JP4508794B2 - 防汚性縮合硬化型オルガノポリシロキサン組成物及び水中構造物 - Google Patents
防汚性縮合硬化型オルガノポリシロキサン組成物及び水中構造物 Download PDFInfo
- Publication number
- JP4508794B2 JP4508794B2 JP2004266636A JP2004266636A JP4508794B2 JP 4508794 B2 JP4508794 B2 JP 4508794B2 JP 2004266636 A JP2004266636 A JP 2004266636A JP 2004266636 A JP2004266636 A JP 2004266636A JP 4508794 B2 JP4508794 B2 JP 4508794B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- component
- organopolysiloxane composition
- groups
- antifouling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(A)ベースポリマーとして、1分子中に少なくとも2個の珪素原子に結合した水酸基及び/又は加水分解性基を有する25℃における粘度が20〜1,000,000mm 2 /sのジオルガノポリシロキサン、
(B)加水分解性基を1分子中に2個以上有するシラン及び/又はその部分加水分解縮合物:(A)成分100質量部に対して0.5〜20質量部、及び
(C)イオン性液体:(A)成分に対して0.01〜30質量%
を配合してなる防汚性縮合硬化型オルガノポリシロキサン組成物、及びこの組成物の硬化物でコーティングされた水中構造物を提供する。
(A)ベースポリマーとして、1分子中に少なくとも2個の珪素原子に結合した水酸基及び/又は加水分解性基を有するジオルガノポリシロキサン
(B)加水分解性基を1分子中に2個以上有するシラン及び/又はその部分加水分解縮合物
(C)イオン性液体
本発明の(A)成分であるジオルガノポリシロキサンは、本発明の縮合硬化型の室温硬化性オルガノポリシロキサン組成物の主剤(ベースポリマー)であり、1分子中に少なくとも2個の珪素原子に結合した水酸基及び/又は加水分解性基を有するジオルガノポリシロキサンが用いられるが、下記一般式(1)で表わされる、分子鎖末端が水酸基及び/又は加水分解性基で封鎖されたジオルガノポリシロキサンを用いることが好ましい。
mは0〜2の整数であるが、Yが水酸基の場合は、mは2が好ましく、Yが加水分解性基の場合は、mは0又は1が好ましい。
なお、本発明において、粘度は回転粘度計により測定した25℃における値である。
これらは1種単独でも2種以上組み合わせても使用することができる。
本発明の(B)成分であるシラン及び/又はその部分加水分解縮合物は、本発明の組成物を硬化させるために必須の成分であって、1分子中にケイ素原子に結合する加水分解可能な基を少なくとも2個有することが必要とされ、下記一般式(2)で表わされるシラン及び/又はその部分加水分解縮合物であることが好ましい。
(式中、R1は独立に非置換又は置換の炭素原子数1〜6の1価炭化水素基、Xは独立に加水分解性基であり、aは0〜2の整数である。)
本発明の(C)成分であるイオン性液体は、本発明の組成物を特徴づける重要な成分である。ここで、イオン性液体とは、室温で液体である溶融塩であり、常温溶融塩とも呼ばれるもので、特に、融点が50℃以下、好ましくは−100〜30℃、より好ましくは−50〜20℃のものをいう。このようなイオン性液体は、蒸気圧がない(不揮発性)、高耐熱性、不燃性、化学的安定である等の特性を有するものである。
本発明の組成物中には、硬化をより促進させるための触媒を添加してもよい。このような硬化用触媒としては、縮合硬化型の室温硬化性組成物に使用されている種々のものを使用することができ、具体例として、鉛−2−エチルオクトエート、ジブチルすずジオクトエート、ジブチルすずアセテート、ジブチルすずジラウレート、ブチルすず−2−エチルヘキソエート、鉄−2−エチルヘキソエート、コバルト−2−エチルヘキソエート、マンガン−2−エチルヘキソエート、亜鉛−2−エチルヘキソエート、カプリル酸第1すず、ナフテン酸すず、オレイン酸すず、ブタン酸すず、ナフテン酸チタン、ナフテン酸亜鉛、ナフテン酸コバルト、ステアリン酸亜鉛等の有機カルボン酸の金属塩;テトラブチルチタネート、テトラ−2−エチルヘキシルチタネート、トリエタノールアミンチタネート、テトラ(イソプロペニルオキシ)チタネート等の有機チタン酸エステル;オルガノシロキシチタン、β−カルボニルチタン、ジイソプロポキシチタンビス(エチルアセトアセテート)、チタンテトラ(アセチルアセトナート)等の有機チタン化合物、有機チタンキレート;アルコキシアルミニウム化合物、3−アミノプロピルトリエトキシシラン、N−(トリメトキシシリルプロピル)エチレンジアミン等のアミノアルキル基置換アルコキシシラン;ヘキシルアミン、リン酸ドデシルアミン等のアミン化合物及びその塩;ベンジルトリエチルアンモニウムアセテート等の第4級アンモニウム塩;酢酸カリウム、酢酸ナトリウム、臭酸リチウム等のアルカリ金属の低級脂肪酸塩;ジメチルヒドロキシルアミン、ジエチルヒドロキシルアミン等のジアルキルヒドロキシルアミン;下記式:
25℃において粘度が1,500mm2/sのα,ω−ジヒドロキシ−ジメチルポリシロキサン90部、比表面積が200m2/gの煙霧状シリカ15部を均一に混合し、150℃で2時間加熱減圧混合した。これにビニルトリス(メチルエチルケトオキシム)シラン12部と、γ−グリシドキシプロピルトリメトキシシラン1部を減圧下で均一になるまで混合した。更に、メチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミド1部を減圧下で均一になるまで混合して組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドをエトキシエチルメチルピロリジウムビス(トリフルオロメタンスルホニル)イミドに変更したこと以外は、実施例1と同様にして組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを、エトキシエチルメチルピロリジウムビス(トリフルオロメタンスルホニル)イミドに変更し、添加量を0.1部としたこと以外は、実施例1と同様にして組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを、エトキシエチルメチルモルフォリニウムビス(トリフルオロメタンスルホニル)イミドに変更したこと以外は、実施例1と同様にして組成物を調製した。
25℃における粘度が5,500mm2/sであり、分子鎖両末端がトリメトキシシリルエチレン基で封鎖されたジメチルポリシロキサン90部、比表面積が200m2/gの煙霧状シリカ15部を均一に混合し、150℃で2時間加熱減圧混合した。これにビニルトリメトキシシラン8部と、ジイソプロポキシチタンビス(エチルアセトアセテート)2部及びγ−グリシドキシプロピルトリメトキシシラン0.5部を減圧下で均一になるまで混合した。更に、エトキシエチルメチルピロリジウムビス(トリフルオロメタンスルホニル)イミド1部を減圧下で均一になるまで混合して組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを使用しないこと以外は、実施例1と同様にして組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを、フェニル基5モル%含有し、25℃における粘度が100mm2/sであり、分子鎖両末端がトリメチルシロキシ基で封鎖されたメチルフェニルシロキサン・ジメチルシロキサン共重合体15部に変更したこと以外は、実施例1と同様にして組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを、側鎖としてポリオキシエチレン基を含有し、25℃における粘度が100mm2/sであり、分子鎖両末端がトリメチルシロキシ基で封鎖された、HLB値が2のジメチルポリシロキサンに変更したこと以外は、実施例1と同様にして組成物を調製した。
実施例1のメチルトリn−オクチルアンモニウムビス(トリフルオロメタンスルホニル)イミドを、ベンジルトリエチルアンモニウムアセテートの4級アンモニウム塩に変更したこと以外は、実施例1と同様にして組成物を調製した。
上記の実施例及び比較例で得た組成物を、エポキシ系防食塗料(膜厚200μm)を用いて予め塗装した被塗板に、硬化膜厚が300μmになるように塗装して試験塗板とした。このように作製した試験塗板を、23℃,50%RHの条件で7日間かけて硬化させた。これらの硬化後の試験塗板を神奈川県海岸の沖合いに1.5mの深さで12ヶ月間にわたって懸垂試験を行った。フジツボ等の貝類、海藻類の付着状況を観察し、結果を表1に示した。
Claims (6)
- (A)ベースポリマーとして、1分子中に少なくとも2個の珪素原子に結合した水酸基及び/又は加水分解性基を有する25℃における粘度が20〜1,000,000mm 2 /sのジオルガノポリシロキサン、
(B)加水分解性基を1分子中に2個以上有するシラン及び/又はその部分加水分解縮合物:(A)成分100質量部に対して0.5〜20質量部、及び
(C)イオン性液体:(A)成分に対して0.01〜30質量%
を配合してなる防汚性縮合硬化型オルガノポリシロキサン組成物。 - (B)成分が、下記一般式(2)で表わされるシラン及び/又はその部分加水分解縮合物であることを特徴とする請求項1又は2に記載の防汚性縮合硬化型オルガノポリシロキサン組成物。
R1 aSiX4-a (2)
(式中、R1は独立に炭素原子数1〜6の非置換の1価炭化水素基又はハロゲン化アルキル基、Xは独立に加水分解性基であり、aは0〜2の整数である。) - (C)成分のイオン性液体が、4級アンモニウムカチオンとアニオンとからなるイオン性液体である請求項1乃至3のいずれか1項に記載の防汚性縮合硬化型オルガノポリシロキサン組成物。
- 更に、充填剤としてBET比表面積が10m2/g以上の親水性シリカ及び/又は疎水性シリカを含有することを特徴とする請求項1乃至4のいずれか1項に記載の防汚性縮合硬化型オルガノポリシロキサン組成物。
- 請求項1乃至5のいずれか1項に記載の組成物の硬化物でコーティングされた水中構造物。