WO2005099893A2 - Composition and method for making silicon-containing products - Google Patents
Composition and method for making silicon-containing products Download PDFInfo
- Publication number
- WO2005099893A2 WO2005099893A2 PCT/US2005/012302 US2005012302W WO2005099893A2 WO 2005099893 A2 WO2005099893 A2 WO 2005099893A2 US 2005012302 W US2005012302 W US 2005012302W WO 2005099893 A2 WO2005099893 A2 WO 2005099893A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon
- silica
- silica product
- ppm
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B21/00—Nitrogen; Compounds thereof
- C01B21/06—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron
- C01B21/068—Binary compounds of nitrogen with metals, with silicon, or with boron, or with carbon, i.e. nitrides; Compounds of nitrogen with more than one metal, silicon or boron with silicon
- C01B21/0685—Preparation by carboreductive nitridation
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/90—Carbides
- C01B32/914—Carbides of single elements
- C01B32/956—Silicon carbide
- C01B32/963—Preparation from compounds containing silicon
- C01B32/977—Preparation from organic compounds containing silicon
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/90—Carbides
- C01B32/914—Carbides of single elements
- C01B32/956—Silicon carbide
- C01B32/963—Preparation from compounds containing silicon
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/90—Carbides
- C01B32/914—Carbides of single elements
- C01B32/956—Silicon carbide
- C01B32/963—Preparation from compounds containing silicon
- C01B32/97—Preparation from SiO or SiO2
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B33/00—Silicon; Compounds thereof
- C01B33/02—Silicon
- C01B33/021—Preparation
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B33/00—Silicon; Compounds thereof
- C01B33/08—Compounds containing halogen
- C01B33/107—Halogenated silanes
- C01B33/1071—Tetrachloride, trichlorosilane or silicochloroform, dichlorosilane, monochlorosilane or mixtures thereof
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/10—Particle morphology extending in one dimension, e.g. needle-like
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/16—Pore diameter
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S502/00—Catalyst, solid sorbent, or support therefor: product or process of making
- Y10S502/506—Method of making inorganic composition utilizing organic compound, except formic, acetic, or oxalic acid or salt thereof
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S502/00—Catalyst, solid sorbent, or support therefor: product or process of making
- Y10S502/506—Method of making inorganic composition utilizing organic compound, except formic, acetic, or oxalic acid or salt thereof
- Y10S502/507—Synthetic resin, natural resin, polysaccaride, or polypeptide
Definitions
- This invention relates generally to various silicon-containing products and to methods for making such products from starting materials obtained from plant matter or processed plant matter having a significant silica content, most preferably rice hulls and rice straw.
- One aspect of the invention relates to carbon-silica products made by a leaching process wherein the starting materials are treated with a sulfuric acid solution.
- Another aspect of the invention relates to chemical and thermal methods for removing and recovering volatile carbon from compositions made by the leaching process, and to the resultant devolatilized carbon-silica products.
- Another aspect of the invention relates to silicon-containing products made from devolatilized carbon-silica products using a carbothermal process.
- silicon-containing materials include, for example, silicon carbide and silicon nitride, which, in certain forms, are used to produce high performance ceramics and high performance composites. These, and other silicon-containing materials, are used in a variety of applications including electronics, defense, automotive, aerospace, industrial wear parts, advanced glasses, and in chemical and environmental products.
- the molar ratio for the reaction should be approximately 3 : 1 , as sho n by the following formula:
- Si-based products such as ferrosilicon (FeSi) and silicon nitride (Si 3 N 4 ) and silicon tetrachloride (SiCl 4 ) can be produced using the same reactions between carbon and silica.
- FeSi ferrosilicon
- Si 3 N 4 silicon nitride
- SiCl 4 silicon tetrachloride
- the standard commercial process for prodxicing silicon involves the mixing of a carbon source such as coke with crystalline silica., i.e. sand or quartz, in a predetermined ratio and reacting this mixture to produce metallurgical grade silicon.
- silicon carbide produced using the slow and energy- intensive Acheson process is costly and is limited to use in the metallurgical, refractory and abrasives industries and in other applications that do not require high purity, small particle size, and/or whiskers or fibers.
- the production of hdgh-end silicon carbide powders has previously required the use of processes that are e" e more expensive and complicated.
- Silicon nitride can be produced through a variety of processes and is often made commercially using expensive starting materials such- as silicon tetrachloride. The resultant powder, although commercially desirable, is too expensive for use in all but a few high- end applications.
- Rice hulls are the natural sheaths that form on rice grains during their growth. They are removed during the refining of rice and are a waste or low value byproduct of the rice milling industry. Rice straw consists of stem, leaf sheathes, leaf blades and the remains of the panicle after harvesting. Generally, th& amount of rice straw obtained from rice plants is at least equal to the rough yield of * rice harvested. Because of their high silica content, these materials have little value as components of animal feeds. Because rice hulls and rice straw have a relatively large amount of potassium that interacts with the silica at combustion temperatures to produce boiler slag and deposits, and have a large fraction of noncombustible ash, they are similarly viewed as being a poor fuel source.
- Mater Sci, 23(1), 1988 disclosed milling cleaned and dried rice husks to a particle size of about 40 mesh, leaching in hydrochloric (1 N, 3 N, 5 N and 11.3 N), sulfuric (IN, 4.5 N, 9 N and 18 N) and nitric (4.5 N, 9N and 18N) acid at 50°C for 2 hours, washing with distilled water, and drying. The acid-leached husks were then combusted at temperatures ranging from 500 to 700°C. Acid treatment with sulfuric acid was less effective than leaching with either hydrochloric acid or nitric acid at comparable concentrations for reducing the concentrations of oxides of sodium, potassium, calcium, iron, magnesium, manganese, zinc and copper.
- the overall metallic impurity level (reported as oxides) ranged from 300-747 ppm for samples treated with hydrochloric acid, from 496-688 ppm for samples treated with nitric acid, and from 3534-4483 ppm for samples treated with sulfuric acid. Even the best performance, achieved using 11.3 N HCl, failed to produce a 99% reduction in the identified non-silica impurities. No data was presented regarding phosphorous levels either before or after treatment. [0015] R. Conradt, P. Pimkhaokham and U.- Leela-Adisorn, "Nano-structured silica from rice husk", J.
- Non-Crystalline Solids 145 (1992) 75-79, report the acid leaching of washed Thai rice husk by reflux boiling in 2.4 molar hydrochloric acid or 3.6 molar sulfuric acid for 3 hours at a ratio of 100 g. husk /liter.
- the leached husks were subsequently incinerated at 600° C and characterized.
- the investigators concluded that omission of acid pre-treatment yielded a considerably reduced surface area in the incinerated products. Specific surface areas ot 180-250 sq. m/g. are reported for the silica prepared from rice husks.
- the best non-silica mineral level achieved in the ash obtained from rice hulls pretreated with HCl was 6500 ppm.
- the overall non-silica mineral level (reported as oxides) in the digested husks was reported to be 2,500 ppm.
- the digested husk was pyrolysed at 800°C to a constant weight under a flow of argon gas.
- the carbon content of pyrolysed digested husk was determined by heating at 700°C in air for one hour.
- Rahman reported that after more than 3 hours digestion in 12M nitric acid, the digestion product obtained was in the stoichiometric ratio of 2C/SiO 2 and that higher concentrations could not produce the desired ratio. Lower concentrations required a longer time to produce a suitable carbon- silica mixture.
- the weight loss after heating was considered to be the amount of carbon present in the pyrolysed digested husk, and the residue was considered to be pure silica.
- the pyrolysed powder was nitrided by heating in a furnace in a controlled nitrogen atmosphere, raising the temperature gradually to 1430°C, after which the products were burned in a muffle furnace at about 700°C for 30 min. to remove any excess carbon.
- the most important factor contributing to the completeness of reaction was found to be the homogeneity of mixing, and the use of rice husk was said to be an advantage, as the silica and carbon are naturally mixed.
- the rice hulls are burned to form ash, thereby removing all of the carbon, after which the ash is treated with acid to remove minerals from the resulting silica.
- the removal of K + prior to heating the rice hulls allows the silica to maintain a higher specific surface area and smaller particle size upon heating
- Real et al. in 1996 demonstrated that it is advantageous to carry out acid leaching prior to using combustion to reduce the rice hulls to silica. In either situation, the resulting silica is combined with carbon or another reducing agent from another source in order to produce the desired silicon-containing product.
- Rice hulls contain both fixed and volatile carbon.
- the mole ratio of fixed carbon to silica in untreated rice hulls is about 4:1. Consequently, the mole ratio must be adjusted to the proper ratio for the desired product (e.g., about 3:1 for SiC and about 2:1 for Si). It is important to note that this is a mole ratio and is not a mass percentage ratio, as is sometimes used in the prior art. Even a mass percentage ratio as low as 1:1 correlates to a mole ratio of about 5:1, which is well above what is required in most carbothermal reactions. Hunt et al.
- the high reactivity of the carbon after acid treatment, the retention of the high specific area of the silica after acid treatment and the intimate association of the silica and carbon in acid treated rice hulls should enhance the rate of reaction between the silica and the carbon at high temperatures.
- the present invention includes novel processes and intermediate products that can be used to produce high-performance, high purity end products such as silicon, silicon carbide, silicon nitride, silicon tetrachloride and other high purity, silicon- containing products with lower energy requirements and higher throughputs at a fraction of the costs incurred through the use of conventional processes.
- Naturally occurring plant matter, processed plant matter, or mixtures thereof, containing sufficient quantities of both carbon and silica is leached in either a single-stage or multi-stage process using a sulfuric acid solution at a controlled temperature for a suitable time.
- the solid carbon- silica products obtained from the leaching process contain a mole ratio of fixed carbon to silica of at least about 1:1, very low levels of minerals, and high porosity and reactivity.
- the terms “mineral” and “minerals” exclude silica and mean one or more of sodium (Na), potassium (K), magnesium (MG), calcium (Ca), manganese (Mn), iron (Fe), aluminum (Al), boron (B) and phosphorous (P), whether present alone or in combinations with each other, or with other metals or atoms, such as oxygen.
- the fixed carbon and silica are intimately mixed on a micron or even submicron scale, and the silica is present in an amorphous form with large specific surface area.
- the carbon-silica products of the invention are frangible and easily reducible to a fine powder form by milling or other suitable means.
- the carbon-silica products of the leaching process contain volatile carbon that can be removed and recovered by further treatment with acid, or by heating to temperatures up to about 1000 deg C.
- the devolatilized carbon-silica products of the invention embody all the advantages of the carbon-silica products mentioned above and also have low levels of volatile carbon.
- the devolatilized-carbon-silica products can easily be milled to fine powder. Pellets can be formed from either the devolatilized or unde olatilized carbon-silica products without adding external binders.
- the carbon-silica products of the invention can be further reacted in a controlled environment in a carbothermal reactor to produce desired silicon-containing products including but not limited to silicon, silicon carbide, and silicon nitride and silicon tetrachloride.
- desired silicon-containing products including but not limited to silicon, silicon carbide, and silicon nitride and silicon tetrachloride.
- Many of the products made according to the improved carbothermal process of the invention are themselves believed to be novel because of their higher purities and enhanced performance characteristics.
- the high reactivity of the carbon after acid treatment, the retention of the high specific surface area of the silica after acid treatment and the intimate association of the silica and carbon in the carbon-silica products of the invention enhances the rate of reaction between the silica and the carbon at high temperatures.
- any remaining volatile carbon can also be removed and recovered.
- each particle of the carbon-silica products and devolatilized carbon-silica products of the invention embodies very small pieces of carbon and silica mixed together at a micron, submicron, or even nanometric scale, the contact points between the silica and the carbon are very large. Also, because the carbon and silica are amorphous and have large surface areas, the material reacts very fast when producing silicon-containing products. For example, reaction times of about 75 minutes to produce silicon carbide are readily achievable, compared to a day or more when conventional coal, or coke, and sand are used as feed materials.
- a method for leaching naturally occurring plant matter, processed plant matter, and mixtures of naturally occurring and processed plant matter, embodying at least about 3 weight percent silica with sulfuric acid to produce preferred, high purity carbon-silica products.
- the use of rice hulls as the plant matter is preferred.
- a method for making carbon-silica products comprising the steps of comminuting plant matter comprising at least 3 weight percent silica to a particle size ranging from about 10 microns to over 1 millimeter, and contacting and preferably mixing from about 1 to about 35 weight percent of the comminuted plant matter with a sulfuric acid solution having an acid concentration ranging from about 0.01 weight percent to about 30 weight percent at a temperature ranging from about 10°C to about 250°C for a time ranging from about six seconds to about 48 hours.
- a leaching method comprises two or more stages of leaching. Following application of the leaching method as described above, leaching of the washed or unwashed material is repeated one or more additional times to further reduce the remaining mineral content and further adjust the ratio of fixed carbon to silica.
- leaching of the washed or unwashed material is repeated one or more additional times to further reduce the remaining mineral content and further adjust the ratio of fixed carbon to silica.
- fixed carbon-to-silica mole ratios as low as 1:1 or lower can be achieved.
- a leaching method is disclosed that is useful in either single or multiple stages for improved removal of minerals from naturally occurring or processed plant matter containing significant silica contents of greater than about 1 weight percent and preferably greater than 3-5 weight percent or more.
- a leaching method is disclosed that is useful for reducing the amount of volatile carbon in naturally occurring or processed plant matter containing more than about 3 weight percent silica.
- a leaching method is disclosed that is useful for reducing the amount of fixed carbon in naturally occurring or processed plant matter containing more than about 3 weight percent silica.
- a leaching method is disclosed that is useful for converting volatile carbon into fixed carbon in naturally occurring or processed plant matter containing more than about 3 weight percent silica.
- a leaching method is disclosed that is useful for increasing the porosity of the carbon and silica contained in naturally occurring or processed plant matter having more than 3 weight percent silica.
- high purity carbon-silica products are disclosed that comprise fixed carbon and silica in a desired mole ratio and minerals at a level well below 0.1 weight percent. The high purity carbon- silica products exhibit significantly improved porosity and reactivity, and are a preferred material for use in making other silicon-containing products as disclosed below.
- carbon-silica products are disclosed that have a mole ratio of fixed carbon to silica ranging from less than about 2:1 to greater than about 5:1, a total mineral content less than about 200 ppm, most preferably less than about 100 ppm, a boron content less than 1 ppm, and a phosphorous content less than 4 ppm.
- carbon-silica products are disclosed in which the carbon and silica are intimately mixed at a micron, submicron or nanometric scale.
- carbon-silica products can be produced in the form of a fine powder or made into pellets without the need for external binders, and are preferred for use in the subsequent production of silicon-containing products including, but not limited to, silicon carbide, silicon nitride, silicon, and silicon tetrachloride.
- silicon-containing products including, but not limited to, silicon carbide, silicon nitride, silicon, and silicon tetrachloride.
- carbon-silica products are disclosed that comprise accessible internal void volume of from about 30% to about 90%, and most preferably greater than about 50%.
- carbon-silica products are disclosed that are frangible and easily reduced in size with minimal energy consumption to powdered particles sizes in the fine (500 ⁇ m— 50 ⁇ m), very fine (50 ⁇ m -5 ⁇ m) and ultrafine (5 ⁇ m -submicron) categories.
- the average size and size distribution of the resulting particles is controlled by the process parameters as disclosed herein according to the characteristics desired in the final silicon-containing products.
- thermal and chemical devolatilization processes are disclosed that produce high purity, devolatilized carbon-silica products that exhibit significantly improved porosity and reactivity, and are themselves an embodiment of the invention.
- a carbothermal process is disclosed that generally involves heating the carbon-silica product and/or the devolatilized carbon-silica product as disclosed herein in a carbothermal reactor to a very high temperature to initiate reduction of the silica to a silicon-containing product.
- the carbothermal reactor desirably heats the presently disclosed carbon-silica product to about 1250°C to about 2200°C, depending upon the silicon-containing product of interest.
- FIGS, and IB which together comprise a process flow diagram illustrating in simplified n the various steps of preferred methods by which the products disclosed herein are ⁇ e from a preferred starting material such as rice hulls.
- rice hulls and rice straw are especially well suited for use in the present invention, and the following description will focus on the use of rice hulls. It is believed, however, that other naturally occurring or processed plant matter containing at least about 1 weight percent silica, and preferably at least about 3-5 weight percent silica can be similarly used.
- Rice hulls contain both fixed and volatile carbon, with volatile carbon being present primarily in the form of cellulose.
- Untreated rice hulls typically have a mole ratio of fixed carbon to silica of about 4:1, a volatile carbon to fixed carbon weight ratio of about 5.24, and a mineral content ranging from about one to about three weight percent (10,000 to 30,000 ppm).
- the methods of the invention are further described and explained with reference to FIGS. 1 A and IB.
- Rice hulls are desirably milled and screened to adjust the average particle size and to open up the hulls so that they can mix readily with aqueous sulfuric acid solutions as disclosed herein.
- the rice hulls are preferably milled to particle sizes ranging from about 10 ⁇ m to about 1mm. An average particle size of about 150 ⁇ m provides good results.
- the rice hulls contain dirt or other debris, they are preferably washed and dried before milling.
- Rice hulls obtained directly from a rice mill are usually relatively clean and require no washing and drying prior to milling.
- the rice hulls are preferably leached using an aqueous sulfuric acid solution.
- Sulfuric acid is believed to be particularly effective at removing minerals such as phosphorous, for adjusting the ratio of fixed carbon to silica in the leached rice hulls, for reducing the content of volatile carbon, and for increasing the porosity of the leached hulls.
- Suitable aqueous sulfuric acid solutions can comprise acid concentrations ranging from about 0.01 weight percent to more than 30 weight percent acid.
- From about 0.3 to about 1 weight percent acid is suitable for adjusting the mole ratio of fixed carbon to silica and for reducing minerals other than iron to very low levels. From about 1 to about 5 weight percent acid is suitable for accomplishing that which can be done in the low range plus reducing iron to the lowest levels. From about 5 to about 20 weight percent acid concentration is useful for removal of volatile carbon through the likely solubilization of cellulose. Sulfuric acid solutions more concentrated than about 30 weight percent are more expensive, more corrosive, and at high concentrations, may produce undesirable byproducts. By contrast, dilution of the sulfuric acid leaching solution to concentrations approaching the lower end of the range can reduce the effectiveness of the acid and increase the time required to achieve the desired product characteristics.
- the solids concentrations that can be satisfactorily used in the leaching method of the invention can range from. less than one percent to greater- than 35 percent by weight of the resultant mixture, with concentrations preferably ranging from about one to about 30 weight percent.
- a solids concentration in the range of from about 1 to about 10 weight percent provides for optimum removal of phosphorous with a single stage of leaching. However, if extremely low levels of phosphorous are not critical, then a higher solids range of from about 10 to about 30 weight percent provides for reduced water and acid consumption and minimum energy use in drying the carbon-silica product.
- the leaching process can be performed in single or multiple stages in a batch or continuous mode, and with various types of reactors and reactor configurations as desired. Temperatures below boiling (94-100°C) are suitable for removing non-silica
- 140°C, especially above 160°C are effective for removing volatile carbon and, at longer
- the solids and liquid are preferably mixed continuously during the leaching process so that all the solid particles are contacted by acid solution and so that heat is distributed throughout the mixture.
- leachi ⁇ tg times can range from as low as about six seconds to about 48 hours or more.
- the remaining solids are preferably separated from the acid solution and washed with water. Use of this method increases the measured void volume of milled rice hulls -from low values up to values ranging from at least about 30% to about 90%, with values greater than about 50% being generally preferred.
- the leaching method disclosed herein removes a large portion of the minerals that may have originally been present in the silica- containing plant matter.
- the fixed carbon to silica ratio can be adjusted as desired by controlling the sulfuric acid concentration, solids concentration, temperature, residence time and degree of m ing to produce carbon-silica products of high purity, high porosity, high reactivity, fine particle size, and intimately mixed fixed carbon and silica at mole ratios ranging from about 1 :1 or less up to about 5:1 or greater.
- a particular advantage of the subject method is that products can be selectively produced with fixed carbon-to-silica mole ratios of, for example, 1:1, 1.5:1, 2:1, 2.5:1, 3:1, 3.5:1, 4:1, 4.5:1, 5:1, or any preferred stoichiometric ratio for making various silicon-containing products.
- the leaching method of the invention can be demonstrated with a bench scale apparatus in which reactions at or below boiling are carried out in a 3-liter Pyrex resin kettle using a temperature controlled heating mantle. A water-cooled condenser is attached to the top of the kettle to insure t at the acid or solids concentration do not change during the reaction. Reactions above the boiling point of water are carried out in a 2-liter zirconium vessel.
- thermo couple is used to measure reactor temperature and a Teflon device is used to stir the contents of the reaction vessel.
- the reaction vessel and other components are preferably cleaned by treating with 50% HCl and then washed with demineralized water to remove any trace metal contaminants.
- demineralized water For leaching processes conducted at temperatures at or below boiling, the resin kettle is filled with an aqueous sulfuric acid solution and heated to the desired temperature. Once the kettle is at temperature, milled huLls are added to the kettle to give the desired solids concentration. The milled hulls immediately form a uniform mixture in the kettle and the mixture is periodically sampled. All samples are filtered and the filtered solids are washed several times with demineralized water.
- the washed solids samples are dried and are saved along with the filtrate for -analysis.
- an aqueous sulfuric acid solution and milled rice hulls are preferably added, to a zirconium vessel.
- the vessel is sealed and heated with gas-fired heaters to the desired reaction temperature. Once at reaction temperature, the temperature is maintained for the duration of the reaction time and the reaction mixture is periodically sampled. At the end of the reaction time, the vessel is quickly cooled with a water spray to a temperature below boiling. Samples are immediately filtered and then washed several times with demineralized water. The washed solids samples are dried and saved together with the filtrate for analysis.
- the phosphorous level is significantly reduced at temperatures below boiling, it is necessary to leach at temperatures above boiling, typically in the range of 120-14O°C, to achieve removal of phosphorous to very low levels, such as less than 4 ppm.
- the levels of iron are significantly reduced at temperatures below boiling, but it is necessary to go to temperatures above boiling, typically in the range of about 120°C to about 160°C to achieve iron levels of 10-20 ppm. Because boron is naturally low in rice hulls, the resulting boron concentration is less than 1 ppm. The resulting low phosphorous and boron contents make this process and tihe unique carbon-silica product very attractive for the production of photovoltaic grade silicon for use in the production of solar cells, as well as for other industrial applications.
- Test results show that temperature also has a significant effect on the removal of fixed carbon and consequently on the fixed carbon to silica mole ratio.
- sulfuric acid at temperatures as low at 25°C, a certain amount of fixed carbon is solubilized, but to remove enough fixed carbon to achieve the lower ratios of fixed carbon to silica, it is necessary to leach at temperatures at about boiling or above, preferably around 120°C.
- Temperature and time also have a significant effect on the removal of volatile carbon. At temperatures above 160°C and with relatively short reaction times, a large fraction of the volatile carbon is solubilized.
- A.cid concentration affects the rate of solubilization of carbon. For example, at 94°C, 1 0% solids, 100 minutes and 1% acid, the concentration of solubilized carbon in the acid solution is 5-6 gm/L. Under the same conditions at 2.5% acid, the concentration of solubilized carbon is 8-9 gm L. However, the extent of carbon solubilization is essentially the same at both acid concentrations, namely about 12.5 g/L. The effect of acid concentration on the ultimate mole ratio of fixed carbon-to-silica is relatively minor.
- a fixed carbon to silica mole ratio of about 2:1 and a very low level of minerals can be achieved with temperatures between about 94°C and about 140°C, sulfuric acid concentrations of about 1% to about 5% and solids concentrations of about 10% in about two hours.
- a fixed carbon to silica mole ratio of about 3:1 and a very low level of minerals can be achieved at temperatures in the range of about 150°C, sulfuric acid concentrations of about 1% to about 5% and solids concentrations of about 10% in about 4 hours.
- the leaching conditions preserve the intimate relationship between the silica and the fixed carbon, the amorphicity of the carbon and silica, the high surface area of the silica and carbon and provide for an overall increase in measurable void volume. If a fixed carbon to silica mole ratio of 3:1 is desired, but the levels of phosphorous and iron are not critical, a temperature of less than 94°C can be used with acid and solids concentration described above to achieve the sought ratio.
- the high purity (removal of over 99.7% of the minerals) carbon- silica product produced by the leaching process contains a mixture of fixed carbon and silica, together with varying amounts of volatile carbon.
- the carbon and silica are intimately mixed at least on a micron, and generally on a nanometer, scale.
- the carbon- silica product contains high porosity, small average particle size, and is highly reactive. The increased porosity in indicated by the fact that the accessible void volume of the milled rice hull particles is "very low, but, when the material is treated with 1% sulfuric acid at 94°C, the accessible void volume increases to 80%.
- the high reactivity of the produced material is established by the fact that the material undergoes carbothermal reduction significantly faster than when conventional feedstocks are used.
- Conventional feedstocks generally take a day or more to undergo carbothermal reduction.
- the carbon-silica products disclosed herein undergo carbothermal reduction for production of silicon carbide in under 75 minutes and within 5-7 hours for silicon nitride. This results in a substantial energy savings and greater throughput for operation of the carbothermal reactor.
- the leaching method of the invention can also be practiced in multiple stages. The first leaching stage can be used to remove a large portion of the minerals and make adjustments to the fixed carbon to silica mole ratio.
- the washed or unwashed material is then contacted a second time in a sulfuric acid solution. Thereafter, the remaining solids are separated from the acid solution by filtration or another similarly effective means, and washed with water.
- the second leaching stage can be used to reduce the mineral impurities to a lo-wer level than was achieved with a single-stage leaching to further adjust the mole ratio of fixed carbon to silica to a desired ratio ranging between about 5:1 to less than 2:1, and to reduce the level of volatile carbon. Additional stages of leaching can likewise be added to reduce the mineral impurity level of the solids even more while continuing to make adjustments in the fixed carbon to silica mole ratio and volatile carbon content.
- two-stage leaching is useful when it is desirable to carry out the leaching process at high solids concentrations while achieving a low fixed carbon to silica ratio and very low non-silica mineral content, including very low levels of phosphorous.
- higher solids concentrations (approaching 30%) provide higher fixed carbon-to-silica ratios than lower solids concentrations for single-stage leaching.
- Higher solids concentrations also result in a higher phosphorous content than lower solids concentrations for single-stage leaching.
- the first stage will reduce th-e fixed carbon-to-silica ratio to 3:1 or less (but greater than 2:1) and will reduce all the non-silica minerals except phosphorous to very low levels.
- the phosphorous will be significantly reduced compared to the starting values, but will remain higher than desired.
- the first stage is operated at 25% solids, 1% acid, and 140°C for 15 minutes, the fixed carbon-to-silica ratio is reduced to between 3:1 and 2.5:1.
- the levels of sodium, potassium, magnesium, and manganese are reduced to less than 10 ppm. Tlie level of calcium is 10 ppm and the level of iron is 20 ppm. However phosphorous is at 100 ppm.
- the fixed carbon-to-silica mole ratio is further- reduced to low values of around 2:1 or less, and phosphorous is reduced to very low values of less than 4 ppm.
- phosphorous levels are reduced by more than 99.96%, to less than 4 ppm with a single stage of leaching at 120°C, 10 % solids, 1% acid and a time of 15 minutes or less.
- the iron levels are reduced by over 92% to values less than 20 ppm with a single stage of leaching at 140°C, 28.6% solids, 1% acid and a time of 15 minutes or less.
- the leact ⁇ ng process for the sole purpose of reducing total minerals to overall low values for example, the total level of sodium, potassium, magnesium, calcium, manganese, iron and phosphorous is reduced to less than 79 ppm with a single stage of leaching at 120°C, 10% solids, 1% acid and a time of 15 minutes or less.
- the fixed carbon to silica mole ratio of the rice hulls is reduced from 3.88:1 to 3:1 using a single stage of leaching at 25°C, 10% solids, 1% acid and times ranging from 1 minute to 60 minutes.
- this ratio can be reduced to 2:1 with a single stage of leaching at 94°C, 10% solids, 1% acid and a time of 300 minutes.
- the native fixed carbon to silica mole ratio o rice hulls used in this study is 3.88:1. This ratio can be increased to 5:1 with a single stage of leaching at 200°C, 10% solids and 1% acid in 120 minutes.
- the mole ratio of fixed carbon to silica can be increased to any higher value up to about 5:1 by operating a second stage of leaching at a temperature above 160°C for longer reaction times.
- Another application of this invention relates to use of the leaching process, either single stage or multiple stages, for the sole purpose of increasing the porosity.
- the accessible void volume in milled hulls is rapidly increased to 30% after 15 minutes of leaching at 94°C and 1% acid.
- the void volume increases yet further to 80 % after 30 minutes of leaching under the same conditions.
- Another application of the invention relates to use of the leaching process, either single stage or multiple stages, for a combination of any two or more of: removing phosphorous, iron or other minerals from naturally occurring or processed plant matter containing more than 3 weight percent silica; adjusting the mole ratio of fixed carbon to silica; removing volatile carbon; converting volatile car on to fixed carbon; and increasing the porosity of the resultant carbon-silica products.
- Another application of this invention relates to a preferred method for thermally volatilizing the volatile carbon component of the carbon-silica product in a reactor separate from the carbothermal reactor.
- This reaction can be performed in a bench-scale alumina reactor fitted with a metal head plate, and. can be scaled up for industrial application using conventional process equipment. If desired, other materials such as graphite can be used to construct the reactor.
- the bencti-scale reactor is three feet long and six inches in diameter.
- the carbon-silica product is contained in an alumina or graphite crucible that was located at the bottom of the reactor.
- the lower portion of the reactor is positioned in an electric furnace that is controlled by a program that allows different rates of temperature rise.
- the furnace heats the carbon-silica product from ambient temperature to over 1,000°C.
- Argon or nitrogen enters the top of the reactor and is directed to a particular level in the reactor through an adjustable tube.
- Volatilized carbonaceous material exits the reactor through the top.
- a slipstream of this material is sent to a CO monitor, and the majority of the material is directed to a condenser where the condensables are separated from the gases.
- Volatilization starts at about 400°C and reaches a peak at about 600°C. Subsequently, the carbon monoxide levels decrease, reaching a base line at about 950°C. This profile differs from those reported for raw rice hulls in that, with raw rice hulls, the volatilization process starts at ab out 250°C.
- the material that normally volatilizes at lower temperatures has been removed by the leaching process from the carbon-silica product.
- the volatilized gases and vapors can be captured and used as an energy source for the leaching process, the carbothermal process or other processes.
- a further benefit is that a portion of the remaining mineral content is also volatilized with the volatile carbon.
- the volatilized mineral can be collected in order to further purify the resulting devolatilized carbon-silica product.
- the resulting material is in the form of thermal-devolatilized carbon-silica [products, which are unique products and are themselves an embodiment of this invention.
- most if not all of the volatile carbon is removed by further treating the unique carbon-silica products produced from the leaching step with dilute sulfuric acid at temperatures ranging from about 160°C up to about 200°C.
- the residence time at the higher temperatures is very short, on the order of about 1 minute. This significantly lowers the volatile carbon content with minimal effect on the fixed carbon content of the solids.
- This method also removes a portion of the residual minerals left in the carbon silica products derived from the leaching step, enhancing the purity of the resulting high purity acid devolatilized carbon-silica products. The remaining solids are separated from the acid solution and the solids are washed with water.
- the resulting solid material is a high purity, devolatilized carbon-silica product with a predetermined fixed carbon-to-silica ratio and mineral impurities well below 0.1 weight percent.
- a variety of unique acid devolatilized carbon-silica products each of which has a predetermined molar ratio of fixed carbon to silica, contains very low levels of minerals and are highly porous and highly reactive, can be produced by tb.e leaching step followed by an acid devolatilization step.
- the products preferably have a desired mole ratio of fixed carbon to silica from around 3:1 to less than 2:1, have a total mineral content less than 100 ppm, have a boron content less than 1 ppm, and have a phosphorous content less than 4 ppm.
- the products also preferably are highly porous and highly reactive and contain silica and fixed carbon that are intimately mixed at the micron and/or nanometric level. These unique materials can be produced in a fine powder form or made into pellets without the need for external binders.
- the disclosed devolatilized carbon- silica products are preferred for use in the subsequent production of silicon containing products, including, but not limited to, silicon carbide, silicon nitride, silicon, and silicon tetrachloride.
- the carbon-silica products of the invention are frangible and easily reduced in size with minimal energy consumption to particles sizes in the fine (500 ⁇ m to 50 ⁇ m), very fine (50 ⁇ m to 5 ⁇ m) and ultrafine (5 ⁇ m to submicron) categories.
- the average size and size distribution of the resulting particles is set by the physical characteristics desired in the final silicon-containing products.
- Milling devices suitable for this purpose include, for example, batch impeller- type stirred ball mills, continuous disc-type stirred ball mills, continuous vibrating ball mills, batch vertical vibrating ball mills, and fluid energy mills such as a continuous loop mill or a continuous pancake mill.
- Either a carbon-silica product or a devolatilized carbon-silica product can be used as a powder or, in another embodiment of this invention, can be pelletized for- use in subsequent processes.
- the conventional method of producing pellets involves mixing silica and carbon compounds with a binding agent, such as sugar, and then- compressing the mixture into a pellet.
- a binding agent such as sugar
- the use of a conventional binding agent increases the cost of processing and the binding agent may introduce impurities into the pelletized product.
- the unique carbon-silica products and the devolatilized carbon-silica products of the present invention can be pelletized without the use of an additional binder.
- the lignin and cellulose that are present in the product can act as a sufficient binding agent for the silica and carbon.
- use of the current invention results in pellets that have carbon and silica intimately admixed at the ⁇ m and nanometer scale. This intimate mixture of highly reactive forms of the carbon and silica facilitate production of a pellet that reacts more quickly and completely during the subsequent carbothermal reaction than conventional pellets.
- the pelletized products made from carbon-silica products and/or devolatilized carbon-silica products as disclosed herein contain a desired mole ratio of fixed carbon to silica and/or very low levels of minerals, especially low levels of phosphorous and iron, and constitute another embodiment of the invention.
- the carbothermal reduction method of the invention generally involves heating the carbon-silica product and/or the devolatilized carbon-silica product in a carbothermal reactor to a very high temperature to initiate the reduction of the silica to the silicon-containing product.
- Carbothermal reactors generally will heat the carbon-silica composition to about 1350-1800°C, depending upon the silicon-containing product of interest.
- reaction times are extremely fast compared to conventional carbothermal processes that use conventional sources of silica and carbon.
- reaction times are on the order of minutes to a few hours, depending upon the desired silicon-containing product. This compares to times of a day or more for most conventional carbothermal processes that use conventional sources of silica and carbon.
- the fast reaction time provides for significantly lower use of energy and higher throughput compared to conventional carbothermal processes that use conventional sources of silica and carbon.
- carbon silica product and devolatilized carbon silica product are available in the form of fine powder, these products can be readily used in advanced carbothermal reactor systems, whereas conventional sources of carbon and silica cannot.
- Examples of commercial equipment that can be used to implement the advanced carbothermal processes disclosed herein include, but are not limited to, static bed reactors, moving bed reactors, fluidized bed reactors; rotary tube reactors, laser reactors, flame reactors, furnace reactors employing an external heat source; and plasma reactors. Many of these advanced reactors can provide for isothermal conditions and controlled reaction times, both of which are important for silicon-containing product quality.
- novel carbon-silica products of the invention can, if desired, contain significant amounts of volatile carbon, use of these unique materials affords the opportunity to recover significant volatile carbon during the carbothermal process and use such material for energy purposes or other valuable purposes.
- the use of energy from the volatilized carbon can reduce and perhaps eliminate the need to acquire energy from an outside source to operate the carbothermal process.
- a further benefit is that a portion of the remaining mineral content is also volatilized along with the volatile carbon.
- the volatilized minerals can be separately collected in order to further purify the final silicon-containing product.
- the reaction is performed in an alumina reactor fitted with a metal head plate.
- the reactor is three feet long and six inches in diameter.
- the carbon-silica product or the devolatilized carbon-silica product is contained in an alumina or graphite crucible that is located at the bottom of the reactor.
- the lower portion of the reactor is positioned in an electric furnace that is controlled by a program that allows different rates of temperature rise.
- the furnace generally heats the carbon-silica product to a temperature ranging from about 1250 to about 2200°C, preferably from about 1350 to about 1800°C depending upon the type of silicon-containing product to be produced.
- Inert, and/or reactive gas enters the top of the reactor and is directed to a particular level in the reactor through an adjustable tube.
- volatilized carbonaceous material exits the reactor through a gas outlet tube attached to the metal head plate.
- a slipstream of the off-gas is sent to a CO monitor, and the majority of the material is directed to a condenser where the condensables are separated from the gases.
- the atmosphere used in the carbothermal reactor depends upon the silicon-containing product that is desired. For silicon carbide and silicon, argon can be used. To produce silicon nitride, pure nitrogen or 90% nitrogen plus 10% hydrogen or 90% nitrogen plus 10% ammonia can be used.
- a chlorine atmosphere can be used to produce silicon tetrachloride.
- SiO gas Due to the loss of SiO gas from the carbothermal reactor and/or the desire to have carbon in the silicon-containing product, and/or the desire to have excess carbon fed to the reactor to insure complete conversion of the non-carbon reactants, the actual desired mole ratio of fixed carbon to silica will generally be different from the theoretical value. For example, the theoretical fixed carbon to silica mole ratio for production of silicon carbide is 3:1 and the theoretical ratio for production of silicon and silicon nitride is 2:1. However, the optimum ratio for a particular reactor may be less than the theoretical value, depending on the efficiency of the particular reactor in terms of loss of SiO gas..
- This invention provides the means to produce material with a carbon to silica ratio that is "rich” in silica compared to the theoretical ratio to accommodate the loss of SiO.
- this invention provides the means to produce material with a carbon-to-silica ratio that is "rich” in carbon compared to the theoretical ratio in order to accommodate the desire for leftover carbon.
- this invention provides the means to produce a carbon rich carbon-silica product and/or carbon rich devolatilized carbon silica product for such applications.
- this invention provides the means to produce a carbon-silica product or devolatilized carbon-silica product with the optimum carbon-to-silica mole ratio for the given situation.
- Milled rice hulls and the solid and liquid samples were analyzed by a variety of methods. Proximate analysis was used to determine percent moisture, percent volatile carbon, percent fixed carbon, and percent ash in the solids. The solids were also analyzed for total carbon and for SiO 2 . The solid samples were also analyzed for mineral content using spark source mass spectroscopy, glow discharge mass spectroscopy, atomic absorption spectroscopy, and x-ray fluorescence.
- Example 1 Rice hulls were obtained from a mill in Arkansas. The hulls were mixed and then milled in a ring and puck mill to achieve an average particle size of 138 ⁇ m. The milled hulls were analyzed via proximate analysis and for SiO 2 content. They were found to contain 7.17 % moisture, 62.72% volatile carbon, 11.97 % fixed carbon and 18.14 % ash.
- the ash was 85% silica (SiO2).
- the fixed carbon to silica ratio (mole: mole) was 3.88.
- the volatile carbon to fixed carbon ratio (wt %: wt %>) was 5.24.
- the milled hulls were also analyzed for mineral content by spark source mass spectroscopy and contained amounts of the specified minerals as shown in Table 1. Table 1
- a 1% sulfuric acid solution was prepared using demineralized water.
- the acid solution containing 10% milled rice hulls was added to a 2 liter zirconium reactor and heated to 120°C. Once at reaction temperature, the contents of the reactor were sampled frequently. The samples were immediately filtered and washed with demineralized water. The solids were dried and saved for analysis along with the filtrate. [0085] The dried solids were analyzed by proximate analysis and silica analysis. The analyses showed that the fixed carbon to silica mole ratio at 120 minutes was 2.04:1, which is essentially the theoretical ratio for production of silicon and silicon nitride.
- the overall percent removal of the specified minerals using a single stage of leaching was greater than 99.7 %, giving a product with a specified mineral impurity less than 79 ppm.
- sulfuric acid at the temperature and acid concentration used in the test with a single stage of leaching, is very effective at removing phosphorous to very low levels of less than 4 ppm.
- the resulting carbon-silica material was in the form of a fine powder with a void volume of about 80%. In other carbon-silica products leached in a similar manner, the boron level is 1 ppm as measured by spark source mass spectroscopy.
- Example 2 [0086] A 1% sulfuric acid solution was prepared using demineralized water.
- the acid solution containing 10% milled rice hulls was added to a 2 liter zirconium reactor and heated to 160°C. Once at reaction temperature, the contents of the reactor were sampled frequently. The samples were immediately filtered and washed with demineralized water. The solids were dried and saved for analysis along with the filtrate. [0087] The dried solids were analyzed by proximate analysis and silica analysis. The analyses showed that the fixed carbon to silica mole ratio at 180 minutes was 3:1, which is the theoretical ratio for the production of silicon carbide.
- the overall percent removal of the specified minerals using a single stage of leaching was greater than 99.7%, yielding a product with a mineral impurity level less than 79 ppm for the specified minerals.
- sulfuric acid at the temperature and acid concentration used in the test with a single stage of leaching, is very effective at removing phosphorous to very low levels less than 4 ppm.
- the boron level is 1 ppm as measured by spark source niass spectroscopy.
- the resulting carbon-silica material was in the form of a fine powder with a void volume of about 80%.
- Example 3 [0088] A 1% sulfuric acid solution was prepared using demineralized water.
- the acid solution was added to a 3-liter Pyrex resin kettle and heated to 94°C. Once at temperature, milled rice hulls were added to the kettle to create a mixture with 10% solids. The milled hulls were immediately incorporated into the acid solution producing a well-mixed slurry. The reaction was carried out for five minutes. At the end of this time, the contents of the kettle were filtered and washed with demineralized water. The resulting solid material was dried. This procedure was repeated four more times. The dried solids from each run were combined. [0089] The fixed carbon-to-silica mole ratio of the combined carbon-silica product was 2:51:1, which is between the theoretical ratio for producing silicon carbide and the theoretical ratio for producing silicon nitride.
- Example 4 Malvern analysis of the material indicated a d50 particle diameter of 114 um.
- Example 4 The material prepared in Example 3 was used to test the production of silicon carbide. According to a preferred carbothermal method of the invention using bench-scale apparatus, the reaction was performed in the alumina reactor described previously. The reactor was purged with pure argon. After the air was purged from the reactor, the temperature was increased from ambient to the final carbothermal reaction temperature of 1,550°C. The purge with argon was continued. The carbon monoxide in the off-gas was monitored and it was observed that volatilization of volatile carbon started at about 400°C. A carbon monoxide peak was reached at about 600°C and the carbon monoxide level declined, reaching a base line at about 950°C.
- the carbon monoxide level began to increase, indicating the start of the reaction between fixed carbon and silica, and reached a peak at 1,550°C. Soon after reaching 1,550°C, the carbon monoxide level began to decrease rapidly, reaching a baseline level in about 60 minutes.
- the total elapsed time between when the production of silicon carbide started and when it ended was about 75 minutes, which was much shorter than the reaction time for the commercial Acheson process, which reaction time is typically about 36 hours.
- the resulting product contained only silicon carbide and no other crystalline material.
- the silicon carbide is composed of microcrystals with dimensions of about 15 nanometers. These microcrystals are grouped into particles that are about 200 nanometers in diameter. Silicon carbide particles in the nanometric range are sought for the production of high end silicon carbide ceramics and other high-end applications.
- This unique carbothermal process involving the unique carbon-silica product as feedstock and the unique silicon carbide product are embodiments of this invention
- Example 5 The material prepared in Example 3 was used to produce silicon nitride. According to a preferred carbothermal method of the invention using bench-scale apparatus, the reaction was performed in the alumina reactor described previously. The reactor was purged with pure nitrogen and the temperature was increased from ambient to the final carbothermal reaction temperature of 1425° while continuing the nitrogen purge.
- the carbon monoxide in the off-gas was monitored and it was observed that volatilization of volatile carbon started at about 400°C.
- a carbon monoxide peak was reached at about 600°C and the carbon monoxide level then declined, reaching a base line at about 950°C.
- the carbon monoxide level again began to increase, indicating the start of the reaction between fixed carbon and silica, and reached a peak at 1425°C.
- the carbon monoxide level again began to decline, slowly reaching a baseline level.
- the total elapsed time between when the production of silicon nitride started and when it ended was about 5-7 hours.
- the resulting product contained only silicon nitride and no other crystalline material.
- the silicon nitride is a mixture of acicular crystals with a very high aspect ratio and small particles. Silicon nitride consisting of long acicular crystals mixed with small particles is a self-reinforcing form of silicon nitride that is ideal for producing superior silicon nitride ceramics and for other high-end applications.
- This carbothermal process involving the unique carbon-silica product as feedstock and the unique silicon nitride product produced by the process are embodiments of this invention.
- Example 6 [0092] The material prepared in Example 3 was used to produce silicon nitride.
- the reaction was performed in the alumina reactor as described in Example 5 above, except that a mixture of 90% nitrogen and 10% hydrogen was used in place of 100%) nitrogen.
- the total elapsed time was again about 5-7 hours, which was much shorter than the reaction time for the commercial carbothermal process, which time is measured in days.
- the resulting product contained only silicon nitride and no other crystalline material.
- the yield of silicon nitride was about 2 times that obtained with a pure nitrogen atmosphere.
- the silicon nitride was a mixture of small particles only. Silicon nitride consisting of small particles is sought after for the production of high-end ceramics and other high-end applications.
- Example 7 [0093] The material prepared in Example 3 was used to produce silicon nitride. According to a preferred carbothermal method of the invention using bench-scale apparatus, the reaction was performed in the alumina reactor as described in Example 5 above, except that a mixture of 90% nitrogen and 10% ammonia was used in place of 100% nitrogen. The total elapsed time was again about 5-7 hours, which was much shorter than the reaction time for the commercial carbothermal process, which time is measured in days. As determined by x-ray diffraction, the resulting product contained only silicon nitride and no other crystalline material.
- the yield of silicon nitride was comparable to that achieved with a pure nitrogen atmosphere.
- the silicon nitride is a mixture of acicular crystals with a moderate aspect ratio and small particles. This type of material is a self-reinforcing form of silicon nitride that is ideal for the production of superior ceramics and other high-end applications.
- This carbothermal process involving the unique carbon- silica product as feedstock and the unique silicon nitride product produced by the pro cess are embodiments of this invention.
- carbon-silica products as disclosed herein are used in the carbothermal process of the invention, remaining volatile carbon is released at temperatures below the temperature needed to effect the reaction between fixed carbon and silica to make the desired silicon-containing product.
- This released volatile carbon can be captured and used for fuel, either to provide energy to the carbothermal process or to some other process such as, for example, the leaching process. Further devolatilization of the carbon-silica products of the invention inside the reactor will also further reduce the impurities present in the resultant silicon-containing product because some of the contaminating minerals and metals will be volatilized and removed along with the volatile carbon. [0095]
- the above-described processes and the unique carbon-silica products and devolatilized carbon silica products created therefrom can be used in other known reactor configurations or carbothermal processes to produce other types of silicon- containing products.
- the faster reaction times provide a shorter residence time insider the reactor at temperature and there is much less chance for the undesirable secondary effects to occur, meaning that the particle size and crystalline phase of the products are not compromised.
- faster reaction rates typically produce higher product yields
- carbothermal process practiced as disclosed herein using the improved carbon-silica products or devolatilized carbon-silica products of the invention as feed material, will produce better product yields compared to conventional carbothermal processes.
- the carbon-silica products and devolatilized carbon-silica products used as starting materials are very pure, the resulting silicon-containing products are also very pure.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- General Health & Medical Sciences (AREA)
- Silicon Compounds (AREA)
- Carbon And Carbon Compounds (AREA)
Priority Applications (6)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| BRPI0509837-8A BRPI0509837A (pt) | 2004-04-13 | 2005-04-12 | método para fabricar produtos de carbono-sìlica, produto, sìlicio, carboneto de silìcio, nitreto de silìcio, e, tetracloreto de silìcio |
| KR1020067023757A KR101253064B1 (ko) | 2004-04-13 | 2005-04-12 | 규소 함유 생성물을 제조하기 위한 조성물 및 방법 |
| EP05737064A EP1735088A4 (en) | 2004-04-13 | 2005-04-12 | COMPOSITION AND PROCESS FOR PRODUCING SILICON-CONTAINING PRODUCTS |
| AU2005233172A AU2005233172A1 (en) | 2004-04-13 | 2005-04-12 | Composition and method for making silicon-containing products |
| CN200580015881.3A CN101014533B (zh) | 2004-04-13 | 2005-04-12 | 制备含硅产物的组合物和方法 |
| JP2007508454A JP5133051B2 (ja) | 2004-04-13 | 2005-04-12 | 高純度の珪素含有生成物 |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US10/822,924 US7588745B2 (en) | 2004-04-13 | 2004-04-13 | Silicon-containing products |
| US10/822,924 | 2004-04-13 |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| WO2005099893A2 true WO2005099893A2 (en) | 2005-10-27 |
| WO2005099893A3 WO2005099893A3 (en) | 2007-03-08 |
Family
ID=35061317
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/US2005/012302 Ceased WO2005099893A2 (en) | 2004-04-13 | 2005-04-12 | Composition and method for making silicon-containing products |
Country Status (8)
| Country | Link |
|---|---|
| US (2) | US7588745B2 (enExample) |
| EP (1) | EP1735088A4 (enExample) |
| JP (2) | JP5133051B2 (enExample) |
| KR (1) | KR101253064B1 (enExample) |
| CN (1) | CN101014533B (enExample) |
| AU (1) | AU2005233172A1 (enExample) |
| BR (1) | BRPI0509837A (enExample) |
| WO (1) | WO2005099893A2 (enExample) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| WO2013143377A1 (zh) * | 2012-03-26 | 2013-10-03 | 阳光凯迪新能源集团有限公司 | 利用工业烟气去除稻壳中金属离子的方法 |
Families Citing this family (27)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2827592B1 (fr) * | 2001-07-23 | 2003-08-22 | Invensil | Silicium metallurgique de haute purete et procede d'elaboration |
| US8470279B2 (en) * | 2004-04-13 | 2013-06-25 | Si Options, Llc | High purity silicon-containing products and method of manufacture |
| AU2007226533B2 (en) * | 2006-03-15 | 2012-12-13 | Reaction Sciences, Inc. | Method for making silicon for solar cells and other applications |
| CA2659750C (en) * | 2006-08-02 | 2014-05-13 | Neal A. Hammond | Biogenic silica from silica-containing plant material such as rice hulls |
| CN101785990B (zh) * | 2010-02-09 | 2012-07-25 | 乐山师范学院 | 四氯化硅用于活性炭-二氧化硅混合吸附材料的制备 |
| CN101746759B (zh) * | 2010-02-11 | 2012-07-25 | 浙江工业大学 | 一种利用植物纤维合成碳化硅纳米线的方法 |
| CN101837948B (zh) * | 2010-05-05 | 2013-01-09 | 吉林大学 | 一种稻壳液化及综合利用的新方法 |
| WO2012166728A1 (en) * | 2011-06-01 | 2012-12-06 | Robert Larsen | Materials from rice hull ash |
| US9920929B2 (en) * | 2011-06-13 | 2018-03-20 | Ecolab Usa Inc. | Method for reducing slag in biomass combustion |
| JP6005045B2 (ja) * | 2011-07-04 | 2016-10-12 | 太平洋セメント株式会社 | シリカとカーボンの混合物の製造方法 |
| KR101986871B1 (ko) * | 2012-04-02 | 2019-06-07 | 스미토모덴키고교가부시키가이샤 | 다공질 탄소 재료의 제조 방법 |
| CN102649047B (zh) * | 2012-05-17 | 2014-02-19 | 乐山川博吸附材料有限责任公司 | 一种C-SiO2吸附材料的制备方法 |
| WO2013190945A1 (ja) * | 2012-06-20 | 2013-12-27 | 住友電気工業株式会社 | 金属ケイ素及び多孔質炭素の製造方法 |
| KR102017689B1 (ko) * | 2012-10-18 | 2019-10-21 | 엘지이노텍 주식회사 | 탄화규소 분말의 제조 방법 |
| JP6037823B2 (ja) * | 2012-12-27 | 2016-12-07 | 太平洋セメント株式会社 | 高純度の炭化ケイ素の製造方法 |
| KR101484173B1 (ko) * | 2013-07-23 | 2015-01-21 | 광주과학기술원 | 가스 저장용 나노다공성 탄소 소재 및 이의 제조방법 |
| CN105032362A (zh) * | 2015-03-05 | 2015-11-11 | 中霖中科环境科技(安徽)股份有限公司 | 一种对秸秆进行等离子体处理后吸附印染废水的方法 |
| CN107200887A (zh) * | 2017-06-07 | 2017-09-26 | 常州兆威不锈钢有限公司 | 一种覆盖胶 |
| CN109279612A (zh) * | 2018-11-09 | 2019-01-29 | 吉林大学 | 一种水热法制备活性二氧化硅/碳双相填料的方法 |
| CN109437203B (zh) * | 2018-11-09 | 2020-07-31 | 北京科技大学 | 一种高纯一维SiC纳米材料的制备方法 |
| CN111422875B (zh) * | 2020-02-25 | 2021-01-19 | 上海恒仑新能源科技有限公司 | 一种生物氧化亚硅的制备方法及其产物 |
| CN112877093B (zh) * | 2021-01-14 | 2023-12-05 | 长江大学 | 一种破乳剂、破乳剂组合物及其制备方法和应用 |
| CN113336233B (zh) * | 2021-07-13 | 2022-05-13 | 江西省矿产资源保障服务中心 | 一种高纯纳米石英粉的制备方法 |
| CN113353914B (zh) * | 2021-07-13 | 2022-05-24 | 江西省矿产资源保障服务中心 | 一种以矿物为原料制备介孔碳的方法 |
| CN113387366B (zh) * | 2021-07-13 | 2022-05-24 | 江西省矿产资源保障服务中心 | 一种以矿物为原料制备介孔硅的方法 |
| CN116023947A (zh) * | 2022-12-02 | 2023-04-28 | 钱卫群 | 一种固态氢制品及其制备方法和应用 |
| CN115939402B (zh) * | 2023-01-09 | 2023-05-30 | 天目湖先进储能技术研究院有限公司 | 一种硅基材料及其制备方法和在负极中的应用 |
Family Cites Families (87)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3855395A (en) * | 1972-09-06 | 1974-12-17 | Univ Utah | Production of silicon nitride from rice hulls |
| JPS53102300A (en) * | 1977-02-18 | 1978-09-06 | Toshiba Corp | Preparation of type silicon nitride powders |
| US4214920A (en) * | 1979-03-23 | 1980-07-29 | Exxon Research & Engineering Co. | Method for producing solar cell-grade silicon from rice hulls |
| US4247528A (en) * | 1979-04-11 | 1981-01-27 | Dow Corning Corporation | Method for producing solar-cell-grade silicon |
| US4248844A (en) * | 1980-01-28 | 1981-02-03 | Great Lakes Carbon Corporation | Production of SiC from rice hulls and silica |
| JPS6052119B2 (ja) * | 1982-04-01 | 1985-11-18 | タテホ化学工業株式会社 | 窒化珪素ウイスカ−の製造方法 |
| EP0092227B1 (en) * | 1982-04-19 | 1988-07-27 | Nissan Motor Co., Ltd. | Method for controlling reduction ratio of continuously variable transmission with acceleration compensation |
| JPS6052120B2 (ja) * | 1982-06-04 | 1985-11-18 | タテホ化学工業株式会社 | 炭化珪素の製造方法 |
| JPS5935009A (ja) * | 1982-08-19 | 1984-02-25 | Toyota Central Res & Dev Lab Inc | 窒化珪素の製造方法 |
| JPS6016811A (ja) | 1983-07-11 | 1985-01-28 | Toyota Central Res & Dev Lab Inc | 炭化珪素の製造方法 |
| KR850004274A (ko) * | 1983-12-13 | 1985-07-11 | 원본미기재 | 에리트로포이에틴의 제조방법 |
| NZ210501A (en) * | 1983-12-13 | 1991-08-27 | Kirin Amgen Inc | Erythropoietin produced by procaryotic or eucaryotic expression of an exogenous dna sequence |
| US4703008A (en) * | 1983-12-13 | 1987-10-27 | Kiren-Amgen, Inc. | DNA sequences encoding erythropoietin |
| US4610896A (en) * | 1985-04-08 | 1986-09-09 | United Technologies Corporation | Method for repairing a multilayer coating on a carbon-carbon composite |
| US4667016A (en) * | 1985-06-20 | 1987-05-19 | Kirin-Amgen, Inc. | Erythropoietin purification |
| JPS6217012A (ja) | 1985-07-12 | 1987-01-26 | Agency Of Ind Science & Technol | 四塩化ケイ素の製造方法 |
| US4818700A (en) * | 1985-10-25 | 1989-04-04 | Phillips Petroleum Company | Pichia pastoris argininosuccinate lyase gene and uses thereof |
| US4812405A (en) * | 1986-02-18 | 1989-03-14 | Phillips Petroleum Company | Double auxotrophic mutants of Pichia pastoris and methods for preparation |
| DK173067B1 (da) * | 1986-06-27 | 1999-12-13 | Univ Washington | Humant erythropoietin-gen, fremgangsmåde til ekspression deraf i transficerede cellelinier, de transficerede cellelinier sa |
| JPH0622680B2 (ja) * | 1987-09-28 | 1994-03-30 | 工業技術院長 | 触媒及びその製造方法 |
| JPH01189348A (ja) * | 1988-01-22 | 1989-07-28 | Agency Of Ind Science & Technol | 触媒活性成分及び担体の廃触媒からの回収方法 |
| JPH0645450B2 (ja) * | 1988-03-30 | 1994-06-15 | 電気化学工業株式会社 | 四塩化ケイ素の製造方法 |
| WO1990008822A1 (en) * | 1989-02-03 | 1990-08-09 | Genetics Institute, Inc. | Erythropoietin receptor |
| DE3923963A1 (de) * | 1989-07-20 | 1991-01-31 | Behringwerke Ag | Muteine des menschlichen erythropoetins, ihre herstellung und ihre verwendung |
| DE3924746A1 (de) * | 1989-07-26 | 1991-01-31 | Behringwerke Ag | Erythropoietin (epo)-peptide und dagegen gerichtete antikoerper |
| US5856298A (en) * | 1989-10-13 | 1999-01-05 | Amgen Inc. | Erythropoietin isoforms |
| US5085582A (en) * | 1990-07-24 | 1992-02-04 | Eaton Corporation | Silicon nitride containers for the sintering of silicon nitride ceramics |
| US5292654A (en) * | 1990-12-13 | 1994-03-08 | Whitehead Institute For Biomedical Research | Mutant EPO receptor and uses therefor |
| BR9205846A (pt) * | 1991-03-22 | 1994-08-02 | Dow Chemical Co | Processo para preparar um pó de nitreto metálico ou carbeto metálico a partir de um óxido metálico correspondente |
| JP3210383B2 (ja) * | 1992-01-22 | 2001-09-17 | 株式会社東芝 | ヘテロ接合バイポーラトランジスタ |
| US6153407A (en) * | 1992-07-28 | 2000-11-28 | Beth Israel Deaconess Medical Center | Erythropoietin DNA having modified 5' and 3' sequences and its use to prepare EPO therapeutics |
| US5614184A (en) * | 1992-07-28 | 1997-03-25 | New England Deaconess Hospital | Recombinant human erythropoietin mutants and therapeutic methods employing them |
| US5782982A (en) * | 1993-03-26 | 1998-07-21 | Arkenol, Inc. | Method of removing silica or silicates from solids resulting from the strong acid hydrolysis of cellulosic and hemicellulosic materials |
| FI955128L (fi) * | 1993-04-29 | 1995-10-27 | Abbott Lab | Erytropoietiinianalogikoostumuksia ja menetelmä niiden valmistamiseksi ja käyttämiseksi |
| US5364608A (en) * | 1993-07-30 | 1994-11-15 | Eaton Corporation | Method of converting a silicon nitride from alpha-phase to beta-phase, apparatus used therefor, and silicon nitride material made therefrom |
| US5830851A (en) * | 1993-11-19 | 1998-11-03 | Affymax Technologies N.V. | Methods of administering peptides that bind to the erythropoietin receptor |
| US5773569A (en) * | 1993-11-19 | 1998-06-30 | Affymax Technologies N.V. | Compounds and peptides that bind to the erythropoietin receptor |
| US6316254B1 (en) * | 1994-02-14 | 2001-11-13 | University Of Washington | Methods for stimulating erythropoiesis using hematopoietic proteins |
| US5856179A (en) * | 1994-03-10 | 1999-01-05 | Genentech, Inc. | Polypeptide production in animal cell culture |
| US5494892A (en) * | 1994-03-17 | 1996-02-27 | International Flavors & Fragrances Inc. | Methyl substituted propyl-substituted pentamethyl indane derivatives processes for producing same and perfumery uses thereof |
| US6099830A (en) * | 1994-08-09 | 2000-08-08 | Zymogenetics, Inc. | Methods for stimulating erythropoiesis using hematopoietic proteins |
| JPH08104513A (ja) | 1994-10-04 | 1996-04-23 | Takeko Suda | モミガラの含有するケイ酸を、モミガラを浸して処理した処理液から回収する方法。 |
| US5767078A (en) * | 1995-06-07 | 1998-06-16 | Johnson; Dana L. | Agonist peptide dimers |
| US5955349A (en) * | 1996-08-26 | 1999-09-21 | Zymogenetics, Inc. | Compositions and methods for producing heterologous polypeptides in Pichia methanolica |
| US6375735B1 (en) * | 1996-05-06 | 2002-04-23 | Agritec, Inc. | Precipitated silicas, silica gels with and free of deposited carbon from caustic biomass ash solutions and processes |
| KR100199445B1 (ko) * | 1996-06-11 | 1999-06-15 | 이서봉 | 복합분자체 화합물의 제조방법 |
| TW586933B (en) * | 1996-06-20 | 2004-05-11 | Chugai Pharmaceutical Co Ltd | Compositions for treating liver-complaints using EPO |
| US5736383A (en) * | 1996-08-26 | 1998-04-07 | Zymogenetics, Inc. | Preparation of Pichia methanolica auxotrophic mutants |
| US6221608B1 (en) * | 1997-01-22 | 2001-04-24 | Ortho Pharmaceutical Corporation | Methods for identifying erythropoietin receptor binding protein |
| CA2232777C (en) * | 1997-03-24 | 2001-05-15 | Hiroyuki Baba | Method for producing silicon for use in solar cells |
| US6187564B1 (en) * | 1997-07-10 | 2001-02-13 | Beth Israel Deaconess Medical Center | DNA encoding erythropoietin multimers having modified 5′ and 3′ sequences and its use to prepare EPO therapeutics |
| DE69838552T2 (de) * | 1997-07-14 | 2008-05-21 | Bolder Biotechnology, Inc., Louisville | Derivate des wachstumshormons und verwandte proteine |
| KR100641969B1 (ko) * | 1997-07-23 | 2006-11-06 | 로셰 디아그노스틱스 게엠베하 | 내인성 유전자 활성화에 의한 에리트로포이에틴의제조방법 |
| US6165783A (en) * | 1997-10-24 | 2000-12-26 | Neuro Spheres Holdings Ltd. | Erythropoietin-mediated neurogenesis |
| US6448369B1 (en) * | 1997-11-06 | 2002-09-10 | Shearwater Corporation | Heterobifunctional poly(ethylene glycol) derivatives and methods for their preparation |
| TW445295B (en) * | 1997-12-31 | 2001-07-11 | Shiu Li Wei | Expression vector pcDNA3.1-HC for human erythropoietin, BHK-21 host cell line transformed therewith, and production of human erythropoietin using the transformed cell |
| US6274158B1 (en) * | 1998-02-04 | 2001-08-14 | Veronica L. Zaharia Czeizler | Treatment with recombinant human erythropoietin of bleeding in patients with normal and abnormal hemostasis |
| AU2591699A (en) * | 1998-02-09 | 1999-08-23 | University Of Southern California | Method of promoting erythropoiesis |
| IL124015A0 (en) * | 1998-04-08 | 1999-01-26 | Yeda Res & Dev | Pharmaceutical compositions comprising a protein |
| AR019025A1 (es) * | 1998-04-09 | 2001-12-26 | Roche Diagnostics Gmbh | Uso de eritropoyetina en bajas dosis para producir un preparado farmaceutico para el tratamiento de hemocromatosis, preparado farmaceutico combinadoutilizado segun dicho uso y envase farmaceutico unitario que contiene al referido preparado farmaceutico combinado |
| US6310078B1 (en) * | 1998-04-20 | 2001-10-30 | Ortho-Mcneil Pharmaceutical, Inc. | Substituted amino acids as erythropoietin mimetics |
| AU775422B2 (en) * | 1998-06-15 | 2004-07-29 | Gtc Biotherapeutics, Inc. | Erythropoietin analog-human serum albumin fusion |
| US6171821B1 (en) * | 1998-07-24 | 2001-01-09 | Apoptogen, Inc. | XIAP IRES and uses thereof |
| ES2170042T3 (es) * | 1998-08-28 | 2004-10-01 | Gryphon Therapeutics, Inc. | Procedimiento para la preparacion de cadenas de poliamida de longitud precisa y sus conjugados con proteinas. |
| US6165283A (en) * | 1998-10-23 | 2000-12-26 | Dahlin; William G. | Railcar cleaning method and apparatus |
| JP4805432B2 (ja) * | 1998-12-28 | 2011-11-02 | ランクセス・ドイチュランド・ゲーエムベーハー | 木質材又は木質複合材を製造する際に使用される接着剤混入用薬剤 |
| RU2144498C1 (ru) | 1999-02-01 | 2000-01-20 | Земнухова Людмила Алексеевна | Способ получения высокочистых аморфных диоксида кремния и углерода из рисовой шелухи |
| US6994986B2 (en) * | 1999-03-17 | 2006-02-07 | The Board Of Trustees Of The Leland Stanford University | In vitro synthesis of polypeptides by optimizing amino acid metabolism |
| US6642353B1 (en) * | 1999-03-17 | 2003-11-04 | Chugai Seiyaku Kabushiki Kaisha | Peptide ligands for the erythropoietin receptor |
| US6258559B1 (en) * | 1999-03-22 | 2001-07-10 | Zymogenetics, Inc. | Method for producing proteins in transformed Pichia |
| DE60039598D1 (de) * | 1999-04-09 | 2008-09-04 | Ortho Mcneil Pharm Inc | Pharmazeutische zusammensetzungen von erythropoietin |
| CZ299516B6 (cs) * | 1999-07-02 | 2008-08-20 | F. Hoffmann-La Roche Ag | Konjugát erythropoetinového glykoproteinu, zpusobjeho výroby a použití a farmaceutická kompozice sjeho obsahem |
| PE20010288A1 (es) * | 1999-07-02 | 2001-03-07 | Hoffmann La Roche | Derivados de eritropoyetina |
| US6703480B1 (en) * | 1999-11-24 | 2004-03-09 | Palani Balu | Peptide dimers as agonists of the erythropoientin (EPO) receptor, and associated methods of synthesis and use |
| US6348558B1 (en) * | 1999-12-10 | 2002-02-19 | Shearwater Corporation | Hydrolytically degradable polymers and hydrogels made therefrom |
| WO2001045796A2 (en) * | 1999-12-22 | 2001-06-28 | Shearwater Corporation | Method for the preparation of 1-benzotriazolyl carbonate esters of poly(ethylene glycol) |
| KR100414888B1 (ko) * | 2000-02-09 | 2004-01-13 | 알케이케미칼 주식회사 | 쌀겨로부터 실리카를 추출하는 방법 |
| US6586398B1 (en) * | 2000-04-07 | 2003-07-01 | Amgen, Inc. | Chemically modified novel erythropoietin stimulating protein compositions and methods |
| KR100367839B1 (ko) * | 2000-07-13 | 2003-01-10 | 주식회사 이코바이오 | 초본류 식물로 부터 실리카를 추출하는 방법 |
| TW593427B (en) * | 2000-12-18 | 2004-06-21 | Nektar Therapeutics Al Corp | Synthesis of high molecular weight non-peptidic polymer derivatives |
| US6531121B2 (en) * | 2000-12-29 | 2003-03-11 | The Kenneth S. Warren Institute, Inc. | Protection and enhancement of erythropoietin-responsive cells, tissues and organs |
| TWI246524B (en) * | 2001-01-19 | 2006-01-01 | Shearwater Corp | Multi-arm block copolymers as drug delivery vehicles |
| WO2002066372A1 (en) * | 2001-02-19 | 2002-08-29 | Fundação De Amparo Á Pesquisa Do Estado De São Paulo | Oxides extracted from vegetal matter and process therefor |
| JP3598369B2 (ja) | 2001-03-05 | 2004-12-08 | 独立行政法人産業技術総合研究所 | シリカ原料の製造方法 |
| US6406678B1 (en) * | 2001-03-26 | 2002-06-18 | Process Management, Inc. | Process for production of high purity amorphous silica from biogenic material |
| US20030072575A1 (en) * | 2001-10-11 | 2003-04-17 | Howard A. Fromson | Method and apparatus for conveying a workpiece through a workstation and specifically for conveying a lithographic printing plate through a developing station and for applying a developer solution |
| CN1202993C (zh) * | 2003-05-20 | 2005-05-25 | 吉林大学 | 一种从稻壳制备高纯纳米二氧化硅的方法 |
-
2004
- 2004-04-13 US US10/822,924 patent/US7588745B2/en active Active
-
2005
- 2005-04-12 AU AU2005233172A patent/AU2005233172A1/en not_active Abandoned
- 2005-04-12 WO PCT/US2005/012302 patent/WO2005099893A2/en not_active Ceased
- 2005-04-12 KR KR1020067023757A patent/KR101253064B1/ko not_active Expired - Fee Related
- 2005-04-12 BR BRPI0509837-8A patent/BRPI0509837A/pt not_active IP Right Cessation
- 2005-04-12 EP EP05737064A patent/EP1735088A4/en not_active Withdrawn
- 2005-04-12 CN CN200580015881.3A patent/CN101014533B/zh not_active Expired - Fee Related
- 2005-04-12 JP JP2007508454A patent/JP5133051B2/ja not_active Expired - Fee Related
-
2009
- 2009-09-10 US US12/556,754 patent/US8048822B2/en not_active Expired - Fee Related
-
2012
- 2012-09-12 JP JP2012200166A patent/JP5696108B2/ja not_active Expired - Fee Related
Non-Patent Citations (1)
| Title |
|---|
| See references of EP1735088A4 * |
Cited By (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| WO2013143377A1 (zh) * | 2012-03-26 | 2013-10-03 | 阳光凯迪新能源集团有限公司 | 利用工业烟气去除稻壳中金属离子的方法 |
| RU2567629C1 (ru) * | 2012-03-26 | 2015-11-10 | Саншайн Кайди Нью Энерджи Груп Ко., Лтд. | Способ использования промышленного топочного газа для удаления ионов металлов из оболочки рисовых зерен |
| AP3550A (en) * | 2012-03-26 | 2016-01-15 | Sunshine Kaidi New Energy Group Co Ltd | Method utilizing industrial flue gas for removing metal ions from rice hulls |
| EP2832692A4 (en) * | 2012-03-26 | 2016-01-27 | Sunshine Kaidi New Energy Group Co Ltd | METHOD USING AN INDUSTRIAL FLUE GAS FOR REMOVING METALIONS FROM REISH OILS |
Also Published As
| Publication number | Publication date |
|---|---|
| EP1735088A2 (en) | 2006-12-27 |
| BRPI0509837A (pt) | 2007-10-23 |
| CN101014533B (zh) | 2014-03-19 |
| AU2005233172A1 (en) | 2005-10-27 |
| EP1735088A4 (en) | 2011-03-30 |
| US7588745B2 (en) | 2009-09-15 |
| JP2007532468A (ja) | 2007-11-15 |
| JP5696108B2 (ja) | 2015-04-08 |
| US20090324478A1 (en) | 2009-12-31 |
| KR101253064B1 (ko) | 2013-04-11 |
| US20050227868A1 (en) | 2005-10-13 |
| WO2005099893A3 (en) | 2007-03-08 |
| JP2012254931A (ja) | 2012-12-27 |
| CN101014533A (zh) | 2007-08-08 |
| KR20070001269A (ko) | 2007-01-03 |
| US8048822B2 (en) | 2011-11-01 |
| JP5133051B2 (ja) | 2013-01-30 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US8048822B2 (en) | Method for making silicon-containing products | |
| US8470279B2 (en) | High purity silicon-containing products and method of manufacture | |
| JP2007532468A5 (enExample) | ||
| Patil et al. | Preparation of silica powder from rice husk | |
| CA1136382A (en) | Method for producing solar-cell-grade silicon | |
| JP2934648B2 (ja) | 炭化ホウ素の製造方法 | |
| US7638108B2 (en) | High purity silicon-containing products | |
| WO2011022817A1 (en) | Production of high purity silicon from amorphous silica | |
| Okutani | Utilization of silica in rice hulls as raw materials for silicon semiconductors | |
| JPS6227316A (ja) | 高純度炭化珪素微粉末の製造方法 | |
| JP2020090429A (ja) | シリコンの製造方法及び製造装置 | |
| JPH0645449B2 (ja) | 四塩化ケイ素の製造法 | |
| JPH0643247B2 (ja) | 籾殻燃焼灰組成物及びその製造方法 | |
| JP7592394B2 (ja) | 炭化ケイ素粉末の製造方法 | |
| RU2237617C1 (ru) | Способ получения борида хрома | |
| KR970001524B1 (ko) | 탄화규소(SiC) 분말의 제조방법 | |
| WO2025107060A1 (en) | Feedstock for graphitization and process for producing feedstock for graphitization | |
| JPS5845196A (ja) | sicホイスカ−の製造法 | |
| HK1169367B (en) | High purity silicon-containing products and method of manufacture | |
| JPH01249614A (ja) | 籾殻及び籾殻灰からなる固型組成物ならびにその製造方法 | |
| Ali et al. | Synthesis of Pure Silicon and Silicon Based Compounds from Rice Husk; A Review of Recycling the Agro-industrial By-product |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
| AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
| WWE | Wipo information: entry into national phase |
Ref document number: 2005233172 Country of ref document: AU |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2919/KOLNP/2006 Country of ref document: IN |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 12006502015 Country of ref document: PH Ref document number: 2007508454 Country of ref document: JP |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2005737064 Country of ref document: EP |
|
| NENP | Non-entry into the national phase |
Ref country code: DE |
|
| WWW | Wipo information: withdrawn in national office |
Ref document number: DE |
|
| ENP | Entry into the national phase |
Ref document number: 2005233172 Country of ref document: AU Date of ref document: 20050412 Kind code of ref document: A |
|
| WWP | Wipo information: published in national office |
Ref document number: 2005233172 Country of ref document: AU |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 1020067023757 Country of ref document: KR |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 200580015881.3 Country of ref document: CN |
|
| WWP | Wipo information: published in national office |
Ref document number: 2005737064 Country of ref document: EP |
|
| WWP | Wipo information: published in national office |
Ref document number: 1020067023757 Country of ref document: KR |
|
| ENP | Entry into the national phase |
Ref document number: PI0509837 Country of ref document: BR |