JPWO2012026283A1 - Nbr組成物及びシール用ゴム材料 - Google Patents
Nbr組成物及びシール用ゴム材料 Download PDFInfo
- Publication number
- JPWO2012026283A1 JPWO2012026283A1 JP2012530599A JP2012530599A JPWO2012026283A1 JP WO2012026283 A1 JPWO2012026283 A1 JP WO2012026283A1 JP 2012530599 A JP2012530599 A JP 2012530599A JP 2012530599 A JP2012530599 A JP 2012530599A JP WO2012026283 A1 JPWO2012026283 A1 JP WO2012026283A1
- Authority
- JP
- Japan
- Prior art keywords
- wax
- weight
- nbr
- parts
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
2.前記不溶化物発生原因物質は、ワックス成分及び/又はステアリン酸であることを特徴とする上記1.に記載のNBR組成物。
3.前記ワックス成分が、スペシャルワックス(特殊マイクロクリスタリンワックス)、マイクロクリスタリンワックス、パラフィンワックス、蜜蝋、カルナバワックス、ラノリン、木蝋、モンタンワックス、オゾケライト、フィッシャー・トロプシュワックス、ポリエチレンワックス、脂肪酸エステル系ワックス、脂肪酸アミド、ジヘプタルデシルケトンから選ばれる少なくとも1つであることを特徴とする上記2.に記載のNBR組成物。
4.上記1.〜3.のいずれかに記載のNBR組成物を架橋成形して得られるシール用ゴム材料。
5.サイズG25のOリングをサンプルとし、JIS K6262に準拠して測定した第1の圧縮永久歪及び第2の圧縮永久歪が、46%以下であることを特徴とする上記4.に記載のシール用ゴム材料。
ポリマー:
高ニトリル(NBR)ポリマー(日本ゼオン製ニポールDN101 ニトリル含量:42.5% ムーニー粘度[ML1+4(100℃)]=77.5)
55重量部
NBR/PVCブレンドポリマー(JSR製NV60 PVC含量:35%)
45重量部
配合剤:
SRF級カーボンブラック(東海カーボン製シーストG−S)70重量部
酸化亜鉛(正同化学製酸化亜鉛特号) 5重量部
老化防止剤(精工化学製ノンフレックスRD) 2重量部
可塑剤(アジピン酸ジエチルヘキシル) 30重量部
硫黄 0.5重量部
加硫促進剤
CBS(大内新興化学工業製ノクセラーCZ) 2重量部
TMTD(大内新興化学工業製ノクセラーTET) 2.5重量部
PVC含量:
ポリマー中のPVC含量を重量%で示した。
加硫促進剤をのぞく上記配合物を混練後のゴム組成物について、ニーダーから排出する際の排出性を以下の基準で評価し、その結果を表1に示す。
×:ニーダーのローターにゴムが粘着し、ゴムの排出に10分以上要する場合
○:ニーダーのローターにゴムが粘着せず、比較的容易に排出できる場合
JIS K6253:1997に準拠し、タイプAデュロメーター(瞬時)で測定した。
2mmシートの架橋成形体を約5mm×5mmのゴム片に切断し、20gを燃料油(Fuel C:トルエン/イソオクタン=50:50(体積比)、JIS K6258)50mlに浸漬し、これを40℃にて5日間放置した。
次に本浸漬液からゴム片を取り除き、10mlに濃縮し、−15℃に5時間放置させることで浮遊物の形成を促進させ、その後、直ちに常温雰囲気にて2000rpmで5分間遠心分離して浮遊物を沈殿させた。
この沈殿が0.05ml以下を「◎」、0.1ml未満を「○」、0.1ml以上を「×」として評価した。なお、沈殿が0.1ml未満であれば機能上問題はない。
JIS K6262に準拠して測定を実施した。ただし、サンプルとしてOリング(サイズG25)を用い、圧縮率:25%、試験温度100℃で70時間加熱処理とした。製品機能から判断して、46%以下、好ましくは40%以下が良い。
JIS K6262に準拠して測定を実施した。ただし、圧縮率:25%、100℃で15時間後、恒温槽から圧縮装置を取り出してすぐにセット板を開放せずに、セット板を締めたままで常温に放置して、セット板を常温まで冷却した。セット板が常温になった状態で開放し、開放30分後の値を測定し、圧縮永久歪(%)を求めた。製品機能から判断して、46%以下、好ましくは40%以下が良い。
JIS K6259に準拠して試験および評価を行った(40℃、オゾン濃度50pphm、70時間)。亀裂なしは「N.C」とした。亀裂が認められた場合の評価は、JIS K6259附属書1、亀裂の評価方法に従って評価した。製品機能から判断して、「N.C」が好ましい。
JIS K6261に準拠して測定した。機能から判断して、好ましいのは−25℃以下であり、より好ましいのは−30℃以下である。
実施例1において、高ニトリルポリマーを50重量部、NBR/PVCブレンドポリマーを50重量部とした以外は同様にして評価した。
実施例1において、ステアリン酸を0.05重量部、ワックス(精工化学製サンタイトR)を0.05重量部加えた以外は同様にして評価した。
実施例1において、高ニトリルポリマーを100重量部とし、NBR/PVCブレンドポリマーを配合しない以外は同様にして評価した。
実施例1において、高ニトリルポリマーを60重量部、NBR/PVCブレンドポリマーを40重量部とした以外は同様にして評価した。
実施例1において、高ニトリルポリマーを45重量部、NBR/PVCブレンドポリマーを55重量部とした以外は同様にして評価した。
比較例1において、ステアリン酸を1重量部、ワックスを3重量部加えた以外は同様にして評価した。
実施例1において、ステアリン酸を1重量部加えた以外は同様にして評価した。
実施例1において、ワックスを1重量部加えた以外は同様にして評価した。
実施例1において、ステアリン酸を0.5重量部、ワックスを0.5重量%加えた以外は同様にして評価した。
実施例1において、ステアリン酸を0.1重量部、ワックスを0.1重量部加えた以外は同様にして評価した。
Claims (5)
- アクリロニトリル−ブタジエンゴム(NBR)と、ポリ塩化ビニル(PVC)を混合して得られ、PVC含量が15.70〜17.50重量%であるポリマー100重量部に対して、不溶化物発生原因物質を、配合しないか、配合する場合には上限が0.15重量部以下としてなることを特徴とするNBR組成物。
- 前記不溶化物発生原因物質は、ワックス成分及び/又はステアリン酸であることを特徴とする請求項1記載のNBR組成物。
- 前記ワックス成分が、スペシャルワックス(特殊マイクロクリスタリンワックス)、マイクロクリスタリンワックス、パラフィンワックス、蜜蝋、カルナバワックス、ラノリン、木蝋、モンタンワックス、オゾケライト、フィッシャー・トロプシュワックス、ポリエチレンワックス、脂肪酸エステル系ワックス、脂肪酸アミド、ジヘプタルデシルケトンから選ばれる少なくとも1つであることを特徴とする請求項2記載のNBR組成物。
- 請求項1〜3のいずれかに記載のNBR組成物を架橋成形して得られるシール用ゴム材料。
- サイズG25のOリングをサンプルとし、JIS K6262に準拠して測定した第1の圧縮永久歪及び第2の圧縮永久歪が、46%以下であることを特徴とする請求項4に記載のシール用ゴム材料。