CN113161548A - 一种无钴的镍锰正极材料及其制备方法和应用 - Google Patents
一种无钴的镍锰正极材料及其制备方法和应用 Download PDFInfo
- Publication number
- CN113161548A CN113161548A CN202110335607.5A CN202110335607A CN113161548A CN 113161548 A CN113161548 A CN 113161548A CN 202110335607 A CN202110335607 A CN 202110335607A CN 113161548 A CN113161548 A CN 113161548A
- Authority
- CN
- China
- Prior art keywords
- cobalt
- manganese
- nickel
- free
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于电池材料技术领域,公开了一种无钴层状的镍锰正极材料及其制备方法和应用,该无钴层状的镍锰正极材料的化学式为LiaNixMnyMezO2@Mb,Me为Zr、Al、W、Sr、Ti或Mg中的至少一种;M为Al2O3、CeO2、TiO2、Yb2O3、Nb2O5、La2O3、WO3、钛溶胶、铝溶胶、钛铝溶胶、异丙醇铝、钛酸丁酯、磷酸氢二铝或钨酸锂中的至少一种。本发明通过金属氧化物包覆后高温烧结达到浅层包覆,材料浅层包覆有利于阻止材料在循环过程中由于充放电过程材料结构变化和内部应力变化产生的微裂纹扩张。
Description
技术领域
本发明属于电池材料技术领域,具体涉及一种无钴的镍锰正极材料及其制备方法和应用。
背景技术
目前市场上能量密度较高的正极材料为镍钴锰三元正极材料,但是由于镍钴锰三元正极材料中含有钴元素,而钴属于稀缺资源,钴价格呈现出增长趋势,这就使得正极材料的价格随着钴含量发生较大波动,故开发无钴正极材料便成为今后的一种趋势,可降低正极材料由于钴的价格造成成本高的问题,其次市场上对于层状镍锰正极材料的报道较少,尤其是中低镍含量无钴正极材料。
因此,亟需研发一种镍含量相对较低的层状无钴正极材料。
发明内容
本发明旨在至少解决上述现有技术中存在的技术问题之一。为此,本发明提出一种无钴的镍锰正极材料及其制备方法和应用,将正极材料的镍含量做的相对较低,以及通过掺杂高价态金属元素改变正极材料中部分元素价态,可以稳定三元正极材料晶体结构,让锂离子脱出和嵌入,使得能垒降低,使正极材料中存在较多的电子空位,提升正极材料容量。
为实现上述目的,本发明采用以下技术方案:
一种无钴层状的镍锰正极材料,所述无钴层状的镍锰正极材料的化学式为LiaNixMnyMezO2@Mb,所述Me为Zr、Al、W、Sr、Ti或Mg中的至少一种;所述M为Al2O3、CeO2、TiO2、Yb2O3、Nb2O5、La2O3、WO3、钛溶胶、铝溶胶、钛铝溶胶、异丙醇铝、钛酸丁酯、磷酸氢二铝或钨酸锂中的至少一种,其中0.9≤a≤1.10,0.50≤x≤0.70,0.50≤y≤0.30,0.001≤z≤0.009,0.001≤b≤0.005。
优选地,所述无钴层状的镍锰正极材料的比表面积为0.4~0.9m2/g,粒度D50为3.0~5.0μm。
一种无钴层状的镍锰正极材料的制备方法,包括以下步骤:
(1)将镍盐与锰盐配置成A溶液,再滴加氢氧化钠与氨水的混合液,搅拌反应,洗涤,烘干,即得镍锰氢氧化物前驱体NixMny(OH)2;
(2)将所述镍锰氢氧化物前驱体NixMny(OH)2与锂源、掺杂剂混合,进行第一次烧结,粉碎后得到无钴的镍锰正极材料LiaNixMnyMezO2;
(3)将所述无钴的镍锰正极材料LiaNixMnyMezO2与包覆剂A混合,经过第二次烧结、过筛,得到金属氧化物包覆的无钴层状的镍锰正极材料;
(4)将包覆剂B喷雾到所述金属氧化物包覆的无钴层状的镍锰正极材料表面进行湿法包覆,真空干燥,即得双重包覆的无钴层状正极材料LiaNixMnyMezO2@Mb。
优选地,步骤(1)中,所述镍盐为NiSO4、Ni(CH3COO)2、Ni(NO3)2、C2O4·Ni或NiCl2中的至少一种。
优选地,步骤(1)中,所述锰盐为MnSO4、Mn(NO3)2、MnC2O4或MnCl2中的至少一种。
优选地,步骤(1)中,所述A溶液浓度按镍锰离子混合液计算,配置浓度要求为2.0mol/L-3.2mol/L。
优选地,步骤(1)中,所述反应的温度为55±5℃,反应的时间为2-10h。
优选地,步骤(2)中,所述锂源为LiOH·H2O、Li2CO3或CH3COOLi中的至少一种。
优选地,步骤(2)中,所述掺杂剂为ZrO2、Al2O3、Al(OH)3、WO3、SrO、TiO2、Mg(OH)2或MgO2中的至少一种。
优选地,步骤(2)中,所述前驱体中的金属与锂盐的金属摩尔含量比Li/M1=0.9~1.10(M1为前驱体中金属Ni、Co、Mn金属摩尔含量)。
优选地,步骤(2)中,所述第一次烧结的温度为450℃-980℃;第一次烧结的时间为5h-27h。
优选地,步骤(3)中,所述包覆剂A为Al2O3、CeO2、TiO2、Yb2O3、Nb2O5、La2O3或WO3中的至少一种。
优选地,步骤(3)中,所述第二次烧结的温度为250℃-600℃;第二次烧结的时间为5h-12h。
优选地,步骤(4)中,所述包覆剂B为钛溶胶、铝溶胶、钛铝溶胶、异丙醇铝、钛酸丁酯、磷酸氢二铝或钨酸锂中的至少一种。
优选地,步骤(4)中,所述双重包覆的无钴层状的镍锰正极材料为表面膜状包覆和金属氧化物包覆的无钴层状的镍锰正极材料。
优选地,步骤(4)中,所述真空干燥的温度为130℃-180℃。
一种电池,包括所述的无钴层状的镍锰正极材料。
相对于现有技术,本发明的有益效果如下:
1.本发明通过金属氧化物包覆后高温烧结达到浅层包覆,材料浅层包覆有利于阻止材料在循环过程中由于充放电过程材料结构变化和内部应力变化产生的微裂纹扩张;通过在材料表面浅层包覆,能有效阻止微裂纹扩张到材料表面,提升材料在高电压下的使用寿命,提高材料循环性能,材料100次循环容量保持率达到96.5%。
2.本发明在材料表面通过湿法喷雾方式将包覆剂致密的包覆在材料表面,形成区别于干法包覆得到的点接触包覆的致密膜状包覆,更有利于阻止材料直接与电解液接触,抑制材料中的阳离子溶出,提升材料的结构稳定性,提升材料的循环性能。
3.本发明用廉价的Mn取代价值昂贵Co或部分的镍,因材料中不含钴,制备成本下降20-30%。并将材料的镍含量做的相对较低,低成本的锰稳定材料结构,以及通过掺杂高价态金属元素改变材料中部分元素价态,可以稳定材料的晶体结构,让锂离子脱出和嵌入能垒降低,使材料中存在较多的电子空位,提升材料容量,如实施例1中,正极材料的首次充电容量达到208.6mAh/g,首次放电容量达到186.9mAh/g,首次放电效率高达89.6%。
附图说明
图1为实施例1中步骤(3)所得单晶形貌的无钴层状的镍锰正极材料SEM图;
图2为实施例1中步骤(5)所得金属氧化物包覆的单晶形貌无钴层状的镍锰正极材料SEM图;
图3为实施例1中步骤(6)所得双重包覆的无钴层状的镍锰正极材料SEM图;
图4为实施例2中步骤(3)所得类单晶形貌的无钴层状的镍锰正极材料SEM图;
图5为实施例2中步骤(5)所得金属氧化物包覆的类单晶形貌无钴层状的镍锰正极材料SEM图;
图6为实施例1-2包覆剂包覆后无钴层状的镍锰正极材料的包覆示意图;
图7为实施例1-2制得的膜状包覆钛溶胶和金属氧化物包覆的单晶形貌无钴层状的镍锰正极材料以及对比例1-3所得的无钴层状的镍锰正极材料的XRD对比图。
具体实施方式
以下将结合实施例对本发明的构思及产生的技术效果进行清楚、完整地描述,以充分地理解本发明的目的、特征和效果。显然,所描述的实施例只是本发明的一部分实施例,而不是全部实施例,基于本发明的实施例,本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例,均属于本发明保护的范围。
实施例1
本实施例的无钴层状的镍锰正极材料(Li1.06Ni0.6Mn0.3974Me0.0026O2@(Al2O3)0.001·(TiO2)0.0015)的制备方法,具体步骤如下:
(1)将NiSO4与MnSO4按摩尔比Ni:Mn=6:4配置成2.5mol/L的溶液A,放置于反应搅拌釜中搅拌,搅拌转速25rpm/min,再将氢氧化钠与氨水按5m3/h流量滴加入配置好的A溶液中,反应温度为55℃~60℃,反应时间2h,反应完成后使用去离子水洗涤后,放置于离心机中进行过滤,离心转速为600rpm/min,离心时间为90min,然后经过150℃烘干,烘干时间为4h,最后得到无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2;
(2)将上述无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2与碳酸锂、WO3和SrO混合(其中锂与氢氧化物前驱体中Ni、Co、Mn金属的摩尔比为1.06:1,掺杂W元素为2000ppm,掺杂Sr元素为1500ppm),经过高速混合机混合,混合转速为300rpm/min混合10min,500rp m/min混合30min,得到混合物料;
(3)将混合物料在箱式炉中进行第一次烧结,使用装钵量为3.5kg/钵,空气气氛,空气进气压力为0.15Mpa,进气流量使用底进气方式,流量为10m3/h,烧结过程为:先使用3℃/min升温速率将温度升到550℃,然后再2.5℃/min升温速率升温到750℃进行保温5h,然后再已升温速率为2℃/min升温到950℃进行保温11h,最后以3℃/min的降温速率进行降温至室温,再经过气流粉碎,将物料粒度D50粉碎为3.5μm得到单晶形貌的无钴层状的镍锰正极材料,形貌如图1所示;
(4)然后将上述无钴层状的镍锰正极材料与Al2O3混合(其中Al为1000ppm),经过高速混合机,混合转速为200rpm/min混合10min,250rpm/min混合15min,300rpm/min混合20min,得到混合物;
(5)将混合物在箱式炉中进行第二次烧结,烧结过程为:先使用3℃/min升温速率升到600℃,然后进行保温6h,最后以3℃/min降温速率降温到室温,然后经过300目筛网过筛得到Al2O3包覆的单晶形貌无钴层状的镍锰正极材料,形貌如图2所示;
(6)将钛溶胶(其中Ti为1500ppm)在酒精相中稀释3倍后喷雾到金属氧化物包覆的无钴层状的镍锰正极材料上进行湿法包覆,喷雾完成后进行真空烘干,烘干温度为150℃,烘干时间4h,得到双重包覆的无钴层状的镍锰正极材料Li1.06Ni0.6Mn0.3974Me0.0026O2@(Al2O3)0.001·(TiO2)0.0015,如图3所示。
实验测试
(1)正极片制备:以上述实施例1步骤(6)中自制正极材料为活性物质,以NMP为溶剂,将活性物质:SP:聚四氟乙烯按质量比为90:4:6的混合均匀涂在铝箔上,经过辊压等制备得到正极极片。
(2)电池组装:以金属锂作为负极,电解液为1mol/L的LiPF6,在充满氩气的不锈钢干燥手套箱中完成电池组装。
测试:将组装的电池静置12h后采用电池测试系统进行25℃,电流0.1C,充电电压(2.75~4.4)V下测试其电化学性能。
实施例2
本实施例的无钴层状的镍锰正极材料(Li1.04Ni0.6Mn0.3969Me0.0031O2@(Al2O3·TiO2)0.001·(Li2WO4)0.0015)的制备方法,具体步骤如下:
(1)将NiSO4与MnSO4按摩尔比Ni:Mn=6:4配置成2.3mol/L的溶液A,放置于反应搅拌釜中搅拌,搅拌转速优选30rpm/min,再将氢氧化钠与氨水按6.3m3/h流量滴加入配置好的A溶液中,反应温度50℃~55℃,反应时间2.5h,反应完成后使用去离子水洗涤后,放置于离心机中进行过滤,离心转速为600rpm/min,离心时间为90min,然后经过150℃烘干,烘干时间为4h,最后得到无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2;
(2)将上述无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2与碳酸锂、ZrO2、WO3和SrO混合(其中锂与氢氧化物前驱体中Ni、Co、Mn金属的摩尔比为1.04:1,掺杂Zr元素为1500ppm,掺杂W元素为1500ppm,掺杂Sr元素为800ppm),经过高速混合机混合,混合转速为300rpm/min混合10min,400rpm/min混合15min,500rpm/min,混合30min,得到混合物料;
(3)将混合物料在箱式炉中进行第一次烧结,使用装钵量为3.5kg/钵,空气气氛,空气进气压力为0.15Mpa,进气流量使用底进气方式,流量为8m3/h,烧结过程为:先使用3℃/min升温速率将温度升到550℃,然后再2.5℃/min升温速率升温到750℃进行保温6h,然后再已升温速率为2℃/min升温到945℃进行保温11h,最后以3℃/min的降温速率进行降温至室温,再经过气流粉碎,将物料粒度D50粉碎为4.5微米得到类单晶形貌的无钴层状的镍锰正极材料,形貌如图4所示;
(4)然后将上述无钴层状的镍锰正极材料与TiO2、Al2O3混合(其中Ti为1000ppm,Al为1000ppm),经过高速混合机,混合转速为200rpm/min混合10min,250rpm/min混合15min,300rpm/min混合20min,得到混合物;
(5)将混合物在箱式炉中进行第二次烧结,烧结过程为:先使用3℃/min升温速率降温度升到650℃,然后进行保温6h,最后以2.5℃/min降温速率降温到室温,然后经过300目筛网过筛得到金属氧化物包覆的类单晶形貌无钴层状的镍锰正极材料,形貌如图5所示;
(6)将钨酸锂(其中钨为1500ppm)在水相中稀释3.3倍后喷雾到金属氧化物包覆的无钴层状的镍锰正极材料上进行湿法包覆,喷雾完成后进行真空烘干,烘干温度为140℃,烘干时间4.5h,得到双重包覆的类单晶形貌无钴层状镍锰正极材Li1.04Ni0.6Mn0.3969Me0.0031O2@(Al2O3·TiO2)0.001·(Li2WO4)0.0015。
实验测试
(1)正极片制备:以上述实施例2中步骤(5)中自制正极材料为活性物质,以NMP为溶剂,将活性物质:SP:聚四氟乙烯按质量比为90:4:6的混合均匀涂在铝箔上,经过辊压等制备得到正极极片;
(2)电池组装:以金属锂作为负极,电解液为1mol/L的LiPF6,在充满氩气的不锈钢干燥手套箱中完成电池组装。
测试:将组装的电池静置12h后采用电池测试系统进行25℃,电流0.1C,充电电压(2.75~4.4)V下测试其电化学性能。
对比例1
本对比例的无钴层状的镍锰正极材料(Li1.06Ni0.6Mn0.3974Me0.0026O2)的制备方法,具体步骤如下:
(1)将NiSO4与MnSO4按摩尔比Ni:Mn=6:4配置成2.5mol/L的溶液A,放置于反应搅拌釜中搅拌,搅拌转速25rpm/min,再将氢氧化钠与氨水按5m3/h流量滴加入配置好的A溶液中,反应温度为55℃~60℃,反应时间2h,反应完成后使用去离子水洗涤后,放置于离心机中进行过滤,离心转速为600rpm/min,离心时间为90min,然后经过150℃烘干,烘干时间为4h,最后得到无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2;
(2)将上述无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2与碳酸锂、WO3和SrO混合(其中锂与氢氧化物前驱体中Ni、Co、Mn金属的摩尔比为1.06:1,掺杂W元素为2000ppm,掺杂Sr元素为1500ppm),经过高速混合机混合,混合转速为300rpm/min混合10min,500rp m/min混合30min,得到混合物料;
(3)将混合物料在箱式炉中进行第一次烧结,使用装钵量为3.5kg/钵,空气气氛,空气进气压力为0.15Mpa,进气流量使用底进气方式,流量为10m3/h,烧结过程为:先使用3℃/min升温速率将温度升到550℃,然后再2.5℃/min升温速率升温到750℃进行保温5h,然后再已升温速率为2℃/min升温到950℃进行保温11h,最后以3℃/min的降温速率进行降温至室温,再经过气流粉碎,将物料粒度D50粉碎为3.5μm得到单晶形貌的无钴层状的镍锰正极材料,形貌如图1所示;
(4)将物料粒度D50粉碎为3.5微米得到单晶形貌的无钴层状的镍锰正极材料在箱式炉中进行第二次烧结,烧结温度为:先使用3℃/min升温速率升到600℃,然后进行保温6h,,最后以3℃/min降温速率降温到室温,然后经过300目筛网过筛得到单晶形貌无钴层状的镍锰正极材料Li1.06Ni0.6Mn0.3974Me0.0026O2。
对比例1所制备材料测试方法与实施例1中测试步骤(1)(2)(3)一样。
对比例2
本对比例的无钴层状的镍锰正极材料的制备方法,具体步骤如下:
对比例2与实施例1中步骤(1)(2)(3)(4)(5)所得正级材料制备方法一样,所制备材料测试方法与实施例1中测试步骤(1)(2)(3)一样。
对比例3
本对比例的无钴层状的镍锰正极材料的制备方法,具体步骤如下:
(1)将NiSO4与MnSO4按摩尔比Ni:Mn=6:4配置成2.3mol/L的溶液A,放置于反应搅拌釜中搅拌,搅拌转速优选30rpm/min,再将氢氧化钠与氨水按6.3m3/h流量滴加入配置好的A溶液中,反应温度为50℃~55℃,反应时间为2.5h,反应完成后使用去离子水洗涤后,放置于离心机中进行过滤,离心转速为600rpm/min,离心时间90min,然后经过150℃烘干,烘干时间为4h,最后得到无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2;
(2)将上述无钴镍锰氢氧化物前驱体Ni0.6Mn0.4(OH)2与碳酸锂,ZrO2、WO3和SrO混合(其中锂与氢氧化物前驱体中Ni、Co、Mn金属的摩尔比为1.04:1,掺杂Zr元素为1500ppm,掺杂W元素为1500ppm,掺杂Sr元素为800ppm),经过高速混合机混合,混合转速为300rpm/min混合10min,400rpm/min混合15min,500rpm/min,混合30min,得到混合物料;
(3)将混合物料在箱式炉中进行第一次烧结,使用装钵量为3.5kg/钵,空气气氛,空气进气压力为0.15Mpa,进气流量使用底进气方式,流量为8m3/h,烧结温度为:先使用3℃/min升温速率将温度升到550℃,然后再2.5℃/min升温速率升温到750℃进行保温6h,然后再已升温速率为2℃/min升温到945℃进行保温11h,最后以3℃/min的降温速率进行降温至室温,再经过气流粉碎,将物料粒度D50粉碎为4.5微米得到类单晶形貌的无钴层状的镍锰正极材料;
(4)将粒度D50粉碎为4.5微米得到类单晶形貌的无钴层状的镍锰正极材料在箱式炉中进行第二次烧结,烧结温度为:先使用3℃/min升温速率降温度升到650℃,然后进行保温6h,,最后以2.5℃/min降温速率降温到室温,然后经过300目筛网过筛得到类单晶形貌无钴层状的镍锰正极材料Li1.04Ni0.6Mn0.3969Me0.0031O2。
实验测试
(1)正极片制备:以上述对比例3中步骤(4)中自制正极材料为活性物质,以NMP为溶剂,将活性物质:SP:聚四氟乙烯=90:4:6的质量比混合均匀涂在铝箔上,经过辊压等制备得到正极极片;
(2)电池组装:以金属锂作为负极,电解液为1mol/L的LiPF6,在充满氩气的不锈钢干燥手套箱中完成电池组装。
测试:将组装的电池静置12h后采用电池测试系统进行25℃,电流0.1C,充电电压(2.75~4.4)V下测试其电化学性能。
实施例1-2和对比例1-3的正极材料的电化学性能的比较结果,如表1所示:
表1实施例1-2和对比例1-3的正极材料的电化学性能的比较结果
表1为实施例1-2和对比例1-3的正极材料的电化学性能的比较,实施例1在最高电压为4.4V,0.1C首次放电比容量为186.9mAh/g,放电效率为89.6%;50圈循环后放电比容量为184.3mAh/g,第50圈容量保持率为98.6%,第100圈容量保持率为96.5%,这明显优于对比例的正极材料的电化学性能,利用掺杂金属可稳定三元材料晶体结构结构,让锂离子脱出和嵌入能垒降低,还有通过金属氧化物均匀包覆正极材料后再通过钛溶胶膜状包覆在材料表面,降低了电解液与正极材料接触,降低副反应的发生,故通过喷雾方式膜状包覆和包覆金属氧化物已掺杂的单晶正极材料提高了电池的容量和循环性能;其次对比1和对比例3,单晶形貌材料和类单晶形貌材料,类单晶材料容量、首效,以及材料第50圈电性能,第100圈容量保持率,明显略高于单晶样品;对比实施例2和对比例3,对比例1和对比例2,材料的首次放电容量和首效以及50圈比容量和第100圈容量保持率明显较高,说明材料通过金属氧化物包覆正极材料,能有效提升材料电性能,提高电池的容量和循环性能。
图1为实施例1中步骤(3)所得单晶形貌的无钴层状的镍锰正极材料SEM图;从图中可得材料为单晶形貌,且材料单晶分散性较好,一次粒子较均匀。
图2为实施例1中步骤(5)所得金属氧化物包覆的单晶形貌无钴层状的镍锰正极材料SEM图;从图中可得镍锰正极材料表面均匀的包覆着包覆剂。
图3为实施例1中步骤(6)所得膜状包覆钛溶胶和金属氧化物包覆的单晶形貌无钴层状的镍锰正极材料SEM图;从图中可得材料表面经过喷雾包覆后,材料表面均匀的包覆了一层膜状的包覆剂。
图4为实施例2中步骤(3)所得类单晶形貌的无钴层状的镍锰正极材料SEM图;从图中可得材料为类单晶形貌,且一次颗粒大小较均一。
图5为实施例2中步骤(5)所得金属氧化物包覆的类单晶形貌无钴层状的镍锰正极材料SEM图;从图中可得镍锰正极材料表面均匀的包覆着包覆剂。
图6为实施例1-2包覆剂包覆后无钴层状的镍锰正极材料的包覆示意图;从图中形象的展示实施例1和实施例2中材料的双重包覆。
图7所示实施例1-2和对比例1-3所得材料XRD对比图,可以看出,所制备材料具有属于α-NaFeO2型层状结构的特征峰(003)峰,(104)峰,以及常用来表征二维层状结构的有序度的(006)峰与(102)峰以及(108)峰与(110)峰,说明所制备材料具有层状结构;其次材料中的(006)峰与(102)峰以及(108)峰与(110)峰分裂程度较好,说明材料具有有序的层状结构;再其次材料的I(003)/I(104)均大于1.2,说明材料的层状结构较完整;其中实施例1所制备材料具有最好的层状结构,其中I(003)/I(104)达到了1.40的,(006)峰与(102)峰以及(108)峰与(110)峰分裂程度明显较好,说明通过通过金属氧化物均匀包覆正极材料后再通过钛溶胶膜状包覆在材料表面方法所制备材料层状结构较好。
上面结合附图对本发明实施例作了详细说明,但是本发明不限于上述实施例,在所属技术领域普通技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下作出各种变化。此外,在不冲突的情况下,本发明的实施例及实施例中的特征可以相互组合。
Claims (10)
1.一种无钴层状的镍锰正极材料,其特征在于,所述无钴层状的镍锰正极材料的化学式为LiaNixMnyMezO2@Mb,所述Me为Zr、Al、W、Sr、Ti或Mg中的至少一种;所述M为Al2O3、CeO2、TiO2、Yb2O3、Nb2O5、La2O3、WO3、钛溶胶、铝溶胶、钛铝溶胶、异丙醇铝、钛酸丁酯、磷酸氢二铝或钨酸锂中的至少一种,其中0.9≤a≤1.10,0.50≤x≤0.70,0.50≤y≤0.30,0.001≤z≤0.009,0.001≤b≤0.005。
2.根据权利要求1所述的无钴层状的镍锰正极材料,其特征在于,所述无钴层状的镍锰正极材料的比表面积为0.4~0.9m2/g,粒度D50为3.0~5.0μm。
3.权利要求1-2任一项所述的无钴层状的镍锰正极材料的制备方法,其特征在于,包括以下步骤:
(1)将镍盐与锰盐配置成A溶液,再滴加氢氧化钠与氨水的混合液,搅拌反应,洗涤,烘干,即得镍锰氢氧化物前驱体NixMny(OH)2;
(2)将所述镍锰氢氧化物前驱体NixMny(OH)2与锂源、掺杂剂混合,进行第一次烧结,粉碎后得到无钴的镍锰正极材料LiaNixMnyMezO2;
(3)将所述无钴的镍锰正极材料LiaNixMnyMezO2与包覆剂A混合,经过第二次烧结、过筛,得到金属氧化物包覆的无钴层状的镍锰正极材料;
(4)将包覆剂B喷雾到所述金属氧化物包覆的无钴层状的镍锰正极材料表面进行湿法包覆,真空干燥,即得双重包覆的无钴层状的镍锰正极材料LiaNixMnyMezO2@Mb。
4.根据权利要求3所述的制备方法,其特征在于,步骤(1)中,所述镍盐为NiSO4、Ni(CH3COO)2、Ni(NO3)2、C2O4·Ni或NiCl2中的至少一种;步骤(1)中,所述锰盐为MnSO4、Mn(NO3)2、MnC2O4或MnCl2中的至少一种。
5.根据权利要求3所述的制备方法,其特征在于,步骤(2)中,所述锂源为LiOH·H2O、Li2CO3或CH3COOLi中的至少一种。
6.根据权利要求3所述的制备方法,其特征在于,步骤(2)中,所述掺杂剂为ZrO2、Al2O3、Al(OH)3、WO3、SrO、TiO2、Mg(OH)2或MgO2中的至少一种。
7.根据权利要求3所述的制备方法,其特征在于,步骤(2)中,所述第一次烧结的温度为450℃~980℃;第一次烧结的时间为5h-27h;步骤(3)中,所述第二次烧结的温度为250℃~600℃;第二次烧结的时间为5h-12h。
8.根据权利要求3所述的制备方法,其特征在于,步骤(3)中,所述包覆剂A为Al2O3、CeO2、TiO2、Yb2O3、Nb2O5、La2O3或WO3中的至少一种。
9.根据权利要求3所述的制备方法,其特征在于,步骤(4)中,所述包覆剂B为钛溶胶、铝溶胶、钛铝溶胶混合物、异丙醇铝、钛酸丁酯、磷酸氢二铝或钨酸锂中的至少一种。
10.一种电池,其特征在于,包括权利要求1-2任一项所述的无钴层状的镍锰正极材料。