CN103012941B - 一种非交联无卤阻燃电缆绝缘料或护套料及制备方法 - Google Patents
一种非交联无卤阻燃电缆绝缘料或护套料及制备方法 Download PDFInfo
- Publication number
- CN103012941B CN103012941B CN201210393493.0A CN201210393493A CN103012941B CN 103012941 B CN103012941 B CN 103012941B CN 201210393493 A CN201210393493 A CN 201210393493A CN 103012941 B CN103012941 B CN 103012941B
- Authority
- CN
- China
- Prior art keywords
- parts
- free flame
- ethylene
- halogen
- retardant cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种非交联无卤阻燃电缆绝缘料或护套料，包含以下重量组份：乙烯及其共聚物和/或三元乙丙橡胶100份；相容剂0～20份；无卤阻燃剂20～250份；抗氧剂0～5份；润滑剂0～5份；聚合物弹性体0～40份；偶联剂0～3份；色母0～20份；乙烯及其共聚物选自以下材料中的一种或若干种：乙烯-醋酸乙烯共聚物、乙烯-丙烯酸甲酯共聚物、乙烯-丙烯酸乙酯共聚物等。本发明非交联无卤阻燃电缆绝缘料或护套料制成的绝缘层或护套层能够适用于-40～80℃的温度环境，而且一旦不慎发生火灾时不会产生卤化氢等有毒气体，不会因该等有毒气体造成人们生命财产的损害，而且生产成本低。
Description
技术领域
本发明涉及无卤阻燃电缆绝缘料或护套料及制备方法。
背景技术
目前，PVC电线电缆已得到广泛应用。然而，PVC电线电缆存在燃烧过程中会释放出卤化氢等有毒气体。
发明内容
本发明的目的在于提供一种环保的非交联无卤阻燃电缆绝缘料或护套料及制备方法。
为实现上述目的，本发明所提供非交联无卤阻燃电缆绝缘料或护套料，包含以下重量组份：
乙烯及其共聚物和/或三元乙丙橡胶100份；
相容剂0～20份；
无卤阻燃剂20～250份；
抗氧剂0～5份；
润滑剂0～5份；
聚合物弹性体0～40份；
偶联剂0～3份；
色母0～20份；
所述乙烯及其共聚物选自以下材料中的一种或若干种：乙烯-醋酸乙烯共聚物、乙烯-丙烯酸甲酯共聚物、乙烯-丙烯酸乙酯共聚物、乙烯-丙烯酸丁酯共聚物、聚乙烯、低密度聚乙烯、线性低密度聚乙烯、高密度聚乙烯、聚丙烯。
优选地，所述无卤阻燃剂选自氢氧化镁、氢氧化铝、碳酸钙、硼酸锌、高分子量聚磷酸铵、磷酸酯类阻燃剂、三聚氰胺氰脲酸盐或密胺焦磷酸盐中的一种或若干种。
优选地，所述相容剂选自马来酸酐共聚物改性的乙烯-乙酸乙烯酯共聚物、马来酸酐共聚物改性的乙烯-丙烯酸酯共聚物中的一种或两种。
优选地，偶联剂选自硅烷偶联剂、钛酸酯偶联剂、铝酸酯偶联剂。
本发明提供上述非交联无卤阻燃电缆绝缘料或护套料制备非交联无卤阻燃电缆绝缘层或护套层的方法，按重量份将100份乙烯及其共聚物和/或三元乙丙橡胶、0～20份相容剂、20～250份无卤阻燃剂、0～5份抗氧剂、0～5份润滑剂、0～40份聚合物弹性体、0～3份偶联剂、0～20份色母，在100℃～160℃温度条件下混炼均匀后挤出形成非交联无卤阻燃电缆料；然后在100℃～210℃温度条件下，在电缆导电线芯上熔融挤出包覆该电缆料形成绝缘层或护套层。
本发明与现有技术相比具有如下优点和效果：本发明非交联无卤阻燃电缆绝缘料或护套料制成的绝缘层或护套层能够适用于-40～80℃的温度环境，而且一旦不慎发生火灾时不会产生卤化氢等有毒气体，不会因该等有毒气体造成人们生命财产的损害，而且生产成本低。
具体实施方式
为详细说明本发明的技术内容、所实现目的及效果，以下结合实施方式详予说明。
实施例1
按重量份将100份乙烯-醋酸乙烯共聚物(EVA)、5份马来酸酐共聚物改性的乙烯-乙酸乙烯酯共聚物、100份氢氧化镁阻燃剂、2份抗氧剂1010、1份硬脂酸锌，在100℃～160℃温度下混炼均匀后挤出形成非交联无卤阻燃电缆料；然后在100℃～210℃温度条件下，在电缆导电线芯上熔融挤出包覆该电缆料形成绝缘层或护套层。
对上述线电缆进行测定，结果如下：阻燃性氧指数36，使用温度范围-40～80℃；拉伸强度≥12.8MPa；断裂伸长率≥320％；绝缘电压：6000V(绝缘厚度0.8mm)，不击穿；体积电阻率≥1014Ω.cm；环保性能符合欧盟RoHHS环保标准，不含卤素。
实施例2
按重量份将100份三元乙丙橡胶、10份马来酸酐共聚物改性的乙烯-两烯酸酯共聚物、150份高分子量聚磷酸铵阻燃剂、1份抗氧剂944、1份抗铜剂MD-1024、2份硬脂酸镁、聚烯烃弹性体20份、硅烷偶联剂KH550、1份色母，在100℃～160℃温度下混炼均匀后挤出形成非交联无卤阻燃电缆料；然后在100℃～210℃温度条件下，在电缆导电线芯上熔融挤出包覆该电缆料形成绝缘层或护套层。
对上述线电缆进行测定，结果如下：阻燃性氧指数31，使用温度范围-40～80℃；拉伸强度≥11.8MPa；断裂伸长率≥230％；绝缘电压：6000V(绝缘厚度0.8mm)，不击穿；体积电阻率≥1014Ω.cm；环保性能符合欧盟RoHS环保标准，不含卤素。
实施例3
按重量份将50份乙烯-丙烯酸甲酯共聚物、50份三元乙丙橡胶、15份马来酸酐共聚物改性的乙烯-丙烯酸酯共聚物、20份改性氢氧化镁阻燃剂、150份高分子量聚磷酸铵阻燃剂、1抗氧剂DLTP(硫代二丙酸二月桂酯)、1份抗氧剂944、2份抗铜剂MD-1024、4份硬脂酸镁、聚烯烃弹性体20份、硅烷偶联剂KH550、2份色母，在100℃～160℃温度下混炼均匀后挤出形成非交联无卤阻燃电缆料；然后在100℃～210℃温度条件下，在电缆导电线芯上熔融挤出包覆该电缆料形成绝缘层或护套层。
对上述线电缆进行测定，结果如下：阻燃性氧指数36，使用温度范围-40～80℃；拉伸强度≥16.0MPa；断裂伸长率≥335％；绝缘电压：6000V(绝缘厚度0.8mm)，不击穿；体积电阻率≥1014Ω.cm；环保性能符合欧盟RoHS环保标准，不含卤素。
综上所述，本发明非交联无卤阻燃电缆绝缘料或护套料制成的绝缘层或护套层能够适用于-40～80℃的温度环境，而且一旦不慎发生火灾时不会产生卤化氢等有毒气体，不会因该等有毒气体造成人们生命财产的损害，而且生成成本低。
本发明并不局限于上述具体实施方式，熟悉本技术领域的人员还可据此做出多种变化，但任何与本发明等同或相类似的变化都应涵盖在本发明权利要求的范围内。
Claims (1)
1.一种非交联无卤阻燃电缆绝缘料或护套料，其特征在于：所述制备材料由50份乙烯-丙烯酸甲酯共聚物、50份三元乙丙橡胶、15份马来酸酐共聚物改性的乙烯-丙烯酸酯共聚物、20份改性氢氧化镁阻燃剂、150份高分子量聚磷酸铵阻燃剂、1抗氧剂DLTP(硫代二丙酸二月桂酯)、1份抗氧剂944、2份抗铜剂MD-1024、4份硬脂酸镁、聚烯烃弹性体20份、硅烷偶联剂KH550、2份色母组成。