WO2007102341A1 - 抵抗変化型素子、半導体装置、およびその製造方法 - Google Patents
抵抗変化型素子、半導体装置、およびその製造方法 Download PDFInfo
- Publication number
- WO2007102341A1 WO2007102341A1 PCT/JP2007/053610 JP2007053610W WO2007102341A1 WO 2007102341 A1 WO2007102341 A1 WO 2007102341A1 JP 2007053610 W JP2007053610 W JP 2007053610W WO 2007102341 A1 WO2007102341 A1 WO 2007102341A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resistance
- electrode
- resistance change
- layer
- lower electrode
- Prior art date
Description
Claims