WO2014125770A1 - Acier de décolletage contenant du plomb - Google Patents

Acier de décolletage contenant du plomb Download PDF

Info

Publication number
WO2014125770A1
WO2014125770A1 PCT/JP2014/000317 JP2014000317W WO2014125770A1 WO 2014125770 A1 WO2014125770 A1 WO 2014125770A1 JP 2014000317 W JP2014000317 W JP 2014000317W WO 2014125770 A1 WO2014125770 A1 WO 2014125770A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel
cutting
inclusions
fine
content
Prior art date
Application number
PCT/JP2014/000317
Other languages
English (en)
Japanese (ja)
Inventor
橋村　雅之
宏二 渡里
Original Assignee
新日鐵住金株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 新日鐵住金株式会社 filed Critical 新日鐵住金株式会社
Priority to JP2015500126A priority Critical patent/JP5954483B2/ja
Priority to KR1020157018484A priority patent/KR101685863B1/ko
Priority to CN201480009269.4A priority patent/CN104995324B/zh
Publication of WO2014125770A1 publication Critical patent/WO2014125770A1/fr

Abstract

L'invention porte sur un acier de décolletage contenant du plomb ayant une excellente usinabilité. Cet acier de décolletage contenant du plomb contient, en termes de % en masse, 0,005-0,2 % de C, 0,3-2,0 % de Mn, 0,005-0,2 % de P, 0,01-0,7 % de S, 0,03-0,5 % de Pb, 0,004-0,02 % de N et 0,003-0,03 % de O, le reste comprenant du Fe et des impuretés. L'acier contient des inclusions de Pb (40) ayant un diamètre de 0,01-0,5 μm en termes de diamètre de cercle équivalent, le nombre des inclusions étant supérieur ou égal à 10 000 par mm2.
PCT/JP2014/000317 2013-02-18 2014-01-23 Acier de décolletage contenant du plomb WO2014125770A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2015500126A JP5954483B2 (ja) 2013-02-18 2014-01-23 鉛快削鋼
KR1020157018484A KR101685863B1 (ko) 2013-02-18 2014-01-23 납 쾌삭강
CN201480009269.4A CN104995324B (zh) 2013-02-18 2014-01-23 含铅易切削钢

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013029261 2013-02-18
JP2013-029261 2013-02-18

Publications (1)

Publication Number Publication Date
WO2014125770A1 true WO2014125770A1 (fr) 2014-08-21

Family

ID=51353787

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/000317 WO2014125770A1 (fr) 2013-02-18 2014-01-23 Acier de décolletage contenant du plomb

Country Status (5)

Country Link
JP (1) JP5954483B2 (fr)
KR (1) KR101685863B1 (fr)
CN (1) CN104995324B (fr)
TW (1) TWI510650B (fr)
WO (1) WO2014125770A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016199843A1 (fr) * 2015-06-10 2016-12-15 新日鐵住金株式会社 Acier de décolletage
JPWO2018021452A1 (ja) * 2016-07-27 2019-05-30 日本製鉄株式会社 機械構造用鋼
WO2021132371A1 (fr) * 2019-12-23 2021-07-01 Ｊｆｅスチール株式会社 Acier de décolletage et son procédé de fabrication

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018159617A1 (fr) 2017-02-28 2018-09-07 Ｊｆｅスチール株式会社 Tige de fil destinée à couper
TWI717990B (zh) * 2019-12-23 2021-02-01 日商杰富意鋼鐵股份有限公司 快削鋼及其製造方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4203763A (en) * 1977-12-21 1980-05-20 Scandinavian Lancers Aktiebolag Method of manufacturing a lead alloy steel and a steel made according to the method
JPS5585658A (en) * 1978-12-25 1980-06-27 Daido Steel Co Ltd Free cutting steel
JPS6223970A (ja) * 1985-07-24 1987-01-31 Nippon Steel Corp 連続鋳造による低炭素硫黄−鉛快削鋼
EP1054074A2 (fr) * 1999-05-21 2000-11-22 POHANG IRON & STEEL CO., LTD. Acier de decolletage contenant du bismuth et du soufre et présentant de ductilité excellent à haut température, et son procédé de fabrication
JP2005307241A (ja) * 2004-04-19 2005-11-04 Daido Steel Co Ltd 高硫黄快削鋼
WO2008066194A1 (fr) * 2006-11-28 2008-06-05 Nippon Steel Corporation Acier de décolletage avec une excellente aptitude à la fabrication
JP2009120955A (ja) * 2008-12-19 2009-06-04 Nippon Steel Corp 被削性に優れる鋼およびその製造方法

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4806304A (en) * 1983-05-09 1989-02-21 Daido Tokushuko Kabushiki Kaisha Free cutting steel
JP3437079B2 (ja) 1998-02-05 2003-08-18 株式会社神戸製鋼所 切りくず処理性に優れた機械構造用鋼
JP2000119801A (ja) * 1998-08-11 2000-04-25 Kobe Steel Ltd 被削性に優れた黒鉛鋼
JP2000319753A (ja) * 1999-04-30 2000-11-21 Daido Steel Co Ltd 低炭素硫黄系快削鋼
KR100740414B1 (ko) * 2000-03-24 2007-07-16 제이에프이 스틸 가부시키가이샤 재질 이방성이 작고 강도, 인성 및 피삭성이 우수한비조질 강 및 그의 제조 방법
JP4264329B2 (ja) 2002-11-15 2009-05-13 新日本製鐵株式会社 被削性に優れる鋼
JP4348163B2 (ja) 2002-11-15 2009-10-21 新日本製鐵株式会社 被削性に優れる鋼及びその製造方法
JP4323778B2 (ja) * 2002-11-15 2009-09-02 新日本製鐵株式会社 被削性に優れる鋼の製造方法
JP4264247B2 (ja) * 2002-11-15 2009-05-13 新日本製鐵株式会社 被削性に優れる鋼およびその製造方法
JP2005273000A (ja) * 2004-02-26 2005-10-06 Sanyo Special Steel Co Ltd 被削性に優れた機械構造用鋼

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4203763A (en) * 1977-12-21 1980-05-20 Scandinavian Lancers Aktiebolag Method of manufacturing a lead alloy steel and a steel made according to the method
JPS5585658A (en) * 1978-12-25 1980-06-27 Daido Steel Co Ltd Free cutting steel
JPS6223970A (ja) * 1985-07-24 1987-01-31 Nippon Steel Corp 連続鋳造による低炭素硫黄−鉛快削鋼
EP1054074A2 (fr) * 1999-05-21 2000-11-22 POHANG IRON & STEEL CO., LTD. Acier de decolletage contenant du bismuth et du soufre et présentant de ductilité excellent à haut température, et son procédé de fabrication
JP2005307241A (ja) * 2004-04-19 2005-11-04 Daido Steel Co Ltd 高硫黄快削鋼
WO2008066194A1 (fr) * 2006-11-28 2008-06-05 Nippon Steel Corporation Acier de décolletage avec une excellente aptitude à la fabrication
JP2009120955A (ja) * 2008-12-19 2009-06-04 Nippon Steel Corp 被削性に優れる鋼およびその製造方法

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016199843A1 (fr) * 2015-06-10 2016-12-15 新日鐵住金株式会社 Acier de décolletage
JPWO2016199843A1 (ja) * 2015-06-10 2018-04-12 新日鐵住金株式会社 快削鋼
EP3309272A4 (fr) * 2015-06-10 2018-10-24 Nippon Steel & Sumitomo Metal Corporation Acier de décolletage
JPWO2018021452A1 (ja) * 2016-07-27 2019-05-30 日本製鉄株式会社 機械構造用鋼
EP3492615A4 (fr) * 2016-07-27 2019-12-25 Nippon Steel Corporation Acier pour structures de machines
WO2021132371A1 (fr) * 2019-12-23 2021-07-01 Ｊｆｅスチール株式会社 Acier de décolletage et son procédé de fabrication
JP6927444B1 (ja) * 2019-12-23 2021-09-01 Ｊｆｅスチール株式会社 快削鋼およびその製造方法
KR20220099571A (ko) * 2019-12-23 2022-07-13 제이에프이 스틸 가부시키가이샤 쾌삭강 및 그의 제조 방법
CN114829650A (zh) * 2019-12-23 2022-07-29 杰富意钢铁株式会社 易切削钢及其制造方法
CN114829650B (zh) * 2019-12-23 2023-06-02 杰富意钢铁株式会社 易切削钢及其制造方法
KR102705357B1 (ko) 2019-12-23 2024-09-09 제이에프이 스틸 가부시키가이샤 쾌삭강 및 그의 제조 방법

Also Published As

Publication number Publication date
CN104995324A (zh) 2015-10-21
CN104995324B (zh) 2016-08-24
JP5954483B2 (ja) 2016-07-20
TWI510650B (zh) 2015-12-01
JPWO2014125770A1 (ja) 2017-02-02
TW201437390A (zh) 2014-10-01
KR20150092321A (ko) 2015-08-12
KR101685863B1 (ko) 2016-12-12

Similar Documents

Publication Publication Date Title
JP4424503B2 (ja) 棒鋼・線材
JP5954483B2 (ja) 鉛快削鋼
JP7417091B2 (ja) 鋼材
JP5368830B2 (ja) 機械構造用鋼およびその製造方法ならびに機械構造用部品
JP2010070812A (ja) 冷間鍛造性に優れるオーステナイト系ステンレス快削鋼線材とその製造方法
JP5092578B2 (ja) 低炭素硫黄快削鋼
JP2007239015A (ja) 低炭素硫黄快削鋼材
KR101685864B1 (ko) 납 쾌삭강
JP2017193767A (ja) 冷間鍛造用鋼およびその製造方法
TWI609092B (zh) Quick cut steel
JP6055400B2 (ja) 鋼材およびその製造方法
WO2017068935A1 (fr) Acier pour forgeage à chaud, et article forgé à chaud
JP2018035423A (ja) 浸炭用鋼、浸炭鋼部品及び浸炭鋼部品の製造方法
JP2004176175A (ja) 被削性に優れる鋼及びその製造方法
JP2018035420A (ja) 浸炭用鋼、浸炭鋼部品及び浸炭鋼部品の製造方法
JP2005307241A (ja) 高硫黄快削鋼
JP2009120955A (ja) 被削性に優れる鋼およびその製造方法
JP2017115190A (ja) 熱間圧延棒線材
JP7024921B1 (ja) 快削鋼およびその製造方法
JP7024922B1 (ja) 快削鋼およびその製造方法
WO2024019013A1 (fr) Matériau en acier
JP2024031698A (ja) 鋼材
WO2022107757A1 (fr) Matériau de barre en acier inoxydable et composant électromagnétique
JP2006167726A (ja) 耐摩耗性および耐熱亀裂性に優れる圧延ロール用外層材およびそれを用いた圧延ロール
JP2018035411A (ja) 冷間鍛造用鋼およびその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14751743

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015500126

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20157018484

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14751743

Country of ref document: EP

Kind code of ref document: A1