JPWO2014021167A1 - 親水化シートおよびその製造方法 - Google Patents
親水化シートおよびその製造方法 Download PDFInfo
- Publication number
- JPWO2014021167A1 JPWO2014021167A1 JP2014528093A JP2014528093A JPWO2014021167A1 JP WO2014021167 A1 JPWO2014021167 A1 JP WO2014021167A1 JP 2014528093 A JP2014528093 A JP 2014528093A JP 2014528093 A JP2014528093 A JP 2014528093A JP WO2014021167 A1 JPWO2014021167 A1 JP WO2014021167A1
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- fluororesin
- sheet
- hydrophilic
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
親水化処理としては、一般的に、紫外線レーザーまたはArFレーザーを照射する処理や金属ナトリウム−ナフタレン錯体による化学エッチングする処理(特許文献12)が知られている。
上記フッ素樹脂繊維は、PTFEのみからなることが、得られるフッ素樹脂系シートの特性(撥水性、耐熱性、耐薬品性、通音性等)、性能(フィルタ性能)などの点で好ましい。また、本発明では、上記フッ素樹脂繊維が、PTFE以外に、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体〔PFA〕、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体〔FEP〕、テトラフルオロエチレン−ヘキサフルオロプロピレン−パーフルオロアルキルビニルエーテル共重合体〔EPE〕、ポリ(クロロトリフルオロエチレン)〔PCTFE〕、テトラフルオロエチレン−エチレン共重合体〔ETFE〕、低融点エチレン−テトラフルオロエチレン共重合体、エチレン−クロロトリフルオロエチレン共重合体〔ECTFE〕、ポリフッ化ビニリデン〔PVDF〕、フルオロエチレン−ビニルエーテル共重合体〔FEVE〕およびテトラフルオロエチレン−パーフルオロジオキソール共重合体〔TFEPD〕などの「他のフッ素樹脂」を一種または二種以上含んでなっていてもよく、PTFEと該フッ素樹脂との合計を100重量%とするとき、該フッ素樹脂が0重量%を超えて50重量%未満で含有されると、PTFEのみの場合に比して、耐熱性、耐久性等は多少低下するが、加工性、繊維径制御性等が向上する傾向がある。
この親水性基を有する化合物は、水酸基含有化合物、カルボン酸基含有化合物、スルホン酸基含有化合物、エーテル基含有化合物、エポキシ基含有化合物およびアミノ基含有化合物からなる群より選ばれる少なくとも一種の化合物であり、特にポリビニルアルコール〔PVA〕であることが好ましい。
<親水化シート>
本発明の親水化シートは、PTFEのみからなる繊維、または、PTFEとPTFE以外のフッ素樹脂とを含んでなる繊維(フッ素樹脂繊維)を用いて、特定の工程を経て得られるシート(好ましくは本発明の製造方法により得られるシート)であって、フッ素樹脂繊維を含んでなるフッ素樹脂系シートの親水化処理された後の表面が、水接触角で90°以下の親水性を有する。
本発明で用いるフッ素樹脂系シートは、例えば図3中、実施例2の5,000倍に拡大した画像に示すように、含まれるフッ素樹脂繊維が、主繊維と、主繊維の繊維径より小さい繊維径を有する副繊維とからなり、同じ主繊維内および/または異なる主繊維間を該副繊維が「架橋する」(あるいは「繋げる」とも表現でき、単純に「接触させる」や「絡める」とは異なる態様であって、高分子主鎖に側鎖が架渡したような状態とも言える。)が、その架橋点に結節が形成されていないことを特徴とする。
本発明の親水化シートは、上述したフッ素樹脂系シートを親水化処理してなり、親水化処理された後の表面が親水性であって、濡れ指数として、水接触角が90°以下、好ましくは60°以下、より好ましくは30°以下、さらに好ましくは10°以下であることが、表面張力の大きい水を効率よく良好に濾過できる点で望ましい。
本発明に用いる「親水化処理」として、例えば、フッ素樹脂系シート(の一部表面ないし全面)を「親水性基を有する化合物」で被覆する処理などが挙げられる。
これらの親水性基を有する化合物の中でも、水酸基を多く有するため水酸基含有化合物が好ましく、特にポリビニルアルコール〔PVA〕がより好ましい。
PVAの重量平均分子量としては、特に制限はないが、200〜150,000が好ましく、500〜100,000がより好ましい。分子量が200未満だと、PVAがフッ素樹脂系シート上に固定できず、親水性が失われるおそれがあり、分子量が150,000を超えると、PVAがフッ素樹脂系シート内に浸透せず、内部を親水化できないおそれがある。
フッ素樹脂系シートの露出表面を、親水性基を有する化合物で被覆する方法は、後述する。
本発明の親水化シートの製造方法は、下記工程(i)〜(vi)を含むことが好ましく、なかでも下記工程(iii)および(v),(vi)を含むことを特徴とする。
工程(ii)は、このフッ素樹脂繊維をシート状に成形(すなわちフッ素樹脂繊維シート(a0),(b0)を製造)する工程である。
工程(v)は、上記工程で得られたフッ素樹脂系シートを、「親水性基を有する化合物」の溶液に浸漬し、フッ素樹脂系シートを「親水性基を有する化合物」で被覆する工程である。
上記工程(v)および(vi)を、特に親水化工程ともいう。
工程(ii)の、フッ素樹脂繊維をシート状に成形する方法としては、例えば特許文献1に記載の方法などを用いることができる。
工程(iii)、すなわち副繊維化工程は、加熱された状態(すなわち、加熱処理)で、フッ素樹脂繊維シートに少なくとも二方向の応力を発生させる(すなわち、応力発生処理)工程であるが、前記加熱処理と応力発生処理は、同時に行っても、順に行ってもよい(すなわち、加熱処理を行った後に応力発生処理を行ってもよいし、応力発生処理を行った後に加熱処理を行ってもよい。)。中でも、加熱処理と応力発生処理とを同時に行う場合、加熱処理を行った後に応力発生処理を行った場合の方が、利便性や効率性の観点から好ましく、特に加熱処理と応力発生処理を同時の行った場合の方がより好ましい。
[その1]工程(iii)において主繊維どうしが接した後、工程(iv)において加重から開放されて主繊維どうしが離れる際、一部の主繊維表面の樹脂(例えばPTFE)が納豆の糸が伸びるように糸を引いて引っ張られることで、副繊維が生成される。これは、主繊維間に橋渡しのように副繊維が存在しているケースが多い(副繊維が少ない場合に顕著)という事実から、PTFEのみからなるフッ素樹脂系シートをPTFEの融点(327℃)近くに加熱することで、PTFE繊維表面が溶融・ゲル化し、この加圧の開放過程において、主繊維の弾性復元力により、主繊維どうしが付き離れする際に、主繊維表面のゲル状樹脂が互いの主繊維に引っ張られ、主繊維より細い繊維状の副繊維となることが考えられる。
また、工程(v)において、フッ素樹脂系シートを「親水性基を有する化合物」の溶液に浸漬する時間は、フッ素樹脂系シートの厚さや該水溶液の温度により変動するが、当業者であれば適宜調整することが可能である。
フッ素樹脂系シートを「水に相溶性のある溶媒」に浸漬する時間は、フッ素樹脂系シートの厚さや該溶媒の温度により変動するが、当業者であれば適宜調整することが可能である。
本発明の親水化シートは、気体や液体の濾過・滅菌用のフィルタに好適である。具体的なフィルタとしては、例えば、エアフィルタやベントフィルタ、滅菌用フィルタなどが挙げられる。
既存の電界紡糸法により作製した、縦10cm、横10cm、厚さ65.7μm、重量18.6mg、平均繊維径1μmのPTFE繊維からなるフッ素樹脂繊維シートを、一対のステンレス板の間に挟み、6kgの金型を乗せることで、該フッ素樹脂繊維シートに0.06kg/cm2の圧縮荷重を作用させながら360℃の電気炉の中で1時間保持した。
SEM(S−3400N((株)日立ハイテクノロジーズ製)によりフッ素樹脂系シートの表面を観察し(5,000倍)、副繊維の発生有無を確認した。この結果を表1に示す。
製造例1において、金型の重さを20kg(=0.20kg/cm2の圧縮荷重)に変更した以外は製造例1と同様にしてフッ素樹脂系シートを製造し、副繊維の発生有無を確認した。この結果を表1に示す。
製造例1において、金型の重さを35kg(=0.35kg/cm2の圧縮荷重)に変更した以外は製造例1と同様にしてフッ素樹脂系シートを製造し、副繊維の発生有無を確認した。この結果を表1に示す。
製造例1において、金型を乗せなかった以外は製造例1と同様にしてフッ素樹脂系シートを製造し、副繊維の発生有無を確認した。この結果を表1に示す。
製造例3において、せん断荷重を作用させなかった以外は製造例3と同様にしてフッ素樹脂系シートを製造し、副繊維の発生有無を確認した。この結果を表1に示す。
フッ素樹脂系シートの厚さを、マイクロメータであるLITEMATIC VL-50((株)ミツトヨ製)により測定した。
フッ素樹脂系シートの強度に関して、(株)島津製作所製の「EZ-test」を用い引張試験を行った。測定方法は次の通りである。
この試験片を、つかみ間長を25mmとなるよう引張試験機にとりつけ20mm/minのクロスヘッド速度で引張り、試験片破断時の最大引張荷重と引張強度を求めた。
バブルポイント細孔径とは、フッ素樹脂系シートの最大細孔径を示し、バブルポイント法(ASTM F316-86)により算出した。なお、測定にはGalwick(15.9dyn/cm)を浸漬液として使用した。
d=4γcosθ/ΔP
(式中、θはフッ素樹脂系シートと液体との接触角を、γ[N/m]は液体の表面張力を、ΔPがバブルポイント圧力を表す。)
平均流量径は、ASTM E1294-89のハーフドライ法により求めた。なお、測定にはGalwick(15.9dyn/cm)を浸漬液として使用した。
これらの結果を表2に示す。
フッ素樹脂系シートの粒子捕捉率として、JIS B 9908に準じて、粒子捕集率を測定した。この際、フィルタユニットの替わりに、製造例3および比較製造例1,2で得られた100mm×100mmの大きさのフッ素樹脂系シートを用い、測定用粉じんとして大気塵(0.15μm〜10μm粒径の塵を含む)を用い、空気の流量を面速度14.8cm/sとした。
表3から、フッ素樹脂系シートは、副繊維の発生により、特に従来捕捉が困難とされている0.333μm(=0.15〜0.50μm)粒子径の粒子捕捉性能が向上することが確認された。
製造例1で得られたフッ素樹脂系シートを、室温25℃で、99.7%イソプロピルアルコール〔IPA〕溶液(和光純薬(株)製)に1分間浸漬させた。
その後、自然乾燥することによって、シート表面の水接触角が0°の親水化フッ素樹脂系シートが得られた。
得られた親水化フッ素樹脂系シートの表面に水滴をドロップして10秒後、接触角計(協和界面科学(株)製の接触角計、CA−X型)を用いて水接触角を測定した。
実施例1において、製造例1で得られたフッ素樹脂系シートの代わりに、製造例2および製造例3のそれぞれで得られたフッ素樹脂系シート(いずれも、表面の水接触角が135°)を用いた以外は実施例1と同様にして親水化処理を施し、水接触角を測定した。水接触角は、実施例2,3ともに0°であった。
実施例1において、親水化処理を施さなかった以外は実施例1と同様にして水接触角を測定した。すなわち、製造例1で得られたフッ素樹脂シートの水接触角を測定した。水接触角は135°であった。
Claims (11)
- フッ素樹脂系シートを親水化処理してなる親水化シートであって、
該親水化シートの表面が、水接触角で90°以下の親水性を有し、
該フッ素樹脂系シートが、
主繊維と主繊維の繊維径より小さい繊維径を有する副繊維とからなり、
同じ主繊維内および/または異なる主繊維間を該副繊維が架橋しており、
その架橋点に結節が形成されておらず、
該主繊維および該副繊維が、ポリテトラフルオロエチレン〔PTFE〕を含むフッ素樹脂繊維からなる
ことを特徴とする、親水化シート。 - 上記主繊維の繊維径が100nm以上50μm以下であり、
上記副繊維の繊維径が10nm以上1μm未満である請求項1に記載の親水化シート。 - 上記フッ素樹脂繊維が、PTFE以外に、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体〔PFA〕、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体〔FEP〕、テトラフルオロエチレン−ヘキサフルオロプロピレン−パーフルオロアルキルビニルエーテル共重合体〔EPE〕、ポリ(クロロトリフルオロエチレン)〔PCTFE〕、テトラフルオロエチレン−エチレン共重合体〔ETFE〕、低融点エチレン−テトラフルオロエチレン共重合体,エチレン−クロロトリフルオロエチレン共重合体〔ECTFE〕、ポリフッ化ビニリデン〔PVDF〕、フルオロエチレン−ビニルエーテル共重合体〔FEVE〕、およびテトラフルオロエチレン−パーフルオロジオキソール共重合体〔TFEPD〕からなる群から選択される少なくとも一種のフッ素樹脂を含んでなり、
PTFEと該フッ素樹脂との合計を100重量%とするとき、該フッ素樹脂が0重量%を超えて50重量%未満で含有される請求項1または2に記載の親水化シート。 - 上記フッ素樹脂繊維が、PTFEのみを含んでなる請求項1または2に記載の親水化シート。
- 上記親水化処理が、親水性基を有する化合物で被覆する処理である請求項1〜4のいずれか一項に記載の親水化シート。
- 上記親水性基を有する化合物が、水酸基含有化合物、カルボン酸基含有化合物、スルホン酸基含有化合物、エーテル基含有化合物、エポキシ基含有化合物およびアミノ基含有化合物からなる群より選ばれる少なくとも一種の化合物である請求項5に記載の親水化シート。
- 上記親水性基を有する化合物が、ポリビニルアルコール〔PVA〕である請求項5または6に記載の親水化シート。
- 請求項1〜7のいずれか一項に記載の親水化シートを製造する方法であって、
フッ素樹脂繊維からなるフッ素樹脂繊維シートに対し、加熱された状態で、少なくとも二方向の応力を発生させ上記副繊維を生成させることによって、フッ素樹脂系シートを得る副繊維化工程;および、
該フッ素樹脂系シートの表面に親水化処理を施すことによって、親水化シートを得る親水化工程
を含むことを特徴とする、親水化シートの製造方法。 - 上記フッ素樹脂繊維シートが、電界紡糸法により作製したフッ素樹脂繊維をシート状に成形したフッ素樹脂繊維シートであり、
上記加熱の温度が、180℃以上400℃以下であり、
上記応力を、0.01kg/cm2以上10kg/cm2以下の圧縮荷重およびせん断荷重により発生させる、請求項8に記載の親水化シートの製造方法。 - 上記加熱の温度が、300℃以上360℃以下であり、
上記応力を、0.05kg/cm2以上1kg/cm2以下の圧縮荷重およびせん断荷重により発生させる、請求項9に記載の親水化シートの製造方法。 - 上記親水化工程が、
上記フッ素樹脂系シートを、上記親水性基を有する化合物の溶液に浸漬し、該フッ素樹脂系シートを、該化合物で被覆する工程(v);および、
工程(v)で得られたフッ素樹脂系シートを被覆している該化合物を、架橋する工程(vi)からなる請求項8〜10のいずれか一項に記載の親水化シートの製造方法。