KR880009867A - 수분흡수도가 약해진 신규 침강 무수규산류, 그들의 제법 및 실리콘 탄성 중합체의 강화를 위한 용도 - Google Patents
수분흡수도가 약해진 신규 침강 무수규산류, 그들의 제법 및 실리콘 탄성 중합체의 강화를 위한 용도 Download PDFInfo
- Publication number
- KR880009867A KR880009867A KR1019880001945A KR880001945A KR880009867A KR 880009867 A KR880009867 A KR 880009867A KR 1019880001945 A KR1019880001945 A KR 1019880001945A KR 880001945 A KR880001945 A KR 880001945A KR 880009867 A KR880009867 A KR 880009867A
- Authority
- KR
- South Korea
- Prior art keywords
- silicic anhydride
- silicic
- ppm
- raw material
- less
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (24)
- 적어도 700℃의 온도에서 적어도 1분동안 원료 침강 무수 규산으로 하여금 열처리를 받게하는 것을 특징으로 하는 수분 흡수도가 약한 무수 규산의 제조방법.
- 제1항에 있어서, 전술한 원료 무수 규산으로 하여금 전술한 열처리 전 또는 후에 미립자화 또는 분쇄를 받게하는 것을 특징으로 하는 방법.
- 제1또는 2항에 있어서, 전기한 원료 무수 규산은 평균 크기가 적어도 80㎛인 거의 구형의 구슬형태를 하고 있음을 특징으로 하는 방법.
- 제3항에 있어서 전술한 원료 무수 규산은 압축상태에서의 밀도가 0.2이상이고 BET표면이 100내지 350m2/g사이에 포함되고, CTAB표면이 100내지 350m2/g사이에 포함됨을 특징으로 하는 방법.
- 제3또는 4항중 어느 한 항에 있어서, 전술한 원료 무수 규산은 미립자의 평균크기가 150㎛이상, 바람직하게는 200내지 300㎛사이에 포함됨을 특징으로 하는 방법.
- 제3, 4 또는 5항중 어느 한 항에 있어서, 전술한 원료 무수 규산은 밀도가 0.23내지 0.32사이에 포함됨을 특징으로 하는 방법.
- 제1 내지 6항중 어느 한 항에 있어서, 구슬 형태의 원료 무수 규산에 대해서 700내지 950℃사이, 더욱 상세히는 800내지 900℃사이 및 700내지 900℃사이에 포함되는 온도에서 열처리가 실시되는 것을 특징으로 하는 방법.
- 제1 내지 7항중 어느 한 항에 있어서, 1내지 15분사이, 바람직하게는 2내지 10분 사이에 포함되는 시간동안 열처리가 실시되는 것을 특징으로 하는 방법.
- 제1 및 3내지 8항중 어느 한 항에 따른 방법에 의해 제조될 수 있는, 하기 특성들을 나타내는 유형의 침강 무수 규산:전술한 무수 규산은 또한 평균 크기가 적어도 80㎛인 거의 구형의 구슬 형태를 나타냄.
- 제9항에 있어서, 미립자의 평균크기가 150㎛이상, 바람직하게는 200내지 300㎛사이에 포함됨을 특징으로 하는 무수 규산.
- 제9또는 10항에 있어서, 수분 함량이 기껏해야 3.5%인 것을 특징으로 하는 무수 규산.
- 제9, 10또는 11항에 있어서, 밀도가 0.23내지 0.32사이에 포함되는 것을 특징으로 하는 무수 규산.
- 제9 내지 12항중 어느 한 항에 있어서, 탄소함량이 2500ppm이하, 더욱 바람직하게는 500ppm이하인 것을 특징으로 하는 무수 규산.
- 제9 내지 13항중 어느 한 항에 있어서, 잔여 소디움함량이 기껏해야 1500ppm인 것을 특징으로 하는 무수 규산.
- 제1 내지 8항중 어느 한 항에 따른 방법에 의해 제조될 수 있는, 다음의 특성들을 나타내는 유형의 침강 무수 규산:
- 제15항에 있어서, BET표면/CTAB표면의 비가 0.9내지 1.2사이에 포함됨을 특징으로 하는 무수 규산.
- 제15 또는 16항에 있어서, 탄소함량이 2500ppm이하, 더욱 상세히는 500ppm이하인 것을 특징으로 하는 무수 규산.
- 제15 내지 17항중 어느 한 항에 있어서, 잔여 나트륨 함량이 기껏해야 1500ppm인 것을 특징으로 하는 무수 규산.
- 제15 내지 18항중 어느 한 항에 있어서, 수분 흡수도가 기껏해야 3, 5%인 것을 특징으로 하는 무수 규산.
- 제15 내지 19항중 어느 한 항에 있어서, 밀도가 기껏해야 0.3%의 더욱 상세히는 기껏해야 0.15인 것을 특징으로 하는 무수 규산.
- 제15 내지 20항중 어느 한 항에 있어서, pH가 3.5내지 7.5사이, 더욱 상세히는 4.5내지 6.5사이에 포함됨을 특징으로 하는 무수 규산.
- 제15 내지 21항중 어느 한 항에 있어서, 45㎛의 체상에 체류물에 의해 측정된 미립자의 크기가 0.05%이하인 것을 특징으로 하는 무수 규산.
- 제15 내지 22항중 어느 한 항에 따른 무수규산 또는 제1 내지 8항중 어느 한 항에 따른 방법에 의해 수득된 무수 규산을 사용하는 것을 특징으로 하는 유기 폴리 실록산 혼합물의 강화 방법.
- 제15 내지 22항중 어느 한 항에 따른 무수 규산 또는 제1 내지 8항중 어느 한 항에 따른 방법에 의해 수득된 무수 규산을 포함함을 특징으로 하는 유기 폴리실옥산 혼합물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.