WO2011048648A1 - 透明導電性積層フィルム - Google Patents

透明導電性積層フィルム Download PDF

Info

Publication number
WO2011048648A1
WO2011048648A1 PCT/JP2009/067984 JP2009067984W WO2011048648A1 WO 2011048648 A1 WO2011048648 A1 WO 2011048648A1 JP 2009067984 W JP2009067984 W JP 2009067984W WO 2011048648 A1 WO2011048648 A1 WO 2011048648A1
Authority
WO
WIPO (PCT)
Prior art keywords
transparent conductive
thin film
film
layer
refractive index
Prior art date
Application number
PCT/JP2009/067984
Other languages
English (en)
French (fr)
Inventor
英生 村上
寿幸 大谷
Original Assignee
東洋紡績株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋紡績株式会社 filed Critical 東洋紡績株式会社
Priority to PCT/JP2009/067984 priority Critical patent/WO2011048648A1/ja
Priority to JP2010515708A priority patent/JP4844692B2/ja
Publication of WO2011048648A1 publication Critical patent/WO2011048648A1/ja

Abstract

本発明は、静電容量式タッチパネル等に使用される電極フィルムにおいて、透明導電性薄膜がパターニングされた際に、透明導電性薄膜の有る部分と無い部分での光学特性の差が小さいため、視認性に優れ、かつパターニングが強調されにくい透明導電性フィルムを提供することを目的とする。本発明は、透明プラスチックフィルムからなる基材上に、高屈折率層、低屈折率層及び透明導電性薄膜層をこの順に積層した構成を有し、高屈折率層の屈折率が１．７０～２．５０、膜厚が４～２０ｎｍの範囲にあり、低屈折率層の屈折率が１．３０～１．６０、膜厚が２０～５０ｎｍの範囲である透明導電性積層フィルムに関する。

Description

透明導電性積層フィルム
　本発明は透明プラスチックフィルムからなる基材上に高屈折率層、低屈折率層及び透明導電性薄膜層をこの順で積層した透明導電性フィルムに関するものである。特に静電容量式タッチパネル等のパターニングされた電極フィルムとして用いた場合、透明導電性薄膜層を有する部分と除去された部分での光学特性の差が小さいため、視認性を向上できる透明導電性フィルムに関するものである。
　透明プラスチックフィルムからなる基材上に、透明でかつ抵抗が小さい薄膜を積層した透明導電性フィルムは、その導電性を利用した用途、例えば、液晶ディスプレイやエレクトロルミネッセンス（ＥＬと略記される場合がある）ディスプレイなどのようなフラットパネルディスプレイや、抵抗膜式タッチパネルの透明電極など、電気、電子分野の用途に広く使用されている。
　近年、静電容量式のタッチパネルが携帯電話、携帯音楽端末などのモバイル機器に搭載されるケースが増えてきた。このような静電容量式のタッチパネルではパターニングされた導体上に誘電体層を積層した構成を有し、指などでタッチすることにより、人体の静電容量を介して接地される。この際、パターニング電極と接地点との間の抵抗値に変化が生じ、位置入力を認識する。しかしながら従来の透明導電性フィルムを用いた場合、透明導電性薄膜層を有する部分と除去された部分での光学特性の差が大きいため、パターニングが目立ち、液晶ディスプレイ等の表示体の前面に配置した際に視認性が低下するという問題があった。
　透明導電性フィルムの透過率または色目を向上させるために、反射防止加工等で用いられている屈折率の異なる層を積層させ光の干渉を利用する方法が提案されている。すなわち、透明導電性薄膜層と基材フィルムの間に屈折率の異なる層を設けて光学干渉を利用する方法が提案されている（特許文献１～３）。
特開平１１－２８６０６６号公報 特許第３６２６６２４号公報 特開２００６－３４６８７８号公報　しかしながら、これらの特許文献１～３記載の透明導電性フィルムは、透明導電性フィルムとしての視認性の改善はできるものの、透明導電性薄膜層をパターニングした際、透明導電性薄膜が有る部分と無い部分とでの光学特性の差を小さくすることは考慮されておらず、パターニングした箇所が目立ってしまう。
　すなわち、本発明の目的は、上記の従来の問題点に鑑み、透明導電性薄膜層を有する部分と除去された部分の光学特性の差を小さくすることによって、液晶ディスプレイ等に使用した際に視認性が良好で、かつパターニングが目立たない透明導電性積層フィルムを提供することにある。
　本発明は、上記のような状況に鑑みなされたものであって、上記の課題を解決することができた透明導電性積層とは、以下の構成よりなる。
１．透明プラスチックフィルムからなる基材上に、高屈折率層、低屈折率層及び透明導電性薄膜層をこの順に積層した構成を有し、高屈折率層の屈折率が１．７０～２．５０、膜厚が４～２０ｎｍの範囲にあり、低屈折率層の屈折率が１．３０～１．６０、膜厚が２０～５０ｎｍの範囲であることを特徴とする透明導電性積層フィルム。
２．透明導電性積層フィルムのＪＩＳ　Ｋ７１０５（１９９９年版）によって規定される０．１２５ｍｍの光学くしを使った場合の透過法の像鮮明度と２．０ｍｍの光学くしを使った場合の透過法の像鮮明度の比が下記（１）式を満たすことを特徴とする１．に記載の透明導電性積層フィルム。
　　０．１２５ｍｍ幅くしの値／２ｍｍ幅くしの値≧０．７　　　　　（１）
３．透明導電性薄膜層が非晶質な金属酸化物薄膜からなることを特徴とする１．又は２．に記載の透明導電性積層フィルム。
４．透明導電性薄膜層が酸化スズの含有率が１０～６０質量％である非晶質なインジウム－スズ複合酸化物であることを特徴とする３．に記載の透明導電性積層フィルム。
５．１．～４．いずれかに記載の透明導電性積層フィルムの透明導電性薄膜層をパターニングした透明導電性積層フィルムの透明導電性薄膜層側に、屈折率が１．４０～１．７０の誘電体層を積層したことを特徴とする透明導電性積層フィルム。
６．５．に記載の透明導電性積層フィルムのパターニングによる透明導電性薄膜層を有する部分と有しない部分の光学特性の差が下記（２）式及び（３）式を満たすことを特徴とする透明導電性積層フィルム。
　　０≦｜Ｔ１－Ｔ０｜≦１．０　　　　（２）
　　０≦｜ｂ１－ｂ０｜≦１．０　　　　（３）
　（Ｔ１：透明導電性薄膜層を有する部分のフィルムの全光線透過率、
　　ｂ１：透明導電性薄膜層を有する部分のフィルムのカラーｂ値、
　　Ｔ０：透明導電性薄膜層を有しない部分のフィルムの全光線透過率、
　　ｂ０：透明導電性薄膜層を有しない部分のフィルムのカラーｂ値）
　本発明の透明導電性積層フィルムは、透明プラスチックフィルムからなる基材上に、高屈折率層、低屈折率層及び透明導電性薄膜層の順に積層した構成を有し、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性の差が小さいため、液晶ディスプレイ等の表示体の前面に配置しても透明導電性薄膜層のパターニングが目立たないため、視認性の低下を抑制できる。
　本発明の透明導電性積層フィルムは、透明プラスチックフィルムからなる基材上に、高屈折率層、低屈折率層及び透明導電性薄膜層をこの順に積層した構成を有する。
　さらに、上記透明導電性積層フィルムの透明導電性薄膜層をパターニングした透明導電性積層フィルムの透明導電性薄膜層側に、誘電体層を積層したことを特徴とする透明導電性積層フィルムである。
　以下、各層別に詳細に説明する。
（透明プラスチックフィルムからなる基材）
　本発明で用いる透明プラスチックフィルムからなる基材とは、有機高分子をフィルム状に溶融押出し又は溶液押出しをしてフィルム状に成形し、必要に応じ、長手方向及び／又は幅方向に延伸、熱固定、熱弛緩処理を施したフィルムである。有機高分子としては、ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリエチレン－２，６－ナフタレート、ポリプロピレンテレフタレート、ナイロン６、ナイロン４、ナイロン６６、ナイロン１２、ポリイミド、ポリアミドイミド、ポリエーテルサルファン、ポリエーテルエーテルケトン、ポリカーボネート、ポリアリレート、セルロースプロピオネート、ポリ塩化ビニール、ポリ塩化ビニリデン、ポリビニルアルコール、ポリエーテルイミド、ポリフェニレンスルフィド、ポリフェニレンオキサイド、ポリスチレン、シンジオタクチックポリスチレン、ノルボルネン系ポリマーなどが挙げられる。
　これらの有機高分子のなかで、ポリエチレンテレフタレート、ポリプロピレンテレフタレート、ポリエチレン－２，６－ナフタレート、シンジオタクチックポリスチレン、ノルボルネン系ポリマー、ポリカーボネート、ポリアリレートなどが好適である。また、これらの有機高分子は他の有機重合体の単量体を少量共重合してもよいし、他の有機高分子をブレンドしてもよい。
　本発明で用いる透明プラスチックフィルムからなる基材の厚みは、１０～３００μｍであることが好ましく、より好ましくは７０～２６０μｍである。プラスチックフィルムの厚みが１０μｍ未満では機械的強度が不足し、透明導電性薄膜のパターン形成工程でのハンドリングが難しくなるため好ましくない。一方、厚みが３００μｍを越えると、タッチパネルの厚みが厚くなりすぎるため、モバイル機器などには適さない。
　本発明で用いる透明プラスチックフィルムからなる基材は、本発明の目的を損なわない範囲で、前記フィルムをコロナ放電処理、グロー放電処理、火炎処理、紫外線照射処理、電子線照射処理、オゾン処理などの表面活性化処理を施してもよい。
　また、本発明で用いる透明プラスチックフィルムからなる基材には、高屈折率層との密着性向上、耐薬品性の付与、オリゴマーなどの低分子量物の析出防止を目的として、硬化型樹脂を主たる構成成分とする硬化物層を設けてもよい。
　前記の硬化型樹脂は、加熱、紫外線照射、電子線照射などのエネルギー印加により硬化する樹脂であれば特に限定されなく、シリコーン樹脂、アクリル樹脂、メタクリル樹脂、エポキシ樹脂、メラミン樹脂、ポリエステル樹脂、ウレタン樹脂などが挙げられる。生産性の観点からは、紫外線硬化型樹脂を主成分とする硬化型樹脂が好ましい。
　このような紫外線硬化型樹脂としては、例えば、多価アルコールのアクリル酸又はメタクリル酸エステルのような多官能性のアクリレート樹脂、ジイソシアネート、多価アルコール及びアクリル酸又はメタクリル酸のヒドロキシアルキルエステルなどから合成されるような多官能性のウレタンアクリレート樹脂などを挙げることができる。必要に応じて、これらの多官能性の樹脂に単官能性の単量体、例えば、ビニルピロリドン、メチルメタクリレート、スチレンなどを加えて共重合させることができる。
　また、高屈折率層と硬化物層との付着力を向上するために、硬化物層を更に表面処理することが有効である。具体的な方法としては、グロー放電又はコロナ放電を照射する放電処理法を用いて、カルボニル基、カルボキシル基、水酸基を増加させる方法、酸又はアルカリで処理する化学薬品処理法を用いて、アミノ基、水酸基、カルボニル基などの極性基を増加させる方法、などが挙げられる。
　紫外線硬化型樹脂は、通常、光重合開始剤を添加して使用される。光重合開始剤としては、紫外線を吸収してラジカルを発生する公知の化合物を特に限定なく使用することができ、このような光重合開始剤としては、例えば、各種ベンゾイン類、フェニルケトン類、ベンゾフェノン類などを挙げることができる。光重合開始剤の添加量は、紫外線硬化型樹脂１００質量部に対して、１～５質量部とすることが好ましい。
　塗布液中の樹脂成分の濃度は、コーティング法に応じた粘度などを考慮して適切に選択することができる。例えば、塗布液中に紫外線硬化型樹脂、光重合開始剤の合計量が占める割合は、通常は２０～８０質量％である。また、この塗布液には、必要に応じて、その他の公知の添加剤、例えば、シリコーン系界面活性剤、フッ素系界面活性剤などのレベリング剤などを添加してもよい。
　本発明において、調製された塗布液は透明プラスチックフィルムからなる基材上にコーティングされる。コーティング法には特に限定されなく、バーコート法、グラビアコート法、リバースコート法などの従来から知られている方法を使用することができる。
　また、硬化物層の厚みは０．１～１５μｍの範囲であることが好ましく、より好ましくは０．５～１０μｍ、特に好ましくは１～８μｍである。硬化物層の厚みが０．１μｍ未満の場合には、十分に架橋した構造が形成されにくくなるため、耐薬品性が低下しやすくなり、オリゴマーなどの低分子量による密着性の低下もおこりやすくなる。一方、硬化物層の厚みが１５μｍを超える場合には、生産性が低下する傾向がある。
　また、硬化物層を設けたフィルムや導電性積層フィルムのすべり性を向上するために、硬化物層に粒子を含有させることも好ましい。この場合は、下記条件を満たすように硬化物層中に粒子を含有させることが好ましい。
　すなわち、ＪＩＳ　Ｋ７１０５（１９９９年版）によって規定される０．１２５ｍｍの光学くしを使った場合の透過法の像鮮明度と２．０ｍｍの光学くしを使った場合の透過法の像鮮明度の比が０．１２５ｍｍ幅くしの値／２ｍｍ幅くしの値≧０．７の範囲に設計することが好ましい。さらに好ましくは０．８以上である。０．７未満の場合には、高精細な液晶ディスプレイ等の表示体の前面に設置した場合、ギラツキ現象が生じるために視認性が低下する。
　硬化物層に含有させる粒子としては特に限定はないが、無機粒子（例えば、シリカ、炭酸カルシウムなど）、耐熱性有機粒子（例えば、シリコン粒子、ＰＴＦＥ粒子、ポリイミド粒子など）、架橋高分子粒子（架橋ＰＳ粒子、架橋アクリル系粒子など）が例示される。これらの粒子の平均粒径（電子顕微鏡法による）は、０．０５～５μｍが好ましく、０．１～２μｍであることがより好ましい。平均粒径が０．０５μｍ未満の場合、粒子を分散させることが困難であり、凝集粒子した粗大粒子が多くなり好ましくない。平均粒径が５μｍを超えると、高精細な液晶ディスプレイ等の表示体の前面に設置した場合、ギラツキ現象が生じるために視認性が低下する場合がある。
（高屈折率層）
　本発明で用いることのできる高屈折率層の屈折率は１．７０～２．５０の範囲であり、好ましくは１．９０～２．３０、より好ましくは１．９０～２．１０である。１．７０未満の場合、低屈折率層との屈折率差が小さすぎるため、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となる。一方、屈折率が２．５０を越える場合、斜め方向のパターニングを目立たなくすることが困難となり、また、工業的に適した材料も存在しない。高屈折率層の具体的素材としては、ＴｉＯ２、Ｎｂ２Ｏ５、ＺｒＯ２、Ｔａ２Ｏ５、ＺｎＯ、Ｉｎ２Ｏ３、ＳｎＯ２等およびこれらの複合酸化物および硫化亜鉛ＺｎＳが挙げられる。これらのなかでも生産性の観点からＺｎＯ、Ｉｎ２Ｏ３、ＳｎＯ２およびこれらの複合酸化物が好ましい。また、これらの酸化物または硫化物に屈折率調整のために任意の酸化物、硫化物を添加しても構わない。
　高屈折率層の膜厚は、４～２０ｎｍであり、好ましくは、７～１５ｎｍ、より好ましくは８～１３ｎｍである。膜厚が４ｎｍ未満の場合、不連続な膜となり、膜の安定性が低下する。一方、膜厚が２０ｎｍを超える場合、光の反射が強くなるため、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となり、液晶ディスプレイ等の表示体の前面に配置した際に透明導電性薄膜層のパターニングが目立ってしまい、視認性が低下する。ただし、高屈折率層の屈折率と膜厚は任意に変えるよりも、光学膜厚（屈折率×膜厚）が一定になるように制御することが好ましい。
　本発明における高屈折率層の成膜方法としては、真空蒸着法、スパッタリング法、ＣＶＤ法、イオンプレーティング法、スプレー法などが知られており、必要とする膜厚に応じて、前記の方法を適宜用いることができるが、膜厚のバラツキを低減するという観点からスパッタリング法が好ましい。
　スパッタリング法では一般的に金属ターゲットから反応性ガスを導入して金属酸化物を作製する反応性スパッタリング法と酸化物ターゲットから金属酸化物をする方法がある。反応性スパッタリング法においては反応性ガスの流量によって成膜速度が急激に変化する遷移領域が存在する。このため膜厚のバラツキを抑制するには酸化物ターゲットを用いることが好ましい。
（低屈折率層）
　本発明で用いる低屈折率層の屈折率は１．３０～１．６０であり、好ましくは１．４～１．１．５５、より好ましくは１．４３～１．５０である。屈折率が１．３０未満の場合、ポーラスな膜となるため、その上に形成した透明導電性薄膜層の電気特性を低下させてしまう。一方、屈折率が１．６０を越える場合、透明導電性薄膜層との光の干渉が弱くなりすぎるため、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となり、液晶ディスプレイ等の表示体の前面に配置した際に透明導電性薄膜層のパターニングが目立ってしまい、視認性が低下する。見え視認性が低下する。
　低屈折率層の具体的素材としては、ＳｉＯ２、Ａｌ２Ｏ３などの透明金属酸化物及びＳｉＯ２－Ａｌ２Ｏ３等の複合金属酸化物、ＣｕＦ２、ＣｅＦ２、ＭｎＦ２、ＭｇＦ２などの金属フッ化物およびこれらの複合フッ化物が挙げられる。また、これらの酸化物またはフッ化物に屈折率調整のために任意の酸化物、硫化物を添加しても構わない。
　低屈折率層の膜厚は、２０～５０ｎｍであり、好ましくは２５～４５ｎｍ、より好ましくは３０～４０ｎｍである。５０ｎｍを超えると透明導電性薄膜層との光の干渉により、波長依存性が強くなりすぎるため、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となる。一方２０ｎｍ未満の場合、透明導電性薄膜層との光の干渉が起こりにくく、透過率を向上することができないため、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となり、液晶ディスプレイ等の表示体の前面に配置した際に透明導電性薄膜層のパターニングが目立ってしまい、視認性が低下する。ただし、低屈折率層の屈折率と膜厚は任意に変えるよりも、光学膜厚（屈折率×膜厚）が一定になるように制御することが好ましい。
　本発明における低屈折率層の成膜方法としては、真空蒸着法、スパッタリング法、ＣＶＤ法、イオンプレーティング法、スプレー法などが知られており、必要とする膜厚に応じて、前記の方法を適宜用いることができるが、膜厚のバラツキを低減するという観点からスパッタリング法が好ましい。一般的にスパッタリングで形成する場合は反応性ＤＣ又はＡＣスパッタリング法が用いられる。成膜速度を向上するためにＤＣ又はＡＣ電源の電圧値を一定に保つように反応性ガス流量を制御するインピーダンス制御又は特定元素のプラズマ中での発光強度を一定に保つように反応性ガス流量を制御するプラズマエミッション法が用いられる。
（透明導電性薄膜層）
　本発明における透明導電性薄膜としては、酸化インジウム、酸化スズ、酸化亜鉛、インジウム－スズ複合酸化物、スズ－アンチモン複合酸化物、亜鉛－アルミニウム複合酸化物、インジウム－亜鉛複合酸化物などが挙げられる。これらのうち、環境安定性や回路加工性の観点から、インジウム－スズ複合酸化物が好適である。
　本発明において透明導電性薄膜層を積層して、透明導電性積層フィルムの表面抵抗値を好ましくは５０～２０００Ω／□、更に好ましくは１００～１５００Ω／□とすることによって、透明導電性積層フィルムとしてタッチパネルなどに使用できる。表面抵抗値が５０Ω／□未満であったり、２０００Ω／□を超える場合、タッチパネルの位置認識精度が悪くなり、好ましくない。
　透明導電性薄膜の膜厚は、４～３０ｎｍの範囲が好ましく、更に好ましくは１０～２５ｎｍである。透明導電性薄膜の膜厚が４ｎｍ未満の場合、連続した薄膜になりにくく、良好な導電性が得られにくくなる。一方、透明導電性薄膜の膜厚が３０ｎｍよりも厚い場合、透明導電性薄膜層をパターニングした際、透明導電性薄膜層を有する部分と有しない部分の光学特性を近づけることが困難となる。
　透明導電性薄膜は、結晶質、非晶質いずれであっても良い。透明導電膜の機械的強度が高いものを求める場合には結晶質であることが好ましい。
　透明導電性薄膜に柔軟性を求める場合や、微細なパターンニング加工等の良好なエッチングを求める場合には、透明導電性薄膜層は非晶質であることが好ましい。結晶質な透明導電性薄膜層を用いた場合、塩酸などで透明導電性薄膜をパターニングする際に溶けにくいため、加工に時間がかかる、微細なパターニングがきれいにできない等の問題が生じる。
　非晶質な透明導電性薄膜層を得るために、ドーパント量を調整することが好ましい。例えば、透明導電性薄膜層としてインジウム－スズ複合酸化物を用いる場合、酸化スズの含有率は１０～６０質量％が好ましく、更に好ましくは２０～５０質量％である。酸化スズ含有率が１０質量％未満の場合、成膜中に結晶化を抑制することが困難となる。一方、酸化スズの含有率が６０質量％を超える場合、ターゲットの密度を向上させることが困難となり、生産中に放電異常が発生しやすくなり生産性の観点から好ましくない。
　また生産性の観点から透明導電性薄膜は高屈折率層と同じ組成であることが好ましい。組成が異なる場合、高屈折率用、透明導電性薄膜用のそれぞれのターゲットおよびカソードが必要となり、設備的にも大掛かりな装置となってしまう。
　透明導電性薄膜の層構造は、単層構造でもよいし、２層以上の積層構造でもよい。２層以上の積層構造を有する透明導電性薄膜の場合、各層を構成する前記の金属酸化物は同一でもよいし、異なっていてもよい。
　本発明における透明導電性薄膜の成膜方法としては、真空蒸着法、スパッタリング法、ＣＶＤ法、イオンプレーティング法、スプレー法などが知られており、必要とする膜厚に応じて、前記の方法を適宜用いることができる。
　例えば、スパッタリング法の場合、酸化物ターゲットを用いた通常のスパッタリング法、あるいは、金属ターゲットを用いた反応性スパッタリング法等が用いられる。この時、反応性ガスとして、酸素、窒素、等を導入したり、オゾン添加、プラズマ照射、イオンアシスト等の手段を併用したりしてもよい。また、本発明の目的を損なわない範囲で、基板に直流、交流、高周波などのバイアスを印加してもよい。
（屈折率が１．４０～１．７０の誘電体層（保護層））
　本発明において屈折率が１．４０～１．７０の誘電体層とは、表示体の部材として透明導電性積層フィルムを使用する際に透明導電性薄膜を保護するために積層する保護層としての目的と、指などでタッチした際の静電容量変化を大きくし、位置入力精度を向上させる目的を併せ持つ層である。
　屈折率が１．４０～１．７０の誘電体層としては、例えば、ＳｉＯ２、Ａｌ２Ｏ３などの透明金属酸化物及びＳｉＯ２－Ａｌ２Ｏ３等の複合金属酸化物、アクリル、シリコーン、ポリエステル系の樹脂からなる有機物等が用いられる。本発明の導電性積層フィルムは、このような誘電体層が設置された状態であってもパターニングが目立ちにくく、視認性に優れる。
（透明導電性積層フィルムの光学特性）
　本願発明においては、透明導電性積層フィルムの透明導電性薄膜層をパターニングしてから、屈折率が１．４０～１．７０の誘電体層を透明導電性薄膜層側に積層した状態において、透明導電性薄膜層を有する部分と有しない部分の光学特性の差が少ないことが重要であり、下記（２）及び（３）式を満たすことが好ましい。
　　０≦｜Ｔ１－Ｔ０｜≦１．０　　　　　（２）
　　０≦｜ｂ１－ｂ０｜≦１．０　　　　　（３）
　（Ｔ１：透明導電性薄膜層を有する部分のフィルムの全光線透過率、
　　ｂ１：透明導電性薄膜層を有する部分のフィルムのカラーｂ値、
　　Ｔ０：透明導電性薄膜層を有しない部分のフィルムの全光線透過率、
　　ｂ０：透明導電性薄膜層を有しない部分のフィルムのカラーｂ値）
　Ｔ１は９０％以上であることが好ましく、さらには９０．５％以上であることが好ましい、ｂ１は－２～２が好ましく、より好ましくは－１．０～１．５であり、さらに好ましくは０～１．５である。
　Ｔ１、ｂ０、Ｔ０、ｂ０は、各層間での反射光の干渉を考慮し、各層の光学厚みを高屈折率層の屈折率は１．７０～２．５０、高屈折率層の膜厚は４～２０ｎｍ、低屈折率層の屈折率は１．３０～１．６０、低屈折率層の膜厚は２０～５０ｎｍの範囲内で調整することにより、達成することができる。
　また、ｂ値は上記調整の中で、分光透過率のピークを４５０～５３０ｎｍの範囲にすることで調整することができる。さらに好ましい分光透過率のピークは４７０～５１０ｎｍである。
　また、透明導電性積層フィルムのＪＩＳ　Ｋ７１０５（１９９９年版）によって規定される０．１２５ｍｍの光学くしを使った場合の透過法の像鮮明度と２．０ｍｍの光学くしを使った場合の透過法の像鮮明度の比が０．７以上であることが好ましい。０．７未満の場合には、高精細な液晶ディスプレイ等の表示体の前面に設置した場合、ギラツキ現象が生じるために視認性が低下してしまう。
　以下、実施例により本発明をさらに詳細に説明するが、本発明はこれらの実施例によりなんら限定されるものではない。なお、透明導電性積層フィルムの性能は、下記の方法により測定した。
（１）全光線透過率
　ＪＩＳ－Ｋ７１３６に準拠し、日本電色工業（株）製、ＮＤＨ－１００１ＤＰを用いて、全光線透過率を測定した。
　なお、（２）式及び（３）式におけるＴ１、Ｔ０は、パターニングした透明導電性積層フィルムに屈折率が１．４０～１．７０の誘電体層を透明導電性薄膜層側に積層した状態において測定した透明導電性薄膜層を有する部分及び透明導電性薄膜層が無い部分の値である。
（２）表面抵抗値
　ＪＩＳ－Ｋ７１９４に準拠し、４端子法にて表面抵抗値を測定した。測定器は、三菱油化（株）製、Ｌｏｔｅｓｔ　ＡＭＣＰ－Ｔ４００を用いた。
（３）カラーｂ値
　ＪＩＳ－Ｋ７１０５に準拠し、色差計（日本電色工業製、ＺＥ－２０００）を用いて、標準の光Ｃ／２でカラーｂ値を測定した。
　なお、（２）式及び（３）式におけるｂ１、ｂ０は、パターニングした透明導電性積層フィルムに屈折率が１．４０～１．７０の誘電体層を透明導電性薄膜層側に積層した状態において測定した透明導電性薄膜層を有する部分及び透明導電性薄膜層が無い部分の値である。
（４）視認性評価
　透明導電性積層フィルムにエッチングレジストを印刷した後、１Ｎ塩酸中に浸漬、アルカリ浸漬により、１×３ｃｍのパターンを形成した。透明導電性薄膜側に屈折率１．５２のアクリル系粘着層を有する二軸配向ポリエチレンテレフタレート（以下ＰＥＴと略記する）フィルムを保護フィルムとして貼り合わせた。富士通社製ＦＭＶ－ＢＩＢＬＯＬＯＯＸ　Ｔ７０Ｍ／Ｔを用いて画面を白色表示にし、保護フィルムを貼り合わせたフィルムをその前に置いて、様々な角度からパターニングの見え方を評価した。
　　○：　パターニングがほとんどみえない。
　　△：　パターニングが少しみえる。
　　×：　パターニングがみえる。
（５）ギラツキ評価
　富士通社製ＦＭＶ－ＢＩＢＬＯＬＯＯＸ　Ｔ７０Ｍ／Ｔを用いて画面を緑色表示にしてフィルムをその前においてギラツキを評価した。
　　○：　ギラツキが全く気にならない。
　　△：　ギラツキがほとんど気にならない。
　　×：　ギラツキが気になる。
（６）像鮮明度
　ＪＩＳ－Ｋ７１０５（１９９９年版）に準拠し、スガ試験機社製ＩＣＭ－１Ｔを用いて、光学くしが０．１２５ｍｍ、２．０ｍｍでの像鮮明度を測定した。
（７）高屈折率層、低屈折率層、透明導電性薄膜層の膜厚
　高屈折率層、低屈折率層、透明導電性薄膜層を積層したフィルム試料片を１ｍｍ×１０ｍｍの大きさに切り出し、電子顕微鏡用エポキシ樹脂に包埋した。これをウルトラミクロトームの試料ホルダに固定し、包埋した試料片の短辺に平行な断面薄切片を作製した。次いで、この切片の薄膜の著しい損傷がない部位において、透過型電子顕微鏡（ＪＥＯＬ社製、ＪＥＭ－２０１０）を用い、加速電圧２００ｋＶ、明視野で観察倍率１万倍にて写真撮影を行って得られた写真から膜厚を求めた。
（８）高屈折率層、低屈折率層、透明導電性薄膜層の屈折率
　シリコンウェハー上に各層をそれぞれ同成膜条件にて作製した試料について分光エリプソメーター（大塚電子株式会社製、ＦＥ－５０００）を用いて５５０ｎｍの屈折率を評価した。また、各層を設けたフィルムの分光透過率測定データに対して光学シミュレーションソフトを用いてフィッティングを行い、屈折率を算出した。この際、各層の膜厚は前記膜厚評価方法により評価した値を用いた。さらにこのように算出した各層の屈折率がシリコンウェハー上の各層の屈折率と大差ないことを確認した。
（９）透明導電性薄膜のエッチング時間
１ｃｍ×１０ｃｍの切り出した透明導電性積層フィルムを４０℃　１Ｎの塩酸水溶液に浸漬し、端子間抵抗値が１ＭΩ以上となる時間を測定した。
〔実施例１〕
　光重合開始剤含有紫外線硬化型アクリル系樹脂（大日精化工業社製、セイカビームＥＸＦ－０１Ｊ）１００質量部に、溶剤としてトルエン／ＭＥＫ（８０／２０：質量比）の混合溶媒を、固形分濃度が５０質量％になるように加え、撹拌して均一に溶解し塗布液を調製した。
　両面に易接着層を有する二軸配向透明ＰＥＴフィルム（東洋紡績社製、Ａ４３４０、厚み１８８μｍ）に、塗膜の厚みが５μｍになるように、調製した塗布液を、マイヤーバーを用いて塗布した。８０℃で１分間乾燥を行った後、紫外線照射装置（アイグラフィックス社製、ＵＢ０４２－５ＡＭ－Ｗ型）を用いて紫外線を照射（光量：３００ｍＪ／ｃｍ２）し、塗膜を硬化させた。次いで、反対面についても同様に塗膜を設けた後、１８０℃で１分間の加熱処理を施して、揮発成分の低減を行った。
　また、この硬化物層を積層した二軸配向透明ＰＥＴフィルムを真空暴露してフィルムの含有水分量を下げるために、真空チェンバー中で巻き返し処理を行った。このときの圧力は０．００２Ｐａであり、暴露時間は２０分とした。また、センターロールの温度は４０℃とした。
　次に、この硬化物層上に高屈折率層としてインジウム－スズ複合酸化物からなる透明導電性薄膜を成膜した。このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとして酸化スズを３６質量％含有した酸化インジウム（住友金属鉱山社製、密度６．９ｇ／ｃｍ３）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加した。また、Ａｒガスを１３０ｓｃｃｍ、Ｏ２ガスを表面抵抗値が最小となるＯ２流量の３倍の流速で流し、０．４Ｐａの雰囲気下でＤＣマグネトロンスパッタリング法を用いて成膜した。ただし、通常のＤＣではなく、アーク放電を防止するために、日本イーエヌアイ製ＲＰＧ－１００を用いて５μｓ幅のパルスを５０ｋＨｚ周期で印加した。また、センターロール温度は０℃として、スパッタリングを行った。
　また、雰囲気の酸素分圧をスパッタプロセスモニター（ＬＥＹＢＯＬＤ　ＩＮＦＩＣＯＮ社製、ＸＰＲ２）にて常時観測しながら、インジウム－スズ複合酸化物薄膜中の酸化度が一定になるように酸素ガスの流量計及びＤＣ電源にフィートバックした。以上のようにして、屈折率１．９６、厚さ１０ｎｍのインジウム－スズ複合酸化物からなる高屈折率層を堆積させた。このようにして得られた高屈折率層の表面抵抗値は１×１０６Ω／□以上であった。
　さらに前記高屈折層上に低屈折率層としてＳｉＯ２薄膜を形成するため、シリコンをターゲットに用いて、直流マグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流した。また、基板の背面には０℃の冷却ロールを設けて、透明プラスチックフィルムを冷却した。このときのターゲットには７．８Ｗ／ｃｍ２の電力を供給し、ダイナミックレートは２３ｎｍ・ｍ／分であった。
　また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ３５ｎｍ、屈折率１．４６の低屈折率層を堆積させた。
　次に、この低屈折率層上にインジウム－スズ複合酸化物からなる透明導電性薄膜を成膜した。このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとして酸化スズを３６質量％含有した酸化インジウム（住友金属鉱山社製、密度６．９ｇ／ｃｍ３）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加した。また、Ａｒガスを１３０ｓｃｃｍ、Ｏ２ガスを表面抵抗値が最小となる流速で流し、０．４Ｐａの雰囲気下でＤＣマグネトロンスパッタリング法を用いて成膜した。ただし、通常のＤＣではなく、アーク放電を防止するために、日本イーエヌアイ製ＲＰＧ－１００を用いて５μｓ幅のパルスを５０ｋＨｚ周期で印加した。また、センターロール温度は１０℃として、スパッタリングを行った。
　また、雰囲気の酸素分圧をスパッタプロセスモニター（ＬＥＹＢＯＬＤ　ＩＮＦＩＣＯＮ社製、ＸＰＲ２）にて常時観測しながら、インジウム－スズ複合酸化物薄膜中の酸化度が一定になるように酸素ガスの流量計及びＤＣ電源にフィートバックした。以上のようにして、厚さ１５ｎｍ、屈折率１．９６のインジウム－スズ複合酸化物からなる透明導電性薄膜を堆積させた。
〔実施例２〕
　透明導電性薄膜層の膜厚を２５ｎｍとする以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔実施例３〕
　硬化物層に平均粒子径１．０μｍのシリカ粒子を添加する以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔実施例４〕
　硬化物層に平均粒子径１０．０μｍのシリカ粒子を添加する以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔実施例５〕
　実施例１において硬化物層上に高屈折率層としてジルコニア－シリコン複合酸化物（ＺｒＯ２－ＳｉＯ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてＺｒＳｉ２（三井金属製）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加し直流マグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ１２ｎｍ、屈折率１．７５の高屈折率層を堆積させた。
〔実施例６〕
　実施例１において硬化物層上に高屈折率層としてチタン酸化物（ＴｉＯ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてＴｉ（三井金属製）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加し直流マグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ８ｎｍ、屈折率２．２９の高屈折率層を堆積させた。
〔実施例７〕
　実施例１において硬化物層上に高屈折率層として硫化亜鉛（ＺｎＳ）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとして硫化亜鉛（三井金属製）に用いて、２Ｗ／ｃｍ２の１３．５６ＭＨｚの高周波電力を印加しマグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ７．５ｎｍ、屈折率２．４３の高屈折率層を堆積させた。
〔実施例８〕
　実施例１において硬化物層上に低屈折率層としてフッ化マグネシウム（ＭｇＦ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてフッ化マグネシウム（三井金属製）に用いて、２Ｗ／ｃｍ２の１３．５６ＭＨｚの高周波電力を印加しマグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ４０ｎｍ、屈折率１．３６の低屈折率層を堆積させた。
〔実施例９〕
　実施例１において硬化物層上に低屈折率層としてアルミニウムーシリコン複合酸化物（Ａｌ２Ｏ３－ＳｉＯ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてＡｌ－Ｓｉ（５０：５０ｗｔ％）（三井金属製）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加しマグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ３５ｍ、屈折率１．５５の低屈折率層を堆積させた。
〔実施例１０〕
　実施例１において透明導電性薄膜の厚さを１０ｎｍとした以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
〔実施例１１〕
　実施例１において透明導電性薄膜をターゲットとして酸化スズを１０質量％含有した酸化インジウム（住友金属鉱山社製、密度７．１ｇ／ｃｍ３）を用いて成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
〔実施例１２〕
　実施例１において透明導電性薄膜をターゲットとして酸化スズを５５質量％含有した酸化インジウム（住友金属鉱山社製、密度６．７ｇ／ｃｍ３）を用いて成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
〔比較例１〕
　高屈折率層、低屈折率層を設けずに、透明導電性薄膜層の膜厚を２２ｎｍとした以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔比較例２〕
　高屈折率層を設けない以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔比較例３〕
　低屈折率層の膜厚を１０ｎｍにした以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔比較例４〕
　低屈折率層の膜厚を１００ｎｍにした以外は実施例１と同様にして透明導電性積層フィルムを作製した。
〔比較例５〕
　実施例１において硬化物層上に高屈折率層としてアルミニウムーシリコン複合酸化物（Ａｌ２Ｏ３－ＳｉＯ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてＡｌ－Ｓｉ（５０：５０ｗｔ％）（三井金属製）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加しマグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ２２ｍ、屈折率１．５５の高屈折率層を堆積させた。
〔比較例６〕
　実施例１において硬化物層上に低屈折率層としてジルコニア－シリコン複合酸化物（ＺｒＯ２－ＳｉＯ２）からなる薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
　このとき、スパッタリング前の圧力を０．０００１Ｐａとし、ターゲットとしてＺｒＳｉ２（三井金属製）に用いて、２Ｗ／ｃｍ２のＤＣ電力を印加し直流マグネトロンスパッタリング法で、真空度を０．２７Ｐａ、ガスとしてＡｒガスを５００ｓｃｃｍ、Ｏ２ガスを８０ｓｃｃｍの流速で流し成膜を行った。また、成膜中の電圧値を常時観測しながら、電圧値が一定となるように酸素ガスの流量計にフィートバックした。以上のようにして、厚さ２９ｎｍ、屈折率１．７５の低屈折率層を堆積させた。
〔実施例１３〕
　実施例１においてターゲットとして酸化スズを５質量％含有した酸化インジウム（住友金属鉱山社製、密度７．１ｇ／ｃｍ３）を用いて結晶質の透明導電性薄膜を成膜した以外は、実施例１と同様にして透明導電性積層フィルムを作製した。
Figure JPOXMLDOC01-appb-T000001
　表１の結果より、本願発明の範囲を満足する実施例１～１３記載の透明導電性積層フィルムは、透明導電性薄膜層をパターニングしても、パターニングされた部分が目立たないため、液晶ディスプレイ等の表示体の前面に配置して用いた際に、視認性に優れるものであった。
　一方、高屈折率層、低屈折率層が適切に配置されていない、又は膜厚が適切でない比較例１～６に記載の透明導電性積層フィルムは、パターニングされた部分が目立つために視認性が劣った。実施例１３は視認性に優れるものであったが透明導電性薄膜が結晶質であるためエッチング時間が長く、パターニング加工に難があった。
　本発明の透明導電性積層フィルムは、透明導電性薄膜層のパターニング部と非パターニング部の光学特性の差が小さく、液晶ディスプレイ等の表示体の前面に配置した際、視認性に優れるため、静電容量式のタッチパネル用の電極フィルムとして特に好適である。
本発明の透明導電性積層フィルムの説明図である。
　　　１０：透明導電性積層フィルム
　　　１１：透明プラスチックフィルム（基材）
　　　１２：硬化物層
　　　１３：高屈折率層
　　　１４：低屈折率層
　　　１５：透明導電性薄膜層
　　　２０：誘電体層

Claims (6)

  1. 　透明プラスチックフィルムからなる基材上に、高屈折率層、低屈折率層及び透明導電性薄膜層をこの順に積層した構成を有し、高屈折率層の屈折率が１．７０～２．５０、膜厚が４～２０ｎｍの範囲にあり、低屈折率層の屈折率が１．３０～１．６０、膜厚が２０～５０ｎｍの範囲であることを特徴とする透明導電性積層フィルム。
  2. 　透明導電性積層フィルムのＪＩＳ　Ｋ７１０５（１９９９年版）によって規定される０．１２５ｍｍの光学くしを使った場合の透過法の像鮮明度と２．０ｍｍの光学くしを使った場合の透過法の像鮮明度の比が下記（１）式を満たすことを特徴とする請求項１に記載の透明導電性積層フィルム。
    　　０．１２５ｍｍ幅くしの値／２ｍｍ幅くしの値≧０．７　　　　　（１）
  3. 　透明導電性薄膜層が非晶質な金属酸化物薄膜からなることを特徴とする請求項１又は２に記載の透明導電性積層フィルム。
  4. 　透明導電性薄膜層が酸化スズの含有率が１０～６０質量％である非晶質なインジウム－スズ複合酸化物であることを特徴とする請求項３に記載の透明導電性積層フィルム。
  5. 　請求項１～４いずれかに記載の透明導電性積層フィルムの透明導電性薄膜層をパターニングした透明導電性積層フィルムの透明導電性薄膜層側に、屈折率が１．４０～１．７０の誘電体層を積層したことを特徴とする透明導電性積層フィルム。
  6. 　請求項５に記載の透明導電性積層フィルムのパターニングによる透明導電性薄膜層を有する部分と有しない部分の光学特性の差が下記（２）式及び（３）式を満たすことを特徴とする透明導電性積層フィルム。
    　　０≦｜Ｔ１－Ｔ０｜≦１．０　　　　（２）
    　　０≦｜ｂ１－ｂ０｜≦１．０　　　　（３）
    　（Ｔ１：透明導電性薄膜層を有する部分のフィルムの全光線透過率、
    　　ｂ１：透明導電性薄膜層を有する部分のフィルムのカラーｂ値、
    　　Ｔ０：透明導電性薄膜層を有しない部分のフィルムの全光線透過率、
    　　ｂ０：透明導電性薄膜層を有しない部分のフィルムのカラーｂ値）
PCT/JP2009/067984 2009-10-19 2009-10-19 透明導電性積層フィルム WO2011048648A1 (ja)