RU2012112869A - Водопоглощающие полимерные частицы - Google Patents

Водопоглощающие полимерные частицы Download PDF

Info

Publication number
RU2012112869A
RU2012112869A RU2012112869/04A RU2012112869A RU2012112869A RU 2012112869 A RU2012112869 A RU 2012112869A RU 2012112869/04 A RU2012112869/04 A RU 2012112869/04A RU 2012112869 A RU2012112869 A RU 2012112869A RU 2012112869 A RU2012112869 A RU 2012112869A
Authority
RU
Russia
Prior art keywords
polymer particles
water
absorbing polymer
polymerization chamber
gas
Prior art date
Application number
RU2012112869/04A
Other languages
English (en)
Other versions
RU2563654C2 (ru
Inventor
Райнер Добрава
Томас ДАНИЭЛЬ
Уве ШТЮВЕН
Марко Крюгер
ВИЛЛАНУЭВА Франциско Хавьер ЛОПЕС
Норберт ХЕРФЕРТ
Карин ФЛОРЕ
Штефан БЛЯЙ
Майкл А. МИТЧЕЛЛ
Original Assignee
Басф Се
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Басф Се filed Critical Басф Се
Publication of RU2012112869A publication Critical patent/RU2012112869A/ru
Application granted granted Critical
Publication of RU2563654C2 publication Critical patent/RU2563654C2/ru

Abstract

1. Способ получения водопоглощающих полимерных частиц путем полимеризации капель раствора мономера, содержащегоa) по меньшей мере один этиленненасыщенный мономер, который имеет кислотные группы и может быть по меньшей мере частично нейтрализован,b) по меньшей мере один сшивающий агент,c) по меньшей мере один инициатор,d) необязательно один или несколько этиленненасыщенных мономеров, которые могут сополимеризоваться с мономерами, указанными в а),e) необязательно один или несколько водорастворимых полимеров, иf) воду,в окружающей нагретой газовой фазе и пропускания спутного потока газа через камеру полимеризации, отличающийся тем, что температура газа, выходящего из камеры полимеризации, составляет 130°С или менее, скорость газа внутри камеры полимеризации составляет по меньшей мере 0,5 м/с, и капли создаются с помощью каплеобразующей пластины, имеющей множество отверстий.2. Способ по п.1, отличающийся тем, что температура газа, выходящего из камеры полимеризации, составляет от 115 до 125°С.3. Способ по любому из пп.1 или 2, отличающийся тем, что скорость газа внутри камеры полимеризации составляет от 0,7 до 0,9 м/с.4. Способ по любому из пп.1 или 2, отличающийся тем, что расстояние между отверстиями составляет от 15 до 30 мм.5. Способ по любому из пп.1 или 2, отличающийся тем, что диаметр отверстий составляет от 150 до 200 мкм.6. Способ по любому из пп.1 или 2, отличающийся тем, что водопоглощающие полимерные частицы подвергаются последующему сшиванию с использованием соединений, которые включают группы, которые могут образовывать по меньшей мере две ковалентные связи с карбоксилатными группами полимерных частиц.7. Способ по любому из пп.1 �

Claims (17)

1. Способ получения водопоглощающих полимерных частиц путем полимеризации капель раствора мономера, содержащего
a) по меньшей мере один этиленненасыщенный мономер, который имеет кислотные группы и может быть по меньшей мере частично нейтрализован,
b) по меньшей мере один сшивающий агент,
c) по меньшей мере один инициатор,
d) необязательно один или несколько этиленненасыщенных мономеров, которые могут сополимеризоваться с мономерами, указанными в а),
e) необязательно один или несколько водорастворимых полимеров, и
f) воду,
в окружающей нагретой газовой фазе и пропускания спутного потока газа через камеру полимеризации, отличающийся тем, что температура газа, выходящего из камеры полимеризации, составляет 130°С или менее, скорость газа внутри камеры полимеризации составляет по меньшей мере 0,5 м/с, и капли создаются с помощью каплеобразующей пластины, имеющей множество отверстий.
2. Способ по п.1, отличающийся тем, что температура газа, выходящего из камеры полимеризации, составляет от 115 до 125°С.
3. Способ по любому из пп.1 или 2, отличающийся тем, что скорость газа внутри камеры полимеризации составляет от 0,7 до 0,9 м/с.
4. Способ по любому из пп.1 или 2, отличающийся тем, что расстояние между отверстиями составляет от 15 до 30 мм.
5. Способ по любому из пп.1 или 2, отличающийся тем, что диаметр отверстий составляет от 150 до 200 мкм.
6. Способ по любому из пп.1 или 2, отличающийся тем, что водопоглощающие полимерные частицы подвергаются последующему сшиванию с использованием соединений, которые включают группы, которые могут образовывать по меньшей мере две ковалентные связи с карбоксилатными группами полимерных частиц.
7. Способ по любому из пп.1 или 2, отличающийся тем, что водопоглощающие полимерные частицы покрываются неорганическими инертными веществами, органическими полимерами, катионными полимерами, поливалентными катионами металлов, восстановителями, антиоксидантами, полиолами, микрокремнеземом и/или поверхностно-активными веществами.
8. Водопоглощающие полимерные частицы, имеющие более одной полости, отличающиеся тем, что внутренний диаметр полостей составляет от 1 до 50 мкм.
9. Водопоглощающие полимерные частицы, получаемые согласно любому из пп.1-7, отличающиеся тем, что полимерные частицы имеют среднюю сферичность от 0,86 до 0,99, насыпную плотность по меньшей мере 0,58 г/см3, и средний диаметр частиц от 250 до 550 мкм, где распределение диаметра частиц составляет менее 0,7, причем отношение частиц, имеющих одну полость, к частицам, имеющим более одной полости, составляет менее 1,0.
10. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что полимерные частицы имеют насыпную плотность от 0,7 до 1 г/см3.
11. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что распределение диаметра частиц составляет менее 0,6.
12. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что в набухшем состоянии внутренний диаметр полостей частиц составляет по меньшей мере 1 мкм.
13. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что полимерные частицы имеют показатель удержания в центрифуге по меньшей мере 30 г/г, поглощение при высокой нагрузке по меньшей мере 20 г/г и проводимость потока солевого раствора по меньшей мере 10·10-7 см3с/г.
14. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что полимерные частицы имеют показатель удержания в центрифуге по меньшей мере 20 г/г, поглощение при высокой нагрузке по меньшей мере 15 г/г и проводимость потока солевого раствора по меньшей мере 80·10-7 см3с/г.
15. Водопоглощающие полимерные частицы по п.8 или 9, отличающиеся тем, что полимерные частицы имеют показатель удержания в центрифуге по меньшей мере 30 г/г, поглощение при высокой нагрузке по меньшей мере 16 г/г и проводимость потока солевого раствора по меньшей мере 20·10-7 см3с/г.
16. Агломерированные водопоглощающие полимерные частицы на основе водопоглощающих полимерных частиц по любому из пп.8-15.
17. Абсорбирующее жидкость изделие, содержащее
(A) верхний проницаемый для жидкости слой,
(B) нижний непроницаемый для жидкости слой и
(C) абсорбирующую жидкость сердцевину между слоем (А) и слоем (В), содержащую от 5 до 90 мас.% волокнистого материала и от 10 до 95 мас.% водопоглощающих полимерных частиц согласно любому из пп.8-14,
(D) необязательный принимающий-распределяющий слой между (А) и (С), содержащий от 80 до 100 мас.% волокнистого материала и от 0 до 20 мас.% водопоглощающих полимерных частиц согласно любому из пп.8-14,
(E) необязательный слой ткани, расположенный непосредственно над и/или под (С); и
(F) другие необязательные компоненты.
RU2012112869/04A 2009-09-04 2010-09-02 Водопоглощающие полимерные частицы RU2563654C2 (ru)