CN103437194B - 一种免车缝的热熔胶tpu皮革及其制备方法 - Google Patents
一种免车缝的热熔胶tpu皮革及其制备方法 Download PDFInfo
- Publication number
- CN103437194B CN103437194B CN201310359652.XA CN201310359652A CN103437194B CN 103437194 B CN103437194 B CN 103437194B CN 201310359652 A CN201310359652 A CN 201310359652A CN 103437194 B CN103437194 B CN 103437194B
- Authority
- CN
- China
- Prior art keywords
- weight portion
- hot melt
- melt adhesive
- weight
- tpu
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
性能 | TPU | PVC | 丁腈橡胶 | 氯丁橡胶 | 天然橡胶 |
硬度(邵尔) | 95 | 87 | 78 | 70 | 77 |
拉伸强度 | 28.2、25.3 | 16、14.3 | 11.6 | 10.3 | 16.3 |
伸长率/% | 700 | 309 | 400 | 400 | 574 |
Claims (10)