JPWO2018163953A1 - ポリアスパラティック塗料組成物、塗膜、及び塗装物品 - Google Patents
ポリアスパラティック塗料組成物、塗膜、及び塗装物品 Download PDFInfo
- Publication number
- JPWO2018163953A1 JPWO2018163953A1 JP2019504516A JP2019504516A JPWO2018163953A1 JP WO2018163953 A1 JPWO2018163953 A1 JP WO2018163953A1 JP 2019504516 A JP2019504516 A JP 2019504516A JP 2019504516 A JP2019504516 A JP 2019504516A JP WO2018163953 A1 JPWO2018163953 A1 JP WO2018163953A1
- Authority
- JP
- Japan
- Prior art keywords
- group
- polyisocyanate
- molar ratio
- mass
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
アスパラギン酸エステル化合物と、脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られるポリイソシアネートを含み、式(1)で表されるモル比xが0.05以上0.5以下、式(4)で表されるモル比dが0.02以上0.5以下、及び式(5)で表されるモル比eが0以上0.05以下であるポリイソシアネート組成物と、を含む、ポリアスパラティック塗料組成物が提供される。モル比x=(B+C+D)/(A+B+C+D) (1)モル比d=D/(A+B+C+D) (4)モル比e=E/A (5)上記式中、ポリイソシアネート組成物における、Aはイソシアヌレート基の含有量、Bはイミノオキサジアジンジオン基の含有量、Cはウレトジオン基の含有量(モル%)、Dはアロファネート基の含有量(モル%)、Eはビウレット基の含有量(モル%)を示す。
Description
本発明は、ポリアスパラティック塗料組成物、塗膜、及び塗装物品に関する。
本願は、2017年3月7日に日本に出願された特願2017−043117号及び特願2017−043140号と2017年7月5日に日本に出願された特願2017−132041号に基づき優先権を主張し、その内容をここに援用する。
本願は、2017年3月7日に日本に出願された特願2017−043117号及び特願2017−043140号と2017年7月5日に日本に出願された特願2017−132041号に基づき優先権を主張し、その内容をここに援用する。
ポリウレア塗料組成物のうち脂肪族系であるポリアスパラティック塗料組成物は、アミノ基を含有するアスパラギン酸エステル化合物並びにイソシアネート基を含有する脂肪族及び/又は脂環族ポリイソシアネート組成物から形成される。芳香族系ポリウレア塗料組成物の欠点である紫外線暴露で塗膜黄変することが大きく低減されて、従来から各種塗料、床材、防水材等の広範囲な用途で利用されている。
アスパラギン酸エステル化合物は、ポリウレタン塗料組成物の主剤ポリオールと比較して粘度が低く、ポリアスパラティック塗料組成物中の希釈溶剤を大幅に低減させられるために、ハイソリッド処方や無溶剤処方とすることが可能である。また、アスパラギン酸エステル化合物のアミノ基と脂肪族及び/又は脂環族ポリイソシアネートのイソシアネート基との反応性が速いために、ポリアスパラティック塗料組成物はポリウレタン塗料組成物と比較して室温下でも硬化速度が速く、機械強度に優れているという特長を有している。
例えば、特許文献1には、アスパラギン酸エステル骨格を有する第二級アミノ基を含有するポリアミン成分と、脂肪族ポリイソシアネート組成物でイソシアネート基を含有するポリイソシアネート成分とからなる、脂肪族系ポリウレア塗料組成物であるポリアスパラティック塗料組成物が開示されている。当該塗料組成物は比較的にポットライフが長く、塗膜硬度が高いことから高圧衝突混合スプレー機を使用せずに施工可能であるという特徴を有している。
しかしながら、特許文献1に提案されるようなポリアスパラティック塗料組成物については、脂肪族ポリイソシアネート組成物自体の粘度が高く、脂肪族ポリイソシアネート組成物及び/又はポリアスパラティック塗料組成物に希釈溶剤を加える必要があるため、ハイソリッド処方や無溶剤処方とすることに関して更なる改善の余地を有している。また、特に刷毛やローラー等の手塗り時に現場配合する際に、ポットライフに関しても更なる改善の余地を有している。
そこで、本発明は、脂肪族及び/又は脂環族ポリイソシアネート組成物がハイソリッド処方や無溶剤処方に適した低粘度で、硬化性や乾燥性を維持しつつ、塗膜を形成した際に、耐薬品性や硬度及び耐候性に優れ、かつ、ポットライフにも優れるという特長を有しているポリアスパラティック塗料組成物を提供することを目的とする。
本発明者は、鋭意研究した結果、特定構造を有する脂肪族及び/又は脂環族ポリイソシアネート組成物、具体的には、イソシアヌレート基、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基、ビウレット基及び/又はウレトンイミノ基の含有量(モル%)が所定の関係にある脂肪族及び/又は脂環族ポリイソシアネート組成物を、ポリアスパラティック塗料組成物に適用することで、ハイソリッド処方や無溶剤処方に適した低粘度で、硬化性を維持しつつ、ポリアスパラティック塗料組成物を使用した塗膜が耐薬品性及び耐候性に優れ、かつ、ポットライフにも優れることを見出し、本発明を完成させるに至った。
すなわち、本発明は、以下の構成を有する。
すなわち、本発明は、以下の構成を有する。
(1)(A)下記式(I):
式(I)中、Xはn価のポリアミンの第一級アミノ基を除去することによって得られたn価の有機基であり、R1及びR2は反応条件下でイソシアネート基に対して不活性である同じ又は異なった有機基であり、nは2以上の整数である、
で表されるアスパラギン酸エステル化合物と、
(B1)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られるポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下であるポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
上記式中、Aはポリイソシアネート組成物(B1)における下記式(II)で表されるイソシアヌレート基の含有量(モル%)、Bはポリイソシアネート組成物(B1)における下記式(III)で表されるイミノオキサジアジンジオン基の含有量(モル%)、Cはポリイソシアネート組成物(B1)における下記式(IV)で表されるウレトジオン基の含有量(モル%)、Dはポリイソシアネート組成物(B1)における下記式(V)で表されるアロファネート基の含有量(モル%)、Eはポリイソシアネート組成物(B1)における下記式(VI)で表されるビウレット基の含有量(モル%)を示す。
で表されるアスパラギン酸エステル化合物と、
(B1)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られるポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下であるポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
上記式中、Aはポリイソシアネート組成物(B1)における下記式(II)で表されるイソシアヌレート基の含有量(モル%)、Bはポリイソシアネート組成物(B1)における下記式(III)で表されるイミノオキサジアジンジオン基の含有量(モル%)、Cはポリイソシアネート組成物(B1)における下記式(IV)で表されるウレトジオン基の含有量(モル%)、Dはポリイソシアネート組成物(B1)における下記式(V)で表されるアロファネート基の含有量(モル%)、Eはポリイソシアネート組成物(B1)における下記式(VI)で表されるビウレット基の含有量(モル%)を示す。
(2)前記ポリイソシアネート組成物におけるモル比dが0.03以上0.3以下であり、前記ポリイソシアネート組成物における下記式(6)で表されるモル比fが0.001以上0.005以下である、前記(1)に記載のポリアスパラティック塗料組成物。
モル比f=F/(A+B+C+D) (6)
前記式中、A、B、C及びDは、前記(1)に記載の通りであり、Fはポリイソシアネート組成物(B1)における下記式(VII)で表されるウレトンイミノ基の含有量(モル%)を示す。
モル比f=F/(A+B+C+D) (6)
前記式中、A、B、C及びDは、前記(1)に記載の通りであり、Fはポリイソシアネート組成物(B1)における下記式(VII)で表されるウレトンイミノ基の含有量(モル%)を示す。
(3)前記ポリイソシアネート組成物におけるモル比dが0.04以上0.3以下であり、さらに、下記式(2)で表されるモル比bが0以上0.4以下、及び、下記式(3)で表されるモル比cが0以上0.3以下である、前記(1)又は(2)に記載のポリアスパラティック塗料組成物。
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
前記式中、A,B、C及びDは、前記(1)で記載の通りである。
(4)(A)下記一般式(I)で示されるアスパラギン酸エステル化合物と、
(B2)下記一般式(VIII)で示されるトリイソシアネート化合物(b1)を含むポリイソシアネート組成物と、を含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記トリイソシアネート化合物(b1)の含有量が20質量%以上100質量%以下であるポリアスパラティック塗料組成物。
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
前記式中、A,B、C及びDは、前記(1)で記載の通りである。
(4)(A)下記一般式(I)で示されるアスパラギン酸エステル化合物と、
(B2)下記一般式(VIII)で示されるトリイソシアネート化合物(b1)を含むポリイソシアネート組成物と、を含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記トリイソシアネート化合物(b1)の含有量が20質量%以上100質量%以下であるポリアスパラティック塗料組成物。
式(I)中、Xはn価のポリアミンの第一級アミノ基を除去することによって得られたn価の有機基であり、R1及びR2は反応条件下でイソシアネート基に対して不活性である同じ又は異なった有機基であり、nは2以上の整数である。
式(VIII)中、複数あるY1は、それぞれ独立に、単結合、又は、エステル構造及びエーテル構造からなる群より選択される1種以上を含んでもよい炭素数1〜20の2価の炭化水素基である。複数あるY1は、それぞれ同一であってもよく異なっていてもよい。R3は、水素原子又は炭素数1〜12の1価の炭化水素基である。
(5)前記ポリイソシアネート組成物(B2)は、さらに、脂肪族ジイソシアネート及び脂環式ジイソシアネートからなる群より選択される1種以上のジイソシアネートから得られるポリイソシアネート(b2)を含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記ポリイソシアネート(b2)の含有量が0質量%よりも大きく80質量%以下である前記(4)に記載のポリアスパラティック塗料組成物。
(6)(A)下記式(I)で表されるアスパラギン酸エステル化合物と、
前記ポリイソシアネート組成物(B2)の総量に対する前記ポリイソシアネート(b2)の含有量が0質量%よりも大きく80質量%以下である前記(4)に記載のポリアスパラティック塗料組成物。
(6)(A)下記式(I)で表されるアスパラギン酸エステル化合物と、
式(I)中、Xはn価のポリアミンの第一級アミノ基を除去することによって得られたn価の有機基であり、R1及びR2は反応条件下でイソシアネート基に対して不活性である同じ又は異なった有機基であり、nは2以上の整数である。
(B3)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含むポリイソシアネート組成物であって、ポリイソシアネート組成物の総量に対するウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上30.0質量%以下である、ポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。
(7)前記ポリイソシアネート組成物(B3)が、更にイソシアヌレート基を含む、前記(6)に記載のポリアスパラティック塗料組成物。
(8)前記ポリイソシアネート組成物の、25℃における粘度が10mPa.s以上1000mPa.s以下である、前記(1)〜(7)のいずれか一項に記載のポリアスパラティック塗料組成物。
(9)前記アスパラギン酸エステル化合物のアミノ基と、前記ポリイソシアネート組成物のイソシアネート基との当量比が、アミノ基:イソシアネート基=10:1〜1:10である、前記(1)〜(8)のいずれか一項に記載のポリアスパラティック塗料組成物。
(10)前記ジイソシアネートモノマーが、ヘキサメチレンジイソシアネートを含む、前記(1)〜(9)のいずれか一項に記載のポリアスパラティック塗料組成物。
(11)前記(1)〜(10)のいずれか一項に記載のポリアスパラティック塗料組成物により形成された、塗膜。
(12)前記(11)に記載の塗膜を備える、塗装物品。
(B3)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含むポリイソシアネート組成物であって、ポリイソシアネート組成物の総量に対するウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上30.0質量%以下である、ポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。
(7)前記ポリイソシアネート組成物(B3)が、更にイソシアヌレート基を含む、前記(6)に記載のポリアスパラティック塗料組成物。
(8)前記ポリイソシアネート組成物の、25℃における粘度が10mPa.s以上1000mPa.s以下である、前記(1)〜(7)のいずれか一項に記載のポリアスパラティック塗料組成物。
(9)前記アスパラギン酸エステル化合物のアミノ基と、前記ポリイソシアネート組成物のイソシアネート基との当量比が、アミノ基:イソシアネート基=10:1〜1:10である、前記(1)〜(8)のいずれか一項に記載のポリアスパラティック塗料組成物。
(10)前記ジイソシアネートモノマーが、ヘキサメチレンジイソシアネートを含む、前記(1)〜(9)のいずれか一項に記載のポリアスパラティック塗料組成物。
(11)前記(1)〜(10)のいずれか一項に記載のポリアスパラティック塗料組成物により形成された、塗膜。
(12)前記(11)に記載の塗膜を備える、塗装物品。
本発明に係るポリアスパラティック塗料組成物によれば、ハイソリッド処方や無溶剤処方に適した低粘度で、硬化性や乾燥性を維持しつつ、係るポリアスパラティック塗料組成物を使用した塗膜が耐薬品性や硬度及び耐候性に優れ、かつ、ポットライフにも優れる。
以下、本発明を実施するための形態について詳細に説明する。以下の本実施形態は、本発明を説明するための例示であり、本発明を以下の内容に限定する趣旨ではない。本発明は、その要旨の範囲内で適宜に変形して実施できる。
〔ポリアスパラティック塗料組成物〕
本発明の第1の実施形態のポリアスパラティック塗料組成物は、(A)下記式(I)で表されるアスパラギン酸エステル化合物と、
本発明の第1の実施形態のポリアスパラティック塗料組成物は、(A)下記式(I)で表されるアスパラギン酸エステル化合物と、
〔式(I)中、Xはn価のポリアミンの第一級アミノ基を除去することによって得られたn価の有機基であり、R1及びR2は反応条件下でイソシアネート基に対して不活性である同じ又は異なった有機基であり、nは2以上の整数である。〕
(B1)脂肪族及び/又は脂環族ジイソシアネートモノマーからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られるポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下であるポリイソシアネート組成物と、を含む。
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
前記式中、Aはポリイソシアネート組成物における下記式(II)で表されるイソシアヌレート基の含有量(モル%)、Bはポリイソシアネート組成物における下記式(III)で表されるイミノオキサジアジンジオン基の含有量(モル%)、Cはポリイソシアネート組成物における下記式(IV)で表されるウレトジオン基の含有量(モル%)、Dはポリイソシアネート組成物における下記式(V)で表されるアロファネート基の含有量(モル%)、Eはポリイソシアネート組成物における下記式(VI)で表されるビウレット基の含有量(モル%)を示す。
前記ポリイソシアネート組成物において、モル比dが0.03以上0.3以下であることが好ましく、さらに、下記式(6)で表されるモル比fが0.001以上0.005以下であることが好ましい。
モル比f=F/(A+B+C+D) (6)
前記式中、Fはポリイソシアネート組成物における下記式(VII)で表されるウレトンイミノ基の含有量(モル%)を示す。
モル比f=F/(A+B+C+D) (6)
前記式中、Fはポリイソシアネート組成物における下記式(VII)で表されるウレトンイミノ基の含有量(モル%)を示す。
前記ポリイソシアネート組成物において、モル比dが0.04以上0.3以下であることが好ましく、さらに、下記式(2)で表されるモル比bが0以上0.4以下、及び、下記式(3)で表されるモル比cが0以上0.3以下であることが好ましい。
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
前記式中、A、B、C、及びDは前記の通りである。
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
前記式中、A、B、C、及びDは前記の通りである。
本実施形態で用いられるアスパラギン酸エステル化合物のアミノ基と、ポリイソシアネート組成物のイソシアネート基との当量比は、好ましくはアミノ基:イソシアネート基=10:1〜1:10であり、より好ましくはアミノ基:イソシアネート基=5:1〜1:5であり、さらに好ましくはアミノ基:イソシアネート基=2:1〜1:2である。
アスパラギン酸エステル化合物のアミノ基と、ポリイソシアネート組成物のイソシアネート基との当量比(アミノ基/イソシアネート基)が10/1以下であることによって、硬化性をより良好とすることができる傾向にある。イソシアネート基とアミノ基との当量比(アミノ基/イソシアネート基)が1/10以上であることによって、本実施形態のポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
アスパラギン酸エステル化合物のアミノ基と、ポリイソシアネート組成物のイソシアネート基との当量比(アミノ基/イソシアネート基)が10/1以下であることによって、硬化性をより良好とすることができる傾向にある。イソシアネート基とアミノ基との当量比(アミノ基/イソシアネート基)が1/10以上であることによって、本実施形態のポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
〔アスパラギン酸エステル化合物〕
本実施形態で用いられる(A)アスパラギン酸エステル化合物は、下記式(I)で表される。
本実施形態で用いられる(A)アスパラギン酸エステル化合物は、下記式(I)で表される。
式(I)中、Xはn価のポリアミンの第一級アミノ基を除去することによって得られたn価の有機基であり、R1及びR2は反応条件下でイソシアネート基に対して不活性である同じ又は異なった有機基であり、nは2以上の整数である。
本実施形態において、式(I)中のXは、特に限定されないが、耐黄変性の観点から、芳香族基を有さない脂肪族及び/又は脂環族ポリアミンが好ましく、例えば、下記群から選ばれるn価のポリアミン:エチレンジアミン、1,2−ジアミノプロパン、1,4−ジアミノブタン、1,5−ジアミノペンタン、1,6−ジアミノヘキサン、2,5−ジアミノ−2,5−ジメチルヘキサン、2,2,4−及び/又は2,4,4−トリメチル−1,6−ジアミノヘキサン、1,11−ジアミノウンデカン、1,12−ジアミノドデカン、1−アミノ−3,3,5−トリメチル−5−アミノメチルシクロヘキサン、2,4−及び/又は2,6−ヘキサヒドロトリレンジアミン、2,4’−及び/又は4,4’−ジアミノジシクロヘキシルメタン、3,3’−ジメチル−4,4’−ジアミノジシクロヘキシルメタン、2,4,4’−トリアミノ−5−メチルジシクロヘキシルメタン、並びに148以上6000以下の数平均分子量を有し、第一級アミノ基が脂肪族的に結合したポリエーテルポリアミンに基づく。
好ましくは、1,4−ジアミノブタン、1,5−ジアミノペンタン、1,6−ジアミノヘキサン、2,2,4−及び/又は2,4,4−トリメチル−1,6−ジアミノヘキサン、1−アミノ−3,3,5−トリメチル−5−アミノメチルシクロヘキサン、4,4’−ジアミノジシクロヘキシルメタン、3,3’−ジメチル−4,4’−ジアミノジシクロヘキシルメタンに基づく。より好ましくは、4,4’−ジアミノジシクロヘキシルメタン、3,3’−ジメチル−4,4’−ジアミノジシクロヘキシルメタンに基づく。
好ましくは、1,4−ジアミノブタン、1,5−ジアミノペンタン、1,6−ジアミノヘキサン、2,2,4−及び/又は2,4,4−トリメチル−1,6−ジアミノヘキサン、1−アミノ−3,3,5−トリメチル−5−アミノメチルシクロヘキサン、4,4’−ジアミノジシクロヘキシルメタン、3,3’−ジメチル−4,4’−ジアミノジシクロヘキシルメタンに基づく。より好ましくは、4,4’−ジアミノジシクロヘキシルメタン、3,3’−ジメチル−4,4’−ジアミノジシクロヘキシルメタンに基づく。
本実施形態において、式(I)中のR1及びR2に規定した、「反応条件下でイソシアネート基に対して不活性」とは、これらの基が、水酸基、アミノ基、又はチオール基のようなツェレビチノフ活性水素含有基(CH酸性化合物)を有さないことを意味する。
R1及びR2は相互に独立に、好ましくは炭素数1以上10以下のアルキル基であり、より好ましくはメチル基、エチル基、又はブチル基である。
R1及びR2は相互に独立に、好ましくは炭素数1以上10以下のアルキル基であり、より好ましくはメチル基、エチル基、又はブチル基である。
本実施形態において、式(I)中のnは、好ましくは2以上6以下、より好ましくは2以上4以下の整数であり、よりさらに好ましくは2である。
本実施形態の(A)アスパラギン酸エステル化合物の製造方法は特に限定されないが、例えば、下記式(VII)で表される第一級ポリアミンと、下記式(VIII)で表されるマレイン酸エステル又はフマル酸エステルとの反応によって製造される。
X−[NH2]n (VII)
R1OOC−CH=CH−COOR2 (VIII)
〔式中、X、R1、R2、nは、式(I)で表されるものと同義である。〕
本実施形態の(A)アスパラギン酸エステル化合物の製造方法は特に限定されないが、例えば、下記式(VII)で表される第一級ポリアミンと、下記式(VIII)で表されるマレイン酸エステル又はフマル酸エステルとの反応によって製造される。
X−[NH2]n (VII)
R1OOC−CH=CH−COOR2 (VIII)
〔式中、X、R1、R2、nは、式(I)で表されるものと同義である。〕
適当なポリアミンとしては、特に限定されないが、例えば、Xを基礎として上記したジアミンである。また、適当なマレイン酸エステル又はフマル酸エステルとしては、特に限定されないが、例えば、式(I)中のR1及びR2に規定した基をR1及びR2として有するマレイン酸エステル又はフマル酸エステルである。好ましくは、R1及びR2が炭素数1以上10以下のアルキル基であるマレイン酸エステル又はフマル酸エステルが挙げられ、より好ましくはマレイン酸ジメチル、マレイン酸ジエチル、マレイン酸ジブチル及び対応するフマル酸エステルが挙げられる。
記載された出発物質からのアスパラギン酸エステル化合物の調製は、好ましくは0℃以上100℃以下の温度範囲で行なう。当該出発物質は、第一級アミノ基の各々において、少なくとも1つ、好ましくは1つだけオレフィン二重結合が存在するような比率で使用される。所望によって、反応後は蒸留することで、過剰に使用した出発原料を除去することができる。反応はバルクで、又は適当な溶剤(特に限定されないが、例えば、メタノール、エタノール、プロパノール又はジオキサン、或いはこのような溶剤の混合物)の存在下で行なうことができる。
〔ポリイソシアネート組成物(B1)〕
本実施形態で用いられるポリイソシアネート組成物(B1)は、脂肪族及び/又は脂環族ジイソシアネートモノマーからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られる脂肪族及び/又は脂環族ポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下である。
本実施形態で用いられるポリイソシアネート組成物(B1)は、脂肪族及び/又は脂環族ジイソシアネートモノマーからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られる脂肪族及び/又は脂環族ポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下である。
前記モル比dは、0.03以上0.3以下であることが好ましく、0.04以上0.3以下であることがより好ましい。
また、下記式(2)で表されるモル比bが0以上0.4以下であることが好ましく、下記式(3)で表されるモル比cが0以上0.3以下であることが好ましい。
また、下記式(6)で示されるモル比fが0.001以上0.005以下であることが好ましい。
また、下記式(2)で表されるモル比bが0以上0.4以下であることが好ましく、下記式(3)で表されるモル比cが0以上0.3以下であることが好ましい。
また、下記式(6)で示されるモル比fが0.001以上0.005以下であることが好ましい。
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
モル比f=F/(A+B+C+D) (6)
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
モル比f=F/(A+B+C+D) (6)
前記式中、Aはポリイソシアネート組成物における下記式(II)で表されるイソシアヌレート基の含有量(モル%)、Bはポリイソシアネート組成物における下記式(III)で表されるイミノオキサジアジンジオン基の含有量(モル%)、Cはポリイソシアネート組成物における下記式(IV)で表されるウレトジオン基の含有量(モル%)、Dはポリイソシアネート組成物における下記式(V)で表されるアロファネート基の含有量(モル%)、Eはポリイソシアネート組成物における下記式(VI)で表されるビウレット基の含有量(モル%)、Fはポリイソシアネート組成物における下記式(VII)で表されるウレトンイミノ基の含有量(モル%)を示す。
モル比xの下限値は、好ましくは0.1であり、より好ましくは0.15であり、さらに好ましくは0.2である。モル比xの上限値は、好ましくは0.4であり、より好ましくは0.35であり、さらに好ましくは0.3である。
モル比xが0.05以上であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
モル比xが0.5以下であることによって、ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
モル比xが0.05以上0.5以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイミノオキサジアジンジオン化反応、ウレトジオン化反応、アロファネート化反応により、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基を形成し、モル比を調整することが挙げられる。
モル比xが0.05以上であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
モル比xが0.5以下であることによって、ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
モル比xが0.05以上0.5以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイミノオキサジアジンジオン化反応、ウレトジオン化反応、アロファネート化反応により、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基を形成し、モル比を調整することが挙げられる。
イミノオキサジアジンジオン基のモル比は、モル比b=B/(A+B+C+D)のモル比として、好ましくは0.35以下であり、より好ましくは0.3以下であり、さらに好ましくは0.25以下であり、よりさらに好ましくは0.2以下であり、さらにより好ましくは0.1以下である。
モル比bが0.4以下であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。ポリアスパラティック塗料組成物を使用した塗膜の耐候性をより向上させる観点から、モル比bは0.2以下であることがより好ましい。
モル比bが0.4以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイミノオキサジアジンジオン化反応により、イミノオキサジアジンジオン基を形成し、モル比bを調整することが挙げられる。
モル比bが0.4以下であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。ポリアスパラティック塗料組成物を使用した塗膜の耐候性をより向上させる観点から、モル比bは0.2以下であることがより好ましい。
モル比bが0.4以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイミノオキサジアジンジオン化反応により、イミノオキサジアジンジオン基を形成し、モル比bを調整することが挙げられる。
ウレトジオン基のモル比は、モル比c=C/(A+B+C+D)のモル比として、好ましくは0.25以下である。
モル比cが0.3以下であることによって、硬化性をより維持することができる傾向にある。ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させる観点から、モル比cは0.25以下であることがより好ましい。
モル比cが0.3以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するウレトジオン化反応により、ウレトジオン基を形成し、モル比cを調整することが挙げられる。
モル比cが0.3以下であることによって、硬化性をより維持することができる傾向にある。ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させる観点から、モル比cは0.25以下であることがより好ましい。
モル比cが0.3以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するウレトジオン化反応により、ウレトジオン基を形成し、モル比cを調整することが挙げられる。
アロファネート基のモル比は、モル比d=D/(A+B+C+D)のモル比として、好ましくは0.03以上0.3以下であり、より好ましくは0.04以上0.3以下であり、より更に好ましくは0.05以上0.25以下である。
ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現する観点から、モル比dは0.02以上であることが好ましい。
硬化性をより維持する観点から、モル比dは0.5以下であることが好ましい。
ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させる観点から、モル比dは、0.25以下であることがより好ましい。
モル比dが前記範囲となるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するアロファネート化反応により、アロファネート基を形成し、モル比dを調整することが挙げられる。
ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現する観点から、モル比dは0.02以上であることが好ましい。
硬化性をより維持する観点から、モル比dは0.5以下であることが好ましい。
ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させる観点から、モル比dは、0.25以下であることがより好ましい。
モル比dが前記範囲となるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するアロファネート化反応により、アロファネート基を形成し、モル比dを調整することが挙げられる。
ビウレット基のモル比は、モル比e=E/Aのモル比として、0以上0.05以下である。好ましくは0.03以下であり、より好ましくは0.02以下であり、さらに好ましくは0.01以下である。
モル比eが0.05以下であることによって、ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
モル比eが0.05以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するビウレット化反応により、ビウレット基を形成し、モル比eを調整することが挙げられる。
モル比eが0.05以下であることによって、ポリアスパラティック塗料組成物を使用した塗膜の耐薬品性及び耐候性を向上させることができる傾向にある。
モル比eが0.05以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するビウレット化反応により、ビウレット基を形成し、モル比eを調整することが挙げられる。
ウレトンイミノ基のモル比は、モル比f=F/(A+B+C+D)のモル比として、より好ましくは0.001以上0.004以下であり、さらに好ましくは0.001以上0.003以下であり、よりさらに好ましくは0.001以上0.002以下である。
モル比fが0.001以上であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。
モル比fが0.005以下であることによって、ポリアスパラティック塗料組成物のポットライフをより向上させることができる傾向にある。
モル比fが0.001以上0.005以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイソシアヌレート化反応を実施した後、触媒を失活させ、その後に140〜160℃程度の温度で、数時間程度反応させることにより制御する方法や、1−ブチルホスホラン等のヘテロ環含有リン系化合物を触媒として、20〜80℃程度の温度で、数時間から数十時間程度反応させたポリイソシアネート組成物を一部混合されることで、モル比fを調整することが挙げられる。
モル比fが0.001以上であることによって、ポリイソシアネート組成物(B1)がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。
モル比fが0.005以下であることによって、ポリアスパラティック塗料組成物のポットライフをより向上させることができる傾向にある。
モル比fが0.001以上0.005以下であるようなポリイソシアネート組成物(B1)を得る方法としては、例えば、後述するイソシアヌレート化反応を実施した後、触媒を失活させ、その後に140〜160℃程度の温度で、数時間程度反応させることにより制御する方法や、1−ブチルホスホラン等のヘテロ環含有リン系化合物を触媒として、20〜80℃程度の温度で、数時間から数十時間程度反応させたポリイソシアネート組成物を一部混合されることで、モル比fを調整することが挙げられる。
モル比x、モル比b、モル比c、モル比d、モル比e、及びモル比fを、上述したような範囲に調整するためには、後述する〔ポリイソシアネートの製造方法〕に記載される方法を適宜使用して、ポリイソシアネート組成物における各基のモル比を調整すればよい。これらのモル比は、後述する実施例に記載の方法に基づき、13C−NMRによって測定することができる。
本実施形態で用いられるポリイソシアネート組成物のイソシアネート含有量(以下、「NCO含有量」ともいう。)は、当該ポリイソシアネート組成物の総量(100質量%)に対して、好ましくは10質量%以上60質量%以下である。NCO含有量の下限値は、より好ましくは13質量%であり、さらに好ましくは15質量%である。NCO含有量の上限値は、より好ましくは55質量%であり、さらに好ましくは50質量%である。
NCO含有量が10質量%以上であることによって、硬化性をより維持することができる傾向にある。
NCO含有量が60質量%以下であることによって、ジイソシアネートモノマー質量濃度をより好適な範囲に調整することができる傾向にある。NCO含有量は、後述する実施例に記載の方法によって測定することができる。
NCO含有量が10質量%以上であることによって、硬化性をより維持することができる傾向にある。
NCO含有量が60質量%以下であることによって、ジイソシアネートモノマー質量濃度をより好適な範囲に調整することができる傾向にある。NCO含有量は、後述する実施例に記載の方法によって測定することができる。
本実施形態で用いられるポリイソシアネート組成物の25℃における粘度は、好ましくは10mPa.s以上1000mPa.s以下である。粘度の下限値は、より好ましくは50mPa.sであり、さらに好ましくは100mPa.sであり、よりさらに好ましくは200mPa.sである。粘度の上限値は、より好ましくは900mPa.sであり、さらに好ましくは800mPa.sであり、よりさらに好ましくは700mPa.sである。
粘度が10mPa.s以上であることによって、硬化性をより維持することができる傾向にある。
粘度が1000mPa.s以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。粘度は、後述する実施例に記載の方法によって測定することができる。
粘度が10mPa.s以上であることによって、硬化性をより維持することができる傾向にある。
粘度が1000mPa.s以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。粘度は、後述する実施例に記載の方法によって測定することができる。
本実施形態で用いられるポリイソシアネート組成物の数平均分子量は、好ましくは150以上900以下である。
数平均分子量の下限値は、より好ましくは180であり、さらに好ましくは220であり、よりさらに好ましくは250である。
数平均分子量の上限値は、より好ましくは800であり、さらに好ましくは700であり、よりさらに好ましくは600である。
数平均分子量が150以上であることによって、硬化性をより維持することができる傾向にある。
数平均分子量が900以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。数平均分子量は、後述する実施例に記載の方法によって測定することができる。
数平均分子量の下限値は、より好ましくは180であり、さらに好ましくは220であり、よりさらに好ましくは250である。
数平均分子量の上限値は、より好ましくは800であり、さらに好ましくは700であり、よりさらに好ましくは600である。
数平均分子量が150以上であることによって、硬化性をより維持することができる傾向にある。
数平均分子量が900以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。数平均分子量は、後述する実施例に記載の方法によって測定することができる。
本実施形態で用いられるポリイソシアネート組成物のイソシアネート基平均数は、好ましくは2.0以上6.0以下である。
イソシアネート基平均数の下限値は、より好ましくは2.2であり、さらに好ましくは2.4であり、よりさらに好ましくは2.6であり、さらにより好ましくは2.8である。
イソシアネート基平均数の上限値は、より好ましくは5.0であり、さらに好ましくは4.0であり、よりさらに好ましくは3.5であり、さらにより好ましくは3.0である。
イソシアネート基平均数が2.0以上であることによって、硬化性をより維持することができる傾向にある。
イソシアネート基平均数が6.0以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。イソシアネート基平均数は、後述する実施例に記載の方法によって測定することができる。
イソシアネート基平均数の下限値は、より好ましくは2.2であり、さらに好ましくは2.4であり、よりさらに好ましくは2.6であり、さらにより好ましくは2.8である。
イソシアネート基平均数の上限値は、より好ましくは5.0であり、さらに好ましくは4.0であり、よりさらに好ましくは3.5であり、さらにより好ましくは3.0である。
イソシアネート基平均数が2.0以上であることによって、硬化性をより維持することができる傾向にある。
イソシアネート基平均数が6.0以下であることによって、ポリイソシアネート組成物がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。イソシアネート基平均数は、後述する実施例に記載の方法によって測定することができる。
本実施形態で用いられるポリイソシアネート組成物のジイソシアネートモノマー質量濃度は、当該脂肪族及び/又は脂環族ポリイソシアネートの総量(100質量%)に対して、好ましくは0質量%以上1.0質量%以下であり、より好ましくは0.5質量%以下であり、さらに好ましくは0.3質量%以下である。
ジイソシアネートモノマー質量濃度が1.0質量%以下であることによって、硬化性をより維持することができる傾向にある。ジイソシアネートモノマー質量濃度は、後述する実施例に記載の方法によって測定することができる。
ジイソシアネートモノマー質量濃度が1.0質量%以下であることによって、硬化性をより維持することができる傾向にある。ジイソシアネートモノマー質量濃度は、後述する実施例に記載の方法によって測定することができる。
〔ジイソシアネートモノマー〕
本実施形態で用いられるジイソシアネートモノマーは、脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される。
本実施形態で用いられる脂肪族ジイソシアネートとしては、特に限定されないが、好ましくは炭素数4以上30以下の脂肪族ジイソシアネートであり、例えば、テトラメチレンジイソシアネート、ペンタメチレンジイソシアネート、ヘキサメチレンジイソシアネート(以下、「HDI」と略す)、2,2,4−トリメチル−1,6−ヘキサメチレンジイソシアネート、及びリジンジイソシアネートが挙げられる。その中でも、工業的入手の容易さからHDIがより好ましい。上記に示した脂肪族ジイソシアネートは、1種を単独で使用しても2種以上を併用しても構わない。
本実施形態で用いられるジイソシアネートモノマーは、脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される。
本実施形態で用いられる脂肪族ジイソシアネートとしては、特に限定されないが、好ましくは炭素数4以上30以下の脂肪族ジイソシアネートであり、例えば、テトラメチレンジイソシアネート、ペンタメチレンジイソシアネート、ヘキサメチレンジイソシアネート(以下、「HDI」と略す)、2,2,4−トリメチル−1,6−ヘキサメチレンジイソシアネート、及びリジンジイソシアネートが挙げられる。その中でも、工業的入手の容易さからHDIがより好ましい。上記に示した脂肪族ジイソシアネートは、1種を単独で使用しても2種以上を併用しても構わない。
本実施形態で用いられる脂環族ジイソシアネートとしては、特に限定されないが、好ましくは炭素数8以上30以下の脂環族ジイソシアネートであり、例えば、イソホロンジイソシアネート(以下、「IPDI」と略す)、1,3−ビス(イソシアナトメチル)−シクロヘキサン、4,4’−ジシクロヘキシルメタンジイソシアネート、ノルボルネンジイソシアネート、及び水添キシリレンジイソシアネートが挙げられる。その中でも、耐候性及び工業的入手の容易さから、IPDIがより好ましい。上記に示した脂環族ジイソシアネートは、1種を単独で使用しても2種以上を併用しても構わない。
ジイソシアネートモノマーとして、脂肪族ジイソシアネートの1種又は2種以上と、脂環族ジイソシアネートの1種又は2種以上とを組み合わせて用いることもできる。
〔ポリイソシアネートの製造方法〕
本実施形態で用いられるポリイソシアネートの製造方法を説明する。本実施形態で用いられるポリイソシアネートは、イソシアヌレート基を形成するイソシアヌレート化反応、イミノオキサジアジンジオン基を形成するイミノオキサジアジンジオン化反応、ウレトジオン基を形成するウレトジオン化反応、アロファネート基を形成するアロファネート化反応、ビウレット基を形成するビウレット化反応、及びウレトンイミノ基を形成するウレトンイミノ化反応を、過剰のジイソシアネートモノマー存在下で一度に実施して、反応終了後に、未反応のジイソシアネートモノマーを除去して得ることができる。
また、上記の反応を別々に行ない、それぞれ得たポリイソシアネートを、各官能基のモル比が上記範囲となるように混合してもよい。ここで、製造の簡便さからは、上記反応を一度に行ないポリイソシアネートを得ることが好ましく、各官能基のモル比を自由に調整する観点からは、別々に製造した後に混合することが好ましい。
本実施形態で用いられるポリイソシアネートの製造方法を説明する。本実施形態で用いられるポリイソシアネートは、イソシアヌレート基を形成するイソシアヌレート化反応、イミノオキサジアジンジオン基を形成するイミノオキサジアジンジオン化反応、ウレトジオン基を形成するウレトジオン化反応、アロファネート基を形成するアロファネート化反応、ビウレット基を形成するビウレット化反応、及びウレトンイミノ基を形成するウレトンイミノ化反応を、過剰のジイソシアネートモノマー存在下で一度に実施して、反応終了後に、未反応のジイソシアネートモノマーを除去して得ることができる。
また、上記の反応を別々に行ない、それぞれ得たポリイソシアネートを、各官能基のモル比が上記範囲となるように混合してもよい。ここで、製造の簡便さからは、上記反応を一度に行ないポリイソシアネートを得ることが好ましく、各官能基のモル比を自由に調整する観点からは、別々に製造した後に混合することが好ましい。
ジイソシアネートモノマーからイソシアヌレート基を含有するポリイソシアネートを誘導するための触媒としては、一般的に使用されるイソシアヌレート化反応触媒が挙げられる。イソシアヌレート化反応触媒としては、特に限定されないが、好ましくは一般に塩基性を有するもので、例えば、(1)テトラメチルアンモニウム、テトラエチルアンモニウム、テトラブチルアンモニウム等のテトラアルキルアンモニウムのハイドロオキサイド;その酢酸塩、オクチル酸塩、ミリスチン酸塩、安息香酸塩等の有機弱酸塩、(2)トリメチルヒドロキシエチルアンモニウム、トリメチルヒドロキシプロピルアンモニウム、トリエチルヒドロキシエチルアンモニウム、トリエチルヒドロキシプロピルアンモニウム等のヒドロキシアルキルアンモニウムのハイドロオキサイド;その酢酸塩、オクチル酸塩、ミリスチン酸塩、安息香酸塩等の有機弱酸塩、(3)酢酸、カプロン酸、オクチル酸、ミリスチン酸等のアルキルカルボン酸の錫、亜鉛、鉛等の金属塩、(4)ナトリウム、カリウム等の金属アルコラート、(5)ヘキサメチレンジシラザン等のアミノシリル基含有化合物、(6)マンニッヒ塩基類、(7)第3級アミン類とエポキシ化合物との併用、(8)トリブチルホスフィン等の燐系化合物が挙げられる。
この中で、不要な副生成物を生じさせにくい観点からは、好ましくは4級アンモニウムの有機弱酸塩であり、より好ましくはテトラアルキルアンモニウムの有機弱酸塩である。
上述したイソシアヌレート化反応触媒は、仕込んだジイソシアネートモノマーの質量に対して、好ましくは10質量ppm以上1000質量ppm以下である。その上限値は、より好ましくは500質量ppmであり、さらに好ましくは100質量ppmである。また、イソシアヌレート化反応温度としては、好ましくは50℃以上120℃以下であり、より好ましくは60℃以上90℃以下である。イソシアヌレート化反応温度が120℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
上述したイソシアヌレート化反応触媒は、仕込んだジイソシアネートモノマーの質量に対して、好ましくは10質量ppm以上1000質量ppm以下である。その上限値は、より好ましくは500質量ppmであり、さらに好ましくは100質量ppmである。また、イソシアヌレート化反応温度としては、好ましくは50℃以上120℃以下であり、より好ましくは60℃以上90℃以下である。イソシアヌレート化反応温度が120℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
所望の転化率(イソシアヌレート化反応で生成したポリイソシアネートの、仕込んだジイソシアネートモノマーに対する質量割合)でイソシアヌレート化反応を、特に限定されないが、例えば、リン酸、酸性リン酸エステル等の酸性化合物の添加によって停止する。本実施形態のポリイソシアネートを得るためには、反応の進行を初期で停止する必要がある。
しかしながら、イソシアヌレート化反応は、初期の反応速度が非常に速いため、反応の進行を初期で停止することに困難が伴い、反応条件、特に触媒の添加量及び添加方法は慎重に選択する必要がある。
例えば、触媒の一定時間毎の分割添加方法等が好適なものとして推奨される。
したがって、本実施形態で用いられるポリイソシアネートを得るためのイソシアヌレート化反応の転化率は、好ましくは30%以下であり、より好ましくは25%以下であり、さらに好ましくは20%以下である。
イソシアヌレート化反応の転化率が30%以下であることによって、脂肪族及び/又は脂環族ポリイソシアネート組成物がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
例えば、触媒の一定時間毎の分割添加方法等が好適なものとして推奨される。
したがって、本実施形態で用いられるポリイソシアネートを得るためのイソシアヌレート化反応の転化率は、好ましくは30%以下であり、より好ましくは25%以下であり、さらに好ましくは20%以下である。
イソシアヌレート化反応の転化率が30%以下であることによって、脂肪族及び/又は脂環族ポリイソシアネート組成物がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
ジイソシアネートモノマーからイミノオキサジアジンジオン基を含有するポリイソシアネートを誘導するための触媒としては、特に限定されないが、例えば、一般にイミノオキサジアジンジオン化反応触媒として知られている下記(1)又は(2)の触媒が使用できる。
(1)テトラメチルアンモニウムフルオリド水和物、テトラエチルアンモニウムフルオリド等の、一般式M[Fn]、又は一般式M[Fn(HF)m]で表される(ポリ)フッ化水素(式中、m及びnは、m/n>0の関係を満たす各々整数であり、Mは、n荷電カチオン(混合物)又は合計でn価の1個以上のラジカルを示す。)
(2)3,3,3−トリフルオロカルボン酸;4,4,4,3,3−ペンタフルオロブタン酸;5,5,5,4,4,3,3−ヘプタフルオロペンタン酸;3,3−ジフルオロプロパ−2−エン酸等の一般式R1−CR’2−C(O)O−、又は、一般式R2=CR’−C(O)O−(式中、R1、及びR2は、必要に応じて分岐状、環状、及び/又は不飽和の炭素数1〜30のパーフルオロアルキル基を示し、R’は、同一又は異なって、水素原子、炭素数1〜20のアルキル基、及びアリール基からなる群から選択され、必要に応じてヘテロ原子を含有するものを示す。)と、第4級アンモニウムカチオン、又は第4級ホスホニウムカチオンからなる化合物。
(2)3,3,3−トリフルオロカルボン酸;4,4,4,3,3−ペンタフルオロブタン酸;5,5,5,4,4,3,3−ヘプタフルオロペンタン酸;3,3−ジフルオロプロパ−2−エン酸等の一般式R1−CR’2−C(O)O−、又は、一般式R2=CR’−C(O)O−(式中、R1、及びR2は、必要に応じて分岐状、環状、及び/又は不飽和の炭素数1〜30のパーフルオロアルキル基を示し、R’は、同一又は異なって、水素原子、炭素数1〜20のアルキル基、及びアリール基からなる群から選択され、必要に応じてヘテロ原子を含有するものを示す。)と、第4級アンモニウムカチオン、又は第4級ホスホニウムカチオンからなる化合物。
入手容易性の観点から上記(1)が好ましく、安全性の観点から上記(2)が好ましい。
上述したイミノオキサジアジンジオン化反応触媒の配合量は、仕込んだジイソシアネートモノマーの質量に対して、好ましくは10質量ppm以上1000質量ppm以下である。
その下限値は、より好ましくは20質量ppmであり、さらに好ましくは40質量ppmであり、よりさらに好ましくは80質量ppmである。
その上限値は、より好ましくは800質量ppmであり、さらに好ましくは600質量ppmであり、よりさらに好ましくは500質量ppm以下である。
上述したイミノオキサジアジンジオン化反応触媒の配合量は、仕込んだジイソシアネートモノマーの質量に対して、好ましくは10質量ppm以上1000質量ppm以下である。
その下限値は、より好ましくは20質量ppmであり、さらに好ましくは40質量ppmであり、よりさらに好ましくは80質量ppmである。
その上限値は、より好ましくは800質量ppmであり、さらに好ましくは600質量ppmであり、よりさらに好ましくは500質量ppm以下である。
また、イミノオキサジアジンジオン化反応温度としては、好ましくは40℃以上120℃以下である。
その下限値は、より好ましくは50℃であり、さらに好ましくは55℃である。その上限値は、より好ましくは100℃であり、さらに好ましくは90℃であり、よりさらに好ましくは80℃である。
イミノオキサジアジンジオン化反応温度が40℃以上であることによって、反応速度を高く維持することが可能である傾向にある。イミノオキサジアジンジオン化反応温度が120℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
その下限値は、より好ましくは50℃であり、さらに好ましくは55℃である。その上限値は、より好ましくは100℃であり、さらに好ましくは90℃であり、よりさらに好ましくは80℃である。
イミノオキサジアジンジオン化反応温度が40℃以上であることによって、反応速度を高く維持することが可能である傾向にある。イミノオキサジアジンジオン化反応温度が120℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
ジイソシアネートモノマーからウレトジオン基を含有するポリイソシアネートを誘導するための触媒としては、特に限定されないが、例えば、第3ホスフィンである、トリ−n−ブチルホスフィン、トリ−n−オクチルホスフィン等のトリアルキルホスフィン;トリス−(ジメチルアミノ)ホスフィン等のトリス(ジアルキルアミノ)ホスフィン;シクロヘキシル−ジ−n−ヘキシルホスフィン等のシクロアルキルホスフィンが挙げられる。
上述したウレトジオン化反応触媒の多くは、同時にイソシアヌレート化反応も促進し、ウレトジオン基含有ポリイソシアネートに加えてイソシアヌレート基含有ポリイソシアネートを生成する。所望の転化率(ウレトジオン化反応で生成したポリイソシアネートの、仕込んだジイソシアネートモノマーに対する質量割合)になった時点で、特に限定されないが、例えば、リン酸、パラトルエンスルホン酸メチル等のウレトジオン化反応触媒の失活剤を添加してウレトジオン化反応を停止する。反応停止後、必要があれば、濾過する。
上述したウレトジオン化反応触媒の多くは、同時にイソシアヌレート化反応も促進し、ウレトジオン基含有ポリイソシアネートに加えてイソシアヌレート基含有ポリイソシアネートを生成する。所望の転化率(ウレトジオン化反応で生成したポリイソシアネートの、仕込んだジイソシアネートモノマーに対する質量割合)になった時点で、特に限定されないが、例えば、リン酸、パラトルエンスルホン酸メチル等のウレトジオン化反応触媒の失活剤を添加してウレトジオン化反応を停止する。反応停止後、必要があれば、濾過する。
また、上述したウレトジオン化反応触媒を用いることなく、ジイソシアネートモノマーを加熱することでウレトジオン基を得ることもできる。ウレトジオン化反応温度としては、好ましくは120℃以上であり、より好ましくは130以上170℃以下であり、さらに好ましくは140℃以上160℃以下である。
また、ウレトジオン化反応時間としては、好ましくは30分以上4時間以下であり、より好ましくは1以上3時間以下であり、さらに好ましくは1時間以上2時間以下である。
また、ウレトジオン化反応時間としては、好ましくは30分以上4時間以下であり、より好ましくは1以上3時間以下であり、さらに好ましくは1時間以上2時間以下である。
ジイソシアネートモノマーからアロファネート基を含有するポリイソシアネートを誘導するための触媒としては、特に限定されないが、例えば、錫、鉛、亜鉛、ビスマス、ジルコニウム、ジルコニル等のアルキルカルボン酸塩;2−エチルヘキサン酸錫、ジブチル錫ジラウレート等の有機錫化合物;2−エチルヘキサン酸鉛等の有機鉛化合物;2−エチルヘキサン酸亜鉛等の有機亜鉛化合物;2−エチルヘキサン酸ビスマス、2−エチルヘキサン酸ジルコニウム、2−エチルヘキサン酸ジルコニルが挙げられる。これらは、1種を単独又は2種以上を併用することができる。
また、上述したイソシアヌレート化反応触媒もアロファネート化反応触媒となり得る。上述したイソシアヌレート化反応触媒を用いて、アロファネート化反応を行なう場合は、イソシアヌレート基含有ポリイソシアネートも当然のことながら生成する。アロファネート化反応触媒として、上述したイソシアヌレート化反応触媒を用いて、アロファネート化反応とイソシアヌレート反応を行なうことが経済的生産上、好ましい。
上述したアロファネート化反応触媒の配合量は、仕込んだジイソシアネートモノマーの質量に対して、好ましくは10質量ppm以上1000質量ppm以下である。
その下限値は、より好ましくは20質量ppmであり、さらに好ましくは40質量ppmであり、よりさらに好ましくは80質量ppmである。
その上限値は、より好ましくは800質量ppmであり、さらに好ましくは600質量ppmであり、よりさらに好ましくは500質量ppm以下である。
その下限値は、より好ましくは20質量ppmであり、さらに好ましくは40質量ppmであり、よりさらに好ましくは80質量ppmである。
その上限値は、より好ましくは800質量ppmであり、さらに好ましくは600質量ppmであり、よりさらに好ましくは500質量ppm以下である。
また、アロファネート化反応温度としては、好ましくは40℃以上180℃以下である。その下限値は、より好ましくは60℃であり、さらに好ましくは80℃であり、よりさらに好ましくは100℃である。その上限値は、より好ましくは160℃であり、さらに好ましくは140℃である。
アロファネート化反応温度が40℃以上であることによって、反応速度を高く維持することが可能である傾向にある。アロファネート化反応温度が180℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
アロファネート化反応温度が40℃以上であることによって、反応速度を高く維持することが可能である傾向にある。アロファネート化反応温度が180℃以下であることによって、ポリイソシアネートの着色等を効果的に抑制できる傾向にある。
アロファネート基の形成に用いることのできるアルコールは、好ましくは炭素、水素及び酸素のみで形成されるアルコールであり、より好ましくはモノアルコールであり、さらに好ましくは分子量200以下のモノアルコールである。その具体的な化合物は、特に限定されないが、例えば、メタノール、エタノール、プロパノール、ブタノール、ペンタノール、ヘキサノール、ヘプタノール、オクタノール、ノナノール等のモノアルコール;エチレングリコール、1,3−ブタンジオール、ネオペンチルグリコール、2−エチルヘキサンジオール等のジオールが挙げられる。これらは1種を単独又は2種以上を併用してもよい。
上述したイソシアヌレート化反応、イミノオキサジアジンジオン化反応、ウレトジオン化反応、及びアロファネート化反応は、それぞれ逐次行なうこともできるし、そのいくつかを並行して行なうこともできる。好ましくはイソシアヌレート化反応を先行させて、その後、ウレトジオン化反応を行なう。より好ましくは、イソシアヌレート化反応を先行させて、その後、熱によるウレトジオン化反応を行なえば、製造工程を簡略化できる。
反応終了後の反応液から、未反応ジイソシアネートモノマーを薄膜蒸留、抽出等により除去し、本実施形態で用いられるポリイソシアネートを得ることができる。
反応終了後の反応液から、未反応ジイソシアネートモノマーを薄膜蒸留、抽出等により除去し、本実施形態で用いられるポリイソシアネートを得ることができる。
ジイソシアネートモノマーからビウレット基を含有するポリイソシアネートを誘導するためには、ビウレット結合を有するポリイソシアネートは、水、t−ブタノール又は尿素等のいわゆるビウレット化剤とジイソシアネートモノマーとを、(ビウレット化剤)/( ジイソシアネートモノマーのイソシアネート基)のモル比が約1/2 〜 約1/100となる条件で反応させた後、未反応のジイソシアネートモノマーを除去することで得ることができる。これらの技術に関しては、例えば、特開昭53 −106797号公報、特開昭55 − 11452号公報及び特開昭59−95259号公報等に開示されている。
ジイソシアネートモノマーからウレトンイミノ基を含有するポリイソシアネートを誘導する方法としては、例えば、前記イソシアヌレート化反応を実施した後、触媒を失活させ、その後に140〜160℃程度の温度で、数時間程度反応させることにより制御する方法や、1−ブチルホスホラン等のヘテロ環含有リン系化合物を触媒として、20〜80℃程度の温度で、数時間から数十時間程度反応させたポリイソシアネート組成物を一部混合する方法が挙げられる。上記方法の中でも、入手の容易さの観点から、前者のイソシアヌレート化反応を実施した後、触媒を失活させ、その後に140〜160℃程度の温度で数時間程度反応させる方法が好ましい。
得られたポリイソシアネートに対して、例えば、貯蔵時の着色を抑制する目的で、酸化防止剤や紫外線吸収剤を添加してもよい。酸化防止剤としては、例えば、2,6−ジ−t−ブチル−p―クレゾール等のヒンダードフェノール、紫外線吸収剤としては、例えば、ベンゾトリアゾール、ベンゾフェノンが挙げられる。これらは、1種を単独又は2種以上を併用してもよい。これらの添加量は、好ましくは10質量ppm以上500質量ppm以下である。
<その他構成成分>
〔多価活性水素化合物〕
本実施形態のポリアスパラティック塗料組成物は、アスパラギン酸エステル化合物(A)と、ポリイソシアネート組成物(B1)以外の樹脂成分として、さらに多価活性水素化合物を含んでも良い。
本実施形態で用いられる多価活性水素化合物としては、特に限定されないが、例えば、ポリオール、ポリアミン及びアルカノールアミンからなる群より選ばれる少なくとも1種を含むことが好ましく、その中でも、ポリオールを含むことがより好ましい。
〔多価活性水素化合物〕
本実施形態のポリアスパラティック塗料組成物は、アスパラギン酸エステル化合物(A)と、ポリイソシアネート組成物(B1)以外の樹脂成分として、さらに多価活性水素化合物を含んでも良い。
本実施形態で用いられる多価活性水素化合物としては、特に限定されないが、例えば、ポリオール、ポリアミン及びアルカノールアミンからなる群より選ばれる少なくとも1種を含むことが好ましく、その中でも、ポリオールを含むことがより好ましい。
ポリオールとしては、特に限定されないが、例えば、ポリエステルポリオール、アクリルポリオール、ポリエーテルポリオール、ポリオレフィンポリオール、フッ素ポリオール、ポリカーボネートポリオール、及びポリウレタンポリオールが挙げられる。上記に示したポリオールは、1種を単独で使用しても2種以上を併用しても構わない。
ポリエステルポリオールとしては、特に限定されないが、例えば、コハク酸、アジピン酸、セバシン酸、ダイマー酸、無水マレイン酸、無水フタル酸、イソフタル酸、及びテレフタル酸のカルボン酸からなる群より選ばれる1種又は2種以上の二塩基酸と、エチレングリコール、プロピレングリコール、ジエチレングリコール、ネオペンチルグリコール、トリメチロールプロパン、及びグリセリンからなる群より選ばれる1種又は2種以上の多価アルコールとの縮合反応によって得られるポリエステルポリオール、並びに、例えば多価アルコールを用いたε−カプロラクトンの開環重合により得られるポリカプロラクトン類が挙げられる。
アクリルポリオールとしては、特に限定されないが、例えば、ヒドロキシル基を有するエチレン性不飽和結合含有単量体の単独又は混合物と、これと共重合可能な他のエチレン性不飽和結合含有単量体の単独又は混合物と、を共重合させることにより得られるものが挙げられる。
ヒドロキシル基を有するエチレン性不飽和結合含有単量体としては、特に限定されないが、例えば、アクリル酸ヒドロキシエチル、アクリル酸ヒドロキシプロピル、アクリル酸ヒドロキシブチル、メタクリル酸ヒドロキシエチル、メタクリル酸ヒドロキシプロピル、及びメタクリル酸ヒドロキシブチルが挙げられる。好ましくは、アクリル酸ヒドロキシエチル、及びメタクリル酸ヒドロキシエチルである。
上記単量体と共重合可能な他のエチレン性不飽和結合含有単量体としては、特に限定されないが、例えば、アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル、アクリル酸イソプロピル、アクリル酸−n−ブチル、アクリル酸イソブチル、アクリル酸−n−ヘキシル、アクリル酸シクロヘキシル、アクリル酸−2−エチルヘキシル、アクリル酸ラウリル、アクリル酸ベンジル、アクリル酸フェニル等のアクリル酸エステル;メタクリル酸メチル、メタクリル酸エチル、メタクリル酸プロピル、メタクリル酸イソプロピル、メタクリル酸−n−ブチル、メタクリル酸イソブチル、メタクリル酸−n−ヘキシル、メタクリル酸シクロヘキシル、メタクリル酸−2−エチルヘキシル、メタクリル酸ラウリル、メタクリル酸ベンジル、メタクリル酸フェニル等のメタクリル酸エステル;アクリル酸、メタクリル酸、マレイン酸、イタコン酸等の不飽和カルボン酸;アクリルアミド、メタクリルアミド、N,N−メチレンビスアクリルアミド、ダイアセトンアクリルアミド、ダイアセトンメタクリルアミド、マレイン酸アミド、マレイミド等の不飽和アミド;メタクリル酸グリシジル、スチレン、ビニルトルエン、酢酸ビニル、アクリロニトリル、フマル酸ジブチル等のビニル系単量体;ビニルトリメトキシシラン、ビニルメチルジメトキシシラン、γ−(メタ)アクリロキシプロピルトリメトキシシラン等の加水分解性シリル基を有するビニル系単量体が挙げられる。
ポリエーテルポリオール類としては、特に限定されないが、例えば、多価ヒドロキシ化合物の単独又は混合物に、リチウム、ナトリウム、カリウム等の水酸化物;アルコラート、アルキルアミン等の強塩基性触媒を使用して、エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド、シクロヘキセンオキサイド、スチレンオキサイド等のアルキレンオキサイドの単独又は混合物を付加して得られるポリエーテルポリオール類;エチレンジアミン類等の多官能化合物にアルキレンオキサイドを反応させて得られるポリエーテルポリオール類;これらポリエーテル類を媒体としてアクリルアミド等を重合して得られるいわゆるポリマーポリオール類が挙げられる。
上記の多価ヒドロキシ化合物としては、
(1)ジグリセリン、ジトリメチロールプロパン、ペンタエリスリトール、ジペンタエリスリトール等、
(2)エリスリトール、D−トレイトール、L−アラビニトール、リビトール、キシリトール、ソルビトール、マンニトール、ガラクチトール、ラムニトール等の糖アルコール系化合物、
(3)アラビノース、リボース、キシロース、グルコース、マンノース、ガラクトース、フルクトース、ソルボース、ラムノース、フコース、リボデソース等の単糖類、
(4)トレハロース、ショ糖、マルトース、セロビオース、ゲンチオビオース、ラクトース、メリビオース等の二糖類、
(5)ラフィノース、ゲンチアノース、メレチトースなどの三糖類、
(6)スタキオース等の四糖類
が挙げられる。
(1)ジグリセリン、ジトリメチロールプロパン、ペンタエリスリトール、ジペンタエリスリトール等、
(2)エリスリトール、D−トレイトール、L−アラビニトール、リビトール、キシリトール、ソルビトール、マンニトール、ガラクチトール、ラムニトール等の糖アルコール系化合物、
(3)アラビノース、リボース、キシロース、グルコース、マンノース、ガラクトース、フルクトース、ソルボース、ラムノース、フコース、リボデソース等の単糖類、
(4)トレハロース、ショ糖、マルトース、セロビオース、ゲンチオビオース、ラクトース、メリビオース等の二糖類、
(5)ラフィノース、ゲンチアノース、メレチトースなどの三糖類、
(6)スタキオース等の四糖類
が挙げられる。
ポリオレフィンポリオールとしては、特に限定されないが、例えば、水酸基を2個以上有するポリブタジエン、水素添加ポリブタジエン、ポリイソプレン、水素添加ポリイソプレンが挙げられる。ポリオールの統計的1分子が持つ水酸基数(以下、「水酸基平均数」ともいう)は2以上であることが好ましい。ポリオールの水酸基平均数が2以上であることによって、得られる塗膜の架橋密度の低下を抑制することができる傾向にある。
フッ素ポリオールとは、分子内にフッ素を含むポリオールであり、例えば特開昭57−34107号公報、特開昭61−275311号公報で開示されているフルオロオレフィン、シクロビニルエーテル、ヒドロキシアルキルビニルエーテル、モノカルボン酸ビニルエステル等の共重合体が挙げられる。
ポリカーボネートポリオール類としては、特に限定されないが、例えば、ジメチルカーボネート等のジアルキルカーボネート;エチレンカーボネート等のアルキレンカーボネート;ジフェニルカーボネート等のジアリールカーボネート等の低分子カーボネート化合物;上述したポリエステルポリオールに用いられる低分子ポリオールとを、縮重合して得られるものが挙げられる。
ポリウレタンポリオールとしては、特に限定されないが、例えば、常法によりポリオールとポリイソシアネートとを反応させることにより得ることができる。カルボキシル基を含有しないポリオールとしては、例えば低分子量のものとして、エチレングリコール、プロピレングリコールが例示され、例えば高分子量のものとして、アクリルポリオール、ポリエステルポリオール、ポリエーテルポリオールが例示される。
上記に示したポリオールの樹脂あたりの水酸基価は、特に限定されないが、10mgKOH/樹脂g以上300mgKOH/樹脂g以下であることが好ましい。樹脂あたりの水酸基価が10mgKOH/樹脂g以上であることによって、架橋密度が減少することを抑制し、目的とする物性を十分に達成することができる傾向にある。樹脂あたりの水酸基価が300mgKOH/樹脂g以下であることによって、架橋密度が過度に増大することを抑制し、塗膜の機械強度を維持することができる傾向にある。
前記水酸基価は、JIS K1557に準拠して測定することができる。
上記で列挙したポリオールの中でも、アクリルポリオール、及びポリエステルポリオールが好ましい。ポリオールを用いる場合のポリアスパラティック塗料組成物において、イソシアネート基と水酸基との当量比は、好ましくは10:1〜1:10である。
前記水酸基価は、JIS K1557に準拠して測定することができる。
上記で列挙したポリオールの中でも、アクリルポリオール、及びポリエステルポリオールが好ましい。ポリオールを用いる場合のポリアスパラティック塗料組成物において、イソシアネート基と水酸基との当量比は、好ましくは10:1〜1:10である。
ポリアミンとしては、特に限定されないが、第一級アミノ基又は第二級アミノ基を1分子中に2個以上有するものが好ましく、その中でも、1分子中に3個以上有するものがより好ましい。
ポリアミンの具体例としては、特に限定されないが、例えば、エチレンジアミン、プロピレンジアミン、ブチレンジアミン、トリエチレンジアミン、ヘキサメチレンジアミン、4,4’−ジアミノジシクロヘキシルメタン、ピペラジン、2−メチルピペラジン、イソホロンジアミン等のジアミン類;ビスヘキサメチレントリアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン、ペンタメチレンヘキサミン、テトラプロピレンペンタミン等の3個以上のアミノ基を有する鎖状ポリアミン類;1,4,7,10,13,16−ヘキサアザシクロオクタデカン、1,4,7,10−テトラアザシクロデカン、1,4,8,12−テトラアザシクロペンタデカン、1,4,8,11−テトラアザシクロテトラデカン等の環状ポリアミン類が挙げられる。
ポリアミンの具体例としては、特に限定されないが、例えば、エチレンジアミン、プロピレンジアミン、ブチレンジアミン、トリエチレンジアミン、ヘキサメチレンジアミン、4,4’−ジアミノジシクロヘキシルメタン、ピペラジン、2−メチルピペラジン、イソホロンジアミン等のジアミン類;ビスヘキサメチレントリアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン、ペンタメチレンヘキサミン、テトラプロピレンペンタミン等の3個以上のアミノ基を有する鎖状ポリアミン類;1,4,7,10,13,16−ヘキサアザシクロオクタデカン、1,4,7,10−テトラアザシクロデカン、1,4,8,12−テトラアザシクロペンタデカン、1,4,8,11−テトラアザシクロテトラデカン等の環状ポリアミン類が挙げられる。
アルカノールアミンとは、1分子中に、アミノ基と水酸基を有する化合物である。アルカノールアミンとしては、特に限定されないが、例えば、モノエタノールアミン、ジエタノールアミン、アミノエチルエタノールアミン、N−(2−ヒドロキシプロピル)エチレンジアミン、モノ−、ジ−(n−又はイソ−)プロパノールアミン、エチレングリコール−ビス−プロピルアミン、ネオペンタノールアミン、及びメチルエタノールアミンが挙げられる。
〔その他成分〕
本発明形態のポリアスパラティック塗料組成物は、必要に応じて、既存のメラミン樹脂、エポキシ樹脂、ポリウレタン樹脂をさらに含んでもよい。また、上述したポリオールがカルボキシル基を有する場合には、オキサゾリン基含有化合物、カルボジイミド基含有化合物を配合することができる。また、上述したポリオールがカルボニル基を有する場合には、ヒドラジド基含有化合物、セミカルバジド基含有化合物を配合することができる。これらの化合物は1種を単独で配合するだけでなく、2種以上を併用して配合することもできる。
本発明形態のポリアスパラティック塗料組成物は、必要に応じて、既存のメラミン樹脂、エポキシ樹脂、ポリウレタン樹脂をさらに含んでもよい。また、上述したポリオールがカルボキシル基を有する場合には、オキサゾリン基含有化合物、カルボジイミド基含有化合物を配合することができる。また、上述したポリオールがカルボニル基を有する場合には、ヒドラジド基含有化合物、セミカルバジド基含有化合物を配合することができる。これらの化合物は1種を単独で配合するだけでなく、2種以上を併用して配合することもできる。
本実施形態のポリアスパラティック塗料組成物は、必要に応じて、ヒンダードフェノール等の酸化防止剤、ベンゾトリアゾール、ベンゾフェノン等の紫外線吸収剤;酸化チタン、カーボンブラック、インジゴ、キナクリドン、パールマイカ等の顔料;アルミ等の金属粉顔料;ヒドロキシエチルセルロース、尿素化合物、マイクロゲル等のレオロジーコントロール剤;錫化合物、亜鉛化合物、アミン化合物等の硬化促進剤をさらに含んでもよい。
<ポリアスパラティック塗料組成物の製造方法>
本実施形態のポリアスパラティック塗料組成物は、上述のアスパラギン酸エステル化合物(A)と、上述のポリイソシアネート組成物(B1)と、必要に応じて、その他の構成成分等とを、公知の方法を用いて、混合することで得られる。
本実施形態のポリアスパラティック塗料組成物は、上述のアスパラギン酸エステル化合物(A)と、上述のポリイソシアネート組成物(B1)と、必要に応じて、その他の構成成分等とを、公知の方法を用いて、混合することで得られる。
本発明の第2の実施形態のポリアスパラティック塗料組成物は、(A)下記一般式(I)で示されるアスパラギン酸エステル化合物と、(B2)下記一般式(VIII)で示されるトリイソシアネート化合物(b1)を含むポリイソシアネート組成物とを含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記トリイソシアネート化合物(b1)の含有量が20質量%以上100質量%以下である。
本実施形態において、第1の実施形態と同じ構成についてはその説明を省略する。
前記ポリイソシアネート組成物(B2)の総量に対する前記トリイソシアネート化合物(b1)の含有量が20質量%以上100質量%以下である。
本実施形態において、第1の実施形態と同じ構成についてはその説明を省略する。
式(I)中、X、n、R1及びR2は第1の実施形態において記載の通りである。
式(VIII)中、複数あるY1は、それぞれ独立に、単結合、又は、エステル構造及びエーテル構造からなる群より選択される1種以上を含んでもよい炭素数1〜20の2価の炭化水素基である。複数あるY1は、それぞれ同一であってもよく異なっていてもよい。R3は、水素原子又は炭素数1〜12の1価の炭化水素基である。
[トリイソシアネート化合物(b1)]
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B2)は、上記一般式(VIII)で表されるトリイソシアネート化合物(b1)を含む。
(Y1)
一般式(VIII)中、複数あるY1は、それぞれ独立に、単結合、又は、エステル構造及びエーテル構造からなる群より選択される1種以上を含んでもよい炭素数1〜20の2価の炭化水素基である。複数あるY1は、それぞれ同一であってもよく異なっていてもよい。
前記炭素数1〜20の2価の炭化水素基としては、脂肪族基であってもよく、芳香族基であってもよい。前記脂肪族基は、直鎖状、分岐状又は環状のいずれであってもよい。 前記直鎖状又は分岐状の脂肪族基としては、例えば、アルカンジイル基(アルキレン基)、アルキリデン基等が挙げられる。
前記環状の脂肪族基としては、例えば、シクロアルキレン基等が挙げられる。
前記芳香族基としては、例えば、フェニレン基等のアリーレン基が挙げられる。
中でも、前記炭素数1〜20の2価の炭化水素基としては、アルキレン基であることが好ましい。
前記アルキレン基としては、例えば、メチレン基、ジメチレン基、トリメチレン基、テトラメチレン基、エチレン基、n−プロピレン基、n−ブチレン基等が挙げられる。
また、Y1における前記エステル構造及びエーテル構造からなる群より選択される1種以上を含んでもよい炭素数1〜20の2価の炭化水素基としては、例えば、下記一般式(VIII−1)で表される基(以下、「基(VIII−1)」と称する場合がある」)が挙げられる。
*1−(CH2)n1−Y2−(CH2)n2−*2 ・・・(VIII−1)
基(VIII−1)において、*1は上記一般式(VIII)中のCとの結合手を表し、*2が上記一般式(VIII)中のNCOのNとの結合手を表す。また、n1とn2は、1≦n1+n2≦20を満たす整数である。すなわち、n1及びn2の両方とも0になることはなく、n2が1以上であることが好ましい。
n1は、0〜20の整数であり、0〜19の整数であることが好ましく、0〜4の整数がより好ましく、0〜2の整数がさらに好ましい。n2は、0〜20の整数であり、1〜20の整数であることが好ましく、1〜4の整数がより好ましく、1または2であることがさらに好ましい。n1及びn2の組み合わせとしては、例えば、n1=0、n2=2の組み合わせ、n1=2、n2=2の組み合わせが好ましい。
基(VIII−1)において、Y2は、エステル構造(−C(=O)−O−)又はエーテル構造(−O−)である。中でも、反応速度が上がることから、Y2はエステル構造であることが好ましい。
また、複数あるY1のうち少なくとも1つが、脂肪族基及び芳香族基からなる群の1種以上を有する場合、ポリイソシアネート組成物をより低粘度とすることができ、本実施形態のポリアスパラティック塗料組成物から得られた塗膜の耐候性をより良好とすることができる。
また、複数あるY1のうち少なくとも1つが、エステル構造を有する場合、ポリイソシアネート組成物の耐熱性をより向上することができ、イソシアネート基の反応性をより高めることができる。
また、複数あるY1のうちの少なくとも1つが炭化水素基のみからなる場合(好ましくは、複数あるY1のうちのすべてが炭化水素基のみからなる場合)、ポリイソシアネート組成物の耐加水分解性をより向上することができる。
(R3)
R3は、水素原子、又は、炭素数1〜12の1価の炭化水素基である。R3における炭化水素基としては、特に限定されず、アルキル基、アルケニル基、アルキニル基等が挙げられる。中でも、R3としては、水素原子が好ましい。
本実施形態において、複数あるY1のうち少なくとも1つが、脂肪族基及び芳香族基からなる群より選択される1種以上を有する場合、トリイソシアネート化合物(II)で好ましいものとして具体的には、例えば、特公昭63−15264号公報(参考文献1)に開示されている4−イソシアネートメチル−1,8−オクタメチレンジイソシアネート(以下、「NTI」と称する、分子量251)、特開昭57−198760号公報(参考文献2)に開示されている1,3,6−ヘキサメチレントリイソシアネート(以下、「HTI」と称する、分子量209)、特公平4−1033号公報(参考文献3)に開示されているビス(2−イソシアナトエチル)2−イソシアナトグルタレート(以下、「GTI」と称する、分子量311)、特開昭53−135931号公報(参考文献4)に開示されているリジントリイソシアネート(以下、「LTI」と称する、分子量267)等が挙げられる。
中でも、イソシアネート基の反応性をより向上できる観点から、複数あるY1のうち少なくとも1つが、脂肪族基及び芳香族基からなる群より選択される1種以上を有する場合、トリイソシアネート化合物(b1)としては、NTI、GTI又はLTIが好ましく、NTI又はLTIがより好ましく、LTIがさらに好ましい。
本実施形態において、複数あるY1のうち少なくとも1つが、エステル構造を有する場合、トリイソシアネート化合物(b1)で好ましいものとして具体的には、例えば、特公平4−1033号公報(参考文献3)に開示されているGTI(分子量311)、特開昭53−135931号公報(参考文献4)に開示されているLTI(分子量267)等が挙げられる。
本実施形態において、複数あるY1のうちの少なくとも1つが炭化水素基のみからなる場合、トリイソシアネート化合物(b1)で好ましいものとして具体的には、例えば、特公昭63−15264号公報(参考文献1)に開示されているNTI(分子量251)、特開昭57−198760号公報(参考文献2)に開示されているHTI(分子量209)等が挙げられる。
(トリイソシアネート化合物(b1)の含有量)
本実施形態において、ポリイソシアネート組成物(B2)の総量に対する、トリイソシアネート化合物(b1)の含有量の下限値は、20質量%以上であり、40質量%以上であることが好ましく、60質量%以上であることがより好ましく、80質量%以上であることがさらに好ましい。ポリイソシアネート組成物(B2)の総量に対する、トリイソシアネート化合物(b1)の含有量が上記下限値以上であることにより、本実施形態のポリアスパラティック塗料組成物を硬化させて得られる塗膜の硬度を向上させることができる。
一方、ポリイソシアネート組成物(B2)の総量に対する、トリイソシアネート化合物(b1)の含有量の上限値は、特別な限定はなく、例えば、100質量%以下であってもよい。
(トリイソシアネート化合物(b1)の分子量)
本実施形態において、トリイソシアネート化合物(b1)の分子量の下限値は、139以上であることが好ましく、150以上であることがより好ましく、180以上がさらに好ましく、200以上が特に好ましい。
一方、トリイソシアネート化合物(b1)の分子量の上限値は、1000以下であることが好ましく、800以下であることがより好ましく、600以下であることがさらに好ましく、400以下であることが特に好ましい。
すなわち、トリイソシアネート化合物(b1)の分子量は、139以上1000以下であること好ましく、150以上800以下であることがより好ましく、180以上600以下であることがさらに好ましく、200以上400以下であることが特に好ましい。
トリイソシアネート化合物(b1)の分子量が上記下限値以上であることにより、結晶性をより抑制することができ、上記上限値以下であることにより、低粘度化をより達成することができる。
(トリイソシアネート化合物(b1)の製造方法)
本実施形態において、ポリイソシアネート組成物(B2)に含まれるトリイソシアネート化合物(b1)は、例えば、アミノ酸誘導体、エーテルアミン及びアルキルトリアミン等のアミンをイソシアネート化して得ることができる。
前記アミノ酸誘導体としては、例えば2,5−ジアミノ吉草酸、2,6−ジアミノヘキサン酸、アスパラギン酸、グルタミン酸等が挙げられる。これらアミノ酸誘導体はジアミンモノカルボン酸又はモノアミンジカルボン酸であるため、カルボキシ基を、例えばエタノールアミン等のアルカノールアミンでエステル化することで、エステル構造を有するトリアミンとすることができる。得られたエステル構造を有するトリアミンは、アミンのホスゲン化等により、エステル構造を含むトリイソシアネート化合物とすることができる。
前記エーテルアミンとしては、例えば、ポリオキシアルキレントリアミンである三井化学ファイン社の商品名「D403」等が挙げられる。これらエーテルアミンはトリアミンであり、アミンのホスゲン化等により、エーテル構造を含むトリイソシアネート化合物とすることができる。
前記アルキルトリアミンとしては、例えば、トリイソシアナトノナン(4−アミノメチル−1,8−オクタンジアミン)等が挙げられる。これらアルキルトリアミンはトリアミンであり、アミンのホスゲン化等により、炭化水素のみを含むトリイソシアネート化合物とすることができる。
[ポリイソシアネート(b2)]
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B2)は、上述のトリイソシアネート化合物(b1)以外に、さらに、脂肪族ジイソシアネート及び脂環式ジイソシアネートからなる群より選択される1種以上のジイソシアネートから得られるポリイソシアネート(b2)を含んでいてもよい。なお、ここでいう「ジイソシアネートから得られるポリイソシアネート」とは、ジイソシアネートを複数結合させて得られる複数のイソシアネート基を有する反応物(ポリイソシアネート)を意味する。
本実施形態で用いられる脂肪族ジイソシアネート及び脂環式ジイソシアネートは、第1の実施形態と同様のものを使用することができる。
(ポリイソシアネート(b2)の含有量)
本実施形態においてポリイソシアネート組成物(B2)の総量に対する、ポリイソシアネート(b2)の含有量の上限値は、80質量%以下であることが好ましく、60質量%以下であることがより好ましく、40質量%以下であることがより更に好ましく、20質量%以下であることがよりさらに好ましい。
ポリイソシアネート(b2)の含有量が上記上限値以下であることによって、本実施形態のポリアスパラティック塗料組成物を硬化させて得られる塗膜の硬度を向上させることができる。
一方、ポリイソシアネート組成物(B2)の総量に対する、ポリイソシアネート(b2)の含有量の下限値は、特別な限定はなく、例えば、0質量%以上であってもよい。
[ポリイソシアネート(b2)の製造方法]
本実施形態におけるポリイソシアネート(b2)は、例えば、イソシアヌレート基を形成するイソシアヌレート化反応、イミノオキサジアジンジオン基を形成するイミノオキサジアジンジオン化反応、ウレトジオン基を形成するウレトジオン化反応、アロファネート基を形成するアロファネート化反応、ビウレット基を形成するビウレット化反応、及び/又は、ウレトンイミノ基を形成するウレトンイミノ化反応を、過剰のジイソシアネート存在下で一度に実施して、反応終了後に、未反応のジイソシアネートを除去して得ることができる。すなわち、上記反応により得られるポリイソシアネートは、上述のジイソシアネートが複数結合したものであり、且つ、イソシアヌレート基、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基、ビウレット基、及びウレトンイミノ基からなる群から選択される1種類以上を有する反応物である。
また、上記の反応を別々に行ない、それぞれ得たポリイソシアネートを特定比率で混合してもよい。
中でも、製造の簡便さからは、上記反応を一度に行いポリイソシアネートを得ることが好ましく、各官能基のモル比を自由に調整する観点からは、別々に製造した後に混合することが好ましい。
ポリイソシアネートにおける各官能基のモル比については、第1の実施形態と同程度であることが好ましい。
<ポリイソシアネート組成物(B2)の物性>
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B2)の物性(イソシアネート含有量、粘度、数平均分子量、イソシアネート基の平均数)は、第1の実施形態と同程度であることが好ましい。
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B2)の物性(イソシアネート含有量、粘度、数平均分子量、イソシアネート基の平均数)は、第1の実施形態と同程度であることが好ましい。
<その他構成成分> 前記第1の実施形態と同様のものを配合することができる。
<ポリアスパラティック塗料組成物の製造方法>
本実施形態のポリアスパラティック塗料組成物は、上述の(A)アスパラギン酸エステル化合物(I)と、上述のトリイソシアネート化合物(b1)を含むポリイソシアネート組成物(B2)と、必要に応じて、その他樹脂成分等とを、公知の方法を用いて、混合することで得られる。
本発明の第3の実施形態のポリアスパラティック塗料組成物は、(A)下記式(I)で表されるアスパラギン酸エステル化合物と、(B3)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含み、ポリイソシアネート組成物(B3)の総量に対するウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上30.0質量%以下であるポリイソシアネート組成物、とを含む。
式(I)中、X、n、R1及びR2は第1の実施形態において記載の通りである。
本実施形態において、第1または第2の実施形態と同じ構成についてはその説明を省略する。
本実施形態において、第1または第2の実施形態と同じ構成についてはその説明を省略する。
〔ポリイソシアネート組成物(B3)〕
本実施形態で用いられる(B3)ポリイソシアネート組成物は、脂肪族及び/又は脂環族ジイソシアネートモノマーからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含み、ウレトジオン2量体とモノアルコールアロファネート体の、(B3)ポリイソシアネート組成物の総量に対する含有量が0.2質量%以上30.0質量%以下である。本実施形態のポリイソシアネート組成物(B3)は、好ましくはイソシアヌレート基を含む。
本実施形態において、2官能ウレタンアダクトとは、ジオール1分子とジイソシアネートモノマー2分子とがウレタン結合を介して結合した構造の化合物を指す。
本実施形態で用いられる(B3)ポリイソシアネート組成物は、脂肪族及び/又は脂環族ジイソシアネートモノマーからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含み、ウレトジオン2量体とモノアルコールアロファネート体の、(B3)ポリイソシアネート組成物の総量に対する含有量が0.2質量%以上30.0質量%以下である。本実施形態のポリイソシアネート組成物(B3)は、好ましくはイソシアヌレート基を含む。
本実施形態において、2官能ウレタンアダクトとは、ジオール1分子とジイソシアネートモノマー2分子とがウレタン結合を介して結合した構造の化合物を指す。
本実施形態で用いられるポリイソシアネート組成物(B3)における、ウレトジオン2量体とモノアルコールアロファネート体の、(B3)ポリイソシアネート組成物の総量に対する含有量は、0.2質量%以上30.0質量%以下である。好ましくは0.3質量%以上25.0質量%以下であり、より好ましくは0.4質量%以上20.0質量%以下であり、さらに好ましくは0.5質量%以上15.0質量%以下である。
ウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上であることによって、ポリイソシアネート組成物(B3)がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
ウレトジオン2量体とモノアルコールアロファネート体の含有量が30.0質量%以下であることによって、乾燥性をより維持すること及びポリアスパラティック塗料組成物を使用した塗膜の耐薬品性を向上させることができる傾向にある。
ウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上であることによって、ポリイソシアネート組成物(B3)がハイソリッド処方や無溶剤処方に適した低粘度を発現することができる傾向にある。
ウレトジオン2量体とモノアルコールアロファネート体の含有量が30.0質量%以下であることによって、乾燥性をより維持すること及びポリアスパラティック塗料組成物を使用した塗膜の耐薬品性を向上させることができる傾向にある。
<ポリイソシアネート組成物(B3)の物性>
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B3)の物性(イソシアネート含有量、粘度、数平均分子量、イソシアネート基平均数)は、第1の実施形態と同程度であることが好ましい。
本実施形態のポリアスパラティック塗料組成物に含まれるポリイソシアネート組成物(B3)の物性(イソシアネート含有量、粘度、数平均分子量、イソシアネート基平均数)は、第1の実施形態と同程度であることが好ましい。
本実施形態で用いられるポリイソシアネート組成物(B3)におけるジイソシアネートモノマー質量濃度は、ポリイソシアネート組成物(B3)の総量(100質量%)に対して、好ましくは1.0質量%以下であり、より好ましくは0.5質量%以下であり、さらに好ましくは0.3質量%以下である。
ジイソシアネートモノマー質量濃度が1.0質量%以下であることによって、乾燥性をより維持することができる傾向にある。ジイソシアネートモノマー質量濃度は、後述する実施例に記載の方法によって測定することができる。
〔ジイソシアネートモノマー〕
本実施形態で用いられるジイソシアネートモノマーは、脂肪族及び/又は脂環族ジイソシアネートからなる群より選択され、第1の実施形態と同様のものを使用することができる。
〔ジオール〕
本実施形態で用いられるジオールは、特に限定されないが、例えば、2価の脂肪族、脂環族、芳香族アルコールが挙げられ、具体的には、エチレングリコール、プロパンジオール、1,4−ブタンジオール、1,3−ブタンジオール、1,6−ヘキサンジオール、1,4−ヘキサンジオール、1,6−シクロヘキサンジオール、1,4−シクロヘキサンジオール、メチルペンタンジオール、シクロヘキサンジメタノール、メチルペンタンジオール、ネオペンチルグリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、水添ビスフェノールA等が挙げられる。また、上述したジオールを原料としたポリエステルポリオール、ポリプロピレングリコール、ポリエチレングリコール、ポリテトラエチレングリコール等の2価アルコールであってもよい。
〔ポリイソシアネート組成物(B3)の製造方法〕
本実施形態で用いられるポリイソシアネート組成物(B3)の製造方法を説明する。本実施形態で用いられる2官能ウレタンアダクトは、過剰のジイソシアネートモノマー存在下でジオールとのウレタン基を形成するウレタン化反応終了後に、未反応のジイソシアネートモノマーを除去して得ることができる。
ウレタン化反応温度としては、好ましくは50℃以上160℃以下であり、より好ましくは60℃以上120℃以下である。ウレタン化反応温度が160℃以下であることによって、ポリイソシアネート組成物の着色等を効果的に抑制できる傾向にある。また、ウレタン化反応時間としては、好ましくは30分以上4時間以下であり、より好ましくは1時間以上3時間以下であり、さらに好ましくは1時間以上2時間以下である。
ジイソシアネートモノマーとジオールとの仕込み比であるイソシアネート基と水酸基との当量比(イソシアネート基/水酸基)は、好ましくは2/1〜50/1である。当量比が2/1以上であることによって、ポリイソシアネート組成物(B3)がハイソリッド処方や無溶剤処方により適した低粘度を発現することができる傾向にある。当量比が50/1以下であることによって、2官能ウレタンアダクトの収率をより高められる傾向にある。
本実施形態で用いられるウレトジオン2量体は、後述するウレトジオン化反応により、ウレトジオン基を形成し、ウレトジオン2量体の質量%を調整することが挙げられる。
本実施形態で用いられるモノアルコールアロファネートは、後述するアロファネート化反応により、アロファネート基を形成し、モノアルコールアロファネートの質量%を調整することが挙げられる。
また、本実施形態で用いられるポリイソシアネート組成物は、第1の実施形態と同様に、イソシアヌレート基を形成するイソシアヌレート化反応、イミノオキサジアジンジオン基を形成するイミノオキサジアジンジオン化反応、ウレトジオン基を形成するウレトジオン化反応、及びアロファネート基を形成するアロファネート化反応を、過剰のジイソシアネートモノマー存在下で一度に実施して、反応終了後に、未反応のジイソシアネートモノマーを除去して得ることができる。また、上記の反応を別々に行ない、それぞれ得たポリイソシアネートを特定比率で混合してもよい。ここで、製造の簡便さからは、上記反応を一度に行ないポリイソシアネートを得ることが好ましく、各官能基のモル比を自由に調整する観点からは、別々に製造した後に混合することが好ましい。
<その他構成成分> 前記第1の実施形態と同様のものを配合することができる。
<ポリアスパラティック塗料組成物の製造方法>
本実施形態のポリアスパラティック塗料組成物は、上述の(A)アスパラギン酸エステル化合物(I)と、上述のポリイソシアネート組成物(B3)と、必要に応じて、その他樹脂成分等とを、公知の方法を用いて、混合することで得られる。
<用途>
上述した実施形態のポリアスパラティック塗料組成物は、ロール塗装、カーテンフロー塗装、スプレー塗装、静電塗装、ベル塗装、浸漬、ローラー塗装、刷毛塗装等によって、鋼板や表面処理鋼板等の金属、プラスチック、無機材料等のセラミック、ガラス、コンクリートに対して、プライマー、中塗り、又は上塗りとして好適に使用される。当該ポリアスパラティック塗料組成物は、美粧性、耐候性、耐酸性、防錆性、耐チッピング性、密着性等を付与するために好適に用いられる。また、当該ポリアスパラティック塗料組成物は、接着剤、粘着剤、エラストマー、フォーム、表面処理剤等としても有用である。
上述した実施形態のポリアスパラティック塗料組成物は、ロール塗装、カーテンフロー塗装、スプレー塗装、静電塗装、ベル塗装、浸漬、ローラー塗装、刷毛塗装等によって、鋼板や表面処理鋼板等の金属、プラスチック、無機材料等のセラミック、ガラス、コンクリートに対して、プライマー、中塗り、又は上塗りとして好適に使用される。当該ポリアスパラティック塗料組成物は、美粧性、耐候性、耐酸性、防錆性、耐チッピング性、密着性等を付与するために好適に用いられる。また、当該ポリアスパラティック塗料組成物は、接着剤、粘着剤、エラストマー、フォーム、表面処理剤等としても有用である。
〔塗膜、塗装物品〕
本実施形態の塗膜は、上述した実施形態のポリアスパラティック塗料組成物によって形成される。また、本実施形態の塗装物品は、本実施形態の塗膜を備える。特に限定されないが、例えば、本実施形態のポリアスパラティック塗料組成物を、ロール塗装、カーテンフロー塗装、スプレー塗装、静電塗装、ベル塗装、浸漬、ローラー塗装、刷毛塗装等によって塗装後、常温乾燥又は焼付け工程を経ることで、塗膜を形成することができる。
本実施形態の塗膜は、上述した実施形態のポリアスパラティック塗料組成物によって形成される。また、本実施形態の塗装物品は、本実施形態の塗膜を備える。特に限定されないが、例えば、本実施形態のポリアスパラティック塗料組成物を、ロール塗装、カーテンフロー塗装、スプレー塗装、静電塗装、ベル塗装、浸漬、ローラー塗装、刷毛塗装等によって塗装後、常温乾燥又は焼付け工程を経ることで、塗膜を形成することができる。
以下、実施例によって本実施形態を更に詳細に説明するが、本実施形態はこれらの実施例に限定されるものではない。以下に、各種物性の測定及び各種評価の方法について説明する。なお、特に明記しない場合は、「部」及び「%」は、「質量部」及び「質量%」を意味する。
(物性1)NCO含有量(質量%)
ポリイソシアネートのNCO含有量(イソシアネート含有量、質量%)は次のように測定した。三角フラスコに製造例で製造したポリイソシアネート1〜3gを精秤(Wg)、トルエン20mLを添加し、ポリイソシアネートを完全に溶解した。その後、2規定のジ−n−ブチルアミンのトルエン溶液10mLを添加し、完全に混合後、15分間室温放置した。さらに、この溶液にイソプロピルアルコール70mLを加えて、完全混合した。この溶液を1規定塩酸溶液(ファクターF)で、指示薬を用いて滴定して、滴定値V2mLを得た。同様の滴定操作についてポリイソシアネートを用いないで行ない、滴定値V1mLを得た。得られた滴定値V2mLおよび滴定値V1mLから、ポリイソシアネートのNCO含有量を、下記式に基づいて算出した。
NCO含有量=(V1−V2)×F×42/(W×1000)×100
ポリイソシアネートのNCO含有量(イソシアネート含有量、質量%)は次のように測定した。三角フラスコに製造例で製造したポリイソシアネート1〜3gを精秤(Wg)、トルエン20mLを添加し、ポリイソシアネートを完全に溶解した。その後、2規定のジ−n−ブチルアミンのトルエン溶液10mLを添加し、完全に混合後、15分間室温放置した。さらに、この溶液にイソプロピルアルコール70mLを加えて、完全混合した。この溶液を1規定塩酸溶液(ファクターF)で、指示薬を用いて滴定して、滴定値V2mLを得た。同様の滴定操作についてポリイソシアネートを用いないで行ない、滴定値V1mLを得た。得られた滴定値V2mLおよび滴定値V1mLから、ポリイソシアネートのNCO含有量を、下記式に基づいて算出した。
NCO含有量=(V1−V2)×F×42/(W×1000)×100
(物性2)粘度(mPa.s)
ポリイソシアネートの粘度は、E型粘度計(商品名:RE−85R、東機産業社製)を用いて25℃で測定した。測定に際しては、標準ローター(1°34’×R24)を用いた。回転数は、以下の通りで設定した。
100r.p.m.(128mPa.s未満の場合)
50r.p.m.(128mPa.s以上256mPa.s未満の場合)
20r.p.m.(256mPa.s以上640mPa.s未満の場合)
10r.p.m.(640mPa.s以上1280mPa.s未満の場合)
5r.p.m.(1280mPa.s以上2560mPa.s未満の場合)
2.5r.p.m.(2560mPa.s以上5184mPa.s未満の場合)
1.0r.p.m.( 5184mPa.s以上12960mPa.s未満の場合)
0.5r.p.m.(12960mPa.s以上25920mPa.s未満の場合)
ポリイソシアネートの粘度は、E型粘度計(商品名:RE−85R、東機産業社製)を用いて25℃で測定した。測定に際しては、標準ローター(1°34’×R24)を用いた。回転数は、以下の通りで設定した。
100r.p.m.(128mPa.s未満の場合)
50r.p.m.(128mPa.s以上256mPa.s未満の場合)
20r.p.m.(256mPa.s以上640mPa.s未満の場合)
10r.p.m.(640mPa.s以上1280mPa.s未満の場合)
5r.p.m.(1280mPa.s以上2560mPa.s未満の場合)
2.5r.p.m.(2560mPa.s以上5184mPa.s未満の場合)
1.0r.p.m.( 5184mPa.s以上12960mPa.s未満の場合)
0.5r.p.m.(12960mPa.s以上25920mPa.s未満の場合)
(物性3)数平均分子量
ポリイソシアネートの数平均分子量は、下記の装置を用いたゲルパーミエーションクロマトグラフ(以下、「GPC」と略す。)測定によるポリスチレン基準の数平均分子量で求めた。
ポリイソシアネートの数平均分子量は、下記の装置を用いたゲルパーミエーションクロマトグラフ(以下、「GPC」と略す。)測定によるポリスチレン基準の数平均分子量で求めた。
装置:東ソー社製「HLC−8120GPC」(商品名)
カラム:東ソー社製「TSKgel SuperH1000」(商品名)×1本
「TSKgel SuperH2000」(商品名)×1本
「TSKgel SuperH3000」(商品名)×1本
キャリアー:テトラハイドロフラン
検出方法:示差屈折計
カラム:東ソー社製「TSKgel SuperH1000」(商品名)×1本
「TSKgel SuperH2000」(商品名)×1本
「TSKgel SuperH3000」(商品名)×1本
キャリアー:テトラハイドロフラン
検出方法:示差屈折計
(物性4)イソシアネート基平均数
ポリイソシアネートのイソシアネート基平均数は、(物性1)NCO含有量と(物性3)数平均分子量とから下記式に基づいて算出した。
イソシアネート基平均数=数平均分子量×NCO含有量/100/42
ポリイソシアネートのイソシアネート基平均数は、(物性1)NCO含有量と(物性3)数平均分子量とから下記式に基づいて算出した。
イソシアネート基平均数=数平均分子量×NCO含有量/100/42
(物性5)ジイソシアネートモノマー質量濃度(質量%)
ポリイソシアネートのジイソシアネート質量濃度は、次のように求めた。最初に、20mLサンプル瓶をデジタル天秤に乗せ試料を約1g精秤した。次に、ニトロベンゼン(内部標準液)を0.03〜0.04g加え精秤した。最後に、酢酸エチルを約9mL加えた後、蓋をしっかりして十分に混合し、サンプルを調製した。調製したサンプルを以下の条件で、ガスクロマトグラフィー分析し、定量した。
ポリイソシアネートのジイソシアネート質量濃度は、次のように求めた。最初に、20mLサンプル瓶をデジタル天秤に乗せ試料を約1g精秤した。次に、ニトロベンゼン(内部標準液)を0.03〜0.04g加え精秤した。最後に、酢酸エチルを約9mL加えた後、蓋をしっかりして十分に混合し、サンプルを調製した。調製したサンプルを以下の条件で、ガスクロマトグラフィー分析し、定量した。
装置:SHIMADZU社製「GC−8A」
カラム:信和化工社製「Silicone OV−17」
カラムオーブン温度:120℃
インジェクション/ディテクター温度:160℃
カラム:信和化工社製「Silicone OV−17」
カラムオーブン温度:120℃
インジェクション/ディテクター温度:160℃
(物性6)各モル比
Bruker社製Biospin Avance600(商品名)を用いた、13C−NMRの測定によって、イソシアヌレート基、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基、ビウレット基、及びウレトンイミノ基のモル比を求めた。
具体的な測定条件は以下の通りであった。
Bruker社製Biospin Avance600(商品名)を用いた、13C−NMRの測定によって、イソシアヌレート基、イミノオキサジアジンジオン基、ウレトジオン基、アロファネート基、ビウレット基、及びウレトンイミノ基のモル比を求めた。
具体的な測定条件は以下の通りであった。
13C−NMR装置:AVANCE600(ブルカー社製)
クライオプローブ(ブルカー社製)
Cryo Probe
CPDUL
600S3−C/H−D−05Z
共鳴周波数:150MHz
濃度:60wt/vol%
シフト基準:CDCl3(77ppm)
積算回数:10000回
パルスプログラム:zgpg30(プロトン完全デカップリング法、待ち時間2sec)
クライオプローブ(ブルカー社製)
Cryo Probe
CPDUL
600S3−C/H−D−05Z
共鳴周波数:150MHz
濃度:60wt/vol%
シフト基準:CDCl3(77ppm)
積算回数:10000回
パルスプログラム:zgpg30(プロトン完全デカップリング法、待ち時間2sec)
以下のシグナルの積分値を、測定している炭素の数で除して、その値から各モル比を求めた。
イソシアヌレート基のモル量(モル%、「A」で示す。):148.6ppm付近:積分値÷3
イミノオキサジアジンジオン基のモル量(モル%、「B」で示す。):144.6ppm付近:積分値÷1
ウレトジオン基のモル量(モル%、「C」で示す。):157.5ppm付近:積分値÷2
アロファネート基のモル量(モル%、「D」で示す。):154ppm付近:積分値÷1
ビウレット基のモル量(モル%、「E」で示す。):156ppm付近:積分値÷2
ウレトンイミノ基のモル量(モル%、「F」で示す。):159.5ppm付近:積分値÷1
イミノオキサジアジンジオン基のモル量(モル%、「B」で示す。):144.6ppm付近:積分値÷1
ウレトジオン基のモル量(モル%、「C」で示す。):157.5ppm付近:積分値÷2
アロファネート基のモル量(モル%、「D」で示す。):154ppm付近:積分値÷1
ビウレット基のモル量(モル%、「E」で示す。):156ppm付近:積分値÷2
ウレトンイミノ基のモル量(モル%、「F」で示す。):159.5ppm付近:積分値÷1
求めた各モル比は、以下の6種であり、それぞれについてポリイソシアネート組成物を試料とした値を求めた。
モル比x=(B+C+D)/(A+B+C+D)
モル比b=B/(A+B+C+D)
モル比c=C/(A+B+C+D)
モル比d=D/(A+B+C+D)
モル比e-=E/A
モル比f=F/(A+B+C+D)
モル比b=B/(A+B+C+D)
モル比c=C/(A+B+C+D)
モル比d=D/(A+B+C+D)
モル比e-=E/A
モル比f=F/(A+B+C+D)
(物性7、物性8)ウレトジオン2量体、モノアルコールアロファネート体の含有量
前記(物性3)数平均分子量に示すGPC測定において、ウレトジオン2量体、モノアルコールアロファネート体の含有量を定量した。
原料として用いたジイソシアネートの2倍の分子量に相当するピーク面積%をウレトジオン2量体の含有量とした。
原料として用いたジイソシアネートの2倍の分子量とモノアルコールに相当するピーク面積%をモノアルコールアロファネート体の含有量とした。
前記(物性3)数平均分子量に示すGPC測定において、ウレトジオン2量体、モノアルコールアロファネート体の含有量を定量した。
原料として用いたジイソシアネートの2倍の分子量に相当するピーク面積%をウレトジオン2量体の含有量とした。
原料として用いたジイソシアネートの2倍の分子量とモノアルコールに相当するピーク面積%をモノアルコールアロファネート体の含有量とした。
(評価1)ハイソリッド性
ポリイソシアネート組成物の25℃における粘度から、下記の基準でハイソリッド性を評価した。
◎:500mPa.s未満
○:500mPa.s以上1000mPa.s未満
△:1000mPa.s以上1200mPa.s未満
×:1200mPa.s以上
ポリイソシアネート組成物の25℃における粘度から、下記の基準でハイソリッド性を評価した。
◎:500mPa.s未満
○:500mPa.s以上1000mPa.s未満
△:1000mPa.s以上1200mPa.s未満
×:1200mPa.s以上
(評価2)硬化性
「Desmophen1420」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価201mgKOH/樹脂g)と「Desmophen1520」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価191mgKOH/樹脂g)を質量比で1/1に事前にブレンドした。そのブレンドしたアスパラギン酸エステル化合物とポリイソシアネート組成物とを、NCO/NH=1.1になるように配合し、酢酸n−ブチルで塗料固形分=90質量%となるように調整して、ポリアスパラティック塗料組成物を得た。得られたポリアスパラティック塗料組成物をポリプロピレン(PP)板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で24時間乾燥させることで硬化塗膜を得た。得られた硬化塗膜をPP板から剥がし、アセトン中に23℃で24時間浸漬後、未溶解部質量の浸漬前質量に対する値(ゲル分率)を計算し、下記の基準で硬化性を評価した。
「Desmophen1420」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価201mgKOH/樹脂g)と「Desmophen1520」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価191mgKOH/樹脂g)を質量比で1/1に事前にブレンドした。そのブレンドしたアスパラギン酸エステル化合物とポリイソシアネート組成物とを、NCO/NH=1.1になるように配合し、酢酸n−ブチルで塗料固形分=90質量%となるように調整して、ポリアスパラティック塗料組成物を得た。得られたポリアスパラティック塗料組成物をポリプロピレン(PP)板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で24時間乾燥させることで硬化塗膜を得た。得られた硬化塗膜をPP板から剥がし、アセトン中に23℃で24時間浸漬後、未溶解部質量の浸漬前質量に対する値(ゲル分率)を計算し、下記の基準で硬化性を評価した。
◎:ゲル分率が80%以上
○:ゲル分率が70%以上80%未満
△:ゲル分率が60%以上70%未満
×:ゲル分率が60%未満
○:ゲル分率が70%以上80%未満
△:ゲル分率が60%以上70%未満
×:ゲル分率が60%未満
(評価3)耐薬品性
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で7日間乾燥させることで硬化塗膜を得た。その後、キシレンを染込ませたコットンボールを塗膜に1分間乗せた後の塗膜の外観変化で評価した。
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で7日間乾燥させることで硬化塗膜を得た。その後、キシレンを染込ませたコットンボールを塗膜に1分間乗せた後の塗膜の外観変化で評価した。
○:塗膜の外観変化なし
△:塗膜の外観変化僅かにあり
×:塗膜の外観変化あり
△:塗膜の外観変化僅かにあり
×:塗膜の外観変化あり
(評価4)耐候性
アルミニウム板に予め市販の溶剤系2液アクリルウレタン白エナメル塗料をスプレー塗装してセッティング後に80℃で2時間焼付けを行ない、室温で2週間以上養生させて、60度光沢値が10%以下になるまで表面を#1000のサンドペーパーで研磨した白板を基材として準備した。その基材上に(評価2)と同様にして得られたポリアスパラティック塗料組成物を白板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で7日間乾燥させることで硬化塗膜を得た。その後、スガ試験機(株)製デューパネル光コントロールウェザーメーターFDPを用いて、JIS K5600−7−8の条件で評価した。
○:1500時間暴露した後の60度光沢保持率が90%以上
△:1500時間暴露した後の60度光沢保持率が80%以上90%未満
×:1500時間暴露した後の60度光沢保持率が80%未満
アルミニウム板に予め市販の溶剤系2液アクリルウレタン白エナメル塗料をスプレー塗装してセッティング後に80℃で2時間焼付けを行ない、室温で2週間以上養生させて、60度光沢値が10%以下になるまで表面を#1000のサンドペーパーで研磨した白板を基材として準備した。その基材上に(評価2)と同様にして得られたポリアスパラティック塗料組成物を白板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で7日間乾燥させることで硬化塗膜を得た。その後、スガ試験機(株)製デューパネル光コントロールウェザーメーターFDPを用いて、JIS K5600−7−8の条件で評価した。
○:1500時間暴露した後の60度光沢保持率が90%以上
△:1500時間暴露した後の60度光沢保持率が80%以上90%未満
×:1500時間暴露した後の60度光沢保持率が80%未満
(評価5)ポットライフ
(評価2)と同様にして得られたポリアスパラティック塗料組成物を23℃でゲル化するまでの時間を測定し、下記の基準でポットライフを評価した。
◎:ゲル化までの時間が150分以上
○:ゲル化までの時間が120分以上150分未満
△:ゲル化までの時間が90分以上120分未満
×:ゲル化までの時間が90分未満
(評価2)と同様にして得られたポリアスパラティック塗料組成物を23℃でゲル化するまでの時間を測定し、下記の基準でポットライフを評価した。
◎:ゲル化までの時間が150分以上
○:ゲル化までの時間が120分以上150分未満
△:ゲル化までの時間が90分以上120分未満
×:ゲル化までの時間が90分未満
(評価6)硬度
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で24時間乾燥させることで硬化塗膜を得た。得られた硬化塗膜について、ケーニッヒ硬度をBYK Chemie社の振り子式硬度計により23℃で測定し、下記の基準で硬度を評価した。
◎:ケーニッヒ硬度が120以上
○:ケーニッヒ硬度が110以上120未満、
△:ケーニッヒ硬度が100以上110未満
×:ケーニッヒ硬度が100未満
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で24時間乾燥させることで硬化塗膜を得た。得られた硬化塗膜について、ケーニッヒ硬度をBYK Chemie社の振り子式硬度計により23℃で測定し、下記の基準で硬度を評価した。
◎:ケーニッヒ硬度が120以上
○:ケーニッヒ硬度が110以上120未満、
△:ケーニッヒ硬度が100以上110未満
×:ケーニッヒ硬度が100未満
(評価7)乾燥性
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で乾燥させてタックフリーまでの時間について、下記の基準で乾燥性を評価した。
○:60分間未満
△:60分間以上120分間未満
×:120分間以上
(評価2)と同様にして得られたポリアスパラティック塗料組成物をガラス板に、アプリケーターで乾燥膜厚80μm以上100μm以下になるように塗装し、23℃で乾燥させてタックフリーまでの時間について、下記の基準で乾燥性を評価した。
○:60分間未満
△:60分間以上120分間未満
×:120分間以上
[製造例1−1]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラブチルアンモニウムアセテートを2−エチル−1−ヘキサノールで10質量%に希釈した溶液を0.15部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が43.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.1質量%、25℃における粘度が1350mPa.s、数平均分子量590、イソシアネート基平均数3.2、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−1を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラブチルアンモニウムアセテートを2−エチル−1−ヘキサノールで10質量%に希釈した溶液を0.15部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が43.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.1質量%、25℃における粘度が1350mPa.s、数平均分子量590、イソシアネート基平均数3.2、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−1を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−2]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.12部を仕込み、撹拌下反応器内温度を80℃で2時間保持した。そこに、イソシアヌレート化反応触媒トリメチル−2−メチル−2−ヒドロキシエチルアンモニウムヒドロキシドをイソブタノールで5質量%に希釈した溶液を0.08部添加し、イソシアヌレート化反応を行ない、転化率が20%になった時点で燐酸を添加し反応を停止した。その後、反応液を160℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.2質量%、25℃における粘度が470mPa.s、数平均分子量540、イソシアネート基平均数3.0、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−2を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.12部を仕込み、撹拌下反応器内温度を80℃で2時間保持した。そこに、イソシアヌレート化反応触媒トリメチル−2−メチル−2−ヒドロキシエチルアンモニウムヒドロキシドをイソブタノールで5質量%に希釈した溶液を0.08部添加し、イソシアヌレート化反応を行ない、転化率が20%になった時点で燐酸を添加し反応を停止した。その後、反応液を160℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.2質量%、25℃における粘度が470mPa.s、数平均分子量540、イソシアネート基平均数3.0、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−2を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−3]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.42部を仕込み、撹拌下反応器内温度を80℃で2時間保持した。そこに、イソシアヌレート化反応触媒トリメチル−2−メチル−2−ヒドロキシエチルアンモニウムヒドロキシドをイソブタノールで5質量%に希釈した溶液を0.08部添加し、イソシアヌレート化反応を行ない、転化率が18%になった時点で燐酸を添加し反応を停止した。その後、反応液を160℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.1質量%、25℃における粘度が310mPa.s、数平均分子量520、イソシアネート基平均数2.9、HDIモノマー質量濃度0.2質量%のポリイソシアネートP−3を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.42部を仕込み、撹拌下反応器内温度を80℃で2時間保持した。そこに、イソシアヌレート化反応触媒トリメチル−2−メチル−2−ヒドロキシエチルアンモニウムヒドロキシドをイソブタノールで5質量%に希釈した溶液を0.08部添加し、イソシアヌレート化反応を行ない、転化率が18%になった時点で燐酸を添加し反応を停止した。その後、反応液を160℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.1質量%、25℃における粘度が310mPa.s、数平均分子量520、イソシアネート基平均数2.9、HDIモノマー質量濃度0.2質量%のポリイソシアネートP−3を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−4]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラブチルアンモニウムアセテートを2−エチル−1−ヘキサノールで0.2質量%に希釈した溶液を2.5部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が41.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量20.8質量%、25℃における粘度が470mPa.s、数平均分子量560、イソシアネート基平均数2.8、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−4を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラブチルアンモニウムアセテートを2−エチル−1−ヘキサノールで0.2質量%に希釈した溶液を2.5部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が41.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量20.8質量%、25℃における粘度が470mPa.s、数平均分子量560、イソシアネート基平均数2.8、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−4を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−5]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.09部、2−エチル−1−ヘキサノール3部を仕込み、撹拌下反応器内温度を80℃で1時間保持した。そこに、イソシアヌレート化反応触媒テトラメチルアンモニウムカプリエートを0.005部添加し、イソシアヌレート化反応を行ない、反応液屈折率変化が0.0085になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量20.4質量%、25℃における粘度が340mPa.s、数平均分子量540、イソシアネート基平均数2.6、未反応HDI質量濃度0.1質量%のポリイソシアネートP−5を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、イソブタノール0.09部、2−エチル−1−ヘキサノール3部を仕込み、撹拌下反応器内温度を80℃で1時間保持した。そこに、イソシアヌレート化反応触媒テトラメチルアンモニウムカプリエートを0.005部添加し、イソシアヌレート化反応を行ない、反応液屈折率変化が0.0085になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量20.4質量%、25℃における粘度が340mPa.s、数平均分子量540、イソシアネート基平均数2.6、未反応HDI質量濃度0.1質量%のポリイソシアネートP−5を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−6]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イミノオキサジアジンジオン化反応触媒テトラブチルホスホニウム水素ジフルオリドをイソプロパノールで70質量%に希釈した溶液を0.05部添加し、内温を70℃以下で保持してイミノオキサジアジンジオン化反応を行ない、反応液のNCO含有率が43.3質量%になった時点でp−トルエンスルホン酸をイソプロパノールで40質量%に希釈した溶液を0.0575部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が640mPa.s、数平均分子量570、イソシアネート基平均数3.2、HDIモノマー質量濃度0.2質量%のポリイソシアネートP−6を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イミノオキサジアジンジオン化反応触媒テトラブチルホスホニウム水素ジフルオリドをイソプロパノールで70質量%に希釈した溶液を0.05部添加し、内温を70℃以下で保持してイミノオキサジアジンジオン化反応を行ない、反応液のNCO含有率が43.3質量%になった時点でp−トルエンスルホン酸をイソプロパノールで40質量%に希釈した溶液を0.0575部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が640mPa.s、数平均分子量570、イソシアネート基平均数3.2、HDIモノマー質量濃度0.2質量%のポリイソシアネートP−6を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−7]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、ウレトジオン化反応触媒トリ−n−ブチルホスフィン(Cytop(商標)340、Cytec)を1.5部添加し、ウレトジオン化反応を行ない、反応液屈折率測定による転化率が40%になった時点でメチル−p−トルエンスルホネートを1.33部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量22.1質量%、25℃における粘度が150mPa.s、数平均分子量440、イソシアネート基平均数2.3、HDIモノマー質量濃度0.3質量%のポリイソシアネートP−7を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、ウレトジオン化反応触媒トリ−n−ブチルホスフィン(Cytop(商標)340、Cytec)を1.5部添加し、ウレトジオン化反応を行ない、反応液屈折率測定による転化率が40%になった時点でメチル−p−トルエンスルホネートを1.33部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量22.1質量%、25℃における粘度が150mPa.s、数平均分子量440、イソシアネート基平均数2.3、HDIモノマー質量濃度0.3質量%のポリイソシアネートP−7を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[製造例1−8]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を160℃で1.5時間保持した。反応器内温度を140℃に下げて、イソシアヌレート化反応触媒ヘキサメチルジシラザンを1部添加し、30分間イソシアヌレート化反応を行なった後、反応器内温度を90℃に下げて、n−ブタノールを0.55部添加し、1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が520mPa.s、数平均分子量540、イソシアネート基平均数3.0、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−8を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を160℃で1.5時間保持した。反応器内温度を140℃に下げて、イソシアヌレート化反応触媒ヘキサメチルジシラザンを1部添加し、30分間イソシアヌレート化反応を行なった後、反応器内温度を90℃に下げて、n−ブタノールを0.55部添加し、1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が520mPa.s、数平均分子量540、イソシアネート基平均数3.0、HDIモノマー質量濃度0.1質量%のポリイソシアネートP−8を得た。得られたポリイソシアネートについて、13C−NMRの測定から求めた各モル比を表1に記載した。
[実施例1−1]
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、ポリイソシアネートP−1を58部、ポリイソシアネートP−5を14部仕込み、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性の結果を表4に示す。引続き、アスパラギン酸エステル化合物を加えてポリアスパラティック塗料組成物を調製し、硬化性、耐薬品性、耐候性を評価した。得られた結果を表6に示す。
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、ポリイソシアネートP−1を58部、ポリイソシアネートP−5を14部仕込み、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性の結果を表4に示す。引続き、アスパラギン酸エステル化合物を加えてポリアスパラティック塗料組成物を調製し、硬化性、耐薬品性、耐候性を評価した。得られた結果を表6に示す。
[実施例1−2〜1−6、比較例1−1〜1−5]
表2又は3で示した配合とする以外は、実施例1−1と同様にして、ポリイソシアネート組成物を得た。得られたポリイソシアネートの各物性の結果を表4又は5に示す。引続き、アスパラギン酸エステル化合物に対して、硬化性、耐薬品性、耐候性を評価した。得られた結果を表6に示す。
表2又は3で示した配合とする以外は、実施例1−1と同様にして、ポリイソシアネート組成物を得た。得られたポリイソシアネートの各物性の結果を表4又は5に示す。引続き、アスパラギン酸エステル化合物に対して、硬化性、耐薬品性、耐候性を評価した。得られた結果を表6に示す。
上記結果から、実施例における脂肪族ポリイソシアネート組成物は、ハイソリッド処方又は無溶剤処方に適切な低粘度であることが少なくとも確認された。また、実施例における脂肪族ポリイソシアネート組成物を含有するポリアスパラティック塗料組成物を用いることによって、硬化性を維持しつつ、耐薬品性及び耐候性に優れ、かつ、ポットライフにも優れる塗膜を得ることができた。
[合成例2−1]NTIの合成
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内に4−アミノメチル−1,8−オクタメチレンジアミン(以下、「トリアミン」と称する場合がある)1060gをメタノール1500gに溶かし、これに35%濃塩酸1800mLを冷却しながら徐々に滴下した。次いで、減圧下にてメタノール及び水を除去して濃縮し、60℃/5mmHgにて24時間乾燥して、白色固体のトリアミン塩酸塩を得た。得られたトリアミン塩酸塩650gを微粉末としてo−ジクロルベンゼン5000gに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が100℃に達した時点でホスゲンを200g/Hrの速度にて吹込みはじめ、さらに昇温を続けた。次いで、反応液が180℃に達したら、そのまま温度を保持し、12時間ホスゲンを吹込み続けた。次いで、減圧下にて溶存ホスゲン及び溶媒を留去した後、真空蒸留することにより、沸点161〜163℃/1.2mmHgの無色透明な4−イソシアネートメチル−1,8−オクタメチレンジイソシアネート(以下、「NTI」と称する場合がある)420gを得た。NTIのNCO含有率は、50.0質量%であった。
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内に4−アミノメチル−1,8−オクタメチレンジアミン(以下、「トリアミン」と称する場合がある)1060gをメタノール1500gに溶かし、これに35%濃塩酸1800mLを冷却しながら徐々に滴下した。次いで、減圧下にてメタノール及び水を除去して濃縮し、60℃/5mmHgにて24時間乾燥して、白色固体のトリアミン塩酸塩を得た。得られたトリアミン塩酸塩650gを微粉末としてo−ジクロルベンゼン5000gに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が100℃に達した時点でホスゲンを200g/Hrの速度にて吹込みはじめ、さらに昇温を続けた。次いで、反応液が180℃に達したら、そのまま温度を保持し、12時間ホスゲンを吹込み続けた。次いで、減圧下にて溶存ホスゲン及び溶媒を留去した後、真空蒸留することにより、沸点161〜163℃/1.2mmHgの無色透明な4−イソシアネートメチル−1,8−オクタメチレンジイソシアネート(以下、「NTI」と称する場合がある)420gを得た。NTIのNCO含有率は、50.0質量%であった。
[合成例2−2]LTIの合成
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内にエタノールアミン122.2g、o−ジクロロベンゼン100mL、トルエン420mLを入れ、氷冷化塩化水素ガスを導入し、エタノールアミンを塩酸塩に転換した。次いで、リジン塩酸塩182.5gを添加し、反応液を加熱して80℃まで昇温し、エタノールアミン塩酸塩を溶解させ、塩化水素ガスを導入してリジン二塩酸塩とした。次いで、塩化水素ガスを20から30mL/分で通過させ、反応液を加熱して116℃まで昇温し、水が留出しなくなるまでこの温度を維持した。次いで、生成した反応混合物をメタノール及びエタノールの混合液中で再結晶してリジンβ−アミノエチルエステル三塩酸塩165gを得た。このリジンβ−アミノエチルエステル三塩酸塩100gを微粉末としてo−ジクロロベンゼン1200mLに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が120℃に達した時点でホスゲンを0.4モル/時間の速度にて吹込みはじめ、10時間保持した。次いで、反応液を150℃まで昇温し、反応液中のリジンβ−アミノエチルエステル三塩酸塩をほとんど溶解させた。次いで、冷却後ろ過し、減圧下にて溶存ホスゲン及び溶媒を留去した。次いで、真空蒸留することにより、沸点155〜157℃/0.022mmHgの無色透明なLTI 80.4gを得た。LTIのNCO含有率は、47.1質量%であった。
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内にエタノールアミン122.2g、o−ジクロロベンゼン100mL、トルエン420mLを入れ、氷冷化塩化水素ガスを導入し、エタノールアミンを塩酸塩に転換した。次いで、リジン塩酸塩182.5gを添加し、反応液を加熱して80℃まで昇温し、エタノールアミン塩酸塩を溶解させ、塩化水素ガスを導入してリジン二塩酸塩とした。次いで、塩化水素ガスを20から30mL/分で通過させ、反応液を加熱して116℃まで昇温し、水が留出しなくなるまでこの温度を維持した。次いで、生成した反応混合物をメタノール及びエタノールの混合液中で再結晶してリジンβ−アミノエチルエステル三塩酸塩165gを得た。このリジンβ−アミノエチルエステル三塩酸塩100gを微粉末としてo−ジクロロベンゼン1200mLに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が120℃に達した時点でホスゲンを0.4モル/時間の速度にて吹込みはじめ、10時間保持した。次いで、反応液を150℃まで昇温し、反応液中のリジンβ−アミノエチルエステル三塩酸塩をほとんど溶解させた。次いで、冷却後ろ過し、減圧下にて溶存ホスゲン及び溶媒を留去した。次いで、真空蒸留することにより、沸点155〜157℃/0.022mmHgの無色透明なLTI 80.4gを得た。LTIのNCO含有率は、47.1質量%であった。
[合成例2−3]GTIの合成
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内にグルタミン酸塩酸塩275g、エタノールアミン塩酸塩800g、トルエン150mLを入れ、塩化水素ガスを吹き込みながら、水が共沸しなくなるまで110℃にて24時間加熱還流した。次いで、生成した反応混合物をメタノール及びエタノールの混合液中で再結晶して、ビス(2−アミノエチル)グルタメート三塩酸塩270gを得た。このビス(2−アミノエチル)グルタメート三塩酸塩85gをo−ジクロロベンゼン680gに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が135℃に達した時点でホスゲンを0.8モル/時間の速度にて吹込みはじめ、そのまま温度を保持し、13時間ホスゲンを吹込み続けた。次いで、反応生成物をろ過後、減圧濃縮し、さらに薄膜蒸発缶で精製することにより、GTI54gを得た。GTIのNCO含有率は、39.8質量%であった。
撹拌機、温度計、ガス導入管を取り付けた4ツ口フラスコ内にグルタミン酸塩酸塩275g、エタノールアミン塩酸塩800g、トルエン150mLを入れ、塩化水素ガスを吹き込みながら、水が共沸しなくなるまで110℃にて24時間加熱還流した。次いで、生成した反応混合物をメタノール及びエタノールの混合液中で再結晶して、ビス(2−アミノエチル)グルタメート三塩酸塩270gを得た。このビス(2−アミノエチル)グルタメート三塩酸塩85gをo−ジクロロベンゼン680gに懸濁させ、かきまぜながら反応液を昇温した。次いで、反応液が135℃に達した時点でホスゲンを0.8モル/時間の速度にて吹込みはじめ、そのまま温度を保持し、13時間ホスゲンを吹込み続けた。次いで、反応生成物をろ過後、減圧濃縮し、さらに薄膜蒸発缶で精製することにより、GTI54gを得た。GTIのNCO含有率は、39.8質量%であった。
[実施例2−1]ポリアスパラティック塗料組成物の製造
合成例2−1で得られたNTIについて、各物性及びハイソリッド性を評価した。
次いで、「Desmophen1420」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価201mgKOH/樹脂g)と「Desmophen1520」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価191mgKOH/樹脂g)とを質量比が1/1になるように予め混合した。予め混合したアスパラギン酸エステル化合物とNTIとを、NCO/NH=1.1になるように混合し、酢酸n−ブチルで塗料固形分が90質量%となるように調整して、ポリアスパラティック塗料組成物を得た。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
合成例2−1で得られたNTIについて、各物性及びハイソリッド性を評価した。
次いで、「Desmophen1420」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価201mgKOH/樹脂g)と「Desmophen1520」(アスパラギン酸エステル化合物、Covestro社製の商品名、アミン価191mgKOH/樹脂g)とを質量比が1/1になるように予め混合した。予め混合したアスパラギン酸エステル化合物とNTIとを、NCO/NH=1.1になるように混合し、酢酸n−ブチルで塗料固形分が90質量%となるように調整して、ポリアスパラティック塗料組成物を得た。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
[実施例2−2]ポリアスパラティック塗料組成物の製造
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、NTIを29部、デュラネートTKA−100(商品名)(旭化成株式会社製、イソシアヌレート型、Mn=650)を7部仕込んだ。次いで、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性及びハイソリッド性の結果を表7に示す。
次いで、得られたポリイソシアネート組成物を用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、NTIを29部、デュラネートTKA−100(商品名)(旭化成株式会社製、イソシアヌレート型、Mn=650)を7部仕込んだ。次いで、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性及びハイソリッド性の結果を表7に示す。
次いで、得られたポリイソシアネート組成物を用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
[実施例2−3〜2−5、2−7、2−9、比較例2−1〜2−3]
トリイソシアネート化合物の種類及びトリイソシアネート化合物又はデュラネートTKA−100の含有量が表7又は8で示す値となるようにした以外は、実施例2−2と同様の方法を用いて、ポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性及びハイソリッド性の結果を表7(実施例2−3〜2−5、2−7、2−9)及び表8(比較例2−1〜2−3)に示す。
次いで、得られた各ポリイソシアネート組成物を用いて、実施例2−1と同様の方法を用いて、各ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7及び8に示す。
トリイソシアネート化合物の種類及びトリイソシアネート化合物又はデュラネートTKA−100の含有量が表7又は8で示す値となるようにした以外は、実施例2−2と同様の方法を用いて、ポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性及びハイソリッド性の結果を表7(実施例2−3〜2−5、2−7、2−9)及び表8(比較例2−1〜2−3)に示す。
次いで、得られた各ポリイソシアネート組成物を用いて、実施例2−1と同様の方法を用いて、各ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7及び8に示す。
[実施例2−6]
合成例2−2で得られたLTIについて、各物性及びハイソリッド性を評価した。
次いで、LTIを用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
合成例2−2で得られたLTIについて、各物性及びハイソリッド性を評価した。
次いで、LTIを用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
[実施例2−8]
合成例2−3で得られたGTIについて、各物性及びハイソリッド性を評価した。
次いで、GTIを用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
合成例2−3で得られたGTIについて、各物性及びハイソリッド性を評価した。
次いで、GTIを用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表7に示す。
[比較例2−4]
デュラネートTKA−100について、各物性及びハイソリッド性を評価した。
次いで、デュラネートTKA−100を用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表8に示す。
デュラネートTKA−100について、各物性及びハイソリッド性を評価した。
次いで、デュラネートTKA−100を用いて、実施例2−1と同様の方法を用いて、ポリアスパラティック塗料組成物を製造した。得られたポリアスパラティック塗料組成物について、硬化性及び硬度を評価した。得られた結果を以下の表8に示す。
表7から、ポリイソシアネート組成物の総量に対するトリイソシアネート化合物の含有量が20質量%以上では、ポリイソシアネート組成物の粘度は1200mPa・s未満であり、低粘度であった。また、これら粘度が低いポリイソシアネート組成物を含有するポリアスパラティック塗料組成物は硬化性に優れていた。さらに、当該ポリアスパラティック塗料組成物から得られた塗膜の硬度は100以上であり、硬度が高かった。
一方、表8から、ポリイソシアネート組成物の総量に対するトリイソシアネート化合物の含有量が20質量%未満では、ポリイソシアネート組成物の粘度は1200mPa・s以上であり、高粘度であった。また、これら粘度が高いポリイソシアネート組成物を含有するポリアスパラティック塗料組成物は硬化性に優れるが、得られる塗膜の硬度が100未満であり、硬度が低かった。
以上のことから、本実施形態のポリアスパラティック塗料組成物は、低粘度のポリイソシアネート組成物を含むことで、優れた硬化性を有することが確かめられた。また、当該ポリアスパラティック塗料組成物を用いることで、高い硬度の塗膜を得られることが確かめられた。
一方、表8から、ポリイソシアネート組成物の総量に対するトリイソシアネート化合物の含有量が20質量%未満では、ポリイソシアネート組成物の粘度は1200mPa・s以上であり、高粘度であった。また、これら粘度が高いポリイソシアネート組成物を含有するポリアスパラティック塗料組成物は硬化性に優れるが、得られる塗膜の硬度が100未満であり、硬度が低かった。
以上のことから、本実施形態のポリアスパラティック塗料組成物は、低粘度のポリイソシアネート組成物を含むことで、優れた硬化性を有することが確かめられた。また、当該ポリアスパラティック塗料組成物を用いることで、高い硬度の塗膜を得られることが確かめられた。
[製造例3−1]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラメチルアンモニウムカプリエートを0.01部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が43.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が1350mPa.s、数平均分子量600、イソシアネート基平均数3.3、HDIモノマー質量濃度0.1質量%、ウレトジオン2量体の含有量0.1質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−1を得た。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、イソシアヌレート化反応触媒テトラメチルアンモニウムカプリエートを0.01部添加し、イソシアヌレート化反応を行ない、反応液のNCO含有率が43.8質量%になった時点で燐酸を添加し反応を停止した。その後、反応液を90℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量23.4質量%、25℃における粘度が1350mPa.s、数平均分子量600、イソシアネート基平均数3.3、HDIモノマー質量濃度0.1質量%、ウレトジオン2量体の含有量0.1質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−1を得た。
[製造例3−2]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、1,3−ブタンジオール3.5部を仕込み、撹拌下反応器内温度を160℃で1時間保持し、ウレタン化反応を行なった。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量19.7質量%、25℃における粘度が440mPa.s、数平均分子量460、イソシアネート基平均数2.2、HDIモノマー質量濃度0.2質量%、ウレトジオン2量体の含有量15.7質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−2を得た。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、1,3−ブタンジオール3.5部を仕込み、撹拌下反応器内温度を160℃で1時間保持し、ウレタン化反応を行なった。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量19.7質量%、25℃における粘度が440mPa.s、数平均分子量460、イソシアネート基平均数2.2、HDIモノマー質量濃度0.2質量%、ウレトジオン2量体の含有量15.7質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−2を得た。
[製造例3−3]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、分子量400のポリエチレングリコール15.9部を仕込み、撹拌下反応器内温度を90℃で4時間保持し、ウレタン化反応を行なった。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量11.2%、25℃における粘度が600mPa.s、数平均分子量740、イソシアネート基平均数2.0、HDIモノマー質量濃度0.3質量%、ウレトジオン2量体の含有量0.5質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−3を得た。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、分子量400のポリエチレングリコール15.9部を仕込み、撹拌下反応器内温度を90℃で4時間保持し、ウレタン化反応を行なった。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量11.2%、25℃における粘度が600mPa.s、数平均分子量740、イソシアネート基平均数2.0、HDIモノマー質量濃度0.3質量%、ウレトジオン2量体の含有量0.5質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−3を得た。
[製造例3−4]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、2−エチル−1−ヘキサノール7.8部を仕込み、撹拌下反応器内温度を130℃に保持した。そこに、アロファネート化反応触媒2−エチルヘキサン酸ジルコニウムを2−エチル−1−ヘキサノールで20質量%に希釈した溶液を0.025部添加し、アロファネート化反応を行ない、反応液の屈折率上昇が0.0052になった時点で燐酸を添加し反応を停止した。その後、反応液を130℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量17.2質量%、25℃における粘度が110mPa.s、数平均分子量510、イソシアネート基平均数2.1、HDIモノマー質量濃度0.2質量%、ウレトジオン2量体の含有量4.4質量%、モノアルコールアロファネート体の含有量70.7質量%のポリイソシアネートQ−4を得た。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部、2−エチル−1−ヘキサノール7.8部を仕込み、撹拌下反応器内温度を130℃に保持した。そこに、アロファネート化反応触媒2−エチルヘキサン酸ジルコニウムを2−エチル−1−ヘキサノールで20質量%に希釈した溶液を0.025部添加し、アロファネート化反応を行ない、反応液の屈折率上昇が0.0052になった時点で燐酸を添加し反応を停止した。その後、反応液を130℃で1時間保持した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量17.2質量%、25℃における粘度が110mPa.s、数平均分子量510、イソシアネート基平均数2.1、HDIモノマー質量濃度0.2質量%、ウレトジオン2量体の含有量4.4質量%、モノアルコールアロファネート体の含有量70.7質量%のポリイソシアネートQ−4を得た。
[製造例3−5]
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、ウレトジオン化反応触媒トリ−n−ブチルホスフィン(Cytop(商標)340、Cytec)を1.5部添加し、ウレトジオン化反応を行ない、反応液屈折率測定による転化率が40%になった時点でメチル−p−トルエンスルホネートを1.33部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量22.1質量%、25℃における粘度が150mPa.s、数平均分子量440、イソシアネート基平均数2.3、HDIモノマー質量濃度0.3質量%、ウレトジオン2量体の含有量39.6質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−5を得た。
撹拌機、温度計、還流冷却管、窒素吹き込み管、滴下ロートを取り付けた4ツ口フラスコ内を窒素雰囲気にし、HDI100部を仕込み、撹拌下反応器内温度を60℃に保持した。そこに、ウレトジオン化反応触媒トリ−n−ブチルホスフィン(Cytop(商標)340、Cytec)を1.5部添加し、ウレトジオン化反応を行ない、反応液屈折率測定による転化率が40%になった時点でメチル−p−トルエンスルホネートを1.33部添加し反応を停止した。冷却した反応液を濾過後、薄膜蒸発缶を用いて未反応HDIを除去した。NCO含有量22.1質量%、25℃における粘度が150mPa.s、数平均分子量440、イソシアネート基平均数2.3、HDIモノマー質量濃度0.3質量%、ウレトジオン2量体の含有量39.6質量%、モノアルコールアロファネート体の含有量0.0質量%のポリイソシアネートQ−5を得た。
[実施例3−1]
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、ポリイソシアネートQ−1を44部、ポリイソシアネートQ−2を30部仕込み、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性の結果を表10に示す。引続き、アスパラギン酸エステル化合物に対して、乾燥性、耐薬品性を評価した。得られた結果を表10に示す。
撹拌機、温度計、還流冷却管、窒素吹き込み管を取り付けた4ツ口フラスコ内を窒素雰囲気にし、ポリイソシアネートQ−1を44部、ポリイソシアネートQ−2を30部仕込み、均一になるまで撹拌してポリイソシアネート組成物を得た。得られたポリイソシアネート組成物の各物性の結果を表10に示す。引続き、アスパラギン酸エステル化合物に対して、乾燥性、耐薬品性を評価した。得られた結果を表10に示す。
[実施例3−2〜3−8、比較例3−1〜3−4]
表10又は11で示した配合とする以外は、実施例3−1と同様にして、ポリイソシアネート組成物を得た。得られたポリイソシアネートの各物性の結果を表10又は11に示す。引続き、アスパラギン酸エステル化合物に対して、乾燥性、耐薬品性を評価した。得られた結果を表10又は11に示す。
表10又は11で示した配合とする以外は、実施例3−1と同様にして、ポリイソシアネート組成物を得た。得られたポリイソシアネートの各物性の結果を表10又は11に示す。引続き、アスパラギン酸エステル化合物に対して、乾燥性、耐薬品性を評価した。得られた結果を表10又は11に示す。
上記結果から、実施例の脂肪族ポリイソシアネート組成物は、ハイソリッド処方又は無溶剤処方に適切な低粘度であることが少なくとも確認された。また、実施例の脂肪族ポリイソシアネート組成物を含有するポリアスパラティック塗料組成物を用いることによって、乾燥性を維持しつつ、耐薬品性に優れる塗膜を得ることができた。
本発明に係るポリアスパラティック塗料組成物は、ロール塗装、カーテンフロー塗装、スプレー塗装、静電塗装、ベル塗装、浸漬、ローラー塗装、刷毛塗装等によって、鋼板や表面処理鋼板等の金属、プラスチック、無機材料等のセラミック、ガラス、コンクリートに対して、プライマー、中塗り、又は上塗りとして好適に使用される。当該ポリアスパラティック塗料組成物は、美粧性、耐候性、耐酸性、防錆性、耐チッピング性、密着性等を付与するために好適に用いられる。また、当該ポリアスパラティック塗料組成物は、接着剤、粘着剤、エラストマー、フォーム、表面処理剤等としても有用である。
Claims (12)
- (A)下記式(I):
で表されるアスパラギン酸エステル化合物と、
(B1)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーから得られるポリイソシアネートを含み、下記式(1)で表されるモル比xが0.05以上0.5以下、下記式(4)で表されるモル比dが0.02以上0.5以下、及び下記式(5)で表されるモル比eが0以上0.05以下であるポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。
モル比x=(B+C+D)/(A+B+C+D) (1)
モル比d=D/(A+B+C+D) (4)
モル比e=E/A (5)
上記式中、Aはポリイソシアネート組成物(B1)における下記式(II)で表されるイソシアヌレート基の含有量(モル%)、Bはポリイソシアネート組成物(B1)における下記式(III)で表されるイミノオキサジアジンジオン基の含有量(モル%)、Cはポリイソシアネート組成物(B1)における下記式(IV)で表されるウレトジオン基の含有量(モル%)、Dはポリイソシアネート組成物(B1)における下記式(V)で表されるアロファネート基の含有量(モル%)、Eはポリイソシアネート組成物(B1)における下記式(VI)で表されるビウレット基の含有量(モル%)を示す。
- 前記ポリイソシアネート組成物(B1)におけるモル比dが0.04以上0.3以下であり、さらに、下記式(2)で表されるモル比bが0以上0.4以下、及び、下記式(3)で表されるモル比cが0以上0.3以下である、請求項1又は2に記載のポリアスパラティック塗料組成物。
モル比b=B/(A+B+C+D) (2)
モル比c=C/(A+B+C+D) (3)
前記式中、A、B、C及びDは、請求項1に記載の通りである。 - (A)下記一般式(I)で示されるアスパラギン酸エステル化合物と、
(B2)下記一般式(VIII)で示されるトリイソシアネート化合物を含むポリイソシアネート組成物と、を含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記トリイソシアネート化合物(b1)の含有量が20質量%以上100質量%以下であるポリアスパラティック塗料組成物。
- 前記ポリイソシアネート組成物(B2)は、さらに、脂肪族ジイソシアネート及び脂環式ジイソシアネートからなる群より選択される1種以上のジイソシアネートから得られるポリイソシアネート(b2)を含み、
前記ポリイソシアネート組成物(B2)の総量に対する前記ポリイソシアネート(b2)の含有量が0質量%よりも大きく80質量%以下である請求項4に記載のポリアスパラティック塗料組成物。 - (A)下記式(I)で表されるアスパラギン酸エステル化合物と、
(B3)脂肪族及び/又は脂環族ジイソシアネートからなる群より選択される1種又は2種以上のジイソシアネートモノマーとジオールとから得られる2官能ウレタンアダクトを含み、(B3)ポリイソシアネート組成物の総量に対するウレトジオン2量体とモノアルコールアロファネート体の含有量が0.2質量%以上30.0質量%以下である、ポリイソシアネート組成物と、
を含む、ポリアスパラティック塗料組成物。 - 前記(B3)ポリイソシアネート組成物が、更にイソシアヌレート基を含む、請求項6に記載のポリアスパラティック塗料組成物。
- 前記ポリイソシアネート組成物の、25℃における粘度が10mPa.s以上1000mPa.s以下である、請求項1〜7のいずれか一項に記載のポリアスパラティック塗料組成物。
- 前記アスパラギン酸エステル化合物のアミノ基と、前記ポリイソシアネート組成物のイソシアネート基との当量比が、アミノ基:イソシアネート基=10:1〜1:10である、請求項1〜8のいずれか一項に記載のポリアスパラティック塗料組成物。
- 前記ジイソシアネートモノマーが、ヘキサメチレンジイソシアネートを含む、請求項1〜9のいずれか一項に記載のポリアスパラティック塗料組成物。
- 請求項1〜10のいずれか一項に記載のポリアスパラティック塗料組成物により形成された、塗膜。
- 請求項11に記載の塗膜を備える、塗装物品。