CN103589066A - Pp/hdpe阻燃合金塑料 - Google Patents

Pp/hdpe阻燃合金塑料 Download PDF

Info

Publication number
CN103589066A
CN103589066A CN201310561438.2A CN201310561438A CN103589066A CN 103589066 A CN103589066 A CN 103589066A CN 201310561438 A CN201310561438 A CN 201310561438A CN 103589066 A CN103589066 A CN 103589066A
Authority
CN
China
Prior art keywords
hdpe
fire retardant
parts
density polyethylene
alloy plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310561438.2A
Other languages
English (en)
Inventor
陈斌
张荣福
印玲
赵亚红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Hans Mould Shape Co Ltd
Original Assignee
Shanghai Hans Mould Shape Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Hans Mould Shape Co Ltd filed Critical Shanghai Hans Mould Shape Co Ltd
Priority to CN201310561438.2A priority Critical patent/CN103589066A/zh
Publication of CN103589066A publication Critical patent/CN103589066A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种PP/HDPE阻燃合金塑料。所述PP/HDPE阻燃合金塑料，由下述重量份组分组成：聚丙烯50份，高密度聚乙烯20-40份，三元乙丙橡胶10-30份，阻燃剂15-25份，所述阻燃剂由40-60wt%聚螺环磷酸酯二酰胺和40-60wt%氰尿酸三聚氰胺组成。本产品阻燃性较优异，可以用注塑工艺轻易加工成各种形状的汽车内饰件，如手套箱内盖板、手套箱斗、副仪表板本体、储物盒衬垫、面板储物盒。

Description

PP/HDPE阻燃合金塑料
技术领域
本发明涉及一种PP/HDPE阻燃合金塑料。
背景技术
PP，聚丙烯，CAS登录号：9003-07-0，是由丙烯聚合而制得的一种热塑性树脂。是目前所有塑料中最轻的品种之一。它对水特别稳定，在水中的吸水率仅为0.01%，成型性好。
HDPE，高密度聚乙烯，是一种结晶度高、非极性的热塑性树脂。高密度聚乙烯为无毒、无味、无臭的白色颗粒，熔点约为130℃，相对密度为0.941～0.960。它具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。介电性能，耐环境应力开裂性亦较好。熔化温度220～260℃。
三元乙丙橡胶，英文缩写为EPDM，是乙烯、丙烯以及非共轭二烯烃的三元共聚物，1963年开始商业化生产。EPDM最主要的特性就是其优越的耐氧化、抗臭氧和抗侵蚀的能力。
然而，现有的PP/HDPE合金塑料的阻燃性能并不佳。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种PP/HDPE阻燃合金塑料，具有良好的阻燃性能。
本发明的技术问题是通过如下技术方案实现的：
一种PP/HDPE阻燃合金塑料，由下述重量份组分组成：聚丙烯50份，高密度聚乙烯20-40份，三元乙丙橡胶10-30份，阻燃剂15-25份，
所述阻燃剂为聚螺环磷酸酯二酰胺和/或氰尿酸三聚氰胺，优选地，所述阻燃剂由40-60wt%聚螺环磷酸酯二酰胺和40-60wt%氰尿酸三聚氰胺组成。将聚螺环磷酸酯二酰胺和氰尿酸三聚氰胺简单搅拌混合均匀，即可制得该阻燃剂。
本发明还公开了上述PP/HDPE阻燃合金塑料的制备方法：按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述PP/HDPE阻燃合金塑料。
具体的，可以为按配比称取各组分，在高速混合机中，室温下控制转速在300-400转/分钟，混合2-8分钟，取出后转入螺杆挤出机中，在170-210℃温度下挤出造粒，即获得所述PP/HDPE阻燃合金塑料。
显然，在本发明中为提高产品的其他性能，还可以适应性地添加其他助剂，如稳定剂、抗氧剂和着色剂等。
具体的，在本发明中：
聚螺环磷酸酯二酰胺，由季戊四醇与三氯氧磷反应制得中间体螺环磷酸酯二酰氯，再以该季戊四醇磷酰氯与二乙烯三胺反应制得。在《含磷氮碳膨胀型阻燃剂的合成与性能研究》（余乐华，史铁钧，张方，等.含磷氮碳膨胀型阻燃剂的合成与性能研究[J].胶体与聚合物，2013，31（3）：109～111）中提供了该原料的具体的制备方法。
氰尿酸三聚氰胺，英文名称melamine cyanurate，CAS号：37640-57-6。
本产品阻燃性较优异，可以用注塑工艺轻易加工成各种形状的汽车内饰件，如手套箱内盖板、手套箱斗、副仪表板本体、储物盒衬垫、面板储物盒。
具体实施方式
实施例1-3
按照表1中对应实施例1-3数据称取各原料。
将各组分加入到高速混合机中，室温下控制转速在350转/分钟，混合5分钟，转入螺杆挤出机中，在190℃温度下挤出造粒，即获得所述PP/HDPE阻燃合金塑料。
表1：PP/HDPE阻燃合金塑料配方表单位：公斤
实施例1 实施例2 实施例3 对比例1
聚丙烯 50 50 50 50
高密度聚乙烯 30 30 30 30
三元乙丙橡胶 20 20 20 20
聚螺环磷酸酯二酰胺 20 / 10 /
氰尿酸三聚氰胺 / 20 10 /
表1中，聚丙烯为中石化广州石化分公司生产的牌号J641共聚PP树脂。高密度聚乙烯为台湾塑胶公司牌号7200F的HDPE树脂。三元乙丙橡胶为美国陶氏EPDM5565的EPDM树脂。
对比例1
按照表1中对应的对比例1数据称取各组分，采用实施例1所述方法，即获得所述PP/HDPE阻燃合金塑料。
测试例
对实施例1～3和对比例1的PP/HDPE阻燃合金塑料性能进行测试。
表2：PP/HDPE阻燃合金塑料性能测试表
UL-94阻燃等级，（1.6mm） LOI，%
实施例1 V0 27.4
实施例2 V0 25.7
实施例3 V0 28.6
对比例1 V1 20.2
由测试数据可以明显的得出，聚螺环磷酸酯二酰胺和氰尿酸三聚氰胺复配使用，相对于阻燃剂单独使用，阻燃效果协同增效。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (1)

1.一种PP/HDPE阻燃合金塑料，其特征在于，由下述重量份组分组成：聚丙烯50份，高密度聚乙烯20-40份，三元乙丙橡胶10-30份，阻燃剂15-25份，
所述阻燃剂为聚螺环磷酸酯二酰胺和/或氰尿酸三聚氰胺，优选地，所述阻燃剂由40-60wt%聚螺环磷酸酯二酰胺和40-60wt%氰尿酸三聚氰胺组成。
CN201310561438.2A 2013-11-12 2013-11-12 Pp/hdpe阻燃合金塑料 Pending CN103589066A (zh)