CN103483762B - 汽车内饰件用阻燃pc/abs塑料合金 - Google Patents
汽车内饰件用阻燃pc/abs塑料合金 Download PDFInfo
- Publication number
- CN103483762B CN103483762B CN201310460914.1A CN201310460914A CN103483762B CN 103483762 B CN103483762 B CN 103483762B CN 201310460914 A CN201310460914 A CN 201310460914A CN 103483762 B CN103483762 B CN 103483762B
- Authority
- CN
- China
- Prior art keywords
- abs
- plastic alloy
- inflaming retarding
- automotive interior
- interior part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了汽车内饰件用阻燃PC/ABS塑料合金,包括50重量份ABS树脂,45-55重量份PC树脂,0.5-1.5重量份聚四氟乙烯和30-50重量份的复合阻燃剂,所述复合阻燃剂包括无卤膨胀型阻燃剂。本发明的汽车内饰件用阻燃PC/ABS塑料合金具有较好的阻燃性,适合于注塑成各种汽车内饰件。
Description
技术领域
本发明涉及一种塑料合金,尤其涉及汽车内饰件用阻燃PC/ABS塑料合金。
背景技术
PC/ABS合金,是聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物的混合物,是由聚碳酸酯PC和丙烯腈-苯乙烯-丁二烯共聚物ABS合金而成的热可塑性塑胶,结合了两种材料的优异特性,ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线UV等性质,可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。典型应用范围为手机外壳、计算机和商业机器壳体、电器设备、草坪园艺机器、汽车零件仪表板、内部装修以及车轮盖。
然而,目前的PC/ABS合金阻燃性能并不佳。
发明内容
针对现有技术中存在的上述不足,本发明所要解决的技术问题是提供一种汽车内饰件用阻燃PC/ABS塑料合金,具有良好的阻燃性能。
本发明所要解决的技术问题是通过如下技术方案实现的:
汽车内饰件用阻燃ABS塑料,包括50重量份ABS树脂,45-55重量份PC树脂,0.5-1.5重量份聚四氟乙烯和30-50重量份的复合阻燃剂,所述复合阻燃剂包括无卤膨胀型阻燃剂。
优选地,
所述无卤膨胀型阻燃剂为聚螺环磷酸酯二酰胺。
所述复合阻燃剂由30-70wt%聚螺环磷酸酯二酰胺和30-70wt%氰尿酸三聚氰胺组成。
将聚螺环磷酸酯二酰胺和氰尿酸三聚氰胺简单搅拌混合均匀,即可制得该复合阻燃剂。
本发明的汽车内饰件用阻燃ABS塑料可以采用本行业通用的方法进行制备,显然本发明的创新之处并不在于制备方法,而仅在于原料的选择,特别是阻燃剂的选择。可以采用下述方法进行制备:按配比称取各组分,混合均匀后,熔融混炼、挤出造粒,即获得所述汽车内饰件用阻燃PC/ABS合金。
具体的,可以为按配比称取各组分,在高速混合机中,室温下控制转速在300-400转/分钟,混合5-10分钟,取出后转入螺杆挤出机中,在240-260℃温度下挤出造粒,即获得所述汽车内饰件用阻燃PC/ABS合金。
显然,在本发明中为提高产品的其他性能,还可以适应性地添加其他助剂,如光稳定剂、抗氧剂、着色剂和抗静电剂等。
具体的,在本发明中:
所述聚螺环磷酸酯二酰胺,由季戊四醇与三氯氧磷反应制得中间体螺环磷酸酯二酰氯,再以该季戊四醇磷酰氯与二乙烯三胺反应制得。在《含磷氮碳膨胀型阻燃剂的合成与性能研究》(余乐华,史铁钧,张方,等.含磷氮碳膨胀型阻燃剂的合成与性能研究[J].胶体与聚合物,2013,31(3):109~111)中提供了该制备方法。
氰尿酸三聚氰胺,英文名称melamine cyanurate,CAS号:37640-57-6。
本发明的汽车内饰件用阻燃PC/ABS塑料合金具有较好的阻燃性,适合于注塑成各种汽车内饰件。
具体实施方式
下面结合实施例对本发明作进一步描述。
ABS树脂选用吉林石化公司的通用级ABS9815F树脂。
PC树脂选用日本帝人公司的L-1250YPC树脂。
实施例1
按照表1中对应的实施例1数据称取各组分,将各组分加入到高速混合机中,室温下控制转速在350转/分钟,混合10分钟,取出后转入螺杆挤出机中,在180℃温度下挤出造粒,即获得所述汽车内饰件用阻燃PC/ABS塑料合金。
表1:汽车内饰件用阻燃PC/ABS塑料合金配方表单位:公斤
实施例1 | 实施例2 | 对比例1 | |
ABS树脂 | 50 | 50 | 50 |
PC树脂 | 50 | 50 | 50 |
聚四氟乙烯 | 1 | 1 | 1 |
聚螺环磷酸酯二酰胺 | 20 | 40 | / |
氰尿酸三聚氰胺 | 20 | / | 40 |
实施例2
按照表1中对应的实施例2数据称取各组分,采用实施例1所述方法,即获得所述汽车内饰件用阻燃PC/ABS塑料合金。
对比例1
按照表1中对应的对比例1数据称取各组分,采用实施例1所述方法,即获得所述汽车内饰件用阻燃PC/ABS塑料合金。
测试例1
对实施例1-2及对比例1进行测试,具体数据见表2。
表2:汽车内饰件用阻燃PC/ABS塑料合金阻燃性能测试表
UL-94阻燃等级,(1.6mm) | LOI,% | |
实施例1 | V0 | 29.4 |
实施例2 | V0 | 27.2 |
对比例1 | V1 | 26.8 |
由上表测试数据可以明显得出,相对于现有技术(对比例1),本发明(实施例1和实施例2)具有较好的阻燃性能。
实施例1中聚螺环磷酸酯二酰胺和氰尿酸三聚氰胺阻燃剂复配使用,相对于实施例2和对比例1的阻燃剂单独使用,阻燃效果协同增效。
Claims (1)
1.汽车内饰件用阻燃PC/ABS塑料,包括50重量份ABS树脂,45-55重量份PC树脂,0.5-1.5重量份聚四氟乙烯和30-50重量份的复合阻燃剂,其特征在于:所述复合阻燃剂由30-70wt%聚螺环磷酸酯二酰胺和30-70wt%氰尿酸三聚氰胺组成。