WO2013099697A1 - アクティブマトリクス基板 - Google Patents

アクティブマトリクス基板 Download PDF

Info

Publication number
WO2013099697A1
WO2013099697A1 PCT/JP2012/082784 JP2012082784W WO2013099697A1 WO 2013099697 A1 WO2013099697 A1 WO 2013099697A1 JP 2012082784 W JP2012082784 W JP 2012082784W WO 2013099697 A1 WO2013099697 A1 WO 2013099697A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
transparent conductive
insulating layer
active matrix
inorganic insulating
Prior art date
Application number
PCT/JP2012/082784
Other languages
English (en)
French (fr)
Inventor
美崎　克紀
Original Assignee
シャープ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by シャープ株式会社 filed Critical シャープ株式会社
Priority to CN201280063901.4A priority Critical patent/CN104011587B/zh
Priority to US14/368,557 priority patent/US9035302B2/en
Publication of WO2013099697A1 publication Critical patent/WO2013099697A1/ja

Abstract

　アクティブマトリクス基板（１００Ａ）は、基板（１１）と、基板に支持された、半導体層（１４）、ゲート電極（１２ｇ）、ソース電極（１６Ｓ）およびドレイン電極（１６Ｄ）を有するＴＦＴ（１０Ａ）と、少なくとも一方がＴＦＴのドレイン電極と電気的に接続された、引張応力を有する第１透明導電層（２２）および第２透明導電層（２４）と、第１透明導電層と第２透明導電層との間に形成された、無機絶縁層の積層体（２３Ｓ１）とを有し、積層体は、引張応力を有する第１無機絶縁層（２３ａ１）と、第１無機絶縁層を挟むように形成され、圧縮応力を有する第２および第３無機絶縁層（２３ｂ１、２３ｃ１）とを有し、且つ、積層体は全体として引張応力を有する。

Description

アクティブマトリクス基板
　本発明は、アクティブマトリクス基板に関し、特に、液晶表示装置に好適に用いられるアクティブマトリクス基板に関する。
　アクティブマトリクス型の液晶表示装置は、一般に、画素ごとにスイッチング素子として薄膜トランジスタ（ＴＦＴ）が形成されたアクティブマトリクス基板（「ＴＦＴ基板」と呼ばれることもある）と、カラーフィルタなどが形成された対向基板（「カラーフィルタ基板」と呼ばれることもある）と、アクティブマトリクス基板および対向基板の間に設けられた液晶層とを備えている。薄膜トランジスタに電気的に接続された画素電極と、共通電極との電位差に応じた電界が液晶層に印加され、この電界によって液晶層中の液晶分子の配向状態が変化することにより、各画素の光透過率を制御して表示を行うことができる。
　アクティブマトリクス型の液晶表示装置には、その用途に応じて様々な表示モードが提案され、採用されている。表示モードとしては、ＴＮ（Ｔｗｉｓｔｅｄ　Ｎｅｍａｔｉｃ）モード、ＶＡ（Ｖｅｒｔｉｃａｌ　Ａｌｉｇｎｍｅｎｔ）モード、ＩＰＳ（Ｉｎ－Ｐｌａｎｅ－Ｓｗｉｔｃｈｉｎｇ）モード、ＦＦＳ（Ｆｒｉｎｇｅ　Ｆｉｅｌｄ　Ｓｗｉｔｃｈｉｎｇ）モードなどが挙げられる。
　これらの液晶表示装置の中には、アクティブマトリクス基板が無機絶縁層を間に介して形成された２つの透明導電層を有するものがある。無機絶縁層を間に挟んだ２つの透明導電層で形成される電極の構造を、簡単のために、「２層電極構造」ということにする。
　例えば、一般的なＦＦＳモードでは、特許文献１に開示されているように、下層の透明導電層が共通電極として設けられ、上層の透明導電層が複数のスリットを形成された画素電極として設けられる。なお、特許文献２に開示されているように、ＦＦＳモードにおいて、画素電極が下層電極として設けられ、複数のスリットが形成された共通電極が上層電極として設けられる構成も知られている。
特開２００２－１８２２３０号公報 特開２０１１－５３４４３号公報
　また、出願人は、後述するように、２層電極構造を利用した補助容量を有する液晶表示装置を研究開発している。具体的には、下層の透明導電層を補助容量対向電極（共通電圧または補助容量対向電圧が供給される）とし、上層の透明導電層を画素電極とした構成を検討している。この液晶表示装置は、例えばＶＡモードであるが、他の表示モードにも適用できる。
　本発明は、上記の２層電極構造を有するアクティブマトリクス基板に、詳細は比較例を参照して後述するが、以下の課題があることを見出した。
　まず、２層電極構造において、２つの透明導電層の間に形成された層間絶縁膜（図８に示す比較例のアクティブマトリクス基板２００Ａの第３層間絶縁層２３Ｐ）と透明導電層との密着性が低く、剥がれやすいという問題がある。
　さらに、２層電極構造において、透明導電層と層間絶縁膜との密着性を改善するために、種々の無機絶縁層を検討したところ、密着性を向上させることができる無機絶縁層（例えば、引張応力を有する窒化シリコン（ＳｉＮx）層）を用いると、透明導電層（一般に、ＩＴＯ（インジウム錫酸化物）またはＩＺＯ（インジウム亜鉛酸化物）などで代表される透明無機酸化物から形成される）が窒化シリコン層によって、界面近傍の酸化物が還元され金属化される結果、透明導電層の光の透過率が低下するという問題がある。
　本発明は、上記の問題の少なくとも一部を解決したアクティブマトリクス基板を提供することを目的とする。
　本発明の実施形態によるアクティブマトリクス基板は、基板と、前記基板に支持され、半導体層、ゲート電極、ソース電極およびドレイン電極を有する薄膜トランジスタと、少なくとも一方が前記薄膜トランジスタの前記ドレイン電極と電気的に接続された、第１透明導電層および第２透明導電層と、前記第１透明導電層と前記第２透明導電層との間に形成された、無機絶縁層の積層体とを有し、前記積層体は、引張応力を有する第１無機絶縁層と、前記第１無機絶縁層を挟むように形成され、圧縮応力を有する第２および第３無機絶縁層とを有し、且つ、前記積層体は全体として引張応力を有する。本発明の実施形態によるアクティブマトリクス基板においては、引張応力を有する前記第１無機絶縁層が、前記第１透明導電層および前記第２透明導電層のいずれにも直接接触することがない。
　ある実施形態において、前記第１無機絶縁層は、屈折率が１．８０４以下の窒化シリコン層である。
　ある実施形態において、前記第２無機絶縁層および前記第３無機絶縁層は、屈折率が１．８０５以上の窒化シリコン層である。
　ある実施形態において、前記第１透明導電層は前記第２透明導電層よりも前記基板の近くに形成されており、前記第２無機絶縁層は前記第３無機絶縁層よりも前記基板の近くに形成されており、前記積層体は、前記第１透明導電層と前記第２無機絶縁層との間に第４無機絶縁層をさらに有する。
　ある実施形態において、前記第４無機絶縁層は、屈折率が１．４以上１．６以下の酸化シリコン層である。
　ある実施形態において、前記積層体は、前記第２透明導電層と前記第３無機絶縁層との間に第５無機絶縁層をさらに有する。
　ある実施形態において、前記第５無機絶縁層は、屈折率が１．４以上１．６以下の酸化シリコン層である。
　ある実施形態において、前記第１透明導電層および前記第２透明導電層は、ＩＴＯ層またはＩＺＯ層である。
　ある実施形態において、前記半導体層は、酸化物半導体層である。前記酸化物半導体層は、例えば、Ｉｎ－Ｇａ－Ｚｎ－Ｏ系の半導体（ＩＧＺＯ系半導体）を含む。
　ある実施形態において、前記第１透明導電層は、電気的にフローティング状態にあり、前記第２透明導電層は、画素電極である。
　ある実施形態において、前記第１透明導電層は、補助容量対向電極であり、前記第２透明導電層は、画素電極である。この実施形態のアクティブマトリクス基板は、例えば、垂直配向（ＶＡ）モードの液晶表示装置に用いられる。
　ある実施形態において、前記第１透明導電層は、共通電極であり、前記第２透明導電層は、複数のスリットを有する画素電極である。この実施形態のアクティブマトリクス基板は、例えば、ＦＦＳモードの液晶表示装置に用いられる。
　ある実施形態において、前記アクティブマトリクス基板は、前記薄膜トランジスタを覆う有機絶縁層をさらに有し、前記有機絶縁層の一部は、前記積層体の一部と直接接触している。
　本発明の実施形態によると、引張応力を有する２つの透明導電層の間に形成された、無機絶縁層の積層体によって、剥離が抑制される。また、本発明の実施形態によると、積層体に含まれる引張応力を有する第１無機絶縁層が、第１透明導電層および第２透明導電層のいずれにも直接接触することがないので、例えば、第１無機絶縁層を窒化シリコン層で形成しても、第１透明導電層および第２透明導電層を構成している透明酸化物（ＩＴＯ、ＩＺＯ）を還元することがなく、光の透過率の低下を招かない。
本発明の実施形態によるアクティブマトリクス基板１００Ａの模式的な平面図である。 アクティブマトリクス基板１００Ａの模式的な断面図であり、（ａ）は、図１中のＡ－Ａ’線に沿った断面を示し、（ｂ）は図１中のＢ－Ｂ’線に沿った断面を示している。 本発明の実施形態による他のアクティブマトリクス基板１００Ｂの模式的な断面図であり、（ａ）および（ｂ）は、図２（ａ）および（ｂ）にそれぞれ対応する断面を示している。 （ａ）～（ｄ）は、アクティブマトリクス基板１００Ｂの製造方法を説明するための模式的な断面図である。 本発明の実施形態によるさらに他のアクティブマトリクス基板１００Ｃの模式的な平面図である。 アクティブマトリクス基板１００Ｃの模式的な断面図であり、（ａ）は、図５中のＡ－Ａ’線に沿った断面を示し、（ｂ）は図５中のＢ－Ｂ’線に沿った断面を示している。 （ａ）～（ｄ）は、アクティブマトリクス基板１００Ｃの製造方法を説明するための模式的な断面図である。 比較例のアクティブマトリクス基板２００Ａの模式的な断面図である。 （ａ）および（ｂ）は、膜の内部応力の評価方法を説明するための模式図である。
　以下、図面を参照して、本発明の実施形態によるアクティブマトリクス基板の構造と製造方法を説明する。以下では、２層電極構造を有するＶＡモードの液晶表示装置に用いられるアクティブマトリクス基板を例示する。しかし、本発明の実施形態はこれに限られず、上述のＦＦＳモードの液晶表示装置に用いられるアクティブマトリクス基板の他、他の表示装置にも適用できる。
　まず、図１および図２を参照して、本発明の実施形態によるアクティブマトリクス基板１００Ａの構造を説明する。図１は、本発明の実施形態によるアクティブマトリクス基板１００Ａの模式的な平面図である。図２は、アクティブマトリクス基板１００Ａの模式的な断面図であり、図２（ａ）は、図１中のＡ－Ａ’線に沿った断面を示し、図２（ｂ）は図１中のＢ－Ｂ’線に沿った断面を示している。
　アクティブマトリクス基板１００Ａは、基板（例えばガラス基板）１１と、基板１１に支持され、半導体層１４、ゲート電極１２ｇ、ソース電極１６Ｓおよびドレイン電極１６Ｄを有する薄膜トランジスタ（以下、ＴＦＴという。）１０Ａと、少なくとも一方がＴＦＴ１０Ａのドレイン電極１６Ｄと電気的に接続された、引張応力を有する第１透明導電層２２および第２透明導電層２４と、第１透明導電層２２と第２透明導電層２４との間に形成された、無機絶縁層の積層体２３Ｓ１とを有している。ここでは、第１透明導電層２２は、第２透明導電層２４よりも基板１１に近い側に形成されており、第２透明導電層２４が、ＴＦＴ１０Ａのドレイン電極１６Ｄと電気的に接続されている。
　ここで、第１透明導電層２２および第２透明導電層２４は、ＩＴＯ層またはＩＺＯ層である。ＩＴＯ層およびＩＺＯ層は、いずれも引張応力を有することが知られている。特に、ＩＴＯ層はＩＺＯ層に比べて、引張応力が大きく、剥がれやすい。ＩＴＯ層やＩＺＯ層が引張応力を有する理由は必ずしも明らかではないが、成膜温度や条件等によらず、一般に引張応力を有する。各層の内部応力（引張応力または圧縮応力）については、図９を参照して後述する。
　積層体２３Ｓ１は、引張応力を有する第１無機絶縁層２３ａ１と、第１無機絶縁層２３ａ１を挟むように形成され、圧縮応力を有する第２無機絶縁層２３ｂ１および第３無機絶縁層２３ｃ１とを有している。第２無機絶縁層２３ｂ１は、第１無機絶縁層２３ａ１の基板１１側に形成されており、第３無機絶縁層２３ｃ１は、第１無機絶縁層２３ａ１の基板１１とは反対側に形成されている。積層体２３Ｓ１は全体として引張応力を有する。また、アクティブマトリクス基板１００Ａにおいては、引張応力を有する第１無機絶縁層２３ａ１が、第１透明導電層２２および第２透明導電層２４のいずれにも直接接触することがない。
　ここで、第１無機絶縁層２３ａ１は、例えば、屈折率が１．８０４以下の窒化シリコン層である。第２無機絶縁層２３ｂ１および第３無機絶縁層２３ｃ１は、例えば、屈折率が１．８０５以上の窒化シリコン層である。
　一般に、窒化シリコン層や酸化シリコン層は、圧縮応力を有することが知られている。ただし、屈折率が１．８０４以下の窒化シリコン層は例外的に引張応力を有する。従って、図８に示す比較例のアクティブマトリクス基板２００Ａのように、第３層間絶縁層２３Ｐとして、屈折率が１．８０４以下の窒化シリコン層を用いると、第３層間絶縁層２３Ｐの剥離を抑制することはできる。しかしながら、屈折率が１．８０４以下の窒化シリコン層は、還元力が強く、例えばＩＴＯ層２２、２４と接触した状態で、熱処理を行うと、窒化シリコン層とＩＴＯ層２２、２４との界面近傍のＩＴＯを還元し、金属化する。そうすると、ＩＴＯ層２２、２４の光透過率は低下する。第１透明導電層２２および第２透明導電層２４としてＩＺＯ層を用いる場合も同様である。
　そこで、アクティブマトリクス基板１００Ａにおいては、屈折率が１．８０４以下の窒化シリコン層２３ａ１（引張応力を有する）を、屈折率が１．８０５以上の窒化シリコン層２３ｂ１と窒化シリコン層２３ｃ１（圧縮応力を有する）とで挟んだ構造を有する積層体２３Ｓ１を用いることによって、引張応力を有する屈折率が１．８０４以下の窒化シリコン層２３ａ１が、第１透明導電層（ＩＴＯ層またはＩＺＯ層）２２および第２透明導電層（ＩＴＯ層またはＩＺＯ層）２４のいずれにも直接接触することを防止している。
　積層体２３Ｓ１は、全体として、引張応力を有するように構成されている。例えば、屈折率が１．８０５以上の窒化シリコン層２３ｂ１および２３ｃ１の厚さをそれぞれｔｈｂ１およびｔｈｃ１とし、屈折率が１．８０４以下の窒化シリコン層２３ａ１の厚さをｔｈａ１とすると、ｔｈａ１≧ｔｈｂ１＋ｔｈｃ１の関係を満足することが好ましい。このとき、ｔｈｂ１およびｔｈｃ１は、それぞれ独立に１００ｎｍ以下であることが好ましい。もちろん、厳密には、各層の応力の大きさは、各層の厚さだけでなく、各膜の構造（組成など）の影響を受けるので、上記の関係を有しない場合でも、積層体２３Ｓ１が全体として引張応力を有することがある。発明者の検討によると、上記の関係を満足すれば、積層体２３Ｓ１は、全体として、引張応力を有する。なお、ｔｈｂ１およびｔｈｃ１が１００ｎｍを超えると、生産効率の低下という問題が生じることがあるので、ｔｈｂ１およびｔｈｃ１はそれぞれ独立に１００ｎｍ以下であることが好ましい。
　アクティブマトリクス基板１００Ａは、ＴＦＴ１０Ａを覆う有機絶縁層１９をさらに有しており、有機絶縁層１９の一部は、積層体２３Ｓ１の一部と直接接触している。有機絶縁層１９は、例えば、透明のポジ型感光性樹脂で形成されている。ガラス基板などの無機材料で形成された基板上に形成された有機絶縁層１９は、一般に、引張応力を有している。従って、圧縮応力を有する無機絶縁層は、有機絶縁層１９に対する密着性が低い。これに対して、アクティブマトリクス基板１００Ａにおいては、引張応力を有する積層体２３Ｓ１の一部が有機絶縁層１９の一部と接触しているので、密着性に優れる。従って、積層体２３Ｓ１は、その下面が接する第１透明導電層２２および有機絶縁層１９との密着性に優れるので、剥離することが抑制される。
　本発明の実施形態によるアクティブマトリクス基板１００Ａにおいて、第１透明導電層２２の一部２２ａはどこにも接続されておらず、電気的にフローティング状態にあり、シールド電極２２ａとして機能し、第２透明導電層２４の一部２４ｐは画素電極として機能する。すなわち、第１透明導電層２２は、画素電極２４ｐの電位が、基板１１上に形成された種々の電極や配線による電界からの影響を受けないように保護する。
　なお、第１透明導電層２２の一部２２ａを補助容量対向電極２２ａとして用いてもよい。このとき、補助容量対向電極２２ａと、画素電極２４ｐと、これらの間の積層体２３Ｓ１が補助容量として機能する。補助容量は、第１透明導電層２２および第２透明導電層２４で形成されているので、画素開口率を低下させることなく、大きな容量値を有し得る。従って、ＴＦＴ１０Ａのように、ゲートバスライン１２上にソースコンタクトホール１５ａおよびドレインコンタクトホール１５ｂを有する構成を採用することによる、寄生容量の増大に伴うフィードスルー電圧の増大を抑制することが可能となる。
　半導体層１４は、例えば、酸化物半導体層である。酸化物半導体は移動度が高いので、２層電極構造を利用して形成される比較的大きな容量値の補助容量を十分に速く充電できる。酸化物半導体層は、例えばＩｎ－Ｇａ－Ｚｎ－Ｏ系の半導体（以下、「ＩＧＺＯ系半導体」と略する。）を含む。ここで、ＩＧＺＯ系半導体は、Ｉｎ（インジウム）、Ｇａ（ガリウム）、Ｚｎ（亜鉛）の三元系酸化物であって、Ｉｎ、ＧａおよびＺｎの割合（組成比）は特に限定されず、例えばＩｎ：Ｇａ：Ｚｎ＝２：２：１、Ｉｎ：Ｇａ：Ｚｎ＝１：１：１、Ｉｎ：Ｇａ：Ｚｎ＝１：１：２等を含む。ＩＧＺＯ系半導体は、アモルファスでもよいし、結晶質でもよい。結晶質ＩＧＺＯ系半導体としては、ｃ軸が層面に概ね垂直に配向した結晶質ＩＧＺＯ系半導体が好ましい。このようなＩＧＺＯ系半導体の結晶構造は、例えば、特開２０１２－１３４４７５号公報に開示されている。参考のために、特開２０１２－１３４４７５号公報の開示内容の全てを本明細書に援用する。
　ここで、図９を参照して、各層（膜）の内部応力の評価方法を説明する。シリコンウエファ１の上に、評価対象の膜を堆積する。図９（ａ）に示したように、シリコンウエファ１が上に凸に反ると、膜２ａには、圧縮応力ａcが発生している。このとき、シリコンウエファ１には引張応力が発生している。逆に、図９（ｂ）に示したように、シリコンウエファ１が下に凸に反ると、膜２ｂには、引張応力ａｔが発生している。このとき、シリコンウエファ１には圧縮応力が発生している。
　反りの大きさを測定することによって、シリコンウエファ１の弾性率およびディメンジョン（厚さ、大きさ）と、膜２ａ、２ｂの弾性率およびディメンジョン（厚さ、大きさ）とから、内部応力の大きさを定量的に求めることができる。ここでは、膜ストレス計（テンコール社製）を用いて、各層の内部応力が引張応力か圧縮応力であるかを求めた。なお、膜ストレス計を用いて、曲率半径を求めることによって、内部応力の大きさを求めることができる。
　次に、図１および図３を参照して、本発明の実施形態による他のアクティブマトリクス基板１００Ｂの構造を説明する。図３は、本発明の実施形態による他のアクティブマトリクス基板１００Ｂの模式的な断面図であり、図３（ａ）および（ｂ）は、図２（ａ）および（ｂ）にそれぞれ対応するアクティブマトリクス基板１００Ｂの断面を示している。アクティブマトリクス基板１００Ｂの平面構造は、図１に示したアクティブマトリクス基板１００Ａと同じである。
　アクティブマトリクス基板１００Ｂが有する積層体２３Ｓ２の構造は、アクティブマトリクス基板１００Ａの積層体２３Ｓ１の構造と異なっている。
　積層体２３Ｓ２は、引張応力を有する第１無機絶縁層２３ａ２と、第１無機絶縁層２３ａ２を挟むように形成され、圧縮応力を有する第２無機絶縁層２３ｂ２および第３無機絶縁層２３ｃ２とを有している。この部分の積層構造は、積層体２３Ｓ１と同じである。積層体２３Ｓ２は、さらに、第１透明導電層２２と第２無機絶縁層２３ｂ２との間に、すなわち第２無機絶縁層２３ｂ２の基板１１側に、第４無機絶縁層２３ｄ２を有し、且つ、第２透明導電層２４と第３無機絶縁層２３ｃ２との間に、すなわち第３無機絶縁層２３ｃ２の基板１１とは反対側に、第５無機絶縁層２３ｅ２をさらに有する。積層体２３Ｓ２も、積層体２３Ｓ１と同様に、全体として引張応力を有する。
　ここで、第１無機絶縁層２３ａ２は、例えば、屈折率が１．８０４以下の窒化シリコン層であり、第２無機絶縁層２３ｂ２および第３無機絶縁層２３ｃ２は、例えば、屈折率が１．８０５以上の窒化シリコン層である。また、第４無機絶縁層２３ｄ２および第５無機絶縁層２３ｅ２は、屈折率が１．４以上１．６以下の酸化シリコン層である。屈折率が１．４以上１．６以下の酸化シリコン層も圧縮応力を有する。
　例えば、屈折率が１．８０５以上の窒化シリコン層２３ｂ２および２３ｃ２の厚さをそれぞれｔｈｂ２およびｔｈｃ２とし、屈折率が１．４以上１．６以下の酸化シリコン層２３ｄ２および２３ｅ２の厚さをそれぞれｔｈｄ２およびｔｈｅ２とし、屈折率が１．８０４以下の窒化シリコン層２３ａ２の厚さをｔｈａ２とすると、ｔｈａ２≧ｔｈｂ２＋ｔｈｃ２＋ｔｈｄ２＋ｔｈｅ２の関係を満足することが好ましい。このとき、ｔｈｂ２、ｔｈｃ２、ｔｈｄ２およびｔｈｅ２は、上記と同じ理由から、それぞれ独立に１００ｎｍ以下であることが好ましい。もちろん、厳密には、各層の応力の大きさは、各層の厚さだけでなく、各膜の構造（組成など）の影響を受けるので、上記の関係を有しない場合でも、積層体２３Ｓ２が全体として引張応力を有することがある。発明者の検討によると、上記の関係を満足すれば、積層体２３Ｓ２は、全体として、引張応力を有する。
　アクティブマトリクス基板１００Ｂも、ＴＦＴ１０Ａを覆う有機絶縁層１９をさらに有しており、有機絶縁層１９の一部は、積層体２３Ｓ２の一部と直接接触している。従って、積層体２３Ｓ２は、アクティブマトリクス基板１００Ａの積層体２３Ｓ１と同様に、その下面が接する第１透明導電層２２および有機絶縁層１９との密着性に優れるので、剥離することが抑制される。
　積層体２３Ｓ２を有するアクティブマトリクス基板１００Ｂは、積層体２３Ｓ１を有するアクティブマトリクス基板１００Ａに比べて、透明導電層の還元反応をより効果的に抑制できるという利点がある。
　次に、図４（ａ）～（ｄ）を参照して、アクティブマトリクス基板１００Ｂの製造方法を説明する。図４（ａ）～（ｄ）は、アクティブマトリクス基板１００Ｂの製造方法を説明するための模式的な断面図であり、図３（ａ）のＴＦＴ１０Ａの近傍および図３（ｂ）のゲート端子部１２ｔ付近の断面構造を併せて示している。
　まず、図４（ａ）に示すように、基板（例えばガラス基板）１１を用意し、基板１１上に、ゲートメタル膜を形成し、それをパターニングすることによって、ゲートメタル層１２を形成する。ゲートメタル層１２は、ゲート電極１２ｇ、ゲート配線および補助容量バスライン（ＣＳバスライン）、ゲート端子部１２ｔを含む。補助容量バスライン（不図示）は、補助容量対向電極２２ａに接続され、補助容量対向電圧を供給する。ゲートメタル層１２は、種々の公知の導電膜を用いて公知の方法で形成され得る。ゲートメタル層１２は、例えば、ＭｏＮｂ膜／Ａｌ膜の積層膜（Ａｌ膜が下層）で形成される。ＭｏＮｂ膜／Ａｌ膜の厚さは例えば約２０ｎｍ/約５０ｎｍ～約２００ｎｍ/約３００ｎｍである。ゲートメタル層１２は、例えば、Ａｌ膜、Ｃｕ膜、Ｔａ膜またはＴａＮ膜から形成されてもよい。
　続いて、ゲートメタル層１２を覆うように、ゲート絶縁層１３を形成する。ゲート絶縁層１３は、例えば、厚さが約１００ｎｍ～約６００ｎｍの窒化シリコン（ＳｉＮx）、酸化シリコン（ＳｉＯ2）、または、これらの積層膜から形成される。
　ゲート絶縁層１３上に、半導体層１４を形成する。半導体層１４は、例えば、厚さが約２０ｎｍ～約２００ｎｍのＩｎ－Ｇａ－Ｚｎ－Ｏ系半導体（ＩＧＺＯ系半導体）層である。半導体層１４として、ＩＧＺＯ系半導体層以外の酸化物半導体層であってもよいし、多結晶シリコン層など他の公知の半導体層であってもよい。
　次に、半導体層１４を覆うようにエッチストップ層１５を形成する。エッチストップ層１５は、ソースコンタクトホール１５ａおよびドレインコンタクトホール１５ｂ（図１参照）を有している。エッチストップ層１５を形成する際に、ゲート端子部１２ｔを露出するように、エッチングによって、ゲート絶縁層１３に貫通孔を形成する。エッチストップ層１５は、後の、ソース電極１６Ｓおよびドレイン電極１６Ｄを形成するためのエッチング工程において、半導体層１４を保護する。
　次に、図４（ｂ）に示すように、ソースメタル層１６を形成する。ソースメタル層１６は、ソース電極１６Ｓ、ドレイン電極１６Ｄ、ソースバスラインおよびソース端子部１６ｔ（図１参照）を含む。ソース電極１６Ｓおよびドレイン電極１６Ｄは、それぞれ、例えば、ＭｏＮ層１６Ｓａ／Ａｌ層１６Ｓｂ／ＭｏＮ層１６ＳｃおよびＭｏＮ層１６Ｄａ／Ａｌ層１６Ｄｂ／ＭｏＮ層１６Ｄｃの積層体から形成されている。もちろん、ソースメタル層１６は、他の公知の導電膜を用いて形成され得る。このようにして、半導体層１４上にエッチストップ層１５を有するＴＦＴ１０Ａが得られる。
　次に、ＴＦＴ１０Ａを覆う第１層間絶縁層１７を形成する。第１層間絶縁層１７は、典型的には、無機絶縁層であって、例えば、厚さが約５０ｎｍ～約５００ｎｍの窒化シリコン（ＳｉＮx）、酸化シリコン（ＳｉＯ2）、または、これらの積層膜から形成される。
　さらに、第１層間絶縁層１７の上に、第２層間絶縁層１９を形成する。第２層間絶縁層１９は例えば、厚さが約１０００ｎｍ～約５０００ｎｍの透明樹脂層である。透明樹脂層１９は、基板１１の上に平坦な表面を形成する。また、透明樹脂層１９は、一般的な無機絶縁層に比べて、厚い膜を容易に形成でき、且つ、誘電率が低いので、透明樹脂層１９の上に形成される電極（例えば画素電極）と、透明樹脂層１９の下に形成されている電極や配線（例えば、ゲートバスライン１２やソースバスライン１６）との間の寄生容量を小さくできるという利点を有している。第１層間絶縁層１７（およびエッチストップ層１５、ゲート絶縁層１３）には、図１に示した第１コンタクトホール（画素電極用）１７ａ、第２コンタクトホール（ゲート用）１７ｂおよび第３コンタクトホール（ソース用）１７ｃが形成されている。また、第１透明導電層２２の一部２２ａを補助容量対向電極２２ａとして用いる場合には、補助容量対向電極２２ａを補助容量配線（不図示）と接続するためのコンタクトホールが第１層間絶縁層１７、エッチストップ層１５およびゲート絶縁層１３に形成されている。図４（ｂ）に示した工程では、第２層間絶縁層１９の、上記のコンタクトホールに対応する箇所に貫通孔（下層を露出させる孔）が形成される。第２層間絶縁層１９は例えばポジ型感光性樹脂で形成され、上記貫通孔はフォトリソグラフィ工程で形成される。
　次に、図４（ｃ）に示すように、第１層間絶縁層１７を貫通するコントタクトホール１７ａと、第１層間絶縁層１７、エッチストップ層１５およびゲート絶縁層１３を貫通するコントタクトホール１７ｂとを形成する。このときに、必要に応じて、補助容量対向電極２２ａを補助容量配線（不図示）と接続するためのコンタクトホールも形成する。
　その後、第２層間絶縁層１９上に、第１透明導電層２２を形成する。例えば、厚さが約４０ｎｍ～約１５０ｎｍのＩＴＯ膜をスパッタリング法（条件：例えば、Ａｒ／Ｏ2：３００ｓｃｃｍ／１ｓｃｃｍ、圧力：０．６Ｐａ、ＤＣ電力：２．５ｋＷ）で形成する。得られたＩＴＯ膜をパターニングすることによって、シールド電極または補助容量対向電極２２ａ、第１コンタクト電極２２ｃおよび第１透明端子電極２２ｔを含む第１透明導電層２２が得られる。
　次に、図４（ｄ）に示すように、第１透明導電層２２の上に、積層体２３Ｓ２を形成する。
　例えば、第１透明導電層２２の上に、酸化シリコン層２３ｄ２（条件：例えば、ＳｉＨ4／Ｎ2Ｏ：５０～３００／１０００～７０００ｓｃｃｍ、圧力：１００～３００Ｐａ、ＲＦ電力：４００～３０００Ｗ）、窒化シリコン層２３ｂ２（条件：例えば、ＳｉＨ4／ＮＨ3／Ｎ2：１００～５００／１００～１０００／１０００～６０００ｓｃｃｍ、圧力：１００～３００Ｐａ、ＲＦ電力：４００～４０００Ｗ）、窒化シリコン層２３ａ２（条件：例えば、ＳｉＨ4／ＮＨ3／Ｎ2：１００～５００／１００～１０００／１０００～６０００ｓｃｃｍ、圧力：１００～３００Ｐａ、ＲＦ電力：４００～４０００Ｗ）、窒化シリコン層２３ｃ２（条件：ＳｉＨ４／ＮＨ3／Ｎ2：１００～５００／１００～１０００／１０００～６０００ｓｃｃｍ、圧力：１００～３００Ｐａ、ＲＦ電力：２００～２０００Ｗ）および酸化シリコン層２３ｅ２（条件：えば、ＳｉＨ4／Ｎ2Ｏ：５０～３００／１０００～７０００ｓｃｃｍ、圧力：１００～３００Ｐａ、ＲＦ電力：４００～３０００Ｗ）をこの順で形成する。各層の屈折率および厚さは、以下の通りである。また、図９を参照して説明したように、それぞれの膜を単独でシリコンウエファ１上に形成し、膜ストレス計を用いて測定した内部応力の結果を併せて示す。なお各層の内部応力の大きさは膜厚に依存しない。
　酸化シリコン層２３ｄ２および２３ｅ２は、例えば、屈折率が１．４６、厚さが２０ｎｍで、圧縮応力は約５０ＭＰａである。
　窒化シリコン層２３ｂ２および２３ｃ２は、例えば、屈折率が１．８５、厚さが２０ｎｍで、圧縮応力が１５０ＭＰａである。
　窒化シリコン層２３ａ２は、例えば、屈折率が１．７５、厚さが２００ｎｍで、引張応力は２００ＭＰａである。
　次に、第２透明導電層２４を形成する。第１透明導電層２２と同様に、例えば、厚さが約４０ｎｍ～約１５０ｎｍのＩＴＯ膜をスパッタリング法で形成する。得られたＩＴＯ膜をパターニングすることによって、画素電極２４ｐ、第２コンタクト電極２４ｃおよび第２透明端子電極２４ｔを含む第２透明導電層２４が得られる。
　このようにして、図３に示したアクティブマトリクス基板１００Ｂが得られる。なお、アクティブマトリクス基板１００Ａも、上記酸化シリコン層２３ｄ２および２３ｅ２を省略することによって、同様の方法で製造することができる。
　次に、図５および図６を参照して、本発明の実施形態によるさらに他のアクティブマトリクス基板１００Ｃの構造を説明する。図５は、本発明の実施形態によるさらに他のアクティブマトリクス基板１００Ｃの模式的な平面図である。図６は、アクティブマトリクス基板１００Ｃの模式的な断面図であり、図６（ａ）は、図５中のＡ－Ａ’線に沿った断面を示し、図６（ｂ）は図５中のＢ－Ｂ’線に沿った断面を示している。
　上述したアクティブマトリクス基板１００Ｂの積層体２３Ｓ２は、５つの無機絶縁層を有しているが、第４無機絶縁層２３ｄ２および第５無機絶縁層２３ｅ２のいずれか一方を省略することができる。アクティブマトリクス基板１００Ｃが有する積層体２３Ｓ３は、アクティブマトリクス基板１００Ｂが有する積層体２３Ｓ２の第５無機絶縁層２３ｅ２を有しない。
　すなわち、積層体２３Ｓ３は、引張応力を有する第１無機絶縁層２３ａ３と、第１無機絶縁層２３ａ３を挟むように形成され、圧縮応力を有する第２無機絶縁層２３ｂ３および第３無機絶縁層２３ｃ３とを有している。この部分の積層構造は、積層体２３Ｓ１と同じである。積層体２３Ｓ３は、さらに、第１透明導電層２２と第２無機絶縁層２３ｂ３との間に、すなわち第２無機絶縁層２３ｂ３の基板１１側に、第４無機絶縁層２３ｄ３を有している。積層体２３Ｓ３も、積層体２３Ｓ１および２３Ｓ２と同様に、全体として引張応力を有する。
　ここで、第１無機絶縁層２３ａ３は、例えば、屈折率が１．８０４以下の窒化シリコン層であり、第２無機絶縁層２３ｂ３および第３無機絶縁層２３ｃ３は、例えば、屈折率が１．８０５以上の窒化シリコン層である。また、第４無機絶縁層２３ｄ３は、屈折率が１．４以上１．６以下の酸化シリコン層である。
　例えば、屈折率が１．８０５以上の窒化シリコン層２３ｂ３および２３ｃ３の厚さをそれぞれｔｈｂ３およびｔｈｃ３とし、屈折率が１．４以上１．６以下の酸化シリコン層２３ｄ３の厚さをそれぞれｔｈｄ３とし、屈折率が１．８０４以下の窒化シリコン層２３ａ３の厚さをｔｈａ３とすると、ｔｈａ３≧ｔｈｂ３＋ｔｈｃ３＋ｔｈｄ３の関係を満足することが好ましい。このとき、ｔｈｂ３、ｔｈｃ３、およびｔｈｄ３は、上記と同じ理由から、それぞれ独立に１００ｎｍ以下であることが好ましい。もちろん、厳密には、各層の応力の大きさは、各層の厚さだけでなく、各膜の構造（組成など）の影響を受けるので、上記の関係を有しない場合でも、積層体２３Ｓ３が全体として引張応力を有することがある。発明者の検討によると、上記の関係を満足すれば、積層体２３Ｓ３は、全体として、引張応力を有する。
　アクティブマトリクス基板１００Ｃも、ＴＦＴ１０Ｃを覆う有機絶縁層１９をさらに有しており、有機絶縁層１９の一部は、積層体２３Ｓ３の一部と直接接触している。従って、積層体２３Ｓ３は、アクティブマトリクス基板１００Ａの積層体２３Ｓ１およびアクティブマトリクス基板１００Ｂの積層体２３Ｓ２と同様に、その下面が接する第１透明導電層２２および有機絶縁層１９との密着性に優れるので、剥離することが抑制される。
　積層体２３Ｓ３を有するアクティブマトリクス基板１００Ｃは、積層体２３Ｓ１を有するアクティブマトリクス基板１００Ａに比べて、透明導電層の還元反応をより効果的に抑制できるという利点がある。
　上記のアクティブマトリクス基板１００Ａおよび１００Ｂが有するＴＦＴ１０Ａは、エッチストップ型のＴＦＴであるのに対し、アクティブマトリクス基板１００Ｃが有するＴＦＴ１０Ｃは、チャネルエッチ型のＴＦＴである。
　次に、図７（ａ）～（ｄ）を参照して、アクティブマトリクス基板１００Ｃの製造方法を説明する。図７（ａ）～（ｄ）は、アクティブマトリクス基板１００Ｃの製造方法を説明するための模式的な断面図であり、図６（ａ）のＴＦＴ１０Ｃの近傍および図６（ｂ）のゲート端子部１２ｔ付近の断面構造を併せて示している。以下の説明では、各構成要素を形成する材料や厚さ等は、図４（ａ）～（ｄ）を参照して先に説明したのと同じあってよいので、省略する。
　まず、図７（ａ）に示すように、基板１１を用意し、基板１１上に、ゲートメタル膜を形成し、それをパターニングすることによって、ゲートメタル層１２を形成する。ゲートメタル層１２は、ゲート電極１２ｇ、ゲート配線および補助容量バスライン（ＣＳバスライン）、ゲート端子部１２ｔを含む。
　続いて、ゲートメタル層１２を覆うように、ゲート絶縁層１３を形成し、ゲート絶縁層１３上に、半導体層１４を形成する。
　次に、ソース電極１６Ｓおよびドレイン電極１６Ｄを含むソースメタル層１６を形成する。
　次に、ＴＦＴ１０Ｃを覆う第１層間絶縁層１７を形成する。第１層間絶縁層１７（およびゲート絶縁層１３）には、図５に示した第１コンタクトホール（画素電極用）１７ａ、第２コンタクトホール（ゲート用）１７ｂおよび第３コンタクトホール（ソース用）１７ｃが形成されている。また、第１透明導電層２２の一部２２ａを補助容量対向電極２２ａとして用いる場合には、補助容量対向電極２２ａを補助容量配線（不図示）と接続するためのコンタクトホールが第１層間絶縁層１７およびゲート絶縁層１３に形成されている。図７（ｂ）に示した工程では、第２層間絶縁層１９の、上記のコンタクトホールに対応する箇所に貫通孔（下層を露出させる孔）が形成される。
　次に、図７（ｃ）に示すように、第１層間絶縁層１７を貫通するコントタクトホール１７ａおよび第１層間絶縁層１７およびゲート絶縁層１３を貫通するコントタクトホール１７ｂを形成する。このときに、必要に応じて、補助容量対向電極２２ａを補助容量配線（不図示）と接続するためのコンタクトホールも形成する。
　その後、第２層間絶縁層１９上に、第１透明導電層２２を形成する。ＩＴＯ膜をパターニングすることによって、シールド電極または補助容量対向電極２２ａ、第１コンタクト電極２２ｃおよび第１透明端子電極２２ｔを含む第１透明導電層２２が得られる。
　次に、図７（ｄ）に示すように、第１透明導電層２２の上に、積層体２３Ｓ３を形成する。積層体２３Ｓ３は、図４（ｄ）において、上記酸化シリコン層２３ｅ２を省略することによって、同様の方法で形成することができる。その後、第２透明導電層２４を形成する。ＩＴＯ膜をパターニングすることによって、画素電極２４ｐ、第２コンタクト電極２４ｃおよび第２透明端子電極２４ｔを含む第２透明導電層２４が得られる。このようにして、図５および図６に示したアクティブマトリクス基板１００Ｃが得られる。
　ここでは、チャネルエッチ型ＴＦＴを備えるアクティブマトリクス基板１００Ｃを例示したが、上述のエッチストップ型アクティブマトリクス基板に適用することもできるし、逆に、チャネルエッチ型ＴＦＴを備えるアクティブマトリクス基板に上述の積層体２３Ｓ１、２３Ｓ２を適用することもできる。
　また、上記の実施形態では、２層電極構造を有するＶＡモードの液晶表示装置に用いられるアクティブマトリクス基板を例示したが、これに限られず、本発明の実施形態は、種々のモードの液晶表示装置に用いられるアクティブマトリクス基板に適用される。例えば、上述のＦＦＳモードの液晶表示装置に用いられるアクティブマトリクス基板に適用する場合、第１透明導電層２２は共通電極であり、第２透明導電層２４は、複数のスリットを有する画素電極である。
　本発明の実施形態は、アクティブマトリクス基板、特に、液晶表示装置に好適に用いられるアクティブマトリクス基板に適用される。
　１０Ａ、１０Ｃ　薄膜トランジスタ（ＴＦＴ）
　１１　　　基板
　１２　　　ゲートメタル層（ゲートバスライン）
　１２ｇ　　ゲート電極
　１２ｔ　　ゲート端子部
　１３　　　ゲート絶縁層
　１４　　　半導体層
　１５　　　エッチストップ層
　１５ａ、１５ｂ　コンタクトホール（ソース、ドレイン用）
　１６　　　ソースメタル層（ソースバスライン）
　１６Ｓ　　ソース電極
　１６Ｄ　　ドレイン電極
　１６ｔ　　ソース端子部
　１７　　　第１層間絶縁層（無機絶縁層）
　１７ａ　　第１コンタクトホール（画素電極用）
　１７ｂ　　第２コンタクトホール（ゲート用）
　１７ｃ　　第３コンタクトホール（ソース用）
　１９　　　第２層間絶縁層（透明樹脂層）
　２２　　　第１透明導電層
　２２ａ　　シールド電極または補助容量対向電極
　２２ｃ　　第１コンタクト電極
　２２ｔ　　第１透明端子電極
　２３Ｐ　　第３層間絶縁層
　２３Ｓ１、２３Ｓ２、２３Ｓ３　無機絶縁層積層体
　２３ａ１、２３ｂ１、２３ｃ１　無機絶縁層
　２３ａ２、２３ｂ２、２３ｃ２、２３ｄ２、２３ｅ２　無機絶縁層
　２３ａ３、２３ｂ３、２３ｃ３、２３ｄ３　無機絶縁層
　２４　　　第２透明導電層
　２４ｃ　　第２コンタクト電極
　２４ｐ　　画素電極
　２４ｔ　　第２透明端子電極
　１００、１００Ａ、１００Ｂ、１００Ｃ　アクティブマトリクス基板

Claims (13)

  1. 　基板と、
    　前記基板に支持され、半導体層、ゲート電極、ソース電極およびドレイン電極を有する薄膜トランジスタと、
    　少なくとも一方が前記薄膜トランジスタの前記ドレイン電極と電気的に接続された、第１透明導電層および第２透明導電層と、
    　前記第１透明導電層と前記第２透明導電層との間に形成された、無機絶縁層の積層体とを有し、
    　前記積層体は、引張応力を有する第１無機絶縁層と、前記第１無機絶縁層を挟むように形成され、圧縮応力を有する第２および第３無機絶縁層とを有し、且つ、前記積層体は全体として引張応力を有する、アクティブマトリクス基板。
  2. 　前記第１無機絶縁層は、屈折率が１．８０４以下の窒化シリコン層である、請求項１に記載のアクティブマトリクス基板。
  3. 　前記第２無機絶縁層および前記第３無機絶縁層は、屈折率が１．８０５以上の窒化シリコン層である、請求項１または２に記載のアクティブマトリクス基板。
  4. 　前記第１透明導電層は前記第２透明導電層よりも前記基板の近くに形成されており、前記第２無機絶縁層は前記第３無機絶縁層よりも前記基板の近くに形成されており、
    　前記積層体は、前記第１透明導電層と前記第２無機絶縁層との間に第４無機絶縁層をさらに有する、請求項１から３のいずれかに記載のアクティブマトリクス基板。
  5. 　前記第４無機絶縁層は、屈折率が１．４以上１．６以下の酸化シリコン層である、請求項４に記載のアクティブマトリクス基板。
  6. 　前記積層体は、前記第２透明導電層と前記第３無機絶縁層との間に第５無機絶縁層をさらに有する、請求項４または５に記載のアクティブマトリクス基板。
  7. 　前記第５無機絶縁層は、屈折率が１．４以上１．６以下の酸化シリコン層である、請求項６に記載のアクティブマトリクス基板。
  8. 　前記第１透明導電層および前記第２透明導電層は、ＩＴＯ層またはＩＺＯ層である、請求項１から７のいずれかに記載のアクティブマトリクス基板。
  9. 　前記半導体層は、酸化物半導体層である、請求項１から８のいずれかに記載のアクティブマトリクス基板。
  10. 　前記第１透明導電層は、電気的にフローティング状態にあり、前記第２透明導電層は、画素電極である、請求項１から９のいずれかに記載のアクティブマトリクス基板。
  11. 　前記第１透明導電層は、補助容量対向電極であり、前記第２透明導電層は、画素電極である、請求項１から９のいずれかに記載のアクティブマトリクス基板。
  12. 　前記第１透明導電層は、共通電極であり、前記第２透明導電層は、複数のスリットを有する画素電極である、請求項１から９のいずれかに記載のアクティブマトリクス基板。
  13. 　前記薄膜トランジスタを覆う有機絶縁層を有し、前記有機絶縁層の一部は、前記積層体の一部と直接接触している、請求項１から１２のいずれかに記載のアクティブマトリクス基板。
PCT/JP2012/082784 2011-12-28 2012-12-18 アクティブマトリクス基板 WO2013099697A1 (ja)