JP2009066984A - 熱プレス成形用離型フィルム - Google Patents
熱プレス成形用離型フィルム Download PDFInfo
- Publication number
- JP2009066984A JP2009066984A JP2007239610A JP2007239610A JP2009066984A JP 2009066984 A JP2009066984 A JP 2009066984A JP 2007239610 A JP2007239610 A JP 2007239610A JP 2007239610 A JP2007239610 A JP 2007239610A JP 2009066984 A JP2009066984 A JP 2009066984A
- Authority
- JP
- Japan
- Prior art keywords
- release film
- resin
- release
- acid
- hot press
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】少なくとも一方の表面が離型層として構成されている熱プレス成形用離型フィルムであって、前記の離型層は、官能基を有する融点60℃以上の離型剤(B−1)及び融点100℃以上のポリオレフィン樹脂(B−2)からなる群より選ばれた少なくとも一種の離型性付与剤(B)と残存テトラヒドロフラン量が300ppm以下であるポリブチレンテレフタレート樹脂(A)とを含む樹脂組成物から成り、濡れ張力が30mN/m以下である熱プレス成形用離型フィルム。
【選択図】なし
Description
本発明で使用するポリブチレンテレフタレート樹脂(PBT樹脂と略記することがある)の固有粘度は、フェノール/1,1,2,2−テトラクロルエタン(重量比1/1)の混合溶媒を使用し、30℃で測定した値として、通常0.7〜2.0dl/g、好ましくは0.8〜1.8dl/g、更に好ましくは0.8〜1.5dl/gである。固有粘度が0.7dl/g未満の場合は、PBT含有樹脂組成物を使用したフィルムの機械的強度が不十分となるおそれがある。固有粘度が2.0dl/gを超える場合は、溶融粘度が高くなり、流動性が悪化し、特に多層共押出フィルム成形において、層間の厚み精度が低下する恐れがある。
本発明における離型性付与剤(B)は次の機能を発揮する。すなわち、フレキシブルプリント基板の製造工程において、電気回路を形成したフレキシブルプリント基板本体に、熱硬化型接着剤によってカバーレイフィルムを熱プレス接着する際、カバーレイフィルムとプレス熱板とが接着するのを防止するため、離型フィルムを使用する。離型性付与剤(B)は、離型フィルムの離型層の樹脂に配合され、離型フィルムの接着の防止をより促進する機能を発揮する。本発明における離型性付与剤(B)は、融点が60℃以上の官能基を有する離型剤(B−1)及び融点が100℃以上のポリオレフィン樹脂(B−2)から成る群より選ばれる少なくとも一種である。
本発明で使用する離型剤(B−1)は、射出成形などにおける金型と溶融樹脂との密着性を低下させるための、分子量が通常300〜8000のプラスチック用離型剤が使用可能であるが、融点が60℃以上で官能基を有している必要がある。ここで官能基とは、ポリブチレンテレフタレートと親和性を向上させる有機残基であり、例えば、カルボキシル基、エステル基、水酸基、カルボン酸金属塩基、アルコキシ基、エーテル基、ケトン基、エポキシ基、アミノ基、アミド基などであり、一分子中に少なくとも一つ以上の官能基を有している必要がある。融点が60℃以上で、同時に官能基を有していることにより、フレキシブルプリント基板などの製造における熱プレス中に離型層のポリブチレンテレフタレート樹脂からの飛散やブリードアウトが抑制され、基板の汚染トラブルが減少する。なお、融点は、示差走査熱量計を使用し、昇温速度20℃/分で測定した融解の吸熱ピーク温度を意味する。
本発明で使用するポリオレフィン樹脂とは、α−オレフィンを主体とする分子量10000以上の重合体である。主成分のα−オレフィンとしては、炭素数2〜10の範囲のオレフィンが好ましく、例えば、エチレン、1−ブテン、1−ペンテン、4−メチル−1−ペンテン、1−ヘキセン、1−ヘプテン、1−オクテン等が挙げられ、α−オレフィン以外の共重合成分としては、例えば、アクリル酸、メタクリル酸、エチルアクリル酸エステル、メチルメタクリル酸エステル、グリシジルアクリル酸エステル、酢酸ビニル、ビニルアルコール、(無水)マレイン酸などが挙げられる。
本発明において、離型層中のポリブチレンテレフタレート樹脂(A)100重量部に対する離型剤(B−1)の割合は、通常0.05〜5重量部、好ましくは0.07〜3重量部である。0.05重量部未満の場合は離型性改善効果が認められず、10重量部を超える場合は、銅回路などの汚染を引き起こし、歩留まりが低下することがある。一方、離型層中のポリブチレンテレフタレート樹脂(A)100重量部に対する離型剤(B−2)の割合は、通常5〜100重量部、好ましくは10〜70重量部である。5重量部未満の場合は離型性改善効果が認められず、100重量部を超える場合は、銅回路などの汚染や耐熱性の低下を引き起こし、歩留まりが低下することがある。そして、本発明における離型層の濡れ張力は、離型性付与剤の種類や配合量を適切に選択することにより、30mN/m以下に調節される。
本発明の離型フィルムは、単層構造であってもよく、多層構造であってもよい。離型フィルムが単相構造であるときは、ポリブチレンテレフタレート樹脂(A)と離型性付与剤(B)とを含む樹脂組成物の溶融成形法により作製することができる。上記の溶融成形法としては特に限定されず、例えば、空冷又は水冷インフレーション押出法、Tダイ押出法などの従来公知の熱可塑性樹脂フィルムの成膜方法が挙げられる。また、本発明の離型フィルムが多層構造を有する場合には、例えば、共押出Tダイ法などの既知の方法により製造することが出来る。更に、上述のように、溶融成形法により得られたフィルムに熱処理を施すことにより、特に高い離型性を実現した離型層を得ることが出来る。
表1に示される組成比でブレンド後、二軸押出機(日本製鋼所社製「TEX30HTCT」)を使用し、250℃のシリンダー温度で、また、ベント孔を70Torrに減圧にし、揮発分を除去しながら、溶融混練し、ペレット化した。
JIS K6768−1999に従って濡れ張力を測定した。
上記のプリント配線基板から離型フィルムを引き剥がすときの離型の容易さから、次の指標にて評価した。
3:TPXの離型フィルムと同等の離型性である。
2:TPXの離型フィルムより離型が困難である。
1:TPXの離型フィルムよりかなり離型が困難てあり、実用レベルでない。
上記プリント配線基板から離型フィルムを引き剥がした後のプリント配線基板表面の転写物の有無を目視観察し、次の指標にて評価した。
3:僅かな転写物による曇りがあるが、実用上問題ない。
2:転写物によるやけ・曇りがあり、洗浄しても落ちず、実用レベルでない。
1:樹脂上の付着物があり、全く実用レベルでない。
離型フィルムの表面に、押出成形の方向(MD方向)及びそれに対して直角方向(TD方向)に100mm間隔の標線をそれぞれ記入した。離型フィルムを鏡板に挟み、170℃、荷重3MPaで60分間プレスを行った後、標線間距離の測定を行い、MDとTDの寸法変化率を算出し、その平均値を求めた。1.5%以下であれば、熱プレス成形用離型フィルムとして実用上好ましい。
Claims (6)
- 少なくとも一方の表面が離型層として構成されている熱プレス成形用離型フィルムであって、前記の離型層は、官能基を有する融点60℃以上の離型剤(B−1)及び融点100℃以上のポリオレフィン樹脂(B−2)からなる群より選ばれた少なくとも一種の離型性付与剤(B)と残存テトラヒドロフラン量が300ppm以下であるポリブチレンテレフタレート樹脂(A)とを含む樹脂組成物から成り、濡れ張力が30mN/m以下であることを特徴とする熱プレス成形用離型フィルム。
- ポリブチレンテレフタレート樹脂(A)の示差熱分析による降温速度20℃/分での結晶化温度が175℃以上である請求項1に記載の熱プレス成形用離型フィルム。
- ポリブチレンテレフタレート樹脂(A)の末端カルボキシル基量が50eq/t以下である請求項1又は2に記載の熱プレス成形用離型フィルム。
- 離型性付与剤(B)がポリプロピレン樹脂である請求項1〜3の何れかに記載の熱プレス成形用離型フィルム。
- 離型層中のポリブチレンテレフタレート樹脂(A)100重量部に対する離型剤(B−1)の割合が0.05〜5重量部であり、ポリオレフィン樹脂(B−2)の割合が5〜100重量部である請求項1〜4の何れかに記載の熱プレス成形用離型フィルム。
- プリント配線基板、フレキシブルプリント配線基板または多層プリント配線板の熱プレス成形用離型フィルムである請求項1〜5の何れかに記載の熱プレス成形用離型フィルム。