WO2014010680A1 - フェライト系ステンレス鋼板および酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法 - Google Patents

フェライト系ステンレス鋼板および酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法 Download PDF

Info

Publication number
WO2014010680A1
WO2014010680A1 PCT/JP2013/069004 JP2013069004W WO2014010680A1 WO 2014010680 A1 WO2014010680 A1 WO 2014010680A1 JP 2013069004 W JP2013069004 W JP 2013069004W WO 2014010680 A1 WO2014010680 A1 WO 2014010680A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
stainless steel
ferritic stainless
steel sheet
oxide film
Prior art date
Application number
PCT/JP2013/069004
Other languages
English (en)
French (fr)
Inventor
秦野　正治
修 池上
Original Assignee
新日鐵住金ステンレス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=49916121&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2014010680(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 新日鐵住金ステンレス株式会社 filed Critical 新日鐵住金ステンレス株式会社
Priority to CN201380033470.1A priority Critical patent/CN104379790B/zh
Priority to EP13816357.1A priority patent/EP2871251B1/en
Publication of WO2014010680A1 publication Critical patent/WO2014010680A1/ja

Abstract

　このフェライト系ステンレス鋼板は、質量％にて、Ｃ：０．０２％以下、Ｓｉ：０．１５％以下、Ｍｎ：０．３～１％、Ｐ：０．０４％以下、Ｓ：０．００３％以下、Ｃｒ：２０～２５％、Ｍｏ：０．５～２％、Ａｌ：０．１％以下、Ｎ：０．０２％以下、Ｎｂ：０．００１～０．５％、残部がＦｅおよび不可避的不純物からなり、かつ（１）式を満たすことを特徴とする。　２．５＜Ｍｎ／（Ｓｉ＋Ａｌ）＜８．０　・・・（１）　ただし、（１）式でＭｎ、Ｓｉ、Ａｌはそれぞれの元素の含有量（質量％）を意味する。

Description

フェライト系ステンレス鋼板および酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法
　本発明は、高温で良好な電気伝導性を有する酸化皮膜を形成するとともに，長期使用においても優れた皮膜密着性を兼備したフェライト系ステンレス鋼板に関する。本発明は，特に、固体酸化物型燃料電池のセパレーターおよびその周辺の高温部材に適する。
　本出願は、２０１２年７月１３日に日本に出願された特願２０１２－１５７５４０号と、２０１３年６月２０日に日本に出願された特願２０１３－１２９６９２号とを基礎出願とし、その内容を取り込むものとする。
　近年、石油を代表とする化石燃料の枯渇化、ＣＯ2排出による地球温暖化現象等の問題から、従来の発電システムに替わる新しいシステムの実用化が求められている。その１つとして、分散電源，自動車の動力源としても実用的価値が高い「燃料電池」が注目されている。燃料電池にはいくつかの種類がある。燃料電池の中でも固体酸化物型燃料電池（ＳＯＦＣ）は、エネルギー効率が高く、将来の普及拡大が有望視されている。
　固体酸化物型燃料電池の作動温度は、近年、固体電解質膜の改良により６００～９００℃で作動するＳＯＦＣシステムが主流となっている。この温度域で作動する固体酸化物型燃料電池の材料として、高価で加工性の悪いセラミックスから、安価で加工性の良好な金属材料の適用が検討されている。
　金属材料に求められる特性は、先ず、６００～９００℃の温度域で優れた「耐酸化性」を有していることである。次に、セラミックス系の固体酸化物と同等の「熱膨張係数」を有することである。これらの基本的特性に加えて、高温での発電時にセラミックス系固体酸化物と密着した状態において良好な「電気伝導性」を呈することである。ただし、普及拡大の視点からは、安価で高温・長期使用において酸化皮膜の剥離を抑制して電気伝導性を損なわない耐久性に優れた金属材料の適用が課題となっている。
　高温での耐酸化性に優れる金属材料としては、例えば，ＪＩＳ　Ｇ　４３０５に規定するＳＵＳ３０９Ｓ，ＳＵＳ３１０Ｓがある。しかし、これら高Ｃｒ高Ｎｉタイプのオーステナイト系ステンレス鋼は熱膨張係数が大きい。このため、起動・停止が行われる状況下では熱膨張・熱収縮の繰り返しにより熱変形やスケール剥離が発生し、使用できない。一方、フェライト系ステンレス鋼の熱膨張係数はセラミックス系固体酸化物と同程度である。このため、耐酸化性，電気伝導性の要件を兼ね備えていれば最適な候補材料となる。
　従来、特許文献１～３において、上述した耐酸化性と電気伝導性を兼備したフェライト系ステンレス鋼が開示されている。特許文献１～３には、（Ｙ，ＲＥＭ（希土類元素），Ｚｒ）のグル－プから選ばれる１種または２種以上を含むことを特徴とする高Ｃｒタイプのフェライト系ステンレス鋼が開示されている。これら文献記載の発明は、鋼表面にＣｒ系酸化皮膜を形成させ，（Ｙ，ＲＥＭ，Ｚｒ）の添加によりＣｒ系酸化皮膜の耐酸化性と電気伝導性を改善する技術思想に基づいている。
　他方、希土類元素の添加に頼らず、耐酸化性を損なわず電気伝導性を付与したフェライト系ステンレス鋼が開示されている。特許文献４に記載のものは、鋼表面にＣｒ系酸化皮膜を形成させ，（Ｙ，ＲＥＭ，Ｚｒ）等の希土類元素を必須とせず，導電性の高いＣｕの添加により耐酸化性を損なわず電気伝導度を高める技術思想に基づいている。特許文献５は、ＴｉあるいはＮｂが共存するＡｌ系酸化皮膜を主体とした皮膜構造とすることにより、皮膜の導電性を向上させている。
　上述したように、従来，ＳＯＦＣのセパレーター用金属材料としては、Ｃｒ系酸化皮膜を形成させ、（１）大変高価な希土類元素（Ｙ，ＲＥＭ，Ｚｒ）の添加、（２）導電性の高いＣｕの添加や、ＴｉあるいはＮｂが共存するＡｌ系酸化皮膜への改質により、耐酸化性と電気伝導性を改善した高Ｃｒタイプのフェライト系ステンレス鋼である。前者（１）のステンレス鋼は、普及拡大の視点からコスト低減に大きな課題がある。後者（２）のステンレス鋼は、高温長期使用においての酸化皮膜の成長とそれに伴う電気伝導性の低下に課題がある。すなわち、レアアースである希土類元素の添加に頼ることなく、長期使用において酸化皮膜の電気伝導性と密着性に優れ、工業的に安価に大量生産可能なフェライト系ステンレス鋼については未だ出現していないのが現状である。
特開２００３－１７３７９５号公報 特開２００５－３２０６２５号公報 特開２００６－５７１５３号公報 特開２００６－９０５６号公報 特開２０１２－６７３９１号公報 熱処理；３３，（１９９３），２５１
　本発明は、従来から開示されている希土類元素を添加したフェライト系ステンレス鋼と遜色ない酸化皮膜の電気伝導性と密着性を、安価に大量生産可能なフェライト系ステンレス鋼で達成する技術思想に基づくものである。すなわち、本発明は、従来技術で課題となっている希土類元素の添加に頼ることなく、使用前の熱処理またはＳＯＦＣ作動時の熱により、電気伝導性と密着性に優れた酸化皮膜を形成できる耐久性に優れたＳＯＦＣ用のセパレーター用フェライト系ステンレス鋼板を提供するものである。
（１）質量％にて、Ｃ：０．０２％以下、Ｓｉ：０．１５％以下、Ｍｎ：０．３～１％、Ｐ：０．０４％以下、Ｓ：０．００３％以下、Ｃｒ：２０～２５％、Ｍｏ：０．５～２％、Ａｌ：０．１％以下、Ｎ：０．０２％以下、Ｎｂ：０．００１～０．５％、残部がＦｅおよび不可避的不純物からなり、かつ２．５＜Ｍｎ／（Ｓｉ＋Ａｌ）＜８．０を満たすことを特徴とするフェライト系ステンレス鋼板。
　ただし、上記式でＭｎ、Ｓｉ、Ａｌはそれぞれの元素の含有量（質量％）を意味する。
（２）さらに質量％にて、Ｔｉ：０．５％以下、Ｖ：０．５％以下、Ｎｉ：２％以下、Ｃｕ：１％以下、Ｓｎ：１％以下、Ｂ：０．００５％以下、Ｍｇ：０．００５％以下、Ｃａ：０．００５％以下、Ｗ：１％以下、Ｃｏ：１％以下、Ｓｂ：０．５％以下の１種または２種以上を含有していることを特徴とする（１）に記載するフェライト系ステンレス鋼板。
（３）さらに質量％にて、Ｚｒ：０．１％以下、Ｌａ：０．１％以下、Ｙ：０．１％以下、ＲＥＭ：０．１％以下、の１種または２種以上を含有していることを特徴とする（１）または（２）に記載するフェライト系ステンレス鋼板。
（４）鋼板表面に、ＣｒならびにＭｎが濃化した導電性と密着性に優れた酸化皮膜が形成されていることを特徴とする（１）～（３）のいずれかに記載するフェライト系ステンレス鋼板。
（５）（１）～（３）のいずれか一項に記載のフェライト系ステンレス鋼板に対して５００～１０００℃の温度範囲で２４ｈｒ以下の予備酸化処理を行うことを特徴とする酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法。
　以下、上記（１），（２），（３），（４）、（５）の鋼に係わる発明をそれぞれ本発明という。また、（１）～（５）の発明を合わせて、本発明ということがある。
Ｍｎ／（Ｓｉ＋Ａｌ）と７５０℃の接触抵抗率との関係。 Ｍｎ／（Ｓｉ＋Ａｌ）と７５０℃の剥離率との関係。
　本発明者らは、前記した課題を解決するために、高Ｃｒフェライト系ステンレス鋼板において、ＳＯＦＣの高温・長期使用を想定した耐酸化性と、電気伝導性に及ぼすＭｎ，Ｓｉ，Ａｌ量の相関について鋭意実験と検討を重ね、本発明を完成させた。以下に本発明で得られた知見について説明する。
　酸化皮膜の電気伝導性と密着性は、ＳｉとＡｌを極力低減して、かつ０．３％以上のＭｎを添加することで顕著に向上した。ＳＯＦＣ作動温度域の６００～９００℃を想定した場合、酸化皮膜はＣｒ2Ｏ3を主体とし、Ｃｒ2Ｏ3に加えてＭ3Ｏ4型酸化物（Ｍ＝Ｍｎ，Ｃｒ）を形成する。一般的に、ＳｉやＡｌの酸化物は、電気抵抗を著しく高めることが知られている。ＳｉやＡｌの酸化物生成と鋼界面への濃化を同時に抑止することで、電気伝導性を改善することができる。更に、Ｃｒ2Ｏ3酸化皮膜においてＭ3Ｏ4型酸化物を共存させることで、電気伝導性はより高くなる挙動を示すことが分かった。このような酸化皮膜改質による電気伝導性改善に係るメカニズムについては、未だ不明な点も多いが，（ａ）と（ｂ）の作用効果が可能性として考えられる。（ａ）Ｍ3Ｏ4型酸化物の生成により、Ｃｒ2Ｏ3皮膜中に導入された空孔性欠陥が電気伝導性を担っている。（ｂ）Ｃｒ2Ｏ3と比較して価数の大きいＭ3Ｏ4型酸化物が、半導体から良導体的作用（ドナー作用）を付与する。
　また、当該酸化皮膜は、酸化皮膜と地鉄界面の剥離を抑制して、良好な密着性を有した。酸化皮膜の密着性向上には、ＳｉとＡｌの低減による内部酸化物の抑止に加えて、酸化皮膜と地鉄界面でのＭｎ酸化物（ＭｎＯ）の生成も寄与している可能性が考えられる。
　上述したように、ＳｉとＡｌを低減しつつ必要量のＭｎを添加することで、Ｃｒ2Ｏ3皮膜の健全性（耐酸化性）を損なうことなく、むしろ酸化皮膜の密着性を向上させ、かつ希土類元素の添加に頼ることなく電気伝導性を付与できる全く新規な知見が得られた。前記（１）～（５）の本発明は、上述した検討結果に基づいて完成されたものである。
　以下、本発明の各要件について詳しく説明する。なお、各元素の含有量の「％」表示は「質量％」を意味する。
　成分の限定理由を以下に説明する。
　Ｃは、鋼中に含まれる不可避的不純物元素である。Ｃは，本発明の目標とするＣｒ2Ｏ3皮膜の健全性を阻害する。そのため，Ｃ量は低いほど好ましい。Ｃ含有量の過度な低減は、精錬コストの大幅な上昇を招く。従って、Ｃ含有量の上限は０．０２％とする。耐酸化性と製造性の点から，Ｃ含有量の好ましい下限は０．００１％であり、好ましい上限は０．０１％である。
　Ｓｉは、一般的な脱酸元素である。Ｓｉは、本発明の目標とする酸化皮膜の電気伝導性と密着性を阻害する。そのため、Ｓｉ量は低いほど好ましい。Ｓｉの過度な低減は、精錬コストの増大を招く。従って、Ｓｉ含有量の上限は０．１５％とする。本発明の目標とする特性と製造性を両立する点から、Ｓｉ含有量の好ましい下限は０．０１％であり、さらに好ましい下限は０．０５％である。Ｓｉ含有量の好ましい上限は０．１２％であり、さらに好ましい上限は０．１％である。
　Ｍｎは、脱酸元素として有効に作用する。加えてＭｎは、前記した通り、本発明の目標とする酸化皮膜の電気伝導性と密着性を向上させる作用を持つ。本発明では、Ｍｎ含有量０．３％以上において、その効果が発現する。従って、Ｍｎ含有量の下限は０．３％とする。Ｍｎの過度な添加は、Ｃｒ2Ｏ3皮膜の健全性を阻害して、耐酸化性と電気伝導性の低下を招く。そのため、Ｍｎ含有量の上限は１％とする。本発明の目標とする特性を効率的に発現させる視点から、Ｍｎ含有量の好ましい下限は０．４％であり、好ましい上限は０．８％である。
　Ｐは、鋼中に含まれる不可避的不純物元素である。Ｐは，本発明の目標とする耐酸化性の低下を招く。そのため，Ｐ含有量の上限は０．０４％とする。しかし，Ｐ含有量の過度の低減は、精錬コストの上昇を招く。従って、Ｐ含有量の下限は０．０１％とすることが好ましい。耐酸化性と製造性の点から，Ｐ含有量のより好ましい下限は０．０２％であり、好ましい上限は０．０３％である。
　Ｓは、鋼中に含まれる不可避的不純物元素である。Ｓは，本発明の目標とする耐酸化性を低下させる。特に，Ｍｎ系介在物や固溶Ｓの存在は，高温・長時間使用におけるＣｒ2Ｏ3皮膜を破壊する起点として作用する。そのため，Ｓ量は低いほど好ましい。Ｓ含有量の過度の低減は原料や精錬コストの上昇を招く。従って、Ｓ含有量の上限は０．００３％とする。耐酸化性と熱間加工性や製造コストの点から，Ｓ含有量の好ましい下限は０．０００２％であり、好ましい上限は０．００１％である。
　Ｃｒは、本発明の目標とする耐酸化性と、金属セパレーターとしての要件である熱膨張係数を確保する上で、基本の構成元素である。本発明においては、Ｃｒ含有量が２０％未満では、目的とする基本特性が十分に確保されない。従って、Ｃｒ含有量の下限は２０％とする。しかし，Ｃｒの過度の添加は、熱間圧延鋼材の靭性や延性が著しく低下し，製造性を阻害する。本発明の目標とする合金コスト抑制という視点から、Ｃｒ含有量の上限は２５％とする。基本特性と製造性およびコストの点から，Ｃｒ含有量の好ましい下限は２１％であり、好ましい上限は２３％である。
　Ｍｏは、本発明の金属セパレーターとしての要件である熱膨張係数を確保する上で、有効な構成元素である。さらに、Ｍｏは、固溶強化元素として作用し、高温部材として必要な高温強度の確保においても有効に作用する。これら効果を得るために、Ｍｏ含有量の下限を０．５％とする。Ｍｏの過度の添加は、原料コストの上昇や製造性を阻害する。従って、Ｍｏ含有量の上限は２％である。コスト対効果の点から，Ｍｏ含有量の好ましい下限は０．８％であり、好ましい上限は１．５％である。
　Ａｌは、強力な脱酸元素である。Ａｌは、本発明の目標とする酸化皮膜の電気伝導性と密着性を阻害する作用を持つ。そのため、Ａｌ量は低いほど好ましい。しかし、Ｓｉ量の低減を図るために、Ａｌを脱酸元素として必要量添加することが好ましい。脱酸効果を得るために、Ａｌ含有量の下限を０．０１％とすることが好ましい。Ａｌ含有量の上限は、本発明の目標とする酸化皮膜の特性を担保するために０．１％とする。本発明の目標とする特性と製造性を両立する点から、Ａｌ含有量のより好ましい下限は０．０２％であり、好ましい上限は０．０６％である。
　Ｎは、鋼中に含まれる不可避的不純物元素である。Ｎは，本発明の目標とするＣｒ2Ｏ3皮膜の健全性を阻害する。そのため，Ｎ量は低いほど好ましい。従って、Ｎ含有量の上限は０．０２％とする。Ｎ含有量の過度の低減は、精錬コストの大幅な上昇を招く。耐酸化性と製造性の点から，Ｎ含有量の好ましい下限は０．００１％であり、好ましい上限は０．０１％である。
　Ｎｂは、ＣやＮを炭窒化物として固定し，本発明の目標とする耐酸化性を向上させるとともに、高温部材として必要な強度を高める作用を持つため添加する。これら効果を得るために、Ｎｂ含有量の下限を０．００１％とする。Ｎｂの過度の添加は、原料コストを上昇させるとともに、加工性を阻害する。このためＮｂ含有量の上限は０．５％である。コスト対効果の点から、Ｎｂ含有量の好ましい下限は０．０５％であり、好ましい上限は０．３５％である。
　本発明のフェライト系ステンレス鋼板は、前記した成分を有し，目標とする酸化皮膜の電気伝導性と密着性の観点から、Ｍｎ量と（Ｓｉ＋Ａｌ）量の関係を規定する必要がある。ＳｉやＡｌの内部酸化を抑止したＣｒ2Ｏ3主体の酸化皮膜において、Ｍｎを濃化させて、Ｍ3Ｏ4型酸化物（Ｍ＝Ｍｎ，Ｃｒ）を生成させて導電性を得るには、Ｍｎ／（Ｓｉ＋Ａｌ）＞２．５とする必要がある。他方、Ｍｎ／（Ｓｉ＋Ａｌ）≧８．０の場合、Ｍ3Ｏ4型酸化物の生成を促進し、Ｃｒ2Ｏ3主体とする酸化皮膜の保護性を阻害するとともに、酸化皮膜の成長により電気伝導性ならびに密着性の低下を招く。従って、目標とする特性を得るために、２．５＜Ｍｎ／（Ｓｉ＋Ａｌ）＜８．０とする。過度なＳｉ，Ａｌの低減を緩和して、目標特性を得る点から、好ましい範囲は、４．０＜Ｍｎ／（Ｓｉ＋Ａｌ）＜７．０とする。式中のＭｎ、Ｓｉ、Ａｌはそれぞれの元素の含有量（質量％）を意味する。
　以下の元素は選択的に添加することができる。
　Ｔｉ、Ｖは、Ｎｂと同様に、ＣやＮを炭窒化物として固定し，本発明の目標とする耐酸化性を向上させる作用を持つ。このため選択的に添加することができる。これら効果を得るために、Ｔｉ、Ｖを添加する場合は下限を０．００１％とすることが好ましい。Ｔｉ、Ｖの過度の添加は、原料コストの上昇や加工性を阻害する。Ｔｉ、Ｖを添加する場合の上限は０．５％である。コスト対効果の点から，Ｔｉ、Ｖを添加する場合のより好ましい下限は０．０５％であり、好ましい上限は０．３５％である。
　Ｎｉは、固溶強化元素として作用し、構造材として必要な高温強度の上昇に寄与するため、選択的に添加することができる。これら効果を得るために、添加する場合はＮｉ含有量の下限を０．１％とすることが好ましい。Ｎｉの過度の添加は、原料コストの上昇や加工性を阻害する。Ｎｉを添加する場合の上限は２％である。コスト対効果の点から，Ｎｉを添加する場合の含有量のより好ましい下限は０．２％であり、好ましい上限は０．８％である。
　Ｂ，Ｍｇ，Ｃａは、熱間加工性を改善する作用を持つため、選択的に添加することができる。これら効果を得るために、Ｂ，Ｍｇ，Ｃａを添加する場合は、下限を０．０００２％とすることが好ましい。しかし，Ｂ，Ｍｇ，Ｃａの過度な添加は、製造性の低下や熱間加工での表面疵を誘発する。Ｂ，Ｍｇ，Ｃａを添加する場合の上限は０．００５％とする。製造性と効果の点から，Ｂ，Ｍｇ，Ｃａを含有する場合の含有量のより好ましい下限は０．０００３％であり、好ましい上限は０．００２％である。
　Ｃｕ、Ｓｎ、Ｓｂは、Ｎｉと同様な効果を有する。Ｃｕ、Ｓｎ、Ｓｂの過度な添加は、析出や偏析により酸化皮膜の密着性や製造性を阻害する作用を持つ。Ｃｕ、Ｓｎをそれぞれ添加する場合の上限は１．０％、好ましくは０．５％以下とする。Ｓｂを添加する場合の上限は０．５％、好ましくは０．２％以下とする。添加する場合の好ましい下限は、Ｃｕ：０．１％、Ｓｎ：０．０１％、Ｓｂ：０．００５％とする。
　Ｗ、Ｃｏは、Ｎｉと同様な固溶強化に加え、酸化皮膜およびその直下に濃化して電気導電性を高める効果も有する。Ｗ、Ｃｏは，高価な元素である。本発明において、Ｗ、Ｃｏは、これら効果を発現するために、選択的に添加しても構わない。Ｗ、Ｃｏをそれぞれ添加する場合の上限は１％、好ましくは０．５％以下とする。Ｗ、Ｃｏを添加する場合の下限は、０．１％とすることが好ましい。
　Ｚｒ，Ｌａ，Ｙ，ＲＥＭは、従来から、酸化皮膜の電気伝導性と健全性を高める上で著しい効果を有する。Ｚｒ，Ｌａ，Ｙ，ＲＥＭは、大変高価な元素である。本発明は、これら元素の添加に頼ることなく、特性を得ることを目標としている。しかしながら、Ｚｒ，Ｌａ，Ｙ，ＲＥＭは、より一層効果を発現するために、選択的に添加しても構わない。Ｚｒ，Ｌａ，Ｙ，ＲＥＭを添加する場合は、下限を０．００１％とすることが好ましい。Ｚｒ，Ｌａ，Ｙ，ＲＥＭを添加する場合，上限を０．１％とする。Ｚｒ，Ｌａ，Ｙ，ＲＥＭを添加する場合、コスト対効果の点から，より好ましい下限は０．０１％であり、好ましい上限は０．０５％である。
　本発明のフェライト系ステンレス鋼は、前記した成分を有し，酸化皮膜の電気伝導性と密着性の観点からＭｎ／（Ｓｉ＋Ａｌ）を規定している。本発明において、製造方法は特に限定するものでない。
　本発明のフェライト系ステンレス鋼板は、主として，熱間圧延鋼帯を焼鈍あるいは焼鈍を省略して、デスケ－リングの後冷間圧延し，続いて仕上げ焼鈍とデスケ－リングした冷延焼鈍板を対象としている。本発明のフェライト系ステンレス鋼板は、場合によっては、冷間圧延を施さない熱延焼鈍板でも構わない。
　さらに、ガス配管用としては、鋼板から製造した溶接菅も含まれる。配管は、溶接菅に限定するものでない。配管は，熱間加工により製造した継ぎ目無し菅でもよい。
　上述した冷間圧延後の仕上げ焼鈍は、８００～１１００℃とするのが好ましい。８００℃未満では鋼の軟質化と再結晶が不十分となり，所定の材料特性が得られないこともある。他方，１１００℃超では粗大粒となり，鋼の靭性・延性を阻害することもある。
　さらに、長期使用を想定した耐久性（導電性および密着性）を向上させるために、上記フェライト系ステンレス鋼板に対して、ＳＯＦＣセパレーター用として使用する前に、予備酸化処理を行うことが好ましい。このことにより、ＳＯＦＣシステムの運転初期において、ＣｒならびにＭｎが濃化した緻密な酸化皮膜を、鋼板表面に均一に形成しておく事が有効である。ＳＯＦＣシステム運転前に、予め緻密な酸化皮膜を表面に形成しておくことで、金属表面の状態と比較して、初期に形成される酸化皮膜の均一性・バリヤー性を高め、長期使用の電気伝導性と耐酸化性を一層向上させることができる。予備酸化処理条件は、５００～１０００℃で１ｍｉｎ以上２４ｈｒ以下とすることが好ましい。予備酸化処理は、大気、不活性ガス、水蒸気を含む大気または不活性ガス中で行うことができる。
　ここで、鋼板表面におけるＣｒならびにＭｎが濃化した酸化皮膜とは、Ｃｒ2Ｏ3を主体として構成された酸化皮膜であり、Ｃｒ2ＭｎＯ4を１０％以上含むものをいう。これら酸化皮膜は、表面のＸ線回折法により評価することができる。具体的には、Ｃｒ2Ｏ3とＣｒ2ＭｎＯ4の最強線の回折ピークにおける積分強度比から算出される。
　以下に、本発明の実施例について述べる。
　表１および表２に成分を示すフェライト系ステンレス鋼を溶製し、熱間圧延を行い、板厚４．０～５．０ｍｍの熱延板として、９００～１０５０℃で焼鈍・酸洗した。次いで、中間焼鈍と冷間圧延を繰り返して、０．４ｍｍ厚の冷延板とし、９００～１０００℃で焼鈍・酸洗を行い、供試材とした。
　鋼Ｎｏ．１～２０は、各元素が本発明の規定範囲内であり，本発明で規定するＭｎ／（Ｓｉ＋Ａｌ）の範囲を満たすものである。これに対して、鋼Ｎｏ．２１～２５は、各元素が本発明の規定範囲から外れ，本発明で規定するＭｎ／（Ｓｉ＋Ａｌ）の範囲を満たすものである。鋼Ｎｏ．２６と２７は、各元素が本発明範囲であり、Ｍｎ／（Ｓｉ＋Ａｌ）が本発明の規定範囲から外れるものである。鋼Ｎｏ．２８～３０は、各元素とＭｎ／（Ｓｉ＋Ａｌ）のいずれも、本発明の規定から外れるものである。尚、鋼Ｎｏ．３０は、従来公知のＲＥＭ添加フェライト系ステンレス鋼である。本発明の目標とする酸化皮膜の電気伝導性と密着性は、鋼Ｎｏ．３０を基準に判定した。
　酸化皮膜の電気伝導性と密着性は、長期使用を想定して、以下の要領で酸化試験を実施して、表面に酸化皮膜を形成してから評価した。
　酸化試験は、ＳＯＦＣの標準的な作動温度を想定した、７５０℃で４．５万時間（５年）の運転で生成する酸化物の生成量を、実験室的に模擬する加速試験条件を検討した。酸化皮膜の成長速度は、例えば，非特許文献１により求めることが可能であり、７５０℃，４．５万時間後の酸化増量は、Ｃｒ2Ｏ3皮膜の場合：１．０ｍｇ／ｃｍ2程度と予測される。これに相当する酸化増量を、比較的短時間で模擬できる加速条件（温度，時間）として、９００℃，４００ｈｒを選定した。試験片寸法は、板厚×２５ｍｍ×２０ｍｍとし，表面と端面はエメリー紙番手＃６００の湿式研磨とした。加速試験後、酸化皮膜の電気伝導性と密着性を評価した。
　酸化皮膜の電気伝導性は、２５ｍｍ×２０ｍｍのＰｔメッシュを、９００℃、３０分で試料表面に焼き付け、ＰｔメッシュにＰｔペーストを用いて電流端子および電圧端子を取り付け、４端子法により測定した。具体的には、マッフル炉へ試料を挿入し、７５０℃に昇温した後、通電（Ｉ）時の電圧降下値（ΔＶ）を測定し、接触抵抗（Ｒ＝ΔＶ／Ｉ）を求めた。その結果から、接触抵抗率（ρ＝Ｒ×Ｓ，Ｓ：通電面積）を算出して、電気伝導性の評価指標とした。
　Ｐｔペーストは、田中貴金属製ＴＲ－７９０５、Ｐｔメッシュは、田中貴金属製φ０．０７６ｍｍを使用した。電圧降下値の測定装置は、アドバンテスト製ＴＲ６１４３（直流電源）を使用した。
　酸化皮膜の密着性は、酸化皮膜表面における剥離率を測定して評価した。具体的には、以下の手順で評価した。酸化試験後、試験片表裏面の外観写真を、実寸から２倍程度に拡大して撮影する。そこで、表面から酸化物の飛散した痕跡である点の個数を数える。これら点は、実寸にして０．５ｍｍ以上のものを対象とし，目視で十分認識可能な大きさとした。剥離率（個／ｃｍ2）は、２試料の表面と裏面の合計４面からカウントした点の個数を、その表面積（２０ｃｍ2）で除することにより算出した。酸化皮膜の剥離を生じることなく、密着性が良好とする判定基準は、１面につき点状の痕跡の個数が１点以下の場合とした。すなわち、剥離率≦０．２（４点／２０ｃｍ2）とした。
　セパレーター用鋼板の基本特性として、７５０℃の熱膨張係数を測定した。試料寸法は５ｍｍ幅×１５ｍｍ長さ、昇温時の雰囲気はＡｒ中、熱膨張係数は２５℃を起点として算出した。測定装置は、ブルカー・エイエックス製ＴＭＡ４０００を使用した。
　鋼Ｎｏ．１～３０の供試材の酸化皮膜の接触抵抗率および剥離率、鋼Ｎｏ．１～３０の供試材の熱膨張係数を表３および表４に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　鋼Ｎｏ．１～２０は、本発明の目標とする酸化皮膜の電気伝導性と密着性の両者を満たし、基本特性である低熱膨張を達成したものである。鋼Ｎｏ．１～２０の表面を、Ｘ線回折法により測定した結果、表面にＣｒ2Ｏ3を主体とし、Ｍｎが濃化した酸化皮膜が形成されていた。鋼Ｎｏ．１～２０の鋼板は、従来公知のＲＥＭ添加フェライト系ステンレス鋼板（鋼Ｎｏ．３０）と同等以上の特性を実現した。これより，本発明で規定する各元素とＭｎ／（Ｓｉ＋Ａｌ）の範囲を満たせば，Ｃｒ2Ｏ3皮膜の良好な耐酸化性を損なうことなく，高温での電気伝導性を付与できることが分かる。
　鋼Ｎｏ．２０は、鋼Ｎｏ．２と同成分である。鋼Ｎｏ．２０では、鋼Ｎｏ．２の供試材を、大気中８００℃，１２ｈで予備酸化してから、上記酸化試験を実施し、その後、電気伝導性と密着性を評価した。鋼Ｎｏ．２０は、予備酸化により酸化皮膜の電気伝導性と密着性を改善したものである。本発明で規定する予備酸化を施すことにより、同一成分の鋼において酸化皮膜の電気伝導性と密着性を高めることができる。Ｎｏ．２０の酸化皮膜は、表面のＸ線回折法によりＣｒ2Ｏ3を主体とし、Ｃｒ2ＭｎＯ4を２０％含むものであった。
　鋼Ｎｏ．２１、２２、２４、２６～２９は、本発明の目標とする酸化皮膜の電気伝導性と密着性の両者あるいはいずれか一方が、得られないものである。これより，本発明で規定する各元素とＭｎ／（Ｓｉ＋Ａｌ）のいずれかの範囲が外れる場合は、酸化皮膜の電気伝導性と密着性を兼備することは困難である。
　鋼Ｎｏ．２３、２５は、酸化皮膜の電気伝導性と密着性が、目標圏内にあるものの、基本特性である低熱膨張が未達となったものである。これより，基本特性を得るためには、規定範囲のＣｒ，Ｍｏを添加する必要がある。
　本発明で規定する各元素の範囲を満たす鋼板（鋼Ｎｏ．１～２０、２６、２７）について、Ｍｎ／（Ｓｉ＋Ａｌ）と７５０℃の接触抵抗率ならびに剥離率との関係を、図１ならびに図２に示す。これより、Ｃｒ2Ｏ3皮膜の良好な密着性を損なうことなく，本発明の目標とする酸化皮膜の電気伝導性（接触抵抗率）と密着性を得るには、本発明で規定する各元素の範囲を有し，かつＭｎ／（Ｓｉ＋Ａｌ）を２．５～８．０の範囲に制御することが重要であることが分かる。酸化皮膜の電気伝導性と密着性の特性を兼備する好適な範囲は、Ｍｎ／（Ｓｉ＋Ａｌ）を４．０～７．０の範囲であることも分かる。
　本発明によれば、各元素の成分とＭｎ／（Ｓｉ＋Ａｌ）の範囲を規定することにより，高価な希土類元素の添加に頼ることなく，ＳＯＦＣ用として、長期使用において優れた酸化皮膜の電気伝導性と密着性を兼備する、フェライト系ステンレス鋼板を提供することが出来る。本発明のフェライト系ステンレス鋼は、特殊な製造方法に依らず，工業的に生産することが可能である。

Claims (5)

  1. 　質量％にて、Ｃ：０．０２％以下、Ｓｉ：０．１５％以下、Ｍｎ：０．３～１％、Ｐ：０．０４％以下、Ｓ：０．００３％以下、Ｃｒ：２０～２５％、Ｍｏ：０．５～２％、Ａｌ：０．１％以下、Ｎ：０．０２％以下、Ｎｂ：０．００１～０．５％、残部がＦｅおよび不可避的不純物からなり、かつ（１）式を満たすことを特徴とするフェライト系ステンレス鋼板。
    　　２．５＜Ｍｎ／（Ｓｉ＋Ａｌ）＜８．０　・・・（１）
    ただし、（１）式でＭｎ、Ｓｉ、Ａｌはそれぞれの元素の含有量（質量％）を意味する。
  2. 　さらに質量％にて、Ｔｉ：０．５％以下、Ｖ：０．５％以下、Ｎｉ：２％以下、Ｃｕ：１％以下、Ｓｎ：１％以下、Ｂ：０．００５％以下、Ｍｇ：０．００５％以下、Ｃａ：０．００５％以下、Ｗ：１％以下、Ｃｏ：１％以下、Ｓｂ：０．５％以下の１種または２種以上を含有していることを特徴とする請求項１に記載するフェライト系ステンレス鋼板。
  3. 　さらに質量％にて、Ｚｒ：０．１％以下、Ｌａ：０．１％以下、Ｙ：０．１％以下、ＲＥＭ：０．１％以下、の１種または２種以上を含有していることを特徴とする請求項１または２に記載するフェライト系ステンレス鋼板。
  4. 　鋼板表面に、ＣｒならびにＭｎが濃化した導電性と密着性に優れた酸化皮膜が形成されていることを特徴とする請求項１～３のいずれか一項に記載するフェライト系ステンレス鋼板。
  5. 　請求項１～３のいずれか一項に記載のフェライト系ステンレス鋼板に対して、５００～１０００℃の温度範囲で２４ｈｒ以下の予備酸化処理を行うことを特徴とする酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法。
PCT/JP2013/069004 2012-07-13 2013-07-11 フェライト系ステンレス鋼板および酸化皮膜の導電性と密着性に優れたフェライト系ステンレス鋼板の製造方法 WO2014010680A1 (ja)