WO2007015439A1 - 耐切創性手袋 - Google Patents

耐切創性手袋 Download PDF

Info

Publication number
WO2007015439A1
WO2007015439A1 PCT/JP2006/315081 JP2006315081W WO2007015439A1 WO 2007015439 A1 WO2007015439 A1 WO 2007015439A1 JP 2006315081 W JP2006315081 W JP 2006315081W WO 2007015439 A1 WO2007015439 A1 WO 2007015439A1
Authority
WO
WIPO (PCT)
Prior art keywords
yarn
fiber
rubber
cut
gloves
Prior art date
Application number
PCT/JP2006/315081
Other languages
English (en)
French (fr)
Inventor
Teruyoshi Takata
Original Assignee
Showa Glove Co.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Glove Co. filed Critical Showa Glove Co.
Priority to JP2007529244A priority Critical patent/JP5349797B2/ja
Priority to EP06768388A priority patent/EP1911866B1/en
Publication of WO2007015439A1 publication Critical patent/WO2007015439A1/ja

Abstract

金属の細線と、フィラメント糸からなる添糸とからなる芯材と、該芯材の周りに被覆繊維が巻きつけられた被覆層とからなる複合繊維で作られた手袋の表面がゴム又は樹脂で被覆されていることを特徴とする耐切創性手袋を提供する。本発明の耐切創性手袋は、吸湿性が良好で、着用心地、使用感及び着用時の作業性に優れるとともに、滑り止め性、防水性、強度及び耐切創性に優れている。

Description

明 細 書 耐切創性手袋 技術分野
本発明は耐切創性手袋に関し、 更に詳しくは、 例えば、 鋭利な刃物 を使用する食肉加工作業、 端部の鋭利なガラスや金属板を取り扱うガラ スの製造あるいは加工作業や金属加工作業等において、 作業者保護のた めに用いられる安全防護布、 防護服、 防護エプロン、 防護手袋等の安全 防護製品に用いられる耐切創性手袋に関する。 背景技術
従来、 この種の耐切創性手袋に用いられる繊維として古くは鎧など 金属繊維のみを用いることが特に西洋などでは主流であった。 近年、 軽 量化、 作業性、 強度等の改善を目的として、 金属繊維と綿糸や高強度フ イラメン卜との複合繊維が各種提案されている。
例えば、 日本国特開平 1 - 2 3 9 1 0 4号公報には、 高強力繊維と 針金とからなる芯材に合成繊維を巻き付けて被覆した芯鞘複合糸が提案 され、 実施例として具体的に、 3 , 4 ' —ジアミノジフヱニルエーテル 共重合ポリバラフヱ二レンテレフタルアミ ド繊維とステンレスワイヤー とを芯材とし、 これにナイ口ン繊維を上下二重に巻きつけた芯鞘複合糸 で編成した手袋が開示されている。
また、 日本国特開昭 6 3 - 3 0 3 1 3 8号公報には、 金属繊維の単 線ワイヤー、 フィラメント糸又は紡績糸からなる芯部を芳香族ポリアミ ド繊維のステーブルにより被覆した芯鞘構造の複合紡績糸が提案されて いる。 また、 日本国特開 2 0 0 0 - 1 7 8 8 1 2号公報には、 表面に高強 度 ·高弾性率繊維と金属細線からなる複合糸を配し、 裏面に嵩高加工糸 又は天然繊維を配した耐切創性手袋が提案されている.。
更に、 米国特許第 6， 4 6 7 , 2 5 1号公報には、 ガラス繊維を芯 部とし、 ポリエチレン繊維又はァラミ ド繊維を鞘部とし、 更にポリエス テル、 ナイロン等の非金属で非高性能繊維からなる被覆繊維を互いに反 対方向に巻きつけた耐切創性複合繊維が提案されている。
更に、 米国特許第 6， 2 6 6 , 9 5 1号公報には、 ステンレススチ —ルワイヤ一と抗菌性処理したアセテート系繊維からなる芯部にポリェ ステル繊維を互いに反対方向に巻きつけた耐切創性繊維及び該繊維から なる手袋等のァバレルが提案されている。
更に、 米国特許第 5 , 6 4 4 , 9 0 7号公報には、 互いに平行に （ para l l e l ) 置かれたワイヤストランドと延伸ポリエチレンファイバ一ス 卜ランドからなるコアと、 このコアの周りに互いに反対方向に巻かれた 少なくとも 2 層のス卜ランドで被覆された、 ァラミ ド繊維を使用しない 耐切創性複合繊維が開示されている。
しかしながら、 上記のような従来の複合繊維は、 耐切創性を有する ものの、 吸湿性が悪く、 また、 該複合繊維を用いて手袋等を編成する際 にステンレスワイヤーやガラス繊維が切れる場合があるなど編み加工性 が悪く、 また、 例えば、 該複合繊維で編成した手袋は着用心地、 使用感 が悪く、 特に、 切断したステンレスワイヤーやガラス繊維が肌をチクチ クと剌激し、 手袋着用時の作業性も満足すべきものではない。 特に、 芯 材として用いたステンレススチールワイヤーやガラス繊維が複合繊維の 外部に露出し、 手指を刺激するチクチク感が大きいという問題を含んで いる。
また、 鋭利な刃物等を取り扱う場合には、 手袋の被覆繊維が切れ埃 が発生したり、 また、 防水性がないため、 作業時に水や油等が染み込む といった問題を含んでいる。
本発明はかかる実情に鑑み、 上記のような従来技術の問題点を解消 し、 吸湿性が良好で、 編み加工性に優れた複合繊維を用いた、 伸縮性、 吸湿性が良好で、 着用心地、 使用感及び着用時の作業性に優れるととも に、 滑り止め性、 防水性、 強度及び耐切創性に優れた耐切創性手袋を提 供することを目的とする。 発明の開示
本発明者はかかる問題点を解決するために鋭意研究の結果、 金属の 細線と、 フイラメント糸からなる添糸とからなる芯材と、該芯材の周り に被覆繊維が卷きつけられた被覆層とからなる複合繊維で作られた手袋 の表面がゴム又は樹脂で被覆されていることを特徴とする耐切創性手袋 が上記目的を達成することを見い出した。
更に、 本発明者は、 手袋を編成する際に、 特定の繊維を用いてプレ 一ティングし、 該プレーティング繊維が手袋の内側に配されるように編 成することにより、 伸縮性、 吸湿性、 着用心地、 使用感及び手袋着用時 の作業性を一層改善できることを見い出した。
本発明は、 かかる知見に基づいて完成されたものである。
上記目的を達成するための本発明の請求項 1は、 金属の細線と、 フ イラメント糸からなる添糸とからなる芯材と、 該芯材の周りに被覆繊維 が巻きつけられた被覆層とからなる複合繊維で作られた手袋の表面がゴ ム又は樹脂で被覆されていることを特徴とする耐切創性手袋を内容とす る。
本発明の請求項 2は、 金属の細線がステンレスからなることを特徴 とする請求項 1記載の耐切創性手袋を内容とする。 本発明の請求項 3は、 添糸が、 ポリエチレン、 ポリエステル、 ポリ パラフヱニレンテレフタルアミ ドから選ばれる少なくとも. 1種のフイラ メン卜糸から選ばれることを特徴とする請求項 1又は 2記載の耐切創性 手袋を内容とする。
本発明の請求項 4は、 ポリエチレンが、 超高分子量ポリエチレンで あることを特徴とする請求項 3記載の耐切創性手袋を内容とする。
本発明の請求項 5は、 添糸がポリエステルであることを特徴とする 請求項 3記載の耐切創性手袋を内容とする。
本発明の請求項 6は、 被覆繊維が、 ポリエチレン、 ポリアラミ ド、 ポリエステル、 ポリアミ ド、 アクリル、 綿、 ウールから選ばれる少なく とも 1種の繊維からなることを特徴とする請求項 1〜 5のいずれか 1項 に記載の耐切創性手袋を内容とする。
本発明の請求項 7は、 ポリエステル又はポリアミ ドからなる繊維が 、 捲縮加工されたものであることを特徴とする請求項 6記載の耐切創性 手袋を内容とする。
本発明の請求項 8は、 被覆層が、 第 1の被覆層とこれとは反対方向 に巻きつけられた第 2の被覆層とからなることを特徴とする請求項 1 〜 7のいずれか 1項に記載の耐切創性手袋を内容とする。
本発明の請求項 9は、 添糸が金属の細線に金属の細線 1 m当たり 1 〜 6 0回卷きつけられていることを特徴とする請求項 1 〜 8のいずれか 1項に言己載の耐切創性手袋を内容とする。
本発明の請求項 1 0は、 合成繊維又は天然繊維でプレーティングさ れ、 プレーティングされた繊維が手袋の内側に配されていることを特徴 とする請求項 1〜 9のいずれか 1項に記載の耐切創性手袋を内容とする 本発明の請求項 1 1は、 プレーティング用の合成繊維が、 ポリアミ ド、 ポリエチレン、 ポリエステル、 ポリフヱニレンテレフタルアミ ド、 レーョンから選ばれる少なくとも 1種の合成繊維とポリウレタンとの複 合繊維、 又は、 ポリアミ ド、 ポリエチレン、 ポリエステル、 ポリフヱ二 レンテレフ夕ルァミ ド、 レーヨンから選ばれる少なくとも 1種の合成繊 維からなることを特徴とする請求項 1 0記載の耐切創性手袋を内容とす る。
本発明の請求項 1 2は、 プレーティング用の天然繊維が綿からなる ことを特徴とする請求項 1 0記載の耐切創性手袋を内容とする。
本発明の請求項 1 3は、 ゴムが天然ゴム、 合成ゴム、 それらの変性 体から選ばれる少なくとも 1種であることを特徴とする請求項 1 〜 1 2 のいずれか 1項に記載の耐切創性手袋を内容とする。
本発明の請求項 1 4は、 合成ゴムが二トリルブタジエンゴム、 スチ レンブタジエンゴム、 クロロプレンゴム、 シリコンゴム、 フッ素ゴム、 クロロスルホン化ポリエチレンゴム、 イソプレンゴム、 それらの変性体 から選ばれる少なくとも 1種であることを特徴とする請求項 1 〜 1 3の いずれか 1項に記載の耐切創性手袋を内容とする。
本発明の請求項 1 5は、 樹脂がポリ塩化ビュル、 ポリウレタン、 ェ チレン一ビニルアルコール共重合体、 ポリ酢酸ビュル、 それらの変性体 から選ばれる少なくとも 1種であることを特徴とする請求項 1 〜 1 3の いずれか 1項に記載の耐切創性手袋を内容とする。 図面の簡単な説明
図 1は、 本発明の耐切創性手袋に用いられる複合繊維の一例を示す 概略図である。
図面中、 番号は下記事項を示す。
1 芯材 1 a 金属の細線
1 b 添糸
2 被覆繊維
2 a 第 1層目の被覆繊維
2 b 第 2層目の被覆繊維
3 被覆層
3 a 第 1層目の被覆層
3 b 第 2層目の被覆層 発明を実施するための最良の形態
本発明の耐切創性手袋に用いられる複合繊維は、 図 1に示すように 、 芯材 1 と、 該芯材 1の周りに被覆繊維 2が卷きつけられた被覆層 3と からなる。
前記芯材 1は金属の細線 1 aと、 フィラメント糸からなる添糸 1 b とからなる。
本発明において用いられる金属の細線 1 aは、 高強度、 高弾性率の ステンレス、 チタン、 アルミニウム、 銀、 ニッケル、 銅、 ブロンズ等が 好ましく、 特に、 低コスト、 高強度である点及び化学的に安定で発請し にくい点でステンレスが好ましい。 ステンレスは正しくはステンレスス チールであるが、 国内では一般にステンレス又はステンと略称されるの で、 本発明においてもステンレスと略称する。
なお、 金属の細線 1 aは撚つたものでは硬く、 複合繊維を用いた製 品、 例えば手袋 （以下、 複合繊維を用いた製品の代表例として手袋を取 りあげる） め風合いが悪くなるので、 本発明では非加工の素線を使用す る。
例えば、 ステンレスの細線は、 通常、 かかる用途では 4 0〜 5 mの太さのもが多く使用されている。 本発明における金属の細線 1 aは 、 複合繊維の編み加工性、 手袋使用時の作業性の点で、 1 .0〜 7 O / m が好ましく、 更に 1 5〜 3 5 が好ましい。 ステンレスの材質として は、 S U S 3 0 4が柔らかく曲げに強い点で好ましい。 金属の細線 1 a は 1 ~ 4本が好適で、 より好ましくは 1〜 3本、 更に好ましくは 1〜 2 本である。 4本を超えると手袋が硬くなり、 手袋着用時の作業性が悪く なる点で好ましくない。
芯材の金属の細線 1 aは、 そのまま被覆繊維 2で被覆しょうとする と、 被覆の工程で金属の細線 1 aの切断が発生するため、 添糸 1 bが必 要である。 添糸 1 bは、 撚糸等の加工をした糸では少なからず伸縮性を 持っているので、 非加工のフィラメント糸が使用される。 伸縮性を持つ た糸を添糸 1 bとしてを使用すると、 その後の被覆工程で被覆する糸も 伸縮性を持つことになる。 ところで、 金属の細線 1 aはそれ自体ほとん ど伸縮性を持っていないので、 被覆繊維 2で被覆した後、 複合皞維が伸 ばされたとき、 その伸びに耐え切れず金属の細線 1 aが切断されてしま う。 切断された金属の細線 1 aは、 複合繊維 2の被覆層 3から外に飛び 出し、 例えば、 手袋製品とされたとき手袋使用者の手の肌をチクチクと 刺激し、 着用心地、 使用感が悪化することになる。 上記とは反対に、 糸 1 bに収縮性があるときも同様である。 即ち、 添糸 l bが収縮した場 合、 金属の細線 1 aは収縮しないので撓みが生じることになるが、 この 撓みは逃げ場がないため、 複合繊維 Ϊの被覆層 3から外に飛び出し手袋 使用者の手の肌を刺激し不快感を与えることになる。
従って、 本発明に用いられる添糸 1 bは、 力学的な伸縮だけでなく 、 熱、 薬品の影響による伸縮の少ないフィラメント糸が好ましい。 具体 的には、 ポリエチレン、 強化ポリエチレンである超高分子量ポリエチレ ン （例えば、 商品名： ダイ二一マ、 東洋紡績株式会社製） 、 ポリエステ ル、 ポリバラフヱ二レンテレフタルアミ ド （例えば、 商品名：ケブラ一 、 デュポン社製） 、 液晶ポリマー、 高強力ポリアリレート.（例えば、 商 品名：べクトラン、 株式会社クラレ製） 等のフィラメ ント糸が挙げられ る。 これらの中では、 超高分子量ポリエチレン、 ポリパラフヱニレンテ レフタルアミ ド、 ポリエステルが物理的安定性が非常に高く、 化学的に も安定性が高いの点で好ましい。 これらは単独で又は必要に応じ 2種以 上組み合わせて用いられる。
これら添糸 1 bの太さは、 通常、 5 0〜 6 0 0デニールのものが好 ましく、 1 0 0〜 4 5 0デニールのものがより好ましい。 5 0デニール 未満のものは、 金属の細線 1 aの切断防止効果が弱くなる傾向がある。 また 6 0 0デニールを超える添糸を使用した場合、 得られる複合繊維が 太くなり、 ごわごわ感が生じ、 着用心地、 使用感が低下する傾向がある 。 また、 添糸 1 bを構成するフィラメ ント数は多い方が金属の細線を包 み込み、 金属の細線 1 aを表面に露出させにくい点で好ましく、 通常、 1 0 0フイラメ ント以上が好ましく、 より好ましくは 1 0 0〜 1 0 0 0 フィラメント、 更に好ましくは 2 0 0〜 1 0 0 0フィラメントである。 1 0 0フィラメ ント未満では金属の細線 1 aを包み込む効果が不十分と なり、 編み加工性が低下し、 また着用心地、 使用感が低下する傾向にあ り、 一方、 1 0 0 0フィラメ ン トを超えると添糸の価格が高くなり利用 しにくい傾向にある。
添糸 l bは、 金属の細線 1 aに巻きつけられていることが好ましい 。 巻きつけ回数は、 該金属の細線 l m当たり 2〜 6 0回、 好ましくは 2 〜 6 0回、 より好ましくは 1 5〜 5 0回、 更に好ましくは 2 5〜 4 5回 である。 この巻きつけにより、 複合糸に張力がかかったとき金属の細線 の切断を防止できる上、 たわみやひずみが生じた時の金属の細線の表面 露出を防止することができる。 卷きつけが 2回未満では上記した効果が 十分に発揮されず、 手袋とした場合、 金属の細線 1 aが切断して飛び出 し、 チクチク感があり触感、 着用心地、 使用感が悪いものとなり、 一方 、 6 0回を越えると張力がかかったとき、 真っ直ぐに伸びている金属の 細線に対して巻かれている添糸は伸びやすく、 張力を添糸に分散できず 、 その結果、 金属の細線が切断される傾向にある。
添糸 1 bは 1〜 3本が適当である。 3本を越えると添糸が太くなり 編み加工性が劣るとともに、 着用心地もゴヮゴヮしたものとなる傾向に ある。
上記した如く、 金属の細線 1 aと添糸 1 bとからなる芯材 1の周り に、 被覆繊維 2を巻きつけて被覆層 3を形成させる。
被覆繊維 2は特に制限されないが、 編み加工性、 樹脂コーティング 加工性、 製品の触感、 肌触り、 フイツ ト性等の着用心地、 使用感、 吸湿 性等を勘案して決定される。 このような点からは、 被覆繊維 2としては 、 ポリエチレン、 ポリアラミ ド、 ポリエステル、 ポリアミ ド （ナイロン
) 、 アクリル、 綿、 ウール等が挙げられる。 被覆繊維 2はマルチフイラ メントでもよく、 また撚糸、 紡績糸であってもよい。 これらの中では、 特に、 ポリエステル、 ポリアミ ド （ナイロン） 、 綿、 ウールが好ましく
、 紡績糸では綿又はポリエステルが柔らかい点で好ましい。 また、 被覆 繊維 2はフィラメントでは捲縮加工されたものが好ましく、 特に捲縮加 ェされたポリエステル繊維、 ポリアミ ド繊維が風合いが良い点で好まし い。
被覆繊維 2の太さは、 金属の細線 1 aの表面露出防止、 編み加工品 の着用心地、 使用感の観点から、 通常 5 0〜 5 0 0デニール （ 1 0 0〜 1 0番手） 程度が好ましく、 5 0〜 3 0 0デニール （ 1 0 0〜 1 5番手 ) 程度がより好ましい。 フィラメントからなる被覆繊維の場合、 フイラ メント数は 2 0〜 5 0 0フィラメントが好ましい。 2 0フィラメント未 満ではフィラメン卜の太さが大きくなりゴヮゴヮしたものとなる傾向に あり、 一方、 5 0 0フイラメン卜を超えると高価になり好ましくない。
被覆繊維 2は、 芯材 1の周りに巻きつけられる。 被覆繊維 2を巻き つける層数は、 層数が少ないと芯材 1を被覆する効果が不十分となり、 芯材が被覆層 3の外に露出する場合があり、 一方、 層数が多いと複合繊 維の編み加工性が低下し、 また、 ごわごわ感が生じ着用心地、 使用感が 低下する傾向がある。 従って、 2層又は 3層が好ましく、 特に 2層が好 ましい。 複合繊維 2を 2層に巻きつける場合、 図 1に示すように、 互い に反対方向、 即ち、 同図では 1層目の被覆繊維 2 aは時計回りの方向に 巻きつけられ、 2層目の複合繊維 2 bは半時計回りの方向に巻きつけら れ、 それぞれ第 1層目の被覆層 3 a、 第 2層目の被覆層 3 bを形成する 被覆繊維 2の巻きつけ回数は、 好ましくは、 芯材 1の長さ l m当り 3 0 0〜 1 2 0 0回、 より好ましくは 4 5 0〜 1 0 0 0回である。 3 0 0回未満では金属の細線 1 aの表面露出を防ぐ目的が十分に達成されず 、 一方、 1 2 0 0回を超えると複合繊維が硬くなるので好ましくない。
被覆繊維 2は一層当たり 1 〜 6本が適当である。 6本を超えると複 合繊維作成時に工程が煩雑になる傾向があり、 また、 ゴヮゴヮ感が生じ やすくなるため好ましくない。
以上のようにして得られた複合繊維は、 編成して耐切創性手袋とさ れる。 耐切創性手袋を製造するに際し、 触感や肌触りが良く、 吸湿性に 富む繊維を用いてプレーティングを施し、 プレーティングした繊維が手 袋の内側になるように編成することにより、 触感や肌触り等の着用心地 、 使用感が良く、 吸湿性に優れた耐切創性手袋を提供することができる このようなプレーティング用繊維としては、 ポリアミ ド、 ポリェチ
0 レン、 ポリエステル、 ポリフヱニレンテレフタルアミ ド、 レーヨンから 選ばれる少なくとも 1種の合成繊維とポリウレタンとの複合繊維、 ポリ アミ ド、 ポリエチレン、 ポリエステル、 ポリフヱニレンテレフタルアミ ド、 レーヨン等の合成繊維や、 綿等の天然繊維が好適である。
プレーティング用繊維は用途により適宜決定すればよいが、 複数種 類の繊維を使用することもできる。 プレーティング用繊維の太さは、 着 用心地、 作業性の観点から 1本あたり 5 0〜 7 0 0デニールが好ましく 、 5 0〜 5 5 0デニールがより好ましい。 5 0デニール未満ではプレー ティングの効果が不十分な傾向があり、 7 0 0デニールを超える場合は プレーティング糸の編み密度が高くなり編み作業性が低下する傾向があ る。 プレーティング用繊維の本数は適宜決定すればよいが、 プレーティ ング加工のしゃすさから 1〜 7本程度が好ましく、 1〜 5本がより好ま しい。
以上のようにして得られた耐切創性手袋は、 滑り止め性、 防水性、 強度を付与するためにゴム又は樹脂で被覆される。 被覆に用いられるゴ ム、 樹脂は従来使用されているものが全て好適に用いられ、 例えば、 ゴ ムとしては、 天然ゴム、 合成ゴム、 それらの変性体のいずれでもよく、 合成ゴムとしては、 二トリルブタジエンゴム （N B R ) 、 スチレンブ夕 ジェンゴム （S B R ) 、 クロロプレンゴム （C R ) 、 、 シリコンゴム、 フッ素ゴム、 クロロスルホン化ポリエチレンゴム、 イソプレンゴム、 そ れらの変性体等が挙げられる。 また、 樹脂としては、 ポリ塩化ビニル、 ポリウレタン、 エチレン一ビュルアルコール共重合体、 ポリ酢酸ビニル 、 それらの変性体等が挙げられる。 これらは単独で又は必要に応じ 2種 以上組み合わせて使用される。
また、 これらのゴム又は樹脂による手袋の被覆範囲は特に限定され ず用途に合わせて適宜決定される。 例えば、 水作業用には手袋全体を被 覆してもよく、 また、 蒸れ防止のためには背の部分以外を被覆してもよ く、 また、 細かい作業用には指先部分のみに被覆してもよい。 また被覆 層は用途に合わせて単層でも多層でもよく、 また、 例えば 2層とする場 合、 1層目と 2層目とを別の材質としてもよい。
以下、 実施例及び比較例を挙げて本発明を更に詳細に説明するが、 本発明はこれらにより何ら制限されるものではない。
尚、 以下の実施例及び比較例において、 Dはデニール、 Fはフイラ メント数を示す。 また、 得られた各サンプル手袋の特性評価を下記の方 法で行い、 得られた結果を表 1に示した。
耐切創性
S 0 d e m a t社製 CUT-TESTER "COUPETE ST " を便用し、 手袋の 掌部について評価した。 綿織物を標準布としてサンプルの前後に切断し 、 円形刃 （4 5 mm ） がサンプルの下部におかれた金属板に接触し、 停止するまでの回転数から （ 1 ) 式により測定デ一夕を計算した。 5回 連続測定し、 5回の平均値からレベルを算出した。
( N + n ) / n ( 1 )
N ：サンプル切断回数
n ：標準布切断回数の平均
(レベル）
1 . 2以上 2 . 5未満 レベル 1
2 . 5以上 5 . 0未満 レベル 2
5 . 0以上 1 0 . 0未満 レベル 3
1 0 . 0以上 2 0 . 0未満 レベル 4
2 0 . 0以上 レベル 5
(作業性、 触感、 吸湿性）
5人のパネラーにより下記の基準で判定しその平均とした。 A：非常に良い、 B ：良い、 C ：普通、 D ：悪い、 E ：非常に悪い まず、 以下の実施例、 比較例で手袋の被覆に用いられるゴム配合溶 液、 樹脂配合溶液を下記に示す。
天然ゴム （NR) ラテックス配合溶液
天然ゴムラテックス中に、 そのゴム固形分 1 0 0重量部に対して、 硫黄 1重量部と、 亜鉛華 1重量部と、 加硫促進剤 （ジブチルジチォカル バミン酸亜鉛） 1重量部とを添加した後、 十分に撹拌、 混合して 2 4時 間程度熟成 （前加硫） させたものに感熱剤 （ポリビニルメチルエーテル ) 1. 5重量部を配合したものを調製した。
二トリルブタジエンゴム （ N B R ) 配合溶液
二ト リルブタジエンゴムラテックス （ N i p 0 1 L X 5 5 0、 日本 ゼオン社製） に、 その固形分 1 0 0重量部に対して硫黄 2重量部、 亜鉛 華 2重量部及びジブチルジチォカルバミン酸亜鉛 0. 5重量部を配合し たものを調製した。
凝固剤
硝酸カルシウムを 2重量0 /0溶解させたメタノール溶液を調製した。 ポリウレタン （PU) 配合溶液
ポリウレタン溶液 （クリスボン 8 1 6 6、 大日本インキ化学工業社 製） をジメチルホルムアミ ドで 2 0 0センチボイズに希釈したものを調 製した。
ポリ塩化ビニル （PVC) 配合溶液
ポリ塩化ビニル樹脂 1 0 0重量部 （P SM— 3 0、 カネ力社製） に 、 可塑剤 1 2 0重量部 （DOP、 大日本ィンキ化学工業社製） 、 安定助 剤 3重量部 （エポキシ化大豆油、 大日本インキ化学工業社製） 、 安定剤 3重量部 （C a— Z n、 旭電化工業社製） を配合したものを調製した。
実施例 1 太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テックス社製ナイロン糸） を 6 3 4回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 6 3 4回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 更に編成した手袋を手型に被せ、 凝固剤に浸したものを、 ニト リルブタジエンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分
、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C E レベル 5であり、 手にはめ ると内側のウーリ一ナイロンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 2
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン 卜糸 （商品名： ダイ二一マ S K 6 0、 東洋紡績株式会社） を 1 0回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テツクス社製ナイ口ン糸） を 6 3 4回 /mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 6 3 4回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 更に編成した手袋を手型に被せ、 凝固剤に浸したものを、 ニト リルブタジエンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分 、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリ一ナイ口ンが手の肌に当たり触感が良く、 伸縮性に優 れ作業性も極めて良好なものであった。 またゴム被覆されている部分は 丈夫で滑り止め性が極めて高いものであった。
実施例 3
太さ 2 5 U mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 5 5回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テツクス社製ナイロン糸） を 6 3 4回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 6 3 4回 で巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 吏に編成した手袋を手型に被せ、 凝固剤に浸したものを、 ニト リルブ夕ジェンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分 、 1 3 0 °Cで 3 0分乾燥 ·加硫を行つた。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリーナイ口ンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 4
太さ 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ント糸 （商品名： ダイ二一マ S K 6 0、 東洋紡績株式会社） を 2回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 7 0 D / 2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハンテ ックス社製ナイ口ン糸） を 7 2 0回/ mで卷きつけ、 更に、 その上に先 のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリー加工ナイ ロン繊維 （ハンテックス社製ナイロン糸） を 7 2 0回/ mで巻きつけて 被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 更に編成した手袋を手型に被せ、 凝固剤に浸したものを、 ニト リルブタジエンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分
、 1 3 Q °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリ一ナイ口ンが手の肌に当たり触感が良く、 伸縮性に優 れ作業性も極めて良好なものであった。 またゴム被覆されている部分は 丈夫で滑り止め性が極めて高いものであつた。
実施例 5
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン ト糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を引きそろえて芯材とし、 その周りに 7 0 D / 2 4 Fからなる 1本のゥ —リー加工ナイロン繊維 （ハンテツクス社製ナイロン糸） を 7 2 0回/ mで巻きつけ、 更に、 その上に先のものと反対方向に、 7 0 D / 2 4 F からなる 1本のウーリー加工ナイロン繊維 （ハンテックス社製ナイロン 糸） を 7 2 0回/ mで卷きつけて被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 更に編成した手袋を手型に被せ、 凝固剤に浸したものを、 ニト リルブタジエンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分 、 1 3 0 ΐで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Εレベル 5であり、 手にはめ ると内側のウーリ一ナイ口ンが手の肌に当たり触感が良く、 伸縮性に優 れ作業性も極めて良好なものであった。 またゴム被覆されている部分は 丈夫で滑り止め性が極めて高いものであつた。
比較例 1
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 7 0回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハン テツクス社製ナイ口ン糸） を 7 2 0回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D Z 2 4 Fからなる 1本のウーリー加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 7 2 0回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 1 0 Gの編み機によって手袋を 編成し、 更に編成した手袋を手型に被せ、 凝固剤に浸したものを、 二卜 リルブタジエンゴム配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分
、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であったが、 手には めるとステンレス細線が複合繊維作成時又は手袋編み工程時の張力に耐 えきれず切れて飛び出しておりチクチク感があり触感が悪かった。 実施例 6
太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D Z 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テツクス社製ナイロン糸） を 6 3 4回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 6 3 4回/ mで卷きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンテッ クス、 FURNIWEB社製） 1本と、 7 0 D / 2 4 Fのウーリ一加工ナイロン繊維 2本からなる F T Y糸 （ 1本のポリゥ レ夕ン繊維に 2本のウーリ一加工ナイ口ン繊維を撚り合わせたもの。 以 下同じ） 1本を使用し、 複合繊維糸が手袋外側になり、 F T Y糸が手袋 内側になるように 1 0 Gの編み機によって手袋を編成し、 更に編成した 手袋を手型に被せ、 凝固剤に浸したものを、 二トリルブタジエンゴム配 合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾 燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリーナイ口ンが手の肌に当たり触感が極めて良く、 伸縮 性、 吸湿性に優れ作業性も極めて良好なものであった。 またゴム被覆さ れている部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 7
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D/ 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン ト糸 （商品名： ダイ二一マ SK 6 0、 東洋紡績株式会社） を 1 0回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D/ 2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハン テツクス社製ナイ口ン糸） を 6 3 4回 /mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D/2 4 Fからなる 1本のウーリー加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 6 3 4回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデックス、 FURNIWEB社製） 1本と 7 0 Dノ 2 4 Fのウーリー加工ナイロン繊維 2本からなる FTY糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F TY糸が手袋内側になるように 1 0 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0°Cで 1 0分、 1 3 0°Cで 3 0分乾燥 '加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリ一ナイロンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 8
太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 曰 本精線株式会社製） 1本と 4 0 0 D/3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン ト糸 （商品名： ダイ二一マ SK 6 0、 東洋紡績株式会社） を 5 5回 Zm ゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D/2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テツクス社製ナイ口ン糸） を 6 3 4回/ mで卷きつけ、 更に、 その上に
9 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリー加工ナ ィ口ン繊維 （ハンテツクス社製ナイ口ン糸） を 6 3 4回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデッ クス、 FURNIWEB社製） 1本と 7 0 2 4 Fのウーリ一加工ナイロン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F T Y糸が手袋内側になるように 1 0 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリーナイロンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであった。
実施例 9
太さ 2 5 Li mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 2回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナイ口ン繊維 （ハンテ ックス社製ナイロン糸） を 7 2 0回 Zmで巻きつけ、 更に、 その上に先 のものと反対方向に、 7 0 D / 4 Fからなる 1本のウーリ一加工ナイ ロン繊維 （ハンテックス社製ナイロン糸） を 7 2 0回/ mで巻きつけて 被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデッ クス、 FURNIWEB社製） 1本と 7 0 D / 2 4 Fのウーリ一加工ナイ口ン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F T Y糸が手袋内側になるように 1 0 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 °Cで 1 0分、 1 3 0 tで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のゥ一リーナイロンが手の肌に当たり触感が良く、 伸縮性に優 れ作業性も極めて良好なものであった。 またゴム被覆されている部分は 丈夫で滑り止め性が極めて高いものであった。
実施例 1 0
太さ 2 5 のステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン ト糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を引きそろえて芯材とし、 その周りに 7 0 D / 2 4 Fからなる 1本のゥ ーリ一加工ナイ口ン繊維 （ハンテツクス社製ナイ口ン糸） を 7 2 0回/ mで卷きつけ、 更に、 その上に先のものと反対方向に、 7 0 D / 2 4 F からなる 1本のウーリ一加工ナイ口ン繊維 （ハンテツタス社製ナイ口ン 糸） を 7 2 0回/ mで卷きつけて被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデックス、 FURNIWEB社製） 1本と 7 0 D / 2 4 Fのウーリ一加工ナイロン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F T Y糸が手袋内側になるように 1 0 Gの 編み機によって手袋を編成し、 更に編成した手袋.を手型に被せ、 凝固剤 に浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 tで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行つた。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ
2 ると内側のゥ一リーナイロンが手の肌に当たり触感が良く、 伸縮性に優 れ作業性も極めて良好なものであった。 またゴム被覆されている部分は 丈夫で滑り止め性が極めて高いものであった。
比較例 2
太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 曰 本精線株式会社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレ ンフィラメント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 7 0回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D / 2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハン テツクス社製ナイロン糸） を 7 2 0回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリ一加工ナ ィロン繊維 （ハンテックス社製ナイロン糸） を 7 2 0回/ mで巻きつけ て被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名： スパンデックス、 FURNIWEB社製） 1本と 7 0 D / 2 4 Fのウーリ一加工ナイ口ン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F T Y糸が手袋内側になるように 1 0 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二卜リルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が CEレベル 5であったが、 手には めるとステンレス細線が複合繊維作成時又は手袋編み工程時の張力に耐 えきれず切れて飛び出しており、 チクチク感があり触感が.悪かつた。
比較例 3
太さ 9 w m、 6 0 7デニールのガラス繊維 （Eガラス） 2束と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレンフィラメント糸 （商品名： ダ ィニーマ S K 6 0、 東洋紡績株式会社） を 3 3回 Zmでゆるやかにから ませながら引きそろえて芯材とし、 その周りに 7 0 Ώ/ 2Λ Fからなる 1本のウーリー加工ナイロン繊維 （ハンテツクス社製ナイロン糸） を 6 3 4回 Zmで卷きつけ、 更に、 その上に先のものと反対方向に、 7 0 D / 2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハンテツクス社製 ナイロン糸） を 6 3 4回/ mで巻きつけて被覆層を形成して複合繊維糸 を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名 ： スパンデッ クス、 FURNIWEB社製） 1本と 7 0 D/ 2 4 Fのウーリ一加工ナイ口ン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F TY糸が手袋内側になるように 7 Gの編 み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤に 浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げたあ と、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が CEレベル 5であったが、 手には めると編み工程で切断されたガラスが被覆糸を突き破り手にチクチク感 があり、 また糸が硬く指を曲げにく く作業性が悪かった。
比較例 4
4 0 0 D/ 3 9 0 Fの超高分子量ポリエチレンフィラメ ン ト糸 （商 品名 ： ダイ二一マ S K 6 0、 東洋紡績株式会社） に 4 0 0 D/ 3 9 0 F の超高分子量ポリエチレンフィラメ ント糸 （商品名 ： ダイニーマ S K 6 0、 東洋紡績株式会社） を 3 3回/ mでゆるやかにからませながら引き そろえて芯材とし、 その周りに 7 0 D/ 2 4 Fからなる 1本のウーリ一 加工ナイロン繊維 （ハンテツクス社製ナイロン糸） を 6 3 4回 Zmで卷 きつけ、 更に、 その上に先のものと反対方向に、 7 0 D/ 2 4 Fからな る 1本のウーリー加工ナイロン繊維 （ハンテツクス社製ナイロン糸） を 6 3 4回 で卷きつけて被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 D.のポリウレ夕 ン繊維 （商品名：スパンデックス、 FURNIWEB社製） 1.本と 7 0 D/ 2 4 Fのウーリー加工ナイロン繊維 2本からなる FT Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F TY糸が手袋内側になるように 7 Gの編 み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤に 浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げたあ と、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は糸が太いため、 作業性や触感はそこそこで 、 またステンレス細線を使用してないため耐切創性が CEレベル 3であり 、 目標とする耐切創性 CEレベル 5を満足するものではなかった。
比較例 5
4 0 0 D/ 2 5 2F フィラメント糸 （商品名：ケプラー、 デュポン 社製） に 4 0 0 D/3 9 0 Fの超高分子量ポリエチレンフィラメント糸 (商品名： ダイ二一マ S K 6 0、 東洋紡績株式会社） を 3 3回 Zmでゆ るやかにからませながら引きそろえて芯材とし、 その周りに 7 0 DZ 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハンテツクス社製ナイ ロン糸） を 6 3 4回/ mで巻きつけ、 更に、 その上に先のものと反対方 向に、 7 0 D/ 2 4 Fからなる 1本のウーリ一加工ナイ口ン繊維 （ハン テツクス社製ナイロン糸） を 6 3 4回/ mで巻きつけて被覆層を形成し て複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデックス、 FURNIWEB社製） 1本と 7 0 D/2 4 Fのウーリ一加工ナイ口ン繊維 2本からなる F T Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F T Y糸が手袋内側になるように 7 Gの編 み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤に 浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げたあ と、 6 0でで 1 0分、 1 3 0°Cで 3 0分乾燥 '加硫を行った。
得られたサンプル手袋は糸が太いため、 作業性や触感はそこそこで 、 またステンレス細線を使用してないため耐切創性が CEレベル 4であり 、 目標とする耐切創性 CEレベル 5を満足するものではなかった。
実施例 1 1
太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 4 0 0 D/3 9 0 Fの超高分子量ポリェチレ ンフィラメント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D/ 2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハン テツクス社製ナイ口ン糸） を 6 3 4回 /mで卷きつけ、 更に、 その上に 先のものと反対方向に、 7 5 D/3 6 Fからなる 2本のポリエステルテ クスチャード繊維 （L E AL E A ENTERPR I S E CO. , L TD. 製） を 6 3 4回 /mで巻きつけて被覆層を形成して複合繊維糸を 得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデックス、 FUMIWEB社製） 1本と .7 0 D/ 2 4 Fのウーリ一加工ナイロン繊維 2本からなる FTY糸 1本を使用し、 複 合繊維糸が手袋外側になり、 F TY糸が手袋内側になるように 1 3 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二卜リルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行つた。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリ一ナイ口ンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 1 2
太さ 2 5； のステンレス細線 （ S U S 3 0 4ステンレス細線、 曰 本精線株式会社製） 1本と 4 0 0 D/ 3 9 0 Fの超高分子量ポリエチレ ンフィラメ ン ト糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その 周りに 7 0 D/2 4 Fからなる 1本のウーリー加工ナイロン繊維 （ハン テックス社製ナイロン糸） を 6 3 4回/ mで巻きつけ、 更に、 その上に 先のものと反対方向に、 7 5 D/3 6 Fからなる 1本のポリエステルテ クスチャード繊維 （L E AL E A ENTERPR I S E CO. ， L TD. 製） を 6 3 4回/ mで巻きつけて被覆層を形成して複合繊維糸を 得た。
次に、 得られた複合繊維糸を用い、 編み工程で 4 0 Dのポリウレ夕 ン繊維 （商品名：スパンデックス、 FURNIWEB社製） 1本と 7 0 D/ 2 4 Fのウーリ一加工ナイロン繊維 2本からなる FT Y糸 1本を使用し、 複 合繊維糸が手袋外側になり、 FTY糸が手袋内側になるように 1 3 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 凝固剤 に浸したものを、 二トリルブタジエンゴム配合溶液に浸漬し、 引上げた あと、 6 0 °Cで 1 0分、 1 3 0 tで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のゥ一リーナイロンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またゴム被覆されている 部分は丈夫で滑り止め性が極めて高いものであつた。
実施例 ί 3
太さ 2 5 mのステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1 本とポリバラフヱ二レンテレフタルアミ ドの 4 0 0 D / 2 5 2 F フィラメント糸 （商品名：ケプラー、 デュポン社製） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 1本のポリエステル短繊維の 2 0番糸 （商品名：ポリエステルスパ ン、 MW E社製） を 8 4 0回/ mで巻きつけ、 更に、 その上に先のもの と反対方向に、 同じく 1本のポリエステル短繊維の 2 0番糸 （商品名： ポリエステルスパン、 MW E社製） を 8 4 0回/ mで巻いて被覆層を形 成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で、 ポリエステル短繊 維 2 0番糸 （商品名：ポリエステルスパン、 MW E社製） を 2本使用し 、 複合繊維糸が手袋外側になり、 ポリエステル短繊維糸が手袋内側にな るように 1 0 Gの編み機によって手袋を編成し、 更に編成した手袋を手 型に被せ、 8 0 °Cに加温したものをを、 天然ゴムラテックス配合溶液に 浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫 を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ たときの触感が良く しつかり感がぁり、 吸汗性に優れ作業性の良好なも のであった。 またゴム被覆されている部分は丈夫で滑り止め性が極めて 高いものであった。
実施例 1 4
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本とポリパラフ 二レンテレフタルアミ ドの 4 0 0 D / 2 5 2 F フィラメント糸 （商品名：ケブラ一、 デュポン社製） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 1本のポリエステル短繊維の 2 0番糸 （商品名：ポリエステルスパ ン、 M W E社製） を 8 4 0回/ mで巻きつけ、 更にその上に先のものと 反対方向に、 同じく 1本のポリエステル短繊維の 2 0番糸 （商品名：ポ リエステルスパン、 MW E社製） を 8 4 0回/ mで卷いて被覆層を形成 して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で、 ポリエステル短繊 維 2 0番糸 （商品名：ポリエステルスパン、 M W E社製） を 3本使用し 、 複合繊維糸が手袋外側になり、 ポリエステル短繊維糸が手袋内側にな るように 1 0 Gの編み機によって、 手袋を編成し、 更に編成した手袋を 手型に被せ、 8 0 °Cに加温したものを、 天然ゴムラテックス配合溶液に 浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 '加硫 を ί亍った。
得られたサンプル手袋は耐切創性が C Εレベル 5であり、 手にはめ たときの触感が良く しつかり感がぁり、 吸汗性に優れ作業性の良好なも のであった。 またゴム被覆されている部分は丈夫で滑り止め性が極めて 高いものであった。
実施例 1 5
太さ. 2 5 u mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本とポリパラフエ二レンテレフタルアミ ドの 4 0 0 D / 2 5 2 F フィラメ ント糸 （商品名：ケブラ一、 デュポン社製） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 1本の綿糸の 2 0番糸 （商品名： コッ トンスパン、 MW E社製） を 8 4 0回/ mで卷きつけ、 更にその上に先のものと反対方向に、 同じく 1本の綿糸の 2 0番糸 （商品名： コッ ト ンスパン、 MW E社製） を 8 4 0回/ mで巻いて被覆層を形成して複合繊維糸をえた。
次に、 得られた複合繊維糸を用い、 編み工程で、 綿糸の 2 0番糸 （ 商品名： コッ トンスパン、 MW E社製） を 2本使用して、 複合繊維糸が 手袋外側になり、 綿糸が手袋内側になるように、 1 0 Gの編み機によつ て手袋を編成し、 更に編成した手袋を手型に被せ、 8 0 °Cに加温したも のを、 天然ゴムラテックス配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ たときの触感が極めて良く、 吸汗性に優れ作業性の良好なものであつた 。 またゴム被覆されている部分は丈夫で滑り止め性が極めて高いもので あった。
実施例 1 6
太さ 2 5 のステンレス細線 （ S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本とポリパラフニ二レンテレフタルアミ ドの 4 0 0 D / 2 5 2 F フィラメント糸 （商品名：ケブラ一、 デュポン社製） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 1本の綿糸の 2 0番糸 （商品名： コッ ト ンスパン、 MW E社製） を 8 4 0回/ mで卷きつけ、 更にその上に先のものと反対方向に、 同じく 1本の綿糸の 2 0番糸 （商品名： コッ トンスパン、 MW E社製） を 8 4 0回/ mで巻いて被覆層を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で、 綿糸の 2 0番糸 （ 商品名： コッ トンスパン、 MW E社製） を 3本使用して、 複合繊維糸が 手袋外側になり、 綿糸が手袋内側になるように 1 0 Gの編み機によって 手袋を編成し、 更に編成した手袋を手型に被せ、 8 0 °Cに加温したもの を、 天然ゴムラテックス配合溶液に浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 ·加硫を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ たときの触感が極めて良く、 吸汗性に優れ作業性の良好なものであった 。 またゴム被覆されている部分は丈夫で滑り止め性が極めて高いもので あつた
実施例 1 7 太さ 2 5 u mのステンレス細線 （SU S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本とポリバラフヱ二レンテレフタルアミ ドの 4 0 0 D/ 2 5 2 Fフィラメ ン ト糸 （商品名：ケプラー、 デュポン社製） を 3 3回 Zmでゆるやかにからませながら引きそろえて芯材とし、 その周 りに 7 0 D/ 2 4 Fからなる 1本のウーリ一加工ナイ口ン繊維 （ハンテ ックス社製） を 8 4 0回 で卷きつけ、 更にその上に先のものと反対 方向に、 7 0 D/2 4 Fからなる 1本のウーリ一加工ナイロン繊維 （ハ ンテツクス社製） を同じく 8 4 0回/ mで巻きつけて被覆層を形成して 複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で、 4 0 Dのポリウレ 夕ン繊維 （商品名：スパンデックス、 FUMIWEB社製） 1本と 7 0 D/ 2 4 Fのウーリーナイロン繊維 2本からなる FT Y糸 1本を使用して、 複 合繊維糸が手袋外側になり、 F TY糸が手袋内側となるように 1 3 Gの 編み機によって手袋を編成し、 更に編成した手袋を手型に被せ、 ポリウ レ夕ン配合溶液に浸漬し、 引上げたあと、 6 0°C温水で DMFを置換除 去し、 1 1 0°Cで 2 0分乾燥を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 手にはめ ると内側のウーリーナイロンが手の肌に当たり触感が極めて良く、 伸縮 性に優れ作業性も極めて良好なものであった。 またウレタン樹脂で被覆 されている部分滑り止め性が極めて高いものであつた。
実施例 1 8
太さ 2 5 mのステンレス細線 （SU S 3 0 4ステンレス細線、 曰 本精線株式会社製） 1本と 4 0 0 D/ 3 9 0 Fの超高分子量ポリエチレ ンのフィラメ ント糸 （商品名： ダイニーマ S K 6 0、 東洋紡績株式会社 製） を 3 3回/ mでゆるやかにからませながら引きそろえて芯材とし、 その周りに 7 0 D/ 2 4 Fからなる 1本のウーリ一加工ナイ口ン繊維 （ ハンテツクス社製） を 8 4 0回/ mで巻きつけ、 更にその上に先のもの と反対方向に、 1本のポリエステル短繊維の 2 0番糸 （商品名：ポリエ ステルスパン、 M W E社製） を同じく 8 4 0回/ mで卷きつけて被覆層 を形成して複合繊維糸を得た。
次に、 得られた複合繊維糸を用い、 編み工程で、 1 4 0 Dのポリゥ レ夕ン繊維 （商品名：スパンデッ クス、 FURNIWEB?土製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレンフィラメ ント糸 （商品名： ダイ二 一マ S K 6 0、 東洋紡績株式会社製） 2本からなる F T Y糸 1本を使用 して、 複合繊維糸が手袋外側になり、 F T Y糸が手袋内側となるように 1 3 Gの編み機によって手袋を編成し、 更に編成した手袋を手型に被せ 、 ポリウレタン配合溶液に浸漬し、 引上げたあと、 6 O 温水で D M F を置換除去し、 1 1 0 °Cで 2 0分乾燥を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 内側の F T Y糸が手の肌に当たり触感が良く、 伸縮性に優れ、 手袋の厚さが薄く 、 作業性の極めて良好なものであった。 またウレタン樹脂で被覆されて いる部分滑り止め性が極めて高いものであつた。
実施例 1 9
太さ 2 5 mのステンレス細線 （S U S 3 0 4ステンレス細線、 日 本精線株式会社製） 1本と 1 4 0 D / 4 3 2 Fのポリエステルフィラメ ン卜糸 （商品名： BC15 32-1SGZ71BT、 東洋紡績株式会社製） を 3 3回
/mでゆるやかにからませながら引きそろえて芯材とし、 その周りに 1 本の綿糸の 3 0番糸 （C olony textile mills ltd.社製） を 8 4 0回/ mで卷きつけ、 更に、 その上に先のものと反対方向に、 同じく 1本のポ リエステル短繊維の 3 2番糸 （FT Ramagloria Sakti Tekstil
Industri, 社製） を 8 4 0回/ mで巻いて被覆層を形成して複合繊維糸 を得た。 次に、 得られた複合繊維糸を用い、 編み工程で、 1 4 0 Dのポリゥ レタン繊維 （商品名：スパンテックス、 FURNIWEB社製） 1本と 4 0 0 D
/ 3 9 0 Fの超高分子量ポリエチレンフィラメント糸 （商品名： ダイ二 一マ S K 6 0、 東洋紡績株式会社製） 2本からなる F T Y糸 1本を使用 して、 複合繊維糸が手袋外側になり、 F T Y糸が手袋内側となるように 1 3 Gの編み機によって手袋を編成し、 更に編成した手袋に撥油処理を 施したものを手型に被せ、 塩化ビニル配合溶液にシャワー塗布し、 引上 げたあと、 2 3 0 °Cで 2分、 1 8 O tで 1 5分乾燥を行った。
得られたサンプル手袋は耐切創性が C Eレベル 5であり、 内側の F T Y糸が手の肌に当たり触感が良く、 伸縮性に優れ、 手袋の厚さが薄く 、 作業性の極めて良好なものであった。 また塩化ビニル樹脂で被覆され ている部分滑り止め性が極めて高いものであつた。
比較例 6
日本国特開平 1 一 2 3 9 1 0 4号公報の実施例 1に準じて、 ポリパ ラフヱ二レンテレフタルアミ ド繊維 （商品名：テクノラート、 帝人化成 株式会社製） の 3 0 0 0デニール 2 0 0 0フィラメントの無捲縮トウを 7 5 0 mmの間隔で一対のローラー間、 牽切比 2 0倍で牽切した紡績糸 ( 1 0 . 6 3番手） 3本 （ 1 5 0 0デニール相当） と可撓性ステンレス ワイヤー （ 2 5 w m ) 2本とをパラレルに引きそろえたものを芯材とし て、 これに 4 2 0デニールのナイロン繊維を上下二重にそれぞれ反対方 向に 6 3 4回/ mで卷きつけて複合繊維を得た。 また、 この複合繊維 2 本を引きそろえ 5 Gの編み機で手袋を編んで、 更に編成した手袋を手型 に被せ、 ポリウレタン配合溶液に浸漬し、 引上げたあと、 6 0 °C温水で D M Fを置換除去し、 1 1 0 °Cで 2 0分乾燥を行った。
得られたサンプル手袋は、 耐切創性が G Eレベルで 5であったが、 添糸が紡績糸であるため加工時に添糸が伸張し、 金属の細線が切断され 、 金属の細線の先端が複合繊維外に露出し、 チクチク感があり、 作業性 が悪いものであった。
比較例 7
一般的な非金属製の耐切創性手袋として、 ポリパラフニ二レンテレ フタルアミ ドの 2 0番手の紡績糸 （商品名：ケプラー、 デュポン社製） 5本を引きそろえ 1 0 Gの編み機で手袋を編んで、 更に編成した手袋を 手型に被せ、 8 0 °Cに加温したものを、 天然ゴムラテックス配合溶液に 浸漬し、 引上げたあと、 6 0 °Cで 1 0分、 1 3 0 °Cで 3 0分乾燥 .加硫 を ί亍った。
得られたサンプル手袋は手にはめたときの触感が良く しつかり感がぁ ものであつたが、 耐切創性が C Eレベル 4であり、 目標とする耐切創性 CEレベル 5を満足するものではなかった。
比較例 8
一般的な非金属製の耐切創性手袋として、 1 4 0 Dのポリウレタン 繊維 （商品名：スパンデックス、 FURNIWEB社製） 1本と 4 0 0 D / 3 9 0 Fの超高分子量ポリエチレンフィラメント糸 （商品名： ダイ二一マ S Κ 6 0、 東洋紡績株式会社製） 2本からなる F T Y糸を 1本を引きそろ え 1 3 Gの編み機で手袋を編んで、 更に編成した手袋を手型に被せ、 ポ リウレタン配合溶液に浸漬し、 引上げたあと、 6 0 °C温水で D M Fを置 換除去し、 1 1 0 °Cで 2 0分乾燥を行った。
得られたサンプル手袋は内側の触感が良く、 伸縮性に優れ、 作業性 の良好なものであつたが、 耐切創性が C Eレベル 2であり、 目標とする 耐切創性 CEレベル 5を満足するものではなかった。
Figure imgf000036_0001
以上のように、 本発明の耐切創性手袋は、 金属の細線とフィラメン ト糸からなる添糸とからなり、 該芯材の周りに被覆繊維を巻きつけて被 覆層を形成した複合繊維からなるため、 吸湿性及び編み加工性に優れ、 着用心地、 伸縮性、 使用感及び着用した状態での作業性に優れていると ともに、 表面がゴムや樹脂で被覆されているため、 滑り止め性、 防水性 、 強度などが付与されるだけでなく、 耐切創性に優れている。
また、 本発明の耐切創性手袋を着用して鋭利な刃物等を取り扱う場 合、 ゴムや樹脂で被覆されているので被覆繊維が切断されるといったト ラブルが起こり難く、 たとえ被覆繊維が切断されたとしてもゴムや樹脂 に捕捉され、 埃が発生することがない。
また、 上記複合繊維を用いて手袋を編成するに際し、 特定の繊維で プレーティングを施し、 このプレーティングした繊維を手袋の内側に配 されるように編成することにより、 伸縮性、 吸湿性は一層高められ、 ま た着用心地、 使用感ゃ着用した状態での作業性の一層改善された耐切創 性手袋を提供することができる。 産業上の利用可能性
叙上のとおり、 本発明の耐切創性手袋は、 着用心地、 使用感及び着 用した状態での作業性が良好であるばかりでなく、 滑り止め性、 防水性 、 強度及び耐切創性においても極めて優れている。

Claims

金属の細線と、 フィラメ ント糸からなる添糸とからなる芯材と、 該 芯材の周りに被覆繊維が卷きつけられた被覆層とからなる複合繊維 で作られた手袋の表面がゴム又は樹脂で被覆されていることを特徴 とする耐切創性手袋。
金属の細線がステンレスからなることを特徴とする請求項 1記載の 耐切創性手袋。
添糸が、 ポリエチレン、 超高分子量ポリエチレン、 ポリエステル、 ポリパラフヱニレンテレフタルアミ ドから選ばれる少なくとも 1種 のフイラメ ント糸から選ばれることを特徴とする請求項 1又は 2記 載の耐切創性手袋。
添糸が超高分子量ポリエチレンであることを特徴とする請求項 3記 載の耐切創性手袋。
添糸がポリエステルであることを特徴とする請求項 3記載の耐切創 性手袋。
被覆繊維が、 ポリエチレン、 ポリアラミ ド、 ポリエステル、 ポリア ミ ド、 ァクリル、 綿、 ウールから選ばれる少なくとも 1種の繊維か らなることを特徴とする請求項 1 ~ 5のいずれか 1項に記載の耐切 創性手袋。
ポリエステル又はポリアミ ドからなる繊維が、 捲縮加工されたもの であることを特徴とする請求項 6記載の耐切創性手袋。
被覆層が、 第 1の被覆層とこれとは反対方向に巻きつけられた第 2 の被覆層とからなることを特徴とする請求項 1〜 7のいずれか 1項 に記載の耐切創性手袋。
添糸が金属の細線に金属の細線 l m当たり 2〜6 0回卷きつけられ ていることを特徴とする請求項 1〜 8のいずれか 1項に記載の耐切 創性手袋。
. 合成繊維又は天然繊維でプレーティングされ、 プレーティングさ れた繊維が手袋の内側に配されていることを特徴とする請求項 1〜 9のいずれか 1項に記載の耐切創性手袋。
. プレーティング用の合成繊維が、 ポリアミ ド、 ポリエチレン、 ポ リエステル、 ポリフエ二レンテレフタルアミ ド、 レーヨンから選ば れる少なくとも 1種の合成繊維とポリウレタンとの複合繊維、 又は 、 ポリアミ ド、 ポリエチレン、 ポリエステル、 ポリフヱニレンテレ フ夕ルアミ ド、 レーヨンから選ばれる少なく とも 1種の合成繊維か らなることを特徴とする請求項 1 0記載の耐切創性手袋。
. プレーティング用の天然繊維が綿からなることを特徴とする請求 項 1 0記載の耐切創性手袋。
. ゴムが天然ゴム、 合成ゴム、 それらの変性体から選ばれる少なく とも 1種であることを特徴とする請求項 1〜 1 2のいずれか 1項に 記載の耐切創性手袋。
. 合成ゴムが二ト リルブタジエンゴム、 スチレンブタジエンゴム、 クロロプレンゴム、 シリコンゴム、 フッ素ゴム、 クロロスルホン丫匕 ポリエチレンゴム、 イソプレンゴム、 それらの変性体から選ばれる 少なく とも 1種であることを特徴とする請求項 1〜 1 3のいずれか 1項に記載の耐切創性手袋。
. 樹脂がポリ塩化ビュル、 ポリウレタン、 エチレン一ビニルアルコ —ル共重合体、 ポリ酢酸ビニル、 それらの変性体から選ばれる少な く とも 1種であることを特徴とする請求項 1〜 1 3のいずれか 1項 に記載の耐切創性手袋。
3
PCT/JP2006/315081 2005-08-01 2006-07-24 耐切創性手袋 WO2007015439A1 (ja)