JP2017084601A - リチウム空気二次電池空気極の製造方法 - Google Patents
リチウム空気二次電池空気極の製造方法 Download PDFInfo
- Publication number
- JP2017084601A JP2017084601A JP2015211535A JP2015211535A JP2017084601A JP 2017084601 A JP2017084601 A JP 2017084601A JP 2015211535 A JP2015211535 A JP 2015211535A JP 2015211535 A JP2015211535 A JP 2015211535A JP 2017084601 A JP2017084601 A JP 2017084601A
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- lithium
- air
- carbon
- air electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
2Li++O2+2e- → Li2O2・・・(2)
以下、実施例を用いて説明する。はじめに、実施例1について説明する。実施例1では、有機酸液としてギ酸を用いた。
次に、実施例2について説明する。実施例2では、有機酸液としてシュウ酸を用いた。
次に、比較例について説明する。比較例では、カーボン(KetjenBlack EC600JD;KB、ライオン社製)粉末を用い、これを純水に加え、超音波を1時間かけた、ここに、H2PtCl6・6H2OとRuCl3を少量ずつ滴下する。次に、液温を80℃に加熱し、水酸化ナトリウムを加えてpHを8に調整する。ここに、0.5mol/リットルのNaBH4を懸濁剤として加え、2時間攪拌する。室温に戻した後、12時間攪拌を継続した後、ろ過し、また、純水で洗浄して粉末を得る。この粉末を80℃に保持して一晩乾燥させ、比較例の触媒担持カーボンを得る。
Claims (5)
- カーボンおよびカーボンに担持された触媒を備える空気極と、リチウムを含んで構成された負極と、前記空気極と前記負極とに挾まれて配置された電解質とを備えるリチウム空気二次電池の空気極を製造するリチウム空気二次電池空気極の製造方法であって、
カーボンとカルボキシル基を有する有機酸と前記触媒を構成する金属の金属塩とを混合した混合体を作製する第1工程と、
前記混合体を加熱することで前記触媒が担持した触媒担持カーボンを作製する第2工程と、
前記触媒担持カーボンを担体に担持させて空気極を成形する第3工程と
を備えることを特徴とするリチウム空気二次電池空気極の製造方法。 - 請求項1記載のリチウム空気二次電池空気極の製造方法において、
前記第2工程では、乾固した前記混合体を加熱することで前記金属からなる前記触媒が担持した触媒担持カーボンを作製する
ことを特徴とするリチウム空気二次電池空気極の製造方法。 - 請求項1記載のリチウム空気二次電池空気極の製造方法において、
前記第2工程では、乾固した前記混合体を加熱することで前記金属が担持した金属担持カーボンを作製し、作製した金属担持カーボンの金属を酸化することで金属酸化物からなる前記触媒が担持した触媒担持カーボンを作製する
ことを特徴とするリチウム空気二次電池空気極の製造方法。 - 請求項1〜3のいずれか1項に記載のリチウム空気二次電池空気極の製造方法において、
前記有機酸は、ギ酸またはシュウ酸であることを特徴とするリチウム空気二次電池空気極の製造方法。 - 請求項1〜4のいずれか1項に記載のリチウム空気二次電池空気極の製造方法において、
前記金属は、白金およびルテニウムの少なくとも1つから構成することを特徴とするリチウム空気二次電池空気極の製造方法。