JP6717295B2 - 色変換フィルム - Google Patents
色変換フィルム Download PDFInfo
- Publication number
- JP6717295B2 JP6717295B2 JP2017509437A JP2017509437A JP6717295B2 JP 6717295 B2 JP6717295 B2 JP 6717295B2 JP 2017509437 A JP2017509437 A JP 2017509437A JP 2017509437 A JP2017509437 A JP 2017509437A JP 6717295 B2 JP6717295 B2 JP 6717295B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- layer
- color conversion
- optical
- isocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
図1は本発明の一実施形態に係る光学フィルムの概略断面図である。図1において、光学フィルム10は、フィルム基材1と、当該フィルム基材1の一方の面上に形成されたマット層2とを備える。マット層2は表面に凹凸を有し、光源からの光を散乱することができる。
ポリオール樹脂は複数の水酸基を有する樹脂である。上記ポリオール樹脂としては、例えば、ポリエーテル系樹脂、ポリエステル系樹脂、ポリカーボネート系樹脂、ポリカプロラクトン系樹脂、アクリル系樹脂、エポキシ系樹脂、セルロース系樹脂、アセタール系樹脂、ポリエチレン系樹脂、ポリスチレン系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、メラミン系樹脂、フェノール系樹脂、及びシリコーン系樹脂等を用いることができる。これらの中でも、光学的透明性に優れていることから、アクリル系樹脂が好適に使用される。
上記イソシアネート系硬化剤は、ポリオール樹脂が有する水酸基と反応することが可能なイソシアネート基を有し、上記ポリオール樹脂を硬化することができる。イソシアネート系硬化剤としては、芳香族イソシアネート及びその誘導体、並びに、脂肪族イソシアネート及びその誘導体が好適に使用される。イソシアネート系硬化剤が芳香族イソシアネート又はその誘導体である場合、フィルム基材1とマット層2との間に一層高い密着性が得られる傾向がある。一方、イソシアネート系硬化剤が脂肪族イソシアネート又はその誘導体である場合、マット層2の耐光性が向上する傾向がある。
(C)成分としての帯電防止剤は水酸基を有し、当該水酸基は上記ポリオール樹脂の水酸基と反応せずに残った上記イソシアネート系硬化剤のイソシアネート基と反応することができる。水酸基を有する帯電防止剤としては、例えば、四級アンモニウム塩、高分子−金属塩複合物、及び導電性高分子等を用いることができる。(C)成分としての帯電防止剤の水酸基当量(1当量の水酸基を含む帯電防止剤の質量(g))は、100〜1000g/eqであることが好ましく、200〜900g/eqであることがより好ましく、300〜800g/eqであることがさらに好ましい。水酸基当量が、100g/eq以上であることにより、(A)成分、(B)成分及び溶媒と(C)成分との相溶性が向上する傾向がある。水酸基当量が1000g/eq以下であることにより、反応性が向上し、過剰なブリードアウトを抑制しやすくなる傾向がある。(C)成分としての帯電防止剤の分子量は、200〜20000であることが好ましく、250〜10000であることがより好ましい。分子量が200以上であることにより、過剰なブリードアウトを抑制することができる傾向がある。分子量が20000以下であることにより、帯電防止効果が得られやすくなる傾向がある。(C)成分としての帯電防止剤は、水酸基を1〜100有していることが好ましく、2〜50有していることがより好ましい。分子中の水酸基の数が1以上であることにより、帯電防止剤の水酸基とイソシアネート基とが反応する機会が増え、過剰なブリードアウトを抑制することができる傾向がある。分子中の水酸基の数が100以下であることにより、(A)成分、(B)成分及び溶媒との相溶性が向上する傾向がある。
マット層2を形成する樹脂組成物は、さらに(D)微粒子を含有することが好ましい。上記微粒子は無機微粒子又は有機微粒子であることができる。無機微粒子としては、シリカ、クレー、タルク、炭酸カルシウム、硫酸カルシウム、硫酸バリウム、珪酸アルミニウム、酸化チタン、合成ゼオライト、アルミナ、及びスメクタイト等が挙げられる。有機微粒子としては、スチレン樹脂、ウレタン樹脂、ベンゾグアナミン樹脂、シリコーン樹脂、及びアクリル樹脂等が挙げられる。これらのうち、球状粒子を得やすく、マット層2の表面の凹凸形状を制御しやすい観点から、有機微粒子を用いることが好ましい。微粒子は、1種のみ使用してもよく、複数種を組み合わせて使用してもよい。上記微粒子の平均粒子径は0.5〜30μmであることが好ましく、1〜20μmであることがより好ましい。平均粒子径が上記範囲内にあることにより、マット層2の表面に、光の散乱に十分であり、且つ、他部材を傷つけないように制御された凹凸を付与することができる傾向がある。
(実施例1)
以下に示す材料を混合し、マット層組成物を調製した。透明フィルム基材(厚さ:25μm、ポリエチレンテレフタレートフィルム、商品名:テイジンテトロンフィルムHPE、帝人デュポンフィルム社製)上にワイヤーバーコーターにより上記マット層組成物を塗布し、塗膜を80℃30秒間乾燥し、50℃72時間エージングすることにより、透明フィルム基材上に厚さ3μmのマット層を形成し、光学フィルムを作製した。
・アクリル系ポリオール樹脂(DIC社製、商品名:アクリディックA−814)100質量部
・イソシアネート系硬化剤(DIC社製、商品名:バーノックDN−980、ヘキサメチレンジイソシアネート系化合物)8.5質量部
・帯電防止剤(四級アンモニウム塩、第一工業製薬社製、商品名:レジスタットPU−101、水酸基当量:316.1g/eq)10質量部
・微粒子(ポリウレタン、平均粒径2μm)10質量部
・溶剤(酢酸エチル)70質量部
帯電防止剤として、レジスタットPU−101 10質量部に代えて、下記表1に示す帯電防止剤を用いたこと以外は、実施例1と同様にしてマット層組成物を調製し、光学フィルムを作製した。
イソシアネート系硬化剤として、バーノックDN−980に代えて、下記表2に示すイソシアネート系硬化剤を用いたこと以外は、実施例1と同様にしてマット層組成物を調製し、光学フィルムを作製した。
イソシアネート系硬化剤として、バーノックDN−980に代えて、下記表2に示すイソシアネート系硬化剤を用いたこと以外は、比較例4と同様にしてマット層組成物を調製し、光学フィルムを作製した。
実施例及び比較例で作製した各光学フィルムを、下記の方法に従って評価した。
JIS−K6911に準拠して高抵抗抵抗率計(ダイアインスツルメンツ社製、ハイレスターMCP−HT260)を用いて、実施例及び比較例で得られた各光学フィルムのマット層の表面抵抗率を測定した。測定結果を表1又は2に示す。
実施例及び比較例で得られた各光学フィルムを温度65℃相対湿度95%の環境下で1000時間保持し、常温環境に取り出した。取り出した各光学フィルムのマット層表面を目視にて観察した。観察結果を、以下の基準に従って評価した。評価結果を表1又は2に示す。
A:ブリードアウトに起因する外観ムラが認められない。
B:ブリードアウトに起因する外観ムラが認められる。
C:ブリードアウトに起因する外観ムラが顕著に認められる。
実施例及び比較例で得られた各光学フィルムを温度65℃相対湿度95%の環境下で1000時間保持し、常温環境に取り出した。バックライトユニットの導光板を模した厚さ188μmのポリカーボネートフィルムと取り出した各光学フィルムとを、マット層とポリカーボネートフィルムとが接するように重ね、これらに25kgf/cm2の荷重を掛け、30秒放置した。その後、各光学フィルムからポリカーボネートフィルムを剥がし、剥がした後のポリカーボネートフィルム表面(剥離面)を目視にて観察した。表面の観察結果を、以下の基準に従って評価した。評価結果を表1又は2に示す。
A:ブリードアウト物の転写が認められない。
B:ブリードアウト物の転写が認められる。
C:ブリードアウト物の転写が顕著に認められる。
実施例及び比較例で得られた各光学フィルムを温度65℃相対湿度95%の環境下で1000時間保持し、常温環境に取り出した。取り出した各光学フィルムのマット層側の表面に対して、JIS K 5400に従い、100マスの碁盤目試験を行い、フィルム基材上に欠けずに残っている碁盤目状のマット層のマスの数を数えた。各光学フィルムのマット層とフィルム基材との密着性を、以下の基準に従って評価した。残っているマスの数と密着性の評価結果を表1又は2に示す。
A:フィルム基材上に欠けずに残っている碁盤目状のマット層の割合が10割である。
B:フィルム基材上に欠けずに残っている碁盤目状のマット層の割合が5割以上10割未満である。
C:フィルム基材上に欠けずに残っている碁盤目状のマット層の割合が5割未満である。
実施例及び比較例で得られた各光学フィルムに、紫外線カーボンアークを光源とした紫外線オートフェードメーター(スガ試験機株式会社製、U48AU)を用いて、マット層側から紫外線を100時間照射した。自動分光光度計(株式会社日立製作所製、U−4100)を用いて、紫外線照射前後における各光学フィルムの透過分光スペクトルを作成し、波長450nmの紫外線の透過率を測定した。紫外線照射前後での黄変を以下の基準に従って評価し、黄変の評価結果を耐光性の評価結果とした。評価結果を表1又は2に示す。
A:紫外線照射前後での透過率の低減が1%未満である。
B:紫外線照射前後での透過率の低減が1%以上3%未満である。
C:紫外線照射前後での透過率の低減が3%以上である。
・エソカードC/25:ライオン・スペシャリティ・ケミカルズ社製、四級アンモニウム塩(水酸基当量:334.5g/eq)
・PEL−25:日本カーリット社製、高分子−Li塩複合物(水酸基当量:758.1g/eq)
・ライトエステルDQ100:共栄社化学社製、四級アンモニウム塩(水酸基なし)
・ジメチルジステアリルアンモニウムクロリド:東京化成工業株式会社製(水酸基なし)
・タケネートD−110N:三井化学社製、キシリレンジイソシアネート系化合物(トリメチロールプロパン付加体)。
・タケネートD−101A:三井化学社製、トルエンジイソシアネート系化合物。
Claims (6)
- 色変換層と、当該色変換層の両面上に形成された一対の光学バリアフィルムと、を備え、
前記光学バリアフィルムの少なくとも一方が、光学フィルムと、蒸着膜層と、を備え、前記蒸着膜層が金属酸化物を含有する、光学バリアフィルムであり、
前記光学フィルムが、フィルム基材と、当該フィルム基材の一方の面上に形成されたマット層とを備え、前記マット層が(A)ポリオール樹脂、(B)イソシアネート系硬化剤、及び(C)水酸基を有する帯電防止剤を含有する樹脂組成物から形成されてなる、光学フィルムであり、
前記蒸着膜層は、前記フィルム基材の前記マット層と反対側に配置されている、色変換フィルム。 - 前記(B)イソシアネート系硬化剤がキシリレンジイソシアネート系化合物である、請求項1に記載の色変換フィルム。
- 前記樹脂組成物が(D)微粒子をさらに含有する、請求項1又は2に記載の色変換フィルム。
- 前記(C)水酸基を有する帯電防止剤が四級アンモニウム塩を含む、請求項1〜3のいずれか一項に記載の色変換フィルム。
- 前記マット層の表面抵抗率が1.0×1013Ω/□以下である、請求項1〜4のいずれか一項に記載の色変換フィルム。
- 前記金属酸化物が酸化ケイ素を含む、請求項1〜5のいずれか一項に記載の色変換フィルム。