RU2009131696A - Новые композиции бетона - Google Patents

Новые композиции бетона Download PDF

Info

Publication number
RU2009131696A
RU2009131696A RU2009131696/03A RU2009131696A RU2009131696A RU 2009131696 A RU2009131696 A RU 2009131696A RU 2009131696/03 A RU2009131696/03 A RU 2009131696/03A RU 2009131696 A RU2009131696 A RU 2009131696A RU 2009131696 A RU2009131696 A RU 2009131696A
Authority
RU
Russia
Prior art keywords
concrete according
parts
concrete
cement
particle size
Prior art date
Application number
RU2009131696/03A
Other languages
English (en)
Inventor
Жан-Франсуа БАТОЗ (FR)
Жан-Франсуа БАТОЗ
Мулуд БЕХЛУЛ (FR)
Мулуд БЕХЛУЛ
Филипп ФОНОЛЛОЗА (FR)
Филипп ФОНОЛЛОЗА
Original Assignee
Лафарж (Fr)
Лафарж
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Лафарж (Fr), Лафарж filed Critical Лафарж (Fr)
Publication of RU2009131696A publication Critical patent/RU2009131696A/ru

Abstract

1. Бетон, содержащий в относительных весовых частях: ! 100 частей портландцемента; ! от 50 до 200 частей песка единого гранулометрического состава с фракциями D10-D90 в диапазоне от 0,063 до 5 мм или смеси песков, из которых в самом мелком песке фракции D10-D90 имеют размер от 0,063 до 1 мм, а в самом крупном песке фракции D10-D90 имеют размер от 1 до 4 мм; ! от 10 до 50 частей зернистого, по существу, непуццоланового материала со средним размером частиц менее 15 мкм; ! от 0,1 до 10 частей суперпластифицирующей добавки; и ! от 10 до 30 частей воды; ! причем бетон, по существу, свободен от микрокремнезема; ! при этом бетон обладает прочностью при сжатии более 100 МПа на 28 день. ! 2. Бетон по п.1, который дополнительно содержит негашеную известь, обожженную известь или оксид кальция. ! 3. Бетон по п.1 или 2, в котором непуццолановый материал содержит молотый известняк или молотый кварц. ! 4. Бетон по п.1 или 2, который содержит молотый известняк, молотый кварц или осажденный карбонат кальция или их смесь. ! 5. Бетон по п. 1, который содержит органические или металлические волокна. ! 6. Бетон по п.5, который содержит 0,5-3,5 об.% металлических волокон относительно объема схватившегося цемента. ! 7. Бетон по п.5, который содержит 2-5 об.% органических волокон относительно объема схватившегося цемента. ! 8. Бетон по любому из пп.5-7, обладающий прочностью при сжатии более 120 МПа. ! 9. Цементная смесь, содержащая материалы, указанные по п.1, и, необязательно, известняк или обожженный доломит, но исключающая воду и, если она жидкая, суперпластифицирующую добавку. ! 10. Применение зернистого, по существу, непуццоланового материала со средним размером частиц менее 15 мкм в качестве замены микро�

Claims (10)

1. Бетон, содержащий в относительных весовых частях:
100 частей портландцемента;
от 50 до 200 частей песка единого гранулометрического состава с фракциями D10-D90 в диапазоне от 0,063 до 5 мм или смеси песков, из которых в самом мелком песке фракции D10-D90 имеют размер от 0,063 до 1 мм, а в самом крупном песке фракции D10-D90 имеют размер от 1 до 4 мм;
от 10 до 50 частей зернистого, по существу, непуццоланового материала со средним размером частиц менее 15 мкм;
от 0,1 до 10 частей суперпластифицирующей добавки; и
от 10 до 30 частей воды;
причем бетон, по существу, свободен от микрокремнезема;
при этом бетон обладает прочностью при сжатии более 100 МПа на 28 день.
2. Бетон по п.1, который дополнительно содержит негашеную известь, обожженную известь или оксид кальция.
3. Бетон по п.1 или 2, в котором непуццолановый материал содержит молотый известняк или молотый кварц.
4. Бетон по п.1 или 2, который содержит молотый известняк, молотый кварц или осажденный карбонат кальция или их смесь.
5. Бетон по п. 1, который содержит органические или металлические волокна.
6. Бетон по п.5, который содержит 0,5-3,5 об.% металлических волокон относительно объема схватившегося цемента.
7. Бетон по п.5, который содержит 2-5 об.% органических волокон относительно объема схватившегося цемента.
8. Бетон по любому из пп.5-7, обладающий прочностью при сжатии более 120 МПа.
9. Цементная смесь, содержащая материалы, указанные по п.1, и, необязательно, известняк или обожженный доломит, но исключающая воду и, если она жидкая, суперпластифицирующую добавку.
10. Применение зернистого, по существу, непуццоланового материала со средним размером частиц менее 15 мкм в качестве замены микрокремнезема при производстве бетона по п.1.
RU2009131696/03A 2007-01-24 2008-01-23 Новые композиции бетона RU2009131696A (ru)