  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/62—Refractory metals or compounds thereof
  • C08F4/64—Titanium, zirconium, hafnium or compounds thereof
  • C08F4/65—Pretreating the metal or compound covered by group C08F4/64 before the final contacting with the metal or compound covered by group C08F4/44
  • C08F4/651—Pretreating with non-metals or metal-free compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F10/02—Ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F10/04—Monomers containing three or four carbon atoms
  • C08F10/06—Propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/62—Refractory metals or compounds thereof
  • C08F4/64—Titanium, zirconium, hafnium or compounds thereof
  • C08F4/647—Catalysts containing a specific non-metal or metal-free compound
  • C08F4/649—Catalysts containing a specific non-metal or metal-free compound organic
  • C08F4/6494—Catalysts containing a specific non-metal or metal-free compound organic containing oxygen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F110/00—Homopolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F110/04—Monomers containing three or four carbon atoms
  • C08F110/06—Propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/16—Copolymers of ethene with alpha-alkenes, e.g. EP rubbers

Definitions

• catalyst components suitable for the stereospecific polymerization of olefins, comprising Ti, Mg, halogen and an electron donor compound selected from esters of substituted succinic acids (substituted succinates).
• Said catalyst components when used in the polymerization of olefins, and in particular of propylene, are capable to give polymers in high yields and with high isotactic index expressed in terms of high xylene insolubility.
• the chemical class of succinates is known in the art. However, the specific succinates of the present invention have never been used as internal electron donors in catalysts for the polymerization of olefins.
• EP-A-86473 mentions the use of unsubstituted succinates as internal donors in catalyst components for the polymerization of olefins.
• the use of diisobutyl succinate and di-n-butyl succinate is also exemplified.
• the results obtained in terms of isotactic index and yields are however poor.
• polycarboxylic acid esters including succinates
• succinates as internal donors in catalyst components for the polymerization of olefins
• Diethyl methylsuccinate and diallyl ethylsuccinate are mentioned in the description although they are not exemplified.
• EP263718 mentions, but does not exemplify the use of diethyl methylsuccinate and di-n-butyl ethylsuccinate as internal donors.
• It is therefore an object of the present invention to provide a solid catalyst component for the polymerization of olefins CH 2 CHR in which R is hydrogen or a hydrocarbon radical with 1- 12 carbon atoms, comprising Mg, Ti, halogen and an electron donor selected from succinates of formula (I):
• radicals R, and R 2 equal to, or different from, each other are a C,-C 20 linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms;
• the radicals R 3 to Rg equal to, or different from, each other, are hydrogen or a C,-C 20 linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms, and the radicals R 3 to Rg which are joined to the same carbon atom can be linked together to form a cycle; with the proviso that when R 3 to R 5 are contemporaneously hydrogen R- j is a radical selected from primary branched, secondary or tertiary alkyl groups, cycloalkyl, aryl, arylalkyl or alkylaryl groups having from 3 to 20 carbon atoms.
• R, and R 2 are preferably C,-C 8 alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl groups. Particularly preferred are the compounds in which R, and R 2 are selected from primary alkyls and in particular branched primary alkyls. Examples of suitable R, and R 2 groups are methyl, ethyl, n-propyl, n- butyl, isobutyl, neopentyl, 2-ethylhexyl. Particularly preferred are ethyl, isobutyl, and neopentyl.
• R 3 to R 5 are hydrogen and B ⁇ is a branched alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl radical having from 3 to 10 carbon atoms.
• Rg is a branched primary alkyl group or a cycloalkyl group having from 3 to 10 carbon atoms.
• Suitable monosubstituted succinate compounds are diethyl sec- butylsuccinate, diethyl thexylsuccinate, diethyl cyclopropylsuccinate, diethyl norbornylsuccinate, diethyl (l ⁇ -)perhydronaphthylsuccinate, diethyl trimethylsilylsuccinate, diethyl methoxysuccinate, diethyl p-methoxyphenylsuccinate, diethyl p-chlorophenylsuccinate diethyl phenylsuccinate, diethyl cyclohexylsuccinate, diethyl benzylsuccinate, diethyl (cyclohexylmethyl)succinate, diethyl t-butylsuccinate, diethyl isobutylsuccinate, diethyl isopropylsuccinate, diethyl neopentylsuccinate,
• Another preferred group of compounds within those of formula (I ) is that in which at least two radicals from R 3 to R e are different from hydrogen and are selected from C,-C 20 linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms. Particularly preferred are the compounds in which the two radicals different from hydrogen are linked to the same carbon atom.
• suitable 2,2-disubstituted succinates are: diethyl 2,2-dimethylsuccinate, diethyl 2-ethyl-2-methylsuccinate, diethyl 2- benzyl-2-isopropylsuccinate, diethyl 2-(cyclohexylmethyl)-2-isobutylsuccinate, diethyl 2- cyclopentyl-2-n-propylsuccinate, diethyl 2J-diisobutylsuccinate, diethyl 2-cyclohexyl-2- ethylsuccinate, diethyl 2-isopropyl-2-methylsuccinate, diethyl 2,2-diisopropyl diethyl 2- isobutyl-2-ethylsuccinate, diethyl 2-(lJJ-trifluoro-2-propyl)-2-methylsuccinate, diethyl 2- isopentyl-2-isobutylsuccinate, diethyl 2-
• R 3 and R 5 or R 4 and Rg are particularly preferred.
• suitable compounds are: diethyl 2,3-bis(trimethylsilyl)succinate, diethyl 2,2-sec- butyl-3-methylsuccinate, diethyl 2-(3,3,3-trifluoropropyl)-3-methylsuccinate, diethyl 2,3- bis(2-ethylbutyl)succinate, diethyl 2J-diethyl-2 -isopropylsuccinate, diethyl 2,3-diisopropyl-2- methylsuccinate, diethyl 2J-dicyclohexyl-2-methylsuccinate, diethyl 2,3-dibenzylsuccinate, diethyl 2,3-diisopropylsuccinate, diethyl 2,3-bis(cyclohexylmethyl)succinate, diethyl 2,3-bis(cyclohexylmethyl)succinate, diethyl 2,3-
• suitable compounds are l-(ethoxycarbonyl)-l-(ethoxyacetyl)-2,6- dimethylcyclohexane, l-(ethoxycarbonyl)-l-(ethoxyacetyl)-2,5-dimethylcyclopentane, 1- (ethoxycarbonyl)- 1 -(ethoxyacetylmethyl)-2-methylcyclohexane, 1 -(ethoxycarbonyl)- 1 -
• the catalyst components of the invention comprise, in addition to the above electron donors, Ti, Mg and halogen.
• the catalyst components comprise a titanium compound, having at least a Ti-halogen bond and the above mentioned electron donor compound supported on a Mg halide.
• the magnesium halide is preferably MgCl 2 in active form which is widely known from the patent literature as a support for Ziegler-Natta catalysts.
• Patents USP 4,298,718 and USP 4,495,338 were the first to describe the use of these compounds in Ziegler- Natta catalysis.
• the magnesium dihalides in active form used as support or co-support in components of catalysts for the polymerization of olefins are characterized by X-ray spectra in which the most intense diffraction line that appears in the spectrum of the non-active halide is diminished in intensity and is broadened to form a halo.
• the preferred titanium compounds used in the catalyst component of the present invention are TiCl 4 and TiCl 3 ; furthermore, also Ti-haloalcoholates of formula Ti(OR) n . y X y , where n is the valence of titanium, X is halogen and y is a number between 1 and n, can be used.
• the preparation of the solid catalyst component can be carried out according to several methods. According to one of these methods, the magnesium dichloride in an anhydrous state and the succinate of formula (I) are milled together under conditions in which activation of the magnesium dichloride occurs. The so obtained product can be treated one or more times with an excess of TiCl 4 at a temperature between 80 and 135 °C. This treatment is followed by washings with hydrocarbon solvents until chloride ions disappeared. According to a further method, the product obtained by co-milling the magnesium chloride in an anhydrous state, the titanium compound and the ⁇ -substituted succinate is treated with halogenated hydrocarbons such as 1,2- dichloroethane, chlorobenzene, dichloromethane, etc. The treatment is carried out for a time between 1 and 4 hours and at temperature of from 40 °C to the boiling point of the halogenated hydrocarbon. The product obtained is then generally washed with inert hydrocarbon solvents such as hexane.
• magnesium dichloride is preactivated according to well known methods and then treated with an excess of TiCl 4 at a temperature of about 80 to 135 °C which contains, in solution, a succinate of formula (I).
• the treatment with TiCl 4 is repeated and the solid is washed with hexane in order to eliminate any non-reacted TiCl 4 .
• a further method comprises the reaction between magnesium alcoholates or chloroalcoholates (in particular chloroalcoholates prepared according to U.S. 4,220,554) and an excess of TiCl 4 comprising the succinate of formula (I) in solution at a temperature of about 80 to 120 °C.
• the solid catalyst component can be prepared by reacting a titanium compound of formula Ti(OR) n _.X v , where n is the valence of titanium and y is a number between 1 and n, preferably TiCl 4 , with a magnesium chloride deriving from an adduct of formula MgCl 2 «pROH, where p is a number between 0J and 6, preferably from 2 to 3.5, and R is a hydrocarbon radical having 1-18 carbon atoms.
• the adduct can be suitably prepared in spherical form by mixing alcohol and magnesium chloride in the presence of an inert hydrocarbon immiscible with the adduct, operating under stirring conditions at the melting temperature of the adduct (100-130 °C). Then, the emulsion is quickly quenched, thereby causing the solidification of the adduct in form of spherical particles. Examples of spherical adducts prepared according to this procedure are described in USP 4,399,054 and USP 4,469,648.
• the so obtained adduct can be directly reacted with the Ti compound or it can be previously subjected to thermally controlled dealcoholation (80-130 °C) so as to obtain an adduct in which the number of moles of alcohol is generally lower than 3 preferably between 0J and 2.5.
• the reaction with the Ti compound can be carried out by suspending the adduct (dealcoholated or as such) in cold TiCl 4 (generally 0 °C); the mixture is heated up to 80-130 °C and kept at this temperature for 0.5-2 hours.
• the treatment with TiCl 4 can be carried out one or more times.
• the succinate of formula (I) can be added during the treatment with TiCl 4 .
• the treatment with the electron donor compound can be repeated one or more times.
• the preparation of catalyst components in spherical form is described for example in European Patent Applications EP-A-395083, EP-A-553805, EP-A-553806, EPA-601525 and WO98/44009.
• the solid catalyst components obtained according to the above method show a surface area (by B.E.T. method) generally between 20 and 500 m 2 /g and preferably between 50 and 400 m 2 /g, and a total porosity (by B.E.T. method) higher than 0.2 cm 3 /g preferably between 0.2 and 0.6 cm 3 /g.
• the porosity (Hg method) due to pores with radius up to 10000 A generally ranges from 03 to 1.5 cmVg, preferably from 0.45 to 1 cmVg.
• a further method to prepare the solid catalyst component of the invention comprises halogenating magnesium dihydrocarbyloxide compounds, such as magnesium dialkoxide or diaryloxide, with solution of TiCl 4 in aromatic hydrocarbon (such as toluene, xylene, etc.) at temperatures between 80 and 130 °C.
• the treatment with TiCl 4 in aromatic hydrocarbon solution can be repeated one or more times, and the ⁇ -substituted succinate is added during one or more of these treatments.
• the desired succinate of formula (I) can be added as such or, in an alternative way, it can be obtained in situ by using an appropriate precursor capable to be transformed in the desired electron donor compound by means, for example, of known chemical reactions such as esterification, transesterification, etc.
• the succinate of formula (I) is used in molar ratio with respect to the MgCl 2 of from 0.01 to 1 preferably from 0.05 to 0.5.
• the additional electron donor compound can be the same as the electron donor (d) disclosed below.
• very good results have been obtained when the 1,3-diethers of formula (II) below are used as internal donors together with a succinate of formula
• the solid catalyst components according to the present invention are converted into catalysts for the polymerization of olefins by reacting them with organoaluminum compounds according to known methods.
• CH 2 CHR, in which R is hydrogen or a hydrocarbyl radical with 1-12 carbon atoms, comprising the product of the reaction between:
• the alkylaluminum compound (b) is preferably selected from the trialkyl aluminum compounds such as for example triethylaluminum, triisobutylaluminum, tri-n-butylaluminum, tri-n- hexylaluminum, tri-n-octylaluminum. It is also possible to use mixtures of trialkylaluminum's with alkylaluminum halides, alkylaluminum hydrides or alkylaluminum sesquichlorides such as AlE ⁇ Cl and Al 2 Et 3 Cl 3 . Also alkylalumoxanes can be used.
• the external donor (c) can be of the same type or it can be different from the succinate of formula (I).
• Preferred external electron donor compounds include silicon compounds, ethers, esters, such as ethyl 4-ethoxybenzoate, amines, heterocyclic compounds and particularly 2,2,6,6-tetramethylpiperidine, ketones and the 1,3-diethers of the general formula (II):
• R 1 , R ⁇ , R m , R IV , R v and R ⁇ are hydrogen or hydrocarbon radicals having from 1 to 18 carbon atoms, and R v ⁇ and RTM, equal or different from each other, have the same meaning of R'-R VI except that they cannot be hydrogen; one or more of the R'-R ⁇ groups can be linked to form a cycle.
• Particularly preferred are the 1,3-diethers in which R 1 * 11 and R vm are selected from C,-C 4 alkyl radicals, R m and RTM form a condensed unsaturated cycle and R 1 , R ⁇ , R v and R ⁇ are hydrogen.
• the use of 9,9- bis(methoxymethyl)fluorene is particularly preferred.
• Another class of preferred external donor compounds is that of silicon compounds of formula R R ⁇ S ⁇ OR 9 )-, where a and b are integer from 0 to 2, c is an integer from 1 to 3 and the sum (a+b+c) is 4; R 7 , R 8 , and R 9 , are C1-C18 hydrocarbon groups optionally containing heteroatoms.
• Particularly preferred are the silicon compounds in which a is 1, b is 1, c is 2, at least one of R 7 and R 8 is selected from branched alkyl, alkenyl, alkylene, cycloalkyl or aryl groups with 3-10 carbon atoms optionally containing heteroatoms and R 9 is a C,-C 10 alkyl group, in particular methyl.
• Examples of such preferred silicon compounds are cyclohexylmethyldimethoxysilane, diphenyldimethoxysilane, methyl-t-butyldimethoxysilane, dicyclopentyldimethoxysilane, 2- ethylpiperidinyl-2-t-butyldimethoxysilane and (1,1,1 -trifiuoro-2-propyl)-2- ethylpiperidinyldimethoxy silane and (1,1,1 -trifluoro-2-propyl)-methyldimethoxy silane.
• examples of such preferred silicon compounds are cyclohexyltrimethoxysilane, t-butyltrimethoxysilane and thexyltrimethoxysilane.
• the electron donor compound (c) is used in such an amount to give a molar ratio between the organoaluminum compound and said electron donor compound (c) of from 0J to 500, preferably from 1 to 300 and more preferably from 3 to 100.
• the catalysts of the invention allow to obtain, with high yields, polymers having a high isotactic index (expressed by high xylene insolubility X.I.), thus showing an excellent balance of properties.
• the succinates of formula (I) can be used also as external donors with good results.
• they are able to give very good results even when they are used as external electron donor compounds in combination with catalyst components containing an internal donor different from the succinates of formula (I).
• the esters of dicarboxylic acids known in the art are normally not able to give satisfactory results when used as external donors.
• the aluminum alkyl compound (ii) has the same meanings of the aluminum compound (b) given above.
• the electron donor compound (d) can be selected from ethers, esters of organic mono or bicarboxylic acids, such as phthalates, benzoates, glutarates, succinates having a different structure from those of formula (I), amines. Preferably, it is selected from 1,3-propanediethers of formula (II) and esters of organic mono or bicarboxylic acids in particular phthalates.
• the preferred ⁇ -olefins to be (co)polymerized are ethene, propene, 1-butene, 4-methyl-l-pentene, 1- hexene and 1-octene.
• the above-described catalysts have been used in the (co)polymerization of propene and ethylene to prepare different kinds of products.
• HDPE high density ethylene polymers
• LLDPE linear low density polyethylenes
• NLDPE and ULDPE very low density and ultra low density
• propylene polymers obtainable with the catalyst of the invention showing broad MWD coupled with high isotactic index and high modulus.
• said polymers having a polydispersity index of higher than 5, a content of isotactic units expressed in terms of pentads of higher than 97% and a flexural modulus of at least 2000 MPa.
• the polydispersity index is higher than 5J
• the flexural modulus is higher than 2100
• the percent of propylene units in form of pentads is higher than 97.5%.
• Any kind of polymerization process can be used with the catalysts of the invention that are very versatile.
• the polymerization can be carried out for example in slurry using as diluent an inert hydrocarbon solvent, or in bulk using the liquid monomer (for example propylene) as a reaction medium. Moreover, it is possible to carry out the polymerization process in gas-phase operating in one or more fluidized or mechanically agitated bed reactors.
• the catalyst of the present invention can be used as such in the polymerization process by introducing it directly into the reactor.
• the catalyst can be pre-polymerized before being introduced into the first polymerization reactor.
• pre-polymerized means a catalyst which has been subject to a polymerization step at a low conversion degree.
• a catalyst is considered to be pre-polymerized when the amount the polymer produced is from about 0J up to about 1000 g per gram of solid catalyst component.
• the pre-polymerization can be carried out with the ⁇ -olefins selected from the same group of olefins disclosed before.
• the conversion of the pre-polymerized catalyst component is from about 0.2 g up to about 500 g per gram of solid catalyst component.
• the pre-polymerization step can be carried out at temperatures from 0 to 80 °C preferably from 5 to 50 °C in liquid or gas-phase.
• the pre-polymerization step can be performed in-line as a part of a continuous polymerization process or separately in a batch process.
• the batch pre- polymerization of the catalyst of the invention with ethylene in order to produce an amount of polymer ranging from 0.5 to 20 g per gram of catalyst component is particularly preferred.
• the polymerization is generally carried out at temperature of from 20 to 120 °C, preferably of from 40 to 80 °C.
• the operating pressure is generally between 0.5 and 10 MPa, preferably between 1 and 5 MPa.
• the operating pressure is generally between 1 and 6 MPa preferably between 1.5 and 4 MPa.
• Hydrogen or other compounds capable to act as chain transfer agents can be used to control the molecular weight of polymer.
• Succinates can be prepared according to known methods described in the literature.
• HMPA hexamethylphosphoramide
• Isobutyric acid (14.6 mL, 157 mmol) was added to a freshly prepared lithium disopropyl amide (LDA) solution (see synthesis of succinate ex 23 , 41 mL, 314 mmol of diisopropylamine and 126 mL of BuLi (2.5 M in hexanes; 314 mmol) and 1 L of THF) at 0 °C. This mixture was stirred at 0 °C for 15 minutes and subsequently for 4 h at 45 °C.
• LDA lithium disopropyl amide
• Density was determined on the homogenized polymers (from the M.I. determination) by using a gradient column and following the ASTM D-1505 procedure. Determination of polydispersity index (P.I.)
• This property is strictly connected with the molecular weight distribution of the polymer under examination. In particular it is inversely proportional to the creep resistance of the polymer in the molten state. Said resistance called modulus separation at low modulus value (500 Pa), was dete ⁇ nined at a temperature of 200 °C by using a parallel plates rheometer model RMS-800 marketed by RHEOMETRICS (USA), operating at an oscillation frequency which increases from 0J rad/sec to 100 rad/sec. From the modulus separation value, one can derive the P.I. by way of the equation:
• the mixture was reacted at 120 °C for 60 min and, then, the supernatant liquid was siphoned off.
• the solid was washed six times with anhydrous hexane (6 x 100 mL) at 60 °C. Finally, the solid was dried under vacuum and analyzed.
• the type and amount of succinate (wt %) and the amount of Ti (wt %) contained in the solid catalyst component are reported in Table 1. Polymerization results are reported in Table 2.
• the polymer obtained in the example 10 was characterized and it showed a polydispersity index of 6, a content of isotactic units expressed in terms of pentads of 98% and a flexural modulus of 2150 MPa.
• the above mentioned solid catalyst component was polymerized according to the general polymerization procedure but without using dicyclopentyldimethoxysilane.
• the solid catalyst component of example 10 was polymerized according to the general polymerization procedure but instead of dicyclopentyldimethoxysilane the electron donors of Table 3 were used. The amount and type of electron donor and the polymerization results are reported in Table 3 Comparative Example 39
• the above mentioned solid catalyst component was polymerized as in the general polymerization procedure.
• the solid catalyst component of example 40 was polymerized according to the general polymerization procedure but without using dicyclopentyldimethoxysilane.
• the above mentioned solid catalyst component was polymerized according to the general polymerization procedure but instead of dicyclopentyldimethoxysilane, 0.35 mmol of diethyl 2,3-diisopropylsuccinate were used.
• the spherical support prepared according to the general method described in Ex. 2 of USP 4,399,054 (but operating at 3000 rpm instead of 10000 rpm) was subjected to thermal treatment, under nitrogen flow, within the temperature range of 50-150 °C, until spherical particles having a residual alcohol content of about 35 wt.% (1J mol of alcohol per mol of MgCl 2 ) were obtained. 16 g of this support were charged, under stirring at 0 °C, to a 750 mL reactor containing 320 mL of pure TiCl 4 .
• the catalyst composition was as follow:
• a 4.0 liter stainless-steel autoclave equipped with a magnetic stirrer, temperature and pressure indicator, feeding line for ethene, propane, hydrogen, and a steel vial for the injection of the catalyst was used and purified by fluxing pure nitrogen at 70 °C for 60 minutes and than washed with propane.
• the solid catalyst of the example 43 was used in the ethylene/ 1-butene copolymerization as reported in the general procedure but without using any external donor.
• the other polymerization conditions are reported in Table 4 while the polymer characteristics are collected in Table 5.
• the solid catalyst of the example 43 was used in the ethylene/ 1-butene copolymerization as reported in the general procedure but by using 0.56 mmol of cyclohexylmethyldimethoxysilane as external donor.
• the solid catalyst of the example 43 was used in the ethylene/ 1-butene copolymerization as reported in the general procedure but by using 0.56 mmol of diethyl 2,3-diisopropylsuccinate as external donor.
• the solid catalyst of the example 43 was used in the ethylene/ 1-butene copolymerization in a fluidized gas-phase reactor as described below.
• the gas-phase apparatus was purified by fluxing pure nitrogen at
• the autoclave was closed and 80 g of propane and 90 g of propene were introduced at 40 °C. The mixture was allowed stirring at 40 °C for 30 minutes. The autoclave was then depressurized to eliminate the excess of unreacted propene, and the obtained prepolymer was injected into the gas-phase reactor by using a propane overpressure (1 bar increase in the gas- phase reactor). The final pressure, in the fluidized reactor, was maintained constant at 75 °C for 180 minutes by feeding a 10 wt.% 1-butene/ethene mixture.
• Example 48 The reactor was depressurised and the temperature was dropped to 30 °C. The collected polymer was dried at 70 °C under a nitrogen flow and weighted. The polymer characteristics are collected in Table 5.
• Example 48 The polymer characteristics are collected in Table 5.
• the solid catalyst was then used in the ethylene/ 1-butene copolymerization as reported in the general procedure but using diethyl 2,3-diisopropylsuccinate as E.D.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Emergency Medicine (AREA)
• Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)

Priority Applications (11)

Applications Claiming Priority (2)

Related Child Applications (1)

Publications (1)

Family

ID=8240100

Family Applications (1)

Country Status (22)

Cited By (176)

Families Citing this family (92)

Citations (8)

Family Cites Families (28)

• 2000
  • 2000-04-12 WO PCT/EP2000/003333 patent/WO2000063261A1/en not_active Ceased
  • 2000-04-12 HU HU0103083A patent/HUP0103083A3/hu unknown
  • 2000-04-12 PL PL00345209A patent/PL345209A1/xx not_active IP Right Cessation
  • 2000-04-12 ES ES00926912T patent/ES2269135T3/es not_active Expired - Lifetime
  • 2000-04-12 CA CA002334743A patent/CA2334743C/en not_active Expired - Lifetime
  • 2000-04-12 CN CNB008011230A patent/CN1240729C/zh not_active Expired - Lifetime
  • 2000-04-12 DE DE60029714T patent/DE60029714T2/de not_active Expired - Lifetime
  • 2000-04-12 BR BRPI0006095-0B1A patent/BR0006095B1/pt active IP Right Grant
  • 2000-04-12 AU AU45486/00A patent/AU777683B2/en not_active Ceased
  • 2000-04-12 EP EP00926912A patent/EP1088009B1/en not_active Expired - Lifetime
  • 2000-04-12 ID IDW20010114A patent/ID28200A/id unknown
  • 2000-04-12 IL IL140154A patent/IL140154A/en active IP Right Grant
  • 2000-04-12 RU RU2001101489/04A patent/RU2225415C2/ru active
  • 2000-04-12 AT AT00926912T patent/ATE335014T1/de active
  • 2000-04-12 US US09/762,363 patent/US6818583B1/en not_active Expired - Lifetime
  • 2000-04-12 JP JP2000612346A patent/JP4717219B2/ja not_active Expired - Lifetime
  • 2000-04-12 CN CNB2003101242368A patent/CN1294159C/zh not_active Expired - Lifetime
  • 2000-04-12 KR KR1020007014289A patent/KR100700957B1/ko not_active Expired - Lifetime
  • 2000-04-13 TW TW089106866A patent/TWI229086B/zh not_active IP Right Cessation
  • 2000-04-14 MY MYPI20001602A patent/MY124016A/en unknown
  • 2000-04-17 AR ARP000101780A patent/AR043275A1/es active IP Right Grant
  • 2000-09-24 SA SA00210385A patent/SA00210385B1/ar unknown
  • 2000-12-14 NO NO20006388A patent/NO20006388L/no not_active Application Discontinuation
• 2004
  • 2004-08-31 US US10/930,452 patent/US20050032633A1/en not_active Abandoned
• 2011
  • 2011-01-11 JP JP2011003209A patent/JP5372030B2/ja not_active Expired - Lifetime

Patent Citations (9)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events