JP6065002B2 - 画像表示装置用粘着シート、画像表示装置の製造方法及び画像表示装置 - Google Patents
画像表示装置用粘着シート、画像表示装置の製造方法及び画像表示装置 Download PDFInfo
- Publication number
- JP6065002B2 JP6065002B2 JP2014512505A JP2014512505A JP6065002B2 JP 6065002 B2 JP6065002 B2 JP 6065002B2 JP 2014512505 A JP2014512505 A JP 2014512505A JP 2014512505 A JP2014512505 A JP 2014512505A JP 6065002 B2 JP6065002 B2 JP 6065002B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- meth
- image display
- acrylate
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
<画像表示装置用粘着シート>
本実施形態の画像表示装置用粘着シートは、粘着層と、粘着層を挟むように積層された一対の基材層と、を備えており、基材層の外縁は、粘着層の外縁よりも外側に張り出している。
厚み0.5mm、幅10mm、長さ10mmの粘着層を作製し、広域動的粘弾性測定装置(Rheometric Scientific社製、Solids Analyzer RSA−II)を用いて、条件「シェアサンドイッチモード、周波数1.0Hz、測定温度範囲−20〜100℃で昇温速度5℃/分」にて測定できる。
(A)(メタ)アクリル酸誘導体ポリマーとは、(メタ)アクリロイル基を分子内に1つ有するモノマーを1種で重合するか又は2種以上組み合わせて共重合したものをいう。なお、本実施形態の効果を損なわない範囲であれば、(A)成分は、(メタ)アクリロイル基を分子内に2個以上有する化合物、又は(メタ)アクリロイル基を有していない重合性化合物(アクリロニトリル、スチレン、酢酸ビニル、エチレン、プロピレン等の重合性不飽和結合を分子内に1個有する化合物、ジビニルベンゼン等の重合性不飽和結合を分子内に2個以上有する化合物)を、(メタ)アクリロイル基を分子内に1つ有するモノマーと共重合させたものであってもよい。
CH2=CXCOOR ・・・(b)
式(b)中、Xは水素原子又はメチル基を示し、Rは炭素数4〜18のアルキル基を示す。
CH2=CXCOO(CpH2pO)qR ・・・(x)
式(x)中、Xは水素原子又はメチル基を示し、Rは水素原子又は炭素数1〜10のアルキル基を示し、pは2〜4の整数を示し、qは1〜10の整数を示す。
(B)(メタ)アクリロイル基を分子内に1つ有する(メタ)アクリル酸誘導体モノマーとしては、前記(A)成分を形成する(メタ)アクリロイル基を分子内に1つ有するモノマーとして例示した化合物と同様のものが挙げられる。
(C)成分の具体例としては、下記式(c)〜(h)で表される化合物が好適に例示される。ただし、式(c)、(d)及び(e)中、sは1から20の整数を示し、式(f)及び(g)中、m及びnはそれぞれ独立に、1から10の整数を示す。
(D)成分は、活性エネルギー線の照射により粘着性樹脂組成物の硬化反応を促進させるために当該組成物に含まれる。ここで活性エネルギー線とは、紫外線、電子線、α線、β線、γ線等をいう。
粘着性樹脂組成物には、必要に応じて上記の(A)、(B)、(C)、及び(D)成分とは別に、各種添加剤を含有させてもよい。含有可能な各種添加剤としては、例えば、粘着性樹脂組成物の保存安定性を高める目的で添加するパラメトキシフェノール等の重合禁止剤、粘着性樹脂組成物を光硬化させて得られる粘着層の耐熱性を高める目的で添加するトリフェニルホスファイト等の酸化防止剤、紫外線等の光に対する粘着性樹脂組成物の耐性を高める目的で添加するHALS(Hindered Amine Light Stabilizer)等の光安定化剤、ガラス等に対する粘着性樹脂組成物の密着性を高めるために添加するシランカップリング剤が挙げられる。
以上に説明した粘着シート1は、次のように製造される。まず、図4に示されるように、重剥離セパレータ3上に粘着層2が形成され、粘着層2上に仮セパレータ6が形成された母材フィルム10を準備する。仮セパレータ6は、例えば、軽剥離セパレータ4と同じ素材からなる層である。
次に、粘着シート1を用いて作製される画像表示装置について説明する。粘着シート1が備える粘着層2は、各種画像表示装置に適用することができる。画像表示装置としては、プラズマディスプレイ(PDP)、液晶ディスプレイ(LCD)、陰極線管(CRT)、電界放出ディスプレイ(FED)、有機ELディスプレイ(OELD)、3Dディスプレイ、電子ペーパー(EP)等が挙げられる。本実施形態の粘着層2は、画像表示装置の反射防止層、防汚層、色素層、ハードコート層等の機能性を有する機能層、透明保護板を組み合わせて貼り合わせるために使用することもできる。
粘着シート1は、画像表示装置の組み立て等において次のように使用される。まず、図11に示されるように、軽剥離セパレータ4を粘着シート1からから剥離して粘着層2の粘着面2bを露出させる。続いて、図12に示されるように、粘着層2の粘着面2bを被着物A1に貼り付け、ローラーR等で押し付ける。この際、被着物A1の表面に設けられた段差60は、粘着層2により埋め込まれる。被着物A1は、例えば画像表示ユニット、透明保護板又はタッチパネルである。続いて、図13に示されるように、重剥離セパレータ3を粘着層2から剥離して粘着層2の粘着面2cを露出させる。続いて、図14に示されるように、粘着層2の粘着面2cを被着物A2に貼り付け、加熱加圧処理(オートクレーブ処理)をする。被着物A2は、例えば画像表示ユニット、透明保護板又はタッチパネルである。このようにして、粘着層2を介して被着物同士を貼り合わせ、積層体を得ることができる。なお、この時の加熱加圧処理条件は、温度が40〜80℃であり、圧力が0.3〜0.8MPaであるが、被着物表面の段差が40〜100μmである場合は、段差近傍の気泡をより除去できる観点から、温度が50〜70℃であり圧力が0.4〜0.7MPaであることが好ましい。また、処理時間は、5〜60分が好ましく、10〜50分であることがより好ましい。
<画像表示装置用粘着シート>
本実施形態の画像表示装置用粘着シートは、フィルム状の粘着層と、粘着層を挟むように積層された第1及び第2の基材層と、第2の基材層に更に積層されたキャリア層と、を備えており、第1の基材層及びキャリア層の外縁は、粘着層の外縁よりも外側に張り出している。
粘着シート1は、次のように製造される。まず、図17に示されるように、キャリアフィルム5上に、重剥離セパレータ3、粘着層2、及び仮セパレータ6が順に積層された母材フィルム10を準備する。仮セパレータ6は、例えば、軽剥離セパレータ4と同じ素材からなる層である。
本実施形態の粘着シート1は、最初に、図23に示されるように、キャリアフィルム5を重剥離セパレータ3から剥離してから用いることを除いては、第一実施形態の粘着シートと同様にして使用することができる。
冷却管、温度計、攪拌装置、滴下漏斗及び窒素導入管の付いた反応容器に、2−エチルヘキシルアクリレート84.0g、2−ヒドロキシエチルアクリレート36.0g及びメチルエチルケトン150.0gを加え、100mL/分の風量で窒素置換しながら、15分間で常温(25℃)から70℃まで加熱することで溶液aを調製した。
(東ソー(株)製、商品名)
使用溶媒:テトラヒドロフラン(THF)
カラム:カラムTSKGEL SuperMultipore HZ−H
(東ソー(株)製、商品名)
カラムサイズ:カラム長が15cm、カラム内径が4.6mm
測定温度:40℃
流量:0.35ml/分
試料濃度:10mg/THF5ml
注入量:20μl
冷却管、温度計、攪拌装置、滴下漏斗及び空気注入管のついた反応容器に、ポリプロピレングリコール(分子量2000)303.92g、ε−カプロラクトン2モルで変性した2−ヒドロキシエチルアクリレート(プラクセルFA2D:ダイセル化学工業株式会社、商品名)8.66g、2−ヒドロキシエチルアクリレート99.74g、p−メトキシフェノール0.12g及びジブチル錫ジラウレート0.5gを加えて空気を流しながら75℃に昇温し、さらに75℃で攪拌しつつ、イソホロンジイソシアネート36.41gを2時間かけて均一滴下し、反応を行った。
A成分:アクリル酸誘導体ポリマー(A−1)
B成分:アクリロイルモルホリン(ACMO)
:2−エチルヘキシルアクリレート(EHA)
C成分:ポリプロピレングリコールジアクリレート(FA−P240A:日立化成工業(株)製「ファンクリル FA−P240A」:式(e)で示され、nの平均値が7)
:ポリウレタンジアクリレート(PUDA:2官能の(メタ)アクリロイル基を有する架橋剤)
D成分:1−ヒドロキシシクロヘキシルフェニルケトン(I−184:BASF社製)
[粘着シート1の作製(3層品)]
重剥離セパレータ3として厚み75μmのポリエチレンテレフタレート(藤森工業(株)社製)、並びに軽剥離セパレータ4及び仮セパレータ6として厚み50μmのポリエチレンテレフタレート(藤森工業(株)社製)を用いて、以下の(I)〜(VI)の手順で粘着シート1を作製した。
配合条件及び露光量を表1及び表2に示すとおりとしたこと以外は、実施例1と同様にして粘着シート1を得た。
各実施例及び比較例で得られた粘着シートについて、以下の(1)〜(6)の評価を行った。
厚さ250μmの粘着層を2枚重ねて約500μm厚さにし、幅10mm、長さ10mmに裁断してサンプルを作製した。前記サンプルを2つ準備し、図24に示すように、治具100を用いて両端のプレートP1と中央のプレートP2との間でサンプルSをはさみ込み測定サンプルとした。そして、広域動的粘弾性測定装置(Rheometric Scientific社製、Solids Analyzer RSA−II)を用いて、サンプルのガラス転移温度(Tg)、剪断貯蔵弾性率、損失弾性率及びtanδを測定した。測定条件は「シェアサンドイッチモード、周波数1.0Hz、測定温度範囲−20〜100℃で昇温速度5℃/分」とした。
各実施例及び比較例で得られた粘着シートを幅50mm、長さ80mmのサイズに裁断した。そして、軽剥離セパレータ4を剥離し、粘着層を58mm×86mm×0.7mm(厚さ)のガラス基板Aにローラーを用いて貼り合わせた。
(評価基準)
段差部内周壁とガラス基板との接合部近傍(開口部が有する4辺)における気泡の有無を確認した。
A:気泡無し、又は1辺のみに気泡が残る
B:2辺に気泡が残る
C:3辺以上に気泡が残る
(III)の切断の工程において、以下の基準で評価した。
(評価基準)
A:重剥離セパレータ3、粘着層2、及び仮セパレータ6を所望の形状に容易に切断できる。
B:粘着層がロータリーブレードに張り付き作業性が低下する、又は重剥離セパレータ3、粘着層2、及び仮セパレータ6を所望の形状に切断できない。
各実施例及び比較例で得られた粘着シートを幅10mm、長さ50mmのサイズに裁断した。そして、軽剥離セパレータ4を剥離し、粘着層2をガラス基板(ソーダライムガラス)又はアクリル樹脂基板(以下、「アクリル基板」という場合もある)に貼り付けた後、紫外線照射装置により各基板側から紫外線を2000mJ/cm2照射した。その後、重剥離セパレータ3を剥離し、引張試験機((株)オリエンテック製「RTC−1210」)を用いて粘着層2を180度剥離した際の、粘着層2と各基板との剥離強度を測定した。測定条件は、剥離速度300mm/分で3秒間剥離とし、測定温度は25℃として測定した。
各実施例及び比較例で得られた粘着シートを幅50mm、長さ100mmのサイズに裁断した。そして、軽剥離セパレータ4を剥離し、粘着層2を、50mm×100mm×0.7mm(厚さ)の寸法のガラス基板に、25℃、大気圧下において、ゴムローラー(ローラー径:50mm、ローラー幅:210mm)を用いて荷重500gで貼付した。
構造体1:ガラス基板とガラス基板の間に粘着層を挟んだ構造体
構造体2:ガラス基板とアクリル樹脂基板の間に粘着層を挟んだ構造体
高温高湿試験(表中では「85℃/85%RH」と記載):評価サンプルを85℃、85%RHの条件下で24時間放置した。
高温試験(表中では「100℃」と記載):評価サンプルを100℃の条件下で24時間放置した。
熱サイクル試験(表中では「TCT」と記載):評価サンプルを−40℃雰囲気に30分間放置し、100℃雰囲気に30分間放置するヒートサイクル(100回)を施した。
(評価基準)
A:剥離及び気泡の発生無し
B:剥離が無く、気泡の数が1個以上5個未満
C:気泡が5個以上発生
*ただし、気泡を5倍のルーペで目視により観察し、直径が約10μm以上の気泡を1個として数えた。
粘着層2が良好に切断でき、所望の形状を備える粘着シートを作製できたものをA、作製できなかったものをBと評価した。
[粘着シート2の作製(4層品)]
(I)実施例1と同様の方法で液状の粘着性樹脂組成物を得た。
(II)この粘着性樹脂組成物を重剥離セパレータ3の一方の面上に塗工して塗膜を形成した後、粘着層2上に仮セパレータ6を積層し、紫外線を照射(200mJ/cm2)し、さらにその後、重剥離セパレータ3の他方の面に、アクリル系接着剤(ヒタレックスK−6040(商品名)、日立化成工業(株)製)をラミネートし、その上にキャリアフィルム5を積層した。
(III)220mm×180mmになるように重剥離セパレータ3、粘着層2、仮セパレータ6及びキャリアフィルム5を切断した。
(IV)粘着層2、重剥離セパレータ3及び仮セパレータ6を205mm×160mmになるように、直径72mmのロータリーブレードにより切断した。切断には、ロータリー式打抜装置を用いた。この時、キャリアフィルム5の長辺側の両辺が、粘着層2の長辺側の両辺より7.5mm張り出すように、また、キャリアフィルム5の短辺側の両辺が、粘着層2の短辺側の両辺より5mm張り出すように切断した。
(V)仮セパレータ6を剥離し、215mm×170mmの軽剥離セパレータ4を粘着層2上に積層した。このようにして、粘着シート2を得た。この時、軽剥離セパレータ4の長辺側の両辺が、粘着層2の長辺側の両辺より5mm張り出すように、又軽剥離セパレータ4の短辺側の両辺が、粘着層2の短辺側の両辺より5mm張り出すように積層した。
Claims (4)
- 粘着層と、前記粘着層を挟むように積層された一対の基材層と、を備えており、
前記基材層の外縁は、前記粘着層の外縁よりも外側に張り出しており、
前記粘着層は、アルキル基の炭素数が4〜18であるアルキル(メタ)アクリレート成分を含む粘着性樹脂組成物に紫外線を照射することにより形成され、且つ25℃における剪断貯蔵弾性率が30〜150kPaである、
画像表示装置用粘着シートを作製する工程と、
前記画像表示装置用粘着シートが備える前記粘着層を介して、被着物同士を貼り合わせて積層体を得る工程と、
前記積層体を、40〜80℃及び0.3〜0.8MPaの条件で加熱加圧処理する工程と、
前記積層体に対し、前記被着物のいずれか一方の側から紫外線を照射する工程と、を備える、
画像表示装置の製造方法。 - 粘着層と、前記粘着層を挟むように積層された第1及び第2の基材層と、前記第2の基材層に更に積層されたキャリア層と、を備えており、
前記第1の基材層及び前記キャリア層の外縁は、前記粘着層の外縁よりも外側に張り出しており、
前記粘着層は、アルキル基の炭素数が4〜18であるアルキル(メタ)アクリレート成分を含む粘着性樹脂組成物に紫外線を照射することにより形成され、且つ25℃における剪断貯蔵弾性率が30〜150kPaである、
画像表示装置用粘着シートを作製する工程と、
前記画像表示装置用粘着シートが備える前記粘着層を介して、被着物同士を貼り合わせて積層体を得る工程と、
前記積層体を、40〜80℃及び0.3〜0.8MPaの条件で加熱加圧処理する工程と、
前記積層体に対し、前記被着物のいずれか一方の側から紫外線を照射する工程と、を備える、
画像表示装置の製造方法。 - 前記粘着性樹脂組成物に照射される前記紫外線の照射エネルギーが、160〜650mJ/cm 2 である、請求項1又は2に記載の画像表示装置の製造方法。
- 前記被着物が、透明保護板及びタッチパネルである、請求項1〜3のいずれか一項に記載の画像表示装置の製造方法。