JP2004530778A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2004530778A5 JP2004530778A5 JP2003509004A JP2003509004A JP2004530778A5 JP 2004530778 A5 JP2004530778 A5 JP 2004530778A5 JP 2003509004 A JP2003509004 A JP 2003509004A JP 2003509004 A JP2003509004 A JP 2003509004A JP 2004530778 A5 JP2004530778 A5 JP 2004530778A5
- Authority
- JP
- Japan
- Prior art keywords
- comonomer
- propylene
- random copolymer
- copolymer
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 125000004805 propylene group Chemical group [H]C([H])([H])C([H])([*:1])C([H])([H])[*:2] 0.000 claims 20
- 229920005604 random copolymer Polymers 0.000 claims 15
- 239000005977 Ethylene Substances 0.000 claims 12
- 229920001577 copolymer Polymers 0.000 claims 12
- VGGSQFUCUMXWEO-UHFFFAOYSA-N ethene Chemical compound C=C VGGSQFUCUMXWEO-UHFFFAOYSA-N 0.000 claims 12
- 238000000034 method Methods 0.000 claims 10
- 239000002002 slurry Substances 0.000 claims 9
- 125000004432 carbon atoms Chemical group C* 0.000 claims 4
- 239000003054 catalyst Substances 0.000 claims 4
- 238000010828 elution Methods 0.000 claims 4
- 239000004711 α-olefin Substances 0.000 claims 4
- 238000006243 chemical reaction Methods 0.000 claims 3
- 238000007334 copolymerization reaction Methods 0.000 claims 3
- 238000004519 manufacturing process Methods 0.000 claims 3
- 238000000071 blow moulding Methods 0.000 claims 2
- 239000000835 fiber Substances 0.000 claims 2
- 238000001746 injection moulding Methods 0.000 claims 2
- 238000006116 polymerization reaction Methods 0.000 claims 2
- 230000000379 polymerizing Effects 0.000 claims 2
- 230000002902 bimodal Effects 0.000 claims 1
- 238000002844 melting Methods 0.000 claims 1
- CTQNGGLPUBDAKN-UHFFFAOYSA-N o-xylene Chemical compound CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 claims 1
- 229920000642 polymer Polymers 0.000 claims 1
- 239000008096 xylene Substances 0.000 claims 1
Claims (29)
- 触媒存在下、プロピレンとコモノマー、但し上記コモノマーはエチレン又は少なくとも4の炭素原子を含むα−オレフィンである、との重合化を含むプロピレンランダム共重合体の製造方法であって、少なくとも1のスラリー反応器を含む第1の反応領域においてプロピレンをコモノマーと重合化させて、第1の重合化生成物を与えること、上記第1の生成物を、少なくとも1の気相反応器を含む第2の反応領域に移動させること、及び上記第1の重合化生成物の存在下、上記気相反応器においてプロピレンをコモノマーと重合化させることを含む多段階工程を含む方法において、気相反応器中の温度がスラリー反応器中の温度よりも少なくとも10℃高い製造方法。
- 上記気相反応器中の温度が、上記スラリー反応器中の温度よりも少なくとも15℃高い、請求項1に記載の方法。
- 気相反応器において製造された生成物のコモノマー含有量がスラリー反応器において製造された生成物のコモノマー含有量より高いところの、請求項1又は2のいずれか1項に記載の方法。
- 気相反応器において生成された生成物のコモノマー含有量が、スラリー反応器において製造された生成物のコモノマー含有量より少なくとも0.5重量%、好ましくは少なくとも1重量%高いところの、請求項3に記載の方法。
- 上記コモノマーがエチレンであるところの、請求項1〜4のいずれか1項に記載の方法。
- スラリー反応器において生成された生成物のエチレン含有量が2〜6重量%、好ましくは2〜4重量%であるところの、請求項5に記載の方法。
- 気相反応器において生成された生成物のエチレン含有量が3〜12重量%、好ましくは4〜10重量%であるところの、請求項5又は6のいずれか1項に記載の方法。
- スラリー反応器がバルク反応器、好ましくはバルクループ反応器であるところの、請求項1〜7のいずれか1項に記載の方法。
- スラリー反応器における温度が70℃以上であるところの、請求項1〜8のいずれか1項に記載の方法。
- 気相反応器における温度が80℃以上、好ましくは85℃以上であるところの、請求項1〜9のいずれか1項に記載の方法。
- スラリー反応器及び気相反応器間の生産比が30:70〜70:30、好ましくは40:60〜60:40、そして特に45:55〜55:45であるところの、請求項1〜10のいずれか1項に記載の方法。
- 触媒が、触媒成分、共触媒成分及び外部供与体を含むチーグラー−ナッタ型触媒系であるところの、請求項1〜11のいずれか1項に記載の方法。
- 請求項1〜12のいずれか1項に記載の方法により得られ得るプロピレンランダム共重合体。
- プロピレンとコモノマー、但し上記コモノマーはエチレン又は少なくとも4の炭素原子を含むα−オレフィンである、との共重合化により製造されるプロピレンランダム共重合体において、TREF法により測定されるコモノマーの分布がマルチモーダル、好ましくはバイモーダルであり、かつTREF法に従って測定された90℃までの温度において溶出する上記共重合体の成分の量が、共重合体の全体量の50重量%未満であるところのプロピレンランダム共重合体。
- TREF法に従って測定された50℃以上の溶出間隔を有する、請求項13又は14のいずれか1項に記載のプロピレンランダム共重合体。
- プロピレンとコモノマー、但し上記コモノマーはエチレン又は少なくとも4の炭素原子を含むα−オレフィンである、との共重合化により製造されたプロピレンランダム共重合体において、該共重合体が、TREF法に従って測定された50℃以上の溶出間隔を有し、かつTREF法に従って測定された90℃までの温度において溶出する上記共重合体の成分の量が共重合体全体量の50重量%未満であるところの、プロピレンランダム共重合体。
- 135℃以上の溶融温度Tmを有する、請求項13〜16のいずれか1項に記載のプロピレンランダム共重合体。
- 6重量%以下のエチレン含有量を有する、請求項13〜17のいずれか1項に記載のプロピレンランダム共重合体。
- プロピレンとコモノマー、但し上記コモノマーはエチレン又は少なくとも4の炭素原子を含むα―オレフィンである、との共重合により製造されるプロピレンランダム共重合体において、該ランダム共重合体はユニモーダルのポリマーであり、TREF法により測定される溶出間隔は式、
Y≦4.5・m+16
ここでYは℃で表される溶出間隔であり、mは重量%で表される共重合体におけるエチレンの百分率である、により与えられるところの共重合体。 - コモノマーがエチレンであるところの、請求項13〜19のいずれか1項に記載のプロピレンランダム共重合体。
- 合計エチレン含有量が3重量%以上、好ましくは5重量%以上であるところの、請求項13〜20のいずれか1項に記載のプロピレンランダム共重合体。
- 合計エチレン含有量が12重量%以下、好ましくは8重量%以下であるところの、請求項13〜21のいずれか1項に記載のプロピレンランダム共重合体。
- キシレン可溶物含有量が4〜24重量%、より好ましくは5〜15重量%、さらにより好ましくは6〜10重量%であるところの、請求項13〜22のいずれか1項に記載のプロピレンランダム共重合体。
- 請求項13〜23のいずれか1項に記載の共重合体を含むフィルム。
- 物品がブロー成型により製造されたところの、請求項13〜23のいずれか1項に記載の共重合体を含む物品。
- 物品が射出成型により製造されたところの、請求項13〜23のいずれか1項に記載の共重合体を含む物品。
- 請求項13〜23のいずれか1項に記載の共重合体を含むファイバ。
- 請求項13〜23のいずれか1項に記載の共重合体を含むパイプ。
- フィルム、ブロー又は射出成型による物品、ファイバ又はパイプの製造のために請求項13〜23のいずれか1項に記載の共重合体を使用する方法。