CN107163275A - 一种用于电磁屏蔽膜的哑光性油墨膜及其制备方法 - Google Patents
一种用于电磁屏蔽膜的哑光性油墨膜及其制备方法 Download PDFInfo
- Publication number
- CN107163275A CN107163275A CN201710561449.9A CN201710561449A CN107163275A CN 107163275 A CN107163275 A CN 107163275A CN 201710561449 A CN201710561449 A CN 201710561449A CN 107163275 A CN107163275 A CN 107163275A
- Authority
- CN
- China
- Prior art keywords
- dumb light
- film
- electromagnetic shielding
- resin
- light ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种用于电磁屏蔽膜的哑光性油墨膜及其制备方法，所述哑光性油墨膜包括基层、亚光层和油墨层，所述括基层、亚光层和油墨层顺次固定连接。所述的哑光性油墨膜，配方设计范围广泛、原料易得，可替代磨砂亚光膜，具有节约资源的优点。其制备方法具有制备方法简便、实用等优点，采用成熟工艺进行制备，方便工业推广应用。
Description
技术领域
本发明涉及电子产品制备技术领域，具体而言，涉及一种用于电磁屏蔽膜的哑光性油墨膜及其制备方法。
背景技术
随着智能手机，平板电脑等数字电子产品的发展，技术进步和社会需求，电子通讯产品线路上会大量地使用电磁屏蔽膜。目前的电磁屏蔽膜油墨层存在配方开发成本高，资源消耗大，调整缓慢，亚光度可设计性较差等不足等问题。油墨的亚光性特征不能满足于不同客户端要求。
有鉴于此，特提出本发明。
发明内容
本发明的第一目的在于提供一种用于电磁屏蔽膜的哑光性油墨膜，以解决上述问题，所述的哑光性油墨膜，配方设计范围广泛、原料易得，可替代磨砂亚光膜，具有节约资源的优点。
本发明的第二目的在于提供一种所述的用于电磁屏蔽膜的哑光性油墨膜的制备方法，该方法具有制备方法简便、实用等优点，采用成熟工艺进行制备，方便工业推广应用。
为了实现本发明的上述目的，特采用以下技术方案：
一种用于电磁屏蔽膜的哑光性油墨膜，所述哑光性油墨膜包括基层、亚光层和油墨层，所述括基层、亚光层和油墨层顺次固定连接。
优选的，所述基层，由按照质量份数计的如下组份制备而成：
亚光填料0.5～10份、助剂0.5～2份、溶剂10～60份和树脂10～40份。
优选的，所述亚光填料选自二氧化硅、滑石粉、硬脂酸铝、硬脂酸钙、苯胺树脂、聚氨酯类化合物中的一种；
更优选的，以质量份数计，所述二氧化硅为0.5～3份；
更优选的，以质量份数计，所述滑石粉为1～2份；
更优选的，以质量份数计，所述硬脂酸铝为0.5～10份；
更优选的，以质量份数计，所述苯胺树脂为0.5～3份；
更优选的，以质量份数计，所述聚氨酯类化合物为0.5～10份。
优选的，所述树脂选自环氧树脂、聚丙烯酸树脂、改性橡胶、酚醛树脂、聚酯树脂、聚酰胺树脂、聚氨酯树脂中的一种或者几种的组合。
优选的，所述助剂为超分散剂或者偶联剂，优选的所述超分散剂选自酰胺类或者聚羧酸盐类分散剂。
优选的，所述溶剂选自酮类、酯类、酰胺类溶剂；
更优选的，所述溶剂选自丙酮、丁酮、环己酮、乙酸乙酯、甲基亚酰胺和亚甲基吡咯烷酮中的一种。
优选的，所述亚光膜层为PET膜或PBT膜。
优选的，所述基层为4-15μm。
优选的，所述油墨层选自环氧树脂体系、亚克力体系、聚氨酯体系、聚丙烯酸体系油墨胶黏剂中的一种。
所述的用于电磁屏蔽膜的哑光性油墨膜，包括以下步骤：
混合亚光填料、助剂、溶剂、树脂混合，加入固化剂固化，将亚光膜层涂布于基层，熟化后形成亚光特征的基层，然后涂布油墨于所述亚光特征的基层，得到该哑光性油墨膜。
与现有技术相比，本发明的有益效果为：
(1)本发明所提供的用于电磁屏蔽膜的哑光性油墨膜，所述的哑光性油墨膜，配方设计范围广泛、原料易得，可替代磨砂亚光膜，具有节约资源的优点。
(2)本发明所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，具有简便、实用等优点，采用成熟工艺进行制备，方便工业推广应用。
附图说明
为了更清楚地说明本发明具体实施方式或现有技术中的技术方案，下面将对具体实施方式或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图是本发明的一些实施方式，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明一种具体实施方式所得用于电磁屏蔽膜的哑光性油墨膜结构示意图。
附图标记：
1-基层； 2-哑光层； 3-油墨层。
具体实施方式
下面将结合附图和具体实施方式对本发明的技术方案进行清楚、完整地描述，但是本领域技术人员将会理解，下列所描述的实施例是本发明一部分实施例，而不是全部的实施例，仅用于说明本发明，而不应视为限制本发明的范围。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
在本发明的描述中，需要说明的是，术语“中心”、“上”、“下”、“左”、“右”、“竖直”、“水平”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。此外，术语“第一”、“第二”、“第三”仅用于描述目的，而不能理解为指示或暗示相对重要性。
在本发明的描述中，需要说明的是，除非另有明确的规定和限定，术语“安装”、“相连”、“连接”应做广义理解，例如，可以是固定连接，也可以是可拆卸连接，或一体地连接；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通。对于本领域的普通技术人员而言，可以具体情况理解上述术语在本发明中的具体含义。
本发明具体实施方式一种用于电磁屏蔽膜的哑光性油墨膜，所述哑光性油墨膜包括基层1、亚光层和油墨层3，所述括基层1、亚光层和油墨层3顺次固定连接。
本发明的膜包括基层1、亚光层和油墨层3，所述基层1、亚光层和油墨层3顺次固定连接，哑光层2不经过磨砂，而是掺入哑光粉体。并且原料易得，可替代磨砂亚光膜，具有节约资源的优点。
本发明一种优选的具体实施方式中，所述基层1，由按照质量份数计的如下组份制备而成：
亚光填料0.5～10份、助剂0.5～2份、溶剂10～60份和树脂10～40份。
按照既定份数制备基层1，树脂一般不溶于水，能溶于有机溶剂。因此，配合适当的溶剂和助剂有助于填料更均匀的分散于树脂中。
本发明一种优选的具体实施方式中，所述亚光填料选自二氧化硅、滑石粉、硬脂酸铝、硬脂酸钙、苯胺树脂、聚氨酯类化合物中的一种；
更优选的，以质量份数计，所述二氧化硅为0.5～3份；
更优选的，以质量份数计，所述滑石粉为1～2份；
更优选的，以质量份数计，所述硬脂酸铝为0.5～10份；
更优选的，以质量份数计，所述苯胺树脂为0.5～3份；
更优选的，以质量份数计，所述聚氨酯类化合物为0.5～10份。
每种填料在一定优选的份数范围内，高度分散于树脂中，得到很好的哑光效果。
本发明一种优选的具体实施方式中，所述树脂选自环氧树脂、聚丙烯酸树脂、改性橡胶、酚醛树脂、聚酯树脂、聚酰胺树脂、聚氨酯树脂中的一种或者几种的组合。
本发明一种优选的具体实施方式中，所述助剂为超分散剂或者偶联剂，优选的所述超分散剂选自酰胺类或者聚羧酸盐类分散剂。
超分散剂又名超级分散剂，一种特殊的表面活性剂，分子结构含有两个在溶解性和极性上相对的基团，其中一个是较短的极性基，称为亲水基，其分子结构特点使其很容易定向排列在物质表面或两相界面上，降低界面张力，对水性分散体系有很好的分散效果。超分散剂的分子结构分为两部分：其中一部分为锚固基团，常见的有-R2N、-R3N+、-COOH、-COO-、-SO3H、-SO2 -、-PO4 2-、多元胺、多元醇及聚醚等，它们可通过离子键、共价键、氢键及范德华力等相互作用紧紧地吸附在固体颗粒表面，防止超分散剂脱附；另一部分为溶剂化链。在极性匹配的分散介质中，溶剂化链与分散介质具有良好的相容性，在分散介质中采取比较伸展的构象，在固体颗粒表面形成足够厚度的保护层。
现有市售超分散剂有BYK、Silock、Elvacite、Hypersol、Solsperse系列等。
本发明一种优选的具体实施方式中，所述溶剂选自酮类、酯类、酰胺类溶剂；
更优选的，所述溶剂选自丙酮、丁酮、环己酮、乙酸乙酯、甲基亚酰胺和亚甲基吡咯烷酮中的一种。
本发明一种优选的具体实施方式中，所述亚光膜层为PET膜或PBT膜。
PET膜聚对苯二甲酸乙二醇酯，化学式为COC6H4COOCH2CH2O。(英文：Polyethyleneterephthalate，简称PET)，由对苯二甲酸二甲酯与乙二醇酯交换或以对苯二甲酸与乙二醇酯化先合成对苯二甲酸双羟乙酯，然后再进行缩聚反应制得。属结晶型饱和聚酯，为乳白色或浅黄色、高度结晶的聚合物，表面平滑有光泽。
聚对苯二甲酸丁二醇酯，又名聚对苯二甲酸四次甲基酯。英文名；Polybutyleneterephthalate。简称PBT PBTP或PTMT，它是对苯甲酸与1,4-丁二醇的缩聚物。可由酯交换法或直接脂化法经缩聚而制得，今后的发展趋势为直接酯化法生产。PBT和PET一起被称为热塑性聚酯。
PBT主链是由每个重复单元为刚性苯环和柔性脂肪醇连接起来的饱和线性分子组成，分子的高度几何规整性和刚性部分使聚合物具有高的机械强度，突出的耐化学试剂性，耐热性和优良的电性能；分子中没有侧链，结构对称，满足紧密堆砌的要求，从而使这种聚合物有高度的结晶形和高熔点，分子的结构决定了PBT具有良好的综合性能。
本发明一种优选的具体实施方式中，所述基层1为4-15μm。
本发明一种优选的具体实施方式中，所述油墨层3选自环氧树脂体系、亚克力体系、聚氨酯体系、聚丙烯酸体系油墨胶黏剂中的一种。
本发明一种优选的具体实施方式中，所述的用于电磁屏蔽膜的哑光性油墨膜，包括以下步骤：
混合亚光填料、助剂、溶剂、树脂混合，加入固化剂固化，将亚光膜层涂布于基层1，熟化后形成亚光特征的基层1，然后涂布油墨于所述亚光特征的基层1，得到该哑光性油墨膜。
本发明所提供一种用于电磁屏蔽膜的哑光性油墨膜的制备方法，具有制备方法简便、实用等优点，采用成熟工艺进行制备，方便工业推广应用。
具体的，在制备的时候，该方法将填料和树脂、助剂、溶剂配入容器中搅拌均匀，分散机高速分散，然后装入球磨机中球磨，管控细度，达到要求过滤出预聚物，然后配入固化剂检验合格即可使用，工艺上采用常规的成熟技术，使得本新型的制造工艺简单易实现，便于在工业上推广应用。
本发明具体实施方式中所采用的各原料信息如下：
聚羧酸盐类分散剂：型号为SN-5029，生产商为广州富飞；
环氧树脂：型号为4129，生产商为吉得化工；
环氧树脂体系油墨胶黏剂：型号为AINK，生产商为本公司制备；
聚氨酯树脂：型号为MR918，生产商为东莞米人占化工；
偶联剂：型号为KH-560，生产商为南京创世化工。
实施例1
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将二氧化硅0.5g、聚羧酸盐类超分散剂0.5g、丙酮59g和环氧树脂40g混合后搅拌25分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用25微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实施例2
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将滑石粉2g、酰胺类超分散剂2g、丙酮60g和聚氨酯树脂36g混合后搅拌30分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用25微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实施例3
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将硬脂酸铝3g、偶联剂1g、甲基亚酰胺10g和环氧树脂40g混合后搅拌25分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用25微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实施例4
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将聚氨酯类化合物1g、聚羧酸盐类分散剂1g、丙酮50g和酚醛树脂40g混合后搅拌25分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用25微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实施例5
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将滑石粉3g、聚羧酸盐类分散剂2g、丙酮55g和环氧树脂40g混合后搅拌25分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用25微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实施例6
本实施例所提供的用于电磁屏蔽膜的哑光性油墨膜的制备方法，包括以下步骤：
(1)、将二氧化硅3g、酰胺类分散剂1g、丙酮46g和环氧树脂30g混合后搅拌25分钟，经分散机高速分散后，装入球磨桶中球磨，球磨后用30微米的滤袋进行过滤，加入固化剂后，得到基层1；
(2)、在步骤(1)中的基层1中上涂布PET膜作为哑光层2并固化，在哑光层2上涂布环氧树脂体系油墨胶黏剂作为油墨层3，熟化后，得到该哑光性油墨膜。
实验例
本申请实施例所提供的用于电磁屏蔽膜的哑光性油墨膜与现用亚光膜(MGF024，苏州城邦达力材料科技有限公司)测试比较，结果如表1所示。
表1测试结果
实验结果表明，本实例体现出对原膜的要求降低，由专有磨砂型体现亚光度转变为由哑光剂体现合适的哑光性能，对原膜要求范围广泛许多。
尽管已用具体实施例来说明和描述了本发明，然而应意识到，以上各实施例仅用以说明本发明的技术方案，而非对其限制；本领域的普通技术人员应当理解：在不背离本发明的精神和范围的情况下，可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围；因此，这意味着在所附权利要求中包括属于本发明范围内的所有这些替换和修改。
Claims (10)
1.一种用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述哑光性油墨膜包括基层、亚光层和油墨层，所述括基层、亚光层和油墨层顺次固定连接。
2.根据权利要求1所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述基层，由按照质量份数计的如下组份制备而成：
亚光填料0.5～10份、助剂0.5～2份、溶剂10～60份和树脂10～40份。
3.根据权利要求2所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述亚光填料选自二氧化硅、滑石粉、硬脂酸铝、硬脂酸钙、苯胺树脂、聚氨酯类化合物中的一种；
优选的，以质量份数计，所述二氧化硅为0.5～3份；
优选的，以质量份数计，所述滑石粉为1～2份；
优选的，以质量份数计，所述硬脂酸铝为0.5～10份；
优选的，以质量份数计，所述苯胺树脂为0.5～3份；
优选的，以质量份数计，所述聚氨酯类化合物为0.5～10份。
4.根据权利要求3所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述树脂选自环氧树脂、聚丙烯酸树脂、改性橡胶、酚醛树脂、聚酯树脂、聚酰胺树脂、聚氨酯树脂中的一种或者几种的组合。
5.根据权利要求3所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述助剂为超分散剂或者偶联剂，优选的所述超分散剂选自酰胺类或者聚羧酸盐类分散剂。
6.根据权利要求3所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述溶剂选自酮类、酯类、酰胺类溶剂；
优选的，所述溶剂选自丙酮、丁酮、环己酮、乙酸乙酯、甲基亚酰胺和亚甲基吡咯烷酮中的一种。
7.根据权利要求1所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述亚光膜层为PET膜或PBT膜。
8.根据权利要求1所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述基层为4-15μm。
9.根据权利要求1所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，所述油墨层选自环氧树脂体系、亚克力体系、聚氨酯体系、聚丙烯酸体系油墨胶黏剂中的一种。
10.根据权利要求1-9任一项所述的用于电磁屏蔽膜的哑光性油墨膜，其特征在于，包括以下步骤：
混合亚光填料、助剂、溶剂、树脂混合，加入固化剂固化，将亚光膜层涂布于基层，熟化后形成亚光特征的基层，然后涂布油墨于所述亚光特征的基层，得到该哑光性油墨膜。