US20060173100A1 - Fluororesin composite compositions - Google Patents

Fluororesin composite compositions Download PDF

Info

Publication number
US20060173100A1
US20060173100A1 US10/546,006 US54600605A US2006173100A1 US 20060173100 A1 US20060173100 A1 US 20060173100A1 US 54600605 A US54600605 A US 54600605A US 2006173100 A1 US2006173100 A1 US 2006173100A1
Authority
US
United States
Prior art keywords
heat
meltable fluoropolymer
layered
composite composition
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/546,006
Other languages
English (en)
Inventor
Jeong Lee
Noriyuki Suzuki
Shousaku Kondo
Hajime Sato
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chemours Mitsui Fluoroproducts Co Ltd
EIDP Inc
Original Assignee
Du Pont Mitsui Fluorochemicals Co Ltd
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=32905269&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20060173100(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Du Pont Mitsui Fluorochemicals Co Ltd, EI Du Pont de Nemours and Co filed Critical Du Pont Mitsui Fluorochemicals Co Ltd
Assigned to DU PONT-MITSUI FLUOROCHEMICALS CO. LTD., E.I. DU PONT DE NEMOURS & COMPANY reassignment DU PONT-MITSUI FLUOROCHEMICALS CO. LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KONDO, SHOUSAKU, LEE, JEONG CHANG, SATO, HAJIME, SUZUKI, NORIYUKI
Publication of US20060173100A1 publication Critical patent/US20060173100A1/en
Priority to US12/580,823 priority Critical patent/US8618203B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/49—Phosphorus-containing compounds
    • C08K5/50—Phosphorus bound to carbon only
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/022—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the choice of material
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/20—Compounding polymers with additives, e.g. colouring
    • C08J3/203—Solid polymers with solid and/or liquid additives
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/02—Elements
    • C08K3/04—Carbon
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K9/00—Use of pretreated ingredients
    • C08K9/04—Ingredients treated with organic substances
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L27/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
    • C08L27/02—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L27/12—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2327/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers
    • C08J2327/02—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment
    • C08J2327/12—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms

Definitions

  • the present invention relates to a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties, and dynamic properties such as storage modulus. More specifically, the present invention relates to a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties, and dynamic properties such as storage modulus which comprises a heat-meltable fluoropolymer fine powder and a particular organically-modified layered-compound.
  • the present invention further relates to a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties, and dynamic properties such as storage modulus which is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound in advance so that the layered-compound is dispersed uniformly in the fine heat-meltable fluoropolymer powder, and then melt-mixing the mixture by use of a melt mixing extruder so that the layered-compound is further dispersed, cleaved or intercalated by shear stress in the heat-meltable fluoropolymer.
  • Heat-meltable fluoropolymers such as tetrafluoroethylene-perfluoro(alkylvinylether) copolymer (PFA), tetrafluoroethylene-hexafluoropropylene copolymer (FEP) and tetrafluoroethylene-ethylene copolymer (ETFE) are used for the holding jigs and tube materials for the chemical liquid supply line in semiconductor manufacturing equipment because of their excellent heat resistance, chemical resistance, non-stickiness and other properties.
  • the tubes made of these resins have to be replaced periodically owing to such problems as the contamination of the peripheral devices and environmental pollution due to the permeation of the chemical liquid. For this reason, there is a demand for materials showing lower chemical liquid permeability.
  • the tubes show low thermal conductivity, and therefore there is also a demand for materials exhibiting higher thermal conductivity.
  • Japanese Patent Publication 2000-190431 describes a multi-layer laminate whose gas or chemical liquid permeability is lowered by melt-mixing a scale-like filler and a fluoropolymer and by laminating.
  • Japanese Patent Publication HEI 2-10226 describes a method in which a layered clay mineral used for a filler is organically-modified, a monomer is inserted into the space between the laminas of this layered-compound where interlaminar distance is increased by organic-modification, and then the layered-compound is dispersed on nano scale by utilizing polymerization energy released during the polymerization of the aforesaid monomer.
  • the aforesaid polymerization method cannot be said to be economical because although the polymerization method allows the filler to be dispersed efficiently, it requires polymerization equipment, entailing high cost. Besides, since the monomer that is inserted between the laminas of the aforesaid layered clay mineral will not stay stably between the laminas, a gas monomer is not preferable, and the choice of the monomer is limited to a liquid monomer.
  • each of Japanese Patent Publication HEI 7-47644 and Japanese Patent Publication HEI 7-70357 describes a method in which a layered clay mineral is organized with organic cations in advance, the layered clay mineral is caused to be infinite-swolled by use of an organic solvent, and then the clay mineral is caused to come into contact with a melted resin liquid so that it is dispersed in the resin on nano scale.
  • such method essentially requires the use of a large amount of an organic solvent in causing a layered clay mineral to be swelled, but a fluoropolymer has the problem of extremely low compatibility with an organic solvent.
  • the infinite-swollen layered-compound by use of the aforesaid organic solvent also has the problem of returning to a swollen state from such infinite-swollen state as part of the organic solvent will evaporate at the temperature of extrusion of the fluoropolymer in such process of coming into contact with the melted resin.
  • the inventors of the present invention have paid notice that the thermal conductivity, gas and chemical liquid barrier properties and dynamic properties such as storage modulus of a heat-meltable fluoropolymer composite can be improved by dispersing a layered-compound in which normally the unit crystal laminas constituting the layered-compound are present in such form that they are piled, further exfoliating (hereinafter referred to as “cleavage” in some cases) part of the layered-compound thus dispersed or exfoliating heat-meltable fluoropolymer between the laminas of the layered-compound so that the number of the laminas of the layered-compound is increased even if the weight percent of the layered-compound laminas that are present in the heat-meltable fluoropolymer is same.
  • cleavage further exfoliating
  • the present invention provides a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties and dynamic properties such as storage modulus.
  • the present invention provides a heat-meltable fluoropolymer composite composition comprising a heat-meltable fluoropolymer fine powder and a layered-compound organically modified by treatment with tetraphenyl phosphonium ions.
  • Use of such particular layered-compound makes it possible to obtain a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties and dynamic properties such as storage modulus only by melt-mixing such layered-compound by exerting shear stress by use of a melt-mixing extruder.
  • the present invention also provides a heat-meltable fluoropolymer composite composition which is obtained by a process (I) in which a heat-meltable fluoropolymer powdery composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound and a process (II) in which such heat-meltable fluoropolymer powdery composition thus obtained is melt-mixed by exerting shear stress by means of a melt-mixing extruder.
  • a process (I) in which a heat-meltable fluoropolymer powdery composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound
  • a process (II) in which such heat-meltable fluoropolymer powdery composition thus obtained is melt-mixed by exerting shear stress by means of a melt-mixing extruder.
  • a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties and dynamic properties such as storage modulus is obtained as a result of the layered-compound is dispersed, exfoliated or exfoliated more uniformly in the heat-meltable fluoropolymer under process (II) in which the materials are melt-mixed under shear stress, in addition to the mixing under process (I).
  • an excellent effect in improving the physical properties can be produced by using a layered-compound organically modified by treatment with organic phosphonium ions, preferably tetraarylphosphonium ions, more preferably tetraphenylphosphonium ions.
  • the present invention provides a process for manufacturing a heat-meltable fluoropolymer composite composition which comprises a process (I) in which a heat-meltable fluoropolymer powdery composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound and a process (II) in which such heat-meltable fluoropolymer powdery composition thus obtained is melted and mixed by exerting shear stress by means of a melt mixing extruder.
  • a process for manufacturing a heat-meltable fluoropolymer composite composition which comprises a process (I) in which a heat-meltable fluoropolymer powdery composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound and a process (II) in which such heat-meltable fluoropolymer powdery composition thus obtained is melted and mixed by exerting shear stress by means of a melt mixing extruder.
  • preferred embodiment is that an agglomerate powder having not more than 10 ⁇ m in average particle size which comprises agglomerated colloidal fine particles of heat-meltable fluoropolymer is used as the heat-meltable fluoropolymer fine powder. Furthermore, according to preferable embodiments of the mixing of a fine heat-meltable fluoropolymer powder and a layered-compound, a high-speed rotary mixer is used.
  • FIG. 1 is an electron microscopic picture of the powdery composition obtained in Example 1 described below.
  • FIG. 2 is an electron microscopic picture of the powdery composition obtained in Example 6 described below.
  • tetrafluoroethylene-perfluoro(alkylvinylether) copolymer (hereinafter referred to as “PFA”), tetrafluoroethylene-hexafluoropropylene copolymer (hereinafter referred to as “FEP”), tetrafluoroethylene-hexafluoropropylene-perfluoro(alkylvinylether) (alkylvinylether) copolymer (hereinafter referred to as “EPE”), tetrafluoroethylene-ethylene copolymer (hereinafter referred to as “ETFE”), polyvinylidenefluoride (hereinafter referred to as “PCTFE”) and chlorotrifluoroethylene-ethylene copolymer (hereinafter referred to as “ECTFE”) can be cited.
  • PFA tetrafluoroethylene-perfluoro(alkylvinylether) copolymer
  • FEP tetrafluoroethylene
  • heat-meltable fluoropolymer examples include tetrafluoroethylene-perfluoro(alkylvinylether) copolymer wherein alkyl group of perfluoro(alkylvinylether) is the one having 1 to 5 carbon atoms, more preferably 1 to 3 carbon atoms.
  • melt viscosity or molecular weight of any of these heat-meltable fluoropolymers there is no particular restriction on the melt viscosity or molecular weight of any of these heat-meltable fluoropolymers.
  • the melt viscosity of the heat-meltable fluoropolymer is preferably 10 g/10 min to 40 g/10 min in terms of the melt index (ASTM D1238: 372° C., 5-kg load).
  • an agglomerated powder having average particle size of not more than 10 ⁇ m, preferably not more than 7 ⁇ m, more preferably not more than 5 ⁇ m, which comprises by agglomerating colloidal fine particles of heat-meltable fluoropolymer having average particle size of approximately 0.2 ⁇ m is used suitably.
  • Such agglomerated powder can be obtained, for example, by adding an electrolytic substance to a heat-meltable fluoropolymer aqueous dispersion obtained by emulsion polymerization which contains in water approximately 1 to 75% by weght of colloidal fine particles of a heat-meltable fluoropolymer whose average particle size is approximately 0.1 to 0.3 ⁇ m, causing the colloidal fine particles of the heat-meltable fluoropolymer to be agglomerated with mechanical agitation, and then separating the agglomerated colloidal fine particles from the aqueous medium, and drying and washing them as required.
  • the electrolytic substance used for the purpose of agglomerating the colloidal fine particles of the heat-meltable fluoropolymer in the heat-meltable fluoropolymer aqueous dispersion water-soluble inorganic or organic compounds such as HCl, H 2 SO 4 , HNO 3 , H 3 PO 4 , Na 2 SO 4 , MgCl 2 , CaCl 2 , sodium formate, potassium acetate and ammonium carbonate can be cited.
  • Preferable examples of the electrolytic substance include the compounds that can be evaporated under the drying process in which the heat-meltable fluoropolymer fine particles after agglomeration are separated and dried, such as HCl and HNO 3 , for example.
  • These electrolytic substances is preferably 1 to 15% by weght, especially 1.5 to 10% by weght against the weight of the heat-meltable fluoropolymer and is preferably added in the form of an aqueous solution to a heat-meltable fluoropolymer aqueous dispersion. If the weight of the electrolytic substance is less than 1% by weght, it will take a long time to agglomerate the colloidal fine particles of the heat-meltable fluoropolymer, and consequently productivity will be decline.
  • the equipment for causing the colloidal fine particles of the heat-meltable fluoropolymer to be agglomerated.
  • the equipment preferably has a means for agitation that is capable of keeping circumferential velocity of not lower than approximately 4 m/sec, such as a propeller vane, turbine vane, paddle vane, paddle-shaped vane, horseshoe-shaped vane and helical vane, and a means for water discharge.
  • the colloidal fine particles of the heat-meltable fluoropolymer are agglomerated to become agglomerated particles and are separated from the aqueous medium so that they will come up and float.
  • agitation speed is preferably kept at not lower than approximately 4 m/sec.
  • agitation speed is lower than 4 m/sec, it will take a long time to cause the colloidal fine particles of the heat-meltable fluoropolymer to be agglomerated, and in addition, the aqueous medium will tend not to be readily discharged from the agglomerated particles of the heat-meltable fluoropolymer. Agitation is carried out until the agglomerated particles are separated from the aqueous medium.
  • the agglomerated heat-meltable fluoropolymer particles thus obtained are washed with water as required and then dried at a temperature not higher than the melting point of the heat-meltable fluoropolymer. Since such fluoropolymer fine powder has weak cohesion force between its inner particles, it is suitable to be ground down to primary particles by means of a high-speed rotating blade of a rotary mixer.
  • the layered-compound used in the present invention is preferably a layered-compound not more than 10 ⁇ m in particle size which has such structure that its unit crystal laminas are present in such form that they are piled.
  • it is one kind of layered-compound selected from among smectite-type clay minerals such as montmorillonite, hectoliter and vermiculite, various clay minerals such as zirconium phosphate and titanium phosphate, micas such as Na-type tetrasiliconfluorine mica and Li-type tetrasiliconfluorine mica, and graphite.
  • Such mica and graphite may be either natural or synthetic materials.
  • Such graphite is preferably scale-like graphite.
  • layered-compounds it is preferably to increase the interlaminar distance by exchanging inorganic ions between laminas with other ions or inserting organic matter (hereinafter referred to as “organic modification”) because it becomes easy to cleave these layered-compounds or intercalate heat-meltable fluoropolymer into them by shear stress in the mixing process in a high-speed rotary mixer or in the melt-mixing process in a melt-mixing extruder.
  • organic modification inorganic ions between laminas with other ions or inserting organic matter
  • the organic matter used in such organizing treatment is preferably organic onium ions.
  • organic onium ions there is no particular restriction on such organic onium ions, and organic onium ions that are not thermally decomposed at a temperature higher by at least 10° C. than the melting point of the heat-meltable fluoropolymer are preferable.
  • phosphonium ions are preferable which show a higher thermal decomposition temperature than ammonium ions, which are generally used as common organic onium ions.
  • Examples of such phosphonium ions include tetraethylphosphonium ions, tetrabutylphosphonium ions, tetrahexylphosphonium ions, dihexadecyldimethylphosphonium ions, dioctyldimethylphosphonium ions, cetyltrimethylphosphonium ions, cetyltriethylphosphonium ions, cetyldimethylethylphosphonium ions, tributylphosphonium ions, trihexylphosphonium ions, dioctylphosphonium ions, hexadecylphosphonium ions, tetraphenylphosphonium ions, n-butyltriphenylphosphonium ions, and benzyltriphenylphosphonium ions.
  • organic onium ions thermally stable even at the heat-meltable fluoropolymer melt molding temperature of at least not lower than 300° C. tetraphenylphosphonium ions, n-butyltriphenylphosphonium ions, and benzyltriphenylphosphonium ions are preferable, and particularly tetraphenylphosphonium ions are preferable.
  • the mixing ratio of the aforesaid layered-compound is preferably 1 to 40% by weight, more preferably 2 to 30% by weight, and much more preferably 3 to 20% by weight based on the weight of the heat-meltable fluoropolymer composite composition.
  • a layered-compound mixing ratio of less than 1% by weight will produce only a little effect in improving the thermal conductivity or gas and chemical liquid barrier properties. Further, a layered-compound mixing ratio of over 40% by weight will cause a problem in processibility and flexibility.
  • the mixing ratio of the heat-meltable fluoropolymer fine powder is preferably 60 to 99% by weight, more preferably 70 to 98% by weight, much more preferably 80 to 97% by weight based on the weight of the heat-meltable fluoropolymer composite composition.
  • the heat-meltable fluoropolymer fine powder should contain a heat-meltable fluoropolymer containing a functional group, that is, a heat-meltable fluoropolymer containing a functional group should be used as part of the heat-meltable fluoropolymer fine powder.
  • heat-meltable fluoropolymer containing a functional group preferred are heat-meltable fluoropolymers containing a functional group selected from the group of the carboxylic acid group or its derivatives, hydroxyl group, nitrile group, cyanato group, carbamoyloxy group, phosphonooxy group, sulphonic acid group or its derivative group, and sulphohalide group, such as —COOH, —CH 2 COOH, —COOCH 3 , —CONH 2 , —OH, —CH 2 OH, —CN, —CH 2 O(CO)NH 2 , —CH 2 OCN, —CH 2 OP(O)(OH) 2 , —CH 2 OP(O)Cl 2 and —SO 2 F.
  • a functional group selected from the group of the carboxylic acid group or its derivatives, hydroxyl group, nitrile group, cyanato group, carbamoyloxy group, phosphonooxy group,
  • Such heat-meltable fluoropolymers can be obtained by obtaining heat-meltable fluoropolymer by emulsion polymerization and then adding or substituting these functional groups, or by copolymerizing a fluorine-containing monomer containing any of the aforesaid functional groups at the time of the polymerization of the heat-meltable fluoropolymer.
  • the heat-meltable fluoropolymer obtained by copolymerizing a fluorine-containing monomer containing any of the aforesaid functional groups at the time of the polymerization of the heat-meltable fluoropolymer is preferably used.
  • fluorine-containing monomer containing the aforesaidan functional group examples include fluorinated vinyl ether compounds containing a functional group that is shown by the formula: CF 2 ⁇ CF [OCF 2 CF(CF 3 )] m —O—(CF 2 ) n —X [where m is 0 to 3; n is 0 to 4; X represents —COOH, —CH 2 COOH, —COOCH 3 , —CONH 2 , —OH, —CH 2 OH, —CN, —CH 2 O(CO)NH 2 , —H 2 OCN, —CH 2 OP(O)(OH) 2 , —CH 2 OP(O)Cl 2 or SO 2 F.]
  • the fluorine-containing monomer containing such functional group is preferably copolymerized in the fluoropolymer containing a functional group in the amount of 0.5 to 10% by weght, preferably 1 to 5% by weght. If the content of the fluorine-containing monomer containing such functional group to be copolymerized is lower than 0.5% by weght, only a little effect will be produced in improving compatibility between the aforesaid layered-compound subjected to organizing treatment and the heat-meltable fluoropolymer and facilitating the insertion of the heat-meltable fluoropolymer between the laminas of the organized layered-compound in the melting and mixing process in a melting and mixing extruder to increase the inter-layer distance and accelerate cleavage, thereby causing the heat-meltable fluoropolymer and the layered-compound to be dispersed more uniformly.
  • the content of the fluorine-containing monomer containing such functional group to be copolymerized is higher than 10% by weight, a reaction similar to crosslinking reaction will occur due to the strong interaction between the fluoropolymers containing a functional group, with the result that the viscosity will increase sharply. This will make the insertion of the compound into the laminas or melt processing difficult and lead the heat resistance of the fluoropolymer containing a functional group to tend to decline.
  • the viscosity or molecular weight of the heat-meltable fluoropolymer containing a functional group is preferably not higher than that of the heat-meltable fluoropolymer and is more preferably close to that of the heat-meltable fluoropolymer.
  • the relative use amount of the heat-meltable fluoropolymer containing a functional group based on the heat-meltable fluoropolymer fine powder differs with the type of the functional group and the content of the fluorine-containing monomer containing a functional group but is normally 0.1 to 50% by weight against 99.9 to 50% by weight of the heat-meltable fluoropolymer fine powder, preferably 1 to 45% by weight against 99 to 55% by weight of the heat-meltable fluoropolymer fine powder.
  • the heat-meltable fluoropolymer containing a functional group is preferably mixed with the heat-meltable fluoropolymer fine powder by means of a high-speed rotary mixer.
  • the heat-meltable fluoropolymer fine powder not more than 10 ⁇ m in average particle size and the layered-compound not more than 10 ⁇ m in average particle size should be pulverized and mixed in advance so that a heat-meltable fluoropolymer fine powder mixed composition in which the layered-compound has been dispersed uniformly in the heat-meltable fluoropolymer fine powder in advance is obtained, and then the layered-compound is further dispersed, exfoliated or exfoliated more uniformly in the heat-meltable fluoropolymer.
  • the layered-compound can be dispersed uniformly in the heat-meltable fluoropolymer fine powder in advance by pulverizing and mixing the heat-meltable fluoropolymer fine powder not more than 10 ⁇ m in average particle size and the layered-compound not more than 10 ⁇ m in average particle size by use of a high-speed rotary mixer having blades or cutter knives that rotate at the rotational speed of not lower than 1,500 rpm or the circumferential velocity of not lower than 35 m/sec, preferably at the rotational speed of 3,000 to 20,000 rpm or the circumferential velocity of 70 to 115 m/sec.
  • any layered-compound that has been organized with tetraphenylphosphonium ions is used as the layered-compound, it is possible to use such mixers to mix such layered-compound and the heat-meltable fluoropolymer fine powder in advance to obtain the raw material for melt mixing under shear stress.
  • antistatic agents such as carbon black may be added to prevent the heat-meltable fluoropolymer fine powder from being deposited on the inside walls of the high-speed rotary mixer due to static electricity.
  • any other additives may be added to suit the purpose.
  • the heat-meltable fluoropolymer composite composition of the present invention which comprises a heat-meltable fluoropolymer fine powder and a layered-compound may be melt-mixed by a melt-mixing extruder after being compacted by use of a compactor so that they may be fed well to the hopper of the melt mixing extruder.
  • twin-screw extruders are preferably used from the perspective of shear stress for the sake of exfoliating the layered-compound more effectively so that it will be dispersed in the heat-meltable fluoropolymer, depending on the type and melt viscosity of the heat-meltable fluoropolymer used.
  • the melt-mixing temperature in such twin-screw extruder is preferably below 360° C. for the objective of avoiding the decomposition of the layered-compound subjected to organic modification.
  • the method for pulverizing and mixing the heat-meltable fluoropolymer fine powder not more than 10 ⁇ m in average particle size and the layered-compound not more than 10 ⁇ m in average particle size in advance by use of a high-speed rotary mixer and then melt-mixing the mixture by use of a melt-mixing mixer is different from the common mixing process for mixing a melt-pelletized heat-meltable fluoropolymer powder several hundred ⁇ m in average particle size or heat-meltable fluoropolymer pellets several thousand ⁇ m in average particle size and a filler.
  • the cleavage or intercalation of an organically modified layered-compound and a heat-meltable resin has to be carried out simultaneously while the layered-compound is being dispersed in the heat-meltable resin in the melt-mixing mixer.
  • the heat-meltable fluoropolymer fine powder and the organically modified layered-compound are pulverized and mixed uniformly in advance by use of a high-speed rotary mixer, and consequently it is possible to shorten overall melt-mixing time in the melting and mixing mixer.
  • cleavage or intercalation is carried out for the most part.
  • a layered-compound organically modified with tetraphenylphosphonium ions is used as the layered-compound, it is possible to take a longer melt-mixing time in a melt-mixing extruder because such layered-compound shows a high temperature at which thermal decomposition begins and high heat resistance, and it is also possible to carry out cleavage or intercalation easily by melt-mixing alone in a melt-mixing extruder even if the pulverizing and mixing process as mentioned above is omitted.
  • tetrafluoroethylene perfluoropropylvinylether (PPVE) was used for tetrafluoroethylene perfluoro(alkylvinylether) copolymer (PFA) copolymer, and the nitrogen gas permeability and thermal conductivity of the heat-meltable fluoropolymer composite composition were measured by the following methods:
  • the nitrogen gas permeability of film approximately 0.3 mm in thickness and 130 mm in diameter which had been prepared by melt-compression-molding the heat-meltable fluoropolymer composite composition at 350° C. was measured at 23° C. by use of a gas permeability measuring device (Model S-69 160 ml) available from Shibata Kagaku Kogyou Co., Ltd. The measurement values were expressed in 10 ⁇ 11 cm 3 (STP) cm/cm 2 .sec.cmHg.
  • the thermal conductivity of a specimen 30 mm in diameter and 7 mm in height cut from a billet (diameter: 35 mm; height: 40 mm) prepared by melt-compression-molding the heat-meltable fluoropolymer composite composition at 350° C. was measured at the specimen pressing torque of 70 cN.m and at 23° C. by use of a hot desk method thermal property determination device (Model TPA-501) available from Kyoto Denshi Kogyou Co., Ltd. It should be noted that the measurement of thermal conductivity was performed only for a heat-meltable fluoropolymer composite composition containing graphite.
  • a specimen 12 mm ⁇ 45 mm ⁇ 1.5 mm was prepared from a sample prepared by melt-compression-molding the heat-meltable fluoropolymer composite composition at 350° C. was measured by the torsion mode at 1 Hz and the temperature rise rate of 5° C./min by use of a ARES dynamic viscoelasticity measuring device available from Rheometric Scientific.
  • the agglomerated PFA particles were caused to come up and float on the aqueous polymerization medium by agitating the dispersion at 450 rpm for 20 min so that the PFA particles were separated from the aqueous polymerization medium.
  • the aqueous polymerization medium was discharged from the agitation tank, and water was put in the agitation tank to wash the PFA particles.
  • the PFA particles were dried at 160° C. for 24 hours, and as a result, PFA fine powder.
  • the average particle size of the PFA fine powder thus obtained was 3 ⁇ m.
  • FIG. 1 shows an electron microscopic picture (magnifying power: 10,000 times) of the powder mixed composition thus obtained. Furthermore, the powder mixed composition was melted and mixed at 350° C.
  • a heat-meltable fluoropolymer composite composition was obtained by the same method as described in Example 1 except that 80% by weight of PFA fine powder and 20% by weight of synthetic graphite were used. The nitrogen gas permeability and thermal conductivity of the heat-meltable fluoropolymer composite composition thus obtained were measured. Measurement results are shown in Table 1.
  • Heat-meltable fluoropolymer composite compositions were obtained by the same method as described in Example 1 except that 90, 85 or 80% by weight of PFA fine powder and 10, 15 or 20% by weight of pure natural graphite (available from SEC Co., Ltd.; SNO-3; average particle size: 3 ⁇ m) as the layered-compound in place of synthetic graphite were used.
  • the nitrogen gas permeability and thermal conductivity of the heat-meltable fluoropolymer composite compositions thus obtained were measured. Measurement results are shown in Table 1.
  • An organized synthetic fluorine mica in which the ion exchange amount of the synthetic fluorine mica was 80 meq per 100 g was obtained by using a synthetic fluorine mica (available from COOP Chemical; Somasif ME-100; average particle size: 4.6 ⁇ m) as the layered clay compound and using tetraphenylsulphonium ions on the basis of Japanese Patent Publication 2003-238819.
  • the temperature of the synthetic fluorine mica using tetraphenylsulphonium ions at which it began to decompose thermally was approximately 450° C. (air: 90 cc/min; temperature rise rate: 10° C./min).
  • FIG. 2 shows an electron microscopic picture (magnifying power: 10,000 times) of the powder mixed composition thus obtained. Furthermore, the powder mixed composition was melted and mixed at 350° C.
  • Heat-meltable fluoropolymer composite compositions were obtained by the same method as described in Example 6 except that 5 or 10% by weight of the synthetic fluorine mica organized with phosphonium ions and 95 or 90% by weight of the PFA fine powder were used.
  • the nitrogen gas permeability and storage modulus of the heat-meltable fluoropolymer composite composition thus obtained were measured. Measurement results are shown in Table 2.
  • a heat-meltable fluoropolymer powder composition was obtained by charging 75% by weight of the PFA fine powder obtained by the same method as described in Example 1, 20% by weight of a functional group-containing PFA fine powder, which is a ternary copolymer of tetrafluoroethylene, perfluoro(propylvinylether) (PPVE) and CF 2 ⁇ CF[OCF 2 CF(CF 3 )]OCF 2 CF 2 CH 2 OH(PPVE content: 3.7% by weight; aforesaid hydroxyl-group-containing monomer content: 1.0% by weight; melt flow rate: 15 g/10 min), and 5% by weight of the synthetic fluorine mica organically modified with phosphonium ions which was obtained by the same method as described in Example 6 to a high-speed rotary mixer (a cutter mixer available from Aikosha Seisakusho Co., Ltd.; AC-200S) and melting and mixing them at 3,600 rpm (circumferential velocity: 75.3 m/sec)
  • the powder composition thus obtained was melted and mixed at 350° C. and 50 rpm in a melting and mixing twin-screw extruder (available from Toyo Seiki Seisakusho Co., Ltd.; Laboplastomill 30C150).
  • a melting and mixing twin-screw extruder available from Toyo Seiki Seisakusho Co., Ltd.; Laboplastomill 30C150.
  • the nitrogen gas permeability and storage modulus of the heat-meltable fluoropolymer composite composition thus obtained were measured. Measurement results are shown in Table 2.
  • the heat-meltable fluoropolymer composite composition of the present invention which was obtained by further melting and mixing the powder mixed composition exhibits higher thermal conductivity and storage modulus and lower nitrogen gas permeability than the case of 100% heat-meltable fluoropolymer fine powder (Comparative Example 1). Furthermore, the heat-meltable fluoropolymer composite composition of the present invention (Examples 1 and 4) shows higher thermal conductivity and storage modulus and lower nitrogen gas permeability than the mixture using PFA pellets of the same composition (Comparative Example 2).
  • the synthetic fluorine mica is completely covered with primary PFA particles 0.2 ⁇ m in average particle size. Consequently, with the present invention, it is possible to disperse a layered-compound such as mica uniformly in the PFA powder at the stage of the mixing of the powder in a high-speed rotary mixer prior to melting and mixing.
  • the present invention it is possible to shorten overall melting and mixing time in the melting and mixing mixer because cleavage or intercalation is carried out primarily in the melting and mixing mixer after the heat-meltable fluoropolymer fine powder and the organized layered-compound are ground and mixed uniformly in advance by use of a high-speed rotary mixer, with the result that the time for dispersing the layered-compound in the melted resin becomes shorter.
  • thermo stability if a resin whose melt molding temperature is high such as the heat-meltable fluoropolymer is used, it is possible by shortening overall melting and mixing time to prevent the decomposition or deterioration of the heat-meltable fluoropolymer containing a functional group which is lower in thermal stability than the organically modified layered-compound or the heat-meltable fluoropolymer.
  • the heat-meltable fluoropolymer composite composition of the present invention obtained by further melting and mixing the powder mixed composition exhibits lower nitrogen gas permeability and higher storage modulus and lower nitrogen gas permeability than the case of 100% heat-meltable fluoropolymer fine powder (Comparative Example 1).
  • the heat-meltable fluoropolymer composite composition using the heat-meltable fluoropolymer containing a functional group in place of part of the heat-meltable fluoropolymer shows lower nitrogen gas permeability and higher storage modulus than the case of the heat-meltable fluoropolymer composite composition not containing the heat-meltable fluoropolymer containing a functional group (Example 7).
  • a layered-compound organically modified with tetraphenylphosphonium ions is used as the layered-compound, it is possible to obtain a composite composition showing low nitrogen gas permeability and high storage modulus without going through the grinding and mixing process (Example 10).
  • the heat-meltable fluoropolymer composite composition of the present invention is useful for use as a molding material for heat-exchanger tubes in acid and alkali tanks requiring chemical resistance and high thermal conductivity and transfer facilities and storage containers used in the semiconductor manufacturing process and various chemical processes and as a lining material for piping and tanks.
  • it is also useful for use in molded articles requiring high elastic modulus or mechanical strength because high load is applied to them.
  • the present invention when a layered-compound organically modified with tetraphenylphosphonium ions is used as the layered-compound, it is possible to obtain a heat-meltable fluoropolymer composite composition having excellent thermal conductivity or dynamic properties such as gas and chemical liquid barrier properties and storage modulus only by melting and mixing the heat-meltable fluoropolymer fine powder and the layered-compound.
  • a heat-meltable fluoropolymer composite composition having excellent thermal conductivity or dynamic properties such as gas and chemical liquid barrier properties and storage modulus by grinding and mixing the heat-meltable fluoropolymer fine powder and the layered-compound in advance by use of a high-speed rotary mixer or the like to disperse the layered-compound in the heat-meltable fluoropolymer fine powder and then by melting and mixing such mixture by use of a melt compounding extruder so that the layered-compound is further dispersed, exfoliated and exfoliated in the heat-meltable fluoropolymer fine powder.
  • Kinds of molded articles finally molded from the heat-meltable fluoropolymer composite composition of the present invention are not particularly limited but include those molded articles requiring higher thermal deformation temperature, high storage modulus or flexural modulus, such as tubes, sheets, rods, fibers, packings and linings, for example.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Processes Of Treating Macromolecular Substances (AREA)
US10/546,006 2003-02-19 2004-02-19 Fluororesin composite compositions Abandoned US20060173100A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/580,823 US8618203B2 (en) 2003-02-19 2009-10-16 Fluoropolymer composite composition

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2003040853 2003-02-19
JP2003-040853 2003-02-19
PCT/JP2004/001868 WO2004074371A1 (ja) 2003-02-19 2004-02-19 フッ素樹脂複合体組成物

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US12/580,823 Division US8618203B2 (en) 2003-02-19 2009-10-16 Fluoropolymer composite composition

Publications (1)

Publication Number Publication Date
US20060173100A1 true US20060173100A1 (en) 2006-08-03

Family

ID=32905269

Family Applications (2)

Application Number Title Priority Date Filing Date
US10/546,006 Abandoned US20060173100A1 (en) 2003-02-19 2004-02-19 Fluororesin composite compositions
US12/580,823 Expired - Fee Related US8618203B2 (en) 2003-02-19 2009-10-16 Fluoropolymer composite composition

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/580,823 Expired - Fee Related US8618203B2 (en) 2003-02-19 2009-10-16 Fluoropolymer composite composition

Country Status (8)

Country Link
US (2) US20060173100A1 (ko)
EP (2) EP1598396B1 (ko)
JP (2) JP4884770B2 (ko)
KR (2) KR100991167B1 (ko)
CN (2) CN101081917B (ko)
AT (2) ATE467659T1 (ko)
DE (1) DE602004027117D1 (ko)
WO (1) WO2004074371A1 (ko)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130184401A1 (en) * 2010-09-30 2013-07-18 Daikin Industries, Ltd. Method for manufacturing fine polytetrafluoroethylene powder
US9309335B2 (en) 2010-09-30 2016-04-12 Daikin Industries, Ltd. Process for producing polytetrafluoroethylene fine powder
US9458316B2 (en) 2010-09-30 2016-10-04 Daikin Industries, Ltd. Dripping inhibitor and resin compound
US9944817B2 (en) 2012-03-26 2018-04-17 Daikin Industries, Ltd. Composite particles, coating powder, coating film, laminate, and method for producing composite particles

Families Citing this family (36)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7691932B2 (en) 2004-09-27 2010-04-06 3M Innovative Properties Company Method of making a composition and nanocomposites therefrom
US7329702B2 (en) 2004-09-27 2008-02-12 3M Innovative Properties Company Composition and method of making the same
US8193270B2 (en) 2004-12-14 2012-06-05 3M Innovative Properties Company Method of making composites and nanocomposites
JP2006321850A (ja) * 2005-05-17 2006-11-30 Du Pont Mitsui Fluorochem Co Ltd フッ素樹脂製摺動部材
JP4530972B2 (ja) * 2005-11-08 2010-08-25 三井・デュポンフロロケミカル株式会社 射出成形用テトラフルオロエチレン共重合体組成物
JP5014692B2 (ja) * 2006-07-07 2012-08-29 日本バルカー工業株式会社 充填材入りフッ素樹脂シートの製造方法および充填材入りフッ素樹脂シート
US20080081182A1 (en) 2006-10-02 2008-04-03 Pham Hoai Nam Fluoropolymer blends with inorganic layered compounds
CN102558720A (zh) * 2010-12-07 2012-07-11 华东理工大学 高导热氟塑料及其制备方法和应用
US9283072B2 (en) 2012-07-25 2016-03-15 W. L. Gore & Associates, Inc. Everting transcatheter valve and methods
US10376360B2 (en) * 2012-07-27 2019-08-13 W. L. Gore & Associates, Inc. Multi-frame prosthetic valve apparatus and methods
US9144492B2 (en) 2012-12-19 2015-09-29 W. L. Gore & Associates, Inc. Truncated leaflet for prosthetic heart valves, preformed valve
US9398952B2 (en) 2012-12-19 2016-07-26 W. L. Gore & Associates, Inc. Planar zone in prosthetic heart valve leaflet
US9968443B2 (en) 2012-12-19 2018-05-15 W. L. Gore & Associates, Inc. Vertical coaptation zone in a planar portion of prosthetic heart valve leaflet
US9101469B2 (en) 2012-12-19 2015-08-11 W. L. Gore & Associates, Inc. Prosthetic heart valve with leaflet shelving
US10321986B2 (en) 2012-12-19 2019-06-18 W. L. Gore & Associates, Inc. Multi-frame prosthetic heart valve
US9737398B2 (en) 2012-12-19 2017-08-22 W. L. Gore & Associates, Inc. Prosthetic valves, frames and leaflets and methods thereof
US10966820B2 (en) * 2012-12-19 2021-04-06 W. L. Gore & Associates, Inc. Geometric control of bending character in prosthetic heart valve leaflets
US10039638B2 (en) 2012-12-19 2018-08-07 W. L. Gore & Associates, Inc. Geometric prosthetic heart valves
WO2014104292A1 (ja) * 2012-12-31 2014-07-03 株式会社Ｐａｔ フッ素樹脂シートとその製造方法
CN106659567B (zh) 2014-08-18 2019-06-14 W.L.戈尔及同仁股份有限公司 带有用于假体瓣膜的一体缝合封套的框架
US9827094B2 (en) 2014-09-15 2017-11-28 W. L. Gore & Associates, Inc. Prosthetic heart valve with retention elements
EP3636711B1 (en) * 2017-06-06 2022-08-31 Tokyo Institute of Technology Fluoroelastomer composition and molded article thereof
JP6915429B2 (ja) * 2017-07-28 2021-08-04 Ａｇｃ株式会社 フッ素樹脂ペレットおよびその製造方法、ならびに電線の製造方法
CN111182856B (zh) 2017-09-12 2022-04-29 W.L.戈尔及同仁股份有限公司 用于假体瓣膜的瓣叶框架附连件
JP7068444B2 (ja) 2017-09-27 2022-05-16 ダブリュ．エル．ゴア アンド アソシエイツ，インコーポレイティド 拡張可能なフレームを備えた人工弁、並びに関連するシステム及び方法
CA3155761A1 (en) 2017-09-27 2019-04-04 W.L. Gore & Associates, Inc. Prosthetic valves with mechanically coupled leaflets
CN116725739A (zh) 2017-10-13 2023-09-12 爱德华兹生命科学公司 叠套式假体瓣膜及递送系统
WO2019089138A1 (en) 2017-10-31 2019-05-09 W. L. Gore & Associates, Inc. Prosthetic heart valve
US11154397B2 (en) 2017-10-31 2021-10-26 W. L. Gore & Associates, Inc. Jacket for surgical heart valve
CN111295158A (zh) 2017-10-31 2020-06-16 W.L.戈尔及同仁股份有限公司 医用瓣膜和促进组织向内生长的瓣叶
CA3078473C (en) 2017-10-31 2023-03-14 W. L. Gore & Associates, Inc. Transcatheter deployment systems and associated methods
FR3076832B1 (fr) * 2018-01-15 2019-12-06 Arkema France Poudre de polymere fluore a fenetre de frittage elargie par traitement thermique et son utilisation dans le frittage laser
USD926322S1 (en) 2018-11-07 2021-07-27 W. L. Gore & Associates, Inc. Heart valve cover
US11497601B2 (en) 2019-03-01 2022-11-15 W. L. Gore & Associates, Inc. Telescoping prosthetic valve with retention element
US20240110051A1 (en) 2021-01-11 2024-04-04 Solvay Specialty Polymers Italy S.P.A. Fluoropolymer composition
JP2023007079A (ja) * 2021-07-01 2023-01-18 株式会社タムロン レンズユニット及び車載カメラ

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5962553A (en) * 1996-09-03 1999-10-05 Raychem Corporation Organoclay-polymer composites
US6057035A (en) * 1997-06-06 2000-05-02 Triton Systems, Inc. High-temperature polymer/inorganic nanocomposites
US20020107320A1 (en) * 2000-12-05 2002-08-08 Asahi Glass Company, Limited Polytetrafluoroethylene agglomerated product and its molded product
US20020168569A1 (en) * 2001-03-19 2002-11-14 Atofina Lithium-ion battery elements manufactured from a microcomposite powder based on a filler and on a fluoropolymer
US20030228463A1 (en) * 2002-06-04 2003-12-11 Abusleme Julio A. Fluoropolymer compositions and inorganic nanometric particles
US6841211B1 (en) * 2000-05-12 2005-01-11 Pechiney Emballage Flexible Europe Containers having improved barrier and mechanical properties

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1236246A (en) 1981-09-09 1988-05-03 Raychem Corporation Electrically conductive polyvinylidene fluoride compositions
JPS5891772A (ja) * 1981-11-28 1983-05-31 Daikin Ind Ltd フツ素樹脂被覆用組成物
JPS5925833A (ja) * 1982-08-04 1984-02-09 Du Pont Mitsui Fluorochem Co Ltd 溶融加工性含フツ素樹脂成形用組成物
JPS6169853A (ja) * 1984-09-14 1986-04-10 Fuji Electric Co Ltd 導電性樹脂組成物
JPH0210226A (ja) 1988-06-29 1990-01-16 Teraoka Seiko Co Ltd 組合せ秤装置
US5320789A (en) 1991-11-06 1994-06-14 Japan Atomic Energy Research Institute Surface modification of fluorine resin with laser light
JPH0747644A (ja) 1993-08-05 1995-02-21 Toray Ind Inc 被覆塩化ビニール系樹脂シートの接合シート及びその接合方法
JP3355716B2 (ja) 1993-09-01 2002-12-09 住友化学工業株式会社 疎水性樹脂組成物の製造方法
JPH07252365A (ja) * 1994-03-15 1995-10-03 Nok Corp フッ素樹脂成形材料の製造法
US5552199A (en) 1994-09-02 1996-09-03 Minnesota Mining And Manufacturing Company Melt-processable electroconductive fluoroplastic
JP3940820B2 (ja) 1995-10-27 2007-07-04 ダイキン工業株式会社 樹脂組成物およびそれを用いた成形品とその製法
DE19542721A1 (de) 1995-11-16 1997-05-22 Sgl Technik Gmbh Verfahren zur Herstellen von Formkörpern aus Kunststoff-Füllstoff-Mischungen mit einem hohen Gehalt an Füllstoffen
WO1999007781A1 (en) * 1997-08-07 1999-02-18 E.I. Du Pont De Nemours And Company Fluoropolymer articles having improved impermeability to fluids
DE19839651B4 (de) 1998-09-01 2006-02-23 Polytetra Gmbh Chemisch weitgehend resistente, schlauchförmige Ummantelung für einen Heizkörper einer elektrischen Heizvorrichtung
JP4175710B2 (ja) 1998-12-25 2008-11-05 三井・デュポンフロロケミカル株式会社 多層積層体
JP2000204214A (ja) * 1999-01-13 2000-07-25 Toyota Central Res & Dev Lab Inc 高分子複合材料
FR2817076A1 (fr) 2000-11-20 2002-05-24 Atofina Poudre microcomposite a base d'un electroconducteur et d'un fluoropolymere et objets fabriques avec cette poudre
JP3908004B2 (ja) 2001-01-17 2007-04-25 三井・デュポンフロロケミカル株式会社 熱溶融性フッ素樹脂粉末組成物の製造方法
JP2002346308A (ja) * 2001-03-19 2002-12-03 Mitsubishi Plastics Ind Ltd フィルタープレス用ダイアフラム
US6689835B2 (en) 2001-04-27 2004-02-10 General Electric Company Conductive plastic compositions and method of manufacture thereof
JP4133035B2 (ja) 2001-07-02 2008-08-13 三井・デュポンフロロケミカル株式会社 導電性フッ素樹脂組成物及びその製法
JP2003238819A (ja) 2002-02-15 2003-08-27 Co-Op Chem Co Ltd 耐熱性フィラー
JP2003277610A (ja) * 2002-03-22 2003-10-02 Mitsui Chemicals Inc 熱可塑性芳香族ポリスルホン樹脂組成物

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5962553A (en) * 1996-09-03 1999-10-05 Raychem Corporation Organoclay-polymer composites
US6057035A (en) * 1997-06-06 2000-05-02 Triton Systems, Inc. High-temperature polymer/inorganic nanocomposites
US6841211B1 (en) * 2000-05-12 2005-01-11 Pechiney Emballage Flexible Europe Containers having improved barrier and mechanical properties
US20020107320A1 (en) * 2000-12-05 2002-08-08 Asahi Glass Company, Limited Polytetrafluoroethylene agglomerated product and its molded product
US20020168569A1 (en) * 2001-03-19 2002-11-14 Atofina Lithium-ion battery elements manufactured from a microcomposite powder based on a filler and on a fluoropolymer
US20030228463A1 (en) * 2002-06-04 2003-12-11 Abusleme Julio A. Fluoropolymer compositions and inorganic nanometric particles

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130184401A1 (en) * 2010-09-30 2013-07-18 Daikin Industries, Ltd. Method for manufacturing fine polytetrafluoroethylene powder
US9006333B2 (en) * 2010-09-30 2015-04-14 Daikin Industries, Ltd. Method for manufacturing fine polytetrafluoroethylene powder
US9309335B2 (en) 2010-09-30 2016-04-12 Daikin Industries, Ltd. Process for producing polytetrafluoroethylene fine powder
US9458316B2 (en) 2010-09-30 2016-10-04 Daikin Industries, Ltd. Dripping inhibitor and resin compound
US9475935B2 (en) 2010-09-30 2016-10-25 Daikin Industries, Ltd. Dripping inhibitor and resin compound
US9944817B2 (en) 2012-03-26 2018-04-17 Daikin Industries, Ltd. Composite particles, coating powder, coating film, laminate, and method for producing composite particles

Also Published As

Publication number Publication date
EP2204411A1 (en) 2010-07-07
JP2011074399A (ja) 2011-04-14
EP1598396A4 (en) 2008-10-22
JP4884770B2 (ja) 2012-02-29
CN1774473A (zh) 2006-05-17
KR20050098945A (ko) 2005-10-12
JP5366156B2 (ja) 2013-12-11
EP1598396B1 (en) 2010-05-12
CN101081917B (zh) 2011-06-08
CN100556953C (zh) 2009-11-04
ATE467659T1 (de) 2010-05-15
JPWO2004074371A1 (ja) 2006-06-01
DE602004027117D1 (de) 2010-06-24
CN101081917A (zh) 2007-12-05
KR20090116815A (ko) 2009-11-11
US8618203B2 (en) 2013-12-31
ATE542857T1 (de) 2012-02-15
EP2204411B1 (en) 2012-01-25
US20100036021A1 (en) 2010-02-11
WO2004074371A1 (ja) 2004-09-02
KR100991167B1 (ko) 2010-11-02
EP1598396A1 (en) 2005-11-23

Similar Documents

Publication Publication Date Title
US8618203B2 (en) Fluoropolymer composite composition
CN101309957B (zh) 具有均匀分布的纳米尺寸无机颗粒的聚合物组合物
JP5333723B2 (ja) ゴム組成物
JP2010222582A (ja) ナノチューブの含有量が高いエラストマーの複合材料の製造方法
FR2959231A1 (fr) Materiau composite thermoplastique et/ou elastomerique a base de nanotubes de carbone et de graphenes
JP2007119769A (ja) 樹脂複合体組成物およびその製造方法
CN103459500A (zh) 包含碳纳米管和具有核-壳结构的颗粒的复合材料
WO2006109568A1 (ja) 芳香族ポリカーボネート樹脂組成物及びそれを用いた成形体
US8784961B2 (en) Fluoropolymer blends with inorganic layered compounds
KR20130008524A (ko) 내충격 개질된 열가소성 조성물의 제조를 위한 혼합물의 용도
JP3720164B2 (ja) 膨潤性雲母層間化合物およびそれを含む熱可塑性樹脂組成物
JP2008088305A (ja) パーフルオロフッ素樹脂複合体組成物
JP4843134B2 (ja) 熱可塑性樹脂組成物の製造方法及び熱可塑性樹脂組成物
JP4116462B2 (ja) 樹脂組成物の製造方法、並びにそれにより製造される樹脂組成物よりなるペレット及び射出成形品
JP2008088306A (ja) パーフルオロフッ素樹脂複合体組成物
Naderi Organoclay‐reinforced dynamically vulcanized thermoplastic elastomers of polyamide‐6/polyepichlorohydrin‐co‐ethylene oxide
JP2008115335A (ja) フッ素樹脂複合体組成物からなる透明部材
JP4116461B2 (ja) 樹脂組成物の製造方法および該製造方法による樹脂ペレット
JP2006097005A (ja) 導電性樹脂組成物及びその製造方法
JP2008069335A (ja) 難燃剤組成物およびその製造法、並びにそれから得られる難燃性樹脂組成物
JP2006321850A (ja) フッ素樹脂製摺動部材
KR20110033335A (ko) 퍼플로우르 불소수지 복합체 조성물
JP2001002947A (ja) 難燃樹脂組成物

Legal Events

Date Code Title Description
AS Assignment

Owner name: DU PONT-MITSUI FLUOROCHEMICALS CO. LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:LEE, JEONG CHANG;SUZUKI, NORIYUKI;KONDO, SHOUSAKU;AND OTHERS;REEL/FRAME:017688/0505

Effective date: 20050810

Owner name: E.I. DU PONT DE NEMOURS & COMPANY, DELAWARE

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:LEE, JEONG CHANG;SUZUKI, NORIYUKI;KONDO, SHOUSAKU;AND OTHERS;REEL/FRAME:017688/0505

Effective date: 20050810

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION