CN104204344A - 玻璃板衬纸用木材纸浆以及玻璃板用衬纸 - Google Patents
玻璃板衬纸用木材纸浆以及玻璃板用衬纸 Download PDFInfo
- Publication number
- CN104204344A CN104204344A CN201380019065.4A CN201380019065A CN104204344A CN 104204344 A CN104204344 A CN 104204344A CN 201380019065 A CN201380019065 A CN 201380019065A CN 104204344 A CN104204344 A CN 104204344A
- Authority
- CN
- China
- Prior art keywords
- glass plate
- paper
- wood pulp
- lining paper
- plate lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及用于玻璃板衬纸的木材纸浆以及玻璃板用衬纸,其中,木材纸浆中的有机硅含量相对于纸浆的绝干质量为0.5ppm以下,玻璃板衬纸以木材纸浆为原料,纸中含有的有机硅的量相对于纸的绝干质量为0.5ppm以下。由本发明的木材纸浆形成的玻璃板用衬纸以及本发明的玻璃板用衬纸能够显著地抑制向玻璃板表面的有机硅的污染,其中玻璃板作为要求高的清洁度和损伤品级的平板显示器的基板材料使用。
Description
技术领域
本发明涉及在保管、运输堆积的多个玻璃板的过程中包装玻璃板的纸、夹入玻璃板之间的纸以及制造这些纸所使用的木材纸浆,其中玻璃板用于液晶显示器、等离子显示器、有机电致发光(有机EL)显示器等的平板显示器。
背景技术
通常,在将多个用于平板显示器的玻璃板堆叠而进行保管的过程、用卡车等运输的流通过程等中,为了防止玻璃板相互受到碰撞并接触而发生刮伤,另外,为了防止污染玻璃表面,在玻璃板之间夹入称为衬纸的纸。
由于与一般的建筑用的窗玻璃板、车辆用的窗玻璃板等相比,用于平板显示器的玻璃板是用于高分辨率显示,所以玻璃表面要保持干净的表面,尽可能没有纸表面中含有的杂质,另外,为了高速应答和视角的扩大,需要良好的平整度。
作为用于这样的用途的衬纸,作为能够防止玻璃板的破裂和表面的损伤的衬纸,也不会污染玻璃表面的衬纸,已经提出了一些这样的衬纸。例如,在专利文献1(特开2012-188785号公报)中,公开了在衬纸的表面形成氟涂层膜的方法。另外,在专利文献2(特开2010-242057号公报)中,公开了聚乙烯系树脂制造的发泡片材和聚乙烯系树脂制造的膜层压的衬纸,在专利文献3(特开2008-208478号公报)中,公开了由含有50wt%以上的漂白化学纸浆的纸浆形成的纸,其是包含特定的环氧烷加成物和水溶性的聚醚改性的有机硅的玻璃用衬纸,而在专利文献4(特开2006-44674号公报)中,公开了使用这样一种原料的玻璃板衬纸,该原料规定了纸中的树脂含量的量并且考虑了玻璃表面的污染。
发明内容
然而,通过这些衬纸并不能完全防止用于平板显示器的玻璃板的表面的污染,根据情况,存在由于某种原因污染玻璃板的表面而使玻璃板的不良率上升的实际情况。
特别是如今从盈利的观点出发,在平板显示器等的制造工艺中要求高成品率,如何防止用于平板显示器的玻璃板的表面的污染非常重要。
本发明的课题是提供面向玻璃板的能够显著地防止该玻璃的表面的污染的衬纸以及用于该衬纸的木材纸浆,其中玻璃板作为要求高的清洁度和损伤品级的平板显示器的基板材料使用。
例如,我们知道,在排列工艺(TFT液晶显示器的制造工艺的其中一个工艺)的彩色滤光片基板制作时,可能发生玻璃板表面被污染的情况、断线等的问题。虽然彩色滤光片基板是通过溅射或真空蒸镀法等在玻璃板内形成半导体膜、ITO膜(透明导电膜)、绝缘膜、铝金属膜等的薄膜来制作的,但是在玻璃板表面存在污染物之后,在由薄膜形成的电路图案中发生断线,这是由于绝缘膜的缺陷而发生短路。另外,在彩色滤光片基板的制作中,虽然通过光刻在玻璃板中形成图案,但是在该工艺中的光刻胶涂布时的玻璃板表面存在污染物之后,在曝光或显影后的光刻胶膜中产生针孔,结果发生断线或短路。在有机EL显示器的制造中也确认发生同样的问题。由于通过溅射、蒸镀或印刷等在玻璃基板中形成ITO阳极、有机发光层、阴极等的薄膜而制作有机EL显示器,所以在玻璃基板表面存在阻碍薄膜的异物之后,会产生不发光的问题。虽然弄清楚这些玻璃板的污染原因较为困难,但是通过本发明的发明人的验证,首次明确该原因是玻璃板用衬底中含有的有机硅。
因此,本发明的发明人将玻璃板用衬纸(下面也称为“玻璃板衬纸”)的制造中所使用的木材纸浆中的有机硅含量降至一定以下,从而将玻璃板用衬纸中的有机硅含量降至一定以下,能够解决上述课题,从而完成本发明。
即,本发明的第一方面涉及用于玻璃板衬纸的木材纸浆,木材纸浆中的有机硅含量相对于纸浆的绝干质量为0.5ppm以下。
优选地,木材纸浆中含有的有机硅的量相对于木材纸浆的绝干质量为0.1ppm以下。
优选地,上述有机硅为硅油。
优选地,上述硅油为二甲基聚硅氧烷。
优选地,上述玻璃板用于显示器,特别优选地,显示器为TFT液晶显示器或者有机EL显示器。
本发明的第二方面涉及玻璃板用衬纸,玻璃板用衬纸以木材纸浆为原料,纸中含有的有机硅的量相对于纸的绝干质量为0.5ppm以下。
优选地,玻璃板用衬纸中含有的有机硅的量相对于纸的绝干质量为0.1ppm以下。
优选地,上述有机硅为硅油。
优选地,上述硅油为二甲基聚硅氧烷。
优选地,上述玻璃板用于显示器,特别优选地,显示器为TFT液晶显示器或者有机EL显示器。
另外,本发明涉及由本发明的第一方面的上述木材纸浆形成的玻璃板衬纸和/或本发明的第二方面的上述玻璃板用衬纸、以及与玻璃板的堆叠物。
此外,本发明也涉及为了制造玻璃板衬纸(特别是本发明的第二方面的玻璃板衬纸)的本发明的第一方面的上述木材纸浆的用途。
由本发明的木材纸浆形成的玻璃板衬纸以及本发明的玻璃板用衬纸能够抑制甚至避免向玻璃板的有机硅转印。由此,通过抑制甚至避免向玻璃板的有机硅转印,能够防止TFT液晶显示器等的制造工艺中的彩色片等的电路断线。
具体实施方式
在将衬纸用于玻璃板时,衬纸中的有机硅存在向玻璃板转印的倾向,特别地,在玻璃板上使用由有机硅含量超过0.5ppm的木材纸浆形成的衬纸或者纸中的有机硅含量超过0.5ppm的衬纸时,向玻璃板转印的有机硅的量显著增加,结果,这次揭示了引起面板形成时的问题的原因。因此,本发明的用于玻璃板衬纸的木材纸浆是这样一种木材纸浆,木材纸浆中含有的有机硅的量相对于木材纸浆的绝干质量为0.5ppm以下。由此,由本发明的木材纸浆形成的玻璃板衬纸的有机硅含量能够在0.5ppm以下。另外,本发明的玻璃板用衬纸是由木材纸浆形成的玻璃用衬纸,纸中含有的有机硅的量相对于纸的绝干质量为0.5ppm以下。另外,本发明中的所谓“绝干”,是指通过干燥使被干燥对象中实质上不存在水分的状态,例如,“绝干”状态的物体在室温(25℃)下每小时的重量变化在1%以下,优选地在0.5%以下,更优选地在0.1%以下。
通常,木材纸浆中的含有有机硅的物质较多。这是由于在木材纸浆的制造过程(特别是清洗工艺)中产生泡沫,为了防止清洗能力低下,有机硅系消泡剂常作为消泡剂使用,来自这种有机硅系消泡剂的有机硅残存在纸浆中。例如,混合在硅油和疏水性二氧化硅的混合物中改性的有机硅、表面活性剂等来制造有机硅系消泡剂。
因此,为了使玻璃衬纸的有机硅含量在0.5ppm以下,特别重要的是作为衬纸的原料的木材纸浆不能含有过多的有机硅。在本发明的第一方面中,虽然未特定限定使作为衬纸的原料的木材纸浆中的有机硅含量降至0.5ppm以下的方法,但是优选地将非有机硅系消泡剂作为制造木材纸浆时使用的消泡剂使用。
作为非有机硅系消泡剂,例如,可以举出矿物油系消泡剂、高级醇系消泡剂、脂肪酸系消泡剂、脂肪酸酯系消泡剂、酰胺系消泡剂、胺系消泡剂、磷酸酯系消泡剂、金属皂系消泡剂、磺酸酯系消泡剂、聚醚系消泡剂和植物油系消泡剂。
例如,矿物油系消泡剂包含碳氢油等的矿物油、矿物蜡等。
例如,高级醇系消泡剂包含辛醇、十六醇等。
例如,脂肪酸系消泡剂包含棕榈酸、油酸、硬脂酸等。
例如,脂肪酸酯系消泡剂包含硬脂酸异戊酯、甘油单蓖麻酯(グリセリンモノリシノレート)、山梨醇单月桂酸酯、山梨醇三油酸酯等。
例如,酰胺系消泡剂包含丙烯酸酯多胺等。
例如,胺系消泡剂包含二烯丙基胺等。
例如,磷酸酯系消泡剂包含磷酸三丁酯、辛基磷酸钠等。
例如,金属皂系消泡剂包含硬脂酸铝、硬脂酸钙、油酸钾等。
例如,磺酸酯系消泡剂包含月桂基磺酸钠、十二烷基磺酸钠等。
例如,聚醚系消泡剂包含:(聚)氧乙烯(聚)氧丙烯加成物等的聚氧化烯类;二甘醇庚醚、聚氧乙烯油基醚、聚氧丙烯丁基醚、聚氧乙烯聚氧丙烯2-乙基己醚、碳原子数为8个以上的高级醇或碳原子数为12~14的仲醇的氧乙烯氧丙烯加成物等的(聚)氧化烯烷基醚类;聚氧丙烯基苯基醚、聚氧乙烯壬基苯基醚等的(聚)氧化烯(烷基)芳基醚类;2,4,7,9-四甲基-5-癸炔-4,7-二醇、2,5-二甲基-3-己炔-2,5-二醇、3-甲基-1-丁炔-3-醇等的炔醇与环氧烷加成聚合的乙炔醚类;二甘醇油酸酯、二乙二醇月桂酸酯、乙二醇二硬脂酸酯等的(聚)氧化烯脂肪酸酯类;聚氧乙烯山梨醇单月桂酸酯、聚氧乙烯山梨醇三油酸酯等的聚氧化烯山梨醇脂肪酸酯类;聚氧丙烯甲基醚硫酸钠、聚氧乙烯十二烷基酚醚硫酸钠等的(聚)氧化烯烷基(芳基)醚硫酸酯盐类;(聚)氧乙烯硬脂酰磷酸酯等的(聚)氧化烯烷基磷酸酯类;聚氧乙烯月桂胺等的(聚)氧化烯烷基胺类;聚氧化烯酰胺等。
例如,植物油系消泡剂包含大豆油、玉米油、椰子油、亚麻油、菜籽油、棉籽油、香油、蓖麻油等的植物油。
另外,非有机硅系消泡剂可以包含疏水性二氧化硅等的无机粒子。作为疏水性二氧化硅,优选使用疏水化处理后的二氧化硅,疏水化处理为通过用甲基等的烷基取代亲水性二氧化硅的硅醇基。
非有机硅系消泡剂也可以根据需要而包含表面活性剂等。因此,非有机硅系消泡剂也可以为乳液型。
本发明中可以使用的木材纸浆为针叶木漂白硫酸盐浆(NBKP)、阔叶木漂白硫酸盐浆(LBKP)、针叶木漂白亚硫酸盐浆(NBSP)、阔叶木漂白亚硫酸盐浆(LBSP)、热磨机械浆(TMP)等的木材纸浆或它们的混合物。以木材纸浆为主体,根据需要该木材纸浆可以与麻、竹、麦秆、洋麻、桑、三桠和木棉等的非木材纸浆、阳离子化纸浆、碱化纸浆等的改性纸浆、人造丝、维尼纶、尼龙、腈纶、涤纶等的合成纤维或化学纤维、或者微原纤化纸浆的一种或多种并用。但是,由于纸浆中含有较多树脂成分的话,会存在带来不利影响(该树脂成分污染玻璃板表面等)的可能性,所以优选单独地使用树脂成分尽可能少的化学纸浆,例如,针叶木漂白硫酸盐浆。另外,磨木纸浆这样的高收率纸浆由于含有较多树脂成分,所以不是优选的纸浆。另外,虽然使合成纤维和化学纤维混合提高了削刀性,提高了衬纸平版时的可操作性,但是由于在废弃物处理方面回收性变差,所以需要注意。
另外,在不损害本发明的性能的范围内,根据需要,可以在以上述木材纸浆为主体的造纸用纤维中添加胶粘剂、防霉剂、各种造纸用填料、湿强剂、干强剂、上浆剂、着色剂、固色剂、成品率提高剂、粘泥控制剂等,然后能够通过公知、现有的长网抄纸机、圆网抄纸机、短网抄纸机、长网与圆网组合的抄纸机等抄制而得到。另外,在添加这些化学试剂时需要小心注意,不能混入虫子或垃圾等。
在制造本发明的木材纸浆时,随着木材纸浆打浆的进行,期待增加纸层间强度的效果。然而,随着打浆的进行,木材纸浆中的微小纤维增加,作为衬纸使用时可能会出现纸屑,所以打浆度优选地不超过必要的限度。因此,在本发明中,优选的打浆度为300~650mlc.s.f.。
在本发明中,优选地,木材纸浆(进而由该木材纸浆形成的玻璃板衬纸)中含有的有机硅的量相对于木材纸浆或者衬纸的绝干质量为0.4ppm以下;更优选地,为0.3ppm以下;更优选地,为0.2ppm以下;特别优选地,为0.1ppm以下。在存在的有机硅的量超过0.1ppm的情况下,在移动终端等非常需要高分辨率显示屏的场合,以转移到玻璃中的微量有机硅为主要原因而出现的彩色片的断线处由于高清,所以较为明显,判断为品质不良的可能性较高。
使用本发明的木材纸浆,通过常用的方法能够得到玻璃板衬纸,具体地为本发明的玻璃板衬纸。在玻璃板衬纸的抄制期间和/或制造后,可以进行压光处理、超级压光处理、软压压光处理、压花等的加工。通过加工处理,能够调整表面性质和厚度。
作为本发明中的有机硅,可以举出硅油。硅油是疏水性的,硅油的分子构造可以为环状、直链状、分支状的任意形状。硅油在25℃下的运动粘度通常在0.65~100,000mm2/s的范围内,但是也可以在0.65~10,000mm2/s的范围内。
作为硅油,例如,可以举出直链状的有机聚硅氧烷、环状的有机聚硅氧烷以及分支状的有机聚硅氧烷。
作为直链状的有机聚硅氧烷、环状的有机聚硅氧烷以及分支状的有机聚硅氧烷,例如,可以举出用下述通式(1)、(2)和(3)表示的有机聚硅氧烷:
R1 3SiO—(R1 2SiO)a—SiR1 3 (1)
R1 (4-c)Si(OSiR1 3)c (3)
(式中,R1各自独立并选自示出为氢原子、羟基、或者取代或非取代的一价烃基、烷氧基的基团,
a是0~1000的整数,
b是3~100的整数,
c是1~4的整数,优选为2~4的整数。)
典型地,取代或非取代的一价烃基是:取代或非取代的碳原子数为1~30(优选地,碳原子数为1~10,更优选地,碳原子数为1~4)的一价饱和烃基;取代或非取代的碳原子数为2~30(优选地,碳原子数为2~10,更优选地,碳原子数为2~6)的一价不饱和烃基;碳原子数为6~30(更优选地,碳原子数为6~12)的一价芳香族烃基。
作为碳原子数为1~30的一价饱和烃基,例如,可以举出甲基、乙基、正丙基、异丙基、正丁基、异丁基、仲丁基、叔丁基、戊基、己基、庚基、辛基、壬基、癸基等的直链或分支状的烷基、以及环戊基、环己基、环庚基、环辛基等的环烷基。
作为碳原子数为2~30的一价不饱和烃基,例如,可以举出乙烯基、1-丙烯基、烯丙基、异丙烯基、1-丁烯基、2-丁烯基、戊烯基、己烯基等的直链或分支状的烯基;环戊烯基、环己烯基等的环烯基;环戊烯基乙基、环己烯基乙基、环己烯基丙基等的环烯基烷基;以及乙炔基、炔丙基等的炔基。
作为碳原子数为6~30的一价芳香族烃基,例如,可以举出苯基、甲苯基、二甲苯基、萘基等的芳基。优选为苯基。另外,除了仅由芳香族烃基组成的基团之外,说明书中的芳香族烃基也包括芳香族烃基与脂肪族饱和烃基合成的基团。作为芳香族烃基与饱和烃基合成的基团的实例,例如,可以举出苄基、苯乙基等的芳烷基。
上述一价烃基上的氢原子可以被一个以上的取代基取代,例如,该取代基选自由卤素原子(氟原子、氯原子、溴原子和碘原子)、包含羟基、甲醇基、环氧基、甘油基、酰基、羧基、氨基、甲基丙烯酸基、巯基、酰胺基、氧化烯基等的有机基团组成的组。具体地,可以举出3,3,3-三氟丙基、3-氯丙基、3-羟基丙基、3-(2-羟基-乙氧基)丙基、3-羧丙基、10-羧基癸基、3-异氰酸丙基等。
作为烷氧基,虽然可以举出甲氧基、乙氧基、丙氧基等,但是优选地为甲氧基或乙氧基,更优选地为甲氧基。
更具体地,作为直链状的有机聚硅氧烷,例如,为分子链两末端三甲基硅氧烷基封锁二甲基聚硅氧烷(2mPa·s或6mPa·s等的低粘度到100万mPa·s等的高粘度的二甲基有机硅)、有机氢聚硅氧烷、分子链两末端三甲基硅氧烷基封锁甲基苯基聚硅氧烷、分子链两末端三甲基硅氧烷基封锁二甲基硅氧烷·甲基苯基硅氧烷共聚物、分子链两末端三甲基硅氧烷基封锁二苯基聚硅氧烷、分子链两末端三甲基硅氧烷基封锁二甲基硅氧烷·二苯基硅氧烷共聚物、三甲基戊苯基三硅氧烷、苯基(三甲基硅氧烷基)硅氧烷、分子链两末端三甲基硅氧烷基封锁甲基烷基聚硅氧烷、分子链两末端三甲基硅氧烷基封锁二甲基聚硅氧烷·甲基烷基硅氧烷共聚物、分子链两末端三甲基硅氧烷基封锁二甲基硅氧烷·甲基(3,3,3-三氟丙基)硅氧烷共聚物、α,ω-二羟基聚二甲基硅氧烷、α,ω-二乙氧基聚二甲基硅氧烷、1,1,1,3,5,5,5-庚甲基-3-辛基三硅氧烷、1,1,1,3,5,5,5-庚甲基-3-十二烷基三硅氧烷、1,1,1,3,5,5,5-庚甲基-3-十六烷基三硅氧烷、三三甲基硅氧烷基甲基硅烷、三三甲基硅烷氧基烷基硅烷、四三甲基硅氧基硅烷、四甲基-1,3-二羟基二硅氧烷、八甲基-1,7-二羟基四硅氧烷、六甲基-1,5-二乙氧基三硅氧烷、六甲基二硅氧烷、八甲基三硅氧烷、高级烷氧基改性的有机硅、高级脂肪酸改性的有机硅、二甲基硅氧烷等。
作为环状的有机聚硅氧烷,例如,为六甲基环三硅氧烷(D3)、八甲基环四硅氧烷(D4)、十甲基环戊硅氧烷(D5)、十二甲基环己硅氧烷(D6)、1,1-二乙基六甲基环四硅氧烷、七甲基苯基环四硅氧烷、1,1-二苯基-六甲基环四硅氧烷、1,3,5,7-四乙烯基四甲基环四硅氧烷、1,3,5,7-四甲基环四硅氧烷、1,3,5,7-四环己基四甲基环四硅氧烷、三(3,3,3-三氟丙基)三甲基环三硅氧烷、1,3,5,7-四(3-甲基丙烯酰氧基)四甲基环四硅氧烷、1,3,5,7-四(3-丙基丙烯酰氧基)四甲基环四硅氧烷、1,3,5,7-四(3-羧丙基)四甲基环四硅氧烷、1,3,5,7-四(3–乙烯氧基丙基)四甲基环四硅氧烷、1,3,5,7-四(对-乙烯基苯基)四甲基环四硅氧烷、1,3,5,7-四[3-(对乙烯基苯基)丙基]四甲基环四硅氧烷、1,3,5,7-四(N-丙烯酰基-N-甲基-3-氨基丙基)四甲基环四硅氧烷、1,3,5,7-四(N,N–双(十二烷酰)-3-氨基丙基)四甲基环四硅氧烷等。
作为分支状的有机聚硅氧烷,可以举出甲基三三甲基硅氧基硅烷、乙基三三甲基硅氧基硅烷、丙基三三甲基硅氧基硅烷、丁基三甲基硅氧基硅烷、苯基三三甲基硅氧基硅烷等。
作为本发明中的硅油,优选地为二甲基聚硅氧烷、二乙基聚硅氧烷、甲基苯基聚硅氧烷、聚二甲基-聚二苯基硅氧烷共聚物、聚甲基-3,3,3-三氟丙基硅氧烷等。作为本发明中的有机硅,典型地为二甲基聚硅氧烷。
本发明中的硅油也可以为改性的硅油。作为改性的硅油,例如,可以举出聚氧化烯改性的硅油。
聚氧化烯改性的硅油是通过分子中硅-碳结合而结合聚氧化烯基的硅油,优选地为常温(具体地,25℃)下显示出水溶性的硅油,更优选地为非离子型硅油。
具体地,聚氧化烯改性的硅油例如为由直链状或分支状的硅氧烷形成的硅油与聚氧化烯的共聚物,虽然存在多种这样的物质,但是优选地为具体用下述化学式(4)表示的物质。
R2 3SiO-(R1 2SiO)d-(R1ASiO)e-SiR2 3 (4)
(式中,
R1各自独立并与上述R1相同,
R2各自独立并为R1或A,
A各自独立并为用R3G表示的基团,R3是取代或非取代的二价烃基,G表示聚氧化烯基,该聚氧化烯基通过环氧乙烷、环氧丙烷等的碳原子数为2~5的环氧烷的至少一种形成,
d表示1~500的整数,
e表示1~50的整数)。
作为取代或非取代的二价烃基,例如,可以举出碳原子数为1~30的直链状或分支状的二价烃基,具体地,可以举出亚甲基、二亚甲基、三亚甲基、四亚甲基、五亚甲基、六亚甲基、七亚甲基、八亚甲基等的碳原子数为1~30的直链状或分支链状的亚烷基;亚乙烯基、亚丙烯基、亚丁烯基、亚己烯基、亚辛烯基等的碳原子数为2~30的链烯基;亚苯基、二亚苯基等的碳原子数为6~30的亚芳基;二亚甲基亚苯基等的碳原子数为7~30的亚烷基亚芳基;以及与这些基团的碳原子结合的氢原子至少部分地被氟等的卤素原子、羟基或者包含甲醇基、环氧基、缩水甘油基、酰基、羧基、氨基、甲基丙烯酸基、巯基、酰胺基、氧化烯基等的有机基团取代的基团。二价烃基优选地为碳原子数为1~30的亚烷基,优选地为碳原子数为1~6的亚烷基,更优选地为碳原子数为3~5的亚烷基。
例如,作为聚氧化烯改性的硅油的具体实例,可以举出下述的物质。
[化2]
(式中,
x为20~160,y为1~25,x/y的值为2~50,A例如为-(CH2)3O-(CH2CH2O)m-(CH2CH2CH2O)n-R4,m为7~40,n为0~40,m+n的值至少为1,A可以通过接枝聚合,也可以通过随机聚合,R4表示氢原子或上述取代或非取代的一价烃基。适当地,m为7~30,n为0~30。)
另外,作为改性的硅油,例如,可以举出氨基烷基改性的硅油。
氨基烷基改性的硅油是通过分子中硅-碳结合而结合氨基烷基的硅油,优选地为常温(具体地,25℃)下显示出10~100000cs的粘度的硅油。
作为上述氨基烷基硅油,可以举出这样的硅油:在上述化学式(4)中,用化学式-(NR4CH2CH2)zNR4 2(式中,R4与各自独立并与上述R4相同,z是0≤z≤4的数)取代G。
从本发明的木材纸浆得到的衬纸(具体地,本发明的玻璃板衬纸)插入在玻璃板之间而被使用。例如,典型地,上述玻璃板衬纸被一张一张地插入多个玻璃板之间,作为一个整体,成为堆叠体,该堆叠体成为保管、运输的对象。另外,可以使用由本发明的木材纸浆形成的衬纸(具体地,本发明的玻璃板衬纸)包装玻璃板单体或上述堆叠体。
虽然未特定限定玻璃板,但是玻璃板优选地为用于等离子显示面板、液晶显示面板(具体地,TFT液晶显示面板)、有机EL显示面板等的平板显示器的玻璃板。在用于平板显示器的玻璃板的表面处形成有精细的电极、间隔件等,通过使用由本发明的木材纸浆形成的玻璃板衬纸(具体地,本发明的玻璃板衬纸),可以抑制甚至避免向玻璃板的有机硅的转印,所以即使在玻璃板的表面处形成精细的电极、间隔件等,也能够抑制甚至避免由有机硅带来的不便,结果,能够抑制甚至避免显示器的缺陷。
具体地,随着显示器的大型化,用于平板显示器的玻璃板的尺寸和重量也增大,但是由本发明的木材纸浆形成的玻璃板衬纸(具体地,本发明的玻璃板衬纸)能够良好地保护这样的大型甚至大重量的玻璃板的表面。具体地,由于由本发明的木材纸浆形成的玻璃板衬纸(具体地,本发明的玻璃板衬纸)含有的有机硅的量极少,所以即使受到大重量的玻璃板的推压,也可以抑制甚至避免有机硅转印到玻璃板上。因此,由本发明的木材纸浆形成的玻璃板衬纸(具体地,本发明的玻璃板衬纸)特别要求表面的清洁度,并能够适合地为用于平板显示器的玻璃板所使用。
实施例
下面虽然通过使用实施例和比较例具体地说明了本发明,但是本发明的范围不限于实施例。
(1)有机硅的定量测定
切下四边均约为1cm的衬纸,用正己烷进行约三个半小时的索氏提取。将得到的提取物在旋转蒸发仪中凝结,然后使其重新溶解在1ml氘代氯仿中,并进行1H-NMR测定。在定量时,为了制作标准曲线,将聚二甲基硅氧烷的氘代氯仿溶液作为标准品,用绝对标准法进行定量。另外,使用AVANCE500型的NMR装置(布鲁克生物自旋公司制造)。
(2)向玻璃的转印试验(运输测试)
在L形支架(铝制的并带有75度的角度)上的玻璃载置面铺上聚氨酯泡沫,从在垂直方向上载置玻璃板的载置面和载置面的后端向着靠背表面在垂直方向上延伸,玻璃板120个,玻璃板尺寸为680mm×880mm×0.7mm,在各玻璃板之间插入玻璃板衬纸,玻璃板放置为与靠背表面平行,将固定在支架上的带状的带子从后部向靠背表面搭整整一周,从而固定玻璃板。为了防止混入来自外部的尘埃或灰尘等,用包装材料覆盖上述那样设置的支架的整个表面。此后,实施用卡车运输的运输测试。运输测试条件:通过运输距离1000km(在运输途中,在40℃×95%RH的环境下保管5天)实施测试。然后,通过FT-IR分析确认玻璃板表面的有机硅的有无。
[木材纸浆的制造]
在由蒸解工艺、清洗工艺、氧脱木素反应工艺、二氧化氯和过氧化氢的多级漂白工艺组成的针叶木漂白硫酸盐浆的制造装置中,在蒸解工艺后去除结,作为去除结后的鼓式洗浆机的清洗液中使用的消泡剂,适量连续地添加矿物油系消泡剂“プロナールA5044”(东邦化学公司制造)的原液(非有机硅类的消泡剂)。另外,作为在冲压清洗的工艺中的清洗冲压中添加的消泡剂,适量地添加同样的“プロナールA5044”。如上所述,在制造工艺中使用非有机硅系消泡剂,得到针叶木漂白硫酸盐浆A。
另外,除了使用作为消泡剂的有机硅系消泡剂“SNデフォーマー551K”(サンノプコ公司制造)之外,其他与上述条件一样,得到针叶木漂白硫酸盐浆B。
[实施例1]
准备100重量份的作为木材纸浆的针叶木漂白硫酸盐浆A,使其解离并调制成打浆度为520mlc.s.f.的浆料,在该浆料中添加0.4重量份(相对于所有纸浆的重量)的作为纸张增强剂的聚丙烯酰胺(商品名:ポリストロン1250、荒川化学工业公司制造),调成浓度为0.4%的纸浆浆料。使用长网抄纸机,将纸浆浆料制成平方米重量为50g/m2的玻璃板衬纸。
[实施例2]
除了将80重量份的针叶木漂白硫酸盐浆A和20重量份的针叶木漂白硫酸盐浆B的混合物用作木材纸浆之外,其他与实施例1相同,得到平方米重量为50g/m2的玻璃板衬纸。
[比较例1]
除了使用100重量份的针叶木漂白硫酸盐浆B之外,其他与实施例1相同,得到平方米重量为50g/m2的玻璃板衬纸。
在表1中示出实施例和比较例中得到的玻璃板衬纸的有机硅含量。玻璃板衬纸的有机硅含量也表示制造该衬纸所使用的木材纸浆中的有机硅含量。
[表1]
通过运输测试确认了实施例和比较例中得到的玻璃板衬纸的向玻璃板的转印,在使用实施例1的衬纸的玻璃板的表面处完全没有检测到有机硅。虽然在使用实施例2的衬纸的玻璃板的表面处确认有一点点的有机硅,但是在使用该玻璃板的液晶面板的阵列形成时,并未观察到彩色片的断线。在使用比较例1的衬纸的玻璃板表面处确认存在有机硅的污染。在使用该玻璃板的液晶面板的阵列形成时,观察到彩色片的断线。
从以上的结果可知,由于本发明的木材纸浆中含有的有机硅的量相对于木材纸浆的绝干质量为0.5ppm以下,所以由本发明的木材纸浆形成的本发明的玻璃板衬纸也只有0.5ppm以下的有机硅含量,因此,能够防止从该玻璃板衬纸向玻璃板的有机硅的转印,结果,能够制造适合进行液晶面板的阵列形成的玻璃板。
Claims (15)
1.一种用于玻璃板衬纸的木材纸浆,所述木材纸浆中的有机硅含量相对于纸浆的绝干质量为0.5ppm以下。
2.根据权利要求1所述的用于玻璃板衬纸的木材纸浆,所述木材纸浆中的有机硅含量相对于纸浆的绝干质量为0.1ppm以下。
3.根据权利要求1或2所述的用于玻璃板衬纸的木材纸浆,其中,所述有机硅为硅油。
4.根据权利要求3所述的用于玻璃板衬纸的木材纸浆,其中,所述硅油为二甲基聚硅氧烷。
5.根据权利要求1至4中任一项所述的用于玻璃板衬纸的木材纸浆,其中,所述玻璃板用于显示器。
6.根据权利要求5所述的用于玻璃板衬纸的木材纸浆,其中,所述显示器是TFT液晶显示器或者有机EL显示器。
7.一种玻璃板衬纸,所述玻璃板衬纸由权利要求1至6中任一项所述的用于玻璃板衬纸的木材纸浆形成。
8.一种玻璃板衬纸,所述玻璃板衬纸以木材纸浆为原料,纸中含有的有机硅的量相对于纸的绝干质量为0.5ppm以下。
9.根据权利要求8所述的玻璃板衬纸,其中,纸中含有的有机硅的量相对于纸的绝干质量为0.1ppm以下。
10.根据权利要求8或9所述的玻璃板衬纸,其中,所述有机硅为硅油。
11.根据权利要求10所述的玻璃板衬纸,其中,所述硅油为二甲基聚硅氧烷。
12.根据权利要求8至11中任一项所述的玻璃板衬纸,其中,所述玻璃板用于显示器。
13.根据权利要求12所述的玻璃板衬纸,其中,所述显示器是TFT液晶显示器或者有机EL显示器。
14.一种堆叠体,所述堆叠体由权利要求7至13中任一项所述的玻璃板衬纸和玻璃板组成。
15.木材纸浆的用途,所述木材纸浆用于制造玻璃板衬纸,其中,所述木材纸浆是权利要求1至6中任一项所述的木材纸浆。