JP2019059180A - 化粧シート及びこれを用いた化粧材 - Google Patents
化粧シート及びこれを用いた化粧材 Download PDFInfo
- Publication number
- JP2019059180A JP2019059180A JP2017187138A JP2017187138A JP2019059180A JP 2019059180 A JP2019059180 A JP 2019059180A JP 2017187138 A JP2017187138 A JP 2017187138A JP 2017187138 A JP2017187138 A JP 2017187138A JP 2019059180 A JP2019059180 A JP 2019059180A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- decorative sheet
- pigment
- infrared
- decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
しかし、カーボンブラックは赤外線を吸収するため、太陽光の照射を多く受ける場所でカーボンブラックを含む化粧材を用いた場合、化粧シートの温度が上昇することによって、化粧材の変形、被着材と化粧シートの剥離などの不具合が生じる場合がある。すなわち、カーボンブラックを含むインキを用いて、ベタ印刷層及び絵柄層を形成した化粧シートは、遮熱性が不十分なものであった。
遮熱性の問題を解決することを目的として、例えば特許文献1の技術が提案されている。
[1]赤外線反射性を有する基材上に、ベタ印刷層及び絵柄層を含む装飾層を有してなり、前記ベタ印刷層は、赤外線透過性又は赤外線反射性を有する顔料とバインダー樹脂とを含み、前記赤外線透過性又は赤外線反射性を有する顔料として、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物、又は、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物、を含み、前記絵柄層がカーボンブラックとバインダー樹脂とを含む、化粧シート。
[2]被着材と上記[1]に記載の化粧シートとを有する化粧材。
本発明の化粧シートは、赤外線反射性を有する基材上に、ベタ印刷層及び絵柄層を含む装飾層を有してなり、前記ベタ印刷層は、赤外線透過性又は赤外線反射性を有する顔料とバインダー樹脂とを含み、前記赤外線透過性又は赤外線反射性を有する顔料として、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物、又は、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物、を含み、前記絵柄層がカーボンブラックとバインダー樹脂とを含むものである。
なお、本明細書において、赤外線とは、波長780〜2500nmの光(いわゆる「近赤外線」)のことを言うものとする。
図1〜2の化粧シート100は、赤外線反射性を有する基材10上に、ベタ印刷層21及び絵柄層22を含む装飾層20を有している。また、図2の化粧シート100は、装飾層20上に、透明性樹脂層30及び表面保護層40を有している。
赤外線反射性を有する基材は、例えば、バインダー樹脂と、赤外線反射性を有する顔料を含むものが挙げられる。なお、以下、「赤外線反射性を有する基材」のことを「基材」と略称する場合がある。
これらの中で、より優れた耐候性及び耐傷性等の表面特性を得る観点から、ポリオレフィン樹脂、ポリエステル樹脂、ポリカーボネート樹脂及びABS樹脂が好ましく、加工適性の観点からポリオレフィン樹脂がより好ましい。
白色顔料として用いられる酸化チタンとしては、具体的には二酸化チタン(TiO2)であり、その結晶型としてはルチル型、アナターゼ型、ルチル型の何れも用いることができる。酸化チタンの粒径としては、白色度、隠蔽性、バインダー樹脂への分散性や製膜乃至印刷適性の点から平均粒径0.5〜5μm程度である。
これらの赤外線反射性を有する顔料の中でも、マンガン系複合酸化物及び酸化チタンが好ましい。すなわち、赤外線反射性を有する基材は、マンガン系複合酸化物を含む基材及び酸化チタンを含む基材が好ましい。
マンガン以外の金属元素は、1種単独であってもよいし、2種以上の組み合わせであってもよい。マンガン以外の金属元素の具体例としては、カルシウム、バリウム等の第2族元素;イットリウム、ランタン、プラセオジム;ネオジム等の第3族元素、チタン、ジルコニウム等の第4族元素;ホウ素、アルミニウム、ガリウム、インジウム等の第13族元素;アンチモン、ビスマス等の第15族元素等の金属元素が挙げられる。これらのなかでも、第2族元素、第4族元素、第15族元素が好ましく、カルシウム、チタン、及びビスマスがより好ましく、カルシウム及びチタンがさらに好ましい。
マンガン系複合酸化物の特に好ましい具体例としては、マンガン、カルシウム及びチタンを含む複合酸化物が挙げられる。
上述したマンガンを含む複合酸化物は、例えば、WO2016/125907A1公報記載に記載されている。
マンガン系複合酸化物を含む基材には、マンガン系複合酸化物以外の赤外線反射性を有する顔料や赤外線透過性を有する顔料を含有していてもよいが、マンガン系複合酸化物を含む基材のL*値が上記範囲となるように調製することが好ましい。
酸化チタンを含む基材には、酸化チタン以外の赤外線反射性を有する顔料や赤外線透過性を有する顔料を含有していてもよいが、酸化チタンを含む基材のL*値が上記範囲となるように調製することが好ましい。
また、後述するベタ印刷層の赤外線透過性又は赤外線反射性を有する顔料に関して、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物と、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物とを比較すると、遮熱性は前者が優れ、暗色度は後者が優れている。
したがって、遮熱性及び暗色度のバランスの観点から、基材としてマンガン系複合酸化物を含む基材を用いる場合には、ベタ印刷層の顔料として、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物を用いることが好ましい。同様に、遮熱性及び暗色度のバランスの観点から、基材として酸化チタンを含む基材を用いる場合には、ベタ印刷層の顔料として、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物を用いることが好ましい。
なお、暗色とは、濃灰色、深緑色、紺色、黒色、濃紫色、臙脂(えんじ)色、茶色等の低明度、低彩色の暗い感じのする色のことをいう。
光安定剤としては、例えばヒンダードアミン系光安定剤が好ましく、中でも(メタ)アクリロイル基、ビニル基、アリル基等のエチレン性二重結合である官能基等を有する反応性基含有ヒンダードアミン系光安定剤が好ましく挙げられる。
また、基材中の光安定剤の含有量は、バインダー樹脂100質量部に対し、好ましくは0.5質量部以上、より好ましくは1質量部以上、更に好ましくは3質量部以上であり、上限として好ましくは10質量部以下、より好ましくは8質量部以下、更に好ましくは6質量部以下である。
基材中の紫外線吸収剤、光安定剤の含有量が上記範囲内であると、ブリードアウトしにくく、優れた添加効果が得られる。
基材の厚さは、取り扱い性及び強度のバランスの観点から、20μm以上が好ましく、30μm以上がより好ましく、40μm以上がさらに好ましい。上限としては、200μm以下が好ましく、160μm以下がより好ましく、100μm以下がさらに好ましい。
酸化法としては、例えばコロナ放電処理、クロム酸化処理、火炎処理、熱風処理、オゾン−紫外線処理法等が挙げられ、凹凸化法としては、例えばサンドブラスト法、溶剤処理法等が挙げられる。これらの表面処理は、基材の種類に応じて適宜選択されるが、一般にはコロナ放電処理法が、表面処理の効果及び操作性等の面から好ましく用いられる。
また、基材と他の層との層間密着性の向上、被着材との接着性の強化等のために、基材にプライマー層、裏面プライマー層を形成する等の処理を施してもよい。これらのプライマー層については、後述する。
本発明の化粧シート100は、基材10上に、ベタ印刷層21及び絵柄層22を含む装飾層20を有する。
ベタ印刷層は、赤外線透過性又は赤外線反射性を有する顔料とバインダー樹脂とを含む層である。
また、ベタ印刷層に含まれる赤外線透過性又は赤外線反射性を有する顔料は、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物、又は、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物、を含む。
具体的な有機顔料の組み合わせとしては、C.I.ピグメントレッド122とC.I.ピグメントイエロー150とC.I.ピグメントブルー15との組み合わせ、C.I.ピグメントレッド122とC.I.ピグメントイエロー109とC.I.ピグメントブルー15との組み合わせ等が挙げられる。
ペリレン系顔料は、ペリレンテトラカルボン酸二無水物の六員環を構成している酸素原子2個を脱落させた構造を有する顔料であり、ペリレンブラック等が挙げられる。
また、赤外線透過性又は赤外線反射性を有する顔料として(A)の顔料を含む場合、該(A)の顔料の含有量は、ベタ印刷層の固形分基準で5〜60質量%であることが好ましく、8〜40質量%であることがより好ましく、10〜30質量%であることがさらに好ましい。
また、赤外線透過性又は赤外線反射性を有する顔料として(B)の顔料を含む場合、該(B)の顔料の含有量は、ベタ印刷層の固形分基準で5〜50質量%であることが好ましく、5〜40質量%であることがより好ましく、5〜30質量%であることがさらに好ましい。
なお、本発明の効果を阻害しない範囲で、(A)の顔料を主体としてさらに(B)の顔料を添加したり、(B)の顔料を主体としてさらに(A)の顔料を添加したりしてもよい。
また、本発明の効果を阻害しない範囲で、その他の赤外線透過性又は赤外線反射性を有する顔料を併用してもよい。その他の赤外線透過性又は赤外線反射性を有する顔料としては、酸化チタン及び酸化鉄が挙げられる。
なお、本明細書において平均粒子径とは、レーザー光回折法による粒度分布測定における質量平均値D50として求めることができる値である。
なお、ベタ印刷層は、単層であってもよいし、複数のベタ印刷層を積層してもよい。
絵柄層は、カーボンブラックとバインダー樹脂とを含むものである。絵柄層はベタ印刷層の基材とは反対側に形成される。
本発明の化粧シートは、相対的に面積が広いベタ印刷層に実質的にカーボンブラックを含まず、相対的に面積が狭い絵柄層がカーボンブラックを含むことにより、遮熱性を満足しつつ、且つ暗色度に優れた意匠を表現できる。
カーボンブラックの平均粒子径は、10〜150nmであることが好ましく、30〜100nmであることがより好ましい。
また、暗色度をより良好にする観点からは、該面積割合を20%以上とすることが好ましく、25%以上とすることがより好ましい。
なお、化粧シートの全面積、及び、カーボンブラックとバインダー樹脂とを含む絵柄層の面積は、化粧シートを平面視した際の面積を意味する。
紫外線吸収剤及び光安定剤としては、基材に含まれ得るものとして例示した、紫外線吸収剤、光安定剤を挙げることができる。紫外線吸収剤及び光安定剤の含有量は、耐候性の向上の観点から、後述する表面保護層中の含有量と同じ範囲を例示することができる。
装飾層により付与する意匠が木目模様の場合、絵柄層は導管溝模様及び/又は節目模様とすることが好ましい。また、装飾層により付与する意匠がトラバーチン等の石の模様の場合、絵柄層は凹陥部模様とすることが好ましい。また、装飾層により付与する意匠がタイル模様又はレンガ模様の場合、絵柄層は目地模様とすることが好ましい。
本発明の化粧シートは、装飾層として、その他の絵柄層(カーボンブラックとバインダー樹脂とを含む絵柄層以外の絵柄層)を有していてもよい。なお、暗色度を高める観点からは、その他の絵柄層を有さないことが好ましい。
その他の絵柄層としては、例えば、アゾメチンアゾ系顔料とバインダー樹脂とを含む絵柄層が挙げられる。
化粧シートは、必要に応じて接着剤層Aを有することができる。
特に、化粧シートが後述する透明性樹脂層を有する場合、装飾層と該透明性樹脂層との層間密着性を向上させるときに、接着剤層Aを設けることは有効である。接着剤層Aを構成する接着剤としては、通常化粧シートで用いられる接着剤を制限なく用いることができる。
化粧シートは、装飾層を保護する観点、耐候性及び耐傷性等の表面特性の向上の観点から、装飾層上に直接、又は他の層を介して透明性樹脂層を積層することが好ましい。透明性樹脂層は単層であってもよいし、2層以上から形成してもよい。
中でも、耐候性及び耐傷性等の表面特性の向上の観点から、ポリオレフィン樹脂、ポリエステル樹脂及び弗素樹脂が好ましく、特にポリオレフィン樹脂が好ましい。ポリオレフィン樹脂としては、着色基材を構成し得るものとして例示した樹脂が挙げられ、中でもポリプロピレン樹脂が好ましい。
弗素樹脂を含む透明性樹脂層は、弗素樹脂とは別に、ポリメチル(メタ)アクリレート、ポリブチル(メタ)アクリレ−ト、メチル(メタ)アクリレート−ブチル(メタ)アクリレート共重合体、エチレン−メチル(メタ)アクリレート共重合体等のアクリ樹脂を含むことが好ましい。
また、弗素樹脂を含む透明性樹脂層を用いる場合、その他の透明性樹脂層を併用し、透明性樹脂層を多層構成とすることが好ましい。この際、その他の透明性樹脂層が装飾層側となるように配置することが好ましい。
紫外線吸収剤、光安定剤としては、基材に用い得るものとして例示した、紫外線吸収剤、光安定剤を挙げることができる。これらの耐候剤の含有量は、耐候性の向上の観点から、着色基材中の含有量と同じ範囲を例示することができる。
また、透明性樹脂層と他の層との層間密着性の向上のために、透明性樹脂層の片面又は両面にプライマー層を形成する等の処理を施してもよい。このプライマー層については、後述する。
化粧シートには、主に耐傷性及び耐候性等の表面特性を付与する観点から、装飾層上に直接、又は他の層(接着剤層A、透明性樹脂層、プライマー層)の上に表面保護層を設けることが好ましい。
表面保護層の形成に用いられる硬化性樹脂としては、2液硬化型樹脂等の熱硬化性樹脂の他、電離放射線硬化性樹脂等が好ましく用いられ、これらの複数種を組み合わせた、例えば、電離放射線硬化性樹脂と熱硬化性樹脂とを併用する、又は硬化性樹脂と熱可塑性樹脂とを併用する、いわゆるハイブリッドタイプであってもよい。
硬化性樹脂としては、表面保護層を構成する樹脂の架橋密度を高め、より優れた耐傷性及び耐候性等の表面特性とを得る観点から、電離放射線硬化性樹脂が好ましく、また、取り扱いが容易との観点から、電子線硬化性樹脂がより好ましい。
電離放射線硬化性樹脂とは、電離放射線を照射することにより、架橋、硬化する樹脂のことであり、電離放射線硬化性官能基を有するものである。ここで、電離放射線硬化性官能基とは、電離放射線の照射によって架橋硬化する基であり、(メタ)アクリロイル基、ビニル基、アリル基等のエチレン性二重結合を有する官能基等が好ましく挙げられる。また、電離放射線とは、電磁波又は荷電粒子線のうち、分子を重合あるいは架橋し得るエネルギー量子を有するものを意味し、通常、紫外線(UV)又は電子線(EB)が用いられるが、その他、X線、γ線等の電磁波、α線、イオン線等の荷電粒子線も含まれる。
電離放射線硬化性樹脂としては、具体的には、従来電離放射線硬化性樹脂として慣用されている重合性モノマー、重合性オリゴマーの中から適宜選択して用いることができる。
多官能性(メタ)アクリレートモノマーとしては、分子中に2つ以上の電離放射線硬化性官能基を有し、かつ該官能基として少なくとも(メタ)アクリロイル基を有する(メタ)アクリレートモノマーが挙げられ、より優れた耐傷性及び耐候性等の表面特性を得る観点から、アクリロイル基を有するアクリレートモノマーが好ましい。
より優れた耐傷性及び耐候性等の表面特性を得る観点から、官能基数は好ましくは2以上であり、上限として好ましくは8以下、より好ましくは6以下、更に好ましくは4以下、特に好ましくは3以下である。これらの多官能性(メタ)アクリレートは、単独で、又は複数種を組み合わせて用いてもよい。
さらに、重合性オリゴマーとしては、他にポリブタジエンオリゴマーの側鎖に(メタ)アクリレート基をもつ疎水性の高いポリブタジエン(メタ)アクリレート系オリゴマー、主鎖にポリシロキサン結合をもつシリコーン(メタ)アクリレート系オリゴマー、小さな分子内に多くの反応性基をもつアミノプラスト樹脂を変性したアミノプラスト樹脂(メタ)アクリレート系オリゴマー、あるいはノボラック型エポキシ樹脂、ビスフェノール型エポキシ樹脂、脂肪族ビニルエーテル、芳香族ビニルエーテル等の分子中にカチオン重合性官能基を有するオリゴマー等がある。
紫外線吸収剤としては、着色基材に含まれ得る紫外線吸収剤として例示した、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、トリアジン系紫外線吸収剤等が挙げられ、トリアジン系紫外線吸収剤が好ましい。
表面保護層中の光安定剤の含有量は、表面保護層を構成する硬化性樹脂100質量部に対し、0.1質量部以上が好ましく、0.5質量部以上がより好ましく、1質量部以上がさらに好ましく、1.5質量部以上がよりさらに好ましい。また上限としては、10質量部以下が好ましく、8質量部以下がより好ましく、5質量部以下がさらに好ましく、3質量部以下がよりさらに好ましい。表面保護層中の紫外線吸収剤、光安定剤の含有量が上記範囲内であると、ブリードアウトすることなく、優れた添加効果が得られる。
化粧シートは、所望に応じてプライマー層を設けることができる。プライマー層は、主に層間密着性の向上効果を得るために設けられる層である。また、プライマー層が、着色基材の表面保護層側とは反対側の面に設けられる場合(このような場合のプライマー層は、「裏面プライマー層」とも称される。)は、基材と被着材との層間密着性を向上することができる。
プライマー層は、基材と装飾層との間、接着剤層Aと透明性樹脂層との間、透明性樹脂層と表面保護層との間、基材の装飾層側とは反対側の面、から選らばれる何れか1箇所以上に設けることができる。
バインダーとしては、例えば、上記のベタ印刷層に用い得るバインダーとして例示した樹脂が好ましく挙げられ、これらを単独で、又は複数種を組み合わせて用いることができる。例えば、ポリカーボネート系ウレタン−アクリル共重合体とアクリルポリオール樹脂との混合物をバインダーとして用いることができる。
プライマー層における紫外線吸収剤の含有量は、プライマー層を構成する樹脂100質量部に対し、好ましくは1質量部以上、より好ましくは5質量部以上、さらに好ましくは10質量部以上であり、また上限として好ましくは40質量部以下、より好ましくは30質量部以下、さらに好ましくは25質量部以下である。
また、プライマー層における光安定剤の含有量は、プライマー層を構成する樹脂100質量部に対し、好ましくは0.5質量部以上、より好ましくは1質量部以上、さらに好ましくは1.5質量部以上、よりさらに好ましくは2質量部以上であり、また上限として好ましくは20質量部以下、より好ましくは15質量部以下、さらに好ましくは10質量部以下、よりさらに好ましくは8質量部以下である。
プライマー層中の紫外線吸収剤及び光安定剤の含有量が上記範囲内であると、プライマー層としての優れた性能とともに、優れた耐候性が得られる。
エンボス加工を行う場合、例えば、化粧シートを好ましくは80℃以上260℃以下、より好ましくは85℃以上160℃以下、さらに好ましくは100℃以上140℃以下に加熱し、化粧シートにエンボス版を押圧して、エンボス加工を行うことができる。エンボス版は、化粧シートの基材を基準として装飾層側に押し当てることが好ましい。
本発明の化粧材は、被着材と上記の本発明の化粧シートとを有するものであり、より具体的には、被着材の装飾を要する側の面と、化粧シートの基材側の面とを対向させて積層したものである。
被着材としては、各種素材の平板、曲面板等の板材、立体形状物品、シート(或いはフィルム)等が挙げられる。例えば、杉、檜、松、ラワン等の各種木材から成る木材単板、木材合板、パーティクルボード、MDF(中密度繊維板)等の木質繊維板等の板材や立体形状物品等として用いられる木質部材;鉄、アルミニウム等の板材や鋼板、立体形状物品、あるいはシート等として用いられる金属部材;ガラス、陶磁器等のセラミックス、石膏等の非セメント窯業系材料、ALC(軽量気泡コンクリート)板等の非陶磁器窯業系材料等の板材や立体形状物品等として用いられる窯業部材;アクリル樹脂、ポリエステル樹脂、ポリスチレン樹脂、ポリプロピレン等のポリオレフィン樹脂、ABS(アクリロニトリル−ブタジエン−スチレン共重合体)樹脂、フェノール樹脂、塩化ビニル樹脂、セルロース樹脂、ゴム等の板材、立体形状物品、あるいはシート等として用いられる樹脂部材等が挙げられる。また、これらの部材は、単独で、又は複数種を組み合わせて用いることができる。
被着材と化粧シートとは、優れた接着性を得るため、接着剤層Bを介して貼り合わせられることが好ましい。
また、接着剤層Bには、粘着剤を用いることもできる。粘着剤としては、アクリル系、ウレタン系、シリコーン系、ゴム系等の粘着剤を適宜選択して用いることができる。
化粧材は、化粧シートと被着材とを積層する工程を経て製造することができる。
本工程は、被着材と、本発明の化粧シートとを積層する工程であり、被着材の装飾を要する側の面と、化粧シートの基材側の面とを対向させて積層する。被着材と化粧シートとを積層する方法としては、例えば、接着剤層Bを介して化粧シートを板状の被着材に加圧ローラーで加圧して積層するラミネート方法等が挙げられる。
1.測定及び評価
1−1.遮熱性
実施例及び比較例で得られた化粧材に、200W形ランプ(白熱灯,岩崎電気(株)製造)を用いて、室温(23℃)、相対湿度50%の条件下、30cm高さから照射し、10分後の化粧材の表面温度を測定し、下記の基準で評価した。
A:表面温度は85℃以上90℃未満であった。
B:表面温度は90℃以上95℃未満であった。
C:表面温度は95℃以上100℃未満であった。
比較例1の化粧シートをリファレンスとして、実施例及び比較例の化粧シートを表面保護層から観察し、木目意匠の暗色の度合いを評価した。リファレンスに対して木目意匠の暗色度が極めて優れるものを3点、リファレンスに対して木目意匠の暗色度が優れるものを2点、リファレンスと同等あるいはリファレンスと同等未満と感じるものを1点として、20人の被験者が評価を行い、平均点を算出した。結果を表1に示す。なお、リファレンスである比較例1は「C」とした。
<評価基準>
A:平均点が2.0以上
B:平均点が1.5以上2.0未満
C:平均点が1.0以上1.5未満
[実施例1]
赤外線反射性を有する基材として、マンガン系複合酸化物を含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均35%、L*値:58)を用意して、該シートの一方の面に、下記処方のベタ印刷層形成用インキ1をグラビアコート法により塗布、乾燥し、厚さ4μmのベタ印刷層(木肌模様)を形成した。
・バインダー樹脂(アクリルウレタン系樹脂) 76質量部
・赤色顔料(C.I.ピグメントレッド122) 10質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 9質量部
(平均粒子径:0.05μm)
・青色顔料(C.I.ピグメントブルー15) 5質量部
(平均粒子径:0.04μm)
・希釈溶剤 適量
・バインダー樹脂(アクリルウレタン系樹脂) 80質量部
・赤色顔料(C.I.ピグメントレッド122) 12質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 6質量部
(平均粒子径:0.05μm)
・黒色顔料(カーボンブラック) 2質量部
・希釈溶剤 適量
次いで、透明性樹脂層の表面にコロナ放電処理を施した後、2液硬化性ウレタン樹脂組成物を塗布してプライマー層(厚さ:2μm)を形成した。
<表面保護層形成用インキ>
・3官能ウレタンアクリレートオリゴマー 100質量部
(質量平均分子量5000)
・無機フィラー 25質量部
(シリカ粒子、平均粒子径:5μm)
得られた化粧シート、及び化粧部材について、上記の評価を行い、その評価結果を表1に示す。
ベタ印刷層形成用インキ1を下記処方のベタ印刷層形成用インキ2に変更した以外は、実施例1と同様にして、実施例2の化粧シート及び化粧材を得た。
・バインダー樹脂(アクリルウレタン系樹脂) 30質量部
・赤外線反射性顔料(TiO2) 50質量部
・赤外線透過性顔料(FeOOH) 9質量部
(平均粒子径:0.1μm)
・赤外線透過性顔料(Fe2O3) 6質量部
(平均粒子径:0.1μm)
・赤外線反射性顔料 5質量部
(金属元素としてマンガン、カルシウム及びチタンを含む複合酸化物)
(石原産業株式会社製、品番:MPT−370、黒色顔料、平均一次粒子径0.8μm)
・希釈溶剤 適量
赤外線反射性を有する基材を、酸化チタンを含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均40%、L*値:90)に変更し、ベタ印刷層形成用インキ1を上記処方のベタ印刷層形成用インキ2に変更した以外は、実施例1と同様にして、実施例3の化粧シート及び化粧材を得た。
赤外線反射性を有する基材を、酸化チタンを含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均40%、L*値:90)に変更した以外は、実施例1と同様にして、実施例4の化粧シート及び化粧材を得た。
赤外線反射性を有する基材を、酸化チタンを含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均40%、L*値:90)に変更し、絵柄層形成用インキ1を下記処方の絵柄層形成用インキ2に変更した以外は、実施例1と同様にして、比較例1の化粧シート及び化粧材を得た。
・バインダー樹脂(アクリルウレタン系樹脂) 80質量部
・赤色顔料(C.I.ピグメントレッド122) 6質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 9質量部
(平均粒子径:0.05μm)
・黒色顔料(アゾメチンアゾ系顔料) 5質量部
(平均粒子径:0.2μm)
・希釈溶剤 適量
赤外線反射性を有する基材を、酸化チタンを含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均40%、L*値:90)に変更し、ベタ印刷層形成用インキ1を下記処方の絵柄層形成用インキ3に変更し、絵柄層形成用インキ1を下記処方の絵柄層形成用インキ3に変更した以外は、実施例1と同様にして、比較例2の化粧シート及び化粧材を得た。
・バインダー樹脂(アクリルウレタン系樹脂) 80質量部
・赤色顔料(C.I.ピグメントレッド122) 6質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 9質量部
(平均粒子径:0.05μm)
・黒色顔料(アゾメチンアゾ系顔料) 5質量部
(平均粒子径:0.2μm)
・希釈溶剤 適量
・バインダー樹脂(アクリルウレタン系樹脂) 76質量部
・赤色顔料(C.I.ピグメントレッド122) 10質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 9質量部
(平均粒子径:0.05μm)
・青色顔料(C.I.ピグメントブルー15) 5質量部
(平均粒子径:0.04μm)
・希釈溶剤 適量
赤外線反射性を有する基材を、酸化チタンを含む基材(厚さ60μm。波長780〜2500nmの分光反射率の平均40%、L*値:90)に変更し、ベタ印刷層形成用インキ1を下記処方の絵柄層形成用インキ4に変更し、絵柄層形成用インキ1を下記処方の絵柄層形成用インキ4に変更した以外は、実施例1と同様にして、比較例3の化粧シート及び化粧材を得た。
・バインダー樹脂(アクリルウレタン系樹脂) 80質量部
・赤色顔料(C.I.ピグメントレッド122) 8質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 10質量部
(平均粒子径:0.05μm)
・黒色顔料(カーボンブラック) 2質量部
・希釈溶剤 適量
・バインダー樹脂(アクリルウレタン系樹脂) 78質量部
・赤色顔料(C.I.ピグメントレッド122) 6質量部
(平均粒子径:0.13μm)
・黄色顔料(C.I.ピグメントイエロー150) 8質量部
(平均粒子径:0.05μm)
・黒色顔料(カーボンブラック) 8質量部
・希釈溶剤 適量
21:ベタ印刷層
22:絵柄層
20:装飾層
30:透明性樹脂層
40:表面保護層
100:化粧シート
Claims (15)
- 赤外線反射性を有する基材上に、ベタ印刷層及び絵柄層を含む装飾層を有してなり、
前記ベタ印刷層は、赤外線透過性又は赤外線反射性を有する顔料とバインダー樹脂とを含み、
前記赤外線透過性又は赤外線反射性を有する顔料として、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物、又は、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物、を含み、
前記絵柄層がカーボンブラックとバインダー樹脂とを含む、化粧シート。 - 前記ベタ印刷層は、固形分基準で前記赤外線透過性又は赤外線反射性を有する顔料を5〜80質量%含む請求項1に記載の化粧シート。
- 前記ベタ印刷層の厚みが0.5〜15μmである、請求項1又は2に記載の化粧シート。
- 前記絵柄層は、固形分基準で前記カーボンブラックを0.1〜5.0質量%含む、請求項1〜3の何れか1項に記載の化粧シート。
- 前記絵柄層の厚みが0.5〜20μmである、請求項1〜4の何れか1項に記載の化粧シート。
- 前記赤外線反射性を有する基材が、マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物を含む基材である、請求項1〜5の何れか1項に記載の化粧シート。
- 前記赤外線反射性を有する基材のJIS Z8781−4:2013に準拠して測定されるCIE(国際照明委員会)L*a*b*表色系のL*値が60以下である、請求項6に記載の化粧シート。
- 前記赤外線透過性又は赤外線反射性を有する顔料が、(A)キナクリドン、イソインドリノン、ニッケルアゾ錯体及びフタロシアニンからなる顔料の群から選択される三種以上の化合物である、請求項6又は7に記載の化粧シート。
- 前記赤外線反射性を有する基材が酸化チタンを含む基材である、請求項1〜5の何れか1項に記載の化粧シート。
- 前記赤外線反射性を有する基材のJIS Z8781−4:2013に準拠して測定されるCIE(国際照明委員会)L*a*b*表色系のL*値が80以上である、請求項9に記載の化粧シート。
- 前記赤外線透過性又は赤外線反射性を有する顔料が、(B)マンガンとマンガン以外の少なくとも1種の金属元素を含む複合酸化物、アゾメチンアゾ系化合物及びペリレン系化合物からなる顔料の群から選択される一種以上の化合物である、請求項9又は10に記載の化粧シート。
- 前記化粧シートの全面積に対する、前記絵柄層の面積の割合が50%以下である請求項1〜11の何れか1項に記載の化粧シート。
- 前記化粧シートが前記装飾層上に透明性樹脂層及び保護層の少なくとも何れかを有する請求項1〜12の何れか1項に記載の化粧シート。
- 前記化粧シートの前記装飾層側の表面の前記ベタ印刷層及び前記絵柄層を有する箇所における、JIS Z8781−4:2013に準拠して測定されるCIE(国際照明委員会)L*a*b*表色系のL*値が45以下である、請求項1〜13の何れか1項に記載の化粧シート。
- 被着材と請求項1〜14の何れか1項に記載の化粧シートとを有する化粧材。