WO1986002170A1 - Polarizing film - Google Patents
Polarizing film Download PDFInfo
- Publication number
- WO1986002170A1 WO1986002170A1 PCT/JP1985/000328 JP8500328W WO8602170A1 WO 1986002170 A1 WO1986002170 A1 WO 1986002170A1 JP 8500328 W JP8500328 W JP 8500328W WO 8602170 A1 WO8602170 A1 WO 8602170A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- polarizing film
- dye
- formula
- atom
- Prior art date
Description
Claims