US20020182961A1 - Reinforced fabric - Google Patents

Reinforced fabric Download PDF

Info

Publication number
US20020182961A1
US20020182961A1 US10/149,590 US14959002A US2002182961A1 US 20020182961 A1 US20020182961 A1 US 20020182961A1 US 14959002 A US14959002 A US 14959002A US 2002182961 A1 US2002182961 A1 US 2002182961A1
Authority
US
United States
Prior art keywords
fabric
thermoplastic material
fabric according
cords
warp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/149,590
Other languages
English (en)
Inventor
Elsie Clercq
Frans Van Giel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bekaert NV SA
Original Assignee
Bekaert NV SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bekaert NV SA filed Critical Bekaert NV SA
Assigned to N.V. BEKAERT S.A. reassignment N.V. BEKAERT S.A. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DE CLERCQ, ELSIE, VAN GIEL, FRANS
Publication of US20020182961A1 publication Critical patent/US20020182961A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B29C70/10—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres
    • B29C70/16—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of substantial or continuous length
    • B29C70/22—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of substantial or continuous length oriented in at least two directions forming a two dimensional structure
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/26—Non-fibrous reinforcements only
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/88—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced
    • B29C70/882—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced partly or totally electrically conductive, e.g. for EMI shielding
    • B29C70/885—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced partly or totally electrically conductive, e.g. for EMI shielding with incorporated metallic wires, nets, films or plates
    • D—TEXTILES; PAPER
    • D03—WEAVING
    • D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
    • D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
    • D—TEXTILES; PAPER
    • D03—WEAVING
    • D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
    • D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
    • D03D15/20—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads
    • D03D15/242—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads inorganic, e.g. basalt
    • D03D15/25—Metal
    • D—TEXTILES; PAPER
    • D03—WEAVING
    • D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
    • D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
    • D03D15/20—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads
    • D03D15/283—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads synthetic polymer-based, e.g. polyamide or polyester fibres
    • D—TEXTILES; PAPER
    • D03—WEAVING
    • D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
    • D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
    • D03D15/40—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the structure of the yarns or threads
    • D03D15/44—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the structure of the yarns or threads with specific cross-section or surface shape
    • D03D15/46—Flat yarns, e.g. tapes or films
    • D—TEXTILES; PAPER
    • D03—WEAVING
    • D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
    • D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
    • D03D15/60—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the warp or weft elements other than yarns or threads
    • D03D15/67—Metal wires
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04B—KNITTING
    • D04B1/00—Weft knitting processes for the production of fabrics or articles not dependent on the use of particular machines; Fabrics or articles defined by such processes
    • D04B1/14—Other fabrics or articles characterised primarily by the use of particular thread materials
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L11/00—Hoses, i.e. flexible pipes
    • F16L11/04—Hoses, i.e. flexible pipes made of rubber or flexible plastics
    • F16L11/08—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall
    • F16L11/085—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall comprising one or more braided layers
    • F16L11/086—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall comprising one or more braided layers two layers
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L11/00—Hoses, i.e. flexible pipes
    • F16L11/04—Hoses, i.e. flexible pipes made of rubber or flexible plastics
    • F16L11/08—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall
    • F16L11/085—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall comprising one or more braided layers
    • F16L11/087—Hoses, i.e. flexible pipes made of rubber or flexible plastics with reinforcements embedded in the wall comprising one or more braided layers three or more layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
    • B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
    • B29K2105/0809—Fabrics
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2305/00—Use of metals, their alloys or their compounds, as reinforcement
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2101/00—Inorganic fibres
    • D10B2101/20—Metallic fibres
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/02—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins
    • D10B2321/021—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polyethylene
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/02—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins
    • D10B2321/022—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polypropylene
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/04—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polymers of halogenated hydrocarbons
    • D10B2321/041—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polymers of halogenated hydrocarbons polyvinyl chloride or polyvinylidene chloride
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/12—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polymers of cyclic compounds with one carbon-to-carbon double bond in the side chain
    • D10B2321/121—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polymers of cyclic compounds with one carbon-to-carbon double bond in the side chain polystyrene
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/02—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyamides
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/04—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyesters, e.g. polyethylene terephthalate [PET]
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/04—Heat-responsive characteristics
    • D10B2401/041—Heat-responsive characteristics thermoplastic; thermosetting
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/06—Load-responsive characteristics
    • D10B2401/061—Load-responsive characteristics elastic
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2401/00—Physical properties
    • D10B2401/06—Load-responsive characteristics
    • D10B2401/062—Load-responsive characteristics stiff, shape retention
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2505/00—Industrial
    • D10B2505/02—Reinforcing materials; Prepregs
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24273—Structurally defined web or sheet [e.g., overall dimension, etc.] including aperture
    • Y10T428/24322—Composite web or sheet
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24777—Edge feature
    • Y10T428/24785—Edge feature including layer embodying mechanically interengaged strands, strand portions or strand-like strips [e.g., weave, knit, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3033—Including a strip or ribbon
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3049—Including strand precoated with other than free metal or alloy
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3179—Woven fabric is characterized by a particular or differential weave other than fabric in which the strand denier or warp/weft pick count is specified
    • Y10T442/322—Warp differs from weft
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3179—Woven fabric is characterized by a particular or differential weave other than fabric in which the strand denier or warp/weft pick count is specified
    • Y10T442/322—Warp differs from weft
    • Y10T442/3228—Materials differ
    • Y10T442/3236—Including inorganic strand material
    • Y10T442/3252—Including synthetic polymeric strand material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3179—Woven fabric is characterized by a particular or differential weave other than fabric in which the strand denier or warp/weft pick count is specified
    • Y10T442/322—Warp differs from weft
    • Y10T442/3228—Materials differ
    • Y10T442/326—Including synthetic polymeric strand material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3382—Including a free metal or alloy constituent
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3382—Including a free metal or alloy constituent
    • Y10T442/339—Metal or metal-coated strand
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3707—Woven fabric including a nonwoven fabric layer other than paper
    • Y10T442/3715—Nonwoven fabric layer comprises parallel arrays of strand material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/40—Knit fabric [i.e., knit strand or strip material]
    • Y10T442/475—Including a free metal or alloy constituent

Definitions

  • the invention relates to a fabric comprising metal cords and thermoplastic material.
  • thermoplastic article in the form of sheet material, obtained by applying heat and pressure to a laminate comprising an upper sheet of a copolyester material, metallic wire, rods or bars and a lower sheet of a copolyester material.
  • a fabric comprising elongated metal elements and a thermoplastic material is provided. At least part of the elongated metal elements are metal cords.
  • thermoplastic material functions as filling element. After applying heat and/or pressure to the fabric, the thermoplastic material fills the interstices between the metal cords. This means that the thermoplastic material must be present in a sufficient volume to fill these interstices. Therefore, the thermoplastic material is present in a volume of at least 40% of the total volume of the fabric. More preferably, the volume of the thermoplastic material is 50% of the total volume of the fabric. The total volume of the fabric has to be considered as the volume of the metal cords and the volume of the thermoplastic material out of which the fabric is made.
  • thermoplastic material can be considered as filling element.
  • thermoplastic material is meant any thermoplast and any thermoplastic elastomer.
  • thermoplastic materials are: polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET), polyethylene napthalate (PEN), polybuteen terephthalate (PBT) polyvinylchloride (PVC), polyester, polyamide (PA), polyimide (PI), polycarbonate (PC), styrene acrilonitryl (SAN), acrylonitril-butadienestyrene (ABS), thermoplastic polyurethane (TPU), thermoplastic polyolefins (TPO), thermoplastic copolyetheresters, copolymers of these polymers or similar materials.
  • PE polyethylene
  • PP polypropylene
  • PS polystyrene
  • PET polyethylene terephthalate
  • PEN polyethylene napthalate
  • PBT polybuteen terephthalate
  • PVC polyvinylchloride
  • polyester polyester
  • PA polyamide
  • PI polyimide
  • PC polycarbonate
  • the polymer material can be present in the fabric as filaments.
  • the thermoplastic material can be present as coating on the metal cords or on a number of metal cords forming strips.
  • thermoplastic material present as filament and/or as coating amounts to at least 40% of the total volume of the fabric.
  • thermoplastic material can also be applied on the fabric.
  • Suitable filaments are for example polyamide filaments, polyethylene filaments, polypropylene filaments or polyester filaments.
  • a filament has to be understood as an elongated element of a thermoplastic material. It may have various cross-sections, such as circular, oval, rectangular. Strips made from a thermoplastic material are also suitable.
  • Different filaments may be plied together to form filament yarn.
  • a fabric can be understood as a woven, knitted or braided structure.
  • Any metal can be used to provide the elongated metal elements.
  • alloys such as high carbon steel or stainless steel alloys are used.
  • At least part of the elongated metal elements are metal cords, such as steel cords.
  • Multistranded cords are preferred to single stranded cords. Suitable cords are high elongation cords and high impact cords.
  • metal wires can be present in the fabric.
  • the wires may have various cross-sections and geometries, they may for example be circular, oval or flat.
  • the tensile strength of the metal elements is preferably higher than 1500 N/mm 2 .
  • the range of the tensile strength is for example between 1500 N/mm 2 to 3000 N/mm 2 or even more.
  • metal cords having a structural elongation may be desired to use.
  • Preferred metal cords have an elongation of more than 0.3%, for example 1%, compared to the initial length of the metal cord on which a force of at least 10% of the total force at rupture of these elements is applied. The elongation of these metal cords is due to the structural deformation of the metal cords.
  • a first group consists of fabrics comprising metal cords and polymer filaments of a thermoplastic material.
  • the fabric may for example be a woven, braided or knitted structure.
  • Some examples of woven structures are:
  • the warp filaments comprise in turn a metal cord and a polymer filament.
  • the number of metal cords or polymer filaments of the warp and the weft can be varied.
  • a second group of fabrics comprises fabrics made from metal cords coated with a thermoplastic material.
  • the coating of a metal cord can be applied by any conventional means.
  • a possible coating method is extrusion.
  • a coated metal cord has to be understood as an element substantially surrounded by at least one layer of a thermoplastic material.
  • thermoplastic threads or filaments around a metal cord.
  • the metal cords are coated with a number of consecutive layers of a thermoplastic material.
  • the material most closely to the metal surface has an elastic modulus which approaches the modulus of the metal cord, whereas the outer layer of thermoplastic material has a modulus approaching the modulus of the material in which the metal cord or cords is/are embedded.
  • the modulus of these layers changes gradually.
  • the fabric may be a woven, braided or knitted structure.
  • Examples of woven structures are:
  • Fabrics whereby the warp and/or the weft are a combination of metal cords and coated metal cords or a combination of polymer filaments and coated metal cords.
  • a third group comprises fabrics made of strips.
  • a strip comprises two or more metal cords embedded in a matrix of a thermoplastic material.
  • the metal cords are preferably located parallel in the plane of the strip.
  • a possible method of manufacturing such a strip is by coextrusion.
  • thermoplastic material can also be applied on the fabric, either a fabric of group one, two or three.
  • the total amount of the thermoplastic material can be influenced. As described above the total volume of the thermoplastic material present in the fabric is at least 40% of the total volume of the fabric.
  • the amount of thermoplastic material can further be influenced by varying the weaving structure or the inweaving factor, either of the warp or the weft or of both, or by varying the number of filaments or metal cords per length unit of the fabric in warp or weft direction.
  • the inweaving factor is defined as the ratio of the length of filament to the length of the woven structure.
  • the fabrics may further comprise glass fibers, organic fibers such as carbon fibers and/or glass fibers or organic fibers coated with a thermoplastic material.
  • the metal cords can be coated with a metallic coating layer such as zinc or a zinc alloy such as brass.
  • a metallic coating layer such as zinc or a zinc alloy such as brass.
  • Another suitable zinc alloy is an alloy comprising 2 to 10% Al and 0.1 to 0.4% of a rare earth element such as La and/or Ce.
  • an adhesion promoter can be applied on the metal cord.
  • Possible adhesion promoters are bifunctional coupling agents such as silane compounds.
  • One functional group of these coupling agents is responsible for the binding with the metal or metal oxides; the other functional group reacts with the polymer.
  • adhesion promoters are aluminates, zirconates or titanates.
  • a fabric comprising the metal cords and the thermoplastic material is subjected to a temperature and/or pressure sufficient to cause the polymeric material to flow and fill the interstices between the metal filaments. This can be done in one step or may require subsequent steps.
  • a layered structure comprising a number of fabrics according to the invention brought into contact with each other, is subjected to a heat and/or pressure treatment.
  • the fabric or layered structure is heated till a temperature that allows the thermoplastic material to soften and to flow out.
  • the temperature remains thereby lower than the melting point of the metal cords.
  • the heat and/or pressure can for example be applied by feeding the fabric through pressure rollers.
  • the metal cords have a high thermal and electric conductivity, the metal cords themselves can also be used to heat and soften the thermoplastic material. The latter way of heating can be considered as very efficient since it decreases the time to soften the thermoplastic material.
  • the thermoplastic material After applying heat and/or pressure to the fabric or to the layered structure, the thermoplastic material has preferably filled the interstices between the metal cords and most preferably the metal cords are completely embedded in the thermoplastic material.
  • a fabric according to this invention has the advantage that it can be flexed or bent to shape. This can for example be realised by placing a fabric or possibly a layered structure comprising a number of fabrics, in a press, possibly in a heated press.
  • a shaped reinforced article can be manufactured in two successive steps.
  • a reinforced sheet can be obtained by applying heat and/or pressure to a fabric according to the invention and in a second step, this reinforced sheet can be deformed to obtain a reinforced article.
  • Possible forming processes are press forming, flow moulding, thermofolding and membrane forming.
  • a fabric or a reinforced sheet is heated to processing temperature and stamped to shape in a two-part-tool under pressure.
  • a fabric or a reinforced sheet is heated to processing temperature, placed in a two-part-tool and then under pressure the mould cavity is filled by polymer matrix flowing into every recess of the mould.
  • thermofolding operation a fabric or a reinforced sheet is heated locally and folded.
  • an autoclave pressure is used to drape the preheated fabric or reinforced sheet over a tool.
  • the reinforced article can further be embedded in a matrix of thermoplastic material either before or after the forming process.
  • a possible method to realise this is by bringing the fabric into contact with a thermoplastic sheet either at one side or at the upper side and at the lower side of the fabric. In this way a laminated structure is formed.
  • the thermoplastic sheets are bonded to the fabric for example by pressing the laminated structure through heated rollers.
  • FIGS. 1 to 5 shows different embodiments of fabrics comprising metal cords and filaments of a thermoplastic material
  • FIG. 6 shows a coated metal cord
  • FIG. 7 is an illustration of a woven fabric comprising coated metal cords
  • FIG. 8 shows a strip, comprising a number of elongated metal members embedded in a matrix of a thermoplastic material.
  • FIG. 9 illustrates a woven fabric comprising strips.
  • FIGS. 1 to 5 are illustrations of fabrics according to the first group of fabrics, comprising metal cords and polymer filaments of a thermoplastic material.
  • FIG. 1 a shows a woven fabric 10 .
  • Metal cords 12 form the warp
  • polymer filaments 14 such as polyamide filaments form the weft.
  • the metal cords are for example steel cords of the type 7 ⁇ 7 ⁇ 0.15.
  • the total volume of the polymer amounts to 50% of the total volume of the fabric.
  • FIG. 1 b shows the cross-section of a woven fabric 10 .
  • FIGS. 2 and 3 shows two embodiments of woven fabrics 20 and 30 , whereby the weft comprises steel cords 22 and 32 , and the warp comprises polyamide filaments 24 and 34 .
  • the steel cords are of the type 7 ⁇ 3 ⁇ 0.15.
  • the number of polymer filaments can be increased in order to increase the total amount of polymer present in the fabric.
  • the metal cords forming the warp are widely spaced and are crisscrossed by a bundle or a group 36 of polymer filaments 34 .
  • the polymer filaments could thereby be interlaced.
  • FIG. 4 shows a woven structure 40 whereby the warp and the weft filaments are a combination of metal cords and polymer filaments.
  • the warp and the weft filaments comprise in turn a steel filament 42 and a polymer filament 44 .
  • FIG. 5 illustrates a knitted structure 50 .
  • Polymer filaments 52 and cords 54 are knitted together.
  • thermoplastic material can be applied on the fabric.
  • FIG. 6 shows a steel cord 64 on which a coating of a thermoplastic material 66 is applied.
  • FIG. 7 is an embodiment of the second group of fabrics. Both the warp and the weft of the woven fabric 70 comprise coextruded steel cords 72 .
  • FIG. 8 shows a strip 80 , comprising a number of elongated metal cords 82 , embedded in a matrix of a thermoplastic material 84 .
  • FIG. 9 is an illustration of embodiments of the third group of fabrics. It shows a woven structure 90 comprising coextruded steel strips 92 .
  • the adhesion between the metal cord and the thermoplastic material could be determined by performing a pull-out test.
  • thermoplastic materials considered in the test are polyamide (PA), polycarbonate (PC), polyethylene terephthalate (PET), polyethylene (PE), polypropylene (PP) and thermoplastic polyurethane.
  • the adhesion to the thermoplastic material can further be improved.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • General Engineering & Computer Science (AREA)
  • Composite Materials (AREA)
  • Inorganic Chemistry (AREA)
  • Woven Fabrics (AREA)
  • Laminated Bodies (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
  • Blow-Moulding Or Thermoforming Of Plastics Or The Like (AREA)
  • Knitting Of Fabric (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Rigid Pipes And Flexible Pipes (AREA)
  • Moulding By Coating Moulds (AREA)
  • Reinforced Plastic Materials (AREA)
  • Prostheses (AREA)
  • Materials For Medical Uses (AREA)
  • Polishing Bodies And Polishing Tools (AREA)
  • Ceramic Products (AREA)
US10/149,590 1999-12-15 2000-12-13 Reinforced fabric Abandoned US20020182961A1 (en)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
EP99204338 1999-12-15
EP99204339 1999-12-15
EP99204338.0 1999-12-15
EP99204340.6 1999-12-15
EP99204340 1999-12-15
EP99204339.8 1999-12-15

Publications (1)

Publication Number Publication Date
US20020182961A1 true US20020182961A1 (en) 2002-12-05

Family

ID=27240152

Family Applications (4)

Application Number Title Priority Date Filing Date
US10/149,590 Abandoned US20020182961A1 (en) 1999-12-15 2000-12-13 Reinforced fabric
US10/149,120 Expired - Lifetime US6787491B2 (en) 1999-12-15 2000-12-13 Woven composite fabric
US10/149,596 Abandoned US20030022579A1 (en) 1999-12-15 2000-12-13 Reinforcing structure for stiff composite articles
US10/797,031 Expired - Fee Related US7304007B2 (en) 1999-12-15 2004-03-11 Woven composite fabric

Family Applications After (3)

Application Number Title Priority Date Filing Date
US10/149,120 Expired - Lifetime US6787491B2 (en) 1999-12-15 2000-12-13 Woven composite fabric
US10/149,596 Abandoned US20030022579A1 (en) 1999-12-15 2000-12-13 Reinforcing structure for stiff composite articles
US10/797,031 Expired - Fee Related US7304007B2 (en) 1999-12-15 2004-03-11 Woven composite fabric

Country Status (9)

Country Link
US (4) US20020182961A1 (fr)
EP (4) EP1237711B1 (fr)
JP (4) JP4880157B2 (fr)
AT (4) ATE291530T1 (fr)
AU (4) AU3012201A (fr)
DE (4) DE60007662T2 (fr)
DK (2) DK1238128T3 (fr)
ES (4) ES2214343T3 (fr)
WO (4) WO2001043951A1 (fr)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030184099A1 (en) * 2002-03-08 2003-10-02 N.V. Bekaert S.A. Reinforced impact beam
US20050082852A1 (en) * 2002-03-08 2005-04-21 N.V. Bekaert S.A. Polynorm N.V. Reinforced impact beam
WO2005103545A1 (fr) * 2004-04-26 2005-11-03 Nv Bekaert Sa Tube renforce d'une bande de cable metallique et polymere
US20060013990A1 (en) * 2004-06-04 2006-01-19 N.V. Bekaert S.A. Textile product comprising metal cords and non-metallic fibers, and a semifinished sheet comprising such textile product
FR2881371A1 (fr) * 2005-01-31 2006-08-04 Faurecia Sieges Automobile Procede de fabrication d'une piece en matiere composite par moulage
US20100147143A1 (en) * 2003-11-03 2010-06-17 Nv Bekaert Sa Stab resistant insert with steel cords and non-woven textile
US20140030948A1 (en) * 2012-07-24 2014-01-30 Liquidmetal Coatings Llc Fiber-containing composites
US20140045400A1 (en) * 2011-04-26 2014-02-13 Nv Bekaert Sa Steel fiber reinforced composites
US20140099498A1 (en) * 2012-10-04 2014-04-10 Magna Steyr Fahrzeugtechnik Ag & Co Kg Carbon composite component
US20140346162A1 (en) * 2012-01-19 2014-11-27 Societe Choletaise De Fabrication Method for the three-dimensional shaping of an object from a flexible cord, a cord for carrying out the method and an object produced in this way
US20150292651A1 (en) * 2012-11-16 2015-10-15 Kongsberg Actuation Systems Ii, Inc. Method of forming a hose assembly
CN112696536A (zh) * 2020-12-31 2021-04-23 四川自强科技有限公司 多金属骨架增强聚乙烯海底输送连续复合管
US20210187788A1 (en) * 2018-05-31 2021-06-24 Lintec Corporation Method of producing carbon-resin composite material, and composite structure for producing carbon-resin composite material
US20220256939A1 (en) * 2021-02-17 2022-08-18 Aspen Medical Products, Llc Customized knitted wearable with reactive material for rigidity
WO2023281180A1 (fr) * 2021-07-06 2023-01-12 Saint-Gobain Performance Plastics France Nappe electroconductrice tridimensionnelle tricotee pour constituer une paroi resistant a la foudre
US11964061B2 (en) 2021-02-17 2024-04-23 Aspen Medical Products, Llc Method of producing a custom orthosis for a patient
WO2024127267A1 (fr) * 2022-12-14 2024-06-20 Anglo American Technical & Sustainability Services Ltd Support de matériau léger

Families Citing this family (48)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1237711B1 (fr) * 1999-12-15 2005-03-23 N.V. Bekaert S.A. Structure de renfort pour articles composites
EP1760380A1 (fr) * 2000-02-17 2007-03-07 Keith Dixon-Roche Renfort pour tuyaux
US7288494B2 (en) * 2001-07-27 2007-10-30 3M Innovative Properties Company Electro-magnetic wave shield cover
DE10152943C2 (de) * 2001-10-26 2003-12-24 Langendorf Textil Gmbh & Co Kg Textiles Flächengebilde
FR2838502B1 (fr) * 2002-04-12 2004-07-09 Fed Mogul Systems Prot Group Gaine auto-fermable de protection thermique et son procede de fabrication
FR2839322B1 (fr) * 2002-05-06 2004-06-11 Geotechnique Et Travaux Specia Structure de filet formee par tricotage de cables metalliques
US20060082168A1 (en) * 2002-11-28 2006-04-20 N.V. Bekaert S.A. Impact beam comprising elongated metal elements
DE20306671U1 (de) 2003-04-30 2003-07-03 Haver & Boecker, 59302 Oelde Drahtgewebe
DE20311945U1 (de) * 2003-08-02 2004-12-09 Haver & Boecker Plattenförmiges Filterelement
US7877099B2 (en) * 2003-12-31 2011-01-25 Intel Corporation Computing system with off-load processing for networking related tasks
EP1655179A1 (fr) * 2004-11-03 2006-05-10 NV Bekaert SA Procédé pour augmenter la résistance aux chocs d'un amortisseur de chocs
US20090081438A1 (en) * 2005-12-08 2009-03-26 Pol Speleers Stab Resistant Insert for Protective Textile Product
BRPI0711130B1 (pt) * 2006-05-01 2017-03-21 Nippon Sheet Glass Co Ltd método para produzir um cordão de reforço, bem como cordão de reforço e produto contendo um cordão de reforço
JP2009062639A (ja) * 2007-09-05 2009-03-26 Nets 101 Kk 織物と織機
EP2205784A4 (fr) * 2007-11-05 2010-12-01 Ibco Srl Materiau en feuille a surface anti-glissante constitue de bandes et de monofilaments
DE202008007444U1 (de) * 2008-06-04 2009-10-15 Dolmar Gmbh Verbrennungsmotor, insbesondere für handgeführte Arbeitsgeräte
EP2159039A1 (fr) * 2008-08-14 2010-03-03 Lm Glasfiber A/S Procédé de fabrication d'une structure composite comportant un matériau magnétisable
KR20100033457A (ko) * 2008-09-20 2010-03-30 정인선 수지호스
CN101713151A (zh) * 2008-10-06 2010-05-26 E.I.内穆尔杜邦公司 复合增强材料及其制造方法和用途
CN101737571B (zh) * 2008-11-13 2012-06-20 E.I.内穆尔杜邦公司 纤维带增强的热塑性管
JP5238460B2 (ja) * 2008-11-17 2013-07-17 株式会社添島勲商店 織物
JP5542354B2 (ja) * 2009-03-18 2014-07-09 タイガースポリマー株式会社 可撓性補強ホース
SI2411572T1 (sl) * 2009-03-23 2016-06-30 Tessitura Tele Metalliche Rossi Oliviero & C. S.R.L. Polizdelek iz kovinske mreže in postopek za njegovo izdelavo
EP2256722A1 (fr) * 2009-05-29 2010-12-01 Akusik & Innovation GmbH Matériau à isolation acoustique ou absorbant le bruit
WO2011008109A1 (fr) * 2009-07-15 2011-01-20 Jonathan Dallas Toye Matériaux tissé pour recouvrir les sols
EP2357275B8 (fr) * 2010-02-11 2021-03-17 Lautratex B.V. Support tissé pour linge et procédé de fabrication d'un tel support tissé
US20120132309A1 (en) * 2010-11-30 2012-05-31 Morris David D Woven textile fabric and innerduct having multiple-inserted filling yarns
DE102010055834A1 (de) * 2010-12-23 2012-06-28 Waldemar Hoening Ohg Vorratseinrichtung mit einer Trägereinrichtung und einem daran aufgenommenen Werkstoffvorrat
DE102011014244A1 (de) * 2011-03-17 2012-09-20 Daimler Ag Fasereinleger für Kraftfahrzeug-Faserbundkunststoffbauteil und Verfahren zur Herstellung des Kraftfahrzeug-Faserbundkunststoffbauteils
DE102011083160A1 (de) * 2011-09-21 2013-03-21 Leichtbau-Zentrum Sachsen Gmbh Textilverstärkter Faserverbund sowie Verfahren zur zerstörungsfreien Prüfung von Faserorientierung und Lagenaufbau in Bauteilen aus textilverstärkten Verbundwerkstoffen
CN102505274A (zh) * 2011-10-29 2012-06-20 常熟市福嘉丽织造有限公司 具有阻燃功能的面料
US8757213B2 (en) 2011-11-04 2014-06-24 Blue Gentian, Llc Commercial hose
US10174870B2 (en) 2011-11-04 2019-01-08 Telebrands Corp. Expandable and contractible garden hose
MX369693B (es) * 2013-02-22 2019-11-19 Nicolon Corp D/B/A Tencate Geosynthetics Americas Construcciones civiles estabilizadas y reforzadas y metodo para hacer las mismas.
US20160002832A1 (en) * 2013-02-28 2016-01-07 Mitsubishi Gas Chemical Company, Inc. Fiber fabric and molded article obtainable by molding fiber fabric
US10441994B2 (en) * 2014-01-09 2019-10-15 Moshe Ore Protecting net
DE102014001383A1 (de) 2014-02-01 2015-08-06 GM Global Technology Operations, LLC (n.d. Ges. d. Staates Delaware) Verbundwerkstoff
DE102014202393A1 (de) * 2014-02-11 2015-08-13 Robert Bosch Gmbh Verfahren zum Herstellen eines thermoplastischen Kunststoffhalbzeugs zur Abschirmung von elektromagnetischer Strahlung und thermoplastisches Kunststoffhalbzeug zur Abschirmung von elektromagnetischer Strahlung
CN103981624A (zh) * 2014-05-28 2014-08-13 长春高琦聚酰亚胺材料有限公司 一种多功能的超保暖抓绒织物及其制备方法
US9963808B2 (en) * 2014-06-11 2018-05-08 Federal-Mogul Powertrain Llc Knit EMI shield and method of construction thereof
CN104147734A (zh) * 2014-06-11 2014-11-19 浙江恒安消防安全设备有限公司 一种双层带坯的消防水带及其制作方法
JP6234404B2 (ja) 2014-07-28 2017-11-22 石川金網株式会社 金属織物、室内装飾品、仕切り部材、衣類、および電磁波シールド部材
US9802454B2 (en) 2014-07-28 2017-10-31 Tenneco Automotive Operating Company Inc. Plastic spring seat having integrated crash member
US9849746B2 (en) 2014-11-04 2017-12-26 Tenneco Automotive Operating Company Inc. Impact reinforced composite spring seat for a shock absorber
WO2016174257A1 (fr) * 2015-04-30 2016-11-03 Ecp Entwicklungsgesellschaft Mbh Rotor pour pompe à fluide ainsi que procédé et moule pour sa fabrication
JP6720545B2 (ja) * 2016-01-15 2020-07-08 住友電装株式会社 シート材及びシート材製造方法
US9873303B2 (en) 2016-03-22 2018-01-23 Tenneco Automotive Operating Company Inc. Damper having reinforced catcher
JP6681637B1 (ja) * 2018-09-27 2020-04-15 株式会社三宅デザイン事務所 布地及び布製品

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4822665A (en) * 1986-02-21 1989-04-18 Basf Aktiengesellschaft Photopolymerizable molding materials containing metal wire inserts
US5102725A (en) * 1991-04-01 1992-04-07 Jps Converter And Industrial Fabric Corp. Dual layer composite fabric
US5212010A (en) * 1991-05-28 1993-05-18 Ketema, Inc. Stabilizing fabric with weave reinforcement for resin matrices
US5236529A (en) * 1989-05-16 1993-08-17 Aerospatiale Societe Nationale Industrielle Fringed thermal protection device and method of manufacturing it
US5883018A (en) * 1996-02-01 1999-03-16 N.V. Bekaert S.A. Stab-resistant insert for protective textile
US5933605A (en) * 1995-11-10 1999-08-03 Hitachi, Ltd. Apparatus for filtering multicast messages transmitted between subnetworks based upon the message content
US6465377B2 (en) * 1997-06-06 2002-10-15 N.V. Bekaert S.A. Canvass reinforcement

Family Cites Families (36)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AT198914B (de) * 1957-03-09 1958-08-11 Franz Blaha Durch ein Geflecht gebildete Sitz-, Lehnen- oder Liegefläche
FR1290278A (fr) 1961-03-01 1962-04-13 Procédé de fabrication des skis et skis obtenus par ledit procédé
GB957248A (en) 1962-06-13 1964-05-06 Communications Patents Ltd Improvements in or relating to bonding of plastic materials
DE1535823C2 (de) * 1965-12-20 1975-07-17 Gustav Wolf, Seil- und Drahtwerke, 4830 Gütersloh Verstärkungsgewebe für Gummi- und Kunststofferzeugnisse
GB1174292A (en) * 1966-03-14 1969-12-17 Brunswick Corp Composite Materials
US3949129A (en) * 1970-05-28 1976-04-06 Hubbard Albert L Elastomer coated fabric
US3837982A (en) * 1970-09-03 1974-09-24 Goodyear Tire & Rubber Wire woven fabric for pneumatic tires
US3979536A (en) * 1971-07-08 1976-09-07 Uniroyal Inc. Zero degree belted tires, and high "soft stretch" belt-forming tapes therefor
DE2150481B2 (de) * 1971-10-09 1973-08-09 Rehau- Plastiks Gmbh, 8673 Rehau Verfahren zur herstellung eines mit ein gewebe bildenden faeden verstaerkten, dichten flexiblen flaechengebildes
US3930091A (en) 1972-09-13 1975-12-30 Kaiser Glass Fiber Corp Unidirectional webbing material
DE2528189C2 (de) * 1974-07-02 1983-02-10 Kuraray Co., Ltd., Kurashiki, Okayama Gewirktes oder gewebtes Tuch mit antistatischen Eigenschaften
JPS541357A (en) 1977-06-06 1979-01-08 Ohji Rubber & Chem Hardwearing rubber linings
BE859230A (nl) * 1977-09-30 1978-03-30 Bekaert Sa Nv Staalkoordversterking voor rubbervoorwerpen, alsmede aldus versterkte voorwerpen
DE2908985C2 (de) * 1979-03-06 1982-05-19 Gerhard Ebeling Drahtzaunfabrik Ohg, 1000 Berlin Krippgitter
US4345626A (en) * 1979-05-04 1982-08-24 Tolliver Wilbur E Circumferential stirrup panel
JPS5715956A (en) * 1981-05-29 1982-01-27 Meisei Shiyoukai Kk Plastic composite material using textile having conductive property
JPS5933046A (ja) * 1982-08-18 1984-02-22 Mitsubishi Electric Corp 金網及びその製造方法
EP0109505A3 (fr) 1982-10-25 1985-01-09 Allied Corporation Structure polymère composite estampable contenant une couche de blindage contre les interférences électromagnétiques
JPS6285050A (ja) * 1985-10-07 1987-04-18 旭化成株式会社 伸長布帛とその製造方法
EP0228725A1 (fr) * 1985-12-02 1987-07-15 N.V. Bekaert S.A. Tissu pour renforcer la raideur d'une bande élastomère et bande élastomère ainsi obtenue
US5089326A (en) * 1987-05-29 1992-02-18 Phillips Petroleum Company EMI shielded composites and process of making same
JPS6483406A (en) * 1987-09-22 1989-03-29 Yokohama Rubber Co Ltd Pneumatic radial tire
JP2757940B2 (ja) * 1988-03-28 1998-05-25 住友ゴム工業株式会社 空気入りタイヤ
FR2645493A1 (fr) 1989-04-11 1990-10-12 Renault Piece de carrosserie automobile a structure composite notamment capot
US5071699A (en) * 1991-02-07 1991-12-10 Exxon Chemical Patents Inc. Antistatic woven coated polypropylene fabric
US5248548A (en) * 1991-11-22 1993-09-28 Memtec America Corporation Stainless steel yarn and protective garments
FR2684696B1 (fr) * 1991-12-10 1994-03-04 Protecma Procede pour la realisation d'un article tricote a base de fils metalliques et nouveau type de tricot ainsi realise.
FR2708294A1 (fr) * 1993-04-29 1995-02-03 Lamagnere Frederique Composite FIT (fibre imprégnée thermoplastique) et métal (cuivre, inox, laiton).
JPH07308726A (ja) * 1994-05-17 1995-11-28 Shinko Kosen Kogyo Kk 通気性成形体の製造方法
DE4438013A1 (de) * 1994-10-25 1996-05-02 Happich Gmbh Gebr Schutzschicht, insbesondere Vandalismus-Schutzschicht
DE59509754D1 (de) * 1995-08-11 2001-11-29 Alfred Buck Halbzeug für Verbundwerkstoff
US5998028A (en) * 1997-08-26 1999-12-07 Eastman Chemical Company Thermoplastic article having metallic wire, rod or bar embedded therein
AU9524798A (en) 1997-10-22 1999-05-10 N.V. Bekaert S.A. Means and methods for enhancing interfacial adhesion between a metal surface anda non-metallic medium and products obtained thereby
ZA9810315B (en) * 1997-11-27 1999-05-18 Bekaert Sa Nv Steel cord with spatially waved elements
GB2335162A (en) * 1998-03-05 1999-09-15 Southfields Coachworks Ltd A composite material suitable for use as,or as part of a closure for a vehicle body
EP1237711B1 (fr) * 1999-12-15 2005-03-23 N.V. Bekaert S.A. Structure de renfort pour articles composites

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4822665A (en) * 1986-02-21 1989-04-18 Basf Aktiengesellschaft Photopolymerizable molding materials containing metal wire inserts
US5236529A (en) * 1989-05-16 1993-08-17 Aerospatiale Societe Nationale Industrielle Fringed thermal protection device and method of manufacturing it
US5102725A (en) * 1991-04-01 1992-04-07 Jps Converter And Industrial Fabric Corp. Dual layer composite fabric
US5212010A (en) * 1991-05-28 1993-05-18 Ketema, Inc. Stabilizing fabric with weave reinforcement for resin matrices
US5933605A (en) * 1995-11-10 1999-08-03 Hitachi, Ltd. Apparatus for filtering multicast messages transmitted between subnetworks based upon the message content
US5883018A (en) * 1996-02-01 1999-03-16 N.V. Bekaert S.A. Stab-resistant insert for protective textile
US6465377B2 (en) * 1997-06-06 2002-10-15 N.V. Bekaert S.A. Canvass reinforcement

Cited By (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7007990B2 (en) * 2002-03-08 2006-03-07 N.V. Bekaert S.A. Reinforced impact beam with layered matrix
US20050023847A1 (en) * 2002-03-08 2005-02-03 N.V. Bekaert S.A. Reinforced impact beam
US20050082852A1 (en) * 2002-03-08 2005-04-21 N.V. Bekaert S.A. Polynorm N.V. Reinforced impact beam
US6883843B2 (en) * 2002-03-08 2005-04-26 N.V. Bekaert S.A. Reinforced impact beam
US20030184099A1 (en) * 2002-03-08 2003-10-02 N.V. Bekaert S.A. Reinforced impact beam
US20060112560A1 (en) * 2002-03-08 2006-06-01 N.V. Bekaert S.A. Reinforced impact beam with layered matrix
US7111882B2 (en) 2002-03-08 2006-09-26 N. V. Bekaert S.A. Reinforced impact beam with woven fabric
US20100147143A1 (en) * 2003-11-03 2010-06-17 Nv Bekaert Sa Stab resistant insert with steel cords and non-woven textile
WO2005103545A1 (fr) * 2004-04-26 2005-11-03 Nv Bekaert Sa Tube renforce d'une bande de cable metallique et polymere
US20070218230A1 (en) * 2004-04-26 2007-09-20 Erwin Lokere Tube Reinforced With a Polymer and Steel Cord Strip
US20060013990A1 (en) * 2004-06-04 2006-01-19 N.V. Bekaert S.A. Textile product comprising metal cords and non-metallic fibers, and a semifinished sheet comprising such textile product
CN100556672C (zh) * 2004-06-04 2009-11-04 贝卡尔特股份有限公司 包含金属线和非金属纤维的纺织制品以及包含这种纺织制品的半成品板材
FR2881371A1 (fr) * 2005-01-31 2006-08-04 Faurecia Sieges Automobile Procede de fabrication d'une piece en matiere composite par moulage
US20140045400A1 (en) * 2011-04-26 2014-02-13 Nv Bekaert Sa Steel fiber reinforced composites
US9723657B2 (en) * 2012-01-19 2017-08-01 Societe Choletaise De Fabrication Method for the three-dimensional shaping of an object from a flexible cord, a cord for carrying out the method and an object produced in this way
US20140346162A1 (en) * 2012-01-19 2014-11-27 Societe Choletaise De Fabrication Method for the three-dimensional shaping of an object from a flexible cord, a cord for carrying out the method and an object produced in this way
US20140030948A1 (en) * 2012-07-24 2014-01-30 Liquidmetal Coatings Llc Fiber-containing composites
US9493909B2 (en) * 2012-07-24 2016-11-15 Liquidmetal Coatings, Llc Fiber-containing composites
US20140099498A1 (en) * 2012-10-04 2014-04-10 Magna Steyr Fahrzeugtechnik Ag & Co Kg Carbon composite component
US10131112B2 (en) * 2012-10-04 2018-11-20 Magna Steyr Fahrzeugtechnik Ag & Co Kg Carbon composite component
US10228081B2 (en) * 2012-11-16 2019-03-12 Kongsberg Actuation Systems Ii, Inc. Method of forming a hose assembly
US20150300537A1 (en) * 2012-11-16 2015-10-22 Kongsberg Actuation Systems Ii, Inc. Method of forming a hose assembly
US20150292651A1 (en) * 2012-11-16 2015-10-15 Kongsberg Actuation Systems Ii, Inc. Method of forming a hose assembly
US10281064B2 (en) * 2012-11-16 2019-05-07 Kongsberg Actuation Systems Ii, Inc. Method of forming a hose assembly
US20210187788A1 (en) * 2018-05-31 2021-06-24 Lintec Corporation Method of producing carbon-resin composite material, and composite structure for producing carbon-resin composite material
CN112696536A (zh) * 2020-12-31 2021-04-23 四川自强科技有限公司 多金属骨架增强聚乙烯海底输送连续复合管
US20220256939A1 (en) * 2021-02-17 2022-08-18 Aspen Medical Products, Llc Customized knitted wearable with reactive material for rigidity
US11964061B2 (en) 2021-02-17 2024-04-23 Aspen Medical Products, Llc Method of producing a custom orthosis for a patient
WO2023281180A1 (fr) * 2021-07-06 2023-01-12 Saint-Gobain Performance Plastics France Nappe electroconductrice tridimensionnelle tricotee pour constituer une paroi resistant a la foudre
WO2024127267A1 (fr) * 2022-12-14 2024-06-20 Anglo American Technical & Sustainability Services Ltd Support de matériau léger

Also Published As

Publication number Publication date
JP2003517110A (ja) 2003-05-20
ATE257524T1 (de) 2004-01-15
EP1237710B1 (fr) 2004-04-14
DE60024485T2 (de) 2006-08-03
US20030082336A1 (en) 2003-05-01
DE60009951T2 (de) 2005-03-24
US20040176007A1 (en) 2004-09-09
ATE311490T1 (de) 2005-12-15
EP1237711A1 (fr) 2002-09-11
ES2214343T3 (es) 2004-09-16
JP4184664B2 (ja) 2008-11-19
AU2673901A (en) 2001-06-25
EP1238128B1 (fr) 2005-11-30
DE60018969D1 (de) 2005-04-28
DE60018969T2 (de) 2006-03-23
DE60007662D1 (de) 2004-02-12
EP1238128A1 (fr) 2002-09-11
ES2237489T3 (es) 2005-08-01
JP2003517106A (ja) 2003-05-20
DE60024485D1 (de) 2006-01-05
ATE264185T1 (de) 2004-04-15
WO2001043951A1 (fr) 2001-06-21
ATE291530T1 (de) 2005-04-15
JP4880157B2 (ja) 2012-02-22
AU3012201A (en) 2001-06-25
AU2010801A (en) 2001-06-25
EP1237710A1 (fr) 2002-09-11
US7304007B2 (en) 2007-12-04
DK1238128T3 (da) 2006-03-13
WO2001044548A1 (fr) 2001-06-21
AU2673801A (en) 2001-06-25
EP1238129A1 (fr) 2002-09-11
JP2003517105A (ja) 2003-05-20
EP1237711B1 (fr) 2005-03-23
US20030022579A1 (en) 2003-01-30
ES2218274T3 (es) 2004-11-16
JP4323127B2 (ja) 2009-09-02
ES2252082T3 (es) 2006-05-16
DE60007662T2 (de) 2004-11-11
US6787491B2 (en) 2004-09-07
JP4007537B2 (ja) 2007-11-14
JP2003517109A (ja) 2003-05-20
WO2001044549A1 (fr) 2001-06-21
WO2001043952A1 (fr) 2001-06-21
DK1238129T3 (da) 2004-04-05
EP1238129B1 (fr) 2004-01-07
DE60009951D1 (de) 2004-05-19

Similar Documents

Publication Publication Date Title
EP1238128B1 (fr) Tissu renforce
US20040229533A1 (en) Layered structure
EP1342623A1 (fr) Poutre de choc renforcé
US6777081B2 (en) Reinforcing structure for stiff composite articles
CN100403954C (zh) 连接带
US7111882B2 (en) Reinforced impact beam with woven fabric
US3846215A (en) Three dimensional reinforcing coil structure and method of forming same
JP3633221B2 (ja) 一方向性補強織物および補修または補強方法
CN113396050A (zh) 多层片和多层片的制造方法
KR0178130B1 (ko) 긴 성형 스트랜드
KR101068641B1 (ko) 농·산업용 섬유 강화 보온 시트의 제조방법
MXPA99004236A (en) Wire nucleus extrusion with neu axle

Legal Events

Date Code Title Description
AS Assignment

Owner name: N.V. BEKAERT S.A., BELGIUM

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DE CLERCQ, ELSIE;VAN GIEL, FRANS;REEL/FRAME:013320/0623;SIGNING DATES FROM 20020528 TO 20020610

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION