CN103842303B - 玻璃微粒沉积体以及玻璃预制件的制造方法 - Google Patents

玻璃微粒沉积体以及玻璃预制件的制造方法 Download PDF

Info

Publication number
CN103842303B
CN103842303B CN201280048193.7A CN201280048193A CN103842303B CN 103842303 B CN103842303 B CN 103842303B CN 201280048193 A CN201280048193 A CN 201280048193A CN 103842303 B CN103842303 B CN 103842303B
Authority
CN
China
Prior art keywords
glass
burner
gas
raw material
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201280048193.7A
Other languages
English (en)
Chinese (zh)
Other versions
CN103842303A (zh
Inventor
石原朋浩
古川将人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Electric Industries Ltd
Original Assignee
Sumitomo Electric Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2012008158A external-priority patent/JP5682577B2/ja
Priority claimed from JP2012008303A external-priority patent/JP5720585B2/ja
Priority claimed from JP2012012384A external-priority patent/JP5953767B2/ja
Priority claimed from JP2012175011A external-priority patent/JP5737240B2/ja
Priority claimed from JP2012175010A external-priority patent/JP5737239B2/ja
Priority claimed from JP2012175012A external-priority patent/JP5737241B2/ja
Application filed by Sumitomo Electric Industries Ltd filed Critical Sumitomo Electric Industries Ltd
Publication of CN103842303A publication Critical patent/CN103842303A/zh
Application granted granted Critical
Publication of CN103842303B publication Critical patent/CN103842303B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B37/00—Manufacture or treatment of flakes, fibres, or filaments from softened glass, minerals, or slags
    • C03B37/01—Manufacture of glass fibres or filaments
    • C03B37/012—Manufacture of preforms for drawing fibres or filaments
    • C03B37/014—Manufacture of preforms for drawing fibres or filaments made entirely or partially by chemical means, e.g. vapour phase deposition of bulk porous glass either by outside vapour deposition [OVD], or by outside vapour phase oxidation [OVPO] or by vapour axial deposition [VAD]
    • C03B37/01413—Reactant delivery systems
    • C03B37/0142—Reactant deposition burners
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B37/00—Manufacture or treatment of flakes, fibres, or filaments from softened glass, minerals, or slags
    • C03B37/01—Manufacture of glass fibres or filaments
    • C03B37/012—Manufacture of preforms for drawing fibres or filaments
    • C03B37/014—Manufacture of preforms for drawing fibres or filaments made entirely or partially by chemical means, e.g. vapour phase deposition of bulk porous glass either by outside vapour deposition [OVD], or by outside vapour phase oxidation [OVPO] or by vapour axial deposition [VAD]
    • C03B37/01413—Reactant delivery systems
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/04—Multi-nested ports
    • C03B2207/06—Concentric circular ports
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/04—Multi-nested ports
    • C03B2207/08—Recessed or protruding ports
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/20—Specific substances in specified ports, e.g. all gas flows specified
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/20—Specific substances in specified ports, e.g. all gas flows specified
    • C03B2207/22—Inert gas details
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/20—Specific substances in specified ports, e.g. all gas flows specified
    • C03B2207/24—Multiple flame type, e.g. double-concentric flame
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/80—Feeding the burner or the burner-heated deposition site
    • C03B2207/81—Constructional details of the feed line, e.g. heating, insulation, material, manifolds, filters
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y02P40/57—Improving the yield, e-g- reduction of reject rates

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Glass Melting And Manufacturing (AREA)
  • Manufacture, Treatment Of Glass Fibers (AREA)
CN201280048193.7A 2011-09-29 2012-09-28 玻璃微粒沉积体以及玻璃预制件的制造方法 Active CN103842303B (zh)

Applications Claiming Priority (25)

Application Number Priority Date Filing Date Title
JP2011214608 2011-09-29
JP2011-214608 2011-09-29
JP2011214780 2011-09-29
JP2011-214780 2011-09-29
JP2012000827 2012-01-05
JP2012-000827 2012-01-05
JP2012-008158 2012-01-18
JP2012008153 2012-01-18
JP2012008218 2012-01-18
JP2012-008153 2012-01-18
JP2012-008218 2012-01-18
JP2012008158A JP5682577B2 (ja) 2011-09-29 2012-01-18 ガラス微粒子堆積体及びガラス母材の製造方法
JP2012-008151 2012-01-18
JP2012008303A JP5720585B2 (ja) 2012-01-18 2012-01-18 ガラス母材の製造方法
JP2012-008303 2012-01-18
JP2012008151 2012-01-18
JP2012-012384 2012-01-24
JP2012012384A JP5953767B2 (ja) 2012-01-24 2012-01-24 ガラス微粒子堆積体の製造方法及びガラス母材の製造方法
JP2012-175010 2012-08-07
JP2012175011A JP5737240B2 (ja) 2012-01-05 2012-08-07 ガラス微粒子堆積体及びガラス母材の製造方法
JP2012-175012 2012-08-07
JP2012-175011 2012-08-07
JP2012175010A JP5737239B2 (ja) 2012-01-18 2012-08-07 ガラス母材の製造方法
JP2012175012A JP5737241B2 (ja) 2011-09-29 2012-08-07 ガラス微粒子堆積体及びガラス母材の製造方法
PCT/JP2012/075240 WO2013047834A1 (ja) 2011-09-29 2012-09-28 ガラス微粒子堆積体及びガラス母材の製造方法

Publications (2)

Publication Number Publication Date
CN103842303A CN103842303A (zh) 2014-06-04
CN103842303B true CN103842303B (zh) 2018-07-03

Family

ID=50804802

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201280048193.7A Active CN103842303B (zh) 2011-09-29 2012-09-28 玻璃微粒沉积体以及玻璃预制件的制造方法

Country Status (5)

Country Link
US (2) US9630872B2 (https=)
EP (1) EP2762456B1 (https=)
CN (1) CN103842303B (https=)
IN (1) IN2014CN02480A (https=)
WO (1) WO2013047834A1 (https=)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018203576A (ja) * 2017-06-06 2018-12-27 住友電気工業株式会社 ガラス微粒子堆積体の製造方法及びガラス母材の製造方法
JP6943802B2 (ja) * 2018-03-29 2021-10-06 古河電気工業株式会社 配管装置
JP6793676B2 (ja) * 2018-04-02 2020-12-02 信越化学工業株式会社 光ファイバ用多孔質ガラス母材の製造装置および製造方法
JP6694915B2 (ja) 2018-06-12 2020-05-20 株式会社フジクラ 多孔質ガラス微粒子体の製造方法および光ファイバ母材の製造方法
CN113227000B (zh) * 2018-12-04 2022-10-21 住友电气工业株式会社 玻璃微粒沉积体的制造装置以及制造方法
JP7170555B2 (ja) * 2019-02-12 2022-11-14 信越化学工業株式会社 光ファイバ用多孔質ガラス母材の製造方法
JP7487734B2 (ja) * 2019-04-03 2024-05-21 住友電気工業株式会社 ガラス母材の製造方法
US20220098084A1 (en) * 2020-05-20 2022-03-31 Corning Incorporated Methods for increasing deposition in a flame hydrolysis deposition process
CN115551812B (zh) * 2020-05-20 2024-05-03 住友电气工业株式会社 玻璃母材制造装置、玻璃母材制造方法、以及母材分布预测方法
JP7428632B2 (ja) 2020-12-14 2024-02-06 信越化学工業株式会社 多孔質ガラス母材の製造方法及び製造装置
CN113354263B (zh) * 2021-07-03 2022-08-26 神光光学集团有限公司 一种生产合成石英玻璃的方法及设备

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS596819B2 (ja) 1978-12-07 1984-02-14 小松電子金属株式会社 ド−プ石英ガラス棒の製造方法
US4220460A (en) * 1979-02-05 1980-09-02 Western Electric Company, Inc. Vapor delivery system and method
US4604118A (en) * 1985-08-13 1986-08-05 Corning Glass Works Method for synthesizing MgO--Al2 O3 --SiO2 glasses and ceramics
JPS63222034A (ja) 1987-03-11 1988-09-14 Furukawa Electric Co Ltd:The 煤状微粒子生成用バ−ナ
JPS63307137A (ja) 1987-06-05 1988-12-14 Furukawa Electric Co Ltd:The 光フアイバ用ガラス母材の製造方法
JPH02102146A (ja) 1988-10-12 1990-04-13 Sumitomo Electric Ind Ltd ガラス微粒子堆積体の製造方法
JPH02133331A (ja) 1988-11-15 1990-05-22 Sumitomo Electric Ind Ltd ガラス微粒子堆積体の製造方法
JPH0669898B2 (ja) 1989-08-08 1994-09-07 矢崎総業株式会社 光ファイバ用多孔質母材合成用トーチ
US5043002A (en) 1990-08-16 1991-08-27 Corning Incorporated Method of making fused silica by decomposing siloxanes
JPH07144927A (ja) 1993-11-24 1995-06-06 Furukawa Electric Co Ltd:The 光ファイバ母材合成用バーナ
JP3567574B2 (ja) 1995-12-26 2004-09-22 住友電気工業株式会社 多孔質ガラス母材合成用バーナ
JP3543537B2 (ja) 1996-05-09 2004-07-14 住友電気工業株式会社 ガラス微粒子合成方法及びそのための焦点型バーナ
KR20010021592A (ko) * 1997-07-08 2001-03-15 알프레드 엘. 미첼슨 실리카 유리를 제조하기 위한 게르마늄 클로라이드 및실록산 원료 및 이의 제조방법
JPH11180719A (ja) 1997-12-24 1999-07-06 Sumitomo Electric Ind Ltd 光ファイバ用ガラス母材の製造方法
JP3816268B2 (ja) 1999-06-14 2006-08-30 信越化学工業株式会社 多孔質ガラス母材の製造方法
JP4471445B2 (ja) 2000-04-06 2010-06-02 信越化学工業株式会社 多孔質ガラス母材の製造方法及びその装置
JP3705169B2 (ja) 2000-09-14 2005-10-12 住友電気工業株式会社 多孔質ガラス体の製造方法
JP4631236B2 (ja) 2001-09-05 2011-02-16 住友電気工業株式会社 ガラス母材の製造プロセスにおける原料供給方法
JP4043768B2 (ja) 2001-11-27 2008-02-06 古河電気工業株式会社 光ファイバ用母材の製造方法
JP2003252635A (ja) * 2002-03-01 2003-09-10 Fujikura Ltd 多孔質母材の製造方法および製造装置
JP2004161555A (ja) 2002-11-14 2004-06-10 Sumitomo Electric Ind Ltd ガラス形成ガスの供給方法、ガラス微粒子堆積体の製造方法及びそれぞれの装置
JP2004210548A (ja) 2002-12-26 2004-07-29 Fujikura Ltd 石英ガラスの製造方法
JP2004300006A (ja) 2003-04-01 2004-10-28 Sumitomo Electric Ind Ltd 多孔質ガラス微粒子堆積体の製造法
JP4460062B2 (ja) 2005-06-10 2010-05-12 古河電気工業株式会社 光ファイバ母材の製造方法
JP5036193B2 (ja) 2006-02-28 2012-09-26 信越化学工業株式会社 石英ガラス製バーナの火炎調整方法
JPWO2010131662A1 (ja) 2009-05-13 2012-11-01 旭硝子株式会社 ＴｉＯ２−ＳｉＯ２ガラス体の製造方法及び熱処理方法、ＴｉＯ２−ＳｉＯ２ガラス体、ＥＵＶＬ用光学基材
JP5678467B2 (ja) 2010-04-30 2015-03-04 住友電気工業株式会社 ガラス母材製造方法
JP5533205B2 (ja) 2010-04-30 2014-06-25 住友電気工業株式会社 ガラス母材製造方法
JP2012006791A (ja) 2010-06-25 2012-01-12 Sumitomo Electric Ind Ltd 光ファイバ母材の製造方法
JP5640920B2 (ja) * 2011-08-18 2014-12-17 信越化学工業株式会社 チタニアドープ石英ガラス及びその製造方法

Also Published As

Publication number Publication date
CN103842303A (zh) 2014-06-04
US20170225998A1 (en) 2017-08-10
WO2013047834A1 (ja) 2013-04-04
EP2762456A1 (en) 2014-08-06
EP2762456A4 (en) 2015-06-03
US10604439B2 (en) 2020-03-31
IN2014CN02480A (https=) 2015-06-19
US9630872B2 (en) 2017-04-25
EP2762456B1 (en) 2020-08-05
US20140305168A1 (en) 2014-10-16

Similar Documents

Publication Publication Date Title
CN103842303B (zh) 玻璃微粒沉积体以及玻璃预制件的制造方法
JP5935882B2 (ja) ガラス微粒子堆積体の製造方法およびガラス母材の製造方法
JP5880532B2 (ja) ガラス微粒子堆積体の製造方法およびガラス母材の製造方法
JP6236866B2 (ja) ガラス微粒子堆積体の製造方法およびガラス微粒子堆積体製造用バーナー
JP4043768B2 (ja) 光ファイバ用母材の製造方法
CN104649577A (zh) 一种对vad和ovd火焰温度进行在线调整的装置和方法
JPWO2020054861A1 (ja) ガラス微粒子堆積体の製造方法及びガラス母材の製造方法
WO2012008406A1 (ja) ガラス微粒子堆積体製造方法およびガラス体製造方法
JP5737241B2 (ja) ガラス微粒子堆積体及びガラス母材の製造方法
CN103708720B (zh) 光纤用多孔质玻璃沉积体的制造方法
JP5737240B2 (ja) ガラス微粒子堆積体及びガラス母材の製造方法
JP7115095B2 (ja) 光ファイバ用母材の製造方法
JP5533205B2 (ja) ガラス母材製造方法
JP7170555B2 (ja) 光ファイバ用多孔質ガラス母材の製造方法
JP5720585B2 (ja) ガラス母材の製造方法
JP5737239B2 (ja) ガラス母材の製造方法
JP5953767B2 (ja) ガラス微粒子堆積体の製造方法及びガラス母材の製造方法
JP6943802B2 (ja) 配管装置
JP6784016B2 (ja) 光ファイバ用母材の製造方法
JP5962382B2 (ja) ガラス微粒子堆積体の製造方法およびガラス母材の製造方法
JP5682577B2 (ja) ガラス微粒子堆積体及びガラス母材の製造方法
WO2019225637A1 (ja) ガラス母材の製造方法
CN103068750B (zh) 用于制造玻璃预制品的方法
JP2012076965A (ja) ガラス母材の製造方法
WO2007123163A1 (ja) 光ファイバ母材の製造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant