CN1668448A - 含有通过加聚交联的硅酮的制品的表面处理方法 - Google Patents

含有通过加聚交联的硅酮的制品的表面处理方法 Download PDF

Info

Publication number
CN1668448A
CN1668448A CN03816963.0A CN03816963A CN1668448A CN 1668448 A CN1668448 A CN 1668448A CN 03816963 A CN03816963 A CN 03816963A CN 1668448 A CN1668448 A CN 1668448A
Authority
CN
China
Prior art keywords
silicone
plasma
pos
cross
optional
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN03816963.0A
Other languages
English (en)
Chinese (zh)
Inventor
L·迪蒙
A·普谢隆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rhodia Chimie SAS
Original Assignee
Rhone Poulenc Chimie SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rhone Poulenc Chimie SA filed Critical Rhone Poulenc Chimie SA
Publication of CN1668448A publication Critical patent/CN1668448A/zh
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/12—Bonding of a preformed macromolecular material to the same or other solid material such as metal, glass, leather, e.g. using adhesives
    • C08J5/124—Bonding of a preformed macromolecular material to the same or other solid material such as metal, glass, leather, e.g. using adhesives using adhesives based on a macromolecular component
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C59/00—Surface shaping of articles, e.g. embossing; Apparatus therefor
    • B29C59/005—Surface shaping of articles, e.g. embossing; Apparatus therefor characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C59/00—Surface shaping of articles, e.g. embossing; Apparatus therefor
    • B29C59/14—Surface shaping of articles, e.g. embossing; Apparatus therefor by plasma treatment
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J7/00—Chemical treatment or coating of shaped articles made of macromolecular substances
    • C08J7/12—Chemical modification
    • C08J7/123—Treatment by wave energy or particle radiation
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J5/00—Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers
    • C09J5/02—Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers involving pretreatment of the surfaces to be joined
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C59/00—Surface shaping of articles, e.g. embossing; Apparatus therefor
    • B29C59/14—Surface shaping of articles, e.g. embossing; Apparatus therefor by plasma treatment
    • B29C2059/145—Atmospheric plasma
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2083/00—Use of polymers having silicon, with or without sulfur, nitrogen, oxygen, or carbon only, in the main chain, as moulding material
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2383/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen, or carbon only; Derivatives of such polymers
    • C08J2383/04—Polysiloxanes

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Manufacturing & Machinery (AREA)
  • General Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Paints Or Removers (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Laminated Bodies (AREA)
  • Moulds For Moulding Plastics Or The Like (AREA)
  • Shaping Of Tube Ends By Bending Or Straightening (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Treatments Of Macromolecular Shaped Articles (AREA)
CN03816963.0A 2002-06-17 2003-06-17 含有通过加聚交联的硅酮的制品的表面处理方法 Pending CN1668448A (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FR0207443A FR2840826B1 (fr) 2002-06-17 2002-06-17 Procede de traitement de surface d'un article comportant du silicone reticule par polyaddition
FR0207443 2002-06-17

Publications (1)

Publication Number Publication Date
CN1668448A true CN1668448A (zh) 2005-09-14

Family

ID=29595309

Family Applications (1)

Application Number Title Priority Date Filing Date
CN03816963.0A Pending CN1668448A (zh) 2002-06-17 2003-06-17 含有通过加聚交联的硅酮的制品的表面处理方法

Country Status (7)

Country Link
US (1) US7423234B2 (enExample)
EP (1) EP1513667A1 (enExample)
JP (1) JP4255911B2 (enExample)
CN (1) CN1668448A (enExample)
AU (1) AU2003255704A1 (enExample)
FR (1) FR2840826B1 (enExample)
WO (1) WO2003106145A1 (enExample)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102354670A (zh) * 2011-10-13 2012-02-15 无锡世一电力机械设备有限公司 一种提高半导体封装可靠性的综合表面处理方法
CN102491254A (zh) * 2011-12-14 2012-06-13 天津大学 一种聚二甲基硅氧烷弹性体选区皱纹化的方法
CN101754563B (zh) * 2008-12-22 2012-10-10 财团法人工业技术研究院 壳体及应用其的喷射式等离子体系统
US8316796B2 (en) 2007-09-10 2012-11-27 Industrial Technology Research Institute Film coating system and isolating device thereof
CN106147601A (zh) * 2015-04-23 2016-11-23 上海晶华胶粘新材料股份有限公司 胶粘剂制品底涂剂及其制备工艺
CN107207912A (zh) * 2015-02-05 2017-09-26 法国圣戈班玻璃厂 用于封装具有防划痕涂层的聚碳酸酯窗玻璃的方法

Families Citing this family (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2840911B1 (fr) * 2002-06-18 2005-09-30 Rhodia Chimie Sa Composition silicone utile notamment pour la realisation de vernis anti-friction, procede d'application de ce vernis sur un support et support ainsi traite
FR2840912B1 (fr) * 2002-06-18 2005-10-21 Rhodia Chimie Sa Emulsion silicone aqueuse pour le revetement de supports fibreux tisses ou non
US8586149B2 (en) 2003-06-18 2013-11-19 Ford Global Technologies, Llc Environmentally friendly reactive fixture to allow localized surface engineering for improved adhesion to coated and non-coated substrates
DE102004033728B4 (de) * 2004-07-13 2009-07-23 Plasmatreat Gmbh Verfahren zum Bearbeiten und Verkleben von Werkstücken aus einem Metall oder einer Metalllegierung mit einer hydratisierten Oxid- und/oder Hydroxidschicht
DE102005020511A1 (de) * 2005-04-29 2006-11-09 Basf Ag Verbundelement, insbeondere Fensterscheibe
JP4586981B2 (ja) * 2005-06-23 2010-11-24 信越化学工業株式会社 自己接着性オルガノポリシロキサン組成物
US7517561B2 (en) * 2005-09-21 2009-04-14 Ford Global Technologies, Llc Method of coating a substrate for adhesive bonding
BRPI0520574A2 (pt) * 2005-09-30 2009-05-19 Airbus Espana Sl método de tratamento superficial de estruturas de material composto com feixes de plasma atmosférico
RU2378117C1 (ru) * 2005-09-30 2010-01-10 Айрбус Эспанья, С.Л. Способ поверхностной обработки структур композиционного материала пучками плазмы при атмосферном давлении
WO2008069856A1 (en) * 2006-12-06 2008-06-12 Dow Corning Corporation Airbag and process for its assembly
FR2925911A1 (fr) * 2007-12-27 2009-07-03 Bmuestar Silicones France Sas Silicones-autoadhesifs, procede de fabrication, complexes les utilisant et applications
WO2009143090A2 (en) * 2008-05-22 2009-11-26 Dow Corning Corporation Process and composition for fabricating non-sewn seams
JP5571295B2 (ja) * 2008-07-14 2014-08-13 東レ・ダウコーニング株式会社 ヒドロシリル化反応により硬化してなるシリコーン層を備えた基材の製造方法および回収された有機溶媒を使用するシリコーン組成物
JP5504491B2 (ja) * 2008-09-17 2014-05-28 国立大学法人 筑波大学 支持体表面の処理用架橋重合体組成物
JP2012508610A (ja) * 2008-11-14 2012-04-12 カーディアック ペースメイカーズ， インコーポレイテッド 埋め込み型医療装置内のポリマーチューブの低温プラズマ接合
US20100159195A1 (en) * 2008-12-24 2010-06-24 Quincy Iii Roger B High repellency materials via nanotopography and post treatment
US8163358B2 (en) 2009-02-18 2012-04-24 Synergeyes, Inc. Surface modification of contact lenses
CN102795592A (zh) * 2012-07-13 2012-11-28 天津大学 Pdms弹性体表面硬质薄膜层选区刻蚀的制备方法及应用
US10978277B2 (en) * 2015-05-11 2021-04-13 Nova Plasma Ltd. Apparatus and method for handling an implant
CN105699703B (zh) * 2016-01-26 2018-08-03 天津大学 利用表面起皱测量偶氮苯薄膜光软化的方法
DE202018006837U1 (de) 2017-02-08 2023-08-02 Elkem Silicones USA Corp. Sekundärbatterie-Pack mit verbessertem Thermomanagement
US10170301B2 (en) 2017-03-29 2019-01-01 International Business Machines Corporation Adhesion of polymers on silicon substrates
JP6921223B2 (ja) 2017-03-29 2021-08-18 エルケム・シリコーンズ・フランス・エスアエスＥＬＫＥＭ ＳＩＬＩＣＯＮＥＳ Ｆｒａｎｃｅ ＳＡＳ 部品のオーバーモールディングに有用な重付加架橋性シリコーン組成物
JP2020516755A (ja) * 2017-04-17 2020-06-11 コーネル ユニバーシティー フッ素フリーの撥油コーティング、その製造方法、及びその使用
DE102017212974B4 (de) * 2017-07-27 2024-08-01 Gerresheimer Bünde Gmbh Verfahren zur Beschichtung und Werkstück
KR102327838B1 (ko) * 2018-09-20 2021-11-17 주식회사 엘지화학 적층필름

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4163082A (en) * 1978-10-23 1979-07-31 Dow Corning Corporation U.V.-radiation method for decreasing surface tack of disposed organopolysiloxane greases and gels
GB2045824B (en) 1979-03-16 1982-12-15 Dow Corning Ltd Treatment of sured silicon elastomer
US4508606A (en) * 1983-02-27 1985-04-02 Andrade Joseph D Process for treating polymer surfaces to reduce their friction resistance characteristics when in contact with non-polar liquid, and resulting products
JPS61244546A (ja) * 1985-04-22 1986-10-30 信越ポリマ−株式会社 耐熱防眩シ−ト
FR2600660B1 (fr) * 1986-06-24 1988-11-18 Rhone Poulenc Chimie Emulsions aqueuses de compositions organopolysiloxane polyaddition pour l'enduction de materiaux souples
FR2617760B1 (fr) * 1987-07-10 1989-11-24 Souriau & Cie Procede d'assemblage de pieces en materiaux polymeres
JP2787349B2 (ja) 1989-10-06 1998-08-13 株式会社スリーボンド ネジ継手部用シール材組成物
JPH0645222B2 (ja) 1989-12-07 1994-06-15 信越化学工業株式会社 シリコーン一体成形物及びその製造法
US5147397A (en) * 1990-07-03 1992-09-15 Allergan, Inc. Intraocular lens and method for making same
US5364662A (en) * 1992-08-14 1994-11-15 Medtronic, Inc. Surface treatment of silicone rubber
EP0643106B1 (en) 1993-09-10 1999-12-22 Shin-Etsu Chemical Co., Ltd. Organopolysiloxane compositions, their preparation and use, rubber articles coated with them
US5506302A (en) * 1993-09-10 1996-04-09 Shin-Etsu Chemical Co., Inc. Organopolysiloxane composition and rubber substrate having a coating thereof
DE4333107A1 (de) 1993-09-29 1995-03-30 Bayer Ag Auf Trägern angebrachte ein- oder mehrlagige Schichtelemente und ihre Herstellung
TW279876B (enExample) 1993-12-27 1996-07-01 Shinetsu Chem Ind Co
US5468815A (en) 1994-01-12 1995-11-21 Minnesota Mining And Manufacturing Low coefficient of friction silicone release formulations incorporating higher alkenyl-functional silicone gums
JP3584410B2 (ja) 1994-09-01 2004-11-04 日本ペイント株式会社 複合塗膜形成方法
JP3379839B2 (ja) 1994-11-11 2003-02-24 ジーイー東芝シリコーン株式会社 ゴムコーティング布用コーティング組成物
FR2738830B1 (fr) * 1995-09-14 1997-12-05 Rhone Poulenc Chimie Emulsion aqueuse de polyorganosiloxane pour l'enduction de matiere textile
US5827921A (en) * 1995-11-29 1998-10-27 Shin-Etsu Chemical Co., Ltd. Silicone-based aqueous emulsion composition
JPH1025698A (ja) 1996-05-07 1998-01-27 Fujimori Kogyo Kk 剥離シートの製造方法
DE19628447A1 (de) 1996-07-15 1998-01-22 Bayer Ag Wäßrige Emulsionen, ein Verfahren zur Herstellung und deren Verwendung
GB9705524D0 (en) 1997-03-18 1997-05-07 Dow Corning Coated textile fabrics
DE29805999U1 (de) * 1998-04-03 1998-06-25 Agrodyn Hochspannungstechnik GmbH, 33803 Steinhagen Vorrichtung zur Plasmabehandlung von Oberflächen
JP3945082B2 (ja) 1999-08-24 2007-07-18 信越化学工業株式会社 コーティング用液状シリコーンゴム組成物及びエアーバッグ布
DE19946252A1 (de) * 1999-09-27 2001-04-05 Fraunhofer Ges Forschung Verfahren zur Herstellung selbstorganisierter Strukturen auf einer Substratoberfläche
DE10011276A1 (de) * 2000-03-08 2001-09-13 Wolff Walsrode Ag Verwendung eines indirrekten atomosphärischen Plasmatrons zur Oberflächenbehandlung oder Beschichtung bahnförmiger Werkstoffe sowie ein Verfahren zur Behandlung oder Beschichtung bahnförmiger Werkstoffe
CA2406050A1 (en) * 2000-04-14 2001-10-25 Karl Reimer Apparatus and method for continuous surface modification of substrates

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8316796B2 (en) 2007-09-10 2012-11-27 Industrial Technology Research Institute Film coating system and isolating device thereof
CN101754563B (zh) * 2008-12-22 2012-10-10 财团法人工业技术研究院 壳体及应用其的喷射式等离子体系统
CN102354670A (zh) * 2011-10-13 2012-02-15 无锡世一电力机械设备有限公司 一种提高半导体封装可靠性的综合表面处理方法
CN102491254A (zh) * 2011-12-14 2012-06-13 天津大学 一种聚二甲基硅氧烷弹性体选区皱纹化的方法
CN102491254B (zh) * 2011-12-14 2014-07-30 天津大学 一种聚二甲基硅氧烷弹性体选区皱纹化的方法
CN107207912A (zh) * 2015-02-05 2017-09-26 法国圣戈班玻璃厂 用于封装具有防划痕涂层的聚碳酸酯窗玻璃的方法
CN106147601A (zh) * 2015-04-23 2016-11-23 上海晶华胶粘新材料股份有限公司 胶粘剂制品底涂剂及其制备工艺

Also Published As

Publication number Publication date
EP1513667A1 (fr) 2005-03-16
AU2003255704A1 (en) 2003-12-31
FR2840826A1 (fr) 2003-12-19
FR2840826B1 (fr) 2005-04-15
US7423234B2 (en) 2008-09-09
JP2005531654A (ja) 2005-10-20
US20060157453A1 (en) 2006-07-20
JP4255911B2 (ja) 2009-04-22
WO2003106145A1 (fr) 2003-12-24

Similar Documents

Publication Publication Date Title
CN1668448A (zh) 含有通过加聚交联的硅酮的制品的表面处理方法
CN1304482C (zh) 主要用于形成减摩清漆的硅酮组合物,将所述清漆施涂于基材的方法,以及处理的基材
CN1296434C (zh) 可交联粘合剂硅氧烷组合物及其在粘结各种基质方面的用途
CN1646631A (zh) 自粘性助交联的硅橡胶混合物和其制备方法以及复合模制件的制备方法及其应用
CN1697900A (zh) 使用可被交联成弹性体的硅氧烷组合物浸渍处理建筑用织物的方法以及如此获得的涂布的建筑用织物
CN1229439C (zh) 硅氧烷组合物和固化的硅氧烷产品
CN1834179A (zh) 可加热固化的聚硅氧烷弹性体的底漆
CN1860182A (zh) 表面性能得到改进的硅氧烷和用于制备该硅氧烷的可固化硅氧烷组合物
CN1072429A (zh) 含有锡化合物的组合物
CN1256995A (zh) 脱模剂
CN1098311C (zh) 由可交联的有机聚硅氧烷组合物制备涂层的方法
CN1678701A (zh) 用于渍浸处理纤维材料的可交联成弹性体的硅氧烷油组合物
CN1229440C (zh) 自粘性热交联单罐装聚硅氧烷组合物
CN1255461C (zh) 过渡金属化合物的混合物提高聚硅氧烷高弹体耐电弧径迹和电弧腐蚀性的用途以及具有该性能的制品
CN1644623A (zh) 加成交联硅氧烷树脂组合物
CN1771126A (zh) 改善了与纸和聚合物膜之间粘附力的纸隔离组合物
CN1662310A (zh) 用于制备含数个通过加聚交联并相互牢固粘合的有机硅元件的组件的方法
CN1875071A (zh) 可固化的硅氧烷组合物及其固化产物
CN1445268A (zh) 有机硅化合物为基础的可交联组合物
CN1829761A (zh) 在金属催化剂存在下通过脱氢缩合可交联的有机硅组合物
CN1639413A (zh) 交联硅氧烷型逆乳液制备“透湿防水”涂层的用途
CN1183112A (zh) 有机聚硅氧烷的水分散液
JP2019019227A (ja) 熱伝導性シリコーン樹脂組成物
CN1288218C (zh) 用作硅氧烷涂料组合物的防雾添加剂的支链型有机硅化合物
CN1668676A (zh) 作为硅氧烷涂料组合物的防雾添加剂的支链型烯基官能硅氧烷聚合物

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
AD01 Patent right deemed abandoned

Effective date of abandoning: 20050914

C20 Patent right or utility model deemed to be abandoned or is abandoned