WO2012043348A1 - 人形毛髪用合成繊維 - Google Patents

人形毛髪用合成繊維 Download PDF

Info

Publication number
WO2012043348A1
WO2012043348A1 PCT/JP2011/071551 JP2011071551W WO2012043348A1 WO 2012043348 A1 WO2012043348 A1 WO 2012043348A1 JP 2011071551 W JP2011071551 W JP 2011071551W WO 2012043348 A1 WO2012043348 A1 WO 2012043348A1
Authority
WO
WIPO (PCT)
Prior art keywords
synthetic fiber
weight
doll hair
shape
doll
Prior art date
Application number
PCT/JP2011/071551
Other languages
English (en)
French (fr)
Inventor
悠 中村
小林　正明
Original Assignee
株式会社カネカ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社カネカ filed Critical 株式会社カネカ
Publication of WO2012043348A1 publication Critical patent/WO2012043348A1/ja

Abstract

　アクリルニトリル30～80重量%と塩化ビニルおよび／または塩化ビニリデン20～70重量%を含むアクリルニトリル系重合体100重量部と、クエン酸エステル系可塑剤10～40重量部を含有する人形毛髪用合成繊維及びその製造方法を提供する。本発明の人形毛髪用合成繊維は、自然な風合いと光沢、優れたスタイリング性、櫛通り性を有する。

Description

人形毛髪用合成繊維
　本発明は、人形毛髪用合成繊維及び、その製造方法に関する。さらに詳しくは、アクリルニトリル系重合体に可塑剤であるアセチルクエン酸トリブチル（ATBC）を添加することにより、自然な光沢、風合いを有し、優れたスタイリング性、櫛通り性を有した人形毛髪用合成繊維に関するものである。
　人形の頭部等に植えられる人形毛髪は、人間の毛髪に近い外観や手触り感、さらには風合い等を有することが求められる。このような人形毛髪用繊維としては、材料にポリプロピレン、ナイロン、塩化ビニリデン系樹脂等を用いたものがよく知られているが、毛髪の外観、風合い、難燃性等に優れることから、アクリル系樹脂を用いた繊維の人形毛髪がよく知られている（特許文献１）。
　近年、玩具会社は、さまざまなヘアデザインの人形を競って開発しており、人形毛髪に対するカール加工性や植毛加工性等の要求精度は高くなる一方である。特に高級人形においては、従来から求められているスタイリング性（毛の散り（Flyaway）が発生せず、纏りやすい性質）はもちろんのこと、それに加えて、自然な光沢や風合い、柔らかな触感、高い櫛通り性を併せ持つ繊維が要望されている。そのため、例えば繊維の繊度に分布を与えることにより、人間の毛髪により近い自然な風合いを実現しようとする発明が開示されている（特許文献２）。
　又、柔らかな触感や櫛通り性の改善について、樹脂に添加する添加剤を変更することにより実現する発明が開示されている（特許文献３）。
　アクリル系樹脂を用いた繊維は、繊維側面の皴により、自然な光沢や風合いを有しながらも、櫛通り性や、スタイリング性には、改善の余地がある。
特公平５－７６８８０号公報 特開２００８－２０４０号公報 特開２００７－３３２４６８号公報
　本発明は、アクリルニトリル系重合体を用いて得られる人形毛髪用合成繊維及び、その製造方法に関し、自然な風合いと光沢、優れたスタイリング性、櫛通り性を有した、人形毛髪用合成繊維を提供することを課題とする。
　本発明は、アクリルニトリル30～80重量%と塩化ビニルおよび／または塩化ビニリデン20～70重量%を含むアクリルニトリル系重合体100重量部と、クエン酸エステル系可塑剤10～40重量部を含有することにより、繊維断面形状を崩さず、繊維側面に不規則で微細な皴を有し、繊維の弾性率を抑えて、自然な風合い、光沢、良好なスタイリング性を有することを特徴とする、人形毛髪用合成繊維を提供するものである。
　又、この人形毛髪用合成繊維は、アクリルニトリル系重合体を用いた繊維であり、単糸繊度が10～120dtexであり、添加剤として、ATBCを加えることを特徴とする。
　さらに、この人形毛髪用合成繊維は、湿式紡糸法において、アクリルニトリル系重合体に対しATBCを加えることを特徴とする製造方法によって作り出されたものである。
　本発明の人形毛髪用合成繊維は、ベタ付き感がなく自然な感触を有し、合成繊維独特のギラギラした光沢がなく、自然な落ち着いた光沢を有し、また、良好な櫛通りとスタイリング性をあわせ持った、より毛髪に近い人形用頭髪として好適に用いることができる。
本発明の実施例１にかかる人形毛髪用合成繊維の側面形状の一例を示す走査型電子顕微鏡写真である。 本発明の実施例２にかかる人形毛髪用合成繊維の側面形状の一例を示す走査型電子顕微鏡写真である。 比較例１にかかる従来の人形毛髪用合成繊維の側面形状の一例を示す走査型電子顕微鏡写真である。 比較例２にかかるアクリルニトリル系共重合体にエポキシ化大豆油を加えた人形毛髪用合成繊維の側面形状の一例を示す走査型電子顕微鏡写真である。
　本発明に使用するアクリルニトリル系重合体は、アクリルニトリル単独重合体と塩化ビニルおよび／または塩化ビニリデン系重合体の混合重合体でもアクリルニトリルと塩化ビニルおよび／または塩化ビニリデンとの共重合体であっても良い。もちろん、アクリルニトリル、塩化ビニル、塩化ビニリデン以外にこれらと共重合可能なビニル系モノマーを共重合せしめた共重合体であっても良い。
　アクリルニトリル系重合体の組成は前記したようにアクリルニトリル30～80重量%と塩化ビニルおよび／または塩化ビニリデン20～70重量%を含むことが好ましく、より好適にはアクリルニトリル40～70重量%と塩化ビニルおよび／または塩化ビニリデン30～60%の組成を挙げることができる。塩化ビニルおよび／または塩化ビニリデンの含量は難燃性を維持するために20重量%以上含有することが好ましい。
　添加されるクエン酸エステル系可塑剤の添加量については、添加量が多すぎる場合、ブリードや紡糸時の断糸、ノズル詰まりを招くため、アクリル二トリル系重合体100重量部に対し、10～40重量部の範囲から、適宜選択することができる。クエン酸エステル系可塑剤添加量の下限値は、好ましくは10重量部以上、より好ましくは15重量部以上、さらに好ましくは20重量部以上である。クエン酸エステル系可塑剤添加量の上限値は、好ましくは40重量部以下、より好ましくは35重量部以下、さらに好ましくは30重量部以下である。
　クエン酸エステル系可塑剤の例として、アセチルクエン酸トリブチル等を好適に用いることができる。
　本発明の実施例１の人形毛髪用合成繊維にかかる繊維側面形状の倍率500倍の走査型電子顕微鏡写真の一例を図１に示す。繊維表面には軸方向に沿って、不規則な形の従来の皴より微細な凹凸を有す。
　表面の凹凸によって光が不規則な方向に反射するため、合成繊維特有のギラギラした光沢が消去され、自然な光沢が得られる。また、この微細な凹凸によってベタツキ感が除去され自然な触感が得られると共に、繊維どうしの絡まりを抑え、良好な櫛通りが得られる。
　本発明のアクリル系樹脂を用いた繊維からなる人形毛髪用合成繊維は、比重に対する繊維の剛性を低下させることにより、スタイリング性、特に毛の散り（Flyaway）を抑制する効果を有する。
　本発明の人形毛髪用合成繊維は植毛用ミシンにて人形頭部に植毛されるためマルチフィラメントであることが好ましい。
　又、単糸繊度は、10～120dtexの太さであることが好ましく、人形毛髪用合成繊維として使用するためには、マルチフィラメントの総繊度は200～2400dtexの範囲が好ましい。
　さらに本発明の人形毛髪用合成繊維の断面形状は、馬蹄形、繭形、L字形、Y字形及び円形などの不規則な形状の断面の中から選ばれた少なくとも１種で構成された断面が使用されるが、特に好ましくは２種以上混合したものが好ましい。かかる不規則な断面形状の繊維が混合することによって、自然な外観や触感の一層の向上が期待できる。
　本発明の人形毛髪用合成繊維は種々の方法によって作りうるが、湿式紡糸方法であることが望ましい。さらには、アクリル二トリル系共重合体を溶解した溶液に、パイプラインホモミキサーやタンク用攪拌機など強攪拌を行うことができる装置を用いて、可塑剤を添加する方法をとることが望ましい。
　以下に実施例を示し、本発明をさらに詳細に説明するが、本発明はこれらの実施例に限定されるものではない。尚、実施例の記載に先立って、評価方法について説明する。
　（実験例１）櫛通り性評価
　塩化ビニルシートでできた、直径2.5cmの球形の人形ヘッドに人形植毛用ミシンを使用して、実施例、比較例それぞれの繊維を植毛した。
　植毛した人形ヘッドを固定し、毛髪を市販ペット用スリッカーブラシを用い人形頭髪の美容専門家５名らによりブラッシングを行い、それを官能評価した。評価基準は以下の通りである。
◎：根元から毛先まで、滑らかに櫛が抜ける。
○：毛先でややひっかかるが、滑らかに櫛が抜ける。
△：毛先でひっかかり、櫛が抜けづらい。
×：根元からひっかかる。
　（実験例２）スタイリング性評価
　塩化ビニルシートでできた、直径2.5cmの球形の人形ヘッドに人形植毛用ミシンを使用して、実施例、比較例それぞれの繊維を植毛した。
　植毛した人形ヘッドを固定し、毛髪を市販ペット用スリッカーブラシを用い人形頭髪の美容専門家５名らによりスタイルのセットを行い、それを官能評価した。評価基準は以下の通りである。
◎：毛の散り（Flyaway）が発生せず、纏る。
○：やや毛の散り（Flyaway）が発生するが、纏る。
△：毛の散り（Flyaway）が発生し、纏まりが悪い。
×：毛の散り（Flyaway）が発生し、纏らない。
　（実験例３）光沢、風合い評価
　塩化ビニルシートでできた、直径2.5cmの球形の人形ヘッドに人形植毛用ミシンを使用して、実施例、比較例それぞれの繊維を植毛した。
　植毛した人形ヘッドを固定し、毛髪を市販ペット用スリッカーブラシを用い人形頭髪の美容専門家５名らにより角度を変えながら人形を観察し、輝きの変化について官能評価を行った。評価基準は以下の通りである。
◎：輝きに変化があり、人毛に近い光沢、風合いを有す。
○：輝きにやや変化があり、人毛に近い光沢、風合いを有す。
△：輝きに変化はあるものの、合成繊維独特の光沢を有す。
×：輝きに変化がなく、合成繊維独特のギラギラとした光沢を有す。
　（実験例４）ヤング率測定
　JIS L1013に記載される繊維の剛性を表す指標を用いて測定した。表１中のヤング率の単位はGPaで表した。
　（実施例１）
　アクリルニトリル50重量%、塩化ビニル49重量%およびメタクリルスルホン酸ソーダ1.0重量%からなるアクリルニトリル系共重合体を、アセトンに溶解し紡糸原液と為した。この紡糸原液に、パイプラインホモミキサーを用いてインラインで、アクリルニトリル系共重合体100重量部あたりATBC20重量部を強攪拌しながら添加し、50m/minにて、0.27mmφ×32孔の紡糸ノズルよりアセトン濃度10%のアセトン‐水系凝固浴に紡出した。ついで常法に従い水洗、乾燥、延伸熱処理を施し、760dtex/32ｆのマルチフィラメントをスプールに巻き取った。得られた人形毛髪用合成繊維は、L字形、Y字形及び扁平形などの不規則な断面形状を有していた。
　得られた人形毛髪用合成繊維について、実験例１から４にしたがって、櫛通り性評価、スタイリング性評価、光沢、風合い評価、ヤング率測定を行った。結果を表１に記した。
　得られた人形毛髪用合成繊維の側面形状の走査型電子顕微鏡写真の一例を図１に示した。得られた人形毛髪用合成繊維の表面には、縦軸方向に沿って多数の微細な凹凸が存在し、輝きに変化があり、人毛に近い光沢、風合いを有していた。
　得られた人形毛髪用合成繊維は、ベタ付き感がなく自然な感触を有し、合成繊維独特のギラギラした光沢がなく、自然な風合いと光沢、優れたスタイリング性、櫛通り性をあわせ持っていた。
　（実施例２）
　アクリルニトリル50重量%、塩化ビニル49重量%およびメタクリルスルホン酸ソーダ1.0重量%からなるアクリルニトリル系共重合体を、アセトンに溶解し紡糸原液と為した。この紡糸原液に、タンク用攪拌機を用いて、アクリルニトリル系共重合体100重量部あたりATBC20重量部を強攪拌しながら添加し、50m/minにて、0.27mmφ×32孔の紡糸ノズルよりアセトン濃度10%のアセトン‐水系凝固浴に紡出した。ついで常法に従い水洗、乾燥、延伸熱処理を施し、760dtex/32ｆのマルチフィラメントをスプールに巻き取った。得られた人形毛髪用合成繊維は、L字形、Y字形及び扁平形などの不規則な断面形状を有していた。
　得られた人形毛髪用合成繊維について、実験例１から４にしたがって、櫛通り性評価、スタイリング性評価、光沢、風合い評価、ヤング率測定を行った。結果を表１に記した。
　得られた人形毛髪用合成繊維の側面形状の走査型電子顕微鏡写真の一例を図２に示した。得られた人形毛髪用合成繊維の表面には、縦軸方向に沿って多数の微細な凹凸が存在し、輝きに変化があり、人毛に近い光沢、風合いを有していた。
　得られた人形毛髪用合成繊維は、ベタ付き感がなく自然な感触を有し、合成繊維独特のギラギラした光沢がなく、自然な風合いと光沢、優れたスタイリング性、櫛通り性をあわせ持っていた。
　（比較例１）
　アクリルニトリル50重量%、塩化ビニル49重量%およびメタクリルスルホン酸ソーダ1.0重量%からなるアクリルニトリル系共重合体を、アセトンに溶解し紡糸原液と為した。この紡糸原液を、50m/minにて、0.27mmφ×32孔の紡糸ノズルよりアセトン濃度10%のアセトン‐水系凝固浴に紡出した。ついで常法に従い水洗、乾燥、延伸熱処理を施し、760dtex/32ｆのマルチフィラメントをスプールに巻き取った。得られた人形毛髪用合成繊維は、L字形、Y字形及び扁平形などの不規則な断面形状を有していた。
　得られた人形毛髪用合成繊維について、実験例１から４にしたがって、櫛通り性評価、スタイリング性評価、光沢、風合い評価、ヤング率測定を行った。結果を表１に記した。
　得られた人形毛髪用合成繊維の側面形状の走査型電子顕微鏡写真の一例を図３に示した。得られた人形毛髪用合成繊維の表面には、縦軸方向に沿って多数の微細な凹凸が存在し、輝きに変化があり、人毛に近い光沢、風合いを有していた。しかし、スタイリング性、櫛通り性の点に難があった。
　（比較例２）
　アクリルニトリル50重量%、塩化ビニル49重量%およびメタクリルスルホン酸ソーダ1.0重量%からなるアクリルニトリル系共重合体を、アセトンに溶解し紡糸原液と為した。この紡糸原液に、タンク用攪拌機を用いてインラインで、アクリルニトリル系共重合体100重量部あたりエポキシ化大豆油20重量部を強攪拌しながら添加し、50m/minにて、0.27mmφ×32孔の紡糸ノズルよりアセトン濃度10%のアセトン‐水系凝固浴に紡出した。ついで常法に従い水洗、乾燥、延伸熱処理を施し、760dtex/32ｆのマルチフィラメントをスプールに巻き取った。得られた人形毛髪用合成繊維は、L字形、Y字形及び扁平形などの不規則な断面形状を有していた。
　得られた人形毛髪用合成繊維について、実験例１から４にしたがって、櫛通り性評価、スタイリング性評価、光沢、風合い評価、ヤング率測定を行った。結果を表１に記した。比較例１と比較すると、櫛通り性にやや改善はみられるものの、光沢が大きく変化し、自然な光沢が失われた。
　得られた人形毛髪用合成繊維の側面形状の走査型電子顕微鏡写真の一例を図４に示した。
Figure JPOXMLDOC01-appb-T000001

Claims (11)

  1. 　アクリルニトリル30～80重量%と塩化ビニルおよび／または塩化ビニリデン20～70重量%を含むアクリルニトリル系重合体100重量部と、クエン酸エステル系可塑剤10～40重量部を含有する人形毛髪用合成繊維。
  2. 　前記クエン酸エステル系可塑剤としてアセチルクエン酸トリブチル（ATBC）を用いることを特徴とする、請求項１に記載の人形毛髪用合成繊維。
  3. 　前記人形毛髪用合成繊維の単糸繊度が10～120dtexである請求項１又は２に記載の人形毛髪用合成繊維。
  4. 　前記アクリルニトリル系重合体が、アクリルニトリル40～70重量%と塩化ビニルおよび／または塩化ビニリデン30～60重量%を含むアクリルニトリル系重合体である請求項１～３のいずれか１項に記載の人形毛髪用合成繊維。
  5. 　前記アクリルニトリル系重合体100重量部と、前記可塑剤15～35重量部を含有する請求項１～４のいずれか１項に記載の人形毛髪用合成繊維。
  6. 　前記アクリルニトリル系重合体100重量部と、前記可塑剤20～30重量部を含有する請求項５に記載の人形毛髪用合成繊維。
  7. 　前記人形毛髪用合成繊維の断面が、馬蹄形、繭形、L字形、Y字形及び円形などの不規則な形状から選ばれる少なくとも１種の形状である請求項１～６のいずれか１項に記載の人形毛髪用合成繊維。
  8. 　前記人形毛髪用合成繊維の断面が、馬蹄形、繭形、L字形、Y字形及び円形などの不規則な形状から選ばれる少なくとも２種の形状である請求項７に記載の人形毛髪用合成繊維。
  9. 　JIS L1013に基づいて測定したヤング率が４GPa以下である請求項１～８のいずれか１項に記載の人形毛髪用合成繊維。
  10. 　前記人形毛髪用合成繊維の繊維断面形状は崩れず、繊維側面の不規則で微細な皴を有し、繊維の弾性率を抑えた、自然な風合い、光沢、良好なスタイリング性を有することを特徴とする、請求項１～９のいずれか１項に記載の人形毛髪用合成繊維。
  11. 　湿式紡糸法を用いることを特徴とする、請求項１～１０のいずれか１項に記載の人形毛髪用合成繊維の製造方法。
PCT/JP2011/071551 2010-09-27 2011-09-22 人形毛髪用合成繊維 WO2012043348A1 (ja)