溶媒を９０部を加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ｂを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを３０枚作成して容器に充填し、化粧料Ｖとしてボディパウダーを得た。
　このようにして得られた実施例１６のボディパウダーは、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
（練り香水の製造）
＜実施例１７＞
（成分）　　　　　　　　　　　　　　　　　　　　　　　　　　　　　（％）
１．ステアリン酸イヌリン（注９）　　　　　　　　　　　　　　　　　　４
２．（パルミチン酸／２－エチルヘキサン酸）デキストリン（注１０）　１０．５
３．ジメチルポリシロキサン（注８）　　　　　　　　　　　　　　　　１０
４．デカメチルシクロペンタシロキサン　　　　　　　　　　　　　　　　５
５．トリイソステアリン酸ジグリセリル　　　　　　　　　　　　　　　残量
６．流動パラフィン　　　　　　　　　　　　　　　　　　　　　　　　　５
７．無水ケイ酸　　　　　　　　　　　　　　　　　　　　　　　　　　１５
８．香料　　　　　　　　　　　　　　　　　　　　　　　　　　　　　１０
注９：レオパールＩＳＫ２（千葉製粉社製）
注１０：レオパールＴＴ２（千葉製粉社製）
（製造方法）
ａ：成分１～７を９０℃で加熱溶解後、成分８を加えて均一に混合し、化粧料組成物Ｍを得た。
ｂ：化粧料組成物Ｍを脱泡後、９０℃に加熱し、化粧料保持体Ａを浸漬し、室温冷却した。
ｃ：ｂを１０枚作成して容器に充填し、化粧料Ｗとして練り香水を得た。
　このようにして得られた実施例１７の練り香水は、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
（頬紅の製造）
＜実施例１８＞
（成分）　　　　　　　　　　　　　　　　　　　　　　　　　　　（％）
１．ベンガラ　　　　　　　　　　　　　　　　　　　　　　　　　　１
２．赤色２０２　　　　　　　　　　　　　　　　　　　　　　　　　０．８
３．赤色２２６　　　　　　　　　　　　　　　　　　　　　　　　　０．３
４．オクチルトリエトキシシラン処理タルク（注７）　　　　　　　１５
５．マイカ　　　　　　　　　　　　　　　　　　　　　　　　　　残量
６．ベンガラ被覆雲母チタン　　　　　　　　　　　　　　　　　　　５
７．無水ケイ酸・酸化チタン被覆マイカ（注１１）　　　　　　　　　３
８．酸化チタン被覆ガラス末（注１２）　　　　　　　　　　　　　　２
９．酸化チタン被覆合成金雲母（注１３）　　　　　　　　　　　　　１
１０．ミツロウ　　　　　　　　　　　　　　　　　　　　　　　　　１
１１．トリオクタン酸セチル　　　　　　　　　　　　　　　　　　１９
１２．バラ花エキス（１％、１，３－ブチレングリコール水溶液）　　０．１
１３．カカオ脂　　　　　　　　　　　　　　　　　　　　　　　　　０．０１
１４．防腐剤（ｐ－オキシ安息香酸メチル）　　　　　　　　　　　適量
１５．香料　　　　　　　　　　　　　　　　　　　　　　　　　　適量
　　　――――――――――――――――――――　化粧料組成物１００％
１６．イソプロピルアルコール　　　　　　　　　　　　　　　　１００部
注１１：チミロンスプレンディドゴールド（メルク社製）
注１２：メタシャインＭＴ１１２０ＲＳ（日本板硝子社製）
注１３：プロミネンスＹＨ（日本光研工業社製）
（製造方法）
ａ：成分１～９を均一に混合した。
ｂ：成分１０～１５を９０℃に加熱混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｎを得た。
ｃ：化粧料組成物Ｎを１００部に、成分１６の揮発性溶媒を１００部加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ａを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを２０枚作成して容器に充填し、化粧料Ｘとして頬紅を得た。
　このようにして得られた実施例１８の頬紅は、外観の発色の良さ、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
（アイカラーの製造）
＜実施例１９＞
（成分）　　　　　　　　　　　　　　　　　　　　　　　　　　　　　（％）
１．グンジョウ　　　　　　　　　　　　　　　　　　　　　　　　　　　３
２．青色１号　　　　　　　　　　　　　　　　　　　　　　　　　　　　２
３．黄色４号　　　　　　　　　　　　　　　　　　　　　　　　　　　　３
４．シリコーン処理マイカ（注１）　　　　　　　　　　　　　　　　　１０
５．マイカ　　　　　　　　　　　　　　　　　　　　　　　　　　　　残量
６．ベンガラ被覆雲母チタン　　　　　　　　　　　　　　　　　　　　１０
７．酸化鉄・無水ケイ酸被覆アルミニウムフレーク（注１５）　　　　　　５
８．酸化チタン被覆合成金雲母（注１６）　　　　　　　　　　　　　　　５
９．酸化チタン被覆ガラス末（注１７）　　　　　　　　　　　　　　　　１
１０．重質流動イソパラフィン　　　　　　　　　　　　　　　　　　　　１
１１．流動パラフィン　　　　　　　　　　　　　　　　　　　　　　　　９
１２．ジカプリン酸プロピレングリコール　　　　　　　　　　　　　　１５
１３．ラベンダー花エキス（１％、１，３－ブチレングリコール水溶液）　０．１
１４．防腐剤（ｐ－オキシ安息香酸メチル）　　　　　　　　　　　　　適量
１５．香料　　　　　　　　　　　　　　　　　　　　　　　　　　　　適量
　　　―――――――――――――――――――――　化粧料組成物１００％
１６．イソプロピルアルコール　　　　　　　　　　　　　　　　　１１５部
注１５：シコパールファンタスティコゴールド（ＢＡＳＦ社製）
注１６：ＨＥＬＩＯＳ　Ｒ１００S（トピー工業社製）
注１７：メタシャインＭＴ１０８０ＲＢ（日本板硝子社製）
（製造方法）
ａ：成分１～９を均一に混合した。
ｂ：成分１０～１５を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｏを得た。
ｃ：化粧料組成物Ｏを１００部に、成分１６の揮発性溶媒を１１５部加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ａを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを１０枚作成して容器に充填し、化粧料Ｙとして頬紅を得た。
　このようにして得られた実施例１９のアイカラーは、外観の発色の良さ、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
（フェイスパウダーの製造）
＜実施例２０＞
（成分）　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　（％）
１．ベンガラ　　　　　　　　　　　　　　　　　　　　　　　　　　　　　０．２
２．黄酸化鉄　　　　　　　　　　　　　　　　　　　　　　　　　　　　　０．５
３．酸化チタン　　　　　　　　　　　　　　　　　　　　　　　　　　　１０
４．酸化亜鉛・硫酸バリウム被覆セリサイト（注１８）　　　　　　　　　　３
５．セリサイト　　　　　　　　　　　　　　　　　　　　　　　　　　　残量
６．メチレンビスベンゾトリアゾリルテトラメチルブチルフェノール
処理タルク（注１９）　　　　　　　　　　　　　　　　　　　　　　　　　５
７．ジエチルアミノヒドロキシベンゾイル安息香酸ヘキシル（注２０）　　　１
８．エチルヘキシルトリアゾン（注２１）　　　　　　　　　　　　　　　　１
９．ビスエチルヘキシルオキシフェノールメトキシフェニル
トリアジン（注２２）　　　　　　　　　　　　　　　　　　　　　　　　　１
１０．トリオクタン酸グリセリル　　　　　　　　　　　　　　　　　　　１０
１１．パラメトキシケイ皮酸２－エチルヘキシル　　　　　　　　　　　　　３
１２．流動パラフィン　　　　　　　　　　　　　　　　　　　　　　　　　８
１３．ジメチルポリシロキサン（注６）　　　　　　　　　　　　　　　　　２
１４．ハチミツ　　　　　　　　　　　　　　　　　　　　　　　　　　　　０．０１
１５．「防腐剤（ｐ－オキシ安息香酸メチル）　　　　　　　　　　　　　　適量
　　　―――――――――――――――――――――――　化粧料組成物１００％
１６．イソプロピルアルコール　　　　　　　　　　　　　　　　　　　　９０部
注１８：ＳＨＡＤＥ　ＬＥＡＦ　Ａ（メルク社製）
注１９：ＭＢＢＴ-タルクＤＭ（大日本化成社製）
注２０：ＵＶＩＮＵＬ　Ａ　ＰＬＵＳ（ＢＡＳＦ社製）
注２１：ＵＶＩＮＵＬ　Ｔ１５０（ＢＡＳＦ社製）
注２２：ＴＩＮＯＳＯＲＢ　Ｓ（ＢＡＳＦ社製）
（製造方法）
ａ：成分１～９を均一に混合した。
ｂ：成分１０～１５を混合溶解し、ａに加えて均一に混合し、化粧料組成物Ｐを得た。
ｃ：化粧料組成物Ｐを１００部に、成分１６の揮発性溶媒を９０部加えてスラリー状とした。
ｄ：ｃに化粧料保持体Ａを浸漬し、温風乾燥して溶媒を除去した。
ｅ：ｄを２０枚作成して容器に充填し、化粧料Ｚとしてフェイスパウダーを得た。
　このようにして得られた実施例２０のフェイスパウダーは、外観の発色の良さ、化粧料のとれ、肌への付着性、強度共に優れる化粧料であった。
（頬紅の製造）
＜実施例２１＞
（化粧料保持体の成形）
　実施例１に示された化粧料保持体Ａの成型と同様の方法を用い、化粧料保持体Ａより直径が小さい、直径１．５ｃｍ程度の立体に成形された花弁の形状をした化粧料保持体Ｄを得た。
（製造方法）
ａ：実施例１８で使用した化粧料組成物Ｎ１００部をイソプロピルアルコール１００部に加えて撹拌して化粧料スラリーＭを調整した。
ｂ：実施例５で使用した化粧料組成物Ａ（黄色の頬紅）１００部をイソプロピルアルコール１８５部に加えて撹拌して化粧料スラリーＮを調整した。
ｃ：ａに化粧料保持体Ａの一面の側縁部を含む上端部を除いた部分を含浸塗布して保持させ、８０℃の送風乾燥機内で３分間乾燥した。
ｄ：ｃの化粧料スラリーＭが保持されていない部分に接着剤を塗布したものを３枚作成し、それぞれの接着剤を塗布した部分を重ね合わせて接着した。
ｅ：ｄの接着した部分の表面と裏面に、スプレーガンを用いてグラデーションを形成するように化粧料スラリーＮを噴霧して保持させた後、８０℃の送風乾燥機内で３分間乾燥してイソプロピルアルコールを除去し、図１６Ａに示すような２色の化粧料組成物でグラデーションが形成された、花弁を組み合わせた立体形状の化粧料ＡＡを得た。
ｆ：上記ｃ～ｅと同様の方法で、化粧料保持体Ａの代わりに化粧料保持体Ｄを用い、図１６Ａに示すような２色の化粧料組成物でグラデーションが形成された、花弁を組み合わせた立体形状の化粧料ＡＢを得た。
ｇ：化粧料ＡＡの立体形状の内側に化粧料ＡＢをセットし、図１６Ｂに示すような２種類の花弁を複数枚組み合わせた、花の立体形状の化粧料ＡＣを得た。
　このようにして得られた実施例２１の頬紅は、外観の発色の良さ、化粧料のとれ、肌への付着性、強度に優れる化粧料であった。
　　２　シート状基材
　３０～３２、４６　化粧料
　　Ｘ、Ｘ’　化粧料保持体

Claims (15)

  1. 　化粧料を保持するための化粧料保持体であって、
    　前記化粧料保持体は、基材を所望の立体形状に成形し、一定の形状を保持してなることを特徴とする化粧料保持体。
  2. 　前記基材は、シート状の基材であることを特徴とする請求項１に記載の化粧料保持体。
  3. 　前記基材は、少なくとも熱可塑性樹脂繊維を含有する不織布であることを特徴とする請求項１または２に記載の化粧料保持体。
  4. 　前記基材は、少なくとも熱可塑性樹脂繊維を含有する布であることを特徴とする請求項１または２に記載の化粧料保持体。
  5. 　前記基材は、熱可塑性樹脂からなる樹脂フィルムであることを特徴とする請求項１または２に記載の化粧料保持体。
  6. 　前記基材は、多孔性であることを特徴とする請求項１乃至５のいずれかに記載の化粧料保持体。
  7. 　前記化粧料保持体は、熱プレス及び真空成形の少なくともいずれかで成形されることを特徴とする請求項１乃至６のいずれかに記載の化粧料保持体。
  8. 　請求項１乃至７のいずれかに記載の化粧料保持体に化粧料組成物が保持されていることを特徴とする化粧料。
  9. 　前記化粧料組成物が、着色顔料を含有することを特徴とする請求項８に記載の化粧料。
  10. 　前記化粧料保持体には、複数色の化粧料組成物が保持されていることを特徴とする請求項８または９に記載の化粧料。
  11. 　前記化粧料保持体に接着剤を塗布し、前記化粧料組成物を保持させることを特徴とする請求項８乃至１０のいずれかに記載の化粧料。
  12. 　化粧料組成物を揮発性の溶媒と混合して化粧料スラリーを調製し、該化粧料スラリーに請求項１乃至７のいずれかに記載の化粧料保持体を浸漬することで保持させた後、前記揮発性の溶媒を除去することを特徴とする化粧料の製造方法。
  13. 　化粧料組成物を揮発性の溶媒と混合して化粧料スラリーを調製し、該化粧料スラリーを請求項１乃至７のいずれかに記載の化粧料保持体に吹き付けて保持させた後、前記揮発性の溶媒を除去することを特徴とする化粧料の製造方法。
  14. 　さらに、前記化粧料保持体に前記化粧料スラリーを吹き付けて保持させた後、前記揮発性の溶媒を除去することを特徴とする請求項１２または１３に記載の化粧料の製造方法。
  15. 　化粧料組成物を加熱溶解してペースト状または液状とし、該ペースト状または該液状の化粧料組成物を請求項１乃至７のいずれかに記載の化粧料保持体に浸漬、または吹き付けにより保持させた後、冷却固化することを特徴とする化粧料の製造方法。
     
PCT/JP2012/062416 2011-05-18 2012-05-15 化粧料保持体、化粧料保持体を用いた化粧料、及び化粧料の製造方法 WO2012157643A1 (ja)