WO2003011966A1 - Molding composition formed from glassy and semicrystalline polymer - Google Patents
Molding composition formed from glassy and semicrystalline polymer Download PDFInfo
- Publication number
- WO2003011966A1 WO2003011966A1 PCT/US2002/024314 US0224314W WO03011966A1 WO 2003011966 A1 WO2003011966 A1 WO 2003011966A1 US 0224314 W US0224314 W US 0224314W WO 03011966 A1 WO03011966 A1 WO 03011966A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- composition
- glassy
- semi
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L33/04—Homopolymers or copolymers of esters
- C08L33/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
- C08L33/10—Homopolymers or copolymers of methacrylic acid esters
- C08L33/12—Homopolymers or copolymers of methyl methacrylate
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L67/00—Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
- C08L67/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
Definitions
- This invention relates to an extrudable highly filled thermoplastic composition that can be used to produce a decorative surface.
- composition of this invention is as a decorative surface, for example in production of counter-tops, vanity tops, bath and shower surfaces, sinks, wall panels and furniture surfacing.
- partially crosslinked acrylic for the production of spas, tubs and showers is well known in the art.
- Fiberglass reinforced polyester is also well known for being used in showers. These products serve the market well, but have a deficiency in that they cannot be easily repaired if scratched or stained.
- U. S. Patent 3,847,865 to Duggins refers to a castable composition for making simulated marble, which comprises an acrylic polymer or a mixture of polymers dissolved in a polymerizable constituent and highly filled with alumina trihydrate. This composition is then cast onto a belt or into a mold then cured to give a flat or shaped article with a reproducible simulated marble pattern. These cast sheets are homogeneous from upper surface to lower surface and are commonly known as solid surface. The ability to restore a marred surface by sanding or scrubbing is known in the trade as renewability and is highly preferred by consumers. CORIAN ® solid surfaces, sold by E. I.
- Cast solid surface sheets are generally V" to %" thick and are produced in high cost specialized equipment so they are more expensive than laminate or cultured marble.
- Thinner sheets are commercially available as a thin continuous cast ATH filled acrylic product called SSN made by Wilsonart International (Temple, Texas, USA). The cost remains much higher than for laminate.
- a second product developed by Wilsonart called SSL is an extruded wollastonite-filled acrylic product. This product is less expensive to produce than continuous cast sheet; however, it has deficiencies in heat resistance and solvent resistance.
- a hot object (about 120°C), placed on a countertop constructed from this sheet, will stick to the countertop because the sheet has become soft, unproved resistance to household chemicals such as nail polish remover is desired.
- General Electric Plastics (Pittsfield, Mass, USA) markets a sheet composition for the decorative surface market called EnduranTM semi-crystalline, high density polybutylene terephthalate (PBT) engineering material.
- Spartech Corporation (St. Louis, Missouri, USA) extrudes the composition into a sheet and sells it under the trademark EndurexTM.
- This product is an extruded barium sulfate- filled blend of polybutylene terephthalate (PBT), polyethylene terephthalate (PET), and polycarbonate.
- the extrudable thermoplastic composition of the invention is formed from a combination by weight of 20-65% glassy polymer, 5-35% semi-crystalline polymer, 0-10% compatibilizing agent for the glassy and semi-crystalline polymers, and 10- 70% of a particulate mineral filler wherein the glassy polymer is the major component by a ratio to the semi-crystalline polymer that ranges from 4/1 to 3/2. More preferable is a range from 3/1 to 3/2.
- thermoplastic composite sheet molding composition allows the production of thin solid surfacing materials providing the superior properties of conventional thicker solid surfacing with the advantages of handling capabilities and the inexpensive selling cost normally associated with high-pressure decorative laminate. Accordingly, it is a primary object of the invention to provide a highly filled, thermoplastic blended polymeric material having improved resistance to heat, stain, and mar.
- the present invention is directed to a highly filled thermoplastic sheet composition comprised of a combination of glassy and semi-crystalline polymers.
- the sheet exhibits improved resistance to heat, stains, and marring.
- glassy and “semi-crystalline” refer to the crystallinity of a polymer. As used herein, the term “glassy” refers to amorphous polymers that exhibit a glass transition temperature (T g ) but not a melt temperature (T m ).
- the T g is at least usual room temperature of 25 C.
- These glassy polymers are capable of being repeatedly melt processed in plastic manufacturing machinery.
- Glassy polymers include, but are not limited to acrylics, poly(methacrylates), atactic polystyrene, polycarbonate, styrene-acrylonitrile (SAN) and polyvinylchloride (PNC). Specific examples include 20 to 35% poly(methylmethacrylate), preferably 30 to 35% poly(methylmethacrylate) .
- the term "semi-crystalline” refers to polymers that exhibit both the glass transition phase and a melt temperature (T m ). Furthermore, the T m is greater than the intended maximum operating temperature. Kitchen countertops routinely encounter operating temperatures of at least 65 C but 95 C is preferable due to high heat applications such as canning or making candy. Therefore, T m is preferably at least 65 C. Semi-crystalline polymers maybe thought of as engineering polymers intended as substitutes for metal and ceramic.
- Semi- crystalline polymers include, but are not limited to polyester, polyamides (such as nylon 6, nylon 6,6, and nylon 6,12), poly(butyl terephthalate), polyethylterephthalate, thermoplastic polyester elastomers (e.g., Hytrel®), polypropylene, stereoregular polystyrene, aramid, and polyketone. Specific examples include 15 to 20% poly(butyl terephthalate) and 10 to 15% nylon 6,12.
- the ratio of glassy to semi-crystalline in the composition of the present invention is important to a successful countertop or like surface.
- the ratio should be such to give a balance of properties related to the stressful use in a kitchen or bath.
- Semi-crystalline polymers have such poor mar resistance they are easily marred by a simple fingernail scratch but have very good heat resistance. When they are first extruded, the surface is mar resistant; however, if a customer uses an abrasive sponge or cleaner on the surface to remove a stain the polymer layer at the surface is removed and the mar performance is reduced to a level unacceptable to consumers, as they desire the ability to renew a stained, scratched, or marred surface. The ability to renew a surface has helped achieve the popularity of solid surface countertops.
- glassy polymers Addition of minor amounts of glassy polymers will improve the mar resistance of semi-crystalline polymers, but not enough to effectively eliminate mars in a high wear area. Better performance is achieved by crosslinking the resin or chemically modifying the polymer chain with hard and soft copolymers to disrupt crystallinity. Crosslinked polymers cannot be extruded, thus the benefit of low-cost production is lost. A polymer chain with hard and soft copolymers is a specialty polymer so its cost is high; the benefit of a low cost product is lost. Conversely, glassy polymers have very good optical clarity, UN resistance and mar resistance but suffer from poor heat resistance. Glassy polymer heat resistance improves with crosslinking with, once again, the loss of extrudability.
- the ratio of glassy resin to semi-crystalline resin that provides the best balance of performances is a blend where the glassy resin constitutes the dominant amount, and just enough semi-crystalline resin is present to provide resistance to heat.
- the weight of the glassy polymer is 20 to 65% and the semi-crystalline polymer is 5 to 35% of the total filled composition provided at least 10% particulate mineral filler is present.
- a preferred ratio of glassy/semi-crystalline polymer is in a range from 4/1 to 3/2. More preferred is a range from 3/1 to 3/2.
- compatibilizing agents are added to polymer blends to improve the synergy of the blended materials.
- the materials are typically heated and sheared, as in an extruder or a blender, i the absence of shear, as in an extruder die or a hot press, the distributed molten polymer domains will coalesce. If this coalescence is permitted, then the properties of the final blend are often poor. Examples of performances that suffer when blends are not compatibilized are toughness, tensile and flexural strength, hardness, and heat resistance.
- Compatibilizing agents are materials that exhibit an affinity for each of the components of the blend and inhibit the coalescence of molten domains.
- Compatibilizing agents include but are not limited to emulsifiers, surfactants, detergents, ethylene vinyl acetate carbon monoxide terpolymer such as Elvaloy® (sold by E. I. DuPont de Nemours & Co, Wilmington, Delaware, USA), ethylene/n- butyl acrylate/glycidyl methacrylate, ethylene/methacrylic ionomeric copolymer such as Surlyn® (also available from DuPont), maleic anhydride grafted polyolefin resins such as Fusabond® (also available from DuPont), core-shell, random copolymer, block copolymers, branched copolymers, or combinations thereof.
- emulsifiers such as Elvaloy® (sold by E. I. DuPont de Nemours & Co, Wilmington, Delaware, USA)
- Surlyn® also available from DuPont
- maleic anhydride grafted polyolefin resins such
- the compatibilizers if employed, will not exceed 10% by weight of a composition, also based on the glassy and semi-crystalline polymers as well as filler. Examples include up to 4% ethylene/n-butyl acrylate/glycidyl methacrylate copolymer and up to 6% ethylene/methacrylic ionomeric copolymer.
- the glassy polymer is poly(methylmethacrylate) and the semi-crystalline polymer is poly(butyl terephthalate)
- the preferred compatibilizer is ethylene/n-butyl acrylate/glycidyl methacrylate in a range from 2-6% by weight.
- the preferred compatibilizer is up to 4% ethylene/n-butyl acrylate/glycidyl methacrylate, or up to 6% ethylene/methacrylic ionomeric copolymer, or a combination thereof.
- the thermoplastic composition includes particulate mineral filler.
- this filler increases the hardness, stiffness or strength of the final article relative to the pure polymer or combination of pure polymers.
- the mineral filler can provide other attributes to the final article. For example, it can provide other functional properties, such as flame retardance, or it may serve a decorative purpose and modify the aesthetics.
- Some representative fillers include alumina, alumina trihydrate (ATH), alumina monohydrate, aluminum hydroxide, aluminum oxide, aluminum sulfate, aluminum phosphate, aluminum silicate, Bayer hydrate, borosilicates, calcium sulfate, calcium silicate, calcium phosphate, calcium carbonate, calcium hydroxide, calcium oxide, apatite, glass bubbles, glass microspheres, glass fibers, glass beads, glass flakes, glass powder, glass spheres, barium carbonate, barium hydroxide, barium oxide, barium sulfate, barium phosphate, barium silicate, magnesium sulfate, magnesium silicate, magnesium phosphate, magnesium hydroxide, magnesium oxide, kaolin, montmorillonite, bentonite, pyrophyllite, mica, gypsum, silica (including sand), ceramic microspheres and ceramic particles, powder talc, titanium dioxide, diatomaceous earth, wood flour, borax, or combinations thereof.
- the fillers can be optionally coat-treated with coupling agents, such as silane (meth)acrylate available from OSI Specialties (Friendly, VN) as Silane 8 Methacrylate A- 174.
- the filler is present in the form of small particles, with an average particle size in the range of from about 5-500 microns.
- ATH is often a preferred filler for poly(methylmethacrylate) (PMMA) systems because the refractive indexes of the two materials are similar.
- ATH presents problems when used as the filler in a solid surface product produced in an extrusion process since it releases water at processing temperatures. Therefore when ATH is employed as a filler, a two step process (described below) can be employed. Barium sulfate has been found to extrude well and achieve the heat and chemical resistance required for countertop applications and is the preferred filler.
- antioxidants such as ternary or aromatic amines, Irganox® (a registered trademark of Ciba Geigy), and sodium hypophosphites
- flame retardants such as halogenated hydrocarbons, mineral carbonates, hydrated minerals, and antimony oxide
- UN stabilizers such as Tinuvin supplied by Ciba Geigy
- stain- resistant agents such as poly(tetrafluoroethylene) (e.g., Teflon® a trademark of DuPont), stearic acid, and zinc stearate), or combinations thereof.
- alumina Al O 3
- Fibers e.g., glass, nylon, and carbon
- the thermoplastic composition can optionally include decorative fillers.
- Such decorative fillers although they may have a minor effect on physical properties, are present primarily for aesthetic reasons.
- suitable decorative fillers include pigments and other water-insoluble colorants, reflective flakes, metal particles, rocks, colored glass, colored sand of various sizes, wood products, such as fibers, pellets and powders, and others.
- the particle size will vary with the nature of the decorative filler and can be as large as several centimeters. It is permissible to include minor amounts of additives such as dyes, parting agents, fluidizing agents, viscosity control agents, curing agents, antioxidants, and the like as are known to those of ordinary skill in the art, as long as they do not detract from the mechanical properties of the invention.
- Sheet can be produced in a one step process by direct sheet extrusion or in a two step process, hi direct extrusion polymer, additives and filler can be added to a twin screw extruder or a co-kneader where the resin is melted and the filler is uniformly dispersed in the melt. The melt then flows to a gear pump and into a sheet die. hi the two step process, additives and filler are added to a twin screw extruder or a co-kneader where the resin is melted and the filler is uniformly dispersed in the melt. The melt then flows to strand die and then to either a melt cutter or to a cooling trough and a pelletizer.
- the pellets and possibly a colorant are then added to a single screw extruder.
- the melt exiting the single screw extruder is usually sent to a gear pump and then into a sheet die.
- the extrudate is then processed through calendaring rolls to achieve the desired finish.
- Extrusion is the preferred process to produce sheet from the composition of the invention. Water and steam interfere with the extrusion of polymers. Therefore, it is preferable to select polymers, compatibilizers, mineral fillers and functional fillers that do not contain water or produce water during extrusion. Care should be taken when using hydrates as they will evolve off water of hydration at typical extruder temperatures.
- Example 2 % 12micron BaSO 4 (Cimbar PC, supplied by CIMBAR Performance Minerals, Cartersville, Georgia).
- the filler was 30 wt. % Cimbar PC mixed with 15 wt. % RCF-015 15micron glass (supplied by Nippon Glass Fiber Co., LTD).
- Crastin® 6129 Semi-crystalline polybutyl terephthalate, Crastin® 6129, which made up 28 wt. % of the final composition was added to the glassy thermoplastic ethylene/methacrylic acid copolymer (Surlyn® 9945, supplied by DuPont) which made up 25 wt. % of the composition.
- This grade of Surlyn® has a Tg less than 25 C.
- the polymers were compatibilized with 2 wt. % of Elvaloy 4170 E/BA/GMA rubber.
- the filler was BaSO4 (Blanc Fixe, supplied by Polar Mineral) at 45 wt. % of the final composition.
- the glassy resin poly(methyl methacrylate) (Plexiglas® NO 45, supplied by Atofina Chemicals, Philadelphia, Pennsylvania, USA) made up 42.0 wt. % of comparative example without a semi-crystalline component.
- Elvaloy® 4170 E/BA GMA rubber made up 6.0 wt. % of the composition as a toughener.
- the filler was a combination of BaSO 4 (Blanc Fixe, supplied Polar Mineral) at 33 wt. %, plus 5.0 wt. % of Glass Fritz plus 10.0 wt. %, and rigid, inert, hollow ceramic (sold under the trade name Zeospheres by 3M Corporation). A color concentrate, 4.0 wt. % was added.
- a comparative example comprising only semi-crystalline polymers contained 45 wt. % Crastin® 6129, 15 wt. % Zytel® 42A, 3.0 wt. % Elvaloy® 4170, and 37 wt. % Blanc Fixe as the filler.
- Thin sheets comprised of blends that are predominately semi-crystalline with a minor component of glassy polymer are considered poor performers in regards to mar and typically measure about 0.2-0.3.
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Manufacture Of Macromolecular Shaped Articles (AREA)
- Polyesters Or Polycarbonates (AREA)
Priority Applications (9)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP2003517149A JP2004536942A (ja) | 2001-08-01 | 2002-08-01 | ガラス質および半結晶質ポリマーから形成される成形組成物 |
| NZ530444A NZ530444A (en) | 2001-08-01 | 2002-08-01 | An extrudable molding composition formed from glassy and semicrystalline polymer |
| BR0211675-8A BR0211675A (pt) | 2001-08-01 | 2002-08-01 | Composição de moldagem e material sólido |
| AU2002317606A AU2002317606B2 (en) | 2001-08-01 | 2002-08-01 | Molding composition formed from glassy and semicrystalline polymer |
| KR1020037017282A KR100840096B1 (ko) | 2001-08-01 | 2002-08-01 | 유리질 및 반결정질 중합체로부터 형성된 성형 조성물 |
| DE60219322T DE60219322T2 (de) | 2001-08-01 | 2002-08-01 | Formmasse aus glasigen und semikristallinen polymeren |
| EP02748278A EP1414898B1 (en) | 2001-08-01 | 2002-08-01 | Molding composition formed from glassy and semicrystalline polymer |
| MXPA04000916A MXPA04000916A (es) | 2001-08-01 | 2002-08-01 | Composicion moldeable formada de polimero cristalino y semicristalino. |
| CA2451137A CA2451137C (en) | 2001-08-01 | 2002-08-01 | Molding composition formed from glassy and semicrystalline polymer |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US09/919,712 US6476111B1 (en) | 2001-08-01 | 2001-08-01 | Extrudable highly filled thermoplastic sheet composition |
| US09/919,712 | 2001-08-01 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| WO2003011966A1 true WO2003011966A1 (en) | 2003-02-13 |
Family
ID=25442518
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/US2002/024314 Ceased WO2003011966A1 (en) | 2001-08-01 | 2002-08-01 | Molding composition formed from glassy and semicrystalline polymer |
Country Status (12)
| Country | Link |
|---|---|
| US (1) | US6476111B1 (enExample) |
| EP (1) | EP1414898B1 (enExample) |
| JP (1) | JP2004536942A (enExample) |
| KR (1) | KR100840096B1 (enExample) |
| AT (1) | ATE358695T1 (enExample) |
| AU (1) | AU2002317606B2 (enExample) |
| BR (1) | BR0211675A (enExample) |
| CA (1) | CA2451137C (enExample) |
| DE (1) | DE60219322T2 (enExample) |
| MX (1) | MXPA04000916A (enExample) |
| NZ (1) | NZ530444A (enExample) |
| WO (1) | WO2003011966A1 (enExample) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US9168693B2 (en) | 2006-05-23 | 2015-10-27 | Nu Cleer Systems Limited | Laminate material |
Families Citing this family (14)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| ES2259744T3 (es) * | 2003-08-08 | 2006-10-16 | A. Schulman Plastics | Masterbatch conteniendo pmma y su empleo para la produccion de films de poliolefina. |
| KR100622600B1 (ko) * | 2004-05-11 | 2006-09-19 | 엘에스전선 주식회사 | 폴리에스테르 비할로겐 조성물 및 이를 이용한 전선 |
| US20050279775A1 (en) * | 2004-06-07 | 2005-12-22 | John Polimeno | Container for distribution of non-catalyzed resin and filler mixture |
| US20060118989A1 (en) * | 2004-12-07 | 2006-06-08 | 3M Innovative Properties Company | Method of making composite material |
| US20080067713A1 (en) * | 2004-12-14 | 2008-03-20 | Robert Bordener | Method of producing and business model for applying a thin laminate sheet of a decorative material |
| US20070251603A1 (en) * | 2006-04-26 | 2007-11-01 | Olson Barry D | Novel surface aesthetics employing magnetic particles |
| US20070254106A1 (en) * | 2006-04-26 | 2007-11-01 | Olson Barry D | Novel aesthetics in surfaces employing deformation and magnetic means |
| US20070252300A1 (en) * | 2006-04-26 | 2007-11-01 | Paplham William P | Novel aesthetics in surfaces |
| DE102007005432A1 (de) * | 2007-01-30 | 2008-07-31 | Evonik Röhm Gmbh | Formmassen für mattierte Polyacrylat-Formkörper |
| US20090043031A1 (en) * | 2007-08-06 | 2009-02-12 | Keith William Pollak | Compatibilized multipolymer composition containing particulate filler |
| US8858850B2 (en) * | 2009-07-02 | 2014-10-14 | E I Du Pont De Nemours And Company | Process for preparing decorative surface appearance in acrylic material employing anisotropic particles |
| US10042395B2 (en) * | 2013-10-11 | 2018-08-07 | Dell Products, Lp | Method of forming composite fiber laminate with variable elasticity and device thereof |
| US11008438B2 (en) * | 2016-12-02 | 2021-05-18 | Composite Technologies International, Llc | Composition and method to form a composite core material |
| CN110819082B (zh) * | 2019-09-30 | 2021-07-06 | 广东轻工职业技术学院 | 一种高熔接痕强度玻纤增强pbt复合材料及其制备方法 |
Citations (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPH10298312A (ja) * | 1997-04-24 | 1998-11-10 | Mitsubishi Chem Corp | 樹脂シート |
| EP0971366A1 (en) * | 1998-07-10 | 2000-01-12 | Pirelli Cables and Systems LLC | Conductive composite material and method for producing it |
| JP2000336226A (ja) * | 1999-05-28 | 2000-12-05 | Toray Ind Inc | 難燃性樹脂組成物、その製造方法および成形品 |
Family Cites Families (23)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3847865A (en) | 1972-04-28 | 1974-11-12 | Du Pont | Use of alumina trihydrate in a polymethyl methacrylate article |
| GB1584400A (en) | 1976-12-24 | 1981-02-11 | Bayer Ag | (2-oxo-imidazoliden-1-yl(carbonylamino)-acetamido-cephalosporins and penicillins |
| US4369282A (en) * | 1979-07-03 | 1983-01-18 | General Electric Company | Modified polyester compositions |
| US4880866A (en) | 1984-10-31 | 1989-11-14 | Hoechst Celanese | Thermoplastic polyester compositions containing certain low molecular weight diepoxide resins and having improved impact behavior |
| CA1332015C (en) * | 1987-08-17 | 1994-09-13 | Yuichi Orikasa | Thermoplastic resin composition and method for preparing the same |
| US4981898A (en) * | 1987-12-31 | 1991-01-01 | General Electric Company | Polycarbonate-polyester blends |
| JPH01229065A (ja) | 1988-03-09 | 1989-09-12 | Polyplastics Co | 熱可塑性ポリエステル樹脂組成物 |
| US4927870A (en) * | 1988-08-25 | 1990-05-22 | The Dow Chemical Company | Ignition resistant modified thermoplastic composition |
| JP2627132B2 (ja) * | 1993-01-19 | 1997-07-02 | 三洋化成工業株式会社 | 顔料マスターバッチ用樹脂組成物 |
| EP0616013B1 (en) * | 1993-03-19 | 1999-06-02 | Mitsubishi Chemical Corporation | Thermoplastic resin composition |
| JPH08208916A (ja) * | 1994-11-08 | 1996-08-13 | Sumitomo Chem Co Ltd | ポリスチレン系樹脂組成物及びその成形品 |
| US5444115A (en) * | 1994-11-21 | 1995-08-22 | E. I. Du Pont De Nemours And Company | Fire resistant poly(methyl methacrylate) composition |
| US6005050A (en) * | 1994-11-28 | 1999-12-21 | Idemitsu Petrochemical Co., Ltd. | Impact resistant polystyrene composition |
| ES2112071T3 (es) | 1995-03-27 | 1998-03-16 | Basf Ag | Procedimiento para la obtencion de termoplasticos. |
| JPH08302117A (ja) * | 1995-05-08 | 1996-11-19 | Idemitsu Kosan Co Ltd | ポリスチレン系樹脂組成物 |
| BE1010713A3 (fr) * | 1996-10-25 | 1998-12-01 | Ucb Sa | Compositions en poudre a base de polyesters semi-cristallins et de copolymeres acryliques; contenant des groupes (meth)acrylyle. |
| JPH1129685A (ja) * | 1997-07-09 | 1999-02-02 | Asahi Chem Ind Co Ltd | 帯電防止性アクリル系樹脂組成物 |
| JPH11100479A (ja) * | 1997-07-30 | 1999-04-13 | Mitsubishi Rayon Co Ltd | 熱可塑性樹脂組成物およびそれを含むマスターバッチ |
| US6013686A (en) | 1998-02-13 | 2000-01-11 | General Electric Company | Blowing agent concentrate |
| JP2000159994A (ja) * | 1998-11-25 | 2000-06-13 | Kanegafuchi Chem Ind Co Ltd | 難燃性熱可塑性樹脂組成物 |
| JP3996716B2 (ja) * | 1998-12-21 | 2007-10-24 | テクノポリマー株式会社 | 熱可塑性樹脂組成物 |
| JP2001131308A (ja) * | 1999-10-29 | 2001-05-15 | Daicel Chem Ind Ltd | 熱可塑性樹脂組成物シート |
| JP2002080728A (ja) * | 2000-09-08 | 2002-03-19 | Sumitomo Chem Co Ltd | 熱可塑性樹脂組成物成形体の製造方法 |
-
2001
- 2001-08-01 US US09/919,712 patent/US6476111B1/en not_active Expired - Lifetime
-
2002
- 2002-08-01 EP EP02748278A patent/EP1414898B1/en not_active Expired - Lifetime
- 2002-08-01 BR BR0211675-8A patent/BR0211675A/pt not_active IP Right Cessation
- 2002-08-01 NZ NZ530444A patent/NZ530444A/en not_active IP Right Cessation
- 2002-08-01 KR KR1020037017282A patent/KR100840096B1/ko not_active Expired - Fee Related
- 2002-08-01 DE DE60219322T patent/DE60219322T2/de not_active Expired - Lifetime
- 2002-08-01 CA CA2451137A patent/CA2451137C/en not_active Expired - Lifetime
- 2002-08-01 MX MXPA04000916A patent/MXPA04000916A/es active IP Right Grant
- 2002-08-01 AU AU2002317606A patent/AU2002317606B2/en not_active Ceased
- 2002-08-01 WO PCT/US2002/024314 patent/WO2003011966A1/en not_active Ceased
- 2002-08-01 JP JP2003517149A patent/JP2004536942A/ja active Pending
- 2002-08-01 AT AT02748278T patent/ATE358695T1/de not_active IP Right Cessation
Patent Citations (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPH10298312A (ja) * | 1997-04-24 | 1998-11-10 | Mitsubishi Chem Corp | 樹脂シート |
| EP0971366A1 (en) * | 1998-07-10 | 2000-01-12 | Pirelli Cables and Systems LLC | Conductive composite material and method for producing it |
| JP2000336226A (ja) * | 1999-05-28 | 2000-12-05 | Toray Ind Inc | 難燃性樹脂組成物、その製造方法および成形品 |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US9168693B2 (en) | 2006-05-23 | 2015-10-27 | Nu Cleer Systems Limited | Laminate material |
Also Published As
| Publication number | Publication date |
|---|---|
| JP2004536942A (ja) | 2004-12-09 |
| CA2451137A1 (en) | 2003-02-13 |
| ATE358695T1 (de) | 2007-04-15 |
| EP1414898B1 (en) | 2007-04-04 |
| US6476111B1 (en) | 2002-11-05 |
| DE60219322T2 (de) | 2008-01-03 |
| NZ530444A (en) | 2006-11-30 |
| MXPA04000916A (es) | 2004-04-02 |
| KR100840096B1 (ko) | 2008-06-19 |
| KR20040022443A (ko) | 2004-03-12 |
| AU2002317606B2 (en) | 2007-01-18 |
| EP1414898A1 (en) | 2004-05-06 |
| CA2451137C (en) | 2010-06-15 |
| BR0211675A (pt) | 2004-07-13 |
| DE60219322D1 (de) | 2007-05-16 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CA2451137C (en) | Molding composition formed from glassy and semicrystalline polymer | |
| AU2002317606A1 (en) | Molding composition formed from glassy and semicrystalline polymer | |
| CN101448894B (zh) | 热塑性树脂组合物和复合成型品 | |
| JP5156761B2 (ja) | つや消しされたポリアクリラート成形体用の成形材料 | |
| KR20060107783A (ko) | 중합체 혼합물 및 사출 성형품을 위한 이의 용도 | |
| US20220193983A1 (en) | Acrylic composition for 3-d printing | |
| WO2018016473A1 (ja) | 熱可塑性樹脂組成物、成形体及び車両材料 | |
| KR100554187B1 (ko) | 열가소성수지성형품 | |
| KR19990014007A (ko) | 열가소성 아크릴 쉬이트와 고압 장식 적층물로서의 용도 | |
| CN101525455A (zh) | 树脂组合物以及由其制备的制品和方法 | |
| JP2003231760A (ja) | 耐白化性アクリル系樹脂フィルムとそれを用いた積層成形品 | |
| JP2003183471A (ja) | アクリル系樹脂フィルム及びそれを積層した射出成形品 | |
| US6696165B1 (en) | Styrene copolymer compositions having reduced surface gloss and composite articles incorporating same | |
| KR20080068818A (ko) | 충격 개선제 크기의 바이모달 분포를 갖는 충격 개선된아크릴 | |
| US6689832B1 (en) | Methacrylate moulding composition for obtaining decorative colored sheet material | |
| KR100788736B1 (ko) | 무도장 외장재용 아크릴계 수지 조성물 | |
| KR20010033682A (ko) | 표면 광택이 감소된 스티렌 공중합체 조성물 및 그를혼입하는 복합물 | |
| JP2000198905A (ja) | 熱可塑性樹脂組成物 | |
| KR102429752B1 (ko) | 무광택 복합시트 및 이의 제조방법 | |
| JPH09272777A (ja) | 熱可塑性樹脂組成物およびそれを用いた積層物 | |
| JP2000326387A (ja) | 熱可塑性アクリル樹脂シート組成物および高圧装飾用積層体の代替品としてのその使用 | |
| JP3035444B2 (ja) | 熱可塑性樹脂積層物 | |
| KR102585620B1 (ko) | 무광 메탈릭 복합시트 및 이의 제조방법 | |
| JPH07238202A (ja) | 熱可塑性樹脂組成物及びその積層物 | |
| JPH01103657A (ja) | ポリカーボネート樹脂組成物 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DE DM DZ EC EE ES FI GB GD GE GH HR HU ID IL IN IS JP KE KG KP KR LC LK LR LS LT LU LV MA MD MG MN MW MX MZ NO NZ OM PH PL PT RU SD SE SG SI SK SL TJ TM TN TR TZ UA UG UZ VN YU ZA ZM Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG UZ VN YU ZA ZM ZW |
|
| AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
| DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
| WWE | Wipo information: entry into national phase |
Ref document number: 2002317606 Country of ref document: AU |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2451137 Country of ref document: CA |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 1020037017282 Country of ref document: KR |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 530444 Country of ref document: NZ |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2003517149 Country of ref document: JP Ref document number: PA/a/2004/000916 Country of ref document: MX |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2002748278 Country of ref document: EP |
|
| WWP | Wipo information: published in national office |
Ref document number: 2002748278 Country of ref document: EP |
|
| REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
| WWG | Wipo information: grant in national office |
Ref document number: 2002748278 Country of ref document: EP |