CN105131228A - 一种聚氨酯催化剂及其应用 - Google Patents

一种聚氨酯催化剂及其应用 Download PDF

Info

Publication number
CN105131228A
CN105131228A CN201510638162.2A CN201510638162A CN105131228A CN 105131228 A CN105131228 A CN 105131228A CN 201510638162 A CN201510638162 A CN 201510638162A CN 105131228 A CN105131228 A CN 105131228A
Authority
CN
China
Prior art keywords
sodium
catalysts
polyurethanes
potassium
polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510638162.2A
Other languages
English (en)
Inventor
阎松
张恒伟
许维相
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liaoning Shihua University
Original Assignee
Liaoning Shihua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liaoning Shihua University filed Critical Liaoning Shihua University
Priority to CN201510638162.2A priority Critical patent/CN105131228A/zh
Publication of CN105131228A publication Critical patent/CN105131228A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种聚氨酯催化剂及其应用，包括一种以上的钠盐和/或钾盐，含量为聚氨酯催化剂含量的5-10wt％；1，8-二氮杂双环-5.4.0-十一烯-7，含量为聚氨酯催化剂含量的20-60wt％；有机溶剂和稳定剂。本发明的有益效果是制备方法操作流程简单、原料价廉、反应温度低，具有易于规模化生产等优点，为制备聚氨酯材料及其工业化生产提供了参考依据。

Description

一种聚氨酯催化剂及其应用
技术领域
本发明属于聚氨酯材料合成技术领域，尤其是涉及一种聚氨酯催化剂及其应用。
背景技术
聚氨酯主要用于航空、铁路、建筑、体育等方面，可用于木制家具及金属的表面罩光，可用于贮罐、管道、冷库、啤酒、发酵罐、保鲜桶的绝热保温保冷，房屋建筑绝热防水，也可用于预制聚氨酯板材，用于制造塑料制品、耐磨合成橡胶制品、合成纤维、硬质和软质泡沫塑料制品、胶粘剂和涂料等，以及各类木器、化工设备、电讯器材和仪表及各种运输工具的表面涂饰。
聚氨酯材料是以多异氰酸酯、多元醇及其它稳定剂为原料，在一定温度下由催化剂催化反应制得的，在聚氨酯材料合成中常用的一类催化剂为金属有机化合物，这类有机金属催化剂最早为铅、汞的有机化合物，但因铅、汞均为重金属，对人体危害较大且会造成严重的环境污染，已被列为禁止使用的产品。
一种可以解决以上问题，并且具有较高催化活性的聚氨酯催化剂还有待于进一步的研究和开发。
发明内容
本发明的目的是提供一种催化活性高、绿色环保的聚氨酯催化剂及其应用，得到的聚氨酯材料物理性能好。
本发明的技术方案是：
一种聚氨酯催化剂，包括
钠盐和/或钾盐，含量为聚氨酯催化剂含量的5-10wt％；
1，8-二氮杂双环-5.4.0-十一烯-7，含量为为聚氨酯催化剂含量的20-60wt％；
有机溶剂和稳定剂。
优选的，所述钠盐为碳酸钠，碳酸氢钠，氢氧化钠、磷酸钠、硝酸钠、亚磷酸钠、醋酸钠、甲酸钠、丙酸钠、丙烯酸钠、苯甲酸钠中的一种或几种。
优选的所述钾盐为碳酸钾，碳酸氢钾，氢氧化钾、磷酸钾、硝酸钾、亚磷酸钾、醋酸钾、甲酸钾、丙酸钾、丙烯酸钾、苯甲酸钾中的一种或几种。
优选的，所述有机溶剂为烷烃。
本发明的另一方面，还包括所述的聚氨酯催化剂，在制备聚氨酯涂料、聚氨酯胶黏剂、聚氨酯弹性体、聚氨酯合成革树脂中的应用。
本发明具有的优点和积极效果是：
1、本发明制备方法操作流程简单、原料价廉、反应温度低，具有易于规模化生产等优点，为制备聚氨酯材料材料及其工业化生产提供了参考依据。
2、所述聚氨酯催化剂催化剂绿色环保、催化活性高。
具体实施方式
实施例1
本实施例提供一种聚氨酯催化剂，在室温下，将3g碳酸钠、8g1，8-二氮杂双环-5.4.0-十一烯-7、14g丙酸钾和20g异辛醇聚氧乙烯醚磷酸酯溶解于24g二乙胺中，混合均匀即得。
本实施例中所述的有机溶剂为三乙胺。
实施例2
本实施例提供一种聚氨酯催化剂，在室温下，将68g苯甲酸钠钠、70g1，8-二氮杂双环-5.4.0-十一烯-7、8g碳酸钾和20g异辛醇聚氧乙烯醚磷酸酯溶解于24g二乙胺中，混合均匀即得。
本实施例中所述的有机溶剂为二乙醚。
实施例3
本实施例提供一种聚氨酯催化剂，在室温下，将3g碳酸钠、50g1，8-二氮杂双环-5.4.0-十一烯-7、55g磷酸钾和20g异辛醇聚氧乙烯醚磷酸酯溶解于24g二乙胺中，混合均匀即得。
本实施例中所述的有机溶剂为环己烷。
以上对本发明的一个实施例进行了详细说明，但所述内容仅为本发明的较佳实施例，不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等，均应仍归属于本发明的专利涵盖范围之内。

Claims (5)

1.一种聚氨酯催化剂，其特征在于：包括
钠盐和/或钾盐，含量为聚氨酯催化剂含量的5-10wt％；
1，8-二氮杂双环-5.4.0-十一烯-7，含量为为聚氨酯催化剂含量的20-60wt％；
有机溶剂和稳定剂。
2.根据权利要求1所述的一种聚氨酯催化剂，其特征在于：所述钠盐为碳酸钠，碳酸氢钠，氢氧化钠、磷酸钠、硝酸钠、亚磷酸钠、醋酸钠、甲酸钠、丙酸钠、丙烯酸钠、苯甲酸钠中的一种或几种。
3.根据权利要求1所述的一种聚氨酯催化剂，其特征在于：所述钾盐为碳酸钾，碳酸氢钾，氢氧化钾、磷酸钾、硝酸钾、亚磷酸钾、醋酸钾、甲酸钾、丙酸钾、丙烯酸钾、苯甲酸钾中的一种或几种。
4.根据权利要求1所述的一种聚氨酯催化剂，其特征在于：所述有机溶剂为烷烃或醚类化合物或胺类化合物。
5.一种如权利要求1-4任一所述的聚氨酯催化剂，在制备聚氨酯涂料、聚氨酯胶黏剂、聚氨酯弹性体、聚氨酯合成革树脂中的应用。
CN201510638162.2A 2015-09-24 2015-09-24 一种聚氨酯催化剂及其应用 Pending CN105131228A (zh)