CN104829946A - 抗静电pp塑料 - Google Patents

抗静电pp塑料 Download PDF

Info

Publication number
CN104829946A
CN104829946A CN201510271615.2A CN201510271615A CN104829946A CN 104829946 A CN104829946 A CN 104829946A CN 201510271615 A CN201510271615 A CN 201510271615A CN 104829946 A CN104829946 A CN 104829946A
Authority
CN
China
Prior art keywords
antistatic
plastic
parts
static
plastics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510271615.2A
Other languages
English (en)
Inventor
袁峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Original Assignee
Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd filed Critical Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority to CN201510271615.2A priority Critical patent/CN104829946A/zh
Publication of CN104829946A publication Critical patent/CN104829946A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种抗静电PP塑料。所述一种抗静电PP塑料，包括下述重量份原料：PP树脂80份；三元乙丙橡胶5-15份；碳酸钙5-15份；3-氨丙基三乙氧基硅烷0.1-0.3份；(3-月桂酰胺丙基)三甲基硫酸甲酯铵0.5-1.5份；月桂酸二乙醇酰胺0.2-0.6份；N,N-二(2-羟乙基)-十四酰胺0.2-0.6份。本发明的抗静电PP塑料的抗静电性较优异，表面不易吸附灰尘，同时拉升强度、弯曲强度、弯曲模量和冲击强度均较高，可用注塑工艺制成各种汽车内饰件。

Description

抗静电PP塑料
技术领域
本发明涉及一种PP塑料，尤其涉及一种抗静电PP塑料。
背景技术
通用塑料一般是指产量大、用途广、成型性好、价格便宜的塑料。通用塑颗粒料有五大品种，即聚乙烯(PE)、聚丙烯(PP)、聚氯乙烯(PVC)、聚苯乙烯(PS)及丙烯腈─丁二烯─苯乙烯共聚合物(ABS)。
聚丙烯，是由丙烯聚合而制得的一种热塑性树脂，简称PP。聚丙烯具有良好的耐热性，制品能在100℃以上温度进行消毒灭菌，在不受外力的条件下，150℃也不变形。聚丙烯的化学稳定性很好，除能被浓硫酸、浓硝酸侵蚀外，对其它各种化学试剂都比较稳定，聚丙烯适合制作各种化工管道和配件，防腐蚀效果良好。聚丙烯有较高的介电系数，且随温度的上升，可以用来制作受热的电器绝缘制品。它的击穿电压也很高，适合用作电器配件等。抗电压、耐电弧性好。
但，通常PP塑料的抗静电效果并不理想。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种抗静电PP塑料。
本发明所要解决的技术问题是通过如下技术方案实现的：
一种抗静电PP塑料，包括下述重量份原料：
优选地，一种抗静电PP塑料，包括下述重量份原料：
本发明的抗静电PP塑料，可以采用本领域的常规方法进行制备，如按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述抗静电PP塑料。
具体的，可以为按配比称取各组分，在高速混合机中，室温下控制转速在300-400转/分钟，混合2-8分钟，200-220℃温度下经双螺杆挤出机挤出造粒，即获得所述抗静电PP塑料。
本发明的抗静电PP塑料的抗静电性较优异，表面不易吸附灰尘，同时拉升强度、弯曲强度、弯曲模量和冲击强度均较高，可用注塑工艺制成各种汽车内饰件。
具体实施方式
下面结合实施例对本发明作进一步描述。
下述实施例中，各原料介绍：
聚丙烯PP为上海石化公司牌号M500R的聚丙烯。
三元乙丙橡胶选用日本三井公司牌号为4095的EPDM树脂。
碳酸钙，纳米级，300目，长兴龙峰粉体材料有限公司生产。
3-氨丙基三乙氧基硅烷，硅烷偶联剂KH 550，CAS号：919-30-2。(3-月桂酰胺丙基)三甲基硫酸甲酯铵，又称抗静电剂LS，英文名：(3-lauramidopropyl)trimethyl ammonium methyl sulfate。
月桂酸二乙醇酰胺，CAS号：120-40-1。
N,N-二(2-羟乙基)-十四酰胺，CAS号：7545-23-5。
实施例1-4
按照表1中对应实施例1-4数据称取各原料。
在高速混合机中，室温下控制高速混合机转速在350转/分钟，混合5分钟，取出后转入双螺杆挤出机中，在210℃温度下挤出造粒，螺杆机转速控制在400转/分钟，即获得所述抗静电PP塑料。
表1：抗静电PP塑料配方表(单位：公斤)
原料 实施例1 实施例2 实施例3 实施例4
PP树脂 80 80 80 80
三元乙丙橡胶 10 10 10 10
碳酸钙 10 10 10 10
3-氨丙基三乙氧基硅烷 0.2 0.2 0.2 0.2
(3-月桂酰胺丙基)三甲基硫酸甲酯铵 1 1 1 1
月桂酸二乙醇酰胺 - 0.6 - 0.3
N,N-二(2-羟乙基)-十四酰胺 - - 0.6 0.3
测试例
对实施例1-4的抗静电PP塑料防静电性能进行测试，按照大众汽车Antistatic property acc.to PV3977进行，时间120s，温度23℃。各测试20次，剔除异常值，再取平均值。
表2：抗静电PP塑料防静电性能测试表
90℃/500h老化后
实施例1 0.45KV
实施例2 0.28KV
实施例3 0.26KV
实施例4 0.16KV
标准：≤0.3KV after 120S。
发明人通过大量实验得出，将抗静电剂(3-月桂酰胺丙基)三甲基硫酸甲酯铵、月桂酸二乙醇酰胺和N,N-二(2-羟乙基)-十四酰胺三者复配，抗静电效果明显，具有协同抗静电效果。
对实施例1-4的抗静电PP塑料表面电阻率进行测试，按照GB/T1410-2006进行。
表3：抗静电PP塑料抗静电性能测试表
表面电阻率/Ω
实施例1 2.2×106
实施例2 1.4×106
实施例3 1.3×106
实施例4 0.8×106
表4：实施例4抗静电PP塑料材料性能测试表
拉伸强度/Mpa 冲击强度/KJ/m2 弯曲强度/Mpa 弯曲模量/Mpa
16.5 1.9 21.4 995

Claims (2)

1.一种抗静电PP塑料，包括下述重量份原料：
2.一种抗静电PP塑料，包括下述重量份原料：
CN201510271615.2A 2015-05-25 2015-05-25 抗静电pp塑料 Withdrawn CN104829946A (zh)